RU2115945C1 - Light-sensitive composition

Info

Publication number: RU2115945C1
Application number: RU97109763A
Authority: RU
Inventors: Э.А. Алмазова; Г.М. Чернов
Original assignee: Закрытое акционерное общество "РЕНТЕХ"
Priority date: 1997-06-10
Filing date: 1997-06-10
Publication date: 1998-07-20

Abstract

FIELD: light-sensitive materials. SUBSTANCE: composition is intended for use in instrumentation engineering , mechanical engineering, polygraphy, textile, and wood-working industries for decorating and making inscriptions and drawings on surfaces. Composition contains, wt %: coloration component, 1.5-5.5; tetrabromomethane, 4-6.5; polybutylmethacrylate, 6-13; dibutyl phthalate, 0.8-1.0; chlorinated polyvinylchloride, 0.6-1.3; organic solvent, the balance. EFFECT: increased lifetime of light-sensitive layer. 1 tbl

Description

Изобретение относится к бессеребряным светочувствительным составам, которые могут быть использованы для получения изображений на различных типах поверхностей. The invention relates to silver-free photosensitive compositions that can be used to obtain images on various types of surfaces.

Изобретение может быть использовано в приборостроении, машиностроении, полиграфии, в строительной индустрии, в текстильной, деревообрабатывающей и других отраслях промышленности, в частности для декорирования, нанесения надписей и рисунков на различные поверхности. The invention can be used in instrumentation, engineering, printing, in the construction industry, in the textile, woodworking and other industries, in particular for decoration, inscriptions and drawings on various surfaces.

Известна светочувствительная композиция, включающая, как и данное изобретение, цветообразующее соединение, четырехбромистый углерод и органический растворитель (см. авт. св. СССР 1029124, кл. G 03 C 1/64, 1983). A photosensitive composition is known, including, like this invention, a color-forming compound, carbon tetrabromide and an organic solvent (see ed. St. USSR 1029124, class G 03 C 1/64, 1983).

Недостатками указанной композиции является отсутствие в составе композиции пленкообразующего компонента, что ограничивает область применения, а именно позволяет наносить светочувствительный слой только на бумажную подложку. The disadvantages of this composition is the lack of a film-forming component in the composition, which limits the scope, namely, it allows you to apply the photosensitive layer only on a paper substrate.

Известен светочувствительный материал, светочувствительный слой которого, как и данное изобретение, включает четырехбромистый углерод, цветообразующее соединение и полимерное связующее (см. авт. св. СССР 750419, кл. G 03 C 1/675, 1980). A photosensitive material is known, the photosensitive layer of which, like this invention, includes carbon tetrabromide, a color-forming compound and a polymer binder (see ed. St. USSR 750419, class G 03 C 1/675, 1980).

Недостатками известного светочувствительного материала является ограничение получаемого изображения по цвету (только синий) и по материалу, служащему подложкой для нанесения светочувствительного слоя (только бумага). The disadvantages of the known photosensitive material is the limitation of the received image by color (blue only) and by the material serving as a substrate for applying the photosensitive layer (paper only).

Известна также светочувствительная композиция, включающая цветообразующий компонент, полимерное связующее, четырехбромистый углерод и органический растворитель, что является совпадающими признаками с данным изобретением (см. авт. св. СССР 930204, кл. G 03 C 1/675, 1982). A photosensitive composition is also known, including a color-forming component, a polymeric binder, carbon tetrabromide and an organic solvent, which are coincident features with this invention (see ed. St. USSR 930204, class G 03 C 1/675, 1982).

Недостатками известной композиции является низкая устойчивость воспроизведенного изображения к действию органического растворителя, что обусловливает сложность получения многоцветных рисунков. The disadvantages of the known composition is the low stability of the reproduced image to the action of an organic solvent, which makes it difficult to obtain multi-color patterns.

Наиболее близким к изобретению составом того же назначения по совокупности признаков является "светочувствительная композиция, состоящая из цветообразующего компонента, полибутилакрилата (М=150000-200000), тетрабромметана, дибутилфталата и органического растворителя [1]. Closest to the invention, the composition for the same purpose in terms of features is a "photosensitive composition consisting of a color-forming component, polybutyl acrylate (M = 150000-200000), tetrabromomethane, dibutyl phthalate and an organic solvent [1].

К недостаткам известной композиции, принятой за прототип, относится то, что при нанесении указанного состава на обрабатываемую поверхность имеет место быстрая потеря светочувствительности слоя, а именно за 10 мин светочувствительность слоя уменьшается вдвое. The disadvantages of the known composition adopted for the prototype, is that when applying the specified composition to the surface to be treated, there is a rapid loss of photosensitivity of the layer, namely, in 10 minutes the photosensitivity of the layer is halved.

Сущность изобретения заключается в следующем. The invention consists in the following.

Изобретение направлено на решение задачи усовершенствования технологии получения надписей и рисунков на различных поверхностях с помощью обработки поверхности светочувствительным составом с последующим экспонированием изображения УФ-светом. The invention is aimed at solving the problem of improving the technology for obtaining inscriptions and drawings on various surfaces by surface treatment with a photosensitive composition, followed by exposure of the image with UV light.

Осуществление изобретения позволяет увеличить срок сохранности светочувствительности обрабатываемой поверхности и обеспечить продление промежутка времени между операцией нанесения светочувствительной композиции и операцией экспонирования воспроизводимого изображения при сохранении адгезионных свойств композиции. The implementation of the invention allows to increase the shelf life of the photosensitivity of the treated surface and to extend the time interval between the operation of applying the photosensitive composition and the operation of exposure of the reproduced image while maintaining the adhesive properties of the composition.

Изобретение представляет собой светочувствительную композицию, существенными признаками которой по сравнению с прототипом является введение в состав композиции полибутилметакрилата и хлорированного поливинилхлорида при следующем соотношении компонентов, мас.%:
Цветообразующий компонент - 1,5-5,5
Тетрабромметан - 4,0 - 6,5
Полибутилметакрилат - 6,0- 13,0
Дибутилфталат - 0,8-1,0
Хлорированный поливилилхлорид - 0,6-1,3
Органический растворитель - Остальное
Исследования показали, что введение в состав композиции двух полимерных соединений, а именно полибутилметакрилата и хлорированного поливинилхлорида, позволяет по крайней мере на порядок увеличить срок сохранности светочувствительного слоя. Пропорциональное соотношение двух полимерных соединений, а именно полибутилметакрилата и хлорированного поливинилхлорида, выбрано экспериментально. Указанное пропорциональное соотношение полимеров позволяет сохранить светочувствительный слой без ухудшения его адгезионных свойств, то есть позволяет получить указанный технический результат при осуществлении изобретения.The invention is a photosensitive composition, the essential features of which, compared with the prototype, is the introduction of polybutyl methacrylate and chlorinated polyvinyl chloride in the composition in the following ratio, wt.%:
Color-forming component - 1.5-5.5
Tetrabromomethane - 4.0 - 6.5
Polybutyl methacrylate - 6.0 - 13.0
Dibutyl phthalate - 0.8-1.0
Chlorinated Polyvinyl Chloride - 0.6-1.3
Organic Solvent - Else
Studies have shown that the introduction of two polymer compounds, namely polybutyl methacrylate and chlorinated polyvinyl chloride, into the composition allows at least an order of magnitude increase in the shelf life of the photosensitive layer. A proportional ratio of two polymer compounds, namely polybutyl methacrylate and chlorinated polyvinyl chloride, was chosen experimentally. The specified proportional ratio of polymers allows you to save the photosensitive layer without compromising its adhesive properties, that is, it allows to obtain the specified technical result in the implementation of the invention.

Полимерные соединения, входящие в состав заявляемой композиции, производятся отечественной промышленностью в соответствии с отраслевыми стандартами: полибутилметакрилат - ТУ 6-01-432-69; хлорированный поливинилхлорид - ОСТ 6-01 -37-79. The polymer compounds that make up the claimed composition are produced by the domestic industry in accordance with industry standards: polybutyl methacrylate - TU 6-01-432-69; chlorinated polyvinyl chloride - OST 6-01 -37-79.

Заявляемая светочувствительная композиция представляет собой смесь ингредиентов, в состав которой в качестве цветообразующих компонентов входят дифениламин и/или индол, и/или ферроцен и/или n-диметиламинобензальдегид, в качестве органического растворителя присутствуют смеси, например ксилол, ацетон, бутилацетат. The inventive photosensitive composition is a mixture of ingredients, the composition of which as color-forming components includes diphenylamine and / or indole and / or ferrocene and / or n-dimethylaminobenzaldehyde, mixtures of, for example, xylene, acetone, butyl acetate are present as an organic solvent.

Пример. Для получения заявляемой светочувствительной композиции в органическом растворителе, представляющем собой смесь 40% ксилола, 30% бутилацетата и 30% ацетона, растворяют при комнатной температуре необходимое количество цветообразующего компонента, тетрабромметана, полибутилметакрилата, дибутилфталата и хлорированного поливинилхлорида. Полученную смесь наносят на подложку путем полива, пульверизации или с помощью центрифуги. Подложкой, то есть материалом, на который требуется нанести изображение, может с равным успехом служить пластина, изготовленная из алюминия, стали, латуни, бронзы или другого металла, полимерная пленка типа полиэтилентерофталатной, ткань как синтетическая, так и натуральная, а также стеклянные и деревянные поверхности. Example. To obtain the inventive photosensitive composition in an organic solvent, which is a mixture of 40% xylene, 30% butyl acetate and 30% acetone, the required amount of a color-forming component, tetrabromomethane, polybutyl methacrylate, dibutyl phthalate and chlorinated polyvinyl chloride is dissolved at room temperature. The resulting mixture is applied to the substrate by irrigation, spraying or using a centrifuge. A plate made of aluminum, steel, brass, bronze or another metal, a polymer film of the type polyethylene-phthalate, a fabric both synthetic and natural, as well as glass and wooden, can serve as a substrate, that is, the material on which the image is to be applied. surface.

Нанесенную композицию высушивают в темноте при комнатной температуре в течение 3 - 5 мин. При этом толщина светочувствительного слоя составляет 5 - 10 мкм. The applied composition is dried in the dark at room temperature for 3-5 minutes. Moreover, the thickness of the photosensitive layer is 5 - 10 microns.

Для получения видимого изображения светочувствительный слой экспонируют светом ртутной лампы ПКР - 4, снабженной светофильтром УФС -6 и БС-6 на расстоянии 20 см. Фиксирование осуществляют тепловой обработкой при 80-100^oC.To obtain a visible image, the photosensitive layer is exposed to the light of a PKR-4 mercury lamp equipped with a UFS-6 and BS-6 light filter at a distance of 20 cm. Fixation is carried out by heat treatment at 80-100 ^o C.

Определение сохранности светочувствительности и сравнение этого показателя с прототипом производили по следующей методике. Сразу по окончании просушки измеряли энергетическую светочувствительность слоя как энергию света, необходимую для получения оптической плотности окраски, равной 1. Далее через равные промежутки времени (10 -15 мин) повторяли измерения светочувствительности слоя. Определяли интервал времени, в течение которого происходит, уменьшение светочувствительности в два раза (τ_1/2) . Результаты испытаний заявляемой композиции с использованием различных цветообразующих компонентов и различным соотношением ингредиентов, входящих в композицию, в сравнении с прототипом приведены в таблице.The determination of the sensitivity of photosensitivity and comparison of this indicator with the prototype was carried out by the following method. Immediately after drying, the energy photosensitivity of the layer was measured as the light energy necessary to obtain the optical density of the color equal to 1. Then, at regular intervals (10 -15 min), measurements of the photosensitivity of the layer were repeated. The time interval during which the light sensitivity was halved (τ _1/2 ) was determined. The test results of the claimed composition using various color-forming components and a different ratio of ingredients included in the composition, in comparison with the prototype are shown in the table.

Таким образом, изложенные сведения свидетельствуют о том, что заявляемая светочувствительная композиция отвечает требуемым критериям патентоспособности и обладает значительными преимуществами по сравнению с известными средствами, предназначенными для достижения той же цели, а именно
- светочувствительная композиция предназначена для использования в приборостроении, машиностроении, полиграфии, в строительной индустрии, в текстильной, деревообрабатывающей и других отраслях промышленности, в частности для декорирования, нанесения надписей и рисунков на различные поверхности,
- для заявляемой светочувствительной композиции, содержащей следующие ингредиенты, мас.%:
Цветообразующий компонент - 1,5-5,5
Тетрабромметан - 4,0-6,5
Полибутилметакрилат - 6,0-13,0
Дибутилфталат - 0,8 -1,0
Хлорированный поливинилхлорид - 0,6-1,3
Органический растворитель - Остальное
подтверждена возможность ее изготовления и применения с помощью описанных в заявке средств и методов.Thus, the above information indicates that the inventive photosensitive composition meets the required criteria for patentability and has significant advantages compared with the known means designed to achieve the same goal, namely
- the photosensitive composition is intended for use in instrumentation, mechanical engineering, printing, in the construction industry, in the textile, woodworking and other industries, in particular for decoration, inscriptions and drawings on various surfaces,
- for the inventive photosensitive composition containing the following ingredients, wt.%:
Color-forming component - 1.5-5.5
Tetrabromomethane - 4.0-6.5
Polybutylmethacrylate - 6.0-13.0
Dibutyl phthalate - 0.8 -1.0
Chlorinated Polyvinyl Chloride - 0.6-1.3
Organic Solvent - Else
confirmed the possibility of its manufacture and use using the means and methods described in the application.

Использование светочувствительной композиции позволяет увеличить срок сохранности светочувствительного слоя по крайней мере на порядок по сравнению с другими известными составами того же назначения при сохранении адгезионных свойств светочувствительного слоя. The use of the photosensitive composition can increase the shelf life of the photosensitive layer by at least an order of magnitude compared with other known formulations of the same purpose while maintaining the adhesive properties of the photosensitive layer.

Claims

A photosensitive composition containing a color-forming component, tetrabromomethane, dibutyl phthalate and an organic solvent, characterized in that it additionally contains polybutyl methacrylate and chlorinated polyvinyl chloride in the following ratio, wt.%:
Color-forming component - 1.5 - 5.5
Tetrabromomethane - 4.0 - 6.5
Polybutyl methacrylate - 6.0 - 13.0
Dibutyl phthalate - 0.8 - 1.0
Chlorinated Polyvinyl Chloride - 0.6 - 1.3
Organic Solvent - Else