RU2105779C1

RU2105779C1 - Composition for anticorrosion coating

Info

Publication number: RU2105779C1
Application number: RU96120652A
Authority: RU
Inventors: Б.С. Смыков; В.А. Аксенов; А.В. Богданов; Д.А. Богданов; В.И. Максимов
Original assignee: Общество с ограниченной ответственностью "Фирма "Самис Лтд."
Priority date: 1996-10-15
Filing date: 1996-10-15
Publication date: 1998-02-27

Abstract

FIELD: chemical industry. SUBSTANCE: present invention describes compositions for anticorrosion coatings which include copolymer based on stillage residues resulting from styrene rectification and are intended preferably for protection of metallic, including steel, structures which are used at metal surface temperatures up to 150 C. The claimed composition comprises, wt. -%: copolymer based on stillage residues resulting from styrene rectification, 8-11; polyvinyl chloride, 11-13; cyclohexanone, 27-29; polystyrene, 4-6; antimony sesquioxide, 4-6; filler, 8-10; pigment, 5-7; and xylene, the balance. At comparatively low cost of coatings, at least by 1.5 times less then that for coatings used at present for the same purpose and having the same properties, the claimed coating retains invariable external appearance and protective properties for prolonged period of time, since composition components afford barrier and adhesion mechanism of protective effect of the claimed coating in the presence of temperature stabilizer. EFFECT: improved properties of the composition. 3 tbl

Description

Изобретение относится к композициям для антикоррозионных покрытий с использованием сополимера на основе кубовых остатков ректификации стирола (сополимер КОРС) и предназначено преимущественно для защиты металлических в том числе, стальных) конструкции, эксплуатируемых при температуре поверхностей металла до +150^oC.The invention relates to compositions for anticorrosion coatings using a copolymer based on distillation distillation residues of styrene (KORS copolymer) and is intended primarily to protect metal structures, including steel), operated at metal surface temperatures up to +150 ^o C.

Известна композиция для антикоррозионного покрытия, включающая сополимер на основе кубовых остатков ректификации стирола (сополимер КОРС) в качестве пленкообразователя, полиариленалкилы, пластификатор, асбест в качестве наполнителя, ксилол в качестве органического растворителя /1/. A known composition for anticorrosion coating, including a copolymer based on distillation residues of styrene rectification (KORS copolymer) as a film former, polyarylenealkyl, a plasticizer, asbestos as a filler, xylene as an organic solvent / 1 /.

Покрытия на основе данной композиции имеют при сравнительно небольшой стоимости, верхнюю границу температурного диапазона применения до температуры поверхности +70^oC.Coatings based on this composition have, at a relatively low cost, an upper limit of the temperature range of application to a surface temperature of +70 ^o C.

Известна композиция для антикоррозионного покрытия, включающая сополимер на основе кубовых остатков ректификации стирола (сополимер КОРС) в качестве пленкообразователя, пластификатор, асбест в качестве наполнителя, ксилол в качестве органического растворителя, сополимер на основе олигомеров бутадиена с метилметакрилатом /2/. A known composition for anticorrosion coating, including a copolymer based on distillation residues of styrene rectification (KORS copolymer) as a film former, plasticizer, asbestos as a filler, xylene as an organic solvent, a copolymer based on butadiene oligomers with methyl methacrylate / 2 /.

Недостатком является то, что при сравнительно небольшой стоимости покрытия оно имеет верхнюю границу диапазона применения до температуры поверхности +70^oC.The disadvantage is that at a relatively low cost of coating, it has the upper limit of the range of application up to a surface temperature of +70 ^o C.

Наиболее близкой по технической сущности, принятой в качестве прототипа, является композиция для антикоррозионного покрытия, включающая сополимер на основе кубовых остатков ректификации стирола (сополимер КОРС), ксилол, наполнитель, пигмент. Кроме того, в известную композицию включен пластификатор и полимеризат ненасыщенных соединений пиролиза жидких и газообразных нефтепродуктов фракции C₈-C₉ -смола СПП 9-14 /3/.The closest in technical essence, adopted as a prototype, is a composition for anti-corrosion coating, including a copolymer based on distillation residues of styrene rectification (KORS copolymer), xylene, filler, pigment. In addition, the known composition includes a plasticizer and a polymerizate of unsaturated pyrolysis compounds of liquid and gaseous petroleum products fraction C ₈ -C ₉ resin SPP 9-14 / 3 /.

Достоинством композиции является сравнительно невысокая стоимость покрытия. Недостатком является то, что покрытие имеет верхнюю границу температурного диапазона применения до температуры поверхности +70^oC.The advantage of the composition is the relatively low cost of coverage. The disadvantage is that the coating has an upper limit of the temperature range of application to a surface temperature of +70 ^o C.

Задача, на решение которой направлено заявляемого изобретения, заключается в создании композиции, обеспечивающей расширение температурного диапазона применения покрытия до температуры поверхности +150^oC при сохранения низкой стоимости в сравнении с ныне используемыми композициями для покрытий с аналогичными свойствами.The problem to which the invention is directed, is to create a composition that expands the temperature range of application of the coating to a surface temperature of +150 ^o C while maintaining a low cost in comparison with the currently used coating compositions with similar properties.

Поставленная задача решена следующим образом. Согласно заявляемому изобретению композиция для антикоррозионного покрытия, включающая сополимер на основе кубовых остатков ректификации стирола, ксилол, пигмент, наполнитель, имеет отличительные существенные признаки в новой совокупности существенных признаков, а именно композиция дополнительно содержит поливинилхлорид, циклогексанон, полистирол и сесквиоксид сурьмы при следующем соотношении компонентов, мас. The problem is solved as follows. According to the claimed invention, the composition for anti-corrosion coating, including a copolymer based on distillation residues of styrene, xylene, pigment, filler, has distinctive essential features in a new set of essential features, namely, the composition additionally contains polyvinyl chloride, cyclohexanone, polystyrene and antimony sesquioxide in the following ratio of components wt.

Сополимер на основе кубовых остатков ректификации стирола 8-11
Поливинилхлорид 11-13
Циклогексанон 27-29
Полистирол 4-6
Сесквиоксид сурьмы 4-6
Наполнитель 8-10
Пигмент 5-7
Ксилол Остальное
Поливинилхлорид для которого введен растворитель-циклогексанон) и полистирол в присутствии содержащегося в покрытии сесквиоксида сурьмы обеспечивают уверенно при температуре до +150^oC преимущественно барьерный механизм защитного действия покрытия, а адгезионный механизм защитного действия покрытия при температуре до +150^oC в присутствии сесквиоксида сурьмы обеспечивает преимущественно сополимер на основе кубовых остатков ректификации стирола, таким образом, предлагаемое покрытие обладают смешанным механизмом защитного действия, дающим наибольший и долговременный защитный эффект, при этом при небольшой стоимости покрытия, не менее чем в 1,5 раза меньшей, чем у используемых в настоящее время для этой же цели покрытий с теми же свойствами.The copolymer based on distillation distillation residues styrene 8-11
Polyvinyl chloride 11-13
Cyclohexanone 27-29
Polystyrene 4-6
Antimony Sesquioxide 4-6
Filler 8-10
Pigment 5-7
Xylene Else
Polyvinyl chloride for which solvent-cyclohexanone has been introduced) and polystyrene in the presence of antimony sesquioxide contained in the coating provide confidently at a temperature of up to +150 ^o C the predominantly barrier mechanism of the protective action of the coating, and the adhesive mechanism of the protective action of the coating at temperatures up to +150 ^o C in the presence of antimony sesquioxide mainly provides a copolymer based on distillation distillation residues of styrene, thus, the proposed coating have a mixed protective mechanism, yes which has the greatest and long-term protective effect, at the same time, at a low coating cost, not less than 1.5 times less than that of coatings currently used for the same purpose with the same properties.

В качестве сополимера на основе кубовых остатков ректификации стирола используют продукт совместной полимеризации кубового остатка ректификации стирола с ангидридами кислот (малеиновым ангидридом) (ГОСТ 11153-75). As a copolymer based on vat residues of rectification of styrene, the product of the joint polymerization of vat residue of rectification of styrene with acid anhydrides (maleic anhydride) is used (GOST 11153-75).

Поливинилхлорид продукт радикально-цепной полимеризации винилхлорида со степенью полимеризации 100-2500, в композиции может быть использован поливинилхлорид ПВХ-66026 (ГОСТ14039-78). Polyvinyl chloride is a product of the radical chain polymerization of vinyl chloride with a degree of polymerization of 100-2500, PVC-66026 polyvinyl chloride (GOST14039-78) can be used in the composition.

Циклогексанон (ГОСТ 24615-78) пимелиновой кетон, в композиции используется как растворитель поливинилхлорида. Cyclohexanone (GOST 24615-78) is a pimeline ketone, used in the composition as a solvent for polyvinyl chloride.

Полистирол полимер, продукт полимеризации стирола (ГОСТ 20289-84). Polystyrene polymer, a product of the polymerization of styrene (GOST 20289-84).

Сесквиоксид сурьмы (ТУ6-09-32-67-84) известен как термостабилизатор пластмасс. Antimony sesquioxide (TU6-09-32-67-84) is known as a heat stabilizer for plastics.

В качестве наполнителя может быть использован тальк молотый для лакокрасочной промышленности (ТУ 21-25-201-77), слюда мусковит молотая (ГОСТ 855-74). Powdered talcum powder for the paint and varnish industry (TU 21-25-201-77), ground muscovite mica (GOST 855-74) can be used as a filler.

В качестве пигмент могут быть использованы диоксид титана пигментный (ТУ 6-10-1650-85), белила цинковые (ГОСТ 202-84), сурик железный (ГОСТ 8135-74), пигмент желтый железноокисный (ГОСТ 18172-72), пигмент красный железноокисный (ТУ 6-10-602-74). As the pigment can be used titanium dioxide pigment (TU 6-10-1650-85), zinc white (GOST 202-84), red iron oxide (GOST 8135-74), yellow iron oxide pigment (GOST 18172-72), red pigment iron oxide (TU 6-10-602-74).

Ксилол нефтяной (ГОСТ 9410-78) органический растворитель. Petroleum xylene (GOST 9410-78) is an organic solvent.

Композицию для антикоррозионного покрытия получают путем вначале образования двух растворов: во-первых, взятого в рецептурном количестве порошкообразного поливинилхлорида в рецептурном количестве циклогексанона, во-вторых, взятого в рецептурном количестве гранулированного полистирола в рецептурном количестве ксилола, а затем смешивают эти растворы одновременно с сополимером на основе кубовых остатков ректификации стирола, взятым в рецептурном количестве, до образования однородной пленкообразующей основы композиции, после чего последнюю перемешивают с рецептурными количествами сесквиоксида сурьмы, наполнителя и пигмента, диспергируют путем обработки в дезинтеграторе и бисерной мельнице до необходимой степени перетира, после чего фильтруют и разливают в тару. The composition for the anticorrosion coating is obtained by first forming two solutions: first, taken in a prescription amount of powdered polyvinyl chloride in a prescription amount of cyclohexanone, secondly, taken in a prescription amount of granular polystyrene in a prescription amount of xylene, and then these solutions are mixed simultaneously with the copolymer on based on still bottoms of styrene rectification, taken in a prescription amount, until a homogeneous film-forming base of the composition is formed, after which the latter is mixed with prescription amounts of antimony sesquioxide, filler and pigment, dispersed by treatment in a disintegrator and a bead mill to the required degree of grinding, after which it is filtered and poured into a container.

На поверхность изделия композицию наносят кистью, краскораспылителем, валиком. On the surface of the product, the composition is applied by brush, spray gun, roller.

Испытания проводили следующим образом. The tests were carried out as follows.

Для определения показателей: внешний вид пленки, эластичность, адгезия, твердость пленки покрытия и теплостойкость пленки при температуре +150^oC подготовка образцов к испытаниям производилась по ГОСТ 8832-76. На стальные образцы из низкоуглеродистой стали Ст.3 с размерами 100х30х1,8 мм при помощи краскораспылителя наносили следующие составы: известная композиция прототип и варианты состава предлагаемой композиции, в один слой с последующей просушкой в течение 2 ч. при 60-65^oC. Толщина пленки после высыхания составила 30 мкм.To determine the indicators: the appearance of the film, elasticity, adhesion, hardness of the coating film and heat resistance of the film at a temperature of +150 ^o C the preparation of samples for testing was carried out according to GOST 8832-76. The following compositions were applied to steel samples of low-carbon steel St.3 with dimensions 100x30x1.8 mm using a spray gun: the known composition is a prototype and the composition of the proposed composition is applied in one layer, followed by drying for 2 hours at 60-65 ^o C. Thickness the film after drying was 30 μm.

Внешний вид определяли после охлаждения визуально при рассеянном свете. Определение эластичности пленки производили по ГОСТ 6806-78, диаметр стержня по шкале гибкости 1 мм, определение твердости пленки производили по ГОСТ 5233-89 на стеклянной пластины. Определение адгезии производили по ГОСТ 15140-78. Appearance was determined visually in ambient light after cooling. The elasticity of the film was determined according to GOST 6806-78, the diameter of the rod on a flexibility scale of 1 mm, the determination of the film hardness was made according to GOST 5233-89 on a glass plate. The adhesion was determined according to GOST 15140-78.

Теплостойкость пленки покрытия при температуре +150^oC определяли путем помещения пластинки с нанесенным и высушенным покрытием в термостат, имеющего температуру +150^oC и соответствующей выдержки. Затем пластинку вынимали, охлаждали до комнатной температуры и рассматривали при дневном свете.The heat resistance of the coating film at a temperature of +150 ^o C was determined by placing the plate with the applied and dried coating in a thermostat having a temperature of +150 ^o C and the corresponding exposure. Then the plate was removed, cooled to room temperature and examined in daylight.

Изобретение иллюстрируют следующие примеры конкретного выполнения (см. табл. 1) и показателей при испытании (см. табл. 2) по внешнему виду пленки покрытия, эластичности, адгезии, твердости. Показатели при испытаниях на теплостойкость пленки покрытия при температуре -150^oC сведены в табл. 3.The invention is illustrated by the following examples of specific performance (see table. 1) and indicators during the test (see table. 2) on the appearance of the coating film, elasticity, adhesion, hardness. The indicators when tested for heat resistance of the coating film at a temperature of -150 ^o C are summarized in table. 3.

Источники информации. Sources of information.

1. Авторское свидетельство СССР N 905245, М. кл. C 09 D 5/08, C 09 D 3/733, опубл. 15.02.82, бюл. N 6. 1. USSR author's certificate N 905245, M. cl. C 09 D 5/08, C 09 D 3/733, publ. 02/15/82, bull. N 6.

2. Авторское свидетельство СССР N 1502593, М. кл. C 09 D 5/08, опубл. 23.08.89, бюл. N 31. 2. USSR author's certificate N 1502593, M. cl. C 09 D 5/08, publ. 08/23/89, bull. N 31.

3. Авторское свидетельство СССР N 1726485, М. кл. C 09 D 5/28, CD 4 B 41/61, опубл. 15.04.92. бюл. N 14 (прототип). 3. Copyright certificate of the USSR N 1726485, M. cl. C 09 D 5/28, CD 4 B 41/61, publ. 04/15/92. bull. N 14 (prototype).

Claims

Composition for anticorrosion coating, including a copolymer based on distillation distillation residues of styrene, xylene, filler, pigment, characterized in that it additionally contains polyvinyl chloride, cyclohexanone, polystyrene and antimony sesquioxide in the following ratio of components, wt.

A copolymer based on distillation distillation residues styrene 8 11
Polyvinyl chloride 11 13
Cyclohexanone 27 29
Polystyrene 4 6
Antimony sesquioxide 4 6
Filler 8 10
Pigment 5 7
Xylene Rest