RU2067560C1

RU2067560C1 - Stained glass

Info

Publication number: RU2067560C1
Authority: RU
Inventors: З.И. Горькая; И.Н. Беликов; Н.И. Захаренко; Р.В. Фетисова; Л.А. Булышева
Original assignee: Акционерное общество открытого типа "Старьстекло"
Priority date: 1991-09-11
Filing date: 1991-09-11
Publication date: 1996-10-10

Abstract

FIELD: glass industry. SUBSTANCE: stained glass has, wt.-%: silicon oxide (SiO₂) 65.00-72.72; aluminium oxide (Al₂O₃) 3.03-8.07; sodium oxide (Na₂O) 12.11-17.00; calcium oxide (CaO) 1.01-5.05; fluorine (F¹) 1.00-4.04; magnesium oxide (MgO) 0.001-4.06; ferric oxide (Fe₂O₃) 0.01-1.01; sulfur (S^-6) 0.0001-1.01; potassium oxide (K₂O,) 0.0001-2.02; calcium fluoride (CaF₂) 0.5-4.04; ferrous sulfide (FeS) 0.012-1.52 and at least one component from the group: cobalt oxide (Co₂O₃) 0.005-0.20; copper oxide (CuO) 0.005-0.50; cerium oxide (Ce₂O₃) 0.001-0.50; manganese oxide (MnO) 0.005-0.50; nickel oxide (NiO) 0.005-0.25, and selenium (Se) 0.005-0.10. Ratio ΣFe₂O₃+S^-2/FeS = 0.67-1.83, ray transmission at wavelength 560-600 nm is 2-14.5%. Glass is used for light-filter making. EFFECT: enhanced quality of glass. 2 tbl

Description

Изобретение относится к составам цветных силикатных стекол, используемых преимущественно в качестве светофильтров, при изготовлении декоративных плафонов, для светильников, мозаик, смальт, цветной коврово-мозаичной плитки, а также в строительных целях для остекления и создания декоративного эффекта. The invention relates to compositions of colored silicate glasses, used primarily as light filters, in the manufacture of decorative shades, for fixtures, mosaics, smalt, colored carpet and mosaic tiles, as well as for construction purposes for glazing and creating a decorative effect.

Известно цветное силикатное стекло следующего состава, мас. Known colored silicate glass of the following composition, wt.

SiO₂ 68,0-74,0
Al₂O₃ 0-5,0
Na₂O 11,0-15,0
K₂O 0-5,0
Fe₂O₃ 0,18-0,4
CaO 6,0-15,0
MgO 0-6,0
Cr₂O₃ 0,08-0,2
S 0,01-0,04
CoO 0-0,015 (1)
Это стекло имеет желтую или зеленую окраску, его чистота цвета не более 97% цветовой тон находится в пределах 568-580 нм, стекло имеет низкое пропускание в интервале 560-600 нм не более 21-35%
Наиболее близким по химическому составу к предлагаемому изобретению является состав стекла, мас.SiO ₂ 68.0-74.0
Al ₂ O ₃ 0-5.0
Na ₂ O 11.0-15.0
K ₂ O 0-5.0
Fe ₂ O ₃ 0.18-0.4
CaO 6.0-15.0
MgO 0-6.0
Cr ₂ O ₃ 0.08-0.2
S 0.01-0.04
CoO 0-0.015 (1)
This glass has a yellow or green color, its color purity is not more than 97%, the color tone is in the range of 568-580 nm, the glass has a low transmission in the range of 560-600 nm, not more than 21-35%
The closest chemical composition to the present invention is the composition of glass, wt.

SiO₂ 68,0-75,0
Al₂O₃ 0,5-3,5
Na₂O 12,0-17,0
CaO 5,0-8,0
MgO 1,0-4,60
Fe₂O₃ 0,005-0,1
S 0,005-0,25
BaO 0,1-2-0
и/или
K₂O 0,01-4,0
F' 0,01-0,5
и/или
Cl' 0,01-0,5
FeS 0,04-0,5
причем соотношение

Недостатком указанного состава стекла является высокое спектральное пропускание от 40 до 65% лучей в интервале длин волн 560-600 нм. Стекло имеет желтый цвет.SiO ₂ 68.0-75.0
Al ₂ O ₃ 0.5-3.5
Na ₂ O 12.0-17.0
CaO 5.0-8.0
MgO 1.0-4.60
Fe ₂ O ₃ 0.005-0.1
S 0.005-0.25
BaO 0.1-2-0
and / or
K ₂ O 0.01-4.0
F '0.01-0.5
and / or
Cl '0.01-0.5
FeS 0.04-0.5
moreover, the ratio

The disadvantage of this glass composition is the high spectral transmittance of 40 to 65% of the rays in the wavelength range of 560-600 nm. Glass has a yellow color.

Целью изобретения является снижение пропускания спектральных лучей с длиной волны 560-600 нм менее 15% получение цветного стекла с широкой цветовой гаммой. The aim of the invention is to reduce the transmission of spectral rays with a wavelength of 560-600 nm less than 15%, the production of colored glass with a wide color gamut.

Стекло имеет следующий состав, мас. Glass has the following composition, wt.

SiO₂ 65,0-72,72
Al₂O₃ 3,03-8,07
Na₂O 12,11-17,00
CaO 1,01-5,04
F' 1,00-4,04
MgO 0,001-4,06
Fe₂O₃ 0,01-1,01
S^-2 0,0001-1,01
K₂O 0,00001-2,02
CaF₂ 0,5-4,04
FeS 0,012-1,52
и, по крайней мере, один краситель из группы,
Co₂O₃ 0,005-0,20
CuO 0,005-0,50
Cr₂O₃ 0,0001-0,50
MnO 0,005-0,50
NiO 0,005-0,25
Se 0,005-0,10
причем соотношение

Присутствие в составе стекла СaF₂ обеспечивает определенное поглощение лучей с длиной волны 560-600 нм и достаточную чистоту цвета, а присутствие, по крайней мере, одного компонента из группы: Сo₂O₃, CuO, Cr₂O₃, MnO, NiO, Se обеспечивает многообразие цветовой гаммы стекла. При этом минимальные количества красителя обеспечивают появление определенной окраски стекла, а максимальные количества красителя ограничены требованием чистоты определенного цвета.SiO ₂ 65.0-72.72
Al ₂ O ₃ 3.03-8.07
Na ₂ O 12.11-17.00
CaO 1.01-5.04
F '1.00-4.04
MgO 0.001-4.06
Fe ₂ O ₃ 0.01-1.01
S ^-2 0.0001-1.01
K ₂ O 0.00001-2.02
CaF ₂ 0.5-4.04
FeS 0.012-1.52
and at least one dye from the group,
Co ₂ O ₃ 0.005-0.20
CuO 0.005-0.50
Cr ₂ O ₃ 0.0001-0.50
MnO 0.005-0.50
NiO 0.005-0.25
Se 0.005-0.10
moreover, the ratio

The presence of CaF ₂ in the glass composition provides a certain absorption of rays with a wavelength of 560-600 nm and sufficient color purity, and the presence of at least one component from the group: Co ₂ O ₃ , CuO, Cr ₂ O ₃ , MnO, NiO, Se provides a variety of colors for glass. In this case, the minimum amount of dye provides the appearance of a certain color of the glass, and the maximum amount of dye is limited by the requirement of purity of a certain color.

Минимальные и максимальные количества основных компонентов определены варочными и выработочными свойствами стекла. The minimum and maximum quantities of the main components are determined by the cooking and developmental properties of the glass.

Присутствие в составе стекла Fe₂O₃, S^-2 и FeS позволяют расширить цветовую гамму стекла, сделать резкие, неприятные для глаза тона более мягкими, естественными. Минимальные количества этих компонентов обусловлены появлением дополнительной окраски, а максимальные количества обусловлены сохранением определенной чистоты тона.The presence of Fe ₂ O ₃ , S ^-2 and FeS in the glass composition allows you to expand the color gamut of the glass, to make harsh, unpleasant for the eye tones softer, more natural. The minimum amounts of these components are due to the appearance of additional color, and the maximum quantities are due to the preservation of a certain purity of tone.

При

< 0,51 пропускание при длине волны 560-600 нм более 15% а при

> 1,33 стекло теряет чистоту цвета.At

<0.51 transmission at a wavelength of 560-600 nm more than 15% and at

> 1.33 glass loses color purity.

В качестве сырьевых материалов могут быть использованы: песок, глинозем, сода, селитра калиевая или поташ, доломит, мел, сульфат натрия, криолит, кремнефтористый натрий, фтористый кальций, крокус, сера, окись железа, соединения хрома, меди, марганца, окись кобальта, окись никеля, селен. As raw materials can be used: sand, alumina, soda, potassium nitrate or potash, dolomite, chalk, sodium sulfate, cryolite, sodium silicofluoride, calcium fluoride, crocus, sulfur, iron oxide, chromium, copper, manganese compounds, cobalt oxide nickel oxide selenium.

Конкретные составы предлагаемого стекла приведены в табл. 1. Стекло легко проваривается, хорошо осветляется, не кристаллизуется при выработке. Варка стекла может осуществляться как в ванной печи, так и в горшковой печи. Температура варки стекла 1360-1450^oC. Среда в печи слабовосстановительная или нейтральная.The specific compositions of the proposed glass are given in table. 1. Glass is easy to boil, brightens well, does not crystallize during production. Glass can be cooked both in the bath furnace and in the pot furnace. The temperature of glass melting is 1360-1450 ^o C. The environment in the furnace is poorly reducing or neutral.

Выработка стекла может производиться ручным методом выдувания, механизированным методом вертикального вытягивания и горизонтального проката. Glass can be produced by manual blowing, by mechanized vertical stretching and horizontal rolling.

Данные стекла могут быть использованы преимущественно в качестве светофильтров, при изготовлении декоративных плафонов, для светильников, мозаик, смальт, цветной коврово-мозаичной плитки, а также в строительных целях для остекления и создания декоративного эффекта. These glasses can be used mainly as light filters, in the manufacture of decorative shades, for fixtures, mosaics, smalt, colored carpet and mosaic tiles, as well as for construction purposes for glazing and creating a decorative effect.

В таблице 2 приведены свойства заявляемого стекла и прототипа. Table 2 shows the properties of the inventive glass and prototype.

Claims

Stained glass, including SiO ₂ , Al ₂ O ₃ , Na ₂ O, CaO, MgO, Fe ₂ O ₃ , S ^-2 , K ₂ O, FeS, F ', characterized in that, in order to increase the reduction in the transmission of spectral rays with a wavelength of 560 600 nm less than 15% and obtaining colored glass with a wide color gamut, it additionally contains CaF ₂ and at least one component from the group Co ₂ O ₃ , CuO, Cr ₂ O ₃ , MnO, NiO, Se in the following the ratio of components, wt.

SiO ₂ 65.0 72.72
Al ₂ O ₃ 3.03 8.07
Na ₂ O 12.11 17.00
CaO 1.01 5.04
MgO 0.001 4.06
Fe ₂ O ₃ 0.01 1.01
S ^- ² 0.0001 1.01
K ₂ O 0.0001 2.02
FeS 0.012 1.52
F '1.00 4.04
CaF ₂ 0.05 4.04
and at least one component from the group
Co ₂ O ₃ 0.005 0.20
CuO 0.005 0.50
Cr ₂ O ₃ 0.0001 0.50
MnO 0.005 0.50
NiO 0.005 0.25
Se 0.005 0.10
moreover, the ratio