RU2019427C1

RU2019427C1 - Sheet glass decorating method

Info

Publication number: RU2019427C1
Authority: RU
Inventors: С.В. Белозор; В.В. Савченко
Original assignee: Белозор Сергей Васильевич; Савченко Владимир Викторович
Priority date: 1992-03-16
Filing date: 1992-03-16
Publication date: 1994-09-15

Abstract

FIELD: application of decorative designs. SUBSTANCE: method involves removing fat from glass sheet surface; positioning required design under glass sheet and drawing contouring lines of design on glass sheet surface by fluid viscous paste; exposing glass sheet to drying till paste is hardened. Paste contains emulsion polyvinyl acetate adhesive and bronze powder or graphite powder and alumina in an amount of 1 part by volume of bronze powder or graphite powder and 0.5 part by volume of alumina to 1-3 parts by volume of polyvinyl acetate. Fat is removed from glass sheet surface by mixture containing alumina and distilled water in an amount of 1 part of alumina and 3 parts of water. Emulsion adhesive may be used with plasticizer. Parquet varnish with addition of aqueous or alcoholic dyes may be used dyeing liquid, applied onto glass sheet surface defined by contouring line relief. EFFECT: increased efficiency and high decorative effect.

Description

Изобретение относится к декоративному искусству и может быть использовано для нанесения декоративных рисунков, узоров, орнаментов на листовое стекло, преимущественно используемое для мебели, двери, в виде самостоятельного панно. The invention relates to decorative art and can be used for applying decorative drawings, patterns, ornaments to sheet glass, mainly used for furniture, doors, in the form of an independent panel.

Известен способ декорирования листового стекла [1] путем подачи на горизонтальную рельефную поверхность окрашивающей жидкости и ее отверждение в течение заданного времени. A known method of decorating sheet glass [1] by feeding on a horizontal embossed surface of the coloring liquid and curing it for a predetermined time.

Однако данный способ не позволяет повысить декоративный эффект листового стекла, так как не позволяет получить на листовом стекле четких, заданных разноцветных рисунков, узоров, орнаментов. However, this method does not allow to increase the decorative effect of sheet glass, since it does not allow to obtain clear, predetermined multi-colored patterns, patterns, ornaments on sheet glass.

Наиболее близким по совокупности признаков является способ декорирования стекла [2], включающий обезжиривание поверхности стекла, нанесение на его лицевую поверхность рельефа контурных линий рисунка пастой, содержащей, например, силикатный клей и наполнитель - молотый грифель или алюминиевую пудру, сушку, окрашивание участков рисунка желатиновой краской и сушку. The closest set of features is the method of decorating glass [2], including degreasing the surface of the glass, applying contour lines of the pattern to the front surface of the drawing with a paste containing, for example, silicate glue and filler - ground lead or aluminum powder, drying, staining of the gelatinous pattern areas paint and drying.

Однако данный способ не позволяет получить на листовом стекле рисунки, узоры, обладающие высокими адгезионными свойствами, так как желатиновые краски боятся влаги, неустойчивы, а также не позволяет повысить декоративный эффект, так как рельеф рисунка выполняется в серых и черных тонах, что не позволяет выполнять декорирование в широком диапазоне цветовой гаммы (например, при использовании для мебели). However, this method does not allow to obtain drawings, patterns with high adhesive properties on sheet glass, since gelatin paints are moisture-resistant, unstable, and also cannot increase the decorative effect, since the relief of the pattern is made in gray and black tones, which does not allow decoration in a wide range of colors (for example, when used for furniture).

Изобретение позволяет повысить устойчивость и прочность узоров, рисунков на листовом стекле от внешних воздействий и повысить декоративный эффект листового стекла. The invention improves the stability and strength of patterns, patterns on sheet glass from external influences and increase the decorative effect of sheet glass.

В способе декорирования листового стекла, включающем обезжиривание поверхности стекла, нанесение на его лицевую поверхность рельефа контурных линий рисунка в соответствии с рисунком на бумаге, подложенной под стекло, пастой на основе клея и наполнителя с последующей сушкой, окрашивание участков рисунка, ограниченного рельефом контурных линий, и сушку, при нанесении рельефа контурных линий рисунка в пасту дополнительно вводят глинозем, в качестве клея используют эмульсионный поливинилацетатный клей, а в качестве наполнителя - бронзовую пудру или порошок графита при соотношении последних к глинозему и клею, соответственно равном 1:0,5:1-3 об.ч. Кроме того, обезжиривание поверхности стекла производят смесью глинозема с дистиллированной водой при их соотношении соответственно 1:3 об.ч. путем ее нанесения на поверхность стекла и сушки с последующим ее удалением. Окраску осуществляют паркетным лаком с добавлением спиртового или водного красителя исходя из заданного цвета и оттенка. Кроме того, при нанесении на лицевую поверхность стекла рельефа контурных линий эмульсионный клей поливинилацетата используют с пластификатором. In a method for decorating sheet glass, including degreasing a glass surface, applying contour lines of a pattern to its front surface in accordance with a pattern on paper laid under glass, a paste based on glue and filler, followed by drying, painting sections of the pattern limited by the contour line relief, and drying, when applying the relief of the contour lines of the pattern, alumina is additionally introduced into the paste, emulsion polyvinyl acetate glue is used as glue, and bronze is used as filler powder or graphite powder with a ratio of the latter to the glue and alumina, respectively equal to 1: 0.5: 3.1 vol In addition, the degreasing of the glass surface is carried out with a mixture of alumina with distilled water at a ratio of 1: 3 vol. by applying it to the surface of the glass and drying, followed by its removal. Coloring is carried out with parquet lacquer with the addition of alcohol or water dye based on a given color and shade. In addition, when applying the relief of contour lines to the glass surface, the emulsion adhesive of polyvinyl acetate is used with a plasticizer.

Способ осуществляют следующим образом. The method is as follows.

Поверхность листового стекла, на которую наносят рисунок, обезжиривают. Для этого на эту поверхность наносят смесь, включающую глинозем и дистиллированную воду в количестве 1 об.ч. : 3 об.ч. соответственно, смесь сушат и после высыхания остатки смеси удаляют. Далее на лицевую поверхность стекла наносят рельеф контурных линий рисунка текучей вязкой пастой в соответствии с рисунком, помещенным под стекло. Паста содержит в качестве основы эмульсионный клей поливинилацетатный (ПВА), который может быть использован с одним из пластификаторов (диметилфталат, дибутилфталат и другим пластификатором), который совмещается с ПВА. В качестве наполнителей паста содержит бронзовую пудру или порошок графита и глинозема в количестве 1 об.ч. бронзовой пудры или порошка графита и 0,5 об.ч. глинозема на 1-3 об.ч. ПВА, что позволяет создать текучую вязкую пасту, обеспечивающую адгезивные качества и цвет рельефа рисунка, гармонирующий с цветом мебели, а также варьировать размерами рельефа. Далее стекло подвергают сушке. Затем на поверхность стекла, ограниченную рельефом контурных линий, наносят окрашивающую жидкость способом налива. При этом в качестве окрашивающей жидкости применяют паркетный лак с добавлением водных или спиртовых красителей. Причем в зависимости от места применения декорированного стекла (мебель, дверь, окно, панно) используют различные красители. Далее стекло сушат для отверждения окрашивающей жидкости. Таким образом, данный способ декорирования позволяет наряду с высокими адгезионными качествами создать разнообразную гамму цветов и оттенков, наносимых на листовое стекло рисунков, узоров, и обеспечить, например, при использовании для мебели цветовую композицию декора стекла с цветом мебели, цветостойкость декора при длительной эксплуатации и устойчивость и прочность от внешних воздействий. The surface of the sheet glass on which the drawing is applied is degreased. For this, a mixture is applied to this surface, including alumina and distilled water in an amount of 1 vol.h. : 3 rpm accordingly, the mixture is dried and, after drying, the residual mixture is removed. Next, the relief of the contour lines of the pattern is applied to the front surface of the glass with a fluid viscous paste in accordance with the pattern placed under the glass. The paste contains emulsion adhesive polyvinyl acetate (PVA) as a base, which can be used with one of the plasticizers (dimethyl phthalate, dibutyl phthalate and other plasticizer), which is combined with PVA. As fillers, the paste contains bronze powder or powder of graphite and alumina in an amount of 1 vol.h. bronze powder or graphite powder and 0.5 vol.h. alumina for 1-3 vol.h. PVA, which allows you to create a fluid viscous paste that provides adhesive qualities and the relief color of the picture, in harmony with the color of the furniture, as well as vary the size of the relief. Next, the glass is dried. Then, a coloring liquid is applied to the glass surface, limited by the relief of the contour lines, by pouring. At the same time, parquet varnish with the addition of water or alcohol dyes is used as a coloring liquid. Moreover, depending on the place of application of the decorated glass (furniture, door, window, panel), various dyes are used. Then the glass is dried to cure the coloring liquid. Thus, this decoration method allows, along with high adhesive qualities, to create a diverse range of colors and shades applied to sheet glass of patterns and patterns, and to ensure, for example, when using furniture for furniture, the color composition of the glass decor with the color of the furniture, the color fastness of the decor during prolonged use and stability and durability from external influences.

Claims

1. METHOD FOR DECORATING SHEET GLASS, including degreasing the glass surface, applying the contour lines of the drawing to its front surface in accordance with the drawing on paper, laid under the glass, a paste based on glue and filler, followed by drying, painting sections of the picture limited by the contour lines relief and drying, characterized in that when applying the relief of the contour lines of the pattern, alumina is additionally introduced into the paste, emulsion polyvinyl acetate glue is used as glue, and as filler - bronze or graphite powder with a volume ratio of the latter, alumina and glue, respectively, 1: 0.5: 1 - 3.

2. The method according to claim 1, characterized in that the degreasing of the glass surface is carried out with a mixture of alumina with distilled water at a volume ratio of 1: 3, respectively, by applying it to the glass surface and drying, followed by its removal.

3. The method according to claim 1, characterized in that the coloring is carried out with parquet varnish with the addition of alcohol or water dye based on a given color and shade.

4. The method according to claim 1, characterized in that when applying the relief of contour lines to the glass surface, emulsion polyvinyl acetate adhesive is used with a plasticizer.