RU2013204C1

RU2013204C1 - Method of making terra-blocks

Info

Publication number: RU2013204C1
Authority: RU
Inventors: Афанасий Епифанович Медведев
Original assignee: Афанасий Епифанович Медведев
Priority date: 1990-09-24
Filing date: 1990-09-24
Publication date: 1994-05-30

Abstract

FIELD: building material production. SUBSTANCE: method comprises steps of charging small vegetable particles, having humidity 6-8% , in quantity 1 mass parts to a mixer, vegetable particles being sawdust, husk, straw, grass, maize, sun flower, mixing the vegetable particles over 1-2 minutes with melt glass, having density 1,2 g/cm³, in quantity 4-6 mass parts; introducing to the mixture, had been for produced, at first cement in quantity 1-2 mass parts upon agitating the mixture over 2-3 minutes and then milled mineral filler, having humidity 6-8 % , in quantity 7-9 mass parts; using for this purpose soil with small content of sand, clay or kaolin; charging the mass, had been produced, to a press mold and subjecting it to cold pressing by pressure 12-20 At over 10 s for making terra-block, curing it at normal conditions at 18-22 C for strengthening. EFFECT: enhanced quality of blocks. 1 cl, 1 tbl

Description

Изобретение относится к производству строительных материалов и может быть использовано во всех областях народного хозяйства для строительства зданий. The invention relates to the production of building materials and can be used in all areas of the national economy for the construction of buildings.

Целью изобретения является получение стеновых блоков и утилизация отходов. The aim of the invention is to obtain wall blocks and waste disposal.

Пресс-массу готовят следующим образом. The press mass is prepared as follows.

В смеситель отвешивают мелкие частицы растительности влажностью 6-8% в количестве 1 мас. ч. Ими могут быть опилки и шелуха, а также солома, сорная трава, стебли кукурузы, подсолнуха, измельченные в виде палочек или крошки размером 2-6 мм. Отвешенные частицы растительности в количестве 1 мас. ч. смешивают в течение 1-2 мин с жидким стеклом плотностью 1,2 г/см³, в количестве 4-6 мас. ч. После чего в полученную смесь при перемешивании в течение 2-3 мин вводят цемент в количестве 1-2 мас. ч. , а затем молотый минеральный наполнитель влажностью 6-8% в количестве 7-9 мас. ч. Для этой цели используют грунт с небольшим содержанием песка, глину или каолин.Small particles of vegetation with a moisture content of 6-8% in an amount of 1 wt. h. They can be sawdust and husk, as well as straw, weed grass, stalks of corn, sunflower, chopped in the form of sticks or chips with a size of 2-6 mm. Suspended particles of vegetation in the amount of 1 wt. hours are mixed for 1-2 minutes with liquid glass with a density of 1.2 g / cm ³ in the amount of 4-6 wt. o'clock Then, in the mixture with stirring for 2-3 minutes, cement is introduced in an amount of 1-2 wt. hours, and then ground mineral filler with a moisture content of 6-8% in an amount of 7-9 wt. h. For this purpose, use soil with a small content of sand, clay or kaolin.

Полученную таким образом массу, например в количестве 4 кг и более, загружают в форму и методом холодного виброуплотнения и прессования давлением 12 - 20 атм в течение 5-10 с получают терра-блок. Блок выдерживают в нормальных условиях при 18 - 22^оС для упрочнения.The mass thus obtained, for example, in an amount of 4 kg or more, is loaded into the mold and a terra block is obtained for 5-10 s by the method of cold vibration compaction and pressing with a pressure of 12–20 atm. The unit is kept in normal conditions at 18 - 22 ^{° C} to harden.

В связи с изменением плотности жидкого стекла соотношение количества массы в компонентах устанавливается опытным путем по времени затвердения массы при приготовлении ее и формовании блоков. In connection with the change in the density of liquid glass, the ratio of the amount of mass in the components is established empirically by the time of hardening of the mass when preparing it and forming blocks.

Физико-механические показатели терра-блока приведены в таблице. Physico-mechanical indicators of the terra block are shown in the table.

Эффективность изобретения состоит в более рациональном использовании отходов от деревообрабатывающей и сельскохозяйственной промышленности в производстве строительных материалов. Использование таких терра-блоков для строительства зданий малой этажности значительно ускорит решение жилищной проблемы. The effectiveness of the invention consists in a more rational use of waste from the woodworking and agricultural industries in the production of building materials. The use of such terra blocks for the construction of low-rise buildings will significantly accelerate the solution of the housing problem.

Claims

METHOD FOR PRODUCING TERRA BLOCKS, including the preparation of mass based on mineral filler, the formation of blocks from the mass and their exposure for hardening, characterized in that, in order to obtain wall blocks and utilize waste, when preparing the mass, the crushed plant particles are mixed with liquid glass at their ratio, respectively, wt. part 1: 4 to 6, after which cement is first introduced into the mixture with stirring in an amount of 1 to 2 wt. hours, and then a mineral filler in the amount of 7 to 9 wt. hours