RU2012629C1 - Copper-base alloy - Google Patents
Copper-base alloy Download PDFInfo
- Publication number
- RU2012629C1 RU2012629C1 SU5026943A RU2012629C1 RU 2012629 C1 RU2012629 C1 RU 2012629C1 SU 5026943 A SU5026943 A SU 5026943A RU 2012629 C1 RU2012629 C1 RU 2012629C1
- Authority
- RU
- Russia
- Prior art keywords
- copper
- manganese
- alloy
- nickel
- iron
- Prior art date
Abstract
Description
Изобретение относится к составам сплавов на основе меди, которые могут быть использованы в приборостроении, а также для изготовления монет, проволоки и других изделий. The invention relates to compositions of alloys based on copper, which can be used in instrumentation, as well as for the manufacture of coins, wire and other products.
Известны различные сплавы на основе меди /1/. There are various alloys based on copper / 1 /.
Известен сплав на основе меди, содержащий следующие компоненты, мас. % : марганец 9,5-11,0; цинк 8,5-10,0; железо 2,2-3,5; никель 1,6-2,0; алюминий 7,5-8,5; углерод 0,08-0,2; медь остальное /2/. Known alloy based on copper, containing the following components, wt. %: manganese 9.5-11.0; zinc 8.5-10.0; iron 2.2-3.5; nickel 1.6-2.0; aluminum 7.5-8.5; carbon 0.08-0.2; copper rest / 2 /.
Целью изобретения является повышение твердости сплава. The aim of the invention is to increase the hardness of the alloy.
Цель достигается тем, что в состав сплава на основе меди, содержащего углерод, железо, никель, алюминий, марганец, дополнительно вводят кремний, при следующем соотношении компонентов, мас. % : углерод 0,3-0,4; железо 2,2-3,5; никель 2,9-3,4; марганец 9,5-11,0; алюминий 3,5-4,2; кремний 3,4-4,2; медь остальное. The goal is achieved by the fact that silicon is additionally introduced into the composition of an alloy based on copper containing carbon, iron, nickel, aluminum, manganese, in the following ratio of components, wt. %: carbon 0.3-0.4; iron 2.2-3.5; nickel 2.9-3.4; manganese 9.5-11.0; aluminum 3.5-4.2; silicon 3.4-4.2; copper the rest.
В таблице приведены составы предложенного сплава. The table shows the compositions of the proposed alloy.
Ожидается, что твердость предложенного сплава на основе меди составит, НВ: для 1 и 3 составов 330±10; для 2 состава 340±10. It is expected that the hardness of the proposed alloy based on copper will be, HB: for 1 and 3 compositions 330 ± 10; for 2 composition 340 ± 10.
Кроме повышения твердости сплава, повышается износостойкость. In addition to increasing the hardness of the alloy, increases wear resistance.
Claims (1)
Углерод 0,3 - 0,4
Железо 2,2 - 3,5
Никель 2,9 - 3,4
Марганец 9,5 - 11,0
Алюминий 3,5 - 4,2
Кремний 3,4 - 4,2
Медь ОстальноеCOPPER ALLOY, containing carbon, iron, nickel, manganese, aluminum, characterized in that, in order to increase hardness, it additionally contains silicon in the following ratio of components, wt. %:
Carbon 0.3 - 0.4
Iron 2.2 - 3.5
Nickel 2.9 - 3.4
Manganese 9.5 - 11.0
Aluminum 3.5 - 4.2
Silicon 3.4 - 4.2
Copper Else