RO128098A2 - Process and installation for making light concrete - Google Patents
Process and installation for making light concrete Download PDFInfo
- Publication number
- RO128098A2 RO128098A2 ROA201100429A RO201100429A RO128098A2 RO 128098 A2 RO128098 A2 RO 128098A2 RO A201100429 A ROA201100429 A RO A201100429A RO 201100429 A RO201100429 A RO 201100429A RO 128098 A2 RO128098 A2 RO 128098A2
- Authority
- RO
- Romania
- Prior art keywords
- mixture
- mixer
- pressure
- installation
- concrete
- Prior art date
Abstract
Description
PROCEDEU ȘI INSTALAȚIE DE FABRICSKE A BETONULUI UȘOR.LIGHT CONCRETE FABRICSKE PROCEDURE AND INSTALLATION.
Invenția se refera la un procedeu și o instalație de fabricare a betonului ușor de zidărie si izolații folosit la construcții civile și industriale.The invention relates to a process and an installation for the manufacture of lightweight masonry concrete and insulation used in civil and industrial constructions.
Este cunoscut un procedeu de fabricare a betoanului celular, brevet RO nr. 120632 si nr. 122189, care consta in introducerea unui amestec alcătuit din ciment, lianți minerali si organici, apa, antrenori de aer si aditivi intr-un malaxor in condiții normale de presiune a mediului înconjurător după care malaxorul se etanseaza si se creeaza in interior o presiune de lucru de 1-6 bari, malaxarea amestecului se realizeaxa prin rotirea malaxorulu timp de 5 -10 minute după care amestecul este descărcat in tipar sub acțiunea forței gravitaționale.A process for the manufacture of aerated concrete, RO patent no. 120632 and no. 122189, which consists in introducing a mixture consisting of cement, mineral and organic binders, water, air entrainers and additives in a mixer under normal conditions of environmental pressure after which the mixer is sealed and a working pressure is created inside of 1-6 bar, the mixing of the mixture is done by rotating the mixer for 5 -10 minutes after which the mixture is discharged into the mold under the action of gravitational force.
Acest procedeu prezintă următoarele dezavantaje:This procedure has the following disadvantages:
-prin introducerea apei si antrenorilor de aer in amestec in condiții normale de mediu o mare parte a antrenorilor de aer fîxeaza in amestec bulele de aer la presiune normala de mediu, astfel presiunea creata după aceasta nu mai are efect asupra creșterii bulelor de aer;-by introducing water and air trainers into the mixture under normal environmental conditions, a large part of the air trainers fixes the air bubbles in the mixture at normal ambient pressure, so the pressure created after this no longer has an effect on the growth of air bubbles;
-prin descărcarea amestecului in tipar sub acțiunea forței hidrostatice se creeaza un jet de amestec, care in zona de descărcare creeaza o structura neuniforma producând spargerea bulelor de aer fixate in amestec;-by discharging the mixture into the mold under the action of hydrostatic force, a mixture jet is created, which in the discharge area creates an uneven structure producing the rupture of air bubbles fixed in the mixture;
-nu pot fi introduși, in amestecul malaxat, adezivi si latexuri care îmbunătățesc performantele tehnice ale betonului ușor;-adhesives and latexes that improve the technical performance of lightweight concrete cannot be introduced into the mixed mixture;
Instalațiile și echipamente de fabricare a betonului ușor de zidărie si izolații prezentate în brevetele RO nr. 120632 si nr. 122189 sunt constituite din: echipamente de mal axare si descărcare a amestecului in tipar, după care tiparele cu amestecul expandat sunt supuse operaților cunoscute si utilizate in mod curent; aceste chipamente cuprind un malaxor care este un recipient metalic de forma cilindrica, prevăzut sau nu cu un jgheab pentru descarcara amestecului, are un orificiu folosit pentru incarnarea si descărcarea amestecului de beton, mai are montat in interior niște șicane pentru omogenizarea amestecului, malaxorulInstallations and equipment for the manufacture of lightweight masonry concrete and insulation presented in RO patents no. 120632 and no. 122189 are made up of: equipment for shoring and unloading the mixture in the mold, after which the molds with the expanded mixture are subjected to known and currently used operations; these fittings comprise a mixer which is a cylindrical metal container, provided or not with a trough for unloading the mixture, has a hole used for incarnation and unloading of the concrete mixture, it has mounted inside some baffles to homogenize the mixture, the mixer
..·/ C·· °° BEIONPROTUBPM * SAL *.. · / C ·· °° BEIONPROTUBPM * SAL *
Ο 5 -05- 2011 realizează malaxarea amestecului de beton in condiții de presiune mai mare decât presiunea normala de mediu.Ο 5 -05- 2011 mixes the concrete mixture in conditions of higher pressure than normal ambient pressure.
Acest malaxor prezintă următoarele dezavantaje:This mixer has the following disadvantages:
-jgheabul este proeminent în exterior si prin incarnarea sa cu amestec creeaza un dezechilibru in mișcarea de rotatie, provocând șocuri si vibrații;-the gutter is prominent on the outside and by its incarnation with the mixture it creates an imbalance in the rotational movement, causing shocks and vibrations;
-șicanele montate in lungul interiorului malaxorului, nu realizează o buna omogenizare a amestecului de beton, avand efecte negative prin spargerea bulelor de aer fixate in amestec;- the baffles mounted along the inside of the mixer, do not achieve a good homogenization of the concrete mixture, having negative effects by breaking the air bubbles fixed in the mixture;
Echipamentul pentru descărcare a amestecului in tipar consta dintr-o piesa de legătură sau un racord flexibil, acestea realizează descărcarea amestecului sub acțiunea forței hidrostatice, aceste echipamente de descărcare produc in zona de impact cu tiparul, un jet de amestec care distruge o mare parte a bulelor de aer fixate in amestec, realizând si o structura celulara neuniforma.The equipment for unloading the mixture in the mold consists of a connecting piece or a flexible connection, they discharge the mixture under the action of hydrostatic force, these unloading equipment produce in the area of impact with the mold, a jet of mixture that destroys much of the air bubbles fixed in the mixture, creating a non-uniform cellular structure.
Prezenta invenție rezolvă problema tehnică a obținerii unui beton ușor de zidărie si izolații cu structura celulara omogenă, cu conductivitate termica mica, calități mecanice îmbunătățite și lipsita de fisuri si capilarii si cu absorbție mica de apa.The present invention solves the technical problem of obtaining a light masonry concrete and insulation with homogeneous cellular structure, with low thermal conductivity, improved mechanical qualities and free of cracks and capillaries and with low water absorption.
Procedeul de fabricare a betonului ușor, conform Invenției, rezolva problema tehnică și înlătură dezavantajele soluțiilot cunoscute din stadiul tehnicii prin aceea că un amestec uscat alcătuit din nisip, ciment si alte adaosuri solide este introdus in condiții normale de presiune atmosferica, de mediu, intrun malaxor care este apoi etanșat si se creeaza in interior o presiune de aer de amestec, mai mare decât presiunea atmosferică de mediu, se omogenizează componentele solide prin rotirea malaxorului și se introduc printr-un distribuitor niște componente fluide de amestec, de ex. apa, antrenori de aer si aditivi, la o presiune mai mare decât presiunea de aer de amestec, se omogenizează componentele uscate cu cele fluide o durata de amestec, de ex. 15 -25 minute, după care se depresurizează malaxorul la presiunea atmosferică de mediu, începând o expandare a amestecului și se continua scăderea presiunii în malaxor .·/ VSILThe process of manufacturing lightweight concrete, according to the Invention, solves the technical problem and removes the disadvantages of the known solutions of the prior art in that a dry mixture consisting of sand, cement and other solid additives is introduced under normal conditions of atmospheric pressure, environment, in a mixer. which is then sealed and a mixing air pressure is created inside, higher than the ambient atmospheric pressure, the solid components are homogenized by rotating the mixer and some fluid mixing components are introduced through a distributor, e.g. water, air entrainers and additives, at a pressure higher than the mixing air pressure, homogenize the dry components with the fluid ones for a mixing duration, e.g. 15 -25 minutes, after which the mixer is depressurized at ambient atmospheric pressure, starting with an expansion of the mixture and the pressure drop in the mixer is continued. · / VSIL
CA-2 0 1 1 - 0 0 4 2 9 -O 5 -05- 2011 până la o ușoară presiune vacuumatică, de ex. de la -0,05 la -0,5 Bar, la care se face o malaxare lentă o durată, de ex. de 1 - 2 minute, pentru expandarea omogenă a amestecului și exteragerea din amestec a bulelor de aer defecte, mari, apoi amestecul este descărcat cu o curgere uniformă, controlată cu ajutorul presiunii vacuumatice, concomitent cu injectarea in amestec a unor adezivi, si latexuri, intr-un tipar, supus unei ușoare vibrări, pe o durată, de exemplu 30-60 sec, pentru a favoriza o dispersare uniformă în amestec a produselor injectate, tipar în care se finalizează procesul de priză, maturare a betonului se realizează in condiții normale de mediu sau in condiții controlate.CA-2 0 1 1 - 0 0 4 2 9 -O 5 -05- 2011 to a slight vacuum pressure, e.g. from -0.05 to -0.5 Bar, at which a slow kneading is done for a duration, e.g. 1-2 minutes, for homogeneous expansion of the mixture and extraction of large, defective air bubbles from the mixture, then the mixture is discharged with a uniform flow, controlled by vacuum pressure, simultaneously with the injection into the mixture of some adhesives and latexes, in a mold, subjected to a slight vibration, for a duration, for example 30-60 sec, to favor a uniform dispersion in the mixture of the injected products, a pattern in which the setting process is completed, the maturation of the concrete is done under normal conditions environmental or under controlled conditions.
Instalația pentru aplicarea procedeului de fabricare a betonului ușor conform invenției, este alcătuită dintr-un malaxor construit din doua tronsoane tronconice unite în zona centrală printr-un inel cilindric și din două capete conice, în care sunt fixate două semiaxe și prevăzute cu niște lagăre de sprijin pe un suport nefigurat, într-una din semiaxe fiind montat un distribuitor pentru încărcarea unor componente fluidice, partea lichida a amestecului și aerul sub presiune, malaxorul având un capac de vizitare, un orificiu pentru încărcarea componentelor solide și descărcarea amestecului, practicat intr-un ștuț filetat și prevăzut cu un dop filetat și un dispozitiv de depresurizare și vacuumare, malaxorul mai fiind prevăzut cu o coroana dintata și un mecanism de acționare și dintr-un dispozitiv de descărcare care se cuplează cu malaxorul printr-o mufa de prindere care are o secțiune de intrare sub forma de cerc și o secțiune de ieșire oval-alungită și care are montat în spate un perete despărțitor, dispozitivul de descărcare fiind echipat cu o instalație de injecție a unor adezivi, si latexuri în amestecul brut descărcat intr-un tipar, numita instalație de injecție fiind alcatuita dintr-o conducta de alimentare si mai multe conducte de distribuție, care sunt alimentate controlat dintr-un rezervor nefigurat.The installation for applying the process of manufacturing lightweight concrete according to the invention, consists of a mixer built of two frustoconical sections joined in the central area by a cylindrical ring and two conical ends, in which two semi-axles are fixed and provided with bearings. support on a non-figured support, in one of the half-axes being mounted a distributor for loading fluid components, the liquid part of the mixture and the pressurized air, the mixer having a manhole cover, a hole for loading solid components and discharging the mixture, practiced in a threaded nozzle and provided with a threaded plug and a depressurizing and vacuuming device, the mixer also being provided with a toothed crown and an actuating mechanism and from a discharge device which is coupled to the mixer by a clamping plug which has an entrance section in the form of a circle and an oval-elongated exit section with a wall mounted at the back partition, the unloading device being equipped with an injection plant of some adhesives, and latexes in the raw mixture unloaded in a mold, said injection plant being composed of a supply pipe and several distribution pipes, which are fed controlled from an unfigured tank.
Invenția prezintă avantajele obținerii unui betonThe invention has the advantages of obtaining a concrete
- cu structură omogenă;- with homogeneous structure;
- fără fisuri și capilare;- without cracks and capillaries;
ίλ’ 2 Ο 1 1 - 0 0 4 2 9 4ίλ ’2 Ο 1 1 - 0 0 4 2 9 4
Ο 5 -05- 2011 tlΟ 5 -05- 2011 tl
- cu conductivitate termica mica;- with low thermal conductivity;
- are absorbție mica de apa- has low water absorption
Se da in continuare un exemplu de realizare a invenției in legătură cu fig.l..4, care reprezintă:An embodiment of the invention is given below in connection with Fig. 1.4, which represents:
- fig. 1- vedere laterală de ansamblu a malaxorului;- fig. 1- general side view of the mixer;
- fig. 2 - vedere din fata a dispozitivului de descărcare,;- fig. 2 - front view of the unloading device;
- fig. 3 - vedere laterala a a dispozitivului de descărcare;- fig. 3 - side view of the unloading device;
- fig. 4 - secțiune transversală prin instalație expandarea amestecului in malaxor si turnarea in tipar;- fig. 4 - cross section by installation expanding the mixture in the mixer and pouring in the mold;
Procedeul de fabricare a betonului ușor, conform invenției, constă în următoarele etape și operații:The process for manufacturing lightweight concrete according to the invention consists of the following steps and operations:
- se introduce intr-un malaxor 1 amestecul alcătuit din nisip, ciment si alte adaosuri solide in condiții normale de presiune atmosferica PO, de mediu,- the mixture of sand, cement and other solid additives is introduced into a mixer 1 under normal conditions of atmospheric pressure PO, environment,
- se etanseaza malaxorul 1 și se creeaza în interior o presiune de aer PI de amestec, mai mare decât presiunea PO atmosferică de mediu,- seal mixer 1 and create a mixture PI air pressure inside, higher than the ambient atmospheric PO pressure,
- se începe malaxarea pentru omogenizarea componentelor solide și- start mixing to homogenize the solid components and
- se introduc printr-un distribuitor 2, componentele fluide de amestec: apa, antrenorii de aer si aditivii, la o presiune P2, mai mare decât presiunea de aer PI de amestec din malaxorul 1;- the fluid mixing components are introduced through a distributor 2: water, air trainers and additives, at a pressure P2, higher than the mixing air pressure PI in the mixer 1;
- după introducerea pârtii lichide a amestecului, se continua mișcarea de rotatie a malaxorului o durata TI, de amestec, de ex. 15 -25 minute,- after the introduction of the liquid part of the mixture, the rotational movement of the mixer is continued for a duration TI, of the mixture, e.g. 15 -25 minutes,
- după care malaxorul 1 este depresurizat la presiunea PO atmosferică, de mediu, în timpul depresurizării începând expandarea amestecului și- after which the mixer 1 is depressurized at ambient atmospheric PO pressure during depressurization starting from the expansion of the mixture, and
- se continua, prin intermediul unui dispozitiv 3 de depresurizare și vacuumare scăderea presiunii în malaxorul 1 până la o ușoară presiune P3 vacuumatică, de ex. de la -0,05 la -0,5 Bar,- the pressure drop in the mixer 1 is continued by means of a depressurizing and vacuuming device 3 to a slight vacuum pressure P3, e.g. from -0.05 to -0.5 Bar,
- se face o malaxare lentă la această presiune scăzută o durată T2 , de ex. de 1 2 minute, pentru omogenizarea amestecului și exteragerea din amestec a bulelor de aer defecte, mari, .· 9Λ- a slow kneading is performed at this low pressure for a duration T2, e.g. 1 2 minutes to homogenize the mixture and remove large, defective air bubbles from the mixture.
Y imm Ă * ♦ ui (\-2 0 1 1 - 0 0 4 2 9 - Ο 5 -05- 2011Y imm Ă * ♦ ui (\ -2 0 1 1 - 0 0 4 2 9 - Ο 5 -05- 2011
- după care amestecul este descărcat cu o curgere uniformă, controlată cu ajutorul presiunii P3 vacuumatice, intr-un tipar 4, în care se finalizează procesul de priză, maturare a betonului se face in condiții normale de mediu sau in condiții controlate. Prin descărcarea controlată cu ajutorul presiunii vacuumatice P3 este înlăturată apariția jetului la descărcare si eliminarea efectelor negative ale acestuia.- after which the mixture is discharged with a uniform flow, controlled by means of the vacuum pressure P3, in a pattern 4, in which the setting process is completed, the maturation of the concrete is done under normal environmental conditions or under controlled conditions. By the controlled discharge with the help of the vacuum pressure P3 the appearance of the jet at the discharge is eliminated and the elimination of its negative effects.
Descărcarea amestecului în tiparele 4 se face prin deplasarea tiparului pe sub piesa de descărcare.Unloading the mixture into patterns 4 is done by moving the pattern under the discharge piece.
- în timpul descărcării în tiparele 4 în fuxul de amestec se injectează, adezivi si latexuri, pentru a căror dispersare uniformă în amestec, tiparul 4 este supus unei ușoare vibrări, cu mijloace în sine cunoscute, pe o durată T3, de exemplu 30-60 sec,- during unloading in patterns 4, adhesives and latexes are injected into the mixing stream, for which uniform dispersion in the mixture, pattern 4 is subjected to a slight vibration, by means known per se, for a duration T3, for example 30-60 sec,
Vibarea finală pe durata T3, are un efect pozitiv atât asupra răspândirii adezivilor si latexurilor in amestec cât și asupra structurii celulare prin evacuarea bulelor de aer deteriorate prin spargere si unirea mai multora si asupra rezistentei mecanice a produsuluui final.The final vibration during T3, has a positive effect both on the spread of adhesives and latexes in the mixture and on the cellular structure by evacuating damaged air bubbles by breaking and joining several and on the mechanical strength of the final product.
Se dă în continuare un exemplu nelimitativ de realizare a instalației de fabricare a betonului ușor de zidărie și izolații conform procedeului conform invenției.The following is a non-limiting example of the installation of a lightweight concrete masonry and insulation installation according to the process according to the invention.
Malaxorul 1, se sprijină pe un suport nefigurat prin intermediul unei semiaxe 5, în care este montat distribuitorul 2 de încărcare a componentelor fluidice, și al unei semiaxe 6, ambele semiaxe fiind prevăzute cu niște lagăre 7. Malaxorul 1 este construit din doua tronsoane tronconice 8, unite în zona centrală printr-un inel cilindric 9 și din doua capete conice 10, în care sunt fixate semiaxele 5 și 6. Malaxorul 1 are un capac de vizitare 11, și un orificiu 12 pentru încărcarea componentelor solide și descărcarea amestecului, practicat intr-un ștuț filetat 13, prevăzut cu un dop filetat 14. Prin distribuitorul 2 se introduce aerul sub presiune si componentele lichide ale amestecului. Malaxorul ° ram» >The mixer 1 is supported on a support not shown by means of a half-axis 5, in which the distributor 2 for loading the fluid components is mounted, and a half-axis 6, both half-axes being provided with bearings 7. The mixer 1 is constructed of two frustoconical sections 8, joined in the central area by a cylindrical ring 9 and two conical ends 10, in which the half-axes 5 and 6 are fixed. The mixer 1 has a manhole cover 11, and a hole 12 for loading the solid components and unloading the mixture, practiced in a threaded nozzle 13, provided with a threaded plug 14. Through the distributor 2 the pressurized air and the liquid components of the mixture are introduced. The mixer ° ram »>
* S.RL * ^-2011-00429-0 5 -05- 2011* S.RL * ^ -2011-00429-0 5 -05- 2011
1, este prevăzut cu o coroana dintata 15 pentru antrenarea de un mecanism de acționare 16.1, is provided with a toothed ring 15 for driving a drive mechanism 16.
Un dispozitiv de descărcare 17, se cuplează cu malaxorul 1, printr-o mufa de prindere 18. Dispozitivul de descărcare 17, are o secțiune de intrare sub forma de cerc si o secțiune de ieșire oval-alungită, și are montat în spate un perete despărțitor 19 care separă partea plină a tiparului 4 cu amestec de partea goala a tiparului pana la umplerea completa a tiparului, care se deplasează pe sub piesa de descărcare,A discharge device 17, is coupled to the mixer 1, through a clamping plug 18. The discharge device 17, has a circular inlet section and an oval-elongated outlet section, and has a wall mounted at the rear. partition 19 separating the full part of the mold 4 with the mixture from the empty part of the mold until the mold is completely filled, moving under the unloading part,
Dispozitivul de descărcare 17 este echipat cu o instalație de injecție alcătuită dintr-o conducta de alimentare 20, si mai multe conducte de distribuție 21, prin care in amestec in timpul descărcării sunt introduși adezivi si latexuri care nu poate fi introdus in tipul malaxarii, (acesta nefiind compatibil cu antrenorul de aer) dar a căror prezenta in amestec conduc la obținerea de betoane ușoare de înalta performantaThe unloading device 17 is equipped with an injection installation consisting of a supply pipe 20, and several distribution pipes 21, through which adhesives and latexes are introduced into the mixture during unloading, which cannot be introduced in the type of kneading, ( it is not compatible with the air trainer) but whose presence in the mixture leads to the production of lightweight high-performance concrete
Acest dispozitiv de descărcare 17 prezintă avantajul ca elimina jetul de amestec la descărcarea in tipar si asigura descărcarea amestecului expandat din malaxor in tipar, fara spargerea bulelor de aer, iar prin injectare in amestec, in timpul descărcării a unor adezivi si latexuri se obțin betoane de înalta performanta.This discharge device 17 has the advantage that it eliminates the mixing jet when unloading in the mold and ensures the unloading of the expanded mixture from the mixer into the mold, without breaking the air bubbles, and by injecting into the mixture, during the unloading of some adhesives and latexes. high performance.
Componentele solide ale amestecului simt introduse in malaxorul 1, in condiții de presiune normale de mediu. Apoi malaxorul se etanseaza, se creeaza in interior presiunea de lucru, se pune in mișcare de rotatie malaxorul si prin distribuitorul 2, se introduce partea lichida a amestecului, după care amestecul este malaxat timp de 15-25 minute.The solid components of the mixture feel introduced into the mixer 1, under normal ambient pressure conditions. Then the mixer is sealed, the working pressure is created inside, the mixer is rotated and through the distributor 2, the liquid part of the mixture is introduced, after which the mixture is kneaded for 15-25 minutes.
După trecerea timpului de malaxare amestecul este expandat in malaxor prin scăderea presiunii din interiorului malaxorului la presiunea PO de mediu. După expandarea amestecului malaxorul se etanseaza din nou si se creaza in interior o ușoara presiune vacumatica P3 după care malaxorul este rotit 1-2 minute cu viteza de rotatie mica pentru a extrage din amestec bulele mari de aer.After the mixing time has elapsed, the mixture is expanded in the mixer by lowering the pressure inside the mixer to the ambient PO pressure. After expanding the mixture, the mixer is sealed again and a slight vacuum pressure P3 is created inside, after which the mixer is rotated for 1-2 minutes at low rotation speed to extract large air bubbles from the mixture.
'S * SIL * «-2 Ο 1 1-00429-7 Ο 5 -05- zoii'S * SIL * «-2 Ο 1 1-00429- 7 Ο 5 -05- zoii
După extragerea din amestec a bulelor mari de aer se oprește malaxorul din mișcarea de rotatie se aduce interiorul malaxorului la presiunea de mediu PO, se cuplează dispozitivul de descărcare, se creaza din nou in malaxor o ușoara presiune vacumatica P3 si amestecul expandat 22 este trecut in tiparul 4, care se deplasează pe un sistem de role 23, prin dispozitivul de descărcare 17 sub controlul presiunii vacuumatice P3 create in malaxorul 1. în timpul descărcării amestecului expandat prin conducta de alimentare 20 și conductele de distribuție 21, se injectează, continuu sau intermitent, in amestecul expandat 22, adezivi si latexuri 24, care nu pot fi introduși in timpul malaxarii datorită incompatibilității acestora cu unele componente inițiale, de ex. cu antrenorul de aer dar a căror prezență în amestec conduc la obținerea de betoane ușoare de înalta performantaAfter extracting the large air bubbles from the mixture, stop the mixer from the rotational movement, bring the inside of the mixer to the ambient pressure PO, connect the discharge device, create again in the mixer a slight vacuum pressure P3 and the expanded mixture 22 is passed into the pattern 4, which moves on a roller system 23, through the discharge device 17 under the control of the vacuum pressure P3 created in the mixer 1. during the discharge of the expanded mixture through the supply line 20 and the distribution pipes 21, is injected, continuously or intermittently , in the expanded mixture 22, adhesives and latexes 24, which cannot be introduced during mixing due to their incompatibility with some initial components, e.g. with the air trainer but whose presence in the mixture leads to obtaining lightweight high-performance concrete
Adezivii si latexurile 24 polimerizează în masa betonului avand ca efect obținerea unor betoane ușoare de înalta performanta.Adhesives and latexes 24 polymerize in the concrete mass, having the effect of obtaining high-performance lightweight concretes.
In timpul procesului se fac manevre și operații cu instalația de fabricare a betonului după cum urmează.During the process, maneuvers and operations are performed with the concrete manufacturing plant as follows.
Se aduce malaxorul 1, cu orificiul 12 pentru incarcarea amestecului, in poziție superioara. Se introduce partea solida a amestecului, se etanseaza orificiul 12, prin infiletarea dopului 14, pe stutul filetat 13. Se introduce aer sub presiune PI de la o sursa nefigurata, conform retetei de fabricație de 1,5 - 7,0 bari prin distribuitorul 2.Bring mixer 1, with hole 12 for loading the mixture, to the upper position. Insert the solid part of the mixture, seal the hole 12, by threading the plug 14, on the threaded nozzle 13. Introduce air under pressure PI from a non-figured source, according to the manufacturing recipe of 1.5 - 7.0 bar through the distributor 2 .
Malaxorul 1, este supus unei mișcări de rotatie prin coroana dintata 15 si mecanismul de acționare 16, pentru malaxare o durata Tl, de amestec de 15 25 minute, iar prin distribuitorul 2 se introduce partea lichida a amestecului.The mixer 1 is subjected to a rotational movement through the toothed ring 15 and the actuating mechanism 16, for mixing a mixing duration Tl of 15 25 minutes, and through the distributor 2 the liquid part of the mixture is introduced.
După terminarea malaxarii, malaxorul 1, este oprit din mișcarea de rotatie cu dispozitivul 3 de depresurizare și vacuumare in partea superioara, și se pune in contact interiorul malaxorului 1, cu presiunea PO de mediu și se realizează expandarea amestecului 22 in malaxorul 1.After finishing the mixing, the mixer 1 is stopped from the rotational movement with the depressurizing and vacuuming device 3 in the upper part, and the inside of the mixer 1 is brought into contact with the ambient PO pressure and the mixture 22 is expanded in the mixer 1.
\ ML ^-2011-00429’0 5 -05- 2011\ ML ^ -2011-00429’0 5 -05- 2011
După expandarea amestecului malaxorul se etanseaza din nou si se creaza in interior o ușoara presiune P3 vacumatica, Se pune malaxorul 1 in mișcare de rotatie cu viteza mica o durată T2 , de ex. de 1 - 2 minute, pentru omogenizarea și pentru extragerea din amestec a bulelor de aer defecte, mari, apoi se oprește si se pune din nou in contact interiorul malaxorului cu presiunea PO de mediu.After expanding the mixture, the mixer is sealed again and a slight vacuum pressure P3 is created inside. The mixer 1 is set in rotational motion at low speed for a duration T2, e.g. for 1 - 2 minutes, to homogenize and extract the defective, large air bubbles from the mixture, then stop and put the interior of the mixer back in contact with the ambient PO pressure.
Se cuplează dispozitivul de descărcare 17, pe orificiul 12, si se aduce malaxorul 1, cu piesa de descărcare 17, in partea inferioara pentru descărcarea amestecului 22, in tiparul 4. Prin dispozitivul 3 de depresurizare și vacuumare se realizează in interiorul malaxorului o presiune P3 vacuumatică, negativă, de la o sursa nefigurata, care asigura descărcarea amestecului fara jet si fara spargerea bulelor de aer. Concomitent cu descărcarea amestecului brut 22 in tiparul 4, care se deplasează pe un sistem de role 23, se injectează in masa amestecului brut expandat 22, prin conducta de alimentare 20, si conductele de distribuție 21, niște adezivi si latexuri 24. Tiparul 4, încărcat cu amestecul expandat este transportat la locul de maturare unde este lasat timp de 5 -10 ore, in condiții normale de mediu sau in condiții controlate după care se debitează, paletizeaza si livrează.Connect the discharge device 17, on the orifice 12, and bring the mixer 1, with the discharge piece 17, in the lower part for the discharge of the mixture 22, in the pattern 4. Through the depressurization and vacuuming device 3 a pressure P3 is realized inside the mixer vacuum, negative, from an unspecified source, which ensures the discharge of the mixture without jet and without breaking the air bubbles. Simultaneously with the unloading of the crude mixture 22 in the pattern 4, which moves on a roller system 23, some adhesives and latexes 24 are injected into the mass of the expanded crude mixture 22, through the supply pipe 20, and the distribution pipes 21. loaded with the expanded mixture is transported to the ripening place where it is left for 5 -10 hours, under normal environmental conditions or under controlled conditions after which it is cut, palletized and delivered.
într-o variantă nelimitativa, betonul ușor de zidărie si izolații este alcătuit dintr- un amestec de nisip si lianți minerali in raport de 2 la 1, sau de 1 la 1, fibre celulozice 1,5 - 3,0 kg/mc, fibre carbonice 0,6 - 1,0 kg/mc, apa obișnuita sau magnetizata in procent de 50 - 60 litri la 100 kg. ciment, aditivi si adezivi specifici betoanelor in procent de 0,2 -1,0 litri/mc.In a non-limiting embodiment, the lightweight masonry concrete and insulation is composed of a mixture of sand and mineral binders in a ratio of 2 to 1, or 1 to 1, cellulose fibers 1.5 - 3.0 kg / m3, fibers carbon dioxide 0.6 - 1.0 kg / m3, ordinary or magnetized water in a percentage of 50 - 60 liters per 100 kg. cement, additives and adhesives specific to concrete in a percentage of 0.2 -1.0 liters / m3.
Claims (2)