RO120488B1

RO120488B1 - Process for tanning fur-ameliorated sheep skins

Info

Publication number: RO120488B1
Application number: RO97-00492A
Authority: RO
Inventors: Ioan Diaconu
Original assignee: Ioan Diaconu
Priority date: 1997-03-13
Filing date: 1997-03-13
Publication date: 2006-02-28

Abstract

The invention relates to a process for tanning sheep skins for fur-ameliorated semi-products, consisting in soaking the preserved skins in two stages, the cleaning stage and the mechanical washing stage, shearing and fleshing them, rinsing them out, centrifuging and pickling them in a float containing salt, synthetic and/or natural oils and organic acids, and tanning them in a float containing basic chromium salts in the presence of synthetic oils, while modifying the pH value up to 3.5...3.6, and finally to 3.9...4.1 with NaHCO3, further on the tanned skins being washed, centrifuged and then dried and subjected to further processing under conditions known per se. The so treated skins exhibit a white clean thick unfelted fur with extensible dermic layer, having compact and smooth feel along the entire surface.

Description

Invenția se referă la un procedeu de tăbăcire a pieilor de ovine, pentru semifabricate înnobilate, pe blană, destinate realizării pieilor Nutriet-Panofix pentru îmbrăcăminte, gulere și căciuli.The invention relates to a process for tanning sheepskin, for upholstered semi-finished goods, on fur, intended for making the Nutriet-Panofix leathers for clothing, collars and caps.

Sunt cunoscute procedee de prelucrare a pieilor de ovine, înnobilate pe blană, procedeele fiind anevoioase și costisitoare, iar valorificarea materiei prime neomogene ca structură și conservare, fiind sub așteptări, multe piei fiind destinate pentru sortimente de piei finite, inferioare.There are known processes for processing sheepskin, ennobled on the fur, the processes being cumbersome and expensive, and the use of non-homogeneous raw materials as structure and conservation, being under expectations, many leathers are destined for assortments of finished, inferior leathers.

Neajunsurile acestor procedee constau în aceea că necesită un consum mare de materiale auxiliare, iar pieile tăbăcite prezintă învelișul pilos cu porțiuni chelite, respectiv, un stadiu avansat de împâslire, ceea ce îngreunează executarea operațiilor de călcat și tuns și, prin urmare, are influență negativă asupra randamentului de utilizare a acestor piei în confecție.The shortcomings of these processes consist in the fact that they require a high consumption of auxiliary materials, and the tanned leathers have a hairy covering with chelated portions, respectively, an advanced stage of plastering, which makes it difficult to perform ironing and trimming operations and therefore has a negative influence. on the efficiency of using these leathers in the preparation.

în descrierile RO 96394, R0100833 și R0110066, sunt prezentate procedee de înnobilare a pieilor ovine cu blană, iar în RO 90893, este prezentat un procedeu de tăbăcire a pieilor bovine, porcine, ovine și caprine.In the descriptions RO 96394, R0100833 and R0110066, there are presented methods of ennobling the sheepskin with fur, and in RO 90893, a process of tanning the cattle, pigs, sheep and goats is presented.

Problema pe care o rezolvă invenția constă în stabilirea succesiunii fazelor, a componentelor flotelor de tratare, astfel încât prin parametrii de înmuiere să fie favorizată o viteză de difuzie mare a agentului de tanare și, prin urmare, să se asigure condiții optime pentru o tanare rapidă și completă, lejeră și permanentă, chiar și în cazul suporturilor demice neuniforme.The problem to be solved by the invention is to determine the sequence of the phases, the components of the treatment fleets, so that the softening parameters are favored by a high diffusion rate of the tanning agent and, therefore, to ensure optimal conditions for a fast tanning. and complete, light and permanent, even in the case of non-uniform demic media.

Procedeul de tăbăcire, conform invenției, înlătură dezavantajele menționate, prin aceea că pieile sunt pregătite, prin înmuiere, în două etape cu ștrecuire intermediară, spălare în două etape, curățare și spălare mecanică, tundere și șeruire, clătire, centrifugare și piclare, în flotă și tăbăcite cu săruri bazice de crom, având 33% bazicitate, în prezență de uleiuri sintetice, cu corectarea pH-ului la 3,5...3,6 și apoi la 3,9...4,1 cu NaHCO₃, pieile tăbăcite fiind, în final, spălate, centrifugate, uscate și prelucrate în condiții în sine cunoscute.The tanning process, according to the invention, removes the disadvantages mentioned, in that the skins are prepared, by softening, in two stages with intermediate cutting, two-stage washing, mechanical cleaning and washing, trimming and waxing, rinsing, centrifuging and pinching and tanned with basic chromium salts, having 33% basicity, in the presence of synthetic oils, with the pH correction at 3.5 ... 3.6 and then at 3.9 ... 4.1 with NaHCO ₃ , the tanned leathers are finally washed, centrifuged, dried and processed under known conditions.

înmuierea se realizează cu 0,5...1 g/l amestec de acizi dicarboxilici alifatici sau cu 0,5...1 g/l acid formic, 0,5...1 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică sau cu 0,5...1 g/l emulgator neionogen pe bază de substanțe grase etoxilate sau cu 0,5...1 g/l alchilsulfați și esteri de alchilsulfați.The softening is carried out with 0.5 ... 1 g / l mixture of aliphatic dicarboxylic acids or with 0.5 ... 1 g / l formic acid, 0.5 ... 1 g / l anionic surfactants and nonionics with synergistic action or with 0.5 ... 1 g / l nonionogenic emulsifier based on ethoxylated fatty substances or with 0.5 ... 1 g / l alkylsulphates and alkylsulphate esters.

Spălarea se realizează cu 0,5...1 g/l Na₂CO₃ și 2...3 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică sau cu 2...3 g/l emulgator neionogen, pe bază de substanțe grase etoxilate, sau cu 2...3 g/l alchilsulfați și esteri de alchilsulfați sau cu 2...3 g/l alcooli grași sulfatați.Washing is performed with 0.5 ... 1 g / l Na ₂ CO ₃ and 2 ... 3 g / l surface anionic and nonionic surfactants with synergistic action or with 2 ... 3 g / l nonionogenic emulsifier, based on ethoxylated fatty substances, or with 2 ... 3 g / l alkylsulphates and alkylsulphate esters or with 2 ... 3 g / l sulphated fatty alcohols.

Pictarea se realizează cu 40...50 g/l sare, 4...8 g/l ulei de ungere sintetic anionic sau cuThe painting is done with 40 ... 50 g / l salt, 4 ... 8 g / l synthetic anionic oil or with

4.. .8 g/l esteri de acizi grași, oxidați și sulfitați și 2...3 g/l amestec de acizi dicarboxilici alifatici și 4...8 g/l formic.4 .. .8 g / l esters of fatty acids, oxidized and sulphite and 2 ... 3 g / l mixture of aliphatic dicarboxylic acids and 4 ... 8 g / l formic.

Tăbăcirea se realizează cu o flotă care conține 40...50 g/l sare, 1,5...2,5 g/l Cr₂O₃, sub formă de săruri bazice de crom de 33% bazicitate și 1....4 g/l ulei sintetic anionic sau 1...4 g/l combinație de materiale sintetice cu catena lungă și înalt sulfatate, conținând și stabilizatori sauTanning is carried out with a fleet containing 40 ... 50 g / l salt, 1.5 ... 2.5 g / l Cr ₂ O ₃ , in the form of basic chromium salts of 33% basicity and 1. ..4 g / l synthetic anionic oil or 1 ... 4 g / l combination of synthetic materials with long and highly sulfated chains, also containing stabilizers or

1.. .4 g/l esteri de acizi grași oxidați și sulfitați.1 .. .4 g / l esters of oxidized and sulphite fatty acids.

Invenția prezintă următoarele avantaje:The invention has the following advantages:

- reduceea consumurilor de materiale auxiliare, precum și reducerea cantității de agenți de tăbăcire;- reducing the consumption of auxiliary materials, as well as reducing the quantity of tanning agents;

- valorificarea superioară chiar și a pieilor cu defecte;- the higher recovery even of faulty leathers;

- uniformitatea tratamentului, pe întreaga suprafață a pielii precum și în secțiune;- uniformity of treatment, throughout the skin surface and in the section;

- îmbunătățirea randamentului de croire, prin reducerea la minimum, a prezenței cheliilor pe suprafața învelișului pilos și prin reduceea numărului de piei rupte sau găurite, ca urmare a eliminării ciulinilor, înainte de prelucrarea pe carne, la mașina de descămat-șeruit.- improving the cutting efficiency, by minimizing the presence of baldness on the surface of the hair cover and reducing the number of broken or drilled skins, as a result of the elimination of chickens, before processing on the meat, in the shredder machine.

RO 120488 Β1 în cele ce urmează, se dau 4 exemple de realizare a propunerii de invenție. 1In the following, there are 4 examples of realizing the invention proposal. 1

Exemplul 1. Procedeul conform unui prim exemplu de realizare constă în introducerea pieilor de cârlan, cu suprafață de 35...45 dm², conservate în hașpel, într-o flotă la temperatura 3 de 25’C, reprezentând 151 apă/1 piele conservată, care conține 0,5 g/l alchilolamine cu conținut de substanțe antiseptice, 0,5 g/l amestec acizi dicarboxilici alifatici și 0,3 g/l produs pe bază de 5 alchilsulfați și esteri de alchilsulfați, agitarea timp de 10 min la început, repaus 3 h, 15 min agitare, repaus 2,5 h și agitare 30 min, la final, curățarea de ciulini și spălarea mecanică pe lână, 7 ștrecuire, înmuiat II, la aceeași temperatură, cu 0,5 g/l alchilolamine cu conținut de substanțe antiseptice, 0,5 g/l amestec de acizi dicarboxilici alifatici și 0,5 g/l produs pe bază de alchilsulfați 9 și esteri de alchilsulfați, agitarea timp de 30 min, repaus 1 h, 5 min agitare/3 h repaus, pe durata nopții, 30 min agitare dimineața, curățarea de scaieți și spalarea mecanică pe lână, centrifugare, 11 tundere, șeruire, spălare în flotă de 38°C (101 apă/1 piele) cu 0,5 g/l Na₂CO₃ și 2 g/l produs pe bază de alchilsulfați și esteri de alchilsulfați, timp de 60 min, scurgere pe boc 15 min, clătire în 13 flota de 30’C (10 1/1 piele) conținând 0,25 g/l acid formic, 15 min agitare, centrifugare, piclare în flota de 25’C (101 apă/1 piele), conținând 40 g/l sare, agitare 10 min cu pieile, adăugare 4 g/l 15 agenți de ungere sintetici anionici (rezistenți la lumină, acizi, săruri de crom), 2 g/l acizi dicarboxilici alifatici în 2...3 porții la intervale de 10 min agitare/20 min repaus, adăugare 4 g/l 17 acid formic 85%, în 4...5 porții, la intervale de 10 min agitare/50 min repaus, în continuare 10 min agitare/8 h repaus, timp de 24 h, odihnă pe boc timp de 48 h, tăbăcirea pieilor piclate și 19 scurse prin introducere directă în flota de tăbăcire, formată din apă de 35°C (101/1 piele), 40 g/l sare, 1,5 g/l Cr₂O₃ de 33°bazicitate și 2 g/l agenți de ungere sintetici anionici, rezistenți la sare, 21 acizi și săruri de crom, agitare 2...3 h la început, apoi 1 h agitare/1 h repaus, timp de 6 h, corectarea pH-ului la 3,5...3,6 cu NaHCO₃, adăugarea în 3...4 porții a 30 min agitare/30 min 23 repaus, 10 min agitare/3 h repaus, pe duarta nopții, corectarea pH -ului la 3,9...4,1 cu NaHCO₃, adăugat în 3 porții a 30 min agitare/30 min repaus, agitare 1 ...2 h reapos în flotă 4...6 h odihnă 25 pe boc peste nopate, spălare în flotă de 30...35’0 cu 0,5 g/l produs pe bază de alchilsulfați și esteri de alchilsulfați și 0,2 g/l acid formic 85% timp de 15 min, centrifugare, întindere, uscare 27 și prelucrare în continuare după tehnologia pieilor de ovine înnobilate pe blană.EXAMPLE 1. The process according to a first embodiment consists in the introduction of the skins, with a surface of 35 ... 45 dm ² , preserved in the hatchery, in a fleet at temperature 3 of 25'C, representing 151 water / 1 skin. Preserved, containing 0.5 g / l alkylolamines containing antiseptic substances, 0.5 g / l aliphatic dicarboxylic acids and 0.3 g / l product based on 5 alkylsulphates and alkylsulphate esters, stirring for 10 min. at first, 3 h rest, 15 min shaking, 2.5 h rest and 30 min shaking, at the end, cleaning the chunks and mechanical washing on the wool, 7 breaks, softened II, at the same temperature, with 0.5 g / l alkylolamines containing antiseptic substances, 0.5 g / l aliphatic dicarboxylic acid mixture and 0.5 g / l alkyl sulphate product 9 and alkyl sulphate esters, stirring for 30 min, resting 1 h, 5 min stirring / 3 h rest, during the night, 30 min shaking in the morning, cleaning the chairs and washing mechanical area on wool, centrifugation, 11 trimming, seaming, 38 ° C (101 water / 1 skin) fleet washing with 0.5 g / l Na ₂ CO ₃ and 2 g / l alkyl sulphate and esters alkyl sulphates, for 60 minutes, drain on mouth 15 minutes, rinsing in 13 30'C fleet (10 1/1 skin) containing 0.25 g / l formic acid, 15 minutes stirring, centrifugation, pickling in 25 'fleet C (101 water / 1 skin), containing 40 g / l salt, shaking 10 min with the skins, adding 4 g / l 15 anionic synthetic lubricants (light resistant, acids, chromium salts), 2 g / l acids aliphatic dicarboxylics in 2 to 3 portions at intervals of 10 min stirring / 20 min rest, adding 4 g / l 17 formic acid 85%, in 4 to 5 portions, at intervals of 10 min stirring / 50 min rest, further 10 min shaking / 8 h rest, for 24 h, rest on the mouth for 48 h, tanning of the damaged skin and 19 leaks by direct introduction into the tanning fleet, formed from water of 35 ° C (101/1 skin) , 40 g / l salt, 1.5 g / l C r ₂ O ₃ of 33 ° basicity and 2 g / l synthetic anionic, salt-resistant lubricants, 21 acids and chromium salts, stirring 2 ... 3 h first, then 1 h stirring / 1 h rest, time 6 hours, pH adjustment to 3.5 ... 3.6 with NaHCO ₃ , addition in 3 ... 4 portions of 30 min stirring / 30 min 23 rest, 10 min stirring / 3 h rest, on the dart nights, pH adjustment to 3.9 ... 4.1 with NaHCO ₃ , added in 3 portions of 30 min stirring / 30 min rest, stirring 1 ... 2 h rest in the fleet 4 ... 6 h rest 25 per mouth over nights, washing in a fleet of 30 ... 35'0 with 0.5 g / l product based on alkyl sulphates and esters of alkyl sulphates and 0.2 g / l formic acid 85% for 15 minutes, centrifugation , stretching, drying 27 and further processing according to the technology of the fur coats.

Pieile astfel tratate prezintă înveliș pilos, alb, curat, des și neîmpâslit, fără chelii, bine 29 degresat, cu stratul dermic extensibil, plin la pipăit și moale, sunt uniform tăbăcite pe toate zonele topografice ale pielii și sunt rezistente la cusătură sau la lumină. 31The skins thus treated have a hairy, white, clean, thick and non-pliable coat, without any balding, well skimmed, with the extensible dermal layer, full to the touch and soft, are evenly tanned on all the topographic areas of the skin and are resistant to staining or light . 31

Exemplul 2. Conform unui al doilea exemplu de realizare, procedeul constă în introducerea pieilor de oi, conservate în hașpel, peste care se adaugă flotă cu temperatura de 20...27’0 33 (20 I apă/1 piele) utilizând pentru înmuiere 0,8 g/l alcooli grași sulfatați, 0,5 g/l formol (37%) șiExample 2. According to a second embodiment, the process consists of introducing the preserved sheepskin into the hatch, on which is added a fleet with a temperature of 20 ... 27'0 33 (20 I water / 1 skin) using for softening. 0.8 g / l sulphated fatty alcohols, 0.5 g / l formol (37%) and

I g/l acid formic 85%, se agită 15 min la început, repaus 2...3 h, agitare 15 min pauză 2...3 h 35 după care se agită 30 min, la final, curățare de ciulini și spălare mecanică pe lâna, ștrecuire, înmuiere în flotă de 20...27’0 (201 apă/1 piele) cu 1 g/l alcooli grași sulfați, 0,8 g/l formol (37%) 37 și 0,9 g/l acid formic 85%, se agită 30 min, repaus 1 h 5 min agitare/3 h repaus, pe durata nopții, min agitare dimineața, curățare de scaieți și spalare mecanică pe lână, centrifugare, tundere, 39 șeruire, spălare I în flotă de 38°C (20 I apă/1 piele) cu 1 g/l Na₂CO₃ și 3 g/l produs pe bază de alchilsulfați și esteri alchilsulfați, timp de 60 min, scurgere pe boc 15 min, clătire în flotă de 41I g / l formic acid 85%, shake 15 min at first, rest 2 ... 3 h, shake 15 min pause 2 ... 3 h 35 after which shake 30 min, at the end, cleansing and washing mechanical on wool, braiding, soaking in the fleet of 20 ... 27'0 (201 water / 1 skin) with 1 g / l sulphate fatty alcohols, 0.8 g / l formol (37%) 37 and 0.9 g / l formic acid 85%, shake 30 min, rest 1 h 5 min shake / 3 h rest, during the night, min shake in the morning, cleaning of chairs and mechanical washing on wool, centrifugation, clipping, 39 wiping, washing I in fleet of 38 ° C (20 I water / 1 skin) with 1 g / l Na ₂ CO ₃ and 3 g / l produced with alkyl sulphates and alkyl sulphate esters, for 60 min, drain on mouth 15 min, rinsing in the fleet of 41

25...30°C (20 I apă/1 piele) conținând 0,30 g/l acid formic, 15 min agitare, centrifugare, spălare25 ... 30 ° C (20 I water / 1 skin) containing 0.30 g / l formic acid, 15 min shaking, centrifugation, washing

II în flotă de 38’C (20 I apă/1 piele) cu 3 g/l produs pe baza de alchilsulfați și esteri de 43 alchilsulfați, timp de 120 min, scurgere pe boc 15 min, clătire în flotă de 25...30’C, conținândII in 38'C fleet (20 I water / 1 skin) with 3 g / l produced on the basis of alkyl sulphates and esters of 43 alkyl sulphates, for 120 minutes, drain on mouth 15 minutes, rinsing in the fleet of 25 ... 30'C, containing

0,3 g/l acid formic 85%, centrifugare, piclare în flotă de 25.._30°C (20 I apă/1 piele) conținând 45 45 g/l sare 6 g/l agenți de ungere sintetici anionici, rezistenți la lumină, săruri, acizi și săruri de crom, introducerea pieilor, agitarea timp de 10 min, adăugare a 4 g/l acid formic 85% în 4 porții, 47 la intervale de 10 min agitare/50 min repaus, în continuare 10 min agitare/8 h repaus, timp de0.3 g / l 85% formic acid, centrifugation, pickling in the 25.._ 30 ° C fleet (20 I water / 1 skin) containing 45 45 g / l salt 6 g / l anionic synthetic lubricants, resistant to light, salts, acids and chromium salts, introduction of the skins, shaking for 10 minutes, addition of 4 g / l formic acid 85% in 4 portions, 47 at intervals of 10 min shaking / 50 min rest, further 10 min shaking / 8 h rest, during

RO 120488 Β1 h, odihnă pe boc, timp de 72 h, tăbăcirea pieilor piclate și scurse prin introducerea directă în flotă formată din apă de 35’C (201 apă/1 piele), 45 g/l sare, 4...8 g/l Cr₂O₃ de 33% bazicitate și 4...5 g/l agenți de ungere sintetici anionici (rezistenți săruri acizi și săruri de crom), agitareRO 120488 Β1 h, rest on mouth, for 72 h, tanning of damaged and drained skins by direct introduction into the fleet consisting of 35'C water (201 water / 1 skin), 45 g / l salt, 4 ... 8 g / l Cr ₂ O ₃ of 33% basicity and 4 ... 5 g / l synthetic anionic lubricants (acid and chromium salts resistant), stirring

2.. .3 h la început, apoi 1 h agitare/1 h repaus, timp de 6 h, corectarea pH-ului la 3,5...3,6 cu NaHCO₃, adăugat în 3...4 porții a 30 min agitare/30 min repaus, 10 min agitare/3 h repaus, pe durata nopții, corectarea pH -ului la 3,9 cu NaHCO₃ adăugat în 3 porții a 30 min agitare/30 min repaus, agitarea 1...2 h repaus în flotă 4...6 h, odihnă pe boc peste noapte, spălare în flotă de2 .. .3 h first, then 1 h stirring / 1 h rest, for 6 h, pH correction at 3.5 ... 3.6 with NaHCO ₃ , added in 3 ... 4 portions of 30 min stirring / 30 min rest, 10 min stirring / 3 h rest, overnight, pH correction to 3.9 with NaHCO ₃ added in 3 portions of 30 min stirring / 30 min rest, stirring 1 ... 2 h rest in the fleet 4 ... 6 h, rest on the boat overnight, washing in the fleet of

30.. .35’C cu 1 g/l emulgator neionogen pe bază de substanțe grase etoxilate și 0,3 g/l acid formic 85% timp de 15 min, centrifugare, întindere, uscare și prelucrare în continuare după tehnologia pieilor de ovine înnobilate pe blană.30 .. .35'C with 1 g / l nonionogenic emulsifier based on ethoxylated fatty substances and 0.3 g / l formic acid 85% for 15 minutes, centrifugation, stretching, drying and further processing according to sheepskin technology ennobled on fur.

Pieile astfel tratate sunt uniforme, nu prezintă chelii, rupturi sau găuri și au o aderență corespunzătoare a stratului papilar față de stratul reticular.The leathers thus treated are uniform, do not show baldness, ruptures or holes and have an adequate adhesion of the papillary layer to the reticular layer.

Exemplul 3. în condițiile prezentate în exemplul nr.1, se tratează piei mici cu deosebirea că, la înmuiat I, se adaugă 0,5 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică, la înmuiat II se adaugă 0,5 g/l componenți fenolici, 0,2 g/l formol 37%, 0,2 g/l acid formic 85% și 0,5 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică, la spălat se adaugă 1 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică, 1 g/l agenți tensioactivi clorurați neionici și 0,5 g/l Na₂CO₃ la piclat se adaugă 40g/l sare, 4 g/l combinație de materiale sintetice cu catena lungă, sulfate și stabilizatori neionici, 2 g/l acizi dicarboxilici și 4 g/l acid formic 85%, la tăbăcit se adaugă 40 g/l sare, 1,5 g/l Cr₂O₃ și 2 g/l combinație de materiale sintetice cu catenă lungă, sulfate și stabilizatori neionici, NaHCO₃ pentru corectarea pH-ului laExample 3. Under the conditions presented in example no. 1, small skins are treated with the difference that, when softened I, 0.5 g / l synergistic anionic and non-ionic surface active agents are added, softened II is added 0, 5 g / l phenolic components, 0.2 g / l 37% formol, 0.2 g / l 85% formic acid and 0.5 g / l synergistic anionic and non-ionic surfactants, with the addition of 1 g / l anionic and nonionic surfactants with synergistic action, 1 g / l nonionic chlorinated surfactants and 0.5 g / l Na ₂ CO ₃ to the spiked add 40g / l salt, 4 g / l combination of synthetic materials with long chain, sulphates and nonionic stabilizers, 2 g / l dicarboxylic acids and 4 g / l formic acid 85%, 40 g / l salt, 1.5 g / l Cr ₂ O ₃ and 2 g / l combination of long-chain synthetic materials, sulphates and non-ionic stabilizers, NaHCO ₃ for pH correction at

3.5.. .3.6 și respectiv NaHCO₃ pentru corectarea pH-ului la 3,9...4,1.3.5 .. .3.6 and NaHCO ₃ respectively for pH correction at 3.9 ... 4.1.

Pieile astfel tratate sunt bine degresate, cu stratul dermic extensibil, plin la pipăit, cu moliciune, cu rezistențe la cusătură sau la lumină și cu aderență corespunzătoare a stratului papilar față de stratul reticular.The skins thus treated are well skimmed, with the extensible dermal layer, full to the touch, with softness, with resistance to seam or light and with proper adhesion of the papillary layer to the reticular layer.

Exemplul 4. Pieile de oi, conservate, se tratează în condițiile prezentate în exemplul 2, cu deosebirea că, la înmuiat I, se adaugă 0,5 g/l formol 37%, 0,8 g/l agenți activi de suprafață anionici, cu acțiune sinergică, 0,8 g/l acid formic, la înmuiat II se adaugă 1 g/l formol 37%, 1 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică și 0,3 g/l acid formic, la spălat I se adaugă 1 g/l Na₂CO₃, 2 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică și 1...2 g/l emulgator neionogen pe bază de substanțe grase etoxilate, la spălat II, se adaugă 1,5 g/l agenți activi de suprafață anionici și neionici cu acțiune sinergică și emulgator neionogen pe bază de substanțe grase etoxilate, la piclat se adăuga 45 g/l sare, 6 g/l esteri de acizi grași oxidați și sulfitați, 8 g/l acid formic 85%, la tăbăcit se adaugă 45 g/l sare, 1,8 g/l Cr₂O₃ de 33% bazicitate și 4 g/l esteri de acizi grași oxidați și sulfitați, NaHCO₃ pentru corectarea pH-ului laExample 4. The preserved sheepskin is treated according to the conditions presented in example 2, with the exception that 0.5 g / l 37% formol, 0.8 g / l anionic surfactants are added to the softened I, with synergistic action, 0.8 g / l formic acid, 1 g / l 37% formol, 1 g / l anionic and nonionic surfactants with synergistic action and 0.3 g / l formic acid are added to the softened II; to wash I add 1 g / l Na ₂ CO ₃ , 2 g / l synergistic anionic and nonionic surfactants and 1 ... 2 g / l nonionogenic emulsifier based on ethoxylated fatty substances, in wash II, add 1.5 g / l anionic and nonionic surfactants with synergistic action and nonionogenic emulsifier based on ethoxylated fatty substances, add 45 g / l salt, 6 g / l esters of oxidized fatty acids and sulphites, 8 g / l 85% formic acid, 45 g / l salt, 1.8 g / l Cr ₂ O ₃ of 33% basicity and 4 g / l esters of oxidized fatty acids and sulfites, NaHCO ₃ for pH correction at

3,5...3,6 și respectiv pentru corectarea pH-ului la 3,9...4,0.3.5 ... 3.6 and pH correction respectively at 3.9 ... 4.0.

Pieile astfel tratate sunt bine și uniform tăbăcite în secțiune și pe zonele topografice ale pielii, prezintă înveliș pilos, curat, fără chelii și sunt rezistente la cusătură sau la lumină.The skins thus treated are well and evenly tanned in the section and on the topographic areas of the skin, they have a hairy, clean coat, without the baldness and are resistant to stitching or light.

Claims

claims

1. Tanning process of sheepskin for semi-finished products on fur, consisting of leather preparation, followed by the tanning itself, characterized in that the preparation of the skins is done by softening in two stages with intermediate shredding, washing in two phases, mechanical cleaning and washing, trimming and waxing, rinsing, centrifuging and pinching in the fleet, and tanning is done with basic chromium salts, with 33% basicity, in the presence of synthetic oils, with pH correction at 3.5 ... 3.6 and, finally, at 3.9 ... 4.1 with NaHCO ₃ , the tanned leathers are washed, centrifuged, dried and processed under known conditions.

RO 120488 Β1

Process according to claim 1, characterized in that the softening is performed 1 with 0.5-1 g / l aliphatic dicarboxylic acid mixture or 0.5-1 g / l formic acid, 0.5. ..1 g / l surface anionic and nonionic surfactants with synergistic action or with 0,5 ... 1 g / l nonionic emulsion - 3 gen based on ethoxylated fatty substances or with 0,5 ... 1 g / l alkylsulphates and esters of alkylsulphates.

3. Process according to claim 1, characterized in that the washing is performed 5 with 0.5 ... 1 g / l Na ₂ CO ₃ and 2 ... 3 g / l surface anionic and nonionic surfactants, with synergistic action. or with 2 ... 3 g / l non-ionic emulsifier based on ethoxylated fatty substances or with 2 ... 3 g / l 7 alkylsulphates and alkylsulphate esters or with 2 ... 3 g / l sulphated fatty alcohols.

4. Process according to claim 1, characterized in that the painting is performed 9 with 40 ... 50 g / l salt, 4 ... 8 g / l synthetic anionic oil or 4 ... 8 g / l esters. of oxidized and sulphite fatty acids and 2 ... 3 g / l mixture of aliphatic dicarboxylic acids and 4 ... 8 g / l formic. 11

5. Process according to claim 1, characterized in that the tanning is carried out with a fleet containing 40 ... 50 g / l salt, 1.5 ... 2.5 g / l Cr ₂ O ₃ , as salts. chrome base 13 of 33% basicity and 1 .... 4 g / l synthetic anionic oil or 1 ... 4 g / l combination of synthetic materials with long and high sulfated chain, also containing stabilizers or 1 ... 4 g / l 15 oxidized and sulphite fatty acid esters.