RO120349B1 - Composition as colloidal emulsion and process for application in fighting against dampness in construction elements - Google Patents
Composition as colloidal emulsion and process for application in fighting against dampness in construction elements Download PDFInfo
- Publication number
- RO120349B1 RO120349B1 RO99-01376A RO9901376A RO120349B1 RO 120349 B1 RO120349 B1 RO 120349B1 RO 9901376 A RO9901376 A RO 9901376A RO 120349 B1 RO120349 B1 RO 120349B1
- Authority
- RO
- Romania
- Prior art keywords
- concentration
- composition
- emulsion
- construction elements
- alkaline
- Prior art date
Abstract
Description
Invenția se referă la o compoziție sub formă de emulsie coloidală și la un procedeu de aplicare a acestei compoziții, cu scopul de a combate igrasia apărută în elementele de construcție, cauzată de infiltrațiile de apă din sol.The invention relates to a composition in the form of a colloidal emulsion and to a process for applying this composition, with the aim of combating the grease that appears in the building elements, caused by the infiltration of water from the soil.
Sunt cunoscute mai multe procedee de îndepărtare a igrasiei, dar care au dezavantajul că prezintă o eficiență redusă, și care necesită, în general, îndepărtarea stratului de tencuială a zidăriei expusă degradării în urma instalării igrasiei, urmată de aplicarea tratamentului și apoi refacerea tencuielii respective. Stratul protector (hidrofob), care se aplică, poate fi pe bază de derivați acrilici sau vinilici (US 4357384), emulsie siliconică (US 4273813), palmitat de zinc împreună cu un precipitat insolubil (GB 477603), bentonită împreună cu aditivi organici și anorganici (US 4366288), silicat amestecat cu silice amorfă, urmat de un tratament cu o soluție conținând unul din componenții următori: acid fosforic, fosfați, sulfați, fluorosilicați sau persulfat de amoniu (US 3977888). Tratamentele se execută prin pensulare sau stropire în unul sau mai multe straturi, formând astfel, în zona de aplicare, o peliculă care împiedică trecerea apei și a sărurilor dizolvate în ea, dinspre interiorul zidăriei spre exterior. Aceste tratamente de suprafață nu întrerup transportul capilar pe verticală, în interiorul zidăriei, dar împiedică evaporarea în zona tratată, având drept rezultat mărirea cantității de apă și intensificarea transportului capilar către zone mai înalte, netratate, care permit evaporarea, până când se ajunge la echilibrul: cantitate transportată = cantitate evaporată. Ca urmare a acestui fenomen, în majoritatea cazurilor, igrasia apare în câțiva ani (uneori chiar în primăvara următoare) imediat deasupra zonei tratate, la interior sau exterior, putând atinge înălțimi de peste 7-10 m, în funcție de înălțimea și natura zidăriei.Several processes for removing the grease are known, but they have the disadvantage of having a low efficiency, and which generally require the removal of the plaster layer of the masonry exposed to degradation following the installation of the grease, followed by the application of the treatment and then the restoration of the plaster. The protective (hydrophobic) layer that is applied can be based on acrylic or vinyl derivatives (US 4357384), silicone emulsion (US 4273813), zinc palmitate together with an insoluble precipitate (GB 477603), bentonite along with organic additives and inorganic (US 4366288), silicate mixed with amorphous silica, followed by treatment with a solution containing one of the following components: phosphoric acid, phosphates, sulphates, fluorosilicates or ammonium persulfate (US 3977888). The treatments are executed by brushing or splashing in one or more layers, thus forming, in the area of application, a film that prevents the passage of water and salts dissolved in it, from the inside of the masonry to the outside. These surface treatments do not interrupt the capillary transport vertically, within the masonry, but they prevent evaporation in the treated area, resulting in an increase in the amount of water and the intensification of capillary transport to higher, untreated areas, which allow evaporation, until it reaches equilibrium. : transported quantity = evaporated quantity. As a result of this phenomenon, in most cases, the igrasia appears in a few years (sometimes even in the following spring) immediately above the treated area, indoors or outdoors, being able to reach heights of over 7-10 m, depending on the height and nature of the masonry.
O situație deosebită se întâlnește la construcțiile situate sub nivelul solului. Zidurile situate sub nivelul solului sunt protejate, în timpul construirii, prin acoperirea, pe suprafața exterioară, cu un strat bituminos, un strat polimeric (poliuretan, polistiren) sau prin alte acoperiri organice sau anorganice. Asemenea tratamente sunt bune atât timp cât nu sunt deteriorate. O dată ce este întreruptă continuitatea stratului, apa ajunge la elementele de zidărie. Difuzia apei prin zidărie face aproape imposibilă localizarea punctului în care acoperirea s-a deteriorat. De asemenea, o dată ce construcția este definitivată, este dificil de reparat acoperirea exterioară a zidurilor situate sub nivelul solului, deoarece trebuie excavat pământul pentru a reface izolația. Excavarea poate cauza mai multe pagube la acoperirea deja fisurată. încercarea de a acoperi și partea interioară a zidului cu un strat hidrofob ar duce la păstrarea apei în zid, eventual, ar duce la urcarea ei prin capilaritate la nivele superioare, ducând în timp la degradarea zidăriei. De asemenea, pentru a aplica un strat hidrofob pe partea interioară a zidăriei, aceasta ar trebui, în prealabil, să fie uscată, lucru destul de greu de realizat.A special situation is encountered in buildings below ground level. The walls below the ground level are protected, during the construction, by covering, on the outer surface, with a bituminous layer, a polymeric layer (polyurethane, polystyrene) or by other organic or inorganic coatings. Such treatments are good as long as they are not damaged. Once the continuity of the layer is interrupted, the water reaches the masonry elements. The diffusion of water through the masonry makes it almost impossible to locate the point where the coating has deteriorated. Also, once the construction is completed, it is difficult to repair the outer covering of the walls below the ground level, because the earth must be excavated to restore the insulation. Excavation can cause more damage to the already cracked coating. Attempting to cover the inner part of the wall with a hydrophobic layer would result in water retention in the wall, possibly leading to its rise through capillaries at higher levels, leading to degradation of the masonry over time. Also, in order to apply a hydrophobic layer on the inside of the masonry, it should first be dried, which is quite difficult to achieve.
Se cunoaște, de asemenea, că pentru etanșarea elementelor subterane de construcție și a solului din împrejurimi se pot folosi (RO 93978) polimeri organici în amestec cu silicat de sodiu, dar procedeul de utilizare a acestora prezintă dezavantajul că necesită umplerea și golirea succesivă a elementului de construcție cu compoziția respectivă și apoi cu o soluție acidă. Dacă procedeul poate fi aplicat cu ușurință pentru etanșarea conductelor sau a altor elemente de construcție subterane cu dimensiuni mici, nu același lucru se întâmplă în cazul incintelor mari unde cantitatea de soluție care ar trebui preparată, manipulată și apoi păstrată pentru a fi refolosită nu se justifică economic.It is also known that for the sealing of the underground elements of the construction and of the surrounding soil (RO 93978) organic polymers can be used mixed with sodium silicate, but the process of using them has the disadvantage that it requires the successive filling and emptying of the element. of construction with the respective composition and then with an acid solution. If the process can be easily applied for sealing pipes or other small underground construction elements, the same is not true for large enclosures where the amount of solution that should be prepared, handled and then retained for reuse is not justified. economic.
Problema tehnică, pe care o rezolvă invenția, constă în realizarea unei compoziții coloidale, care, după impregnare în elementele de construcție, să determine transformarea componentelor aferente într-un gel care să astupe porii elementelor de construcție, printr-un strat hidrofob, impermeabil, întrerupând transportul apei prin capilaritate către părțile superioare ale elementelor.The technical problem, which is solved by the invention, is to make a colloidal composition, which, after impregnation in the construction elements, will determine the transformation of the related components into a gel that will clog the pores of the construction elements, through a hydrophobic, impermeable layer, interrupting the transport of water by capillarity to the upper parts of the elements.
RO 120349 Β1RO 120349 Β1
Compoziția conform invenției este constituită dintr-un component activ ales dintre 1 silice hidratată, silicat de potasiu și/sau silicat de sodiu în concentrație de 5...20% în greutate, procentele fiind exprimate pentru SiO2, un emulgator, de preferință, o sare alcalină a 3 acizilor carboxilici cu 8...20 atomi de carbon în concentrație de până la 10%, un regulator de pH, de preferință, un hidroxid alcalin, carbonat sau bicarbonat alcalin, în proporție de până 5 la 5%, un antiseptic, de preferință tiabendazol, carboximă, oxicarboximă în concentrație de până la 1 %, un anticongelant, de preferință etilenglicol, în concentrație de până la 8% și un 7 colorant pentru mediu bazic, de preferință galben de alizarină, timolftaleină sau albastru de timol în concentrație de până la 1,5%. 9The composition according to the invention consists of an active component selected from 1 hydrated silica, potassium silicate and / or sodium silicate in a concentration of 5 ... 20% by weight, the percentages being expressed for SiO 2 , an emulsifier, preferably, an alkaline salt of 3 carboxylic acids with 8 to 20 carbon atoms up to 10%, a pH regulator, preferably an alkaline hydroxide, carbonate or alkaline bicarbonate, up to 5 to 5%, an antiseptic, preferably thiabendazole, carboxymine, oxycarboximine in concentration up to 1%, an antifreeze, preferably ethylene glycol, in concentration up to 8%, and a 7 colorant for basic medium, preferably yellow alizarin, thymolphthalin or blue. thymol in concentration up to 1.5%. 9
Procedeul de aplicare a compoziției conform invenției constă în aceea că, în vederea întreruperii transportului apei prin capilaritate, elementul de construcție se impregnează cu 11 emulsie coloidală, prin injectare în zid, prin intermediul unor orificii practicate fie pe o parte, fie pe ambele părți ale elementului de construcție, distanța dintre orificii fiind corelată cu raza 13 de difuzie a emulsiei în jurul orificiului, astfel încât să nu mai rămână între orificii porțiuni din elementul de construcție neimpregnat cu emulsie. 15The process of applying the composition according to the invention consists in the fact that, in order to interrupt the transport of water by capillarity, the construction element is impregnated with 11 colloidal emulsion, by injection into the wall, through holes made either on one side or on both sides of the of the construction element, the distance between the orifices being correlated with the radius 13 of diffusion of the emulsion around the orifice, so that it no longer remains between the orifices portions of the construction element not impregnated with emulsion. 15
Silicea hidratată, diluată sau obținută in situ, este un amestec de acid metasilic (H2SiO3)n, acid ortosilicic și acizi polisilicici H2Si2O5, H2Si2O7. Inițial în soluție se formează un 17 sol, care conține molecule cu dimensiuni relativ mici, solubile în apă. Pe măsura creșterii procesului de condensare, se obțin acizi polisilicici de tipul mSiO2 x nH2O cu dimensiuni din ce 19 în ce mai mari, care depășind o anumită limită devin insolubili transformându-se într-o masă gelatinoasă translucidă care conține multă apă. Solul coagulează, obținându-se un gel. în 21 timp, mai repede la încălzire, gelul pierde apa transformându-se într-o masă amorfă cu structuri macromoleculare, tridimensionale din ce în ce mai mari, care obturează porii zidăriei 23 împiedicând astfel urcarea apei prin capilaritate.Hydrated silica, diluted or obtained in situ, is a mixture of metasilic acid (H 2 SiO 3 ) n , orthosilic acid and polysilicon acids H 2 Si 2 O 5 , H 2 Si 2 O 7 . Initially in solution a 17 soil is formed, which contains molecules of relatively small size, soluble in water. As the condensation process increases, polysilicic acids of the type mSiO 2 x nH 2 O are obtained, increasing in size 19 and exceeding a certain limit, becoming insoluble, transforming into a translucent gelatinous mass containing a lot of water. The soil coagulates, obtaining a gel. In 21 time, faster upon heating, the gel loses its water transforming into an amorphous mass with increasingly larger three-dimensional macromolecular structures, which clog the pores of the masonry 23 thus preventing the water from rising through capillarity.
Pentru injectarea compoziției, în zidul supus tratamentului, se practică orificii cu dia- 25 metrul de 8+12 mm, distanțate între ele la 8-12 cm, în plan orizontal sau sub un unghi oarecare față de suprafața verticală a zidului, de o parte și de alta a zidului, sau numai pe o 27 singură parte. Atunci când orificiile se practică pe ambele părți ale zidului (la zidurile situate deasupra nivelului solului), ele trebuie să ajungă până la jumătatea grosimii zidului (fig. 1 și 29 fig. 2), iar când se practică pe o singură parte (atunci când zidul este sub nivelul solului, sau în cazul zidurilor situate deasupra solului, dar accesul la o față a zidului este dificil), ele tre- 31 buie să pătrundă până la 3-4 cm de fața opusă a zidului (fig. 3 și fig. 4). în continuare, dintr-un rezervor, prin intermediul unui sistem de distribuție, se injectează emulsia în zid. Sis- 33 temui de distribuție este compus din tuburi flexibile din material plastic, care au un capăt montat în orificiile practicate și sunt etanșate, pentru a nu permite scurgerea compoziției în 35 exteriorul orificiilor, iar celălalt capăt comunică cu vasul comun umplut cu emulsie. De asemenea, se pot folosi și dispozitive de injectare sub presiune a compoziției. Zidul absoarbe 37 într-o primă fază o cantitate mai mare de emulsie, dar odată cu începerea formării gelului de silice și apoi a structurilor tridimensionale macromoleculare, cantitatea de emulsie absorbită 39 de zid scade, pentru ca odată cu blocarea porilor zidăriei și formarea unui strat impermeabil pentru apă, nici emulsia să nu mai fie absorbită. în acest moment se consideră tratamentul 41 împotriva igrasiei încheiat. Se astupă orificiile cu un amestec ciment:nisip:emulsie de injectat și apoi se reface, dacă este cazul, finisarea exterioară. 43In order to inject the composition, in the wall subjected to the treatment, holes with a diameter of 8 + 12 mm are practiced, spaced 8-12 cm apart, horizontally or at some angle to the vertical surface of the wall, on the one hand. and on the other side of the wall, or only on one side. When the holes are made on both sides of the wall (at the walls above the level of the floor), they should reach up to half the thickness of the wall (figs. 1 and 29 fig. 2), and when they are practiced on one side (when the wall is below the ground level, or in the case of the walls above the ground, but access to one side of the wall is difficult), they must penetrate up to 3-4 cm from the opposite side of the wall (fig. 3 and fig. 4). The emulsion is then injected into the wall from a tank through a distribution system. The distribution system is composed of flexible plastic tubes, which have an end mounted in the holes practiced and are sealed, so as not to allow the composition to flow into the outside of the holes, and the other end communicates with the common vessel filled with emulsion. Also, pressure injection devices of the composition can be used. The wall absorbs 37 in a first phase a larger amount of emulsion, but once the silica gel begins to form and then the macromolecular three-dimensional structures, the amount of emulsion absorbed 39 of the wall decreases, because with the blocking of the masonry pores and the formation of a layer. neither waterproof nor emulsion absorbed. At this point, the treatment against the completed pregnancy is considered 41. The holes are filled with a mixture of cement: sand: emulsion to be injected and then re-finished, if necessary, the exterior finish. 43
Compoziția conform invenției prezintă următoarele avantaje:The composition according to the invention has the following advantages:
- asigură impermeabilizarea elementelor de zidărie, prin blocarea porilor zidăriei în 45 zona tratată;- ensures the waterproofing of the masonry elements, by blocking the pores of the masonry in the 45 treated area;
- remedierea este definitivă - igrasia nu mai apare la nivele mai înalte; 47- the remedy is definitive - the igrasia no longer appears at higher levels; 47
- se elimină complet umiditatea datorată capilarității;- completely eliminates moisture due to capillary;
RO 120349 Β1RO 120349 Β1
- se îmbunătățește rezistența la transfer termic a zidăriei astfel tratate;- the resistance to thermal transfer of the masonry thus treated is improved;
- se obține o rezistență bună la atacul microoganismelor;- good resistance to attack of micro-organisms is obtained;
- compoziția emulsiei de impregnat este compatibilă cu materialele de construcție uzuale;- the composition of the impregnating emulsion is compatible with the usual construction materials;
- se întărește zidăria prin efect de liant asupra materialelor vechi, sfărâmicioase;- the masonry is strengthened by a binder effect on old, crumbly materials;
- este un produs ecologic.- is an organic product.
în continuare, sunt prezentate câteva exemple de realizare a compoziției conform invenției, aplicare a acesteia, în legătură și cu fig. 1...4 care reprezintă:In the following, there are presented some examples of embodiment of the composition according to the invention, its application, in connection with FIG. 1 ... 4 which represents:
- fig. 1, secțiune longitudinală printr-un zid cu igrasie situat deasupra nivelului solului în care s-au practicat orificii pentru injectarea compoziției;FIG. 1, a longitudinal section through a wall of gravel located above the level of the soil in which holes were made for injecting the composition;
- fig. 2, secțiune transversală printr-un zid cu igrasie situat deasupra nivelului solului în care s-au practicat orificii pentru injectarea compoziției;FIG. 2, a cross-section through a gravel wall above the ground level where holes were made for injecting the composition;
- fig. 3, secțiune longitudinală printr-un zid cu igrasie situat sub nivelului solului în care s-au practicat orificiile pe o singură parte pentru injectarea compoziției;FIG. 3, longitudinal section through a gravel wall below the level of the ground in which the holes were made on one side for injection of the composition;
- fig. 4, secțiune transversală printr-un zid cu igrasie situat sub nivelului solului în care s-au practicat orificiile pentru injectarea compoziției;FIG. 4, a cross-section through a gravel wall below the ground level where the holes for injecting the composition were made;
Exemplul 1. Experiment de verificare în condiții de laboratorExample 1. Verification experiment under laboratory conditions
Se formează o emulsie de impregnare din 100 părți masice Nalcoag 1035 silica sol (35% SiO2, densitate 1,25-1,30 g/cm3) - marcă înregistrată Nalco Chemical Co - diluate cu 250 părți masice apă distilată. Se adaugă sub agitare energică: 17 părți masice de palmitat de sodiu drept emulgator, 17 părți masice regulator de pH (NaHCO3), 28 părți masice de etilenglicol, 0,01 părți masice galben de alizarină și metam de sodiu (Nematin-produs comercial) drept fungicid în proporție de 0,01 părți masice.An impregnation emulsion is formed from 100 mass Nalcoag 1035 silica soil (35% SiO 2 , density 1.25-1.30 g / cm 3 ) - registered trademark Nalco Chemical Co - diluted with 250 mass parts distilled water. To be added under vigorous stirring: 17 parts by weight of sodium palmitate as emulsifier, 17 parts by weight pH regulator (NaHCO 3 ), 28 parts by weight ethylene glycol, 0.01 parts by weight yellow alizarin and sodium metam (Nematin-commercial product ) as a fungicide in the proportion of 0.01 mass parts.
Compoziția de injectat trebuie să aibă o concentrație în silicați solubili cuprinsă între 5+20% procente de masă, exprimată în SiO2. O concentrație mai mare de 20% duce la o creștere a viscozității compoziției, fapt ce îngreunează pătrunderea ei în elementele de zidărie și manipularea compoziției, în timp ce o concentrație mai mică de 5% nu asigură un tratament eficace deoarece difuzia compoziției prin elementele zidăriei are loc prea rapid, având drept consecință posibilitatea formării unui strat hidrofob discontinuu.The composition to be injected should have a soluble silicate concentration of 5 + 20% by mass, expressed in SiO 2 . A concentration greater than 20% leads to an increase in the viscosity of the composition, which makes it difficult to penetrate the masonry elements and manipulate the composition, while a concentration of less than 5% does not ensure effective treatment because the diffusion of the composition through the elements of the masonry has place too fast, resulting in the possibility of forming a discontinuous hydrophobic layer.
Pentru experimentări s-au folosit cărămizi ceramice în grupe perechi de câte cinci bucăți împărțite în două loturi: cărămizi martor și cărămizi în care se injectează compoziția antiigrasie. Injectarea s-a făcut respectând condițiile specificate mai sus: practicarea unor orificii, montarea tuburilor de pvc și etanșarea acestora, alimentarea dintr-un vas comun cu soluție situat la circa 1 m deasupra nivelului de așezare a cărămizilor. în continuare, atât cărămizile martor cât și cele în care s-a injectat soluția se plasează pe o suprafață de apă continuă.For experiments, ceramic bricks were used in pairs of five pieces divided into two groups: control bricks and bricks in which the anti-fat composition is injected. The injection was done in accordance with the conditions specified above: holes, pvc pipe fitting and sealing, feeding from a common solution vessel about 1 m above the level of bricks. Next, both the control bricks and those in which the solution was injected are placed on a surface of continuous water.
După 14 zile, se constată următoarele: umezirea prin capilaritate a cărămizilorîn care s-a injectat soluția antiigrasie are loc numai între suprafața de așezare pe apă și nivelul planului de injectare, zona situată deasupra planului de injectare rămânând uscată, în vreme ce lotul cărămizilor martor suferă umezire totală în tot volumul, după maximum patru zile de păstrare pe strat de apă.After 14 days, the following is observed: the wetting by the capillaries of the bricks in which the anti-grease solution was injected takes place only between the surface of settling on the water and the level of the injection plan, the area above the injection plan remaining dry, while the batch of the control bricks undergoes wetting total throughout the volume, after a maximum of four days of water storage.
Cu aceleași rezultate se pot folosi și următoarele soluri de silice hidratată (mărci înregistrate): Snowtex - Nissan Chemical Industries Ltd, Bindzil - Eka Chemicals.With the same results, the following hydrated silica soils (registered trademarks) can be used: Snowtex - Nissan Chemical Industries Ltd, Bindzil - Eka Chemicals.
Exemplul 2. Se formează emulsia de impregnare ca în exemplul 1.Example 2. The impregnation emulsion is formed as in Example 1.
Se consideră un element de construcție situat deasupra nivelului solului, care prezintă igrasie parțială sau pe întreaga suprafață. Se practică cu ajutorul unei rotopercutante orificii pe ambele părți (fig. 1, vedere din față și fig. 2, vedere din profil) ale elementului de construcție. Se montează tuburile flexibile de pvc și se etanșează, apoi se alimenteazăIt is considered to be a construction element located above the ground level, which has partial or entire surface moisture. It is practiced with a rotary drill hole on both sides (fig. 1, front view and fig. 2, profile view) of the construction element. Install the flexible pvc tubes and seal, then feed
RO 120349 Β1 dintr-un vas comun cu emulsie situat la circa 1 m deasupra nivelului de tratare. Se constată 1 că în prima zi emulsia este absorbită în cantitate mare (circa 1,51 pentru 1 m liniar de zidărie, în a doua zi se absorb aproximativ 0,5 I/ m liniar pentru ca, în a treia zi, absorbția să fie ne- 3 semnificativă). în acest moment, se consideră tratamentul împotriva igrasiei încheiat. Se demontează sistemul de distribuție a emulsiei, se astupă orificiile cu un amestec ci- 5 ment:nisip:emulsie și se reface, dacă este cazul finisarea exterioară. După aproximativ o lună se constată că zona din elementul de construcție situată deasupra nivelului de impreg- 7 nare se usucă.RO 120349 Β1 from a common emulsion vessel about 1 m above the treatment level. It is noted 1 that on the first day the emulsion is absorbed in a large quantity (about 1.51 for 1 linear m of masonry, in the second day about 0.5 I / m linear is absorbed so that on the third day the absorption will be non- 3 significant). at this time, the treatment against the completed drug is considered. The distribution system of the emulsion is disassembled, the holes are filled with a cement mixture: sand: emulsion and remade, if necessary, the exterior finish. After about a month it is found that the area of the construction element above the impregnation level dries up.
Exemplul 3. Se prepară o emulsie cu concentrația 10% exprimată în SiO2 din silicat 9 de potasiu (=41%) cu densitatea de 1,41 g/cm3 și un raport K2O:SiO2 de 1:2 prin diluare cu apă demineralizată. în continuare, se procedează ca în exemplul 1. 11Example 3. Prepare an emulsion with 10% concentration expressed in potassium silicate SiO 2 (= 41%) with a density of 1.41 g / cm 3 and a K 2 O: SiO 2 ratio of 1: 2 by dilution with demineralized water. Next, proceed as in Example 1. 11
Se consideră o porțiune din perete îngropat parțial sau total (fig. 3 și fig. 4), care datorită umidității solului prezintă igrasie pe întreaga suprafață sau numai parțial. în acest caz 13 orificiile se practică pe o singură parte a elementului de construcție, astfel încât să ajungă la 3-4 cm de fața opusă a zidului (fig. 4), cu specificarea că în acest caz este necesară 15 impregnarea unei suprafețe mai mari cu emulsie. în continuare se procedează ca în exemplul 2. 17It is considered a partially or totally buried part of the wall (Figs. 3 and Fig. 4), which due to soil moisture has a total or only partial surface area. in this case 13 the holes are practiced on one side of the construction element, so that it reaches 3-4 cm from the opposite side of the wall (fig. 4), specifying that in this case it is necessary to impregnate a larger surface. with emulsion. then proceed as in example 2. 17
După aproximativ 60 zile de la aplicarea tratamentului se constată atât uscarea peretelui subteran cât și uscarea zonei situate deasupra nivelului de injecție. 19After approximately 60 days from the application of the treatment, it is observed both the drying of the underground wall and the drying of the area above the injection level. 19
Claims (2)