PL240739B1 - Composition of multilayer foil, in particular for bag holder forming - Google Patents

Composition of multilayer foil, in particular for bag holder forming Download PDF

Info

Publication number
PL240739B1
PL240739B1 PL426062A PL42606218A PL240739B1 PL 240739 B1 PL240739 B1 PL 240739B1 PL 426062 A PL426062 A PL 426062A PL 42606218 A PL42606218 A PL 42606218A PL 240739 B1 PL240739 B1 PL 240739B1
Authority
PL
Poland
Prior art keywords
density polyethylene
low
layer
polyethylene
mfr
Prior art date
Application number
PL426062A
Other languages
Polish (pl)
Other versions
PL426062A1 (en
Inventor
Adam Kostyra
Original Assignee
Kostyra Adam Akost
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kostyra Adam Akost filed Critical Kostyra Adam Akost
Priority to PL426062A priority Critical patent/PL240739B1/en
Publication of PL426062A1 publication Critical patent/PL426062A1/en
Publication of PL240739B1 publication Critical patent/PL240739B1/en

Description

PL 240 739 B1PL 240 739 B1

Opis wynalazkuDescription of the invention

Przedmiotem wynalazku jest folia wielowarstwowa, w szczególności do formowania uchwytów toreb, mających zastosowanie przy konfekcjonowaniu towarów.The subject of the invention is a multilayer film, in particular for forming bag handles that are used in the packaging of goods.

Dotychczas są znane różne rodzaje wielowarstwowych folii. Z opisu patentowego PL187341 pod tytułem „Materiał opakowaniowy wielowarstwowy, zwłaszcza na opakowania elastyczne” znany jest wielowarstwowy materiał opakowaniowy, zwłaszcza na opakowania elastyczne, który zawiera, patrząc od zewnętrznej powierzchni w kierunku wewnętrznej powierzchni opakowania, zewnętrzną, zasadniczo przezroczystą folię mającą odwrotny druk na swojej powierzchni skierowanej do wewnątrz warstwę pośrednią przylegającą do zadrukowanej powierzchni folii zewnętrznej i nałożoną w postaci płynnej na wewnętrznej zadrukowanej powierzchni folii zewnętrznej warstwę metalizacji przylegającą do wewnętrznej powierzchni warstwy gazoszczelnej i wewnętrzną warstwę środka uszczelniającego, korzystnie w postaci poliolefiny.Various types of multilayer films are known to date. From the patent description PL187341 entitled "Multi-layer packaging material, especially for flexible packages", a multi-layer packaging material, especially for flexible packages, is known, which comprises, looking from the outer surface towards the inner surface of the package, an outer substantially transparent foil having a reverse print on its an inwardly facing intermediate layer adjacent to the printed surface of the outer film and applied in fluid form to the inner printed surface of the outer film a metallization layer adjacent to the inner surface of the gas-tight layer and an inner layer of sealant, preferably in the form of a polyolefin.

Z opisu patentowego PL188626 pod tytułem „Termoplastyczna, wielowarstwowa folia opakowaniowa”, znana jest wielowarstwowa folia opakowaniowa, składająca się z a) rdzeniowej warstwy barierowej dla tlenu, zawierającej kopolimer etylen-alkohol winylowy, b) dwóch warstw zewnętrznych oraz c) dwóch warstw klejowych, z których każda znajduje się pomiędzy warstwą rdzeniową a) i każdą z dwóch warstw zewnętrznych b), jest znamienna tym, że przynajmniej jedna z warstw zewnętrznych zawiera mieszaninę trzech składników A, B i C, w której składnik A jest homogenicznym lub heterogenicznym kopolimerem etylen-alfa-olefina o gęstości od 0,915 g/cm3 do 0,925 g/cm3, składnik B jest homogenicznym lub heterogenicznym kopolimerem etylen-alfa-olefina o gęstości co najmniej 0,925 g/cm3, a składnik C jest homogenicznym lub heterogenicznym kopolimerem etylen-alfa-olefina o gęstości nie większej niż 0,915 g/cm3. Opisane jest także zastosowanie zmodyfikowanych kopolimerów etylen-alfa-olefina o gęstości od około 0,900 g/cm3 do około 0,908 g/cm3 jako warstw klejowych, w celu polepszenia adhezji międzywarstwowej i podatności na uszczelnianie folii z warstwą rdzeniową, zawierającą kopolimer etylen-alkohol winylowy lub poliamid i warstwy zewnętrzne zawierające kopolimer etylen-alfa-olefina.From the patent description PL188626 under the title "Thermoplastic, multilayer packaging film", a multilayer packaging film is known, consisting of a) a core oxygen barrier layer containing an ethylene-vinyl alcohol copolymer, b) two outer layers, and c) two adhesive layers, with each of which is between the core layer a) and each of the two outer layers b), characterized in that at least one of the outer layers comprises a mixture of the three components A, B and C, where component A is a homogeneous or heterogeneous ethylene-alpha copolymer -olefin with a density of 0.915 g / cm 3 to 0.925 g / cm 3 , component B is a homogeneous or heterogeneous ethylene-alpha-olefin copolymer with a density of at least 0.925 g / cm 3 , and component C is a homogeneous or heterogeneous ethylene-alpha copolymer -olefin with a density of not more than 0.915 g / cm 3 . The use of modified ethylene-alpha-olefin copolymers with a density of about 0.900 g / cm 3 to about 0.908 g / cm 3 as adhesive layers is also described to improve interlayer adhesion and sealability of the film with a core layer containing an ethylene-alcohol copolymer. vinyl or polyamide, and outer layers containing ethylene-alpha-olefin copolymer.

Z opisu patentowego PL186579 pod tytułem „Wielowarstwowa folia plastikowa, stosowana do opakowywania produktów spożywczych i sposób wytwarzania wielowarstwowej folii plastikowej, stosowanej do opakowywania produktów spożywczych”, znana jest wielowarstwowa folia opakowaniowa, mająca przynajmniej pięć warstw ułożonych w kolejności i w kontakcie jedna z drugą, która charakteryzuje się tym, że zawiera pierwszą warstwę, stanowiącą przynajmniej 50% wagowo kopolimeru propenu i przynajmniej jednej olefiny alfa wybranej z grupy składającej się z etylenu, butenu-1, metylopentenu-1, heksenu-1, oktenu-1 i ich mieszanin, mającego zawartość propenu przynajmniej 60% wag., drugą i czwartą warstwę, z których każda zawiera przynajmniej 10% pierwszego kopolimeru etylenu i przynajmniej jednej C4-C8 olefiny alfa, przy czym ten kopolimer ma gęstość od 0,900 do 0,915 g/cm3 i wskaźnik topliwości mniejszy niż 1,0 dg/min i przynajmniej 10% drugiego kopolimeru etylenu i od 4 do 18% estru winylowego lub akrylanu alkilowego i przynajmniej 10% modyfikowanego bezwodnikiem trzeciego kopolimeru etylenu i przynajmniej jednej olefiny alfa, estru winylowego lub akrylanu alkilowego i od 0 do 30% czwartego kopolimeru etylenu i przynajmniej jednej C3-C8 olefiny, alfa, mającego gęstość mniejszą niż 0,900 g/cm3 i temperaturę topnienia mniejszą niż 85°C, trzecią warstwę zawierającą przynajmniej 80% wagowo kopolimeru EVOH mającego zawartość etylenu co najmniej 38% molowych i piątą warstwę zawierającą przynajmniej 30% pierwszego kopolimeru etylenu z przynajmniej jedną C4-C8 olefiną alfa, przy czym ten pierwszy kopolimer ma gęstość od 0,900 do 0,915 g/cm3 i wskaźnik topliwości niższy niż 1,0 dg/min i przynajmniej 10% drugiego kopolimeru etylenu z od 4 do 18% estru winylu lub akrylanu alkilowego i od 0 do 30% trzeciego kopolimeru etylenu i przynajmniej jednej C3-C8 olefiny alfa, mającego gęstość mniejszą niż 0,900 g/cm3 i temperaturę topnienia niższą niż 85°C.From the patent description PL186579 entitled "Multilayer plastic film used for packaging food products and method of making a multi-layer plastic film used for packaging food products", a multi-layer packaging film is known having at least five layers arranged in sequence and in contact with each other, which characterized in that it comprises a first layer constituting at least 50% by weight of a copolymer of propene and at least one alpha olefin selected from the group consisting of ethylene, butene-1, methylpentene-1, hexene-1, octene-1 and mixtures thereof, having a % of propene at least 60 wt.%, a second and fourth layer each containing at least 10% of a first ethylene copolymer and at least one C4-C8 alpha olefin, said copolymer having a density of 0.900 to 0.915 g / cm 3 and a melting index less than 1.0 dg / min and at least 10% of a second ethylene copolymer and 4 to 18% of vinyl ester or acrylate % alkyl and at least 10% anhydride-modified third copolymer of ethylene and at least one alpha olefin, vinyl ester or alkyl acrylate, and from 0 to 30% of a fourth ethylene copolymer and at least one C3-C8 alpha olefin, having a density less than 0.900 g / cm 3 and a melting point of less than 85 ° C, a third layer comprising at least 80% by weight of an EVOH copolymer having an ethylene content of at least 38 mole% and a fifth layer comprising at least 30% of a first ethylene copolymer with at least one C4-C8 alpha olefin, the first copolymer having a density of 0.900 to 0.915 g / cm 3 and a melting index lower than 1.0 dg / min and at least 10% of a second ethylene copolymer with 4 to 18% vinyl ester or alkyl acrylate and 0 to 30% of a third ethylene copolymer and at least one A C3-C8 alpha olefin, having a density less than 0.900 g / cm 3 and a melting point less than 85 ° C.

Celem wynalazku jest opracowanie folii wielowarstwowej o właściwościach barierowych powodujących, że uchwyt będzie bardzo dobrze się kleić do torby, jednakże nie będzie się w stosie produkcyjnym sklejać ze sobą, oraz będzie bardziej wytrzymały niż dotychczasowe rozwiązania.The aim of the invention is to develop a multilayer film with barrier properties that make the handle stick very well to the bag, but not stick together in the production stack, and more durable than the previous solutions.

Folia wielowarstwowa, w szczególności do formowania uchwytów toreb, zawierająca trzy warstwy polimerowe wykonane z polietylenu o małej, dużej i wysokiej gęstości, zawierające pigmenty barwiące, charakteryzuje się tym, że w układzie warstw A, C, B warstwa A zawiera od 28 do 32% polietylenu bez dodatków o małej gęstości 924 kg/m3, od 58 do 62% polietylenu małej gęstości 924 kg/m3 z dodatkiem żywic syntetycznych, organicznych i/lub nieorganicznych pigmentów, od 8A multilayer film, in particular for forming bag handles, containing three polymer layers made of low, high and high density polyethylene, containing color pigments, is characterized by the fact that in the A, C, B layer system, the A layer contains from 28 to 32% polyethylene without additives, low density 924 kg / m3 , from 58 to 62% low density polyethylene 924 kg / m3 with the addition of synthetic resins, organic and / or inorganic pigments, from 8

Claims (1)

PL 240 739 B1 do 12% polietylenu wysokiej gęstości 950 kg/m3, następnie warstwa B zawiera od 68 do 72% polietylenu bez dodatków o małej gęstości 924 kg/m3, od 28 do 32% polietylenu o niskiej gęstości 920 kg/m3, warstwa C zawiera od 58 do 62% polietylenu bez dodatków o małej gęstości 924 kg/m3, od 3 do 7% polietylenu wysokiej gęstości 950 kg/m3, od 18 do 22% polietylenu małej gęstości 924 kg/m3 z dodatkiem żywic syntetycznych, organicznych i/lub nieorganicznych pigmentów oraz od 13 do 17% polietylenu o niskiej gęstości 920 kg/m3.PL 240 739 B1 up to 12% high density polyethylene 950 kg / m3 , then layer B contains 68 to 72% polyethylene without additives, low density 924 kg / m3 , 28 to 32% low density polyethylene 920 kg / m3 3 , layer C contains from 58 to 62% low-density polyethylene 924 kg / m3 , from 3 to 7% high-density polyethylene 950 kg / m3 , from 18 to 22% low-density polyethylene 924 kg / m3 with with the addition of synthetic resins, organic and / or inorganic pigments and from 13 to 17% of polyethylene with a low density of 920 kg / m 3 . Poprzez zastosowanie układu warstw wielowarstwowej folii wedle opracowanego rozwiązania uzyskujemy materiał zapewniający wysokie właściwości plastyczne warstwy zewnętrznej (B), którą klei się do torby foliowej, jednocześnie ograniczając właściwości przylegające warstwy wewnętrznej (A).By using a system of layers of multilayer foil according to the developed solution, we obtain a material that ensures high plastic properties of the outer layer (B), which is glued to the foil bag, while limiting the adjacent properties of the inner layer (A). Wytworzona wielowarstwowa folia, w szczególności do formowania rączek toreb, zawierająca trzy warstwy polimerowe wykonane z polietylenu, składa się z trzech warstw, w układzie A, C, B, gdzie:The produced multilayer film, in particular for forming the handles of bags, containing three polymer layers made of polyethylene, consists of three layers, in the A, C, B configuration, where: A to warstwa zewnętrzna uchwytu, o właściwościach umiarkowanie klejących, B to warstwa wewnętrzna, którą przykleja się do torby o właściwościach dobrze klejących, C to warstwa środkowa sklejająca warstwy A i B. Warstwa A zewnętrzna przylegająca do warstwy A drugiej rączki posiada właściwości barierowe ograniczające przenikanie temperatury w procesie zgrzewania rączki z torbą. Warstwa B jest przyklejana do torby. Warstwa C centralna pomiędzy warstwami A i B, zapewnia idealne zespolenie warstw.A is the outer layer of the handle with moderate adhesive properties, B is the inner layer that sticks to the bag with good adhesive properties, C is the middle layer that sticks together layers A and B. The outer layer adjacent to the A layer of the other handle has barrier properties to limit penetration temperature in the process of welding the handle to the bag. Layer B is glued to the bag. The C layer, the central one between the A and B layers, ensures perfect bonding of the layers. Warstwy folii charakteryzuje następujący skład:The foil layers are characterized by the following composition: Warstwa A: przemiał brązowy LD - polietylen bez dodatków o małej gęstości 924 kg/m3 i MFR 1,9 g/10 min (190°C/2,16 kg) - 30%, odpad z nadrukiem LD - polietylen małej gęstości 924 kg/m3 i MFR 1,9 g/10 min (190°C/2,16 kg) oraz mieszanka żywic syntetycznych, organicznych i/lub nieorganicznych pigmentów - 60%, HDPE - polietylen wysokiej gęstości 950 kg/m3 i MFR 0,26 g/10 min (190°C/2,16 kg) - 10%,Layer A: brown milling LD - low-density polyethylene 924 kg / m3 and MFR 1.9 g / 10 min (190 ° C / 2.16 kg) - 30%, waste with print LD - low-density polyethylene 924 kg / m3 and MFR 1.9 g / 10 min (190 ° C / 2.16 kg) and a mixture of synthetic resins, organic and / or inorganic pigments - 60%, HDPE - high density polyethylene 950 kg / m3 and MFR 0.26 g / 10 min (190 ° C / 2.16 kg) - 10%, Warstwa B: przemiał brązowy LD - polietylen bez dodatków o małej gęstości 924 kg/m3 i MFR 1,9 g/10 min (190°C/2,16 kg) - 70%, odpad ze skrawek (mieszanka LD) - polietylen o niskiej gęstości 920 kg/m3 i MFR 1,7 g/10 min (190°C/2,16 kg) - 30%,Layer B: brown milling LD - low-density polyethylene 924 kg / m3 and MFR 1.9 g / 10 min (190 ° C / 2.16 kg) - 70%, scrap waste (LD mix) - polyethylene low density 920 kg / m3 and MFR 1.7 g / 10 min (190 ° C / 2.16 kg) - 30%, Warstwa C: przemiał brązowy LD - polietylen bez dodatków o małej gęstości 924 kg/m3 i MFR 1,9 g/10 min (190°C/2,16 kg) - 60%, HDPE - polietylen wysokiej gęstości'950 kg/m3 i MFR 0,26 g/10 min (190°C/2,16 kg) - 5%, odpad z nadrukiem LD - polietylen małej gęstości 924 kg/m3 i MFR 1,9 g/10 min (190°C/2,16 kg) oraz mieszanka żywic syntetycznych, organicznych i/lub nieorganicznych pigmentów - 20%, odpad ze skrawek (mieszanka LD) - polietylen o niskiej gęstości 920 kg/m3 i MFR 1,7 g/10 min (190°C/2,16 kg) - 15%.Layer C: brown milling LD - low-density polyethylene 924 kg / m3 and MFR 1.9 g / 10 min (190 ° C / 2.16 kg) - 60%, HDPE - high density polyethylene'950 kg / m 3 and MFR 0.26 g / 10 min (190 ° C / 2.16 kg) - 5%, waste with the print LD - low density polyethylene 924 kg / m 3 and MFR 1.9 g / 10 min (190 ° C / 2.16 kg) and a mixture of synthetic resins, organic and / or inorganic pigments - 20%, scrap waste (LD mix) - low-density polyethylene 920 kg / m3 and MFR 1.7 g / 10 min (190 ° C / 2.16 kg) - 15%. Zastrzeżenie patentowePatent claim 1. Folia wielowarstwowa, w szczególności do formowania uchwytów toreb, zawierająca trzy warstwy polimerowe wykonane z polietylenu o małej, dużej i wysokiej gęstości, zawierające pigmenty barwiące, znamienna tym, że w układzie warstw A, C, B warstwa A zawiera od 28 do 32% polietylenu bez dodatków o małej gęstości 924 kg/m3, od 58 do 62% polietylenu małej gęstości 924 kg/m3 z dodatkiem żywic syntetycznych, organicznych i/lub nieorganicznych pigmentów, od 8 do 12% polietylenu wysokiej gęstości 950 kg/m3, następnie warstwa B zawiera od 68 do 72% polietylenu bez dodatków o małej gęstości 924 kg/m3, od 28 do 32% polietylenu o niskiej gęstości 920 kg/m3, warstwa C zawiera od 58 do 62% polietylenu bez dodatków o małej gęstości 924 kg/m3, od 3 do 7% polietylenu wysokiej gęstości 950 kg/m3, od 18 do 22% polietylenu małej gęstości 924 kg/m3 z dodatkiem żywic syntetycznych, organicznych i/lub nieorganicznych pigmentów oraz od 13 do 17% polietylenu o niskiej gęstości 920 kg/m1. A multilayer film, in particular for forming bag handles, comprising three polymer layers made of low, high and high density polyethylene, containing color pigments, characterized in that in the A, C, B layer system, layer A comprises 28 to 32 % of low-density polyethylene 924 kg / m3 , from 58 to 62% of low-density polyethylene 924 kg / m3 with the addition of synthetic resins, organic and / or inorganic pigments, from 8 to 12% of high-density polyethylene 950 kg / m3 3 , then layer B contains from 68 to 72% polyethylene without low-density additives 924 kg / m3 , from 28 to 32% low-density polyethylene 920 kg / m3 , layer C contains from 58 to 62% polyethylene without additives o low density 924 kg / m3 , from 3 to 7% high density polyethylene 950 kg / m3 , from 18 to 22% low density polyethylene 924 kg / m3 with the addition of synthetic resins, organic and / or inorganic pigments and from 13 to 17% low density polyethylene 920 kg / m
PL426062A 2018-06-25 2018-06-25 Composition of multilayer foil, in particular for bag holder forming PL240739B1 (en)