PL190636B3 - Method of obtaining a filling material for abandoned mine workings from reaction wastes of a semi-dry flue gas desulphurisation process

Info

Publication number: PL190636B3
Application number: PL99332017A
Authority: PL
Inventors: Jolanta Kwiatkowska; Paweł Kwiatkowski
Original assignee: Jolanta Kwiatkowska; Kwiatkowski Pawel
Priority date: 1999-03-15
Filing date: 1999-03-15
Publication date: 2005-12-30
Also published as: PL332017A3

Abstract

A method of producing a stowing material to fill empty spaces in the underground parts of mines, from post-reaction wastes from the technology of semi-dry desulphurisation of combustion gases in the amount from 5 to 25 percent by weight mixed with 75-95 percent by weight of fly ash and 0.01-0.1 percent by weight of a flocculent and with 5-15 percent by weight of cement, according to patent PL 184692, characterised in that 25-40 percent by weight of post-reaction wastes is mixed with 60-75 percent by weight of fly ash, and further, the composition produced in such a manner is mixed with water in the proportion of ingredients of 1:3.

Description

Przedmiotem wynalazku jest sposób wytwarzania materiału podsadzkowego do wypełniania pustych przestrzeni w podziemiach kopalń, stanowiący ulepszenie sposobu według patentu głównego PL 184692.The subject of the invention is a method of producing a proppant material for filling voids in underground mines, which is an improvement of the method according to the main patent PL 184692.

Według patentu PL 184692 - sposób wytwarzania materiału podsadzkowego do wypełniania pustych przestrzeni w podziemiach kopalń z odpadów porekreacyjnych pochodzących z technologii półsuchego odsiarczania spalin i popiołów lotnych polega na tym, że 5 do 25% wagowych odpadów poreakcyjnych miesza się z 75 do 95% wagowych popiołów lotnych, a następnie tak wytworzoną mieszaninę miesza się z wodą w stosunku od 0,5:1 do 1:1 składników i w takiej postaci transportuje się ją rurociągami podsadzkowymi do miejsc zużycia. Do mieszaniny odpadów poreakcyjnych i popiołów lotnych można również dodać 0,01do 0,1% wagowych flokulanta przyspieszającego sedymentację lub 5 do 15% wagowych cementu, względnie obie te substancje jednocześnie.According to the patent PL 184692 - a method of producing a backfilling material for filling voids in the underground of mines from post-production waste from the semi-dry flue gas desulphurization technology and fly ash, 5 to 25% by weight of post-reaction waste is mixed with 75 to 95% by weight of fly ash and then the mixture prepared in this way is mixed with water in a ratio of 0.5: 1 to 1: 1 components and in such a form it is transported through backfilling pipelines to the places of consumption. It is also possible to add 0.01 to 0.1% by weight of a sedimentation accelerating flocculant or 5 to 15% by weight of cement, or both at the same time, to the mixture of post-reaction waste and fly ash.

Sposób według patentu głównego, jakkolwiek spełnia swoje zadanie ma tę niedogodność, że uniemożliwia wykorzystanie wszystkich parametrów technicznych materiałów odpadowych pochodzących z wapniowych metod odsiarczania spalin uzyskiwanych zarówno w czasie dwufazowego oczyszczania spalin jak i w czasie wykonywania tej operacji w jednym cyklu, to jest bez wstępnego oczyszczania spalin z pyłów lotnych za pomocą różnego rodzaju filtrów.The method according to the main patent, although fulfilling its task, has the disadvantage that it makes it impossible to use all technical parameters of waste materials derived from calcium flue gas desulphurization methods obtained both during two-phase flue gas cleaning and during this operation in one cycle, i.e. without preliminary flue gas cleaning. from volatile dust using various types of filters.

W praktyce bowiem okazało się, że w czasie odsiarczania spalin, bez wstępnego ich oczyszczania z pyłów lotnych, to znaczy w jednym cyklu, uzyskane odpady poreakcyjne stanowią mieszaninę zawierającą w swoim składzie zarówno popioły lotne jak i gips oraz inne składniki charakterystyczne dla materiału podsadzkowego otrzymywanego sposobem według patentu głównego i mają podobne parametry techniczne. Materiały te nie były jednak dotychczas wykorzystywane w granicach innych niż określono to w patencie głównym, co bardzo niekorzystnie wpływało na koszty podsadzki wytwarzanej tym sposobem.In practice, it turned out that during flue gas desulphurization, without the initial cleaning of flue dust, i.e. in one cycle, the obtained post-reaction waste is a mixture containing both fly ash and gypsum and other components characteristic of the proppant material obtained by the method. according to the main patent and have similar technical parameters. However, these materials have so far not been used within limits other than those specified in the main patent, which greatly adversely affects the cost of the proppant produced by this method.

Praktyczne doświadczenia dowodzą, że przy zachowaniu wymaganych parametrów technicznych, koszty wypełniania pustych przestrzeni w podziemiach kopalń można znacznie obniżyć jeżeli odpady poreakcyjne w ilości od 25 do 40% wagowych zmiesza się z popiołami lotnymi w ilości od 60 do 75% wagowych, a następnie tak uzyskaną kompozycję zmiesza się z wodą w stosunku do 1:3 składników, a najkorzystniej 1:1.Practical experience shows that, while maintaining the required technical parameters, the costs of filling voids in the underground mines can be significantly reduced if post-reaction waste in an amount of 25 to 40% by weight is mixed with fly ash in an amount of 60 to 75% by weight, and then the resultant the composition is mixed with water in a 1: 3 ratio of the ingredients, most preferably 1: 1.

Podobny efekt można również uzyskać jeżeli od 5 do 100% wagowych stałych odpadów otrzymywanych z wapniowych metod odsiarczania spalin w jednym cyklu zmiesza się z 0,01 do 0,1% wagowych flokulanta oraz z 5 do 15% wagowych cementu.A similar effect can also be obtained if 5 to 100% by weight of the solid waste obtained from calcium flue gas desulfurization methods in one cycle is mixed with 0.01 to 0.1% by weight of flocculant and with 5 to 15% by weight of cement.

190 636190 636

Tak wytworzony materiał nadaje się zarówno do podsadzki hydraulicznej stosowanej w podziemiach kopalń jak i do uszczelniania zrobów oraz do profilaktyki przeciwpożarowej i przeciwwybuchowej ponieważ materiał ten ma właściwości szybkiej konsolidacji i dobrego wypełniania wszystkich nawet najmniejszych szczelin w górotworze.The material produced in this way is suitable both for hydraulic backfilling used in mine undergrounds and for sealing goafs as well as for fire and explosion prevention, because this material has the properties of fast consolidation and good filling of all even the smallest gaps in the rock mass.

190 636190 636

Departament Wydawnictw UP RP. Nakład 50 egz. Cena 2,00 zł.Publishing Department of the UP RP. Circulation of 50 copies. Price PLN 2.00.

Claims

Patent claims

1. Method for the production of backfilling material for filling voids in underground mines from post-reaction waste from the semi-dry flue gas desulphurization technology in the amount of 5 to 25% by weight mixed with 75 to 95% by weight of fly ash and 0.01 to 0.1% by weight of flocculant and from 5 to 15% by weight of cement, according to the patent PL 184692, characterized in that 25 to 40% by weight of post-reaction waste is mixed with 60 to 75% by weight of fly ash, and then the composition obtained in this way is mixed with water in a ratio of 1: 3 ingredients.

2. The method according to p. The method of claim 1, characterized in that from 0.5 to 100% by weight of solid waste from calcium flue gas desulphurization methods, not purified of volatile dust, is mixed with water in a ratio of 1: 3 components.