OA19728A - Overhead electrical cables and method for fabricating same - Google Patents

Abstract

A bare overhead electrical cable and a method for the manufacture of an overhead electrical cable. The electrical cable includes a central strength member and at least two conductive layers surrounding the strength member, the two conductive layers being formed from first and second conductive strands respectively. The first conductive strands are formed from first aluminum material and the second conductive strands are formed from a second aluminum material, where the second aluminum material has at least one material property that is different than the same material property of the first aluminum material. For example, the second conductive strands may be formed from an aluminum material having a lower conductivity but higher hardness than the first aluminum material. Such a configuration may be useful when the overhead electrical cable is installed in a geographic region that is subject to heavy ice loading.

Description

OVERHEAD ELECTRICAL CABLES AND METHOD FOR FABRICATING SAME

FIELD

[0001] This disclosure relates to the field of overhead electrical cables for the transmission and distribution of electricity.

BACKGROUND

[0002] Overhead electrical cables for the transmission and distribution of electricity typically include a bare aluminum electrical conductor having sufficient diameter (e.g., cross-sectional area) to safely transmit electricity at high voltages. Although aluminum has a high ratio of conductivity to mass, some aluminum alloys are too weak to be selfsupporting when strung between support structures (e.g., between towers), leading to large sags, and a central strength member must be used to support the aluminum conductor. In a typical configuration, individual métal (e.g., aluminum) conductive strands are helically wound around and supported by the central strength member. When installed, the strength member bears the majority of the mechanical (e.g., tensile) load and is installed under high tensile loading. Traditionally, the strength member is comprised of a plurality of steel strands that are twisted together, a cable configuration referred to as aluminum conductor steel reinforced (ACSR). Recently, other materials hâve been utilized for the strength member, such as advanced fiber-reinforced composite materials having high tensile strength, low coefficient of thermal expansion (CTE) and other désirable thermal and mechanical properties.

[0003] One example of an overhead electrical cable having such a composite strength member is the ACCC® overhead electrical cable available from CTC Global Corporation of Irvine, CA, USA. See, for example, U.S. Patent No. Pat. No. 7,368,162 by Hiel et al, which is incorporated herein by reference in its entirety. The use of such composite strength members advantageously enables the use of high conductivity, fully annealed aluminum for the outer conductive strands. The modulus of elasticity of the carbon fibers used in the ACCC® composite strength member is higher than the modulus of steel (about

235 GPa for carbon fiber vs. about 200 GPa for steel). In the ACCC® strength member, however, an outer layer of glass fibers (elastic modulus of about 45.6 GPa) that surrounds the carbon results in a combined modulus of the ACCC® composite strength member of about GPa, lower than steel. This outer layer of glass fibers is used to improve impact résistance and increase conductorflexibility, and also serves to insulate the carbon fibers from the aluminum strands to prevent galvanic corrosion.

[0004] A number of design criteria go into the configuration of an overhead electrical cable, and the design criteria often dépend upon the local climate at the location where the electrical cable is deployed. For example, when the electrical cable is installed in cold climate areas where snow and ice events are common, ice may accumulate on the surface of the outer conductor under low-load or line-off conditions, when little or no current is flowing through a bare overhead electrical cable, due to a lack of heat that is normally présent under regular operating conditions. Electrical utilities in very heavy ice areas use an ice thickness of as much as 2 inches (50 mm) to calculate iced conductor weight. The added weight of ice accumulation will increase tension on the cable and may cause a significant increase in cable sag, i.e., an increase in the vertical distance between the support points and the lowest point of the cable. High voltage bare overhead electrical cables often traverse roadways, trees and/or lower voltage overhead electrical distribution cables. If these high voltage transmission cables become loaded with ice and sag too close to these objects, they become very dangerous and can lead to failures and the resulting power outages.

[0005] At the same time, the overhead electrical cables must also be able to safely transmit increased electrical loads (e.g., increased voltage) during the warmer summer months when electrical demands are at their highest. Such increased loads can raise the température of the cable (due to résistance heating), causing the cable to thermally expand (lengthen) and sag toward the ground, creating the same problems that may be experienced due to ice loading.

[0006] One solution to these problems is to utilize higher towers to support the cables. However, this solution cornes with an increased cost. Another solution to the ice loading problem is to utilize a strength member having a very high tensile strength, such as a strength memberof a fiber-reinforced composite, and to install the cable between support structures at a very high tension.

SUMMARY

[0007] Heavy ice loading can cause permanent élongation of an overhead electrical cable. As a resuit of an increase in cable tension due to the added weight of ice, the cable may be stretched beyond its initial yield point, which can prevent it from returning to its initial sag or tension condition after the ice is abated. The improved elasticity of fiber-reinforced composite strength member, such as the ACCC® strength member, allows the cable to return to its initial sag and tension condition after the ice load has dissipated.

[0008] There is a need for an overhead electrical cable having a composite strength member that is capable of use under both heavy ice loading conditions and under conditions of very high current, while providing the other benefits associated with the use of the composite strength member.

[0009] In one embodiment, such an overhead electrical cable is disclosed. The overhead electrical cable comprises a strength member and a first conductive layer surrounding the strength member, where the first conductive layer comprises strands of a first aluminum material. A second conductive layer surrounds the first conductive layer, where the second conductive layer comprises strands of a second aluminum material. The second aluminum material has at least one material property that is different than the same material property ofthe first aluminum material.

[0010] The foregoing overhead electrical cable may be characterized as having feature refinements and/or additional features, which may be implemented alone or in any combination. In one characterization, the different material property between the first and second aluminum materials is selected from the group of properties consisting of yield stress, elastic modulus, hardness, electrical conductivity and tensile strength. In one particular characterization, one different material property is yield stress. In one refinement, the second aluminum material has a yield stress that is greater than the yield stress of the first aluminum material. In another particular characterization, the different material property between the first and second aluminum materials is tensile strength. In one refinement, the second aluminum material has a tensile strength that is less than the tensile strength of the first aluminum material. In yet another characterization, the different material property between the first and second aluminum materials is electrical conductivity. In one refinement, the second aluminum material has an electrical conductivity that is greaterthan the electrical conductivity ofthe first aluminum material.

[0011] In another characterization, at least one of the first and the second aluminum materials has an electrical conductivity of at least about 60% IACS (International Annealed Copper Standard). In a further refinement, at least one of the first and the second aluminum materials has a conductivity of at least about 62% IACS. In yet a further refinement, the second aluminum material has an electrical conductivity of at least about 62% IACS. In another characterization, the second aluminum material is a 1350-0 annealed aluminum alloy. In yet another characterization, the first aluminum material is a hardened aluminum alloy. In another characterization, the first aluminum material is selected from an aluminum-zirconium (AlZr) aluminum alloy and a 1350-H19 aluminum alloy.

[0012] The conductive strands may hâve a variety of cross-sections, including circular, oval and polygonal. In one characterization, at least one ofthe first aluminum material strands and the second aluminum material strands are trapézoïdal strands. In a further refinement, both of the first aluminum material strands and the second aluminum material strands are trapézoïdal strands. The overhead electrical cable may comprise more than two layers of conductive strands. In one characterization, the overhead electrical cable comprises a third conductive layer disposed between the first conductive layer and the second conductive layer. In one refinement, the third conductive layer includes conductive strands of a third aluminum material that is different than the first aluminum material and different than the second aluminum material. In another refinement, the third conductive layer comprises strands of the first aluminum material. In yet another refinement, the third conductive layer comprises strands of the second aluminum material. In yet another characterization, the overhead electrical cable comprises at least a fourth conductive layer disposed between the third conductive layer and the second conductive layer.

[0013] In another characterization, the strength member comprises a fiber-reinforced composite strength element. In one refinement, the fiber-reinforced composite strength element comprises substantially continuous reinforcing carbon fibers disposed in a binding matrix. In another refinement, the strength member has a diameter of not greater than about 30 mm. In a further refinement, the strength member has a diameter of at least about 3 mm. In another characterization, the strength member has an ultimate tensile strength (UTS) of at least about 1700 MPa.

[0014] In another embodiment, a method for the manufacture of an overhead electrical cable is disclosed. The method includes the steps of wrapping a plurality of first strands of a first aluminum material onto a strength member to form a first conductive layer, and wrapping a plurality of second strands of a second aluminum material around the first conductive layer to form a second conductive layer. The second aluminum material has at least one material property having a value that is different than a value of the same material property of the first aluminum material.

[0015] The foregoing method may be characterized as having refinements and/or additional steps, which may be implemented alone or in any combination. In one characterization, the plurality of first strands of the first aluminum material hâve a trapézoïdal cross-section. In one refinement, the plurality of second strands of the second aluminum material hâve a trapézoïdal cross-section.

[0016] In another characterization, the method comprises wrapping a plurality of third strands of a third aluminum material around the first conductive layer before the wrapping of the second conductive strands around the first conductive layer. In a further refinement, the method includes the step of wrapping a plurality of fourth strands of a fourth aluminum material around the first conductive layer before the wrapping of the third conductive strands around the first conductive layer.

[0017] In another embodiment, a method for the installation of an electrical transmission line is disclosed. The method includes the steps of stringing an overhead electrical cable between at least two support structures and applying tension to the overhead electrical cable. While the overhead electrical cable is under the applied tension, first and second ends of the overhead electrical cable are clipped such that the overhead electrical cable is at least partially supported by the two support structures and is strung at a clipped-in tension. The overhead electrical cable comprises, a strength member, a first conductive layer surrounding the strength member, the first conductive layer comprising strands of a first aluminum material, and a second conductive layer surrounding the first conductive layer, the second conductive layer comprising conductive strands of a second aluminum material that is different than the first aluminum material, wherein the second aluminum material has at least one material property that is different that the same material property of the first aluminum material.

DESCRIPTION OF THE DRAWINGS

[0018] FIG. 1 illustrâtes a schematic view of an overhead electrical cable according to an embodiment of the présent disclosure.

[0019] FIG. 2 illustrâtes a schematic view of an overhead electrical cable according to an embodiment of the présent disclosure.

[0020] FIG. 3 illustrâtes a schematic view of an overhead electrical cable according to an embodiment of the présent disclosure.

[0021] FIG. 4 illustrâtes a schematic view of an overhead electrical cable according to an embodiment of the présent disclosure.

DESCRIPTION OF THE EMBODIMENTS

[0022] In one embodiment, a bare overhead electrical cable is disclosed. The overhead electrical cable includes a strength member, a first conductive layer surrounding the strength member, and a second conductive layer surrounding the first conductive layer. The first conductive layer includes strands of a first conductive material, and the second conductive layer comprises strands of a second conductive material. The second conductive material has at least one material property that is different than (e.g., has a different value than) the same material property of the first conductive material.

[0023] FIG. 1 illustrâtes a schematic cross-section of an overhead electrical cable 100 according to an embodiment of the présent disclosure. As illustrated in FIG. 1, the strength member 110 includes seven individual strength éléments 112 (e.g., rods) that are combined (e.g., helically wrapped) to form the strength member 110. The strength éléments 112 may be fabricated from steel, in which case the electrical cable 100 would be referred to as an ACSR (aluminum conductor steel reinforced) conductor. Altematively, the strength éléments 112 may be fabricated from a composite material, such as a composite material including structural (e.g., reinforcing) fibers disposed in a binding matrix i.e., where the matrix binds the structural fibers together to form the composite material. Examples of such composite materials are discussed in detail below.

[0024] The first conductive strands 126 and the second conductive strands 128 are fabricated from an electrically conductive material, particularly a métal such as copper or aluminum. For bare overhead electrical cables, aluminum is generally preferred due to its good conductivity and low density (e.g., light weight). As is discussed in more detail below, according to one embodiment, the first conductive layer 120 includes strands 126 of a first aluminum material, and the second conductive layer 122 includes strands 128 of a second aluminum material, where the second aluminum material has at least one material property that is different than (e.g., has a different value than) the same material property ofthe first aluminum material.

[0025] FIG. 2 schematically illustrâtes another configuration for an overhead electrical cable 200. As illustrated in FIG. 2, the strength member 210 also includes seven individual strength éléments 212 that are combined (e.g., helically wrapped) to form the strength member 210, in a manner similar to the embodiment of FIG. 1. The strength éléments 212 may be fabricated from, for example, steel or a reinforced composite, as is discussed with respect to FIG. 1. The first conductive strands 226 and the second conductive strands 228 are also fabricated from an electrically conductive material, as is discussed with respect to FIG. 1. As is discussed in more detail below, according to one embodiment, the first conductive layer 220 includes strands 226 of a first aluminum material, and the second conductive layer 222 includes strands 228 of a second aluminum material that has at least one material property that is different than the same material property of the first aluminum material. The embodiment illustrated in FIG. 2 differs from the embodiment in FIG. 1 in that the conductive strands 226/228 hâve a polygonal (e.g., trapézoïdal) cross-section. The use of such a polygonal cross-section enables a higher density conductive layer 220/222 to be formed. That is, there are substantially no air gaps between adjacent conductive strands either in the same conductive layer or between the conductive layers. This enables the outer diameter of the overhead electrical cable 200 to be reduced (e.g., to be smaller) than if round conductive strands are used (FIG. 1) for the same effective amount of aluminum. The smaller outer diameter may reduce the amount of ice weight on the overhead cable during an ice loading event. That is, the same thickness of ice on an overhead cable that is 0.8 inches in diameter vs a cable that is 1 inch in diameter will produce less ice weight, and less tension, on the overhead cable.

[0026] FIG. 3 schematically illustrâtes yet another configuration for an overhead electrical cable 300. As illustrated in FIG. 3, the first conductive strands 326 of the first conductive layer 320 and the second conductive strands 328 of the second conductive layer 322 are also fabricated from an electrically conductive material, as is discussed with respect to FIG. 1, particularly aluminum. The strands 326/328 hâve a trapézoïdal crosssection as is discussed with respect to FIG. 2. Similarly, the first conductive layer 320 includes strands 326 of a first aluminum material, and the second conductive layer 322 includes strands 328 of a second aluminum material.

[0027] As illustrated in FIG. 3, the strength member 310 includes a single strength element 312. The single strength element 312 may be fabricated from, for example, a reinforced composite material, as is discussed with respect to FIG. 1. The embodiment illustrated in FIG. 3 particularly includes a single strength element 312 having an inner core 314 and an outer layer 316 surrounding the inner core 314. Such a strength element may include, for example, an inner core including high strength carbon fibers and an outer layer comprising glass fibers, a configuration referred to as ACCC® and available from CTC Global Corp., Irvine, CA, USA. See U.S. Patent No. 7,368,162 by Hiel et al., noted above.

[0028] FIG. 4 schematically illustrâtes yet another configuration for an overhead electrical cable 400. As illustrated in FIG. 4, the first conductive strands 426 of the first conductive layer 420 and the second conductive strands 428 of the second conductive layer 422 are also fabricated from an electrically conductive material, as is discussed with respect to FIG. 1, particularly aluminum, and hâve a trapézoïdal cross-section as is discussed with respect to FIG. 2. Similarly, the first conductive layer 420 includes strands 426 of a first aluminum material, and the second conductive layer 422 includes strands 428 of a second aluminum material that is different than the first aluminum material. The strength member 410 includes a single strength element 412 as is discussed with respect to FIG. 3.

[0029] As illustrated in FIG. 4, the overhead electrical cable 400 includes a third conductive layer 424 that includes conductive strands 430 (e.g., third conductive strands). The third conductive layer 424 surrounds the strength member 410 and surrounds the first conductive layer 420. Characterized another way, the third conductive layer 424 is disposed between the first conductive layer 420 and the second conductive layer 422. The third conductive layer 424 may advantageously increase the ampacity of the overhead electrical able, e.g., for purposes of high voltage transmission by providing additional conductor cross-section, e.g., as compared to the embodiment illustrated in FIG. 3. The third conductive strands 430 may be fabricated from the same conductive material as the first conductor strands 426, may be fabricated from the same conductive material as the second conductive strands 428, or may be fabricated from a conductive material that has at least one material property that is different (e.g., has a different value than) than the same material property ofthe first conductive strands 426 and the second conductive strands 428.

[0030] The configurations for an overhead electrical cable illustrated in FIGS. 1-4 are for exemplary purposes, and the overhead electrical cables of the présent disclosure are not limited to those particular configurations. For example, another configuration may include a single element strength member as illustrated in FIG. 3 with round conductor strands as illustrated in FIG. 1. Other configurations will be apparent to one of skill in the art.

[0031] According to the présent disclosure, at least one material property of the conductive strands in one conductive layer are different than (e.g., hâve a different value than) the same material property of the conductive strands in another conductive layer. That is, the conductive (e.g., metallic) materials from which the respective conductive strands are formed may hâve a different Chemical composition (e.g., may be a different alloy), and/or may hâve been processed in a manner that results in a different material property. For example, heat treatment (e.g., annealing) of some metallic materials may produce a conductive strand with different properties compared to a conductive strand of the same material (same Chemical composition) that has not been heat treated. Similarly, work hardening of an alloy with the same Chemical composition may resuit in different mechanical properties.

[0032] By way of example, the material property that is different among the conductive strands may be one or more of yield stress, elastic modulus, hardness, tensile strength and electrical conductivity. In one particular embodiment, the at least one material property that is different among the conductive strands is the yield stress. The elastic modulus (i.e., Young's Modulus) is the tensile elasticity ofthe conductive strand, i.e., the ratio of tensile stress to tensile strain. As the material is subjected to a tensile stress, the material will begin to yield (plastically deform) at some tensile stress, and this point is called the yield stress. Different aluminum alloys and different tempers among similar alloys may hâve different yield stresses. In one particular characterization, the yield stress of an outer conductive layer (e.g., of the outer layer strands) is greater than the yield stress of an inner conductive layer (e.g., than the inner layer strands). That is, when a tensile stress is applied to the conductive layers, an inner conductive layer will plastically deform (yield) before plastic deformation of the outer conductive layer. For example, referring to FIG. 1, the (outer) conductive strands 128 may hâve a higher yield stress than the (inner) conductive strands 126. Similarly, in FIGS. 2 and 3, the conductive strands 228/328 may hâve a higher yield stress than the conductive strands 226/326. In the embodiment of FIG. 4, the conductive strands 426 of the first conductive layer 420 may hâve a loweryield stress than the conductive strands 428 ofthe second conductive layer 422. The intermediate third conductive layer 424 may include strands 430 of a material having a yield stress that is higher than or substantially the same as the strands 426 of the first conductive layer 420. Further, the intermediate third conductive layer 424 may include strands 430 of a material having a yield stress that is the same as or less than the yield stress of the conductive strands 428 in the second conductive layer 422.

[0033] In another characterization, one material property that is different among certain conductive strands is tensile strength. In one particular characterization, an outmost conductive layer has a tensile strength that is greater than the tensile strength of an inner conductive layer. For example, referring to FIG. 1, the (outer) conductive strands 128 may hâve a higher tensile strength than the (inner) conductive strands 126. Similarly, in FIGS. 2 and 3, the conductive strands 228/328 may hâve a tensile strength that is higher than or substantially the same as the conductive strands 226/326. In the embodiment of FIG. 4, the conductive strands 426 of the first conductive layer 420 may hâve a lower tensile strength than the conductive strands 428 of the second conductive layer 422. The intermediate third conductive layer 424 may include strands 430 of a material having a tensile strength that is higher than the tensile strength of the strands 426 of the first conductive layer 420. Further, the intermediate third conductive layer 424 may include strands 430 of a material having a tensile strength that is the same as or less than the tensile strength of the conductive strands 428 in the second conductive layer 422. For the conductive strands having a higher tensile strength, aluminum alloys such as 6201-T81 and 6101 may be used, for example.

[0034] Table I illustrâtes the conductivity, tensile strength, yield stress and maximum (continuous) operating température for several aluminum materials.

Table I - Aluminum Conducting Materials

Description	Name	Conductivity (% IACS)	Tensile Strength (MPa)	Approximate Yield Stress (MPa)	Max. Operating Temp. (°C)
Hard Drawn	1350-H19	61	160-200	165	90
MS Alloy	5005-H19	53.3	250	190	90
MS Alloy	6101	53.5	295	200	90
HS Alloy	6201-T81	52.5	305-315	270	90
MS Alloy	6201-T83	57.5	250	200	90
Fully Annealed	1350-0	63	60-95	25-30	250
Thermal Résistant	TAL (AT1)	60	159-169	150	150
HS Thermal Résistant	KTAL (AT2)	55	225 - 248	200	150
Ultra-Thermal Résistant	ZTAL/UTAL (AT3)	60	159-176	150	210
Extra Thermal Résistant	XTAL (AT4)	58	159-169	150	230

[0035] In another characterization, one material property that is different among certain conductive strands is hardness. Hardness is a measure of localized résistance to plastic deformation, e.g., from mechanical indentation or abrasion. In one particular 5 characterization, an outmost conductive layer has a hardness that is greater than the hardness of an inner conductive layer. For example, referring to FIG. 1, the (outer) conductive strands 128 may hâve a higher hardness than the (inner) conductive strands 126. Similarly, in FIGS. 2 and 3, the conductive strands 228/328 may hâve a hardness that is higher than or substantially the same as the conductive strands 226/326. In the 10 embodiment of FIG. 4, the conductive strands 426 of the first conductive layer 420 may hâve a lower hardness than the conductive strands 428 of the second conductive layer 422. The intermediate third conductive layer 424 may include strands 430 of a material having a hardness that is higher than the hardness of the strands 426 of the first conductive layer 420. Further, the intermediate third conductive layer 424 may include strands 430 of a material having a hardness that is the same as or less than the hardness of the conductive strands 428 in the second conductive layer 422. For the conductive strands having a higher hardness, hardened aluminum alloys such as an aluminumzirconium (AlZr) alloy or a 1350-H19 aluminum alloy may be used.

[0036] In another characterization, one material property that is different among certain conductive strands is electrical conductivity. In one particular characterization, an outmost conductive layer has an electrical conductivity that is greater than the electrical conductivity of an inner conductive layer. For example, referring to FIG. 1, the (outer) conductive strands 128 may hâve a higher electrical conductivity than the (inner) conductive strands 126. Similarly, in FIGS. 2 and 3, the conductive strands 228/328 may hâve an electrical conductivity that is higher than or substantially the same as the conductive strands 226/326. In the embodiment of FIG. 4, the conductive strands 426 of the first conductive layer 420 may hâve a lower electrical conductivity than the conductive strands 428 ofthe second conductive layer 422. The intermediate third conductive layer 424 may include strands 430 of a material having an electrical conductivity that is higher than the electrical conductivity of the strands 426 of the first conductive layer 420. Further, the intermediate third conductive layer 424 may include strands 430 of a material having an electrical conductivity that is the same as or less than the electrical conductivity of the conductive strands 428 in the second conductive layer 422. In any of the foregoing configurations, the conductive strands having a higher electrical conductivity may be fabricated from aluminum having a conductivity of at least about 60% IACS, such as at least about 62% IACS. In one particular characterization, the conductive strands having a higher electrical conductivity may be fabricated from an annealed aluminum alloy, such as a 1350-0 annealed aluminum alloy. In another characterization, the lower conductivity strands (e.g., conductive strands 326 in FIG. 3) may be fabricated from AlZr alloys, such the thermal résistant AlZr alloys listed in Table I.

[0037] As is discussed above with respect to the figures, the overhead electrical cable includes a strength member around which the conductive layers are wrapped. The strength member may include a plurality of strength éléments (e.g., FIGS. 1 and 2), or may include a single strength element (e.g., FIGS. 3 and 4). The strength element(s) may be comprised of a métal such as steel, or may be comprised of other materials such as fiber-reinforced composites. Such composites may include reinforcing fibers disposed in a binding matrix. The reinforcing fibers may be substantially continuous reinforcing fibers that extend along the length of the strength member, and/or may include short reinforcing fibers (e.g., fiber whiskers or chopped fibers) that are dispersed through the binding matrix. The fibers may be selected from a wide range of materials, including but not limited to, carbon, glass, boron, métal oxides, métal carbides, high-strength polymers such as aramid fibers or fluoropolymer fibers, basait fibers and the like. The matrix material may include, for example, a plastic (e.g., polymer) such as a thermoplastic polymer or a thermoset polymer. The matrix may also be a metallic matrix, such as an aluminum matrix. One example of an aluminum matrix composite strength member is illustrated in U.S. Patent No. 6,245,425 by McCullough et al., which is incorporated herein by reference in its entirety.

[0038] One particular example of such a fiber-reinforced composite strength member is used in the ACCC® overhead electrical cable that is manufactured by CTC Global Corporation of Irvine, CA, USA. Such an overhead electrical cable is illustrated, for example, in U.S. Pat. No. 7,368,162 by Hiel et al.. This strength member includes a highstrength carbon fiber inner core surrounded by a glass fiber layer to provide improved flexibility, and to provide résistance to galvanic corrosion of the aluminum conductor by shielding the carbon fibers from the aluminum. FIGS. 3 and 4 illustrate the use of such a composite material as a single-element strength member. The use of a single-element strength member (FIGS. 3 and 4) may enable the strength member to hâve a decreased diameter, e.g., as compared to a multi-element strength member (FIGS. 1 and 2) for the same tensile properties, e.g., for the same tensile strength.

[0039] In one characterization, the strength member has a diameter of at least about 3 mm, such as at least about 5 mm. Such a strength member can advantageously hâve a high tensile strength when fabricated using, e.g., high strength carbon fibers. For example, the strength member may hâve an ultimate tensile strength (UTS) of at least about 1700 MPa, such as at least about 1800 MPa, at least about 1900 MPa, or even at least about 2000 MPa. In another characterization, the strength member has a rated breaking strength of at least about 100 kN, such as at least about 125 kN, or even at least about 150 kN.

[0040] The configuration of the conductive (e.g., aluminum) strands disclosed herein may be particularly useful in régions that expérience heavy ice loading. In this regard, to further reduce the effects of ice loading, the overhead electrical cable may utilize a strength member having a large diameter and/or a very high tensile strength. In one characterization, the strength member has a diameter of at least about 8 mm, such as at least about 9 mm, or even at least about 10 mm. As a practical matter, e.g., for storage and transportation, the diameter of the strength member will not be greater than about 30 mm, such as not greater than about 20 mm. In another characterization, the strength member has an ultimate tensile strength (UTS) of at least about 2200 MPa, such as at least about 2300 MPa, such as at least about 2400 MPa, or even at least about 2500 MPa. Although not limited to any particular maximum UTS, the UTS will typically be not greater than about 3700 MPa. In another characterization, the strength member has a rated breaking strength of at least about 150 kN, such as at least about 160 kN, at least about 170 kN, or even at least about 180 kN.

[0041] Overhead cables that use a fiber-reinforced composite strength member hâve a thermal knee-point. Initially, the tensile load of an installed cable is shared by the strength member and the conductive strands. As the cable’s température rises with increased current, the coefficient of thermal expansion (GTE) of the conductive strands causes them to elongate faster than the lower GTE strength member. As température increases, the conductive strands relax and transfer their tensile load to the strength member. The apex of this transfer is referred to as the thermal knee-point. Because the CTE of the strength member is lower than the GTE of the conductive strands, conductor sag above the thermal knee-point decreases. The ACCC conductor's lower CTE and lower thermal knee-point may reduce thermal sag, i.e., sag due to thermal expansion of the cable.

[0042] A strength member having a very high tensile strength, such as in the ACCC® configuration, enables the use of conductive strands of fully annealed aluminum. Fully annealed aluminum has a higher conductivity than non-annealed aluminum, and therefore can increase ampacity and reduce line losses. However, fully annealed aluminum lacks in some physical properties. For example, the use of fully annealed aluminum may resuit in increased line sag under static loads (e.g., ice loading) since only a relatively small tensile strain will plastically deform the aluminum, reducing tension in the conductor. In one configuration, the overhead electrical cable includes an inner conductive layer of an annealed aluminum and an outer conductive layer of a harder aluminum, such as an Al-Zr alloy. For example, referring to FIG. 3, the strands 326 of the first conductive layer 320 may be formed from a fully-annealed aluminum, and the strands 328 of the second conductive layer 322 may be fabricated from a harder aluminum such as an Al-Zr alloy. The use of an inner layer of high conductivity aluminum and an outer layer of higher hardness aluminum may advantageously provide a high overall conductivity (high ampacity) while reducing mechanical sag, such as from ice loading. This is due to the larger strain range of the harder aluminum in which it eIasticaIly deforms. Altematively, the electrical cable may include a high hardness layer on the inner conductive layer and the high conductivity annealed aluminum on the outer conductivity layer. However, placement of the harder aluminum on the outer layer may provide the additional benefits of higher abrasion résistance.

[0043] The présent disclosure also relates to methods for the fabrication of an overhead electrical cable, e.g., for the fabrication of an overhead electrical cable as described in any of the embodiments above. In one example, a method for the manufacture of an overhead electrical cable is disclosed, comprising the steps of first wrapping a plurality of conductive strands of a first aluminum material onto a strength member to form a first conductive layer, and second wrapping a plurality of conductive strands of a second aluminum material onto the first conductive layer to form a second conductive layer. The second aluminum material has at least one material property having a property value that is different than the property value of the same material property ofthe first aluminum material.

[0044] The présent disclosure also relates to methods for the installation of an electrical transmission line. In one embodiment, the method includes the steps of stringing an overhead electrical cable between at least two support structures, applying tension to the overhead electrical cable, and while the overhead electrical cable is under the applied tension, clipping first and second ends ofthe overhead electrical cable such that the overhead electrical cable is at least partially supported by the two support structures. The overhead electrical cable includes a strength member, a first conductive layer surrounding the strength member, the first conductive layer comprising conductive strands of a first aluminum material, and a second conductive layer surrounding the first conductive layer, the second conductive layer comprising conductive strands of a second aluminum material that is different than the first aluminum material. The second aluminum material has at least one material property that is different that the same material property ofthe first aluminum material.

[0045] The present disclosure also relates to an overhead electrical transmission line comprising an overhead electrical cable. The overhead electrical cable is strung under high tension onto at least two support towers. The overhead electrical cable includes a strength member, a first conductive layer surrounding the strength member, the first conductive layer comprising conductive strands of a first aluminum material, and a second conductive layer surrounding the first conductive layer, the second conductive layer comprising conductive strands of a second aluminum material that is different than the first aluminum material. The second aluminum material has at least one material property that is different that the same material property of the first aluminum material.

[0046] While various embodiments of an overhead electrical cable, a method for making an overhead electrical cable, a method for the installation of an electrical transmission line and an overhead electrical transmission line hâve been described in detail, it is apparent that modifications and adaptations of those embodiments will occur to those skilled in the art. However, it is to be expressly understood that such modifications and adaptations are within the spirit and scope ofthe present disclosure.

Claims (34)

1. What is Claimed is:

   1. An overhead electrical cable, comprising:

   a strength member;

   a first conductive layer surrounding the strength member, the first conductive layer comprising strands of a first aluminum material; and a second conductive layer surrounding the first conductive layer, the second conductive layer comprising strands of a second aluminum material, wherein the second aluminum material has at least one material property that is different than the same material property of the first aluminum material.
2. 2. The overhead electrical cable recited in Claim 1, wherein the at least one material property is selected from the group of properties consisting of yield stress, elastic modulus, hardness, electrical conductivity and tensile strength.
3. 3. The overhead electrical cable recited in Claim 2, wherein the at least one material property is yield stress.
4. 4. The overhead electrical cable recited in Claim 3, wherein the second aluminum material has a yield stress that is greater than a yield stress of the first aluminum material.
5. 5. The overhead electrical cable recited in Claim 2, wherein the at least one material property is tensile strength.
6. 6. The overhead electrical cable recited in Claim 5, wherein the second aluminum material has a tensile strength that is less than a tensile strength of the first aluminum material.
7. 7. The overhead electrical cable recited in Claim 2, wherein the at least one material property is electrical conductivity.
8. 8. The overhead electrical cable recited in Claim 7, wherein the second aluminum material has an electrical conductivity that is greater than the electrical conductivity ofthe first aluminum material.
9. 9. The overhead electrical cable recited in Claim 1, wherein the second aluminum material has an electrical conductivity of at least about 60% IACS.
10. 10. The overhead electrical cable recited in any of the previous claims, wherein the second aluminum material has a conductivity of at least about 62% IACS.
11. 11. The overhead electrical cable recited in any of the previous claims, wherein the second aluminum material is a 1350-0 annealed aluminum alloy.
12. 12. The overhead electrical cable recited in any of the previous claims, wherein the first aluminum material is a hardened aluminum alloy.
13. 13. The overhead electrical cable recited in any of the previous claims, wherein the first aluminum material is selected from an aluminum-zirconium (AlZr) aluminum alloy and a 1350-H19 aluminum alloy.
14. 14. The overhead electrical cable recited in any of the previous claims, wherein at least one of the strands of the first aluminum material and the strands of the second aluminum material are trapézoïdal strands.
15. 15. The overhead electrical cable recited in any of the previous claims, wherein both of the strands of the first aluminum material and the strands of the second aluminum material are trapézoïdal strands.
16. 16. The overhead electrical cable recited in any of the previous claims, further comprising a third conductive layer disposed between the first conductive layer and the second conductive layer.
17. 17. The overhead electrical cable recited in Claim 16, wherein the third conductive layer comprises strands of a third aluminum material that is different than the first aluminum material and different than the second aluminum material.
18. 18. The overhead electrical cable recited in Claim 16, wherein the third conductive layer comprises strands of the first aluminum material.
19. 19. The overhead electrical cable recited in Claim 16, wherein the third conductive layer comprises strands of the second aluminum material.
20. 20. The overhead electrical cable recited in any one of Claims 16 to 19, further comprising a fourth conductive layer disposed between the third conductive layer and the second conductive layer.
21. 21. The overhead electrical cable recited in any ofthe previous claims, wherein the strength member comprises a fiber-reinforced composite strength element.
22. 22. The overhead electrical cable recited in Claim 21, wherein the fiberreinforced composite strength element comprises substantially continuous reinforcing carbon fibers disposed in a binding matrix.
23. 23. The overhead electrical cable recited in any one of Claims 21 to 22, wherein the strength member has a diameter of not greater than about 30 mm.
24. 24. The overhead electrical cable recited in any one of Claims 21 to 23, wherein the strength member has a diameter of at least about 3 mm.
25. 25. The overhead electrical cable recited in any ofthe previous claims, wherein the strength member has an ultimate tensile strength (UTS) of at least about 1700 MPa.
26. 26. The overhead electrical cable recited in any one of Claims 21 to 25, wherein the strength member has an ultimate tensile strength (UTS) of not greater than about 3700 MPa.
27. 27. A method for the manufacture of an overhead electrical cable, comprising the steps of:

    wrapping a plurality of first strands of a first aluminum material onto a strength member to form a first conductive layer; and wrapping a plurality of second strands of a second aluminum material around the first conductive layer to form a second conductive layer, wherein the second aluminum material has at least one material property having a value that is different than a value of the same material property of the first aluminum material.
28. 28. The method recited in Claim 27, wherein the plurality of first strands of the first aluminum material hâve a trapézoïdal cross-section.
29. 29. The method recited in Claim 28, wherein the plurality of second strands of the second aluminum material hâve a trapézoïdal cross-section.
30. 30. The method recited in any one of Claims 27 to 29, further comprising the step of wrapping a plurality of third strands of a third aluminum material around the first conductive layer before the wrapping of the second conductive strands around the first conductive layer.
31. 31. The method recited in Claim 30, further comprising the step of wrapping a plurality of fourth strands of a fourth aluminum material around the first conductive layer before the wrapping ofthe third conductive strands around the first conductive layer.
32. 32. A method for the installation of an electrical transmission line, comprising the steps of:

    stringing an overhead electrical cable between at least two support structures;

    applying tension to the overhead electrical cable;

    while the overhead electrical cable is under the applied tension, clipping first and second ends ofthe overhead electrical cable such that the overhead electrical cable is at least partially supported by the two support structures and is strung at a clipped-in tension;

    wherein the overhead electrical cable comprises, a strength member;

    a first conductive layer surrounding the strength member, the first conductive layer comprising strands of a first aluminum material; and a second conductive layer surrounding the first conductive layer, the second conductive layer comprising conductive strands of a second aluminum material that is different than the first aluminum material, wherein the second aluminum material has at least one material property that is different that the same material property of the first aluminum material.
33. 33. The method recited in Claim 32, wherein the overhead electrical cable is defined in any one of Claims 1 to 26.
34. 34. An overhead electrical transmission line, comprising:

    at least two support structures;

    5 at least a first electrical cable supported by the support structures, wherein the first electrical cable is defined in any one of Claims 1 to 26.