OA18804A - Threaded Joint for pipe and manufacturing method of threaded Joint for pipe. - Google Patents
Threaded Joint for pipe and manufacturing method of threaded Joint for pipe. Download PDFInfo
- Publication number
- OA18804A OA18804A OA1201800228 OA18804A OA 18804 A OA18804 A OA 18804A OA 1201800228 OA1201800228 OA 1201800228 OA 18804 A OA18804 A OA 18804A
- Authority
- OA
- OAPI
- Prior art keywords
- plating layer
- pipe
- threaded connection
- tube
- box
- Prior art date
Abstract
The present invention has an objective to provide a threaded connection for pipe or tube including a pin and a box, having excellent galling resistance, torque property, and anticorrosion property, and still having an excellent adhesiveness with a lubricating coating even when being repeatedly exposed to high temperature and very low temperature, and to provide a method for producing the threaded connection for pipe or tube. The threaded connection for pipe or tube according to the present embodiment includes a pin (3) and a box (6). The pin (3) and the box (6) have contact surfaces including a thread portions (4) and (5) and unthreaded métal contact portions (8) and (10), respectively. The threaded connection for pipe or tube comprises an electroplating layer consisting of a Zn-Ni alloy, a mechanical plating layer consisting of Zn or a Zn alloy, and a lubricating coating, on the contact surface of at least one of the pin (3) and the box (6), in this order from a contact surface side.
Description
DESCRIPTION
TITLE OF INVENTION: THREADED JOINT FOR PIPE AND MANUFACTURING METHOD OF THREADED JOINT FOR PIPE
TECHNICAL FIELD
The présent invention relates to a threaded connection for pipe or tube and a method for producing a threaded connection for pipe or tube.
BACKGROUND ART
For drilling an oil field or a natural gas field, oil country tubular goods are used. In proportion to the depth of a well, multiple Steel pipes are coupled to form the oil country tubular goods. Coupling the Steel pipes is conducted by fastening threaded connections for pipe or tube formed at end portions of the Steel pipes. The Steel pipes are drawn up and loosened for inspection or the like, and after the inspection, the pipes are fastened again and reused.
A threaded connection for pipe or tube includes a pin and a box. The pin has, on an outer peripheral surface of a front end portion of a Steel pipe, a contact surface including an external thread portion and an unthreaded métal contact portion. The box has, on an inner peripheral surface of a front end portion of a steel pipe, a contact surface including an internai thread portion and an unthreaded métal contact portion. The thread portions and the unthreaded métal contact surfaces of the pin and the box repeatedly receive strong friction in fastening (making-up) and loosening (breakingout) Steel pipes. If these portions do not hâve a sufficient durability against friction, galling (unrepairable seizure) occurs when fastening and loosening are repeated. Therefore, a sufficient durability against friction, namely, excellent galling résistance is needed for a threaded connection for pipe or tube.
In conventional practices, to improve galling résistance, a compound grease called dope, containing heavy metals, has been used. By applying the compound grease on the surface of a threaded connection for pipe or tube, the galling résistance of the threaded connection for pipe or tube can be improved. However, heavy metals such as Pb, Zn, and Cu contained in the compound grease may exert an influence on the environment. For this reason, the development of a threaded connection for pipe or tube containing no compound grease has been desired.
Japanese Patent Application Publication No. 2002-221288 (Patent Literature
1) and International Application Publication No. W02009/072486 (Patent Literature
2) propose threaded connections for pipe or tube excellent in galling résistance even without compound grease.
On the contact surfaces of the pin and the box of a threaded connection for pipe or tube described in Patent Literature 1, a porous Zn layer or a porous Zn alloy layer is formed on at least one of thread portions or unthreaded métal contact portions of the threaded connection for pipe or tube by a mechanical plating method, and on the layer, a solid lubricant coating or a liquefied lubricating coating containing no heavy métal powders (e.g., a coating containing a high-basic organometallic sait of a high-basic sulfonate or the like as its main agent) is formed. Patent Literature 1 describes that it is thereby possible to hâve a high anticorrosion property and suppress the occurrence of galling due to occurring or the réduction of gas-tightness at the time of repeating fastening/loosening while dispensing withliquid lubricant, such as compound grease, containing heavy métal powders.
In a threaded connection for pipe or tube described in Patent Literature 2, the contact surface of a box includes, as an uppermost layer, a solid lubricant coating having plasticity or viscoplastic rheological behavior, and the contact surface of a pin includes, as an uppermost layer, a solid anticorrosive coating containing a UV cured resin as a main constituent. Patent Literature 2 describes that it is thereby possible to obtain a threaded connection for pipe or tube that suppresses the occurrence of rust without using compound grease, exerts excellent galling résistance and gas-tightness, has no stickiness on its surface, and is excellent in appearance and inspectability.
CITATION LIST
PATENT LITERATURE
[Patent Literature 1] Japanese Patent Application Publication No. 2002-221288 [Patent Literature 2] International Application Publication No. W02009/072486
SUMMARY OF INVENTION
TECHNICAL PROBLEM
The évaluation of galling résistance is usually conducted while steel pipes to be fastened are centered with each other, However, in actually fastening a threaded connection for pipe or tube, steel pipes (or a steel pipe and a coupling) to be fastened may not be centered with each other. This is called misalignment. When misalignment occurs, the contact surfaces a pin and a box (a thread portion and an unthreaded métal contact portion) receive strong friction as well as shear stress. This shear stress is remarkably larger than that in the case where no misalignment occurs. For this reason, when misalignment occurs, galling is more prone to occur. Therefore, a capability of suppressîng galling even when misalignment occurs, namely, an anti-misalignment property is needed for a threaded connection for pipe or tube.
Meanwhile, the previously-described unthreaded métal contact portion includes a métal seal portion and a shoulder portion. In fastening a threaded connection for pipe or tube, the shoulder portions of a pin and a box corne into contact with each other. A torque occurring at this point is called a shouldering torque. In fastening a threaded connection for pipe or tube, after the torque reaches the shouldering torque, the fastening is further performed until fastening is completed. This increases the gas-tightness of the threaded connection for pipe or tube. When the fastening is further performed, a métal constituting at least one of the pin and the box begins plastic deformation. A torque occurring at this point is called the yield torque.
A torque at the completion of fastening (called a fastening torque) is set so that a sufficient seal interfacial pressure can be obtained irrespective of the amount of thread interférence. When the différence between a shouldering torque and a yield torque, namely, a torque-on-shoulder value is sufficiently large, there is room in the range of fastening torque. As a resuit, the adjustment of the fastening torque becomes easy. Therefore, in addition to the previously-described anti-misalignment property, a threaded connection for pipe or tube is required to hâve an excellent torque property.
Meanwhile, after produced, an oil well pipe is transported by a vessel or the like and is in storage for a certain period of time until it is used. The transportation and the storage of the oil well pipe may last for a long period, Furthermore, the storage of an oil well pipe may be performed in the open-air. When the storage is performed in the open-air for a long period, rust occurs in a threaded connection for oil country tubular goods, and the galling résistance and the gas-tightness of the threaded connection for oil country tubular goods may be reduced, Therefore, in addition to the previously-described galling résistance, a threaded connection for oil country tubular goods is required to hâve an excellent anticorrosion property even when being used in a cold area, warm area, and tropical area at atmospheric températures ranging about -20°C to +50°C, as well as an extremely cold area where an atmospheric température can be -60°C to -20°C.
On contact surfaces (a thread portion and an unthreaded métal portion), a lubricating coating is formed for the purpose of improving galling résistance. As previously described, when an oil well pipe is in storage in the open-air, the oil well pipe may be repeatedly exposed to high température and low température. When being repeatedly exposed to high température and low température, the adhesiveness of the lubricating coating may be reduced. The reduced adhesiveness of the lubricating coating results in the scaling-off of the lubricating coating in performing fastening. The scaling-off of the lubricating coating leads to the réduction in the anti-misalignment property of the threaded connection for pipe or tube, further resulting în an increased shouldering torque. Therefore, for a threaded connection for pipe or tube, high adhesiveness of solid lubricant coating is required even in the case of being subjected to répétitive température changes.
In the threaded connection for pipe or tube disclosed in Patent Literature l, the Zn layer or the Zn alloy layer is porous. For this reason, the adhesiveness of the layer with the solid lubricant coating is satisfactory, providing sufficient galling résistance. However, because of being porous, a gap occurs between the Zn or Zn alloy layer and base material. For this reason, the base material at the occurring gap portion may corrode during a lapse of a long period.
The threaded connection for pipe or tube described in Patent Literature 2 has the adhesiveness and the lubrication property of excellent solid lubricant coating in a usage environment at a normal température. For this reason, the threaded connection for pipe or tube has sufficient galling résistance in a normal température environment. However, the environment température to be used of the threaded connection for pipe or tube may be high or may be low. The base material and the solid lubricant coating of the threaded connection for pipe or tube dîffer in coefficient of thermal expansion from each other. For this reason, when the environment température to be used of the threaded connection for pipe or tube is high, the adhesiveness of the solid lubricant coating is reduced. If the environment température to be used of a threaded connection for pipe or tube is high, the solid lubricant coating is further softened and oxidized. This further reduces the adhesiveness of the solid lubricant coating. On the other hand, if the environment température to be used of the threaded connection for pipe or tube is very low, the solid lubricant coating is hardened and embrittled. This reduces the adhesiveness of the solid lubricant coating. A reduced adhesiveness of the solid lubricant coating leads to the scaling-off or délamination of the solid lubricant coating, resulting in the réduction in the galling résistance of the threaded connection for pipe or tube. In addition, a threaded connection for pipe or tube may be exposed to high température in transportation and may be exposed to very low température in use. Therefore, a threaded connection for pipe or tube is required to hâve a high adhesiveness with a solid lubricant coating even when being repeatedly exposed to high température and very low température.
An objective of the présent invention is to provide a threaded connection for pipe or tube having excellent galling résistance, torque property, and anticorrosion property, and still having an excellent adhesiveness with a lubricating coating even when being repeatedly exposed to high température and very low température, and to provide a method for producing the threaded connection for pipe or tube.
SOLUTION TO PROBLEM
A threaded connection for pipe or tube according to the présent embodiment includes a pin and a box. The pin and the box each includes a contact surface including a thread portion and an unthreaded métal contact portion. The threaded connection for pipe or tube comprises a first plating layer, a second plating layer, and a lubricating coating. The first plating layer is formed on at least one of the contact surfaces of the pin and the box, and is consisting of a Zn-Ni alloy. The second plating layer is formed on the first plating layer, and is a porous plating layer consisting of Zn or a Zn alloy. The lubricating coating is formed on the second plating layer. From a contact surface side, the first plating layer consisting of the Zn-Ni alloy, the second plating layer consisting of Zn or the Zn alloy, and the lubricating coating are stacked in this order.
A method for producing the threaded connection for pipe or tube according to the présent embodiment is a method for producing a threaded connection for pipe or tube including a pin and a box. The pin and a box each includes a contact surface that includes a thread portion and an unthreaded métal contact portion. This producing method according to the présent embodiment comprises an electroplating step, a mechanical plating step, and a lubricating coating forming step. In the electroplating step, a first plating layer consisting of a Zn-Ni alloy is formed by performing electroplating treatment on the contact surface of at least one of the pin and the box. In the mechanical plating step, mechanical plating treatment is performed after forming the first plating layer to form a second plating layer consisting of Zn or a Zn alloy. In the lubricating coating forming step, the lubricating coating is formed on the second plating layer.
EFFECTS OF INVENTION
A threaded connection for pipe or tube according to the présent embodiment has excellent galling résistance, torque property, and anticorrosion property, and still has an excellent adhesiveness with a lubricating coating even when being repeatedly exposed to high température and very low température.
BRIEF DESCRIPTION OF DRAWINGS
[FIG. 1] FIG. 1 is a schematic diagram of fastening of steel pipes when misalignment occurs.
[FIG. 2] FIG. 2 is a graph illustrating the relation between the number of tums and torque in a threaded connection for pipe or tube.
[FIG. 3] FIG. 3 is a diagram illustrating the configuration a threaded connection for pipe or tube according to the présent embodiment.
[FIG. 4] FIG. 4 is a cross-sectional view of the threaded connection for pipe or tube according to the présent embodiment.
[FIG. 5] FIG. 5 is a cross-sectional view of a contact surface of the threaded connection for pipe or tube according to the présent embodiment.
DESCRIPTION OF EMBODIMENTS
The présent embodiment will be described below in detail with reference to the drawings. Identical or équivalent éléments will be denoted by the same reference numerals and the description thereof will not be repeated.
Regarding a threaded connection for pipe or tube including a pin and a box, the présent inventor conducted a variety of studies about the relation between galling résistance, torque property, anticorrosion property, and adhesiveness of lubricating coating. As a resuit, the présent inventor obtained the following findings.
Indexes of galling résistance include high-temperature résistance and antimisalignment property. In conventional threaded connections for pipe or tube, although high-temperature résistance is sufficient, an anti-misalignment property is insufficient in some cases. FIG. I is a schematic diagram for illustrating misalignment. Referring to FIG. I, Steel pipes 100 each include a Steel pipe body (hereafter, simply referred to as a main body) 101 and a coupling 102. The coupling 102 is made up and fixed to the upper end of the main body 101. The Steel pipes 100 each include a pin 103 on an outer peripheral surface at the lower end (the lower end of the main body 101 ), and a box 104 on an inner peripheral surface at the upper end (the upper end of the coupling 102). As illustrated in FIG. I, of the Steel pipes 100 vertically arranged, the pin 103 of the upper Steel pipe 100 is inserted into the box of the lower steel pipe 100, and fastened. This causes vertically arranged Steel pipes 100 to be coupled to each other.
In fastening, it is préférable to perform the fastening with the upper Steel pipe 100 and the lower Steel pipe 100 coaxially arranged. However, there are some cases in reality that, in fastening, the central axis of the upper steel pipe 100 and the central axis of the lower steel pipe 100 are not aligned but toc. This is called misalignment. When fastening is performed with misalignment occurring, galling is prone to occur when compared to the case where no misalignment occurs.
To increase the anti-misalignment property of a threaded connection for pipe or tube, it is effective to form a plating layer having a high hardness and a high melting point on a contact surface having a thread portion and an unthreaded métal contact portion. If a plating layer has a high hardness, the plating layer on a contact surface is hard to be damaged in fastening and loosening. Furthermore, if a plating layer has a high melting point, the plating layer is hard to be melted out even when the température increases locally in fastening and loosening.
Thus, in a threaded connection for pipe or tube according to the present embodiment, a first plating layer consisting of a Zn-Ni alloy is formed on a contact surface. The first plating layer preferably has a porosity is less than 5%. A first plating layer having a porosity of less than 5% can be formed by electroplating treatment. Therefore, the first plating layer is an electroplating layer.
The Zn-Ni alloy constituting the first plating layer has a high hardness and a high melting point. It is therefore possible to increase the anti-misalignment property of the threaded connection for pipe or tube. Zinc (Zn) has a low hardness and a low melting point as compared with copper (Cu), which is conventionally used for plating layers. However, a Zn-Ni alloy, which is a Zn alloy, has a sufficiently high hardness and a sufficiently high melting point. For this reason, the first plating layer can increase the anti-misalignment property.
Using a Zn-Ni alloy enables the anticorrosion property of a threaded connection for pipe or tube to be increased. Zinc (Zn) is a base métal as compared with iron (Fe), nickel (Ni), and chromium (Cr). Therefore, when the first plating layer containing zinc (Zn) is formed on the contact surface, the plating layer corrodes in preference to a Steel material (sacrificial protection). This increases the anticorrosion property of the threaded connection for pipe or tube.
Meanwhile, to increase lubricity, a lubricating coating is usually formed on a contact surface of a threaded connection for pipe or tube. The lubricating coating may be any one of a solid lubricant coating and a liquid lubricating coating. The lubricating coating may decrease in adhesiveness by répétitive exposure to high température and low température. The lubricating coating having a decreased adhesiveness is sealed off when the threaded connection for pipe or tube is fastened and loosened. In particular, in the case where the fastening is performed with misalignment occurring, the lubricating coating is prone to be sealed off. The scaling-off of the lubricating coating leads to a réduction in the lubricîty of a thread portion of the threaded connection for pipe or tube.
The first plating layer is an electroplating layer, thus having a fiat surface. Therefore, when the solid lubricant coating is formed on the first plating layer, the adhesiveness of the lubricating coating is prone to be reduced.
Thus, on the first plating layer, a porous second plating layer consisting of Zn or a Zn alloy is formed, and the lubricating coating is formed on the second plating layer. In this case, the adhesiveness of the lubricating coating is increased. The second plating layer is more porous than the first plating layer. The second plating layer preferably has a porosity of 5 to 80%. The second plating layer being more porous than the first plating layer can be formed by mechanical plating treatment. Therefore, the second plating layer is a mechanical plating layer. The second plating layer being a mechanical plating layer includes roughness on its surface. When the lubricating coating is formed on the surface including roughness, the adhesiveness is increased due to what is called the anchor effect. An increased adhesiveness of the lubricating coating suppresses the scaling-off of the lubricating coating even in the case of répétitive exposure to high température and low température. If the scaling-off of the lubricating coating is suppressed, a high lubricity is kept in fastening and loosening. For this reason, the anti-misalignment property of the threaded connection for pipe or tube is further increased.
Furthermore, if a high lubricity of the threaded connection for pipe or tube is kept, a yield torque in fastening rises. FIG. 2 is a graph illustrating the relation between the number of tums and torque in a thread portion of a threaded connection for pipe or tube. Referring to FIG. 2, when a pin and a box are fastened, the shoulder portions of the pin and the box corne into contact with each other. A torque occurring at this point is called a shouldering torque. In fastening the thread portions of a threaded connection for pipe or tube, after the torque reaches the shouldering torque, the fastening is further performed until fastening is completed. This increases the gas-tightness of between the thread portions of the threaded ίο connection for pipe or tube. When the fastening is further performed, a métal constituting at least one of the pin and the box begins plastic deformation. A torque occurring at this point is called the yield torque.
A torque at the completion of fastening (fastening torque) is set so that a sufficient seal interfacial pressure can be obtained irrespective of the amount of thread interférence. When a torque-on-shoulder value, the différence between a shouldering torque and a yield torque, is sufficiently large, there is room in the range of fastening torque. As a resuit, the adjustment of the fastening torque becomes easy. Preferably, the yield torque is not excessively low. A sufficiently high adhesiveness of the lubricating coating allows the yield torque to be kept high even when fastening and loosening are repeated. That is, the adjustment of the fastening torque remains easy even after répétitive use, showing an excellent torque property.
The threaded connection for pipe or tube according to the present embodiment based on the above findings includes a pin and a box. The pin and the box each hâve a contact surface including a thread portion and an unthreaded métal contact portion. The threaded connection for pipe or tube comprises a first plating layer consisting of a Zn-Ni alloy on the contact surface of at least one of the pin and the box, a porous second plating layer consisting of Zn or a Zn alloy on the first plating layer, and a lubricating coating on the second plating layer. These are stacked in order of the first plating layer, the second plating layer, and the lubricating coating, from a contact surface side.
The threaded connection for pipe or tube according to the present embodiment includes the first plating layer on its contact surface. The Zn-Ni alloy constituting the first plating layer has a high hardness and a high melting point. For this reason, the threaded connection for pipe or tube is excellent in anti-misalignment property. In addition, the Zn-Ni alloy has a sacrificial protection effect. For this reason, the threaded connection for pipe or tube according to the present embodiment is also excellent in anticorrosion property. The threaded connection for pipe or tube according to the present embodiment further includes the second plating layer between the first plating layer and the lubricating coating, the second plating layer consisting of Zn or a Zn alloy. The second plating layer is more porous than the first plating layer. For this reason, the adhesiveness of the lubricating coating to a
H threaded connection for pipe or tube is increased as compared with the case where the lubricating coating is formed directly on the first plating layer. The second plating layer is porous, thus showing a sufficient torque-on-shoulder value, and showing an excellent torque property.
The second plating layer is a mechanical plating layer formed by mechanical plating treatment. Examples of the mechanical plating treatment include blasting treatment using metallic particles to be plated. In this case, the formed second plating layer is porous, and the surface thereof has roughness. Therefore, the adhesiveness of the lubricating coating is increased due to the anchor effect. The mechanical plating treatment may be other well-known similar methods other than the blasting treatment using metallic particles.
The porosity of the second plating layer is preferably 5 to 80%, and more preferably 10 to 60%.
Preferably, the first plating layer has a thickness of l to 20 pm, the second plating layer has a thickness of 2 to 30 pm, and the lubricating coating has a thickness of 5 to 50 pm.
A method for producing the threaded connection for pipe or tube according to the present embodiment is a method for producing the previously described threaded connection for pipe or tube. This producing method comprises an electroplating step, a mechanical plating step, and a lubricating coating forming step. In the electroplating step, the electroplating treatment is performed to form the first plating layer consisting of a Zn-Ni alloy, on the contact surface of at least one of the pin and the box. In the mechanical plating step, mechanical plating treatment is performed after forming the first plating layer to form a second plating layer consisting of Zn or a Zn alloy. In the lubricating coating forming step, the lubricating coating is formed on the second plating layer.
Description will be made below in detail about a threaded connection for pipe or tube and a method for producing a threaded connection for pipe or tube, according to the present embodiment.
[Threaded Connection for Pipe or Tube]
A threaded connection for pipe or tube includes a pin and a box. FIG. 3 is a side view illustratîng a partial cross section of a threaded connection for pipe or tube according to the present embodiment. Referring to FIG. 3, the threaded connection for pipe or tube 50 includes a Steel pipe body l (hereafter, simply referred to as a main body) and a coupling 2. At the both ends of the main body 1, a pin 3 is formed that includes an extemal thread portion on its outer surface. At the both ends of the coupling 2, a box 6 is formed that includes an internai thread portion on its inner surface. By fastening the pin 3 and the box 6, the coupling 2 is attached to the end of the main body 1. Besides, there is an integral-type threaded connection for oil country tubular goods, which does not include a coupling 2 but includes a pin 3 provided at one end of the main body 1 and a box 6 at the other end. The threaded connection for pipe or tube in the present embodiment is available for both of coupling-type threaded connections for pipe or tube and integral-type threaded connections for pipe or tube.
FIG. 4 is a cross-sectional view of the pin and the box of the threaded connection for pipe or tube 50 according to the present embodiment. Referring to FIG. 4, the pin 3 includes a contact surface. The contact surface is a portion that cornes in contact when the pin 3 and the box 6 are fastened. The contact surface includes a thread portion (extemal thread) 4 and an unthreaded métal contact portion. The unthreaded métal contact portion is formed at a front end of the pin 3, including a métal seal portion 8 and a shoulder portion 9. Similarly, the box 6 includes a contact surface. The contact surface includes a thread portion (internai thread) 5 and an unthreaded métal contact portion (a métal seal portion 10 and a shoulder portion 11). As the pin 3 and the box 6 are fastened, both shoulder portions (the shoulder portions 9 and 11 ), both métal seal portions (the métal seal portions 8 and 10), and both thread portions (the extemal thread portion 4 and the internai thread portion 5) corne into contact with each other, respectively.
FIG. 5 is a cross-sectional view of a contact surface of the threaded connection for pipe or tube 50 according to the present embodiment. Referring to FIG. 5, the threaded connection for pipe or tube 50 includes, on the contact surface of at least one of the pin 3 and the box 6, a first plating layer 21, a second plating layer 22, and a lubricating coating 23, in this order from a contact surface side. [First Plating Layer 21]
The first plating layer 21 is formed on the contact surface of at least one of the pin 3 and the box 6. The first plating layer 21 is an electroplating layer consisting of a Zn-Ni alloy. The first plating layer 21 has a high hardness and a high melting point. Therefore, the anti-misalignment property of the threaded connection for pipe or tube 50 is increased. Furthermore, since Zn contained in the first plating layer 21 is a base métal, the anticorrosion property of the threaded connection for pipe or tube 50 is increased.
The Zn-Ni alloy constitutîng the first plating layer 21 contains Zn and Ni, and the balance thereof is consisting of impurities. The impurities are, for example, Fe, S, O, C, and the like. Preferred Zn content in the Zn-Ni alloy is 85 mass%, and more preferably 90 mass%. Preferred Ni content in the Zn-Ni alloy is 10 to 15 mass%. The first plating layer 21 has a large content of Zn, thus being highly effective in sacrificial protection.
Zn and Ni contents in the first alloy layer 21 are measured by the following method. Measurement of Zn and Ni content, for example, is carried out by using a hand-held X-ray fluorescence analyzer (Olympus DP2000 (trade name DELTA Premium)). Any four positions (any of 0° ,90° ,180° , and 270° positions on the circumferential direction of a pipe) on a surface of a métal seal portion, which is plated with a Zn-Ni alloy layer, are measured for the composition analysis. The measured content of Zn and Ni is measured by a measurement mode of the alloy.
A préférable thickness of the first plating layer 21 is 1 to 20 μιη. If the first plating layer 21 has a thickness of 1 pm or more, it is possible to increase the antimisalignment property and the anticorrosion property of the threaded connection for pipe or tube 50 more stably. If the first plating layer 21 has a thickness of 20 pm or less, the adhesiveness of the first plating layer 21 is further stabilized. Therefore, a préférable thickness of the first plating layer 21 is 1 to 20 pin.
The thickness of the first plating layer 21 is measured by the following method. A probe of an overcurrent phase type film thickness measuring device, conforming to ISO (International Organization for Standardization) 21968 (2005), is contacted to a contact surface formed with a first plating layer 21. The phase différence between the high frequency magnetic field on the input side of the probe and the overcurrent, which is raîsed by the high frequency magnetic field on the first plating layer 21, is measured. This phase différence is converted into the thickness of the first plating layer 21. In a film thickness measurement on a threaded connection, any four positions (any of 0° , 90° , 180° , 270° positions on the circumferential direction of a pipe) on a métal seal portion are measured.
The porosity of the first plating layer 21 is preferably less than 5%. When a plating layer is formed by electroplating treatment, the plating layer has a porosity of less than 5%. Porosity in an electroplating layer includes space portions, such as a pin-hole, void portions between fine particles and opening portions inside the particulate mass body, which consist the plating layer.
The porosity of the first plating layer 21 can be measured by a known method. [Second Plating Layer 22]
The second plating layer 22 is formed on the first plating layer 21. The second plating layer 22 is consisting of Zn or a Zn alloy. That is, the second plating layer 22 contains Zn or the Zn alloy, and the balance thereof is consisting of impurities. The impuritîes are, for example, Fe, S, O, C, or the like. The Zn alloy means an alloy having a content of Zn of 50% or more. The Zn alloy is, for example, a Zn-Fe alloy. The second plating layer 22 may be a plating layer consisting of pure Zn and impurities or may be a plating layer consisting of a Zn alloy and impurities. Zn content in the Zn alloy can be measured as in the Zn content in the first plating layer 21.
The second plating layer 22 is porous when compared with the first plating layer, and has roughness on its surface. The lubricating coating 23 is cured while fitting into the roughness, and thus the adhesiveness of the lubricating coating 23 is increased due to what is called the anchor effect, increasing the durability of the lubricating coating. Therefore, even in the case where of the threaded connection for pipe or tube 50 is subjected to repeated fastening and loosening, the scaling-off of the lubricating coating 23 is suppressed. Furthermore, even in the case where the lubricating coating 23 wears due to repeated fastening and loosening of the threaded connection for pipe or tube 50, portion of the lubricating coating 23 or wear débris of the lubricating coating 23 remain inside (in the pores of) the second plating layer 22. For this reason, the threaded connection for pipe or tube 50 keeps a high lubricity.
The second plating layer 22 is a mechanical plating layer formed by mechanical plating treatment. The mechanical plating layer is more porous than an electroplating layer. The porosity of the second plating layer 22 formed by the mechanical plating treatment is, for example, 5 to 80%. The porosity of the second plating layer 22 can be measured as in the above-mentioned porosity of the first plating layer 21.
A preferable thickness of the second plating layer 22 is 2 to 30 pm. If the second plating layer 22 has a thickness of 2 pm or more, it is possible to obtain the adhesiveness of the lubricating coating 23 and an appropriate torque-on-shouider value of the lubricating coating 23, more stably. In contrast, if the second plating layer 22 has a thickness more than 30 pm, the above-described effect is saturated. Therefore, a preferable thickness of the second plating layer 22 is 2 to 30 pm. The thickness of the second plating layer 22 can be measured as of the above-mentioned thickness of the first plating layer 21.
[Lubricating Coating 23]
The lubricating coating 23 is formed on the second plating layer 22. By virtue of the lubricating coating 23, the lubricity of the threaded connection for pipe or tube 50 is increased. The lubricating coating 23 may be a solid lubricant coating or a liquid lubricating coating. Preferably, the lubricating coating 23 is a solid lubricant coating. As the lubricating coating 23, well-known ones can be used. The lubricating coating 23 contains, for example, a lubricating particle and a binding agent. The lubricating coating 23 may contain a solvent and other constituents as necessary.
The lubricating particle reduces the friction coefficient of the surface of the lubricating coating 23. The lubricating particle is not limited in particular as long as the particle has lubricity. The lubricating particle can be, for example, graphite, molybdenum disulfide (M0S2), tungsten disulfide (WSi), boron nitride (BN), polytetrafluoroethylene (PTFE), a graphite fluoride (CFx), calcium carbonate (CaCO3), or a combination thereof. Preferably, graphite, a graphite fluoride, MoS? and PTFE are used. When the lubricant film 23 is set to be 100 mass%, the content of the lubricating particle is preferably 5 to 40 mass%.
The binding agent binds lubricating particle s in the lubricating coating 23. As the binding agent, an organic resin, an inorganic resin, or a mixture thereof can be used. In the case of using the organic resin, a thermosetting resin or a thermoplastic resin can be used. The thermosetting resin includes, for example, an epoxy resin, a polyimide resin, a polycarbodiimide resin, a polyethersulfone resin, a polyetheretherketone resin, phenolic resin, a furan resin, a urea resin, and an acrylic resin. The thermoplastic resin includes, for example, a polyamide-imide resin, a polyethylene resin, a polypropylene resin, a polystyrène resin, and an ethylene vinyl acetate resin.
In the case of using an inorganic resin as the binding agent, a polymetaloxane can be used. The polymetaloxane refers to a high polymer having a main chain skeleton made of repeating metal-oxygen bondings. Preferably, polytitanoxane (TiO) and polysiloxane (Si-O) are used. These inorganic resins are obtained by subjecting métal alkoxides to hydrolysis and condensation. The alkoxy group of the métal alkoxide is, for example, a lower alkoxy group such as methoxy group, ethoxy group, propoxy group, isopropoxy group, isobutoxy group, butoxy group, and tertbutoxy group. When the lubricant film 23 is set to be 100 mass%, the content of the binder is preferably 60 to 95 mass%.
When there is a need for dissolving or dispersing the lubricating particles and the binding agent, a solvent is used. The solvent is not limited in particular as long as it can subject constituents contained in the lubricating coating 23 to dispersion or dissolution. As the solvent, an organic solvent or water can be used. Examples of the organic solvent include toluene and isopropyl alcohol.
The lubricating coating 23 may contain other constituents as necessary. Examples of the other constituents include an anticorrosion, a corrosion inhibitor, a surfactant, a wax, a friction modifier, a pigment, and the like. The contents ofthe lubricating particles, the binding agent, the solvent, and the other constituents are set as appropriate.
The lubricating coating 23 is formed by applying and solidifying the previously described composite on the contact surface of at least one of the pin 3 and the box 6.
[0062] |7
Referring to FIG. 3, in the case of a threaded connection for pipe or tube 50 in which the pin 3 and the box 6 are fastened on shipping, the lubricating coating 23 may be formed on only one of the contact surfaces of the pin 3 and the box 6 before the fastening. In this case, the coupling 2, having a short length, is easier to perform application operation of the composite than the main body l, having a long length. For this reason, it is préférable to form the lubricating coating 23 on the contact surface of the box 6 of the coupling 2. In the threaded connection for pipe or tube 50, at a pipe leading end portion where the pin 3 and the box 6 are not fastened on shipping, the lubricating coating 23 may be formed on both of the contact surfaces of the pin 3 and the box 6 so that the contact surfaces are given an anticorrosion property as well as lubricity. Altematively, the lubricating coating 23 may be formed on only one of the contact surfaces of the pin 3 and the box 6, and on the other contact surface, a solid anticorrosive coating to be described later may be formed. In both cases, it is possible to give galling résistance, gas-tightness, and an anticorrosion property to a thread.
It is préférable to cover the entire contact surface of at least one of the pin 3 and the box 6 with the lubricating coating 23. Only portion of the contact surface (e.g., only seal portions 8 and 10) may be covered with the lubricating coating 23.
The lubricating coating 23 may be single-layered or multi-layered. The term multi-layered refers to the state where the lubricating coating 23 is made up of two or more layers stackîng from the contact surface side. The répétition of applying and solidifying the composite allows the lubricating coating 23 to be made up of two or more layers. The lubricating coating 23 may be formed directly on the contact surface or may be formed after preconditioning treatment to be described later.
A préférable thickness of the lubricating coating 23 is 5 to 50 pm. If the lubricating coating 23 has a thickness of 5 pm or more, it is possible to obtain a high lubricity stably. Meanwhile, if the lubricating coating 23 has a thickness of 50 pm or less, the adhesiveness of the lubricating coating 23 is stabilized. Furthermore, if the lubricating coating 23 has a thickness of 50 pm or less, the thread tolérance (clearance) of a sliding surface is widened, which reduces an interfacial pressure in sliding. For this reason, it is possible to suppress a fastening torque becoming excessively high. Therefore, a préférable thickness of the lubricating coating 23 is 5 to 50 pm.
The thickness of a lubricating coating layer 23 is measured by the following method. Under the same conditions as in the case of applying a lubricant coating layer 23 to a threaded connection for pipe or tube, a lubricant film is applied on a fiat plate. Among the coating conditions of a threaded connection for pipe or tube and fiat plate, the following conditions are to be matched; the distance between an object to be coated and a nozzle tip, injection pressure, viscosity of the composition, rotatîonal speed of the object to be coated, and the like. To match the viscosity of the composition, the températures of a tank, a pipe, and a nozzle outlet, are to be matched between the threaded connection for pipe or tube and the plate. From the différence of the weight of the plate before applying the composition and the weight of the plate after applying the composition, the amount of the applied amount of the composition per unit time is calculated. The composition is solidified on the plate to form a lubricating coating layer 23. The thickness of the lubricating coating layer 23 is measured using a film thickness meter. From the différence of the weight of the plate before applying the composition and the weight of the plate after applying the composition, the weight of the lubricating coating layer 23 is calculated. From the film thickness and the weight of the lubricant coating layer 23, the density of the lubricant coating layer 23 is calculated. Next, from the thread shape and the size (inner diameter and thickness, and the like), the application target area ofthe threaded connection for pipe or tube is calculated. The application target area corresponds to the area of expanding the thread fonning surface having unevenness into a plane surface. From the application time of the composition onto the threaded connection for pipe or tube, the application target area, and the density of and the lubricant coating layer 23, the average thickness ofthe lubricant coating layer 23 against the threaded connection for pipe or tube is calculated.
[Solid Anticorrosive Coating]
The previously-described threaded connection for pipe or tube 50 may include the lubricating coating 23 on the contact surface of one of the pin 3 and the box 6 and may include a solid anticorrosive coating on the contact surface of the other of the pin 3 and the box 6. As previously described, the threaded connection for pipe or tube 50 may be in storage for a long period until it is actually used. In this case, forming the solid anticorrosive coating increases the anticorrosion property of the pin 3 or the box 6.
Examples of the solid anticorrosive coating include chromate coating consisting of chromate. The chromate coating is formed by well-known trivalent chromate treatment.
The solid anticorrosive coating is not limited to a chromate coating. Another solid anticorrosive coating contains, for example, a UV cured resin. In this case, the solid anticorrosive coating has a strength with which the solid anticorrosive coating is not fractured by force applied to it in installing a protector. Furthermore, during transport or storage, the solid anticorrosive coating is not dissolved even when being exposed to water condensed for dew point reasons. Furthermore, the solid anticorrosive coating is not easily softened even at high température of more than 40°C. The UV cured resin is a well-known resin composite. The UV cured resin is not limited in particular as long as it contains a monomer, an oligomer and a photoinitiator and induces photo-polymerization reaction by irradiation with ultraviolet light so as to form a cured coating.
On the other contact surface of the threaded connection for pipe or tube 50, a plating layer may be formed, and on the plating layer, the previously described solid anticorrosive coating may be formed. Altematively, the solid anticorrosive coating may be formed directly on the other contact surface.
[Base Material of Threaded connection for pipe or tube 50]
The composition of a base material of the threaded connection for pipe or tube 50 is not limited in particular. Examples of the base material of the threaded connection for pipe or tube 50 include carbon steels, stainless steels, and alloy steels. Among the alloy steels, high alloy steels such as two-phase stainless steels containing an alloying element such as Cr, Ni, and Mo and Ni alloys hâve a high anticorrosion property. For this reason, using these high alloy steels as the base material of the threaded connection for pipe or tube 50 results in an excellent anticorrosion property in a corrosive environment containing hydrogen sulfîde, carbon dioxide, and the like.
[Method for Producing]
Description will be made below about a method for producing the threaded connection for pipe or tube 50 according to the présent embodiment.
The method for producing the threaded connection for pipe or tube 50 according to the présent embodiment includes an electroplating step, a mechanical plating step, and a lubricating coating forming step.
[Electroplating Step]
In the electroplating step, the electroplating treatment is performed to form the first plating layer 21 on the contact surface of at least one of the pin 3 and the box
6. The electroplating treatment is performed by a well-known method. For example, the electroplating treatment is performed in such a manner that the contact surface of at least one of the pin 3 and the box 6 is immersed in a plating bath containing zinc ions and nickel ions, and tumed on the electricity. As the plating bath, a commercial one is available. The plating bath preferably contains zinc ion: l to 100 g/L and nickel ion; l to 50 g/L. The treatment conditions for the electroplating treatment can be set as appropriate. The electroplating treatment conditions are, for example, plating bath pH: l to 10, plating bath température: 10 to 60°C, current density: l to 100 A/dm2, and a treatment time period: 0.1 to 30 minutes. As prevîously described, a préférable thickness of the first plating layer 21 is l to 20 pm.
[Mechanical Plating Step]
In the mechanical plating step, dry mechanical plating treatment is performed to form the second plating layer 22, which is a mechanical plating layer, on the first plating layer 21. A dry mechanical plating method is, for example, a blast plating method in which a blasting device is used to cause particles to collide with an object to be plated. In the présent embodiment, plating may be performed only on the contact surface. For this reason, the blast plating method, which enables the plating to be performed partially, is suitable.
The Particle used in the dry mechanical plating method such as the blast plating method is a metallic particle that includes Zn or a Zn alloy at least on its surface. The particle may be a metallic particle wholly consisting of Zn or a Zn alloy. A préférable blast medium is made up of a particle the core of which is Fe or a Fe alloy used in Patent Literature 1, having a surface covered with a Zn or Zn alloy
2l layer via a Fe- Zn alloy layer. The particle is available, for example, under the trade name Z Iron from DOWA Iron Powder Industries Co., Ltd. A préférable size of the particle is 0.2 to l .5 mm.
When the metallic particle having a Fe or Fe alloy core the surface of which is covered with Zn or a Zn alloy is subjected to blasting to the threaded connection for pipe or tube 50, only the Zn or the Zn alloy, the coating layer of the particle is adhered to the steel pipe. This forms the second plating layer 2, which is the mechanical plating layer made up of the Zn or the Zn alloy, on the first plating layer 21. The mechanical plating layer is porous, the porosity of which is 5 to 80%. For this reason, forming the lubricating coating 23 and the solid anticorrosive coating on the second plating layer 22 further increases the adhesiveness of the lubricating coating 23 and the solid anticorrosive coating due to what is called the anchor effect. As previously described, a préférable thickness of the second plating layer 22 is 2 to 30 μητ.
[Lubricating Coating Forming Step]
After the mechanical plating step, the lubricating coating forming step is performed. In the lubricating coating forming step, a composite for forming a lubricating coating (hereafter, also referred to as a composite) is first prepared. The composite is formed by mixing the previously described lubricating particle and binding agent. The composite may further contain the previously described solvent or other constituents.
The résultant composite is applied to the second plating layer 22. A method for the application is not limited in particular. For example, the composite containing the solvent is sprayed on the second plating layer 22 using a spray gun. In this case, the composite is applied on the second plating layer 22 uniformly. The pin 3 or the box 6 on which the composite is applied is subjected to drying or drying by heating. The drying by heating is performed by, for example, commercially available direct drying equipment or the like. This makes the composite cured to form the solid lubricating coating 23 on the second plating layer 22. Conditions for the drying by heating can be set as appropriate with the boiling point, melting point, and the like of each constituent contained in the composite taken into considération.
In the case where the composite not containing the solvent is used to form the lubricating coating 23, a hot melt method can be used, for example. In the hot melt method, the composite is heated to get into a fluid state. The composite in the fluîd state is sprayed with a spray gun having a température maintaining fonction. The composite is thereby applied on the second plating layer 22 uniformly. The heating température of the composite can be set as appropriate with the melting point and the softening température of the previously described binding agent and other constituents taken into considération. The pin 3 or the box 6 on which the composite is applied is cooled by air cooling or the like. This makes the composite cured to form the lubricating coating 23 on the second plating layer 22.
[Fonning Solid Anticorrosive Coating (Trivalent Chromate Treatment)]
As previously described, the electroplating step, the mechanical plating step, and the lubricating coating forming step are performed on the contact surface of one of the pin 3 and the box 6, so as to fonn the first plating layer 21, the second plating layer 22, and the lubricating coating 23.
Meanwhile, on the contact surface of the other of the pin 3 and the box 6, the first plating layer 21, the second plating layer 22, and the lubricating coating 23 may be formed, or a plating layer and/or a solid anticorrosive coating may be formed. Description will be made below about the case where the first plating layer 21 and the solid anticorrosive coating composed of the chromate coating is formed on the contact surface of the other of the pin 3 and the box 6.
In this case, the first plating layer 21 is formed by perfomiing the previously described electroplating step. After performing the electroplating step, trivalent chromate treatment is performed to form the solid anticorrosive coating. The trivalent chromate treatment is treatment to form a coating of a trivalent chromate (chromate coating). The chromate coating formed by the trivalent chromate treatment suppresses white rust on the surface of a Zn-alloy-platîng layer. This improves the appearance of a product (however, white rust on a Zn-alloy-platîng layer is not rust of the threaded connection for pipe or tube 50 and thus has no influence on the galling résistance and anticorrosion property of the threaded connection for pipe or tube 50). The trivalent chromate treatment can be performed by a well-known method. For example, the contact surface at least one of the pin 3 and the box 6 is immersed in chromate treatment liquid, or the chromate treatment liquid is sprayed to be applied on the contact surface. Subsequently, the contact surface is rinsed. The contact surface may be rinsed after being immersed in the chromate treatment liquid and energized. The contact surface on which the chromate treatment liquid is applied may be subjected to drying by heating. The conditions for the trivalent chromate treatment can be set as appropriate.
[Pretreatment Step]
In the previously described producing steps, a pretreatment step may be included before the electroplating step, as necessary. Examples of the pretreatment step include pickling and alkaline degreasing. In the pretreatment step, oil content and the like adhered to the contact surface is cleaned off. The pretreatment step may further include grinding processing such as mechanical grinding finishing.
Through the above-described producing steps, the threaded connection for pipe or tube 50 according to the present embodiment is produced.
EXAMPLES
Examples will be described below. It should be noted that the present invention is not limited to the examples. In the examples, the contact surface of a pin will be referred to as a pin surface, and the contact surface of a box will be referred to as a box surface. In addition, the sign % in the examples means mass percent unless otherwise specified.
In the present examples, a threaded Steel pipe called VAM21 (R) from NIPPON STEEL & SUMITOMO METAL CORPORATION was used. The Steel pipe VAM2I (R) was a Steel pipe having an outer diameter of 24.448 cm (9-5/8 inches), and a wall thickness of l. 199 cm (0.472 inches). The Steel pipe was made of a carbon Steel, the Chemical composition of which contained C: 0.21%, Si: 0.25%, Mn: 1.1%, P: 0.02%, S: 0.01%, Cu: 0.04%, Ni: 0.06%, Cr; 0.17%, and Mo: 0.04%, and the balance thereof was Fe and impurities.
A pin surface and a box surface for which a Steel pipe of each test number is used were subjected to the mechanical grinding finishing (at a surface roughness of 3 pm). Subsequently, plating layers (first and second plating layers) or a coating (solid anticorrosive coating, lubricating coating) shown in Table l was formed, so as to préparé the pin and the box of each test number.
[Table l]
CN
TABLE1
| Lubricating Coating Layer (Thickness (gm)) | 1 | Solid Lubricant Coating Containing Graphite Of 5% By Mass, PTFE Of 4% By Mass, And PFPE Of 10% By Mass (30gm) | I | Xylan 1425 (30gm) | Defric coat 405 (20 gin) | Xylan 1425 (30gm) | t |
| Solid Anticorrosive Coating Layer (Thickness (gm)) | Chromate (Trivalent) (0.3gm) | i | Chromate (Trivalent) (0.3gm) | 1 | I | Cliromate (Trivalent) (0.3gm) | |
| Preconditioning Treatment Layer 2 (Thickness (gm)) | I | Dry Mechanical Plating Layer (lOgm) | Dry Mechanical Plating Layer ( 1 Ogm) | Dry Mechanical Plating Layer ( 1 Ogm) | Dry Mechanical Plating Layer (lOgm) | I | |
| Preconditioning Treatment Layer 1 (Thickness (gm)) | Electroplating Layer (8gm) | Electroplating Layer (8gm) | Electroplating Layer (8gm) | Electroplating Layer (Sgm) | Electroplating Layer (8gm) | Electroplating Layer (8gm) | Electroplating Layer (8gm) |
| Pin Surface | Box Surface | Pin Surface | Box Surface | Pin Surface | Box Surface | Pin Surface | |
| Steel Grade | Carbon Steel | Carbon Steel | Carbon Steel | Carbon Steel | |||
| Test Number | — | CN | CO | Ν’ |
ΓΊ
| Xylan 1425 (30μηι) | I | Xylanl425 ; (30μιη) I__________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________________ | r | Xylan 1425 (30μηι) |
| I | Chromate (Trivalent) (0.3μηι) | l | Chromate (Trivalent) (0.3μπι) | I |
| I | I | > | » | Manganèse Phosphating Layer (I2pm) |
| Dry Mechanical Plating Layer (lOgm) | Electroplating Layer (8μιη) | Electroplating Layer (8μηι) | Electroplating Layer (8μηι) | Electroplating Layer (8μπι) |
| Box Surface | Pin Surface | Box Surface | Pin Surface | Box Surface |
| Carbon Steel | Carbon Steel I_____________________________________________________________________________________________________________ | |||
| O |
The method of forming plating layers or coatings was as follows. In each test number, the porosity was measured in a known method. The porosity of the electroplating layers were less than 5%, and the porosity of the dry mechanical plating layers were 5 to 80%. The porosity of the manganèse phosphating layer was less than 30%.
[Test Number l]
For the test number l, a pin surface was plated with Zn-Ni electroplating (Daiwa Fine Chemicals Co., Ltd.) by electroplating, so as to form a first plating layer having a thickness of 8 pm. The conditions for the electroplating were plating bath pH: 6.5, plating bath température: 25°C, current density: 2 A/dm“, and treatment time period: 18 minutes. The composition of the first plating layer was Zn: 85% and Ni: 15%. Furthermore, the obtained first plating layer was subjected to the trivalent chromate treatment. A trivalent chromate treatment liquid was one available under the trade name DAIN Chromate TR-02 from Daiwa Fine Chemicals Co., Ltd. The conditions for the trivalent chromate treatment were bath pH: 4.0, bath température: 25°C, and treatment time period: 50 seconds.
Under the same conditions as those for the pin surface, a first plating layer was formed on a box surface. Subsequently, a second plating layer was formed by the dry mechanical plating treatment (blast plating method). In the dry mechanical plating treatment, a metallic particle including a coating consisting of a Zn-Fe alloy was used. The obtained second plating layer had an average film thickness of 10 pm. On the box surface with the first plating layer and the second plating layer formed thereon, a composite for forming a solid lubricant coating was applied. The composite for forming a solid lubricant coating contained graphite of 5% by mass, PTFE of 4% by mass, and PFPE of 10% by mass. The composite for forming a solid lubricant coating was heated to 13O°C, sprayed to be applied, and cooled to form a solid lubricant coating having an average film thickness of 30 pm.
[Test Number 2]
For the test number 2, a pin surface was subjected to the same treatment as with the test number l. The obtained first plating layer had the same film thickness and Chemical composition as those of the test number l. The thickness of a trivalent chromate coating was estimated to be the same as that of the test number l.
On a box surface, a first plating layer and a second plating layer were formed as with the test number l, and subsequently, a composite for forming a solid lubricant coating under the trade name Xylan1425 was applied. The trade name Xylan1425 contained an epoxy-based resin of 22% by mass, PTFE particles of 9% by mass, a solvent of 18% by mass in total, a pigment, and water of 40% by mass. The composite for forming a solid lubricant coating was sprayed to be applied on the box surface, and then subjected to drying by heating (at 90°C for five minutes) and curing treatment (at 210°C for 20 minutes) to form a solid lubricant coating. The obtained solid lubricant coating had an average film thickness of 30 pm.
[Test Number 3]
For the test number 3, first plating layers and second plating layers were formed on a pin surface and a box surface, as with the box surface of the test number
l. Obtained first and second plating layers had the same film thicknesses and Chemical compositions as those of the test number l. Subsequently, on the pin surface, the following composite for forming a solid lubricant coating was applied. The composite for forming a solid lubricant coating was one available under the trade name DEFRIC COAT 405 from Kawamura Research Lab., Inc., which contained molybdenum disulfide and graphite in an inorganic polymer binder. The composite for forming a solid lubricant coating was sprayed to be applied on the box surface, and then let stand in the atmosphère for three hours. Subsequently, the composite was exposed to humidified hot air at l50°C for ten minutes. The obtained solid lubricant coating had an average film thickness of 20 pm. On the box surface, a solid lubricant coating was formed as with the box surface ofthe test number 2. The obtained solid lubricant coating had the same thickness and Chemical composition as those of the box surface of the test number 2.
[Test Number 4]
For the test number 4, a first plating layer and a trivalent chromate coating were formed on a pin surface, as with the pin surface of the test number l. The formed plating layer and coating had the same thicknesses as those of the test number 1. On the box surface, a second plating layer was formed as with the box surface of the test number 1. The obtained second plating layer had an average film thickness of 10 pm. On the obtained second plating layer, a solid lubricant coating was formed as with the box surface of the test number 2. The obtained solid lubricant coating had the same thickness and Chemical composition as those of the box surface of the test number 2.
[Test Number 5]
For the test number 5, a first plating layer and a trivalent chromate coating were formed on a pin surface, as with the pin surface of the test number l. The formed coating had the same thickness as that of the test number l. On the box surface, a first plating layer was formed as with the pin surface of the test number l. The formed first plating layer had the same thickness as that of the test number l. On the obtained first plating layer, a solid lubricant coating was formed as with the box surface of the test number 2. The obtained solid lubricant coating had the same thickness and Chemical composition as those of the box surface of the test number 2. [Test Number 6]
For the test number 6, a first plating layer and a trivalent chromate coating were formed on a pin surface, as with the pin surface of the test number l. The formed plating layer and coating had the same thicknesses as those of the test number l. On the box surface, a first plating layer was formed as with the pin surface of the test number l. The formed first plating layer had the same thickness as that of the test number l. The box surface with the first plating layer formed thereon was immersed in manganèse phosphate Chemical treatment liquid at 80 to 95°C for ten minutes, whereby a manganèse phosphating layer having a thickness of 12 pm (at a surface roughness 10 pm) was formed. On the box surface with the manganèse phosphating layer formed thereon, a solid lubricant coating was formed as with the box surface of the test number 2. The obtained solid lubricant coating had the same thickness and Chemical composition as those of the box surface of the test number 2.
[Fastening/Loosening Evaluation Test]
As a fastening/loosening évaluation test, galling résistance and a torque property were evaluated. As the galling résistance, high-temperature résistance and an anti-misalîgnment property were evaluated.
[Galling Résistance: High-Temperature Résistance]
To investigate influences that layers on the first plating layer expérience in a high-temperature oil well, a répétitive fastening test was conducted on the pins and the boxes of the test number 2 and the test number 6. Specifically, with the pin and the box fastened at the first fastening, the surroundîngs of the box were heated at 200°C for six hours with a band heater, Subsequently, the pin and the box were loosened, and fastening and loosening were repeated. A fastening speed was 10 rpm at the beginning, then 2 rpm after shouldering. A fastening torque was 42.8 kN-m. The fastening and the loosening of the threaded connection for pipe or tube was performed at a normal température (20°C). Everytime a set of fastening and the loosening were performed, occurrences of galling due to a torque change in fastening were checked visually. At a point in time when an unrepairable galling occurs, the test was terminated. Table 2 shows the results.
[Table 2]
TABLE2
| Endurance Of Coating (Adhesiveness Of Lubricating Coating) | Weather Résistant Test 5) | No Coating Scaling-off | No Coating Scaling-off | No Coating Scaling-off | High Degree Of Coating Scaling-off /Rusting | Medium Degree Of Coating Scaling-off | No Coating Scaling-off | 5) See Table 3 | |
| Anticorrosion Property ___ | Sait Spray Test (2000 Hours) 4) | No Rust | No Rust | No Rust | Rusting After 500 Hours | No Rust | No Rust | 4) Compilant With JIS Z2371:2000 It Was Determined That There Was No Problem With Anticorrosion Property In Long Term Storage If No Rust Occurred For 1500 Hours Or More | |
| Fastening/Loosening | Torque Property | Torque-On-Shoulder Value 3) | 125 | 140 | 115 | 75 | 60 | 95 | 3) Values Assuming That Torque-On-Shoulder Value Takes On 100 When API Dope Is Used In Place Of Solid Lubricant Coating |
| Galling Résistance (Number Of Fastening Succeeding With No Galling) ! | Ant i -Misa l i griment Property 2) | O | O | O | ΓΊ | O | (Note) 1 ) After First Fastening, Outer Circumference Of Box As Fastened Was Heated At 200°C For 6 Hours Using Band Heater 2) Toe Angle Θ Of Misalignment = 5° | ||
| High-Temperature Résistance I ) | I | O | I | I | 1 | CM | |||
| Test Number | •—1 | ri | m | xr |
-32[Evaluation Results]
Referring to Table 2, in the test number 2, no galling occurred after ten répétitions of fastening and loosening. In contrast, in the test number 6, the manganèse phosphating layer of a preconditioning treatment layer 2 suffered hightemperature dégradation. This is considered to be due to the élimination of crystal water, and embrittlement. As a resuit, the fastening and loosening succeeded with no galling up to the second time, whereas unrepairable galling occurred at the third time, and thus the test was terminated.
[Galling Résistance: Anti-Misalignment Property]
The répétition of fastening and loosening with misalignment was performed on the pins and the boxes of the test number l to the test number 6 to evaluate the anti-misalignment property. A toe angle Θ of the misalignment was 5°. The fastening and the loosening were repeated up to ten times. A fastening speed in the fastening and the loosening was IO rpm, and a fastening torque was 42.8 kN-m. Whenever the fastening and the loosening were performed once, a pin surface and a box surface were observed visually. Through the visual observation, occurrences of galling were checked. When the galling was slight and thus repairable, a galling flaw was repaired, and the test was continued. The number of times up to which the fastening and the loosening succeeded without unrepairable galling occurring was measured. Table 2 shows the results.
[Evaluation Results]
Referring to Table 2, in the pins and the boxes of the test number l to the test number 3 and the test number 6, no galling due to misalignment occurred. This is considered to be due to the improvement of adhesiveness with the solid lubricant coating layer brought by the layers on the first plating layer. In contrast, in the test number 4 and the test number 5, the number of fastening was significantly reduced. [Torque Property]
A torque property test was conducted on the pins and the boxes of the test number l to the test number 6. Specifically, a torque-on-shoulder value (the différence between a yield torque and a shouldering torque) was measured as follows. The pins and the boxes of the test number l to the test number 6 were prepared and fastened using a hydraulic power tong manufactured by Weatherford. Even after
-33the fastening, the torque was provided to perform fastening, whereby a torque chart illustrated in FIG. 2 was created. On the torque chart, the torque-on-shoulder value was measured. The shoulderîng torque is a torque value at the time when a shoulder portion cornes in contact, and a torque change begins to deviate from a first linear région (elastic deformation région). Meanwhiie, the yield torque is a torque value at the time when plastic deformation begins. Specifically, the yield torque is a torque value at the time when déviation from a second linear région begins, the second linear région occurring after the torque reaches the shoulderîng torque. Here, there were prepared pins and boxes for which the preconditioning treatment layers l and 2, and the solid anticorrosive coating layers of the test numbers l to 6 were used and treated with the solid lubricant coating layer replaced with a grease that is compilant with the API standard. Assuming that the torque-on-shoulder value of this case is 100, values of the test number l to the test number 6 were determined. Table 2 shows the results.
[Evaluation Results]
Referring to Table 2, in the test number l to the test number 3, the second plating layers, which were mechanical plating layers, were formed, and thus the torque-on-shoulder values were more than 100, showing excellent torque properties. In contrast, in the test number 4 and the test number 5, the torque-on-shoulder values were less than 100, showing low torque properties. In the test number 6, a layer on the first plating layer was a manganèse phosphating layer, and thus the torque-onshoulder value was less than 100, showing a low torque property.
[Anticorrosion Property Evaluation Test: Sait Spray Test]
Specimens were prepared using a carbon steel having the same composition as that of the test number l to the test number 6. The specimens had a size of 70 mm x 150 mm, and a thickness of l mm. The specimens were subjected to the same surface treatment as with the test number l to the test number 6, and a sait spray test was conducted on the specimens. The sait spray test was conducted based on the method described in JIS Z2371:2000. Through visual observation, a time point at which red rust occurred on the surface of the specimen of each test number was measured. Table 2 shows the results.
Claims (5)
1. A threaded connection for pipe or tube comprising a pin and a box, the pin and the box each including a contact surface that includes a thread portion and an unthreaded métal contact portion, the threaded connection for pipe or tube characterized by comprising:
on the contact surface of at least one of the pin and the box, a first plating layer consisting of a Zn-Ni alloy;
a second plating layer on the first plating layer, the second plating layer consisting of Zn or a Zn alloy, and being porous; and a lubricating coating on the second plating layer.
2. The threaded connection for pipe or tube according to claim l, characterized in that the porosity of the second plating layer is 5 to 80%.
3. The threaded connection for pipe or tube according to claim l or claim 2, characterized in that the first plating layer has a thickness of l to 20 pm, the second plating layer has a thickness of 2 to 30 pm, and the lubricating coating has a thickness of 5 to 50 pm.
4. The threaded connection for pipe or tube according to any one of claim l to claim 3, characterized in that the lubricating coating is a solid lubricant coating.
5. A method for producing a threaded connection for pipe or tube that includes a pin and a box, the pin and the box each including a contact surface that includes a thread portion and an unthreaded métal contact portion, the method characterized by comprising the steps of:
on the contact surface of at least one of the pin and the box, forming a first plating layer consisting of a Zn-Ni alloy by performing electroplating treatment;
forming a second plating layer consisting of Zn or a Zn alloy by performing mechanical plating treatment after forming the first plating layer; and