OA16608A - Hardfaced wearpart using brazing and associated method and assembly for manufacturing. - Google Patents

Abstract

An article, such as a hardfaced wearpart, includes a substrate, a sheet metal shell connected to the substrate to define a cavity between the surface of the substrate and the shell, and a composite material filling the cavity and forming a coating on at least a portion of the surface of the substrate, the composite material including a hard particulate material infiltrated with a metallic brazing material. The shell may be connected to the substrate by welding or brazing to the substrate, and may wear away during use. The shell and the substrate may be used as part of an assembly for producing the articles, where the shell is used as a mold for forming the composite material by filling the shell with the hard particulate material and subsequently infiltrating with the brazing material.

Description

[0001] The présent application daims priority to U.S. Provisional Application No. 61/472,470, filed April 6, 2011, which application is incorporated by reference herein in its entirety and made part hereof.

Technical Field of the Disclosure [0002] This disclosure relates to various embodiments of a hardfaced part for use in abrasive environments formed using infiltration brazing or another brazing technique. More particularly, the disclosure relates to products, Systems and methods that pertain to such hardfaced parts. For example, such hardfaced parts can include wear-resistant tools used for ground-engaging machinery (e.g., a point for an excavator), minerai processing equipment such as a tip for a dual roll crusher, trommel screens, or other abrasive applications.

Background [0003] Examples of wear parts produced by infiltration of hard particles are disclosed in U.S. Patent Nos. US4884477, US4949598, and US6073518, and in the publications US20100278604, GB2041427, and W02008103688. Older publications more generally describing manufacturing cemented carbides by an infiltration process include US1512191 and DE420689C (Schroter, 1925, Deutsches Reich). The disclosures of these and ail other publications referenced herein are incorporated by reference in their entirety for ail purposes. The présent invention seeks to overcome certain limitations of these devices and other existing devices, and to provide new features not heretofore available.

Brief Summary [0004] Economical and effective hardfaced wearparts are provided, formed from a substrate, a thin shell, hard particles held within a cavity defined between

the substrate and the shell, and infiltration brazing material that binds these éléments into a composite wearpart. The thin métal shell is expendable, because it typically erodes quickly during use of these hardfaced wearparts. Methods for making such wearparts using infiltration brazing and expendable thin sheils also 5 are provided.

[0005] Aspects of the invention relate to a hardfaced wear part that includes a steel substrate, a steel shell joined to the substrate to define a cavity between the substrate and the shell, and a hard composite filling the cavity, the composite including hardened particles infiltrated with métal brazing. This hardfaced wear 10 part preferably is one where the shell weighs substantially less than the substrate. Furthermore, the shell preferably defines a réservoir outside of the cavity, and more specifically, a flared réservoir outside of the cavity. In some embodiments, the shell defines a funnel-shaped réservoir outside of the cavity. In some of the embodiments, this shell is welded to the substrate.

[0006] Aspects of the invention also relate to an article, such as a hardfaced wearpart, that includes a substrate, a sheet métal shell connected to the substrate to define a cavity between the surface of the substrate and the shell, and a composite material filling the cavity and forming a coating on at least a portion of the surface of the substrate, the composite material including a hard 20 particulate material infiltrated with a metallic brazing material.

[0007] According to one aspect, the shell has an opening to provide access to the cavity to facilitate the insertion of the hardfacing material and the feeding in of the brazing material. The shell may also include a réservoir connected to the shell and positioned outside the cavity in communication with the opening to 25 initially hold the brazing material during manufacture.

[0008] According to another aspect, the shell may be connected to the surface of the substrate by welding or brazing. The shell may further include a conformai band in surface-to-surface contact with a portion of the surface of the substrate around an entire periphery of the shell, such that the shell is connected 30 to the substrate by welding or brazing at least at the conformai band. In this

configuration, the substrate may hâve a bonding surface in surface-to-surface contact with the conformai band, and at least a portion of the substrate within the cavity may be inset with respect to the bonding surface, such that the composite material has an outer surface that is flush with the bonding surface.

[0009] According to a further aspect, the brazing material may be bonded to the surface of the substrate, and may further be bonded to the shell as well.

[0010] According to yet another aspect, the shell may include a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the back piece, where the front piece and the back piece are joined together to form the shell by welding or brazing the front flange to the back flange.

[0011] According to an additional aspect, the particulate material may be or include tungsten carbide, and the metallic brazing material may be or include NiCr-Si-B brazing alloy powder.

[0012] According to a still further aspect, the substrats may hâve a hole in the surface, and an insert rod may be received in the hole, such that the hole is covered by the composite material.

[0013] Additional aspects of the invention relate to a tool having a surface at a point of the tool and a bonding surface located proximate the surface, a composite hardfacing material forming a coating on at least a portion of the surface, and a sheet métal shell in contact with the composite material and surrounding the composite material. The composite hardfacing material includes a hard particulate material infiltrated with a metallic brazing material, where the metallic brazing material is bonded to the surface to connect the composite hardfacing material to the tool. The shell has a conformal’band in contact with the bonding surface of the tool, and the shell is connected to the tool by welding or brazing at least between the conformai band and the bonding surface. A cavity is defined between the surface of the substrate and the shell, and the composite hardfacing material fills the shell.

[0014] Other aspects of the invention relate to a composite wear-resistant tool, comprising a steel shell that defines a cavity, a steel substrate partially filling the cavity to define a void between the shell and the substrate, and a hard composite at least partially filling the void and including hardened particles 5 infiltrated with métal brazing.

[0015] Other aspects of the invention relate to a hardfaced wear part comprising a steel shell that defines a cavity, a steel substrate only partially filling the cavity, and a hard composite in close contact with both the shell and the substrate to define a hard layer protecting the substrate from wear, the 10 composite including hardened particles infiltrated with métal brazing.

[0016] Still other aspects of the invention relate to a hardfaced wear part for earth-moving equipment, comprising a steel substrate, a steel shell generally conforming to at least a portion of the surface of the substrate, defining a cavity between the surface and the shell, and a hard composite at least partially filling 15 the cavity and bonding to both the substrate and the shell, the composite including hardened particles infiltrated with métal brazing. Preferably, the shell has an average shell thickness, the substrate has an average substrate thickness, and the average shell thickness is substantially less than the average substrate thickness.

[0017] Further aspects of the invention relate to a composite wear résistant tool comprising a thin métal shell defining an outer perimeter for a hard composite, a thick métal substrate defining a primary body for a tool, the substrate at least partially surrounded by the shell, and a layer of hard particulate material infiltrated with a brazing alloy defining a hard composite bonded to both 25 the shell and the substrate;

[0018] Still further aspects of the invention relate to an article that includes a substrate, a métal shell connected to the substrate to define a cavity between the surface of the substrate and the shell, a hard material positioned within the cavity, and a metallic brazing material bonding the hard material to the surface of 30 the substrate. As described above, the hard material and· the metallic brazing

material may form a composite hardfacing material covering the surface of the substrate. In one configuration, the hard material may hâve a porous structure, such as a particulate material or a porous preform, that is infiltrated by the metallic brazing material to form the composite hardfacing material. In another 5 configuration, the hard material may hâve a monolithic structure.

[0019] Aspects of the invention also relate to a method for use with a substrate, including connecting a sheet métal shell to the surface of the substrate to define a cavity between the shell and the surface, placing a hard particulate material within the cavity, in close proximity to the surface, placing a 10 metallic brazing material in communication with the cavity, heating the brazing material to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to infiltrate the particulate material in molten form and contact the surface of the substrate, and cooling the brazing material to solidify the brazing material and form a wear 15 résistant composite coating on the surface of the substrate. The brazing material may be bonded to the surface and/or the shell after the brazing material is solidified.

[0020] According to one aspect, the shell has an opening to an exterior of the shell and a flared réservoir is connected to the shell and positioned outside the 20 cavity in communication with the opening, and the brazing material is placed within the réservoir to be in communication with the cavity. The réservoir may be integrally formed with the shell.

[0021] According to another aspect, connecting the shell to the substrate includes welding or brazing the shell to the surface of the substrate. The shell 25 may further include a conformai band extending around a periphery of the shell.

In this configuration, connecting the shell to the substrate may include welding or brazing the conformai band to the surface of the substrate, such that the conformai band is in surface-to-surface contact with a portion of the surface of the substrate around the entire conformai band.

[0022] According to a further aspect, the shell includes a front piece having a front flange extending transverseiy from a back edge of the front piece and a back piece having a back flange extending transverseiy from a front edge of the back piece. The method may further include joining the front piece and the back 5 piece together to form the shell by welding or brazing the front flange to the back flange, [0023] According to yet another aspect, the brazing material is heated to a température sufficient to melt the brazing material, for sufficient time to allow the brazing material to infiltrate the spaces between the hard particles, bonding them 10 together and to the substrate. For example, if using tungsten monocarbide (WC) hard particles and pure copper or AWS BNi-2, the brazing material may be heated to a température of approximately 2050°F for 30 minutes to 1 hour in many applications. This heating may be done in a vacuum furnace in one configuration.

[0024] According to an additional aspect, the method also includes forming the shell, such as by welding or brazing pièces of sheet métal together to form the shell. Other techniques may additionally or alternately be used.

[0025] Other aspects of the invention relate to a method for producing a composite wear-resistant tool that includes the step of infiltrating a layer of hard 20 particles confined between a substrate and an expendable sheet-metal shell.

The shell may be constructed such that it confines the hard particles to desired locations on the substrate, with spécifie thicknesses and shapes defined by contours of both the substrate and the shell. The shell may also be constructed such that it defines a réservoir for containing infiltrating material which will be 25 melted during the step of infiltrating. Almost any type of tool or component that is hardfaced now by welding could be hardfaced by the disclosed methods. These methods may include a step where the particulate material is selected with a type and size distribution so as to give the desired degree of wear résistance for the intended application. These methods may include a step where the 30 particulate material and its size distribution, as well as the type of infiltrating material employed are selected so as to give a desired degree of wear

résistance for an intended application, while at the same time accommodatmg the thermal and transformation expansion différences between the infiltrated layer and the substrate so as to minimize or eliminate cracking and spalling.

[0026] Other aspects of the invention relate to a method of hardfacing métal parts to produce wear-resistant composite products that involves surrounding the part or a portion of the part to be hardfaced with a sheet métal shell, leaving a cavity, welding or high-temperature brazing the shell to the substrate so that the cavity will retain molten métal when heated, at least partially filling the cavity with granular or powdered particles of a wear-resisting material, and then infiltrating the particles with a suitable low-melting material to bond the particles to each other and to the substrate by heating. More spécifie embodiments of a method include providing a réservoir that is intégral to the shell, placing a brazing alloy in the réservoir, heating a combined assembly of substrate, shell, particles of wearresisting material, réservoir and brazing alloy so that the brazing alloy melts and flows into interstices within the particles of wear-resisting material, and cooling the assembly so that the substrate, the shell, the particles of wear-resisting material, and the brazing alloy are bonded together to form a composite wearresistant wearpart.

[0027] Other aspects of the invention relate to a method that includes connecting a métal shell to a surface of a substrate to define a cavity between the shell and the surface, placing a hard material within the cavity, placing a metallic brazing material in communication with the cavity, heating the brazing material to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to contact the hard material and the surface of the substrate in molten form, and then cooling the brazing material to solidify the brazing material and bond the hard material to the surface of the substrate. As described above, the shell may be formed of sheet métal. As also described above, the hard material may be infiltrated by the molten brazing material to form a wear résistant composite material.

[0028] Aspects of the invention also relate to an assembly that includes a tool having an surface configured for engaging earth to move the earth, and a sheet métal shell connected to the tool and having a conformai band conforming to at least a portion of the surface to define a cavity between the surface and the 5 shell. The sheil may further hâve an opening to an exterior of the shell. The shell is connected to the tool by welding or brazing the conformai band to the at least a portion of the surface.

[0029] According to one aspect, the assembly is configured for forming a wear résistant composite coating on the surface by at least partially filling the 10 cavity through the opening with a hard particulate material, placing a metallic brazing material in communication with the cavity, heating the assembly to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to infiltrât© the particulate material in molten form and contact the surface of the tool, and 15 cooling the assembly to solidify the matrix material and form the wear résistant composite coating on the surface. The assembly may also include a flared réservoir connected to the shell and positioned outside the cavity in communication with the opening, where the réservoir is configured to hâve the brazing material placed therein to be in communication with the cavity. After this 20 process, the assembly may include the composite material filling (or partially filling) the cavity and forming a coating on at least a portion of the surface of the tool, where the composite material includes a hard particulate material infiltrated with a metallic brazing material. The brazing material may be bonded to the surface and/or the shell.

[0030] According to another aspect the assembly also includes a flared réservoir connected to the shell and positioned outside the cavity in communication with the opening. The flared réservoir may be integrally formed with the shell.

[0031] According to a further aspect, the conformai band extends around an 30 entire periphery of the shell and around an entire periphery of the surface.

[0032] According to yet another aspect, the shell may include a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the back piece, where the front piece and the back piece are joined together to form the shell by welding or brazing the front flange to the back flange.

[0033] According to an additional aspect, the tool has a hole in the surface, and the assembly further includes an insert rod received ,in the hole. In this configuration, spaces may be defined between the insert rod and an interior wall of the hole.

[0034] Still further aspects of the invention relate to an assembly that includes a tool having an operating surface, a sheet métal shell covering at least a portion of the operating surface and defining a cavity between the shell and the operating surface, and a plurality of spacers engaging the tool and the shell and separating the tool from the shell. The shell has an opening to an exterior of the shell.

[0035] According to one aspect, the assembly is configured for forming a wear résistant composite coating on the operating surface by at least partially filling the cavity with a hard particulate material, placing a metallic brazing material in communication with the cavity, heating the assembly to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to infiltrate the particulate material in molten form and contact the operating surface of the tool, and cooling the assembly to solidify the matrix material and form the wear résistant composite coating on the operating surface. After this process, the assembly may include a composite material at least partially filling the cavity and forming a coating on at least a portion of the operating surface of the tool, the composite material comprising a hard particulate material infiltrated with a metallic brazing material, wherein the brazing material is bonded to the operating surface.

[0036] According to another aspect, the assembly may also include a wall extending from the shell and defining a réservoir connected to the shell and

positioned outside the cavity in communication with the opening, where the réservoir is configured to hâve the brazing material placed therein to be in communication with the cavity.

[0037] Still further aspects of the invention relate to an assembly that may be usable for forming a hardfacing material on the surface of a tool or other substrate. A métal shell is connected to the substrate and has a conformai band conforming to at Ieast a portion of the surface of the substrate to define a cavity between the surface and the shell. The shell further has an opening to an exterior of the shell. The shell may be formed of sheet métal in one configuration, and may be welded or brazed to the substrate, as mentioned above.

[0038] Advantages of the présent disclosure will be more readily understood after considering the drawings and the Detailed Description.

Brief Description of the Drawings [0039] Figs. 1 -4 are perspective views of one embodiment of wearpart with an attached shell.

[0040] Fig. 5 is a top plan view of the embodiment of- a wearpart with an attached shell, as shown in Figs. 1 -4.

[0041] Fig. 6 is a bottom plan view of the embodiment of a wearpart with an attached shell, as shown in Figs. 1 -5.

[0042] Fig. 7 is a left side élévation of the embodiment of a wearpart with an attached shell, as shown in Figs. 1 -6.

[0043] Fig. 8 is a right side élévation of the embodiment of a wearpart with an attached shell, as shown in Figs. 1 -7.

[0044] Fig. 9 is a front élévation of the embodiment of a wearpart with an attached shell, as shown in Figs. 1 -8, with hardfacing material visible inside the shell, protecting a substrate.

[0045] Fig. 10 is a front élévation of an alternate embodiment of a wearpart, in the form of a finished hardfaced wearpart with an attached shell, viewed similarly to the embodiment of Fig. 9. Portions of the shell, seen in Fig. 9 hâve been removed.

[0046] Figs. 11-17 are views corresponding to the views of Figs. 1-7, respectively, but showing the finished hardfaced wearpart of Fig. 10.

[0047] Fig. 18 is a perspective view of another embodiment of wearpart with an attached shell, including a réservoir formed as a funnel.

[0048] Fig. 19 shows a perspective view of a two-part shell for yet another embodiment, with the shell shown in a vertical orientation.

[0049] Fig. 20 is a top plan view of the embodiment of a shell according to Fig. 19, but including a wearpart with an attached two-part shell, and with the wearpart and the shell shown in a vertical orientation.

[0050] Fig. 21 is a left side élévation of the embodiment shown in Fig. 20 of a wearpart with an attached two-part shell.

[0051] Fig. 21a is a left side cross-sectional view of the wearpart of Figs. 20 and 21, shown with an attached two-part shell having another configuration.

[0052] Fig. 22 is a cross sectional view of the embodiment of Figs. 20 and 21, taken generally along line 22-22 in Fig. 20.

[0053] Fig. 23 is a cross sectional view of the embodiment of Figs. 20 and 21, taken generally along line 23-23 in Figs. 20 and 21.

[0054] Fig. 24 shows a cross-sectional view of the embodiment of Fig. 18, taken generally along a plane similarly to the plane used to define the crosssectional view of Fig. 22, but with a substrate and shell shown in a horizontal orientation.

[0055] Fig. 25 shows multiple views, a-j, as part of manufacturing a wearpart, generally according to the embodiment of Figs. 19-23.

[0056] Figs. 26 and 27 show a perspective view of two different embodiments of an underlying substrate that may be used to manufacture a hardfaced wearpart. In both Figs. 26 and 27, the substrate, more specifically a point, is oriented vertically.

[0057] Fig. 28 îs front élévation of a substrate and an attached shell, viewed similarly to Figs. 20 and 25c, with a schematic représentation of two holes each including a hardened insert and two spacers.

[0058] Fig. 29 is a photograph of two hardened inserts for use as with the substrates shown in Fig. 28.

[0059] Fig. 30 is a plan view of a spacer shown in Fig. 29.

[0060] Fig. 31 is a photograph of two examples of the embodiment of a substrate shown in Fig. 27, each example shown with a shell welded in place, ready to receive a proper amount of hard particles and an infiltrant brazing powder.

[0061] Fig. 32 is a photograph of two examples of the embodiment of a substrata and shell shown in Fig. 28, each example shown with the shell filled with infiltrant brazing powder.

[0062] Fig. 33 is a photograph of the two examples from Fig. 32, loaded into a furnace.

[0063] Fig. 34 is a photograph of one of the examples from Figs. 32 and 33, after the shell has worn away during initial digging.

[0064] Fig. 35 is front élévation of a substrate and an attached shell, viewed similarly to Fig. 28, with a schematic représentation of three holes, with a central hole including a hardened insert.

[0065] Fig. 36 is a cross sectional view of the embodiment of Fig. 35, taken generally along line 36-36 in Fig. 35.

[0066] Fig. 37 is a cross sectional view of the embodiment of Fig. 36, with granular carbtde particles filling a cavity defined between the substrate and the shell.

[0067] Fig, 38 is a cross sectional view of the embodiment of Fig. 37, with brazing material filling a réservoir formed by the shell, above the carbide particles.

[0068] Fig. 39 shows a cross-sectional view of the embodiment of Fig. 35-38, after an infiltration brazing cycle with hardfacing material surrounding and protecting the substrate.

[0069] Fig. 40 is a photograph of granular carbide, on the right, and brazing alloy powder on the left.

[0070] Fig. 41 is a graph representing a sample furnace cycle, with température along the vertical axis, and time along the horizontal axis.

[0071] Fig. 42 shows multiple views, labeled a-k, as part of manufacturing another embodiment of a wearpart. The different drawings 42a-42k illustrate selected processing steps as part of infiltration hardfacing a 'dual roll crusher tip.

[0072] Fig. 43 shows multiple views, labeled a-f, as part of manufacturing another embodiment of a wearpart. The different drawings 43a-43f illustrate selected processing steps as part of infiltration hardfacing a dual roll crusher tip, using a shell formed with a venting tube.

[0073] Fig. 44 shows a perspective view of another embodiment of a hardfaced wearpart, with a spherical structure having a .particularly complex surface shape.

[0074] Fig. 45 shows multiple views, labeled a-k, as part of manufacturing another embodiment of a wearpart. The different drawings 45a-45k illustrate selected processing steps as part of infiltration hardfacing a trommel screen for use in minerai dressing.

Detailed Description [0075] While this invention is susceptible of embodiment in many different forms, there are shown in the drawings, and will herein be described in detail, preferred embodiments of the invention with the understanding that the présent disclosure is to be considered as an exemplification of the principles of the

invention and is not intended to limit the broad aspects of the invention to the embodiments illustrated and described.

[0076] In general, the disclosure relates to the use of a métal shell in forming a composite material or other wear résistant material on the surface of a 5 substrate, such as a wearpart, using brazing and/or infiltration techniques, as well as articles formed using such techniques and methods and equipment incorporating such techniques. For example, an article (e.g. a hardfaced wearpart) formed using such techniques may include a substrate, a sheet métal shell connected to the substrate to define a cavity between the surface of the 10 substrate and the shell, and a composite material filling (or partially filling) the cavity and forming a coating on at least a portion of the surface of the substrate, the composite material including a hard particulate material infiltrated with a metallic brazing material. In a more general example, an article formed using such techniques may include a substrate, a métal shell connected to the 15 substrate to define a cavity between the surface of the substrate and the shell, a hard and/or wear résistant material positioned within the cavity, and a metallic brazing material bonding the hard material to the surface of the substrate.

[0077] One embodiment of an article in the form of a hardfaced wearpart 10 is shown in Figs. 1 -9 in the form of a mining point. Unless otherwise specified, a 20 hardfaced wearpart may contain at least one of the structure, components, functionality, and/or variations described, illustrated, and/or incorporated herein. Two basic components of hardfaced wearpart 10 include a primary tool, forming a structural component 12, or more generally a substrate 12, and an outer expendable métal shell 14 forming a mold for hardfacing material. Preferably, 25 substrate 12 is made of métal, such as a steel alloy as is known in the art for ground-engaging tools, and shell 14 is made of sheet métal, such as low-carbon mild” steel. The sheet métal of shell 14 may be made of any material capable of being formed or fabricated to a particular desired shape and capable of withstanding dissolution, melting, or undue weakening by the infiltrating material, 30 or generally by the températures required for infiltration brazing, during the infiltrating process. A variety of other parts and structures may be used to form

the substrate 12 and produce the hardfaced wearpart 10 having the hardfacing material thereon. Examples of such parts and structures include other types of points, shrouds, or runners; teeth for buckets or dredge cutter heads; blades for graders, scrapers, etc.; wear liners for various applications such as for chutes or 5 truck bodies; earth engaging equipment used, e.g., in mining, construction, or drilling; parts for minerai processing equipment such as a tip for a dual roll crusher or a trommel screen; and nearly any other desired parts and structures. The invention may also be used to renew worn parts; the worn parts may be wear parts such as a ground engaging tool or a supporting structure such as a 10 lip of a bucket.

[0078] Hardfacing material bonds to and protects substrate 12, but this hardfacing material is not readily visible in Figs. 1-8, because the hardfacing material is enclosed by shell 14. In general, the hardfacing material includes a hard material and a metallic brazing material bonding the hard material to the 15 substrate 12. The hard material generally has a higher· hardness than the surface of the substrate 12 that is hardfaced. The hard material may also hâve greater wear résistance than the surface of the substrate 12. As discussed in more detail below, the hardfacing material may be a composite formed from a hard material in the form of hard particles, typically available in particulate (e.g. 20 granular or powdered) form such as tungsten carbide particles, infiltrated with an infusing metallic brazing material typically available in granular or powdered form such as a copper-base or nickel-base brazing alloy. It is understood that “metallic materials may include pure metals, as well as alloys and other materials including one or more metals. In another embodiment, the hard 25 material may be in the form of a porous material, which includes particulate material, porous preforms (e.g. sintered preforms), or other porous structure that can be infiltrated by the brazing material. Preferably, such a porous material may hâve a porosity of 5-50%, but may hâve a different porosity in other embodiments. In a further embodiment, the hard material may be a solid, 30 monolithic structure (or multiple structures), such as a tile, plate, or other monolithic structure that is bonded to the surface of the substrate 12 by the

brazing material. In each of these embodiments, the shell 14 is used to hold the hard material in a cavity 50 defined between the shell 14 and the outer surface of the substrate 12, in position for brazing, such as in close proximity to the surface of the substrate 12.

[0079] Shell 14 includes a shell body 16, with an opening 17 to the exterior of the shell body 16 and the cavity 50 defined by the shell body 16, as well as a réservoir 18 in communication with the opening 17. In one embodiment, the réservoir 18 may be integrally formed with the shell body 16, or the réservoir 18 may be formed separately and joined to the shell body 16 in another 10 embodiment. Réservoir 18 is only used during fabrication of wearpart 10, and may be removed (e.g. eut off) or simply ailowed to erode away during operational use of wearpart 10, as discussed in more detail below. Shell 14 is joined to substrate 12 by a conformai band 20, by which shell 14 may be welded to substrate 12. The conformai band 20 may be in surface-to-surface contact 15 with a portion of the substrate 12 around part or ali of the periphery of the shell and the substrate, as discussed below. Alternatively, shell 14 may be brazed to substrate 12, provided that any brazing material used to braze shell 14 to substrate 12 has a melting température that is higher than a melting température for the infusing brazing material. In further embodiments, the shell may be 20 connected to the substrate 12 in another manner. For exemple, the shell may be placed over the substrate 12 using a gasket of ceramic felt or cloth to seal the cavity and prevent leaking of the brazing material during brazing.

[0080] Fig. 9 most clearly shows an example embodiment where that shell 14 has a shell thickness 22 that is substantially less than a nominal thickness of 25 substrate 12. For example, shell 14 may hâve an average shell thickness of approximately 0.105 in., whereas substrate 12 in Figs. 1-9 may hâve a thickness ranging from 1.000 to 3.450 in. in the région covered by the shell. In one embodiment, the shell 14 may be made of sheet métal in the range of 16 Ga (0.060 in. thick) to 10 Ga (0.135 in. thick), which may be useful for a wide range 30 of applications. In other embodiments, the shell 14 may hâve any other suitable thickness. For example, in further embodiments, the shell 14 may be made of a

steel or other metallic plate having a thickness of approximately 0.25 inches, or may be cast, machined from bar stock, or formed in a different manner. It is understood that different portions of the shell 14 may hâve different thicknesses. Also visible in Fig. 9 is a layer of composite hardfacing material, indicated 5 generally at 24.

[0081] The relative thinness of shell 14 when compared to substrate 12 means that shell 14 may be formed easily, relatively inexpensively. For simple shapes of a shell, a relatively low-cost shell 14 may be made by cutting pièces of sheet métal, and welding or brazing those pièces together. Slightly more 10 complicated shapes may be made by bending pièces of sheet métal in particular configurations, and then welding the bent sheet métal pièces together. Complex shapes can be made by sheet métal forming processes such as deep drawing, forming by the Guérin process (rubber pad forming), hydroforming, and/or explosive forming. Précision (‘lost wax) casting could be used as well, although 15 the cost of the lost wax process would often be uneconomical. For particularly complicated shapes, pièces of the shell could be formed by one or more of these processes, and then joined by welding or brazing.

[0082] Very little material is required to form an effective mold, even for relatively large substrates. For example, in the case of mining point 10, the 20 weight of shell 14 would be only about 4½ pounds whereas the weight of the substrate 12 would be 224 pounds. This particular weight of a mining point and shell is merely one example, for one particular sized point. Large variations are possible as to the size of different points in use for different operations. However, ail of the embodiments disclosed herein include a substrate and shell, in which 25 the shell weighs substantially less than the substrate.

[0083] The shell is expendable, performing no structural function in the finished product and usually wearing away quickly during use of the resulting hardfaced wearpart. Accordingly, the particular métal used to form shell 14 need only be strong enough and sufficiently résistant to dissolution to survive the high 30 températures of infiltration brazing. Many readily available, relatively low-cost sheet steels will meet this standard. The combination of a minimal amount of

material, for example less than 5-pounds of sheet steel for a 224-pound substrate, the use of readily available sheet steel, and the use of relatively easy fabrication techniques to make thin métal shell 14 means thgt the cost of shell 14 is often minimal, when compared to a market value of the resulting hardfaced wearpart 10.

[0084] In many applications, the tool substrate can be quite large and heavy, and the tool substrate is often transported or handled with the substrate in a particular orientation relative to gravity. For example, a very heavy substrate may be held securely on a skip or in a fixture, with a région to be hardfaced facing upward. Other substrates may be supported by a base or spécifie surface, with a région to be hardfaced facing upward, sideways, or downward. Yet other substrates may hâve multiple separate régions to be hardfaced, facing in multiple different orientations.

[0085] The light sheet métal shell of the présent disclosure may be readily moved for précisé alignment on a substrate, and then welded to the substrate, regardless of most orientations of the substrate. The thin métal shell is easy to attach reliably to the underlying substrate by welding or high température brazing, without the need for clamping or fixtures, and the joint created is fluidtight even at the high températures required for infiltration brazing. In any type of infiltration hardfacing involving molds, the molten métal brazing material should remain inside the mold. With the thin métal shells of the présent disclosure, reliable attachment to a substrate is achieved without extra clamping or fixtures. The resulting assembly is therefore more easily placed in a furnace for infiltration brazing, allowing substantially greater ease of infiltration hardfacing heavy items.

[0086] Furthermore, the thin métal shell that defines the mold for the infiltration hardfacing may be assembled reliably from multiple parts, and with side-ways-facing opening and/or downward-facing openings that are later sealed by the underlying substrate in combination with welding or high température brazing. This is very different from conventional graphite or ceramic molds for infiltration brazing, which are more difficult to seal to an underlying substrate, typically requiring extensive overlapping surfaces as shown in US4933240. Even

if such conventîonal graphite or ceramic molds are sealed to a substrate at room température, such seals may be likely to fail at the high tem'peratures needed for infiltration brazing, particularly if the substrate and the mold hâve different coefficients of thermal expansion. Accordingly, conventîonal graphite or ceramic molds often are made with upward-facing openings, into which the substrate must be placed. This means that the substrate in such prior art molds must be supported by the mold, or suspended by jigs or framework over the mold.

[0087] Supporting a heavy substrate from a mold may be difficult, and may require substrate-to-mold contact in locations that would be better coated with 10 hard facing material. The use of jigs and framework can create an even heavier and larger assembly, making it more difficult to put the combination of a mold and substrate into a furnace. The thin métal shell of the présent disclosure does not need to support the substrate, allowing numerous embodiments, with various alternative orientations of substrate and mold, and even multiple different 15 orientations of molds on a single substrate.

[0088] Fig. 10 shows a wearpart 110, representing wearpart 10 of Fig. 9, after removal of réservoir 18. This allows transport and handling of wearpart 110 without any interférence from réservoir 18. Figs. 11-17 correspond to Figs. 1 -7, again without réservoir 18. For clarity, part numbers hâve been used in Figs. 1020 17 that correspond to the part numbers of Figs. 1-9, but with an added leading

Ί,” including a substrate 112, a shell 114, and a layer of hardfacing material 124.

[0089] It will be seen from Figs. 10-17 that the thinness of shell 114 results in a finished wearpart 110 that closely matches a desired final shape and weight of 25 a wearpart for operational use. For example, mining points are sized and shaped for digging into particular types of earthen material. The thinness of shell 114 is particularly advantageous because a new, unused point 110, enclosed with an expendable shell 114, has an outer shape that will penetrate earthen material almost identically to an outer shape of such a wearpart 110, after shell 114 30 wears away. Similarly, mining equipment opérâtes in particular ways based on the weight of any attached ground engaging tools, such as points on a bucket. A

new, unused point 110, enclosed with an expendable shell 114, has a weight that is almost identical to a weight of such a wearpart 110, after shell 112 wears away. In the example discussed above, the shell has a weight that is approximately only 2% of the weight of the substrate. After adding the weight of the hardfacing material, the différence in weight of a finished wearpart according to this embodiment, with and without the expendable shell, will vary less than 2%.

[0090] In the embodiment of Figs. 1-9, réservoir 18 is shown as a flared opening, generally coaxial to a long axis of substrate 12, as well as a long axis of 10 shell body 16 and of shell 14. Another embodiment may include a réservoir that is generally perpendicular to a long axis of a substrate, as well as a long axis of a shell body and of a shell. Such an embodiment is shown in Fig. 18, in which part numbers hâve been used that correspond to the part numbers of Figs. 1 -9, but with an added leading ‘'2,” including a substrate 212, a shell 214, and a 15 réservoir 218 in communication with an opening 217 of the shell 212. Réservoir

218 preferably is substantially funnel shaped, with a large mouth 218a, but a relatively small neck 218b. This minimizes any resulting blemish in shell 214, after removal of réservoir 218, which may make for a more visually appealing wear part 210, when new. It also allows for different orientation of substrate 212 20 and shell 214 during infusion brazing, as discussed below, so that various shapes of substrates and shells may be accommodated in partîcular processing facilities, also discussed below. Finally, it may allow for a slightly different composite structure, after infusion brazing, because of a different orientation of substrate 212, shell 214, and réservoir 218 during infusion brazing, relative to 25 gravity, when compared to a normal orientation of substrate 12, shell 14, and réservoir 18 during infusion brazing.

[0091] It is usually simplest to locate any such réservoir portion of a shell above the body of the shell. This arrangement is generally the most favorable as it allows gravity to assist capillary action during the infiltration process. The effect 30 of gravity may be captured by increasing a height 218H of the neck of a funnel, increasing the effective head of molten brazing material contained in a

corresponding Tunnel shaped réservoir. However, capillary action alone may be sufficient in some cases, between hardened particles and melted brazing material, even allowing the melted brazing material to “run uphill” for moderate distances.

[0092] Yet another embodiment of a shell is shown in Fig. 19, as a two-part shell 314, having a two-part conformai band 320. A two-part shell body 316 of shell 314 may be initially formed from a front half piece 326 and a back half piece 328, having a front flange 330 or a rear flange 332, respectively. Front flange 330 extends transversely from the back edge of the front half 326 and rear flange 332 extends transversely from the front edge of the back half 328. Front flange 330 may be joined to rear flange 332 by welding or brazing with a brazing material having a higher melting température than the material intended for infiltration. Two-part shell 314 may be more easily formed than a corresponding one-part shell, in certain configurations. Two-part shell 314 may also be more easily joined to a corresponding substrate, in certain configurations, when compared to such joining with a corresponding one-part shell.

[0093] Two-part shell 314 is shown joined to a portion of a corresponding substrate 312 in the form of a point, in Figs. 20 and 21. Details of an outer geometry for substrate 312 are visible, because shell 314 is represented as partially transparent. An outer geometry for substrate 312 may include a primary body 334 that defines a bonding surface 335 for welding or brazing to conformai band 320. The substrate 312 may provide at Ieast some recess or other relief for the bonding of the hard material. For example, in the embodiment shown in Figs. 20 and 21, the substrate 312 has a plateau 336 slightly inset from an outer surface of primary body 334, and further inset is a valley 338. Plateau 336 may define a ledge 340, and a ramp 342. A distal end of substrate 312 may be shaped to define an angular edge 344, and/or a rounded face 346. In another embodiment, the substrate 312 may not provide any recess or other relief for the hard material.

[0094] Cross sectional viaws of the embodiment of Figs. 20 and 21 are shown in Figs. 22 and 23. Shell 314 extends smoothly away from conformai band 320, defining a cavity 350 between substrate 312 and shell 314. Cavity 350 includes the recess defined by valley 338, and other relative recesses where the 5 distal end of substrate 312 is formed with a reduced thickness relative to shell

314. Cavity 350 defines a resulting thickness of hardfacing material bonded to substrate 312, and the inner geometry of shell 314 defines an ultimate outer geometry of a finished point. In the embodiment of Figs. 20-23, the hardfacing material that will be bonded to substrate 312 generally extends fairly smoothly 10 from adjacent portions of substrate 312, approximately even with the outer surface of substrate 312, rearward of the resulting hardfacing material. In Figs.

and 23, inside surfaces of shell 314 are flush with portions of substrate 312. For example, at conformai band 320 this provides a close fit with the bonding surface 335 to locate shell 314 precisely, relative to substrate 312. At other 15 locations, such as plateau 336, this flush mounting is simply because hardfacing material is not needed, or even because hardfacing material is undesired at such locations. The résultant hardfacing material 324 is flush with adjacent portions of the substrate 12. For example, in the embodiment illustrated, the hardfacing material 324 is flush with the bonding surface 335, as well as other surfaces of 20 substrate 312 that contact the inside surfaces of the shell 314 (e.g. plateau 336).

By not having hardfacing material 324 stand up higher than the adjacent surface of substrate 312, the force required to push point 310 into earthen material is lowered. The aesthetics of hardfaced point 310 are also better without a visually thick hardfacing layer protruding above surrounding surfaces of substrate 312.

However, in another embodiment, shown in FIG. 21a, a shell 314 may flare out from a conformai band 320, so that the hardfacing material that will be bonded to the substrate adds substantially to a thickness of the point, enlarging the distal end of the point relative to the adjacent portions of the substrate 312, including relative to the bonding surface(s) 335.

[0095] Fig. 24 shows a cross-sectional view of the embodiment of Fig. 18, viewed similarly to the cross-sectional view of Fig. 22, but with substrate 212 shown in a horizontal orientation.

[0096] Fig. 25 shows multiple views, a-j, as part of manufacturing a wearpart

310. The different drawings 25a-25j illustrate selected processing steps as part of infiltration hardfacing a mining bucket point. Fig. 25a shows a substrate in the form of a point 312, of a type used for mining buckets, before attachment of any shell, and before forming any layer of hardfacing material on substrate 312. [0097] Figs. 25b, 25c, and 25d correspond directly to Figs. 19, 20, and 21.

Substrate 312 is referred to above more generally as substrate 312. Only a portion of substrate 312 is shown in Figs. 25c and 25d, and that portion is oriented generally vertically, when compared to a generally horizontal orientation of substrate 312 in Fig. 25a. Shell 314 is formed in two halves, and then welded together along flanges, as discussed above. Shell 314 is installed on substrate

312 and then welded in place along its bottom edge, discussed above as conformai band 320. Alternatively, the two halves of shell 314 may first be clamped in place or otherwise held on substrate 312, and then welded together, and/or welded to substrate 312, to better accommodate various surface geometries of substrate 312 and shell 314. When steel shell 314 is joined to substrate 312, the steel shell and the substrate define a cavity 350 between the substrate and the shell.

[0098] In Figs. 25e a hard material in the form of hard particles 352 is introduced into the defined cavity 350 by pouring through the opening 317 in communication with the cavity 350, with the flare of réservoir 318 making it easier to pour in hard particles 352. These hard particles 352 may be allowed to simply fill cavity 350 with gravity feed, or the hard particles 352 may be tamped and/or vibrated, or otherwise packed into place inside the defined cavity 350. In another embodiment, a different type of hard material may be used, including those described above. Additionally, the particles 352 may not completely fill the cavity 350 in another embodiment, as desired. As shown in Fig. 25f, an infiltrant brazing material 354 in powder form may then be poured above the hard particle

layer, held in réservoir 318 of shell 314. The brazing material 354 may be in a different (i.e. non-powdered) form in another embodiment, as described below. As shown in Fig. 25g, réservoir 318 may be sized to define a correct volume of infiltrant brazing material 354, relative to the defined volume of cavity 350 and the hard particle layer 352 held in cavity 350, provided that infiltrant brazing powder 354 is used to substantially fill réservoir 318. The entire assembly in Fig. 25g, including substrate 312, shell 314, the layer of hard particles 352, and the layer of infiltrant brazing powder 354, is ready for an infiltration cycle, as described below.

[0099] The infiltration cycle is carried out in a furnace, of the type represented in Fig. 25h. Preferably, the furnace is a vacuum furnace, although other types of furnaces may be used. The entire assembly of Fig. 25g is placed in such a furnace for the infiltration cycle, during which time the entire assembly is heated to a température high enough to melt infiltrant brazing powder 354. This causes molten brazing material to infiltrate the layer of hard particles 352, forming a composite 324, made up of hard particles 352 infused with an infusing metallic brazing material 354. The infusing brazing material bonds to substrate 312 and hard particles 352.

[00100] The infusing brazing material may also bond to shell 314, although this is not essential. After infiltration, therefore, shell 314 typically is permanently bonded to substrate 312. When the resulting wear-resistant point is used for digging, shell 314 simply wears away, exposing infiltrated layer 324 to perform its wear-resisting function.

[00101] In Fig. 25j, the réservoir portion 318 of shell 314 has been removed, leaving a finished product as a hardfaced wearpart 310, and more specifically, a hardfaced point 310.

[00102] Figs. 26 and 27 show two different embodiments of an underlying substrate that may be used to manufacture a hardfaced wearpart. Fig. 26 shows substrate 312 of Fig. 25a, oriented vertically. Fig. 27 shows an alternative

embodiment of a substrate in the form of a point 412, with two holes 458 formed near a digging end of substrate 412.

[00103] In this embodiment, holes 458 provide surface'intrusions that help improve bonding between substrate 412 and the resulting composite of hard particles and brazing material. The resulting infiltrated hard material in holes 458 modifies how the resulting hardfaced wearpart wears in service. In some embodiments, the resulting infiltrated hard material in holes 458 helps maintain “sharpness and digging efficiency. Further benefits of this nature may be obtained by installing pre-manufactured hard métal inserts in holes 458.

[00104] Fig. 28 represents the embodiment of Fig. 27, with a shell 414 welded to substrate 412. An insert 460 is shown schematically, held in each hole 458. Proper spacing between inner walls of holes 458 and each such insert 460 may be provided by one or more spacers 462. Two spacers 462 are shown mounted on each insert 460. In another embodiment, no spacers 462 may be used. The spacing created by the spacers 462 can provide a transition between the substrate 412 and the insert 460 to resist cracking of the insert 460 due to expansion différences. The brazing material that forms in the spacing can deform to accommodate such différences in expansion and contraction if necessary. In an additional embodiment, the coefficient of thermal expansion of 20 the infiltrated material may be selected to be between the coefficient of thermal expansion of the insert 460 and the coefficient of thermal expansion of the substrate 412 to help reduce cracking due to expansion différences, as similarly described below.

[00105] Two such inserts 460 are shown in Fig. 29, preferably made from 25 sintered tungsten carbide. In another embodiment, the insert(s) 460 may be sintered shapes of one or more other carbides (e.g. chromium carbide, molybdenum carbide, vanadium carbide, etc.). Porous preforms of various carbides may also be used in another embodiment, including tungsten carbide (WC/W₂C), chromium carbide, molybdenum carbide, vanadium carbide, and 30 other carbides. Such porous preforms may be provided in-pure carbide form in one embodiment. In a further embodiment, the insert(s) 460 may be formed of a

ceramic or other material. If ceramic is used, one or more techniques to enhance wetting and/or bonding of the brazing material on the ceramic surface may be used (e.g. active brazing), including such techniques as described below. Preferably, spacers 462 are made from steel with a split hoop 464 and multiple 5 legs 466, and split hoop 464 is spring-like so that spacer 462 stays in place when slid onto one of inserts 460. One such spacer 462 is shown in detail in Fig.

30.

[00106] Fig. 31 is a depiction of two examples of yet another alternative embodiment, each including a substrate in the form of a point 512, and each 10 shown with a shell 514 welded in place, ready to receive a proper amount of hard particles and an infiltrant brazing material, generally as described above. Fig. 32 shows two assemblies ready for an infiltration cycle, each having a point 512 and a shell 514, filled with hard particles (not visible) and brazing material 554. Optionally, a jig 568 is removably attached to each point 512, to help 15 stabilize each point 512 during handling, and during loading and unloading of a furnace, as shown in Fig. 33.

[00107] A finished, partially-worn substrate in the form of a hardfaced point 510 according to the embodiment of Figs. 31-33, is shown in Fig. 34. Hardfaced point 510 was made placing the assembly of Figs. 32 and 33 in a furnace and 20 then heating and cooling the assembly as part of an infiltration cycle as described below. The resulting hardfaced point 10 was used in digging to wear away expendable shell 514, no longer visible in Fig. 34. The grey background surrounding hardfaced point 510 is a removable gauge that measures how much material is worn away during use of hardfaced point 510. As shown, hardfaced 25 point 510 has been hardfaced in such a way that hardfacing material 524 is “on top of the primary surfaces of point 512, so that there is a sharp, angular transition of the outer surface, progressing from point 512 onto hardfacing material 524, indicated at 524a. In certain applications, this angular surface configuration may offer spécifie benefits. In particular, the resulting enlarged 30 digging end of a point, in which hardfacing material 524 is standing above the surrounding surface of point 512, may effectively protect adjacent unhardfaced

surfaces by means of a shadowing effect, without the need for the expense or weight of hardfacing material. Sélective addition of hard-faced material may protect areas subject to substantial wear, and such hard facing material may be unnecessary on other régions of the point.

[00108] The thin métal shells of the présent disclosures are particularly useful when adding hardfacing material to points that hâve been produced by sand casting. It is typical for mining points cast using a green sand process to hâve substantial dimensional variations, such as a thickness that may vary by 0.060 inches in a région corresponding to the conformai band discussed herein, where 10 the shell of the présent disclosure would be attached. Such green-sand-cast points thus are particularly difficult to seal with non-bendable molds such as ceramic molds and graphite molds. However, the thin métal of the various shells disclosed herein may be readily deformed and bent as needed to allow proper welding of the thin métal shell to a green-sand-cast point.

[00109] Yet another embodiment is shown schematically in Fig. 35, including a substrate 612 in the form of a point with three holes 658, but only a single insert 660 in a central one of holes 658, without any spacer. Filling a shell 614 with a mixture of hard particles and brazing material, and then heating and cooling this assembly through an infiltration cycle results in a hardfaced wearpart. Figs. 3620 39 show sections through the central one of holes 658, and illustrate processing steps through which hard métal insert 660 is bonded to hole 658, at the same time an external hardfacing is applied to substrate 612. These steps are represented in the cross-sectional views of Figs. 36-39, with Fig. 39 showing a cross section of a finished hardfaced wearpart 610, including a layer of 25 hardfacing material 624 surrounding and protécting a distal end of substrate 612.

In other embodiments, the insert 660 may be received in a different hole 658 and/or the substrate 612 may include inserts 660 in multiple holes.

[00110] Approximate relative thicknesses are shown in Fig. 39 for substrate 612, shell 614, and layer of hardfacing material 624. For example, a thickness 30 672 is identified for substrate 612, a thickness 674 is identified for shell 614, and a thickness 676 is identified for layer of hardfacing material 624. Thickness 676

also represents a thickness for cavity 650. Sample values for these thicknesses are as follows:

Substrate Thickness 672 near conformai band: 3.450 inches;

Shell Thickness 674 throughout shell: 0.105 inches;

Hardfacing Thickness 676: 0.438 inches.

[00111] Fig. 40 shows two powders, including granular carbide 52, on the right, and brazing alloy powder 54 on the left.

[00112] Tungsten carbide is one example of hard particles that are particularly well suited to use as part of a hard-faced wear part made according to the présent disclosures. Pure carbides such as WC or WC/W₂C may be used, as well as mixtures of various carbides. Also, suitable granular material may be made from crushed sintered carbide material, such as recycled machine tool inserts. The most suitable size of the particulate material dépends on the intended use of the wear part, but sizes in the range of -50 Mesh to +70 Mesh are suitable for many applications. The following alloy of tungsten carbide, titanium carbide, and cobalt has been found to produce particularly effective hard-faced wear parts such as mining points or tooi tips:

Formula	Wt-%	Notes
WC	82	W=Tungsten C=Carbon
TiC	10	Ti=Titanium
Co	8	Co=Cobalt

[00113] Other carbides that may be used as the hard particles in the composite material include cast tungsten carbide (WC/W₂C), tungsten monocarbide (WC), chromium carbide, titanium carbide, molybdenum carbide, vanadium carbide, columbium carbide, chrome white iron shot or grit, among other materials, including mixtures of such materials. As described above, the hard material may be used in a different form, such as a porous preform, a monolithic piece, or other structure. In a further embodiment, the hard material

may be formed of a ceramic material. If a ceramic is .used, one or more techniques may be incorporated to enhance wetting and/or bonding of the ceramic surface by the brazing material. For example, the surface of the ceramic may be coated with a metallic material or other material to enhance wetting by the brazing material. As another example, an active brazing technique may be used, where the brazing material includes a material that deposits on the ceramic surface (e.g. titanium) to enhance wetting and bonding of the brazing material to the ceramic surface. Still further types of hard materials may be used in other embodiments. As described above, the hard material may preferably hâve higher hardness and superior wear résistance to the surface of the substrate to which the hard material is bonded.

[00114] A particularly good choice of brazing alloy powder includes Ni-Cr-Si-B brazing alloy powder that conforms to Class BNi-2 per AWS A5.18.

	Wt-%
Cr	7.00
Si	4.50
B	3.10
Fe	3.00
C	0.06
Ni	Balance

[00115] Other types of brazing materials may possibly be used, as long as such materials are compatible with both the substrate and the hard particles, and such materials are suitable for a particular brazing method. Brazing materials may include pure metals such as copper or silver, but are more typieally standard brazing alloys having a nickel base, copper base, or silver base. Brazing materials may also include other copper-rich alloys, and low melting copper-nickel alloys. Other types of brazing materials that may be used include pure copper, silicon bronze, titanium copper, chromium copper, spinodal bronze, tin bronze, commercial nickel base brazing alloys (BNi-1, BNi-2, etc.), commercial cobalt base brazing alloys (e. g. BCo-1) or other types of brazing

metals and alloys, including precious metals and alloys. As described above, the brazing material may be provided in powdered or other particulate form in one embodiment. The brazing material may be in a different (i.e. non-powdered) form in another embodiment. For example, in one embodiment, the brazing 5 material may be in the form of one or more slugs of cast or wrought material.

Such slugs may be made at a pre-determined weight targeted for a spécifie brazing application, providing quick and efficient installation of the brazing material in the assembly.

[00116] Fig. 41 shows one example of a furnace cycle for the brazing 10 operation using a hard material including tungsten carbide and Ni-Cr-Si-B brazing alloy powder, with température along the vertical axis. In general, the thermal cycle for the brazing operation involves first heating to a température slightly below the melting température of the brazing material and holding to stabilize the température in the entire assembly (including thick and thin 15 sections). Then, the assembly is heated (preferably quickly) to a higher température above the melting point of the brazing material to melt the brazing material and allow it to infiltrate the spaces between the hard particles. This period may be relatively short, such as 30 minutes to 1 hour in one embodiment. The température is then cooled to just below the solidus température of the 20 brazing material, to allow the brazing material to solidify and bond to the hard particles and the substrate, and holding until the température is stabilized throughout the assembly. Finally, the température is cooled so that the part can be removed from the furnace. It is understood that the length of time that températures must be held to stabilize throughout the assembly may be 25 influenced by the size and geometry of the substrate and/or the shell, as larger/thicker components may need longer to heat or cool. The température of the furnace and castings (such as an assembly of a substrate, a shell, hard particles and brazing material) increases and then decreases over time, as shown. The sample furnace cycle of Fig. 41 takes approximately 7-hours, as 30 represented along the horizontal axis, and the brazing step may be performed at approximately 2050°F for 30-60 minutes in one embodiment.

[00117] Fig. 42 shows multiple views, labeled a-k, as part of manufacturing another embodiment of a wearpart 710. The different drawings 42a-42k illustrate selected processing steps as part of infiltration hardfacing a dual roll crusher tip. The resulting hardfaced roll crusher tip has a substrate and thin métal shell 5 substantially separated but bonded together by infused composite hardfacing material, with minimal contact between the substrate and the thin métal shell.

[00118] Fig. 42a shows a substrate 712, prepared by machining, casting or forging. Shell spacing pin holes 780 are drilled, formed, or shaped in substrate 712, as shown in Fig. 42b, and corresponding shell spacers in the form of pins 10 782 are installée! in holes 780, as shown in Fig. 42c. Pins 782 will be used to suspend substrate 712 within a thin métal shell, with desired spacing between substrate 712 and the shell defined by a length of pins 782. The primary purpose of pins 782 is to keep shell 714 and substrate 712 properly spaced apart until cavity 750 is filled with hard particles 752. Pins 782 need only be large enough to 15 survive this filling step of the methods disclosed herein. Accordingly, pins 782 may be made out of various materials, ranging from soft steel pins to premanufactured hardened sintered tungsten carbide pins.

[00119] Fig. 42d shows a sheet métal shell 714, which may be prepared by deep drawing, hydroforming, and/or cutting and welding, as is known in the art of 20 forming sheet métal molds. Substrate 712, with protruding pins 782 is then placed inside shell 714, as shown in Fig. 42e. Turning to Fig. 42f, hard particles 752 may be placed in a cavity 750 defined between substrate 712 and shell 714, and optionally tamped, vibrated, or otherwise packed into cavity 750 to define a hard particle layer between substrate 712 and shell 714. in Fig. 42g, infiltrant 25 material powder 754 is shown being placed above this hard particle layer, held within a predefined volume in a réservoir 718, preferably formed as an intégral portion of shell 714. Réservoir 718 may be sized relative to cavity 750 to provide an optimal quantity of infiltration brazing material 754 to infiltrate and bond hard particles 752 into a composite hardfacing layer. This is represented graphically in 30 Fig. 42h, with an assembly ready for an infiltration cycle.

[00120] Fig. 42i shows a furnace ready for an infiltration cycle, such as described above. Fig. 42j shows the assembly of Fig. 42i, after infiltration cycle complété (j)_t with réservoir 718 still in place. Preferably, réservoir 718 is removed from shell 714, by cutting or other techniques, leaving a finished wear-resistant composite product 710, as shown in Fig. 42k.

[00121] While shell 714 is shown with a spherical lower surface that will typically need to be held in a fixture, other embodiments of a similarly shaped shell may be self-supporting. Furthermore, shell spacing pins 782 may be omitted if substrate 712 is held by a heat-resisting alloy fixture which also locates shell 714 in a desired position relative to substrate 712. Substrate 712 is thereby suspended above and within sheet métal shell 714 during the infiltration process. In yet other embodiments, any such fixture which locates shell 714 in a desired position relative to substrate 712 may be removed after hard particles 752 are packed into place. Hard particles 752 generally do not dissolve or melt during the infiltration process, so hard particles 752 will reliably support substrate 712 during the infiltration process. This allows such fixtures to be removed before placing any assembly of the components in a furnace, such as an assembly of substrate 712, shell 714, hard particles 752, and brazing material 754. Still other embodiments may hang shell 714 from substrate 712. For example, shell 714 could be made so as to hang from a groove, not shown, in a stem of a hub formed as part of substrate 712.

[00122] Methods according to the présent disclosure may be used with a furnace or retort that employs an atmosphère of hydrogen,. argon, or other type of reducing or inert atmosphère, instead of a vacuum furnace. When brazing in such non-vacuum furnaces, it is best to prevent entrapment of gas within the hard particles, as infiltration proceeds. The brazing powder may melt fairly simultaneously, percolating down as a contiguous molten layer, through the hard particles. Adding venting at low points in the thin shell allows gases trapped in the hard particles to escape as the molten brazing material percolates down. Preferably, a vent tube or multiple vent tubes are attached to the thin métal shell at appropriate low points, and the tube or tubes extend upward to a level higher

than a final level of molten brazing material during final stages of infiltration brazing.

[00123] One embodiment of a steel shell 814 for use in non-vacuum furnaces is shown in Figs. 43a-43f. A vent tube 884 extends from a low point of shell 814 5 to prevent gas entrapment during brazing infiltration. Vent tube 884 is attached to shell 814 at a site or sites subject to gas entrapment. Fig. 43b represents a cross-sectional view of substrate 812, shell 814, and vent tube 884. Hard particulate material 852 is poured into cavity 850, between substrate 812 and shell 814, as shown in Fig. 43c. Infiltrant material 854 is then added above hard 10 particle layer 852, as shown in Fig. 43d. Molten infiltrant material 854 is shown partially penetrating layer of hard particles 852, with gas escaping from vent tube 884, in Fig. 43e. After cooling, the hard particle layer and infiltrant material form a composite 824, with at least some of infiltrant material 854 filling vent tube 884, as shown in Fig. 43f. Vent tube 884 and infiltrant material 854 are typically easily 15 eut off the resulting hardfaced wearpart 810.

[00124] Fig. 44 shows a spherical structure having a particularly complex surface shape. This wear part is not intended to represent any particular tool, other than to show a complex tool that could be hardfaced according to the disclosures herein. For example, it could represent an infiltration hardfaced 20 grinding bail with a particularly complicated exterior shape. A finished wearresistant composite product 910 includes pre-manufactured hardened sintered tungsten carbide inserts, two of which are shown schematically as dashed lines 960, bonded to an underlying substrate with infused composite hardfacing material. Manufacture of grinding bail 910 using prior art techniques would 25 require a complicated multi-piece mold, probably made using graphite or ceramtc materials. The combination of a thin sheet métal mold, a preformed substrate, hardened carbide particles, and infiltration brazing créâtes a much more economical process for manufacturing hard-faced tools with complicated surface geometry.

[00125] Fig. 45 shows multiple views, labeled a-k, as part of manufacturing another embodiment of a wearpart 1010. The different drawings 45a-45k

illustrate selected processing steps as part of infiltration hardfacing a trommel screen for use in minerai dressing. The resulting hardfaced trommel screen may hâve a substrate and thin métal shell substantially separated but bonded together by infused composite hardfacing material, with minimal contact between the substrate and the thin métal shell. Alternatively, the substrate and thin métal shell may contact in selected locations, with the shell supporting the substrate during an infiltration cycle. For example, a plurality of shoulders (not shown) may be formed in selected locations of shell 1014, and substrate may rest on and be supported by these shoulders. In other examples, conformai bands or conformai portions (not shown) of shell 1014 may be welded to substrate 1012.

[00126] Fig. 45a shows a substrate 1012, typically prepared by machining, casting or forging. Fig. 45b shows a corresponding shell 1014, and substrate 1012 is shown supported in shell 1014 in Fig. 45c. Pins (not shown) may be used to suspend substrate 1012 within thin métal shell 1014, with desired spacing between substrate 1012 and shell 1012 defined by a length of the pins (not shown) as similarly shown in Fig. 42.

[00127] Fig. 45d shows hard particles 1052 being poured onto substrate 1012. Hard particles 1052 may be pushed into a cavity 1050 defined between substrate 1012 and shell 1014, and optionally tamped, vibrated, or otherwise packed into cavity 1050 to define a hard particle layer between substrate 1012 and shell 1014. In Fig. 45e, infiltrant material powder 1054 is shown being placed in a réservoir 1018, above hard particle layer 1052. Fig. 45f shows a furnace ready for an infiltration cycle. Fig. 45g shows the assembly of Fig. 45e, after being fully loaded with an appropriate amount of infiltrant material powder, and after being heated and cooled through a complété infiltration cycle. Preferably, selected portions of the sheet métal are removed from shell 1014, by cutting or other techniques, leaving a finished wear-resistant composite product 1010, as shown in Fig. 45h. For example, upper edges 1018a of a surrounding wall may be eut off, and upper caps 1018b defining through-holes may be eut off.

[00128] If appropriate choices are made regarding the substrate material for a tool, the shell material, and the brazing material, as well as the type and size

distribution of the particulate material in the hardfacing layer, it is possible to accommodate thermal and transformation strains so as to prevent cracking of the hardfacing layer, as well as any hard métal insert. In one embodiment, the brazing process may be designed so that the infiltrated material has an overall 5 coefficient of thermal expansion that is between the coefficient of thermal expansion of the hard particles and the coefficient of thermal expansion of the substrate. For example, many of the embodiments disclosed herein include a product having a steel substrate and a mild steel shell, with a hardfacing layer of infiltrated cast tungsten carbide particles. Certain steels hâve a coefficient of 10 thermal expansion of approximately 6.5 microinches per inch per degree- F at températures below the austenite range, as found for AISI 1008 Steel. Selecting copper or copper-based alloys as the infiltrating material and selecting a particle size distribution giving 50% cast tungsten carbide will give an average coefficient of thermal expansion of 6.1 microinches per inch per degree-F in the infiltrated 15 material. Providing infiltrated material having an average coefficient of thermal expansion that is relatively similar to a coefficient of thermal expansion for the underlying substrate and the outer layer of sheet métal means that ail of the components will expand and contract at approximately similar rates. This limits any tendency of the infiltrated material to crack or spall, particularly during 20 cooling after the infiltration cycle, or during heating that may occur later, in use of the hardfaced tool.

[00129] Trommel screens such as the example illustrated in Fig. 45h can often exceed 1 meter in the length and width dimensions. Items such as this offer a clear illustration where the présent invention can offer significant advantages in 25 terms of overcoming thermal expansion problems during the infiltration process.

Hard materials which might be selected for wear résistance may hâve thermal expansion characteristics which differ markedly from those of the hardened steel materials which might be used as a substrate, the low-carbon steel materials which might be used as an expendable shell, or the copper-nickel brazing alloy 30 which might be used as a brazing material. As these items get larger, such as 1

meter in the length and width, thermal expansion rates of different éléments become more important.

[00130] Ceramic and graphite molds hâve rates of thermal expansion that are very different from the rate of thermal expansion for the types of steel alloy 5 typically used as a substrate for wear parts. This can lead to problems such as distortion of the finished part, unexpected variations in hardfacing thickness, or even to séparation of various parts of the mold assembly during the thermal process, allowing the molten infiltrating material to spill in the furnace. The lowcarbon steel materials of the présent disclosure are more likely to hâve rates of 10 thermal expansion that are more similar to the rate of thermal expansion for the types of steel alloy typically used as such a substrate. Thus, the combination of a steel alloy substrate, a low carbon steel thin métal shell, hard particles having a particle size distribution giving approximately 50% cast tungsten carbide, and copper as an infiltrating material offers a significant advantage over prior art 15 hardfacing of steel substrates that required use of ceramic and graphite molds.

[00131] The following table gives several examples of coefficients of thermal expansion for selected hard materials, for low carbon steel (a typical shell material), and copper (a typical brazing material). It is understood that this table provides examples for the sake of illustration and other materials may be used 20 as the hard material, the shell, the brazing material, etc.

Material	Thermal Expansion Coefficient (Microlnches/ln/°F)
Macrocrystalline Tungsten Carbide (WC)	3.6
Cast Tungsten Carbide (WC/W2C)	2.9
Chromium Carbide (Cr3C2)	5.7
Titanium Carbide	4.1
Diamond	2.1
AISI 1008 Steel	6.5

Copper

9.2

[00132] The combination of a steel substrate, a thin métal shell, and a properly selected mixture of hard particles having a spécifie size distribution, and an infiltrating material, results in substantial benefits. This combination offers a greater ability to accommodate thermal and transformational strains, and the 5 resulting dimensional changes, particularly when compared to conventional graphite or ceramic molds. The products and methods of the présent disclosure lead to less risk of warping, less risk of unwanted thickness variations in the resulting hardfacing, and less risk of a damaged mold spilling molten métal brazing material inside a furnace during an infiltration cycle.

[00133] In addition, materials such as steel undergo phase transformations which are accompanied by dimensional changes. For example, when dealing with carbon and low alloy steels, the steel expands with increasing température. However, ai approximately 1333 degrees-F, transformation of the steel to a different crystal structure begins. This transformation results in a decrease in dimensions until the transformation is complété and then the material again expands (at a different rate) with further increase of température. On cooling, transformations again occur, with associated expansion-contraction-expansion of dimensions, until the infiltration cycle is complété. Accommodating ail of these expansions and contractions is easier with the disclosed methods using a thin 20 métal shell as a mold, than when using a graphite mold or ceramic mold. With the methods of the présent disclosure, both the substrate to be hardfaced and the mold containing the components of the hardfacing material are made out of steel, so both the substrate and the shell will be going through similar transformations, expansions, and contractions. While there may be some 25 variations as to coefficients of thermal expansion and transformation températures, these variations for a thin métal mold and a métal substrate are substantially less than such variations for a graphite mold or ceramic mold and a métal substrate. It is therefore very difficult to use a graphite mold or a ceramic mold with a métal substrate to make a large, planar Trommel screens such as

the example illustrated in Fig. 45h, without substantial risk of cracking and/or spalling of the hardfacing coating.

[00134] Furthermore, if the particulate material is intended to perform a wearresisting function, considération of the particle size distribution may be required in order to give adéquate wear résistance. For such cases in general, the size distribution must be such that the interparticle spacing is smaller than the size of the abrasive grains encountered in the application. This prevents the hard particles from being undermined and lost. In one embodiment, a particle size of -50 to +70 mesh (as described above) may be sufficient for most applications, such as if the abrasive grains in the application are not appreciably smaller than 70 mesh. For finer abrasives, the particle size distribution should be sized approximately the same or smaller than the abrasive size.

[00135] The disclosed embodiments may also be utilized to renew or refurbish a worn, previously used hardfaced wearpart. For example, in one embodiment, a shell as described above is connected to a substrate in the form of a hardfaced wearpart, and the hard material (e.g. hard particles) is introduced into the shell to be in close proximity to the substrate. The hard material can then be bonded to the substrate by brazing as described above. It is understood that the brazing material may be bonded to the pre-existing (worn) hardfacing material, the underlying original substrate, or both. The hard material and/or the brazing material may be the same as used in the original hardfacing material in one embodiment.

[00136] Several of the disclosed embodiments show a steel substrate used to form a wearpart, with hard material covering the entire or substantially the entire outer operating surface (e.g. the ground engaging surface) of the wearpart. This may allow use of softer steel, because the entirety of the steel is protected by hardfacing material. These embodiments offer advantages, particularly if softer steel has better résistance to fracturing, such as where softer steel has a higher toughness than other harder steels. Softer substrate materials may also hâve better weldability. Furthermore, softer substrate materials are usually much easier to make into an initial substrate to be hardfaced, and such initial

substrates made of softer steeis are therefore less expensive to make that similarly shaped initial substrates made from harder steeis.

[00137] It should be understood that the shell in any of the disclosed embodiments does not necessarily need to closely conform to the exact shape of the substrate. For instance, the shell could be formed so as to give greater thicknesses at high-wear locations such as corners or angular edges of points. Similarly, ribs or “vanes could be created by the resulting hardfacing layer, at particular locations on the substrate of the tool. Such ribs or vanes may be helpful for controlling the flow of abrasive material in which the component may be operating, or for directing movement of earthen material being impacted by the resulting composite wear-resistant tool.

[00138] It should also be understood that any features, components, structures, techniques, etc., that are described with respect to one embodiment herein may be used or usable in connection with any other embodiments described herein, unless explicitly noted otherwise.

[00139] It is believed that the disclosure set forth herein encompasses multiple distinct inventions with independent utility. While each of these inventions has been disclosed in its preferred form, the spécifie embodiments thereof as disclosed and illustrated herein are not to be considered in a limiting sense as numerous variations are possible. Each example defines an embodiment disclosed in the foregoing disclosure, but any one example does not necessarily encompass ail features or combinations that may be eventually claimed. Where the description recites a or “a first” element or the équivalent thereof, such description includes one or more such éléments, neither requiring nor excluding two or more such éléments. Further, ordinal indicators, such as first, second or third, for identified éléments are used to distinguish between the éléments, and do not indicate a required or limited number of such éléments, and do not indicate a particular position or order of such éléments unless otherwise specifically stated.

Claims (30)

1. An article comprising:

a substrate having a surface;

a sheet métal shell connected to the substrate to define a cavity between the surface of the substrate and the shell; and a composite material filling the cavity and forming a coating on at least a portion of the surface of the substrate, the composite material comprising a hard particulate material infiltrated with a metallic brazing material.

2. The article of claim 1, wherein the shell has an opening to an exterior of the shell, and wherein the composite material is exposed to the exterior of the shell through the opening.

3. The article of claim 2, further comprising a réservoir connected to the shell and positioned outside the cavity in communication with the opening.

4. The article of claim 1, wherein the shell is connected to the surface of the substrate by welding or brazing.

5 placing a hard material within the cavity;

placing a metallic brazing material in communication with the cavity;

heating the brazing material to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to contact the hard material and the surface of the substrate in molten 10 form; and cooling the brazing material to solidify the brazing material and bond the hard material to the surface of the substrate.

56. The method of claim 55, wherein the shell has an opening to an exterior of the shell and a réservoir is connected to the shell and positioned outside the

5 melting point of the brazing material and holding the température for a time sufficient for the brazing material to infiltrate the particulate material in molten form and contact the surface of the tool, and cooling the assembly to solidify the matrix material and form the wear résistant composite coating on the surface.

31. The assembly of claim 30, further comprising a flared réservoir connected 10 to the shell and positioned outside the cavity in communication with the opening, wherein the réservoir is configured to hâve the brazing material placed therein to be in communication with the cavity.

32. The assembly of claim 29, further comprising a composite material filling the cavity and forming a coating on at least a portion of the surface of the tool,

5. The article of claim 4, wherein the shell further comprises a conformai band in surface-to-surface contact with a portion of the surface of the substrate around an entire periphery of the shell, wherein the shell is connected to the substrate by welding or brazing at least at the conformai band.

6. The article of claim 6, wherein the substrate has a bonding surface in surface-to-surface contact with the conformai band, and wherein at least a portion of the substrate within the cavity is inset with respect to the bonding surface, such that the composite material has an outer surface that is flush with the bonding surface.

7. The article of claim 1, wherein the brazing material is bonded to the surface of the substrate.

8. The article of claim 7, wherein the brazing material is further bonded to the shell.

9. The article of claim 1, wherein the shell comprises a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the back piece, wherein the front piece and the back piece are joined together to form the shell by welding or brazing the front flange to the back flange.

10 25. The method of claim 20, wherein the brazing material is bonded to the shell after the brazing material is solidified.

10. The article of claim 1, wherein the particulate material comprises tungsten carbide, and the metallic brazing material comprises Ni-Cr-Si-B brazing alloy.

11. The article of claim 1, wherein the substrate has a hole in the surface, further comprising an insert rod received in the hole, wherein the hole is covered by the composite material.

12. A hardfaced wearpart comprising:

a tool having a surface at a point of the tool and a bonding surface located proximate the surface;

a composite hardfacing material forming a coating on at least a portion of the surface, the composite hardfacing material comprising a hard particulate material infiltrated with a metallic brazing material, wherein the metallic brazing material is bonded to the surface to connect the composite hardfacing material to the tool; and a sheet métal shell in contact with the composite material and surrounding the composite material, the shell having a conformai band in contact with the bonding surface of the tool, wherein the shell is connected to the tool by welding or brazing at least between the conformai band and the bonding surface, wherein a cavity is defined between the surface of the substrate and the shell, and the composite hardfacing material fills the shell.

13. The wearpart of claim 12, wherein the shell has an opening to an exterior of the shell, and wherein the composite hardfacing material is exposed to the exterior of the shell through the opening.

14. The wearpart of claim 13, further comprising a réservoir connected to the shell and positioned outside the cavity in communication with the opening.

15 form to form the composite hardfacing material.

66. The method of claim 55, wherein the shell is formed of sheet métal.

67. An assembly comprising:

a substrate having a surface; and a métal shell connected to the substrate to define a cavity between the

15 cavity in communication with the opening, and wherein the brazing material is placed within the réservoir to be in communication with the cavity.

57. The method of claim 55, wherein connecting the shell to the substrate comprises welding or brazing the shell to the surface of the substrate.

58. The method of claim 57, wherein the shell further comprises a conformai 20 band extending around a periphery of the shell, and wherein connecting the shell to the substrate comprises welding or brazing the conformai band to the surface of the substrate, such that the conformai band is in surface-to-surface contact with a portion of the surface of the substrate around the entire conformai band.

59. The method of claim 55, wherein the brazing material is bonded to the 25 shell after the brazing material is solidified.

60. The method of claim 55, wherein the shell comprises a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the back piece, wherein the method further comprises joining thé front piece and the

30 back piece together to form the shell by welding or brazing the front flange to the back flange.

61. The method of claim 55, wherein the particulate material comprises tungsten carbide, and the metallic brazing material comprises Ni-Cr-Si-B brazing alloy, and wherein the brazing material is heated to a température of approximately 2050°F for a time of approximately 30 to 60 minutes.

5

62. The method of claim 55, further comprising welding or brazing pièces of sheet métal together to form the shell.

63. The method of claim 55, wherein the hard material and the metallic brazing material form a composite hardfacing material covering the surface of the substrate.

10

64. The method of claim 63, wherein the hard material has a porous structure that is infiltrated by the metallic brazing material in molten form to form the composite hardfacing material.

65. The method of claim 63, wherein the hard material comprises a particulate material that is infiltrated by the metallic brazing material in molten

15 the composite material comprising a hard particulate material infiltrated with a metallic brazing material, wherein the brazing material is bonded to the surface.

33. The assembly of claim 29, further comprising a réservoir connected to the shell and positioned outside the cavity in communication with the opening.

34. The assembly of claim 33, wherein the réservoir has a flared shape and îs 20 integrally formed with the shell.

35. The assembly of claim 29, wherein the conformai band extends around an entire periphery of the shell and around an entire periphery of the surface.

36. The assembly of claim 29, wherein the shell comprises a front piece having a front flange extending transversely from a back edge of the front piece

15 back piece, wherein the method further comprises joining the front piece and the back piece together to form the shell by welding or brazing the front flange to the back flange.

15. The wearpart of claim 12, wherein the conformai band contacts the bonding surface of the tool around an entire periphery of the shell and is welded or brazed to the conformai band around the entire periphery.

16. The wearpart of claim 12, wherein the brazing material is bonded to the shell.

17. The wearpart of claim 12, wherein the shell comprises a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the back piece, wherein the front piece and the back piece are joined together to form the shell by welding or brazing the front flange to the back flange.

18. The wearpart of claim 12, wherein the particulate material comprises tungsten carbide, and the metallic brazing material comprises Ni-Cr-Si-B brazing alloy.

19. The wearpart of claim 12, wherein the substrate has a hole in the surface, further comprising an insert rod received in the hole, wherein the hole is covered by the composite hardfacing material.

20 surface and the shell, the shell further having an opening ,to an exterior of the shell.

68. The assembly of claim 67, wherein the shell is formed of sheet métal.

69. The assembly of claim 67, wherein the shell is connected to the substrate by welding or brazing the shell to the surface.

25

70. The assembly of claim 67, wherein the shell has a conformai band conforming to at least a portion of the surface.

71. The assembly of claim 70, wherein the shell is connected to the substrate by welding or brazing the conformai band to the at least a portion of the surface.

72. The assembly of claim 67, wherein the assembly is configured for forming

20 alloy, and wherein the brazing material is heated to a température of approximately 2050°F for a time of approximately 30 to 60 minutes.

20. A method comprising:

providing a substrate having a surface;

connecting a sheet métal shell to the surface of the substrate to define a cavity between the shell and the surface;

placing a hard particulate material within the cavity, in close proximity to the surface;

placing a metallic brazing material in communication with the cavity;

heating the brazing material to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to infiltrate the particulate material in molten form and contact the surface of the substrate; and cooling the brazing material to solidify the brazing material and form a wear résistant composite coating on the surface of the substrate.

21. The method of claim 20, wherein the shell has an opening to an exterior of the shell and a réservoir is connected to the shell and positioned outside the cavity in communication with the opening, and wherein the brazing material is placed within the réservoir to be in communication with the cavity.

22. The method of claim 21, wherein the réservoir is integrally formed with the shell.

23. The method of claim 20, wherein connecting the shell to the substrate comprises welding or brazing the shell to the surface of the substrate.

5

24. The method of claim 23, wherein the shell further comprises a conformai band extending around a periphery of the shell, and wherein connecting the shell to the substrate comprises welding or brazing the conformai band to the surface of the substrate, such that the conformai band is in surface-to-surface contact with a portion of the surface of the substrate around the entire conformai band.

25 and a back piece having a back flange extending transversely from a front edge of the back piece, wherein the front piece and the back piece are joined together to form the shell by welding or brazing the front flange to the- back flange.

37. The assembly of claim 29, wherein the tool has a hole in the surface, further comprising an insert rod received in the hole.

30

38. The assembly of claim 37, wherein spaces are defined between the insert rod and an interior wall of the hole.

39. An assembly comprising:

a tool having a surface;

a sheet métal shell covering at least a portion of the surface and defining a cavity between the shell and the surface, the shell further having an opening to an exterior of the shell; and a plurality of spacers engaging the tool and the shell and separating the tool from the shell.

40. The assembly of claim 39, wherein the assembly is configured for forming a wear résistant composite coating on the surface by filling the cavity with a hard particulate material, placing a metallic brazing material in communication with the cavity, heating the assembly to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to infiltrate the particulate material in molten form and contact the surface of the tool, and cooling the assembly to solidify the matrix material and form the wear résistant composite coating on the surface.

41. The assembly of claim 40, further comprising a wall extending from the shell and defining a réservoir connected to the shell and positioned outside the cavity in communication with the opening, wherein the réservoir is configured to hâve a brazing material placed therein to be in communication with the cavity.

42. The assembly of claim 39, further comprising a composite material filling the cavity and forming a coating on at least a portion of the surface of the tool, the composite material comprising a hard particulate material infiltrated with a metallic brazing material, wherein the brazing material is bonded to the surface.

43. An article comprising:

a substrate having a surface;

a métal shell connected to the substrate to define a cavity between the surface of the substrate and the shell;

a hard material positioned within the cavity; and a metallic brazing material bonding the hard material to the surface of the substrate.

44. The article of clatm 43, wherein the shell has an opening to an exterior of the shell, and wherein the composite material is exposed to the exterior of the shell through the opening.

45. The article of claim 44, further comprising a flared réservoir connected to the shell and positioned outside the cavity in communication with the opening.

46. The article of claim 43, wherein the shell is connected to the surface of the substrate by welding or brazing.

47. The article of claim 46, wherein the shell further comprises a conformai band in surface-to-surface contact with a portion of the surface of the substrate around an entire periphery of the shell, wherein the shell is donnected to the substrate by welding or brazing at least at the conformai band.

48. The article of claim 47, wherein the substrate has a bonding surface in surface-to-surface contact with the conformai band, and wherein at least a portion of the substrate within the cavity is inset with respect to the bonding surface.

49. The article of claim 43, wherein the brazing material is further bonded to the shell.

50. The article of claim 43, wherein the shell comprises a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the back piece, wherein the front piece and the back piece are joined together to form the shell by welding or brazing the front flange to the back flange.

51. The article of claim 43, wherein the hard material and the metallic brazing material form a composite hardfacing material covering the surface of the substrate.

52. The article of claim 51, wherein the hard material has a porous structure that is infiltrated by the metallic brazing material to form the composite hardfacing material.

53. The article of claim 51, wherein the hard material comprises a particulate material that is infiltrated by the metallic brazing material to form the composite hardfacing material.

54. The article of claim 43, wherein the shell is formed of -sheet métal.

55. A method comprising:

connecting a métal shell to a surface of a substrate to define a cavity between the shell and the surface;

25 a tool having a surface; and a sheet métal shell connected to the tool and having a conformai band conforming to at least a portion of the surface to define a cavity between the surface and the shell, the shell further having an opening to an exterior of the shell,

30 wherein the shell is connected to the tool by welding or brazing the conformai band to the at least a portion of the surface.

30. The assembly of claim 29, wherein the assembly is configurée! for forming a wear résistant composite coating on the surface by filling the cavity through the opening with a hard particulate material, placing a metallic brazing material in communication with the cavity, heating the assembly to a température above a

26. The method of claim 20, wherein the shell comprises a front piece having a front flange extending transversely from a back edge of the front piece and a back piece having a back flange extending transversely from a front edge of the

27. The method of claim 20, wherein the particulate material comprises tungsten carbide, and the metallic brazing material comprises Ni-Cr-Si-B brazing

28. The method of claim 20, further comprising welding or brazing pièces of sheet métal together to form the shell.

29. An assembly comprising:

30 a wear résistant composite coating on the surface by filling the cavity through the opening with a hard particulate material, placing a metallic brazing material in communication with the cavity, heating the assembly to a température above a melting point of the brazing material and holding the température for a time sufficient for the brazing material to înfiltrate the particulate material in molten form and contact the surface of the tool, and cooling the assembly to solidify the 5 matrix material and form the wear résistant composite coating on the surface.