NZ753757B2 - Water-resistant composition for adsorbing volatile organic compounds - Google Patents
Water-resistant composition for adsorbing volatile organic compounds Download PDFInfo
- Publication number
- NZ753757B2 NZ753757B2 NZ753757A NZ75375714A NZ753757B2 NZ 753757 B2 NZ753757 B2 NZ 753757B2 NZ 753757 A NZ753757 A NZ 753757A NZ 75375714 A NZ75375714 A NZ 75375714A NZ 753757 B2 NZ753757 B2 NZ 753757B2
- Authority
- NZ
- New Zealand
- Prior art keywords
- water
- resistant composition
- use according
- zsm
- vocs
- Prior art date
Abstract
The present invention provides a composition for adsorbing volatile organic compounds (VOCs) derived from organic matter comprising: a) palladium doped zeolite and b) a water-soluble binder which is guar gum, gum arabic, 2-hydroxyethylcellulose, hydroxypropyl methylcellulose and a polyethylene oxide. The invention also provides the use of the composition for adsorbing volatile organic compounds (VOCs) such as ethylene from perishable organic goods. The invention is thereby useful as part of a packaging material for fruit, vegetables, plants and/or cut flowers. . The invention also provides the use of the composition for adsorbing volatile organic compounds (VOCs) such as ethylene from perishable organic goods. The invention is thereby useful as part of a packaging material for fruit, vegetables, plants and/or cut flowers.
Description
WATER-RESISTANT COMPOSITION FOR ADSORBING VOLATILE ORGANIC
COMPOUNDS
This ation is a divisional of New d patent application 716218, which is the
national phase entry in New Zealand of PCT international application
(published as ), filed June 25, 2014, all of which are incorporated herein
by reference.
This invention relates to a water-resistant composition suitable for the tion of volatile
organic compounds (VOCs) derived from organic matter. More particularly, the organic
matter can be perishable organic goods, such as food.
VOCs include a range of compounds which are derived from organic matter. One example
of a VOC derived from organic matter is ethylene, a plant hormone which causes ripening,
whilst another example is trimethylamine, a gas commonly given off by fish as it
decomposes.
The removal of VOCs d from organic matter is of interest for a variety of applications.
The adsorption of ethylene can prevent undesired ripening and softening, loss of colour,
loss of leaves and sprouting to occur in fruit and vegetables, it is also known to prevent
other food and horticultural ts from perishing prematurely, and can help eliminate
unpleasant smells.
/052074 (to Johnson y PLC) relates to the use of palladium doped
hydrogen-ZSM-5 to adsorb VOCs derived from organic .
JP03-280827 (to Toray Industries Inc.) describes an ethylene-removing agent
characterised as being formed as a result of an ion-exchange between some or
substantially all of the exchangeable ions of an organic and/or inorganic ion exchanger with
palladium ions and/or palladium complex ions. The ion-exchanger may be a zeolite which
contains a metal oxide (such as Na20) as an ial component. JP03-280827 does not
describe palladium doped hydrogen-ZSM-5 nor a water-resistant composition comprising
at least one water-soluble binder.
In a first aspect, the present invention provides a water-resistant composition for adsorbing
le organic compounds (VOCs) derived from organic matter comprising:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the en-ZSM-5 is
less than or equal to 200:1 ; and
b) at least one water-soluble binder, wherein the water-soluble binder is selected from
the group consisting of guar gum, gum arabic, 2-hydroxyethylcellulose, hydroxypropyl
methylcellulose and polyethylene oxide.
In another aspect, the present ion relates to a use of a water-resistant composition
for adsorbing volatile organic compounds (VOCs) derived from organic matter, wherein the
resistant composition is defined in the first aspect of the invention.
In r aspect, the present invention es an article comprising: packaging or a
container configured to hold organic ; and a water-resistant composition as defined
in the first aspect of the invention.
In another aspect, the present invention provides an article comprising a water-resistant
composition as defined in the first aspect of the invention, wherein the article is a label or
sheet.
In another aspect, the present invention es an s formulation comprising a
water-resistant composition as defined in the first aspect of the invention and water.
In another aspect, the present invention provides an admix comprising a resistant
composition as defined in the first aspect of the invention.
In the description in this specification reference may be made to subject matter which is not
within the scope of the ed claims. That subject matter should be readily identifiable
by a person skilled in the art and may assist in putting into practice the invention as defined
in the appended claims.
The term “comprising” as used in this specification and claims means “consisting at least in
part of”. When interpreting statements in this specification and claims which include the
term “comprising”, other features besides the features prefaced by this term in each
statement can also be present. Related terms such as ise” and “comprises” are to
be interpreted in similar manner.
bed is a water-resistant composition for adsorbing volatile organic compounds
(VOCs) derived from organic matter comprising:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is less
than or equal to 200:1 ; and
b) at least one water-soluble binder.
By "water-resistant" we mean a composition which is able to substantially resist being
dissolved by water or removed through the action of water under the conditions at which
the ition is to be used. By "derived from" we mean the VOCs are released by the
organic matter and are adsorbed by the water-resistant composition t the VOCs
being combusted or ed before adsorption.
The water-resistant ition may be prepared by providing an aqueous formulation and
substantially drying the aqueous formulation until the water-resistant composition forms.
Accordingly, described is an aqueous formulation comprising:
a) ium doped hydrogen-ZSM-5, n the Si:AI ratio of the hydrogen-ZSM-5 is less
than or equal to 200:1 ;
b) at least one water-soluble binder; and
c) water.
The water-resistant ition and the aqueous formulation comprise palladium doped
hydrogen-ZSM-5. The palladium itself can comprise from 0.1 wt% to 10.0 wt% based on
the total weight of the doped hydrogen-ZSM-5, such as from 0.5 wt% to 5.0 wt% based on
the total weight of the doped hydrogen-ZSM-5.
Hydrogen-ZSM-5 is a commercially available synthetic zeolite having a crystalline
aluminosilicate structure. Hydrogen-ZSM-5 is prepared by a two-step method which firstly
involves the formation of ZSM-5 containing a mixture of alkali metal cations, typically
sodium (i.e. sodium-ZSM-5). The alkali metal form (e.g. the sodium form) is then ionexchanged
to provide hydrogen-ZSM-5. The present ion utilises en-ZSM-5,
wherein the Si:AI ratio of the hydrogen-ZSM-5 is less than or equal to 200:1 , for example
less than or equal to 150:1 , such as less than or equal to 100:1.
Methods of manufacturing palladium doped hydrogen-ZSM-5 are known to the skilled
chemist, and include the use of a variety of palladium salts, such as Pd(N03)2, Pd(OAc)2,
PdCI2, palladium oxalate, tetraamine ium hydrogen carbonate, tetraamine palladium
hydroxide and tetraamine palladium acetate. The hydrogen-ZSM-5 may be calcined after
impregnation with at least one palladium salt, however, for some applications this may not
be necessary. Samples of palladium doped hydrogen-ZSM-5 which are calcined will
comprise elemental palladium and/or at least partially oxidised ium. In some
ments, the palladium-doped en-ZSM-5 is calcined palladium-doped
hydrogen-ZSM-5.
The binder acts as a carrier for the palladium doped hydrogen-ZSM-5 and allows it to
adhere to a substrate. At least one water-soluble binder may be used (e.g. 1 , 2, 3, 4 or 5
water-soluble binders). If more than one binder is used, each binder may of the same type
or of a different type. Suitable binders will exhibit the following characteristics:
a) Solubility in water. In order to prepare the aqueous formulation, the binder will be
substantially e in water or can be forced into on and will thereafter remain in
solution after removal of the forcing conditions. Forcing conditions include, for example,
heating and/or high shear mixing.
b) Water-resistance of the dried composition. Water-based compositions will lly have
the tendency to be more susceptible to water/humidity than organic solvent based systems.
As such, the long term effects of a humid environment on the composition will need to be
taken into account. The present invention, however, balances the properties of the watersoluble
binders in that the binders are substantially soluble in the water-based formulation
and yet form substantially water-resistant compositions on drying.
c) ibility with the palladium doped hydrogen ZSM-5. The water-soluble binders will
have no or substantially no adverse effects on the ium doped hydrogen ZSM-5.
Adverse effects may include undesirably reacting with the palladium doped hydrogen-ZSM-
or inhibiting its VOC adsorption uptake abilities.
Depending on the intended use of the resistant composition, the water-resistant
composition may also comprise one or more of the following characteristics:
d) Approval for use in the operational duty. The selection of a suitable binder will depend
upon the intended use of the resistant ition. In certain embodiments, the
water- soluble binders can be food grade s. Binders which are food grade will be
required when the water-resistant composition is for use with perishable organic goods
such as foods.
In other embodiments, binders which are not food grade may be suitable when the waterresistant
composition is for use with organic matter which is not suitable for consumption
such as .
e) The l stability of the dried composition at the temperature or temperatures at
which the composition is to be used.
f) The e stability of the water-resistant composition. The water-resistant composition
will retain or exhibit no significant loss in activity on e. In certain embodiments, the
water- resistant composition exhibits substantially no loss in activity when stored at room
temperature for at least 12 weeks.
In one embodiment, the soluble binder is a polyvinyl alcohol (PVA). PVAs are watersoluble
polymers which may be manufactured by the hydrolysis (saponification) of polyvinyl
acetate. PVAs are typically described in terms of their degree of hydrolysis (% hydrolysis)
and their e molecular weight (Mw).
Without wishing to be bound by theory, the water-resistance of the dried PVA-containing
compositions appears to increase with increasing Mw and degree of hydrolysis. In some
embodiments, r, the inventors have found that suitable PVAs having a lower Mw
and higher degree of hydrolysis, or a higher Mw and lower degree of hydrolysis may also be
used in the present invention. In some embodiments, the PVA has a % hydrolysis which is
about ≥ 80%. In some embodiments, the % hydrolysis is about > 85%. In some
embodiments, the % hydrolysis is from about 86 to about 99+ %. In some embodiments,
the Mw, is from about 27,000 to about 205,000. In some embodiments, the Mw is from
about 80,000 to about 205,000. In one preferred embodiment, the Mw is from about 85,000
to about 215,000. In one especially preferred embodiment, the Mw is from about 145,000 to
about 0. Examples of suitable PVAs include but are not limited to:
a) a PVA which has an Mw -205,000 and is 88 % hydrolysed (e.g. Mowiol® 40-88 (Mw -
205,000, 88 % hydrolysed);
b) a PVA which has an w 85,000-146,000 and is 99+ % ysed (e.g. h® w 85,000-
146,000, 99+ % hydrolysed);
c) a PVA which has an Mw 89,000-98,000 and is 99+ % ysed (e.g. Aldrich® w 89,000-
98,000, 99+ % ysed);
d) a PVA which has an w 130,000 and is 99+ % ysed;
e) a PVA which has an Mw -145,000 and is 99+ % hydrolysed (e.g. Mowiol® 28-99 (Mw -
145,000, 99+ % hydrolysed));
f) a PVA which has an Mw 0-186,000 and is 99+ % hydrolysed;
g) a PVA which has an Mw 27,000 and is 98 % hydrolysed (e.g. Mowiol® 4-98 (Mw 27,000,
98 % hydrolysed));
h) a PVA which has an Mw 195,000 and is 88 % hydrolysed (e.g. Mowiol® 40-88 (Mw
195,000, 88 % hydrolysed));
i) a PVA which has an Mw 205,000 and is 88 % hydrolysed (e.g. Mowiol® 40-88 (Mw
205,000, 88 % hydrolysed));
In another embodiment, the water-soluble binder may be a gum. Examples of suitable
gums include but are not limited to guar gum or gum .
In yet another embodiment, the water-soluble binder may be a cellulose or derivative
thereof. Suitable celluloses include but are not limited to oxyethylcellulose or
hypromellose (hydroxypropyl methylcellulose).
In yet r embodiment, the water-soluble binder may be a polyethylene oxide (PEO).
In some embodiments, the PEO has a Mw from about 100,000 to about 1 ,000,000. In one
embodiment, the Mw is about 100,000. In another embodiment, the Mw is about 1 ,000,000.
The water-resistant composition may further comprise one or more other components,
such as one or more binder modifiers, driers, plasticisers, fillers, surfactants, pigments or
preservatives. The or each component may be added in any suitable quantity. In one
ment, the water-resistant composition further comprises one or more binder
modifiers. An example of a suitable binder modifier is polytetrafluoroethylene (PTFE).
t wishing to be bound by theory, it is believed that PTFE increases the
hydrophobicity and flexibility of the water-resistant composition. In certain embodiments,
the aqueous formulation may comprise PTFE from about 0.01 to about 10 wt%
concentration of the aqueous ation, such as from about 0.1 to about 7.5 wt%
tration, for example, from about 0.25 to about 5 wt% concentration. The % dry
weight of the PTFE in the water- resistant ition can be calculated by known
s depending on the concentration of the aqueous formulation.
The aqueous formulation may be prepared by any suitable . In one preferred
method, the at least one binder is dissolved in a suitable volume of water with heating (if
required) and/or stirring (if required) to form an aqueous on. The solution is then
mixed with the palladium doped hydrogen-ZSM-5 and, if used, one or more binder
modifiers, driers, plasticisers, fillers, surfactants, ts or preservatives.
Alternatively, a suitable volume of water may be added to an admix comprising the
palladium doped hydrogen-ZSM-5, one or more one water-soluble binders and, ally,
one or more binder modifiers, driers, plasticisers, fillers, surfactants, pigments or
preservatives with heating (if required) and/or stirring (if required) to form an aqueous
solution.
Therefore, described is an admix comprising:
(a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is
less than or equal to 200:1 ;
b) at least one water-soluble binder (e.g. 1 , 2, 3, 4 or 5 water-soluble binders); and
c) optionally, at least one (e.g. 1 , 2, 3, 4 or 5) binder ers, driers, plasticisers, fillers,
surfactants, pigments or preservatives.
An admix conveniently allows the e and transportation of the components prior to the
preparation of the aqueous formulation.
In one ment, the aqueous formulation may be deposited shortly after being
prepared. In another embodiment, the aqueous formulation may be stored for use at a later
time. In the latter instance, it is preferable that on deposition and drying the water-resistant
composition shows little or no deactivation in its ability to adsorb VOCs.
The aqueous formulation may be ted by any suitable method which forms a film or
coating such as printing (e.g. using a k-bar), casting, roller application, brushing, spraying
or like techniques. The mode by which the aqueous formulation is to be applied may
influence the desired viscosity of the formulation. For example, a formulation suitable for
spraying may need to be less viscous than one which is required for roller application. The
viscosity of the ation will be generally nced by the type of binder, as well as the
amount of binder in the formulation. In one embodiment, the s formulation may
comprise the binder from about 0.1 to about 10 wt% concentration of the aqueous
formulation, such as from about 0.5 to about 7.5 wt% concentration, for example, from
about 1 to about 5 wt% concentration. The % dry weight of the binder can be ated by
known methods depending on the concentration of the aqueous formulation.
Howsoever the aqueous formulation is deposited, the ation is then substantially dried
to provide the water-resistant composition. The formulation may be dried at any suitable
temperature. In one red embodiment, the formulation is dried at one or more
atures in the range of about 10°C to about 100°C, for example, from about 15°C to
about 80°C, such as about 20°C to about 75°C. It is preferred that the temperature is
maintained below the decomposition temperature of any component in the formulation and
so when a component is known to decompose within the temperature ranges given above,
the temperature should be maintained below the decomposition ature. Alternatively
or in addition, alternative suitable drying methods may be used, such as drying using a UV
lamp.
Howsoever the drying process is conducted, it may be carried out for a period of time from
about 1 second to about 24 hours. Usually the formulation has dried within about 18 hours
or less. In certain embodiments, the formulation may be dried within about 2 hours. In other
embodiments, the formulation may be dried within about 30 minutes.
Described is an e sing:
packaging or a container configured to hold organic matter; and
a water-resistant composition comprising:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is less
than or equal to 200:1 ; and
b) at least one water-soluble binder.
The water-resistant ition, palladium doped hydrogen-ZSM-5 and at least one watersoluble
binder are as described above.
The organic matter from which the VOCs are derived may be contained within a storage
container or package, such that the water-resistant composition has a closed or semienclosed
environment within which to adsorb the VOCs. In the case of perishable organic
goods, the storage container or e is likely to be the container or package within
which the goods are contained, e.g. crates used to store the goods when in transit or the
packaging within which the goods are kept when on display prior to purchase. In another
embodiment, the water-resistant composition is orated into, or into part of, the
storage container or package itself.
Described is an article comprising:
a water-resistant composition sing:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is less
than or equal to 200:1 ; and
b) at least one water-soluble binder,
and further wherein the article is a label or sheet.
The water-resistant composition, ium doped hydrogen-ZSM-5 and at least one watersoluble
binder are as described above.
The resistant composition may be orated onto or into a label or sheet. The
label or sheet may comprise a substrate which may be suitable for insertion and retention
within a storage container or package. In on to labels to be packaged inside
packaging, the invention includes adhesive labels, decals and the like. In one embodiment,
the aqueous formulation may be deposited onto or into a woven or ven synthetic
fabric. In a preferred embodiment, the substrate is Tyvek®, (i.e. a non-woven substrate of
polyethylene ).
In one embodiment, the water-resistant composition may be used in an open environment,
for example, on open shelves under a loose display of organic produce. In this instance,
the water-resistant composition may comprise any suitable format, such as the labels and
sheets described above.
In yet another embodiment, described is the use of a water-resistant ition as
described above for adsorbing VOCs derived from organic matter.
The c matter can be perishable organic goods, such as items of food and
horticultural produce. The items of food may comprise fruit and/or vegetables. The
horticultural produce may comprise plants and/or cut flowers.
Alternatively, the c matter may comprise refuse. Such refuse may include kitchen
refuse such as waste food, which produces unpleasant odours whilst decomposing.
If the perishable organic goods comprise items of food, the resistant composition
may be packaged in a way to prevent direct contact with the food, e.g. behind a gas
permeable barrier layer. The gas permeable barrier layer may be affixed on top of the
composition itself or may form part of label incorporating the composition.
If, however, the source of VOCs is refuse, the storage ner or package may be a
refuse receptacle.
Controlled atmosphere storage of fresh produce utilizes high levels of C02 and reduced
oxygen to increase the shelf life of the product. Modified atmosphere packaging is used to
enhance the lifetime and/or the quality of food by ng the amount of oxygen (towards
zero) in the atmosphere compared to air. Fresh produce tends to be packed under an
equilibrium modified atmosphere which uses high levels of C02 and reduced levels of
oxygen and which allows a reduced respiration rate. The water-resistant composition may
be conveniently used in a controlled atmosphere or ed atmosphere environment. In
one embodiment, the water-resistant composition may be used in an environment
comprising less than 10 vol% of oxygen. In another embodiment, the level of oxygen in
these environments is t in a range between >0.5 vol% and <10 vol%. For example,
the level of oxygen may be about 1 vol%, about 2 vol%, about 3 vol%, about 4 vol%, about
vol%, about 6 vol%, about 7 vol%, about 8 vol% or about 9 vol%. In another embodiment,
the level of oxygen is substantially 0 vol%. The balance of the gas composition may
comprise an inert gas (such as nitrogen), optionally carbon dioxide and/or optionally carbon
monoxide.
Other methods of using the present ion may be used in appropriate circumstances.
One advantage associated with this invention is that the VOCs can be adsorbed at
relatively low atures, such as in the range of from -10 °C to 50 °C, more commonly
from 0 °C to 40°C. For example, the temperature range may be from about 0°C to about
°C or about 0°C to about 30°C. This enables the water-resistant composition to be used
in the environment within which the organic matter is commonly found, e.g. erators or
at ambient temperature, without ing complex heating and gas recirculation equipment
to be used. Nonetheless, where a particular application allows for heating and gas
recirculation equipment to be used (e.g. a gas conditioning system) the water-resistant
composition may also be operated at an elevated temperature, e.g. above 60 °C.
In one embodiment, the VOCs comprise ethylene. Ethylene is a gaseous hormone
ed by plants that can cause plants to wilt and fruits to ripen. The removal of VOCs
produced by plants can delay these processes enabling food and horticultural produce to
be kept in transit and/or in storage for longer without accelerating perishing. Therefore, a
particular application of this invention is to industries that produce, ship, export and buy
food and horticultural produce. Tests have shown that, unlike prior art methods, the use of
an adsorber according to this invention enables the shelf life of post-climacteric fruit to be
extended (see for example Terry L, ans T, Poulston S, l E and Smith AWJ,
Posthan/est y and logy 45 (2007) 214-220). That is, even after the climacteric
respiratory rise has been initiated, fruit is prevented from ng further (or at least the
rate of ripening ) using ium doped hydrogen-ZSM-5 to adsorb ethylene.
The VOCs may be odorous, for example, sulfur-containing VOCs (such as hydrogen
sulfide), nitrogen-containing VOCs (such as ammonia or triethylamine) or oxygencontaining
VOCs. In one embodiment, the oxygen-containing VOCs comprise
formaldehyde and/or acetic acid. Formaldehyde and acetic acid are malodorous chemicals
that are often found in the home. Formaldehyde may be released from pressed bonded
wood products, such as plywood, but is also found in dyes, textiles, plastics, paper
products, fertilizer, and cosmetics. Acetic acid may be released from kitchen waste and
animal waste. Therefore, one potential application of this invention is to the removal of
malodours from the domestic environment.
At least a proportion of the adsorbed VOCs may be converted into secondary compounds
after adsorption onto the palladium doped hydrogen-ZSM-5.
1. In one embodiment, the water-resistant composition is effective to adsorb the VOCs
to a level of less than or equal to 0.10 ppm, for example to a level of less than or equal to
0.05 ppm. In another embodiment, the water-resistant composition is effective to adsorb
substantially all of the VOCs i.e. no detectable amount of the VOCs remains.
The water-resistant composition may be used uously for VOC removal for an
extended period of time, e.g. several days, (the actual time depending upon the
environment within which it is used). In certain embodiments, the water-resistant
composition may be subjected to water immersion for a period of time (for example, at
least five minutes) without the dried soluble binder ing. Moreover, there is no
significant loss in activity of the palladium doped hydrogen-ZSM-5 after it has been
d to water. As food and horticultural produce are usually stored in humid
environments, these features are also beneficial to the relevant industries.
In order to identify the time when the water-resistant composition has reached its VOC
adsorption capacity, a VOC indicator may be included for use with the water-resistant
composition. Suitable indicators include the palladium based ethylene tor sed in
patent ation JP 60-201252.
In order that the invention may be more fully understood the following non-limiting
es are ed by way of illustration only and with reference to the anying
figures in which:
Figures 1 and 2 illustrate the ethylene removal abilities of PVA itions comprising
palladium doped hydrogen-ZSM-5.
Figure 3 shows the ethylene removal abilities of FE compositions sing
palladium doped hydrogen-ZSM-5.
Figure 4 illustrates the ethylene removal abilities of various gums and osic
compositions comprising palladium doped hydrogen-ZSM-5.
Figure 5 shows the ethylene removal abilities of various compositions comprising palladium
doped hydrogen-ZSM-5 which were subjected to different drying temperatures and times.
Figure 6 illustrates the ethylene removal ability of a fresh and aged sample of PVA-6.
Examples
Example 1
Preparation of doped supports
The palladium doped hydrogen-ZSM-5 was ed using the incipient wetness
impregnation method. Typically 20 g of the hydrogen-ZSM-5 was impregnated with a
nitrate salt or chloride salt of palladium, and then dried at 110 °C before being calcined in
air at 500 °C for 2 hrs to form the palladium doped hydrogen-ZSM-5.
Ethylene adsorption capacity experiments
The ne adsorption capacity of palladium doped hydrogen-ZSM-5 was compared
against ium doped sodium-ZSM-5.
Ethylene Adsorption(c)
2.5 wt% Pd/Na-ZSM-5 (a) 282 µl/g
rative)
2.5 wt% Pd/H-ZSM-5 (b) 4162 µl/g
(a) 2.5 wt% palladium doped sodium-ZSM-5 was prepared using the incipient wetness
impregnation method. Thus, 5g of -ZSM-5 was impregnated with palladium nitrate
solution, dried at 105°C and calcined at 500°C for 2 hours.
(b) 2.5 wt% palladium doped hydrogen-ZSM-5 was ed using the incipient wetness
impregnation method. Thus, 5g of hydrogen-ZSM-5 was impregnated with palladium nitrate
solution, dried at 105°C and calcined at 500°C for 2 hours.
(c) the ethylene adsorption capacity was tested as s: measurements were carried out
in a plug flow reactor at 21 °C with 0.1 g doped support of particle size 250-355 pm with a
flow rate of 50 ml/min of gas comprising 10% 02, 200 ppm C2H4, ~1 % water (where
present) and balance He/Ar.
As can be seen from the data provided above, the ethylene adsorption capacity for
palladium doped en-ZSM-5 is 4162 μΙ/g as compared to 282 μΙ/g for the palladium
doped sodium-ZSM-5 i.e. the palladium doped hydrogen-ZSM-5 has an ethylene
adsorption capacity nearly fifteen times greater than palladium doped sodium-ZSM-5.
Example 3
ation of water-resistant compositions
Aqueous stock solutions of polymer binders were prepared by dissolving the r in
water and stirring with heating until the polymer had tely dissolved. For polyvinyl
alcohol (PVA) based compositions this required >90 °C for a completely clear solution. All
ons were prepared at 4.3 wt.% concentration, unless otherwise stated.
The polymer solution (18 g of 4.3 wt.% r) was weighed out and mixed with
palladium doped en-ZSM-5 (20 g). Mixing was achieved with a Speed mixer® set at
3000 rpm for 30 sec. This equated to a dry weight composition of 4.3% polymer and 95.7%
ium doped hydrogen-ZSM-5 powder. If the viscosity was too high, a 2.5% solution
was prepared (equivalent to 2.15% dry ).
Ethylene removal tests
The formulations were printed onto Tyvek® paper using a 25 μηι k-bar. Samples were left
to dry in air overnight and then stored in sealed plastic bags for ethylene removal testing.
The ethylene removal experiments were carried out at room temperature in an unstirred
batch r (0.86 L) with a 3 x 3 inch (7.62 x 7.62 cm) printed sheet and an initial gas
composition of 550 μΙ_ L"1 (i.e. 550 ppm) ethylene, 40% (v/v) air balanced with Ar. Selected
gas concentrations were measured at hourly intervals with a Varian CP-4900 Micro GC
(Varian Inc., CA). Gas samples (40 ms duration) were taken via an automated recirculating
ng system. Column and injector temperatures were set at 60 and 70°C, respectively.
The 0.15 mm diameter, 10 m long column was packed with PoraPLOT Q. Ethylene and
C02 were ated against 10 μΙ_ L"1 ethylene balanced with air and 5% (v/v) C02
balanced with Ar (Air Products Europe, Surrey, UK). A thermal conductivity detector was
used with He carrier gas at 276 kPa inlet pressure. Peak integration was carried out within
the Varian STAR software.
A graph of ethylene removal rate against time was plotted to assess the quality of the
coating. Water resistance and adhesion was also checked by spraying water onto the
surface and by folding the Tyvek® to look for flaking or cracking. Samples were only tested
for ne uptake if the adhesion was considered acceptable. In the tables, the term
"good adhesion" means the g did not fall off when rubbed or folded once. "Good
water resistance" means the coating did not fall off when sprayed with a jet of water.
Example 4
PVA compositions
PVA compositions were prepared and tested as described in Example 3.
Table 1: PVA compositions
PVA-7 4.3 % stock solution (PVA (75%)-PEG (25%) Poor All removed
(comparative)
PVA-8 2.5% stock solution PVA (75%)-PEG (25%) Poor All d
(comparative)
PVA-9 4.3 %MOWIOLIErPVA 4-88 MW 31 k Good Poor
(comparative) 88% hydrolysed
PVA-10 4.3 % MOWIOr PVA 4-98 Mw 27 k Good Good
98% hydrolysed
PVA-11 4.3 % MOWIOL* PVA 40-88 Mw 195 k Good Good
88% hydrolysed
PVA-12 4.3 % ® PVA 40-88 Mw 205k Good Good
88% hydrolysed
PVA-13 4.3 %PVA (Mw146-186)/PTFE (0.5%) Good Good
PVA-14 4.3 %PVA -186)/PTFE (1%) Good Good
PVA-15 4.3 %PVA (Mw146-186)/PTFE (4.3 %) Good Good
Figure 1 illustrates that PVA-7 and PVA-8 exhibited no significant ethylene adsorption
capacity. The other PVA samples tested, however, demonstrated efficient ethylene
removal (see Figures 1 and 2).
t wishing to be bound by theory, it appears that the PVAs which exhibited good dry
coat adhesion and water-resistance are those which have a higher %hydrolysis and/or Mw.
While low Mw and low % hydrolysis PVAs may provide flexible/softer coatings, the PVAs
tested in this instance do not appear to be sufficiently water-resistant after drying.
Samples made directly from PTFE solutions showed poor adhesion to Tyvek® and so were
not tested further in ethylene uptake experiments. It was found, however, that small
amounts of PTFE added to PVA ations did not significantly affect the rate of ethylene
removal (see Figure 3).
The high molecular weight PVA may cause some cracking when prepared into a coating
and then folded or creased. PVA-15 (which comprises PTFE) appears to be more flexible
than PVA-13 or PVA-14 and therefore does not crack when creased in the same way.
Without wishing to be bound by theory, it is possible that the hydrophobic PTFE acts as a
binder er to introduce greater flexibility to the coating.
Example 5
Gums and Cellulosic itions
Gums and osic compositions were prepared and tested as bed in Example 3.
Table 2: Gums and Cellulosic Compositions
Figure 4 shows that the both the gums and cellulosic compositions A-D performed well in
adsorbing ethylene.
Example 6
Polyethylene Oxide Compositions
Polyethylene oxide compositions were prepared and tested as described in Example 3.
Table 3: Polyethylene Oxides
Figure 4 rates that the polyethylene oxide compositions E and F performed well in
adsorbing ethylene.
Example 7
Variation in drying temperatures and times
A variety of coatings were subjected to different drying temperatures and times. The
experimental conditions described in Example 3 were otherwise unchanged.
Table 4: variation in drying temperatures and times
Figure 5 shows that coatings made from PVA (Mw146-186, 99+ % hydrolysed) or
PVA/PTFE survive heating at 40 °C and 70 °C. This ts that drying is not an issue for
these ations. Sample C (2hydroxyethylcellulose) also performed well after drying a
sheet at 70 °C for 2 hours.
Example 8
Sheet Ageing
PVA coating PVA-6 was retested after 12 weeks storage (at room temperature in a sealed
plastic bag) to assess whether there was any deactivation with storage time. Figure 6
illustrates no icant deactivation occurred over 12 weeks at room temperature for this
sample.
Example 9
sion in water
Sample coatings which had passed the water spray test and showed good ethylene uptake
rates were also tested for longer term water resistance. A square ~ 2cmx2cm was cut out
from the print and submerged in water. The samples were checked after 5 min, 2 hours
and 12 hours for adhesion and softening.
Table 5: submersion in water for 5 minutes
Table 6: submersion in water for 2 hours
Table 7: submersion in water for 12 hours
From these experiments it was found that a variety of polymer binders survived 5 minutes,
2 hours or 12 hours in water.
Example 10
Submersion in water
Samples PVA-2, PVA-4, PVA-5 and PVA-6 (which had been prepared according to
Example 3) were redried at 40 °C for 3 hours and subjected to the water immersion test as
described in Example 9. This was done to ensure that the PVA had adhered tely to
the Tyvek® and to assess whether this improved the on.
Table 8: Results of submerging PVA coated (40 °C) sample in water for up to 12 hours
Table 8 shows a trend of improved water-resistance for the PVA samples with higher Mw.
This was most noticeable after 12 hours gence in water. The higher Mw PVA
samples could only removed by firm rubbing of the coating.
In this specification where reference has been made to patent specifications, other external
documents, or other sources of information, this is generally for the e of providing a
context for discussing the features of the invention. Unless specifically stated otherwise,
reference to such al documents is not to be construed as an admission that such
documents, or such sources of ation, in any jurisdiction, are prior art, or form part of
the common l knowledge in the art.
The following numbered paragraphs define particular aspects of the present disclosure:
1. A water-resistant composition for ing volatile organic compounds (VOCs) derived
from organic matter comprising:
a) palladium doped hydrogen-ZSM-5, n the Si:AI ratio of the hydrogen-ZSM-5 is
less than or equal to 200:1 ; and
b) at least one soluble binder.
2. A water-resistant composition according to paragraph 1, wherein the Si:AI ratio of the
hydrogen- ZSM-5 is less than or equal to 100:1.
3. A water-resistant composition according to paragraph 1 or paragraph 2, wherein the watersoluble
binder is selected from the group consisting of at least one polyvinyl alcohol, gum,
cellulose, cellulose derivative and polyethylene oxide.
4. A water-resistant composition according to any one of the preceding paragraphs, further
comprising one or more binder modifiers, driers, plasticisers, fillers, surfactants, pigments or
preservatives.
. A use of a resistant ition for adsorbing volatile organic compounds (VOCs)
derived from organic matter, wherein the water-resistant composition comprises:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is
less than or equal to 200:1 ; and
b) at least one water-soluble binder.
6. The use according to paragraph 5, wherein the Si:AI ratio of the en-ZSM-5 is less
than or equal to 100:1 .
7. The use according to aph 5 or paragraph 6, wherein the water-soluble binder is
selected from the group consisting of at least one polyvinyl alcohol, gum, cellulose, cellulose
derivative and polyethylene oxide.
8. The use ing to any one of paragraphs 5 to 7, further comprising one or more binder
modifiers, , plasticisers, fillers, surfactants, pigments, preservatives or preservatives.
9. The use according to any one of paragraphs 5 to 8, wherein the organic matter consists of
perishable organic goods.
. The use according to paragraph 9, wherein the able organic goods comprise items of
food or horticultural produce.
11. The use according to paragraph 10, wherein the items of food comprise fruit and/or
vegetables.
12. The use ing to paragraph 10, wherein the horticultural produce comprises plants
and/or cut s.
13. The use according to any of paragraphs 5 to 9, wherein the organic matter comprises
refuse.
14. The use according to any one of paragraphs 5 to 13, wherein the organic matter is
contained in a storage container or package.
. The use according to any one of aphs 5 to 14, wherein the water-resistant
composition is incorporated into, or into part of, the storage container or package.
16. The use according to any one of paragraphs 5 to 15, wherein the water-resistant
composition is incorporated into a label comprising a substrate.
17. The use according to any one of paragraphs 14 or 15, wherein the storage ner or
e is a refuse receptacle.
18. The use according to any one of paragraphs 5 to 17, wherein the VOCs are adsorbed at a
temperature of from -10 °C to 50 °C.
19. The use according to any one of paragraphs 5 to 18, wherein the VOCs are selected from
the group consisting of ethylene, formaldehyde and acetic acid.
. The use according to any of paragraphs 5 to 19, wherein the resistant composition is
used an environment comprising less than 10 vol% of oxygen. 21. The use according to
paragraph 20, wherein the environment is a controlled atmosphere or modified atmosphere
nment.
22. The use according to any one of paragraph 20 or paragraph 21 , wherein the oxygen is
present in the range between >0.5 vol% and <10 vol%.
23. The use according to any one of paragraphs 5 to 22, wherein the VOCs are adsorbed to a
level of less than or equal to 0.10 ppm.
24. An article comprising:
packaging or a container configured to hold organic ; and a water-resistant
composition comprising:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is
less than or equal to 200:1 ; and
b) at least one water-soluble binder.
. An article sing:
a water-resistant composition comprising:
a) palladium doped hydrogen-ZSM-5, n the Si:AI ratio of the hydrogen-ZSM-5 is
less than or equal to 200:1 ; and
b) at least one water-soluble binder,
and further wherein the article is a label or sheet.
26. An aqueous formulation comprising:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is
less than or equal to 200:1 ;
b) at least one water-soluble ;
c) optionally, at least one binder modifier, drier, plasticiser, filler, surfactant, pigment or
preservative; and
d) water.
27. An admix comprising:
a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the en-ZSM-5 is
less than or equal to 200:1 ;
b) at least one water-soluble binder; and
c) optionally, at least one binder er, drier, plasticiser, filler, surfactant, pigment or
preservative.
Claims (29)
1. A water-resistant composition for ing volatile organic compounds (VOCs) derived from organic matter comprising: a) palladium doped hydrogen-ZSM-5, wherein the Si:AI ratio of the hydrogen-ZSM-5 is less than or equal to 200:1 ; and b) at least one water-soluble , wherein the water-soluble binder is selected from the group consisting of guar gum, gum arabic, oxyethylcellulose, hydroxypropyl methylcellulose and polyethylene oxide.
2. A water-resistant composition according to claim 1, wherein the Si:AI ratio of the hydrogen- ZSM-5 is less than or equal to 100:1.
3. A water-resistant composition according to claim 1 or claim 2, further comprising one or more binder modifiers, driers, plasticisers, fillers, surfactants, pigments or preservatives.
4. A water-resistant composition according to claim 1, wherein the polyethylene oxide has a Mw from 100,000 to 1, 000,000.
5. A use of a water-resistant composition for adsorbing volatile c nds (VOCs) derived from organic matter, wherein the water-resistant composition is defined in any one of claims 1 to 4.
6. The use according to claim 5, wherein the organic matter ts of perishable organic goods.
7. The use according to claim 6, wherein the perishable organic goods comprise items of food or horticultural produce.
8. The use according to claim 7, wherein the items of food comprise fruit and/or vegetables.
9. The use ing to claim 7, wherein the ultural e comprises plants and/or cut flowers.
10. The use according to claim 5, wherein the organic matter comprises refuse.
11. The use according to any one of claims 5 to 10, wherein the organic matter is contained in a storage container or package.
12. The use according to any one of claims 5 to 10, wherein the water-resistant composition is incorporated into, or into part of, a storage container or e.
13. The use ing to any one of claims 5 to 12, wherein the water-resistant composition is incorporated into a label comprising a substrate.
14. The use according to claim 11 or claim 12, wherein the storage container or package is a refuse receptacle.
15. The use according to any one of claim 5 to 14, wherein the VOCs are adsorbed at a temperature of from -10 °C to 50 °C.
16. The use according to any one of claims 5 to 15, wherein the VOCs are selected from the group ting of ethylene, formaldehyde and acetic acid.
17. The use according to any of claims 5 to 16, wherein the water-resistant composition is used an environment comprising less than 10 vol% of oxygen.
18. The use according to claim 17, wherein the environment is a controlled atmosphere or modified atmosphere environment.
19. The use according to claim 17 or claim 18, wherein the oxygen is present in the range between >0.5 vol% and <10 vol%.
20. The use according to any one of claims 5 to 19, wherein the VOCs are adsorbed to a level of less than or equal to 0.10 ppm.
21. An article comprising: packaging or a container ured to hold c matter; and a water-resistant composition as defined in any one of claims 1 to 4.
22. An article comprising a water-resistant composition as defined in any one of claims 1 to 4, wherein the article is a label or sheet.
23. An aqueous formulation comprising a resistant composition as defined in any one of claims 1 to 4 and water.
24. An admix comprising a water-resistant composition as defined in any one of claims 1 to 4.
25. A composition according to any one of claims 1 to 4 ntially as herein bed, with reference to any example thereof, and with or without reference to the accompanying drawings.
26. The use according to any one of claims 5 to 20 substantially as herein bed, with reference to any example f, and with or without reference to the accompanying drawings.
27. An article according to claim 21 or claim 22 substantially as herein described, with reference to any example thereof, and with or without reference to the accompanying drawings.
28. An aqueous formulation according to claim 23 substantially as herein described, with reference to any example thereof, and with or without reference to the accompanying drawings.
29. An admix according to claim 24 substantially as herein described, with reference to any example thereof, and with or without reference to the anying drawings.