NZ626099B2 - Fiber composition comprising 1,3-glucan and a method of preparing same - Google Patents
Fiber composition comprising 1,3-glucan and a method of preparing same Download PDFInfo
- Publication number
- NZ626099B2 NZ626099B2 NZ626099A NZ62609912A NZ626099B2 NZ 626099 B2 NZ626099 B2 NZ 626099B2 NZ 626099 A NZ626099 A NZ 626099A NZ 62609912 A NZ62609912 A NZ 62609912A NZ 626099 B2 NZ626099 B2 NZ 626099B2
- Authority
- NZ
- New Zealand
- Prior art keywords
- glucan
- solution
- ionic liquid
- poly
- minutes
- Prior art date
Abstract
Disclosed herein is a solution comprising poly(?(1?3)glucan) and an imidazolium ionic liquid and the use thereof as a spinning solution for the preparation of fibers of poly(?(1?3)glucan) without the requirement of first derivatizing the poly(?(1?3)glucan).
Description
WO 20131101854
TITLE
1 ,3-GLUCAN AND A METHOD OF
FIBER COMPOSITION COMPRISING
PREPARING SAME
This application claims priority to US Provisional Application Nos.
61/582,187 and 61/582,189, both of which were filed on December 30,
2012, the entire contents of which are incorporated by reference herein.
BACKGROUND OF THE INVENTION
This invention relates to fibers formed from a(1 ~3)
polysaccharides, and to methods of producing said fibers. More
particularly, this invention relates to fiber spinning solutions comprising
a(1 ~3) polysaccharides using ionic liquids as solvents.
Cellulose, a polysaccharide consisting of 13(1-7 4 )-linked glucose,
formed by natural processes, (Applied Fiber Science, F. Happey, Ed.,
Chapter 8, E. Atkins, Academic Press, New York, 1979) has become the
preeminent fiber for use in manufactured textiles, films and resins. Cotton,
an especially pure form of naturally occurring cellulose, is well-known for
its beneficial attributes in textile applications.
Cellulosic fibers such as cotton and rayon increasingly present
sustainability issues with respect to land use and environmental imprint.
This may be a significant factor leading to increased level of research into
textiles containing polyester fiber blends with cellulosic materials and more
sustainable solutions for cellulosic-derived materials. It can be desirable to
produce fibers and other cellulosic materials using other glucose-based
polysaccharides - for example in films, fibers and resins that can be
economically produced from renewable resources. In addition it can be
desirable to produce such products using materials that are benign in the
environment.
Poly (a(1-73) glucan), a glucan polymer characterized by having
a(1-73) glycoside linkages, has been isolated by contacting an aqueous
solution of sucrose with a glycosyltransferase (gtfJ) enzyme isolated from
WO 20131101854
Streptococcus salivarius (Simpson et al., Microbiology, 141: 1451-1460,
1995). Poly (a(1-73) glucan) refers to a polysaccharide composed of D
glucose monomers linked by glycosidic bonds. Films prepared from poly
(a(1-73) glucan) tolerate temperatures up to 150°C and provide an
advantage over polymers obtained from 13(1-74) linked polysaccharides
(Ogawa et al., Fiber Differentiation Methods, 47: 353-362, 1980).
U.S. Patent No.7,000,000 disclosed preparation of a
polysaccharide fiber comprising hexose units, wherein at least 50% of the
hexose units within the polymer were linked via (a(1-73) glycoside
linkages using the gtfJ enzyme. The gtfJ enzyme utilizes sucrose as a
substrate in a polymerization reaction producing poly (a(1-73) glucan) and
fructose as end-products (Simpson et al., et al., Microbiology, 141: 1451-
1460,1995).
U.S. Patent No. 7,000,000 discloses a process for preparing fiber
from liquid crystalline solutions of acetylated poly(a(1-73) glucan). Thus
prepared fiber was then de-acetylated resulting in a fiber of poly(a(1-73)
glucan).
W02011056924 discloses the use of combinations of ionic liquids
as solvents for certain polymers, including biopolymers and synthetic
polymers. Ionic liquids can be desirable as solvents because of their
environmental impact, ease of processing, cost, and other potential
benign
benefits.
Rogers, in the Journal of the American Chemical Society (J. Am.
Chem. Soc., Vol. 124,4974-4975 (2002)) and Cai in the Journal of Applied
Polymer Science (Journal of Applied Polymer Science, Vol. 115, 1047-
1053 (2010)) describe ionic liquid solutions of cellulose.
While poly(a(1-73) glucan) and cellulosic polymers are similar in
many aspects, poly(a(1-73) glucan) does not exhibit the same solubility
behavior as cellulosic polymers in ionic liquids.
It can be desirable to provide ionic liquid solutions of poly(a(1-73)
glucan) for use in industrial processes, wherein the glucan fiber does not
WO 20131101854
require a further deacylation of the fiber. Further, it can be desirable to
provide solutions of poly(a(1-73) glucan) using ionic liquids as solvents,
but wherein the poly(a(1-73) glucan) can be recovered from the solution in
a fiber spinning operation.
SUMMARY OF THE INVENTION
In one aspect, an embodiment of the present invention is a solution
comprising poly(a(1-73) glucan) and an ionic liquid comprising a cation
selected from the group consisting of 1-ethyl, 3-methyl imidazolium; 1-
butyl, 3-methyl imidazolium, 1-hexyl, 3-methyl imidazolium, and mixtures
thereof; and, a halide or carboxylate counterion. In one embodiment, the
solution is isotropic.
In another aspect, an embodiment of the present invention is a
process for spinning a fiber from solution of poly(a(1-73) glucan) in an
ionic liquid, the process comprising the steps:
a) forming a mixture by combining (i) an ionic liquid comprising a
cation selected from the group consisting of 1-ethyl, 3-methyl
imidazolium; 1-butyl, 3-methyl imidazolium, 1-hexyl, 3-methyl
imidazolium, and mixtures thereof; and, a halide or carboxylate
counterion; and, (ii) poly(a(1---+3) glucan); said solution having a
solids content of 5 to 25% by weight;
b) heating said mixture under agitation to a temperature below the
boiling point of the ionic liquid to obtain a glucan spinning solution;
c) causing said spinning solution to flow through a spinneret,
thereby forming a fibrous strand;
d) causing said fibrous strand to contact a coagulating liquid
characterized by a pH in the range of 0 to 7, thereby forming a
poly(a(1 ~3) glucan) fiber.
WO 20131101854
BRIEF DESCRIPTION OF THE DRAWING
is a schematic diagram of an apparatus suitable for air gap
or wet spinning of liquid crystalline solutions of hexose polymer to form
polysaccharide fibers.
DETAILED DESCRIPTION OF THE INVENTION
Poly(a(1 ~3) glucan) compositions of the present invention
comprise poly(a(1 ~3) glucan) polymers obtained by polymerization of
sucrose via the action of a glucosyltransferase enzyme, as described in
U.S. Pat. No. 7,000,000, hereby incorporated by reference as if fully set
forth herein.
The poly(a(1 ~3) glucan) polymers of the present invention are
suitable for use as fibers, films, or resins. The poly(a(1 ~3) glucan)
polymers of the present invention are particularly useful as fibers. The
poly(a(1 ~3) glucan) polymers used to form fibers in the present
application must be dissolved in a solution in order to form a spinning
dope, that is, a composition from which glucan fiber can be recovered.
For the purposes of the present invention, by "soluble" it is meant
that the glucan/ionic solvent mixture does not have two or more distinct
phases, and/or that there are no visible particles or agglomerates in the
mixture.
The glucan polymers suitable for use as fibers of the present
invention have a number average molecular weight (Mn) of at least 10,000
Da. It can be desirable for the polymers of the present invention to have
molecular weights of 100,000 Da or more.
of interest of the poly(a(1 ~3) glucan) fibers prepared
Properties
according to the present invention include but are not limited to denier,
tenacity, elongation to break, and initial modulus. Suitability of the fiber for
any particular application generally involves a trade-off among these, and
other fiber properties. In addition, processing parameters are also part of
the trade-off.
WO 20131101854
In one embodiment of the process hereof, the spinneret is a multi
hole spinneret, and a plurality of parallel filaments is produced during
spinning. The filaments can be bundled after coagulation to form a multi
filament yarn.
In an alternative embodiment, the spinneret is a single hole
spinneret, and a monofilament is produced. In the monofilament
embodiment, fiber has a denier of at least 25. In a further embodiment,
the denier is at least 50. In a still further embodiment, the denier is at least
100. In general, finer deniers are preferred.
The fibers prepared according to the process hereof are
characterized by a tenacity of at least 0.25 grams per denier (gpd),
preferably at least 0.50 gpd; modulus of from 30 to about 60 gpd; and, an
elongation to break of from 1 to 10%.
The ionic liquids suitable for use as solvents for the poly(a(1 ~3)
glucan) polymer in the solution of the invention comprise a cation selected
from the group consisting of 1-ethyl, 3-methyl imidazolium; 1-butyl, 3-
methyl imidazolium, 1-hexyl, 3-methyl imidazolium, and mixtures thereof;
and, a halide or carboxylate counterion. Carboxylate is preferred.
1-ethyl, 3-methyl imidazolium carboxylate is preferred. 1-ethyl, 3-
methyl imidazolium acetate is most preferred.
In one embodiment, the solution hereof is isotropic.
In one embodiment, the solution hereof further comprises a non
solvent that can be present up to 50 % by weight with respect to the total
weight of solvent plus non-solvent. Preferably the non-solvent is present
at a concentration of 10 to 30 % by weight of solvent plus non-solvent.
In one embodiment, the present invention is a poly(a(1 ~3) glucan)
polymer/ionic liquid solution that is useful for spinning glucan fibers
(termed herein as "glucan spinning solution"). A glucan spinning solution
suitable for use in the preparation of fibers according to the the present
invention comprise 5 to 25 wt-% of poly(a(1 ~3) glucan) polymer. In one
embodiment, the glucan spinning solution comprises 10 to 20 wt-% of
WO 20131101854
poly(a(1 ~3) glucan) polymer. In a further embodiment, the glucan
spinning solution comprises 10 to 16 wt-% poly(a(1 ~3) glucan) polymer.
Following the practice of the art, the weight percent (wt-%) of the
polymer in the solution is known as "solids content" or "% solids" which as
defined and used herein is mass solute divided by mass of solution.
The poly(a(1 ~3) glucan) polymer suitable for the present invention
is not derivatized, such as to the corresponding poly(a(1 ~3) glucan)
acetate polymer, in order to form a solution and spin a fiber. While
derivatization expands the scope of compositions and conditions under
which fiber can be made, it also requires an additional hydrolysis step to
convert the glucan derivative back to the neat poly(a(1 ~3) glucan)
polymer. In the sense of eliminating the hydrolysis step after spinning, the
present invention represents an improvement over the art.
Glucan spinning solutions of the present invention are obtained by
a process comprising the step of contacting the glucan polymer with the
ionic liquid solvent. For the purposes of the present invention, the term
"ionic liquid solvent" shall encompass mixtures of a plurality of ionic liquid
solvents, or a mixture of one or more neat ionic liquid solvents with a non
solvent, so long as the resulting mixture remains a solvent for the
poly(a(1 ~3) glucan) polymer. The poly(a(1 ~3) glucan) polymer can be
added to the solvent with stirring or agitation, or alternatively the solvent
can be added to the glucan with stirring or agitation. In one embodiment,
the poly(a(1 ~3) glucan) polymer is mixed into the ionic liquid solvent at
ambient temperature, followed by heating under agitation to a temperature
above room temperature but below the boiling point of the ionic liquid
solvent. In an alternative embodiment, the components are mixed under
agitation, and heated simultaneously to a temperature above room
temperature but below the boiling point of the ionic liquid solvent. In yet
another alternative embodiment, the ionic liquid solvent is preheated to a
temperature above room temperature but below the boiling point of the
ionic liquid solvent, followed by mixing in with agitation the poly(a(1 ~3)
glucan) polymer. It is preferred to mix the poly(a(1 ~3) glucan) polymer
WO 20131101854
with the ionic liquid solvent at room temperature followed by gradual
heating under agitation to a temperature below the boiling point of the
ionic liquid solvent. The heating rate is preferably between 1 and 2
degrees per minute. The temperature should be controlled to achieve a
solution viscosity that facilitates efficient mixing.
In another aspect, the present invention is a process for spinning a
glucan fiber from a glucan composition, the process comprising the steps:
a) forming a mixture by combining (i) an ionic liquid comprising a
cation selected from the group consisting of 1-ethyl, 3-methyl
imidazolium; 1-butyl, 3-methyl imidazolium, 1-hexyl, 3-methyl
imidazolium, and mixtures thereof; and, a halide or carboxylate
counterion; and, (ii) a(1---+3) glucan; said solution having a solids
content of 5 to 25% by weight;
b) heating said mixture under agitation to a temperature below the
boiling point of the ionic liquid to obtain a glucan spinning solution;
c) causing said spinning solution to flow through a spinneret,
thereby forming a fibrous strand;
d) causing said fibrous strand to contact a coagulating liquid
characterized by a pH in the range of 0 to 7, thereby forming a
poly(a(1 ~3) glucan) fiber.
In one embodiment, the poly(a(1 ~3) glucan) suitable for the fiber
spinning process of the invention is characterized by Mn of at least 10,000
Oa. In a further embodiment, the Mn is at least 100,000 Oa.
In another aspect, the present invention is a process for obtaining a
glucan fiber from a spinning solution described herein. The process for
spinning glucan acetate fibers is described in U.S. Pat. No. 7,000,000.
The process as described therein is substantially the same as that used
herein, except that the glucan fibers are obtained from the spinning
solution described herein.
Figure 1 is a schematic diagram of an apparatus suitable for use in
the fiber spinning process hereof. The worm gear drive, 1, drives a ram,
2, at a controlled rate onto a piston fitted into a spinning cell, 3. The
WO 20131101854
spinning cell may contain filter assemblies. A suitable filter assembly
includes 100 and 325 mesh stainless steel screens. A spin pack, 5,
contains the spinneret and optionally stainless steel screens as prefilters
for the spinneret. The extruded filament, 6, produced therefrom is
optionally directed through an inert non coagulating layer (typically an air
gap) and into a liquid coagulating bath, 7. The extrudate can be, but need
not be, directed back and forth through the bath between guides, 8, which
are normally fabricated of Teflon® PTFE. Only one pass through the bath
is shown in Figure 1. On exiting the coagulation bath, 7, the thus
quenched filament, 9, can optionally be directed through a drawing zone
using independently driven rolls, 10, around which the thus quenched
filament is wrapped. The quenched filament may optionally be directed
through a second liquid bath, 11, that allows further treatment such as
additional solvent extraction, washing or drawing of the extruded filaments.
The thus prepared filament is then directed through a traversing
mechanism to evenly distribute the fiber on the bobbin, 12, and collected
on plastic or stainless steel bobbins using a wind up, 13. In one
embodiment, the process comprises a plurality of independently driven
rolls.
The spinning solution can be prepared by combining the ionic
liquid, non-solvent if desired, and poly(a(1 ~3) glucan) as described supra.
The solids content of poly(a(1 ~3) glucan) in the solution ranges from 5 to
% wt-% with respect to the total weight of the solution, with 5 to 20 wt-%
preferred. At concentrations of glucan below 5 % by weight, the viscosity
of the solution is greatly reduced. Solution concentrations above 16 % by
weight are increasingly problematical to form. In the range of 16 to 20 %
by weight, increasingly refined solution forming techniques are often
required. It is believed by the inventors hereof that sophisticated mixing
technology will permit formation of solutions having as much as 25%
solids, but solids content of that level have not been obtained in the
specific embodiments infra.
WO 20131101854
In any given embodiment, the solubility limit of glucan is a function
of the molecular weight, the ionic liquid solvent/non-solvent ratio, the
duration of mixing, the viscosity of the solution as it is being formed, the
shear forces to which the solution is subject, and the temperature at which
mixing takes place. In general, lower molecular weight glucan will be
more soluble than higher molecular weight, other things being equal.
Generally, higher shear mixing, longer mixing time, and higher
temperature will be associated with higher solubility. The maximum
temperature for mixing is limited by the boiling point of the solvents. The
optimum ionic liquid solvent/non-solvent ratio may change depending
upon the other parameters in the mixing process.
In one embodiment of the process hereof, the spinning solution is
isotropic.
The invention is further described in, but not limited by, the
following specific embodiments thereof.
PREPARATION OF GLUCOSYL TRANSFERASE (GTFJ) ENZYME
Materials
Dialysis tubing (Spectrapor 25225-226, 12000 molecular weight cut-off)
was obtained from VWR (Radnor, PA); Dextran and ethanol were obtained
from Sigma Aldrich. Sucrose was obtained from VWR; Suppressor 7153
antifoam was obtained from Cognis Corporation (Cincinnati, OH); All other
chemicals were obtained from commonly used suppliers of such
chemicals.
Seed medium
The seed medium, used to grow the starter cultures for the
fermenters, contained: yeast extract (Amberx 695, 5.0 grams per liter,
g/L), K2HP04 (10.0 g/L), KH2P04 (7.0 g/L), sodium citrate dihydrate (1.0
g/L), (NH4 )2S04 (4.0 g/L), MgS04 heptahydrate (1.0 g/L) and ferric
ammonium citrate (0.10 g/L). The pH of the medium was adjusted to 6.8
WO 20131101854
using either 5N NaOH or H2S04 and the medium was sterilized in the
flask. Post sterilization additions included glucose (20 mLlL of a 50% w/w
solution) and ampicillin (4 mLlL of a 25 mg/mL stock solution).
Fermenter medium
The growth medium used in the fermenter contained: KH2P04
(3.50 g/L), FeS04 heptahydrate (0.05 g/L), MgS04 heptahydrate (2.0 g/L),
sodium citrate dihydrate (1.90 g/L), yeast extract (Ambrex 695, 5.0 g/L),
Suppressor 7153 antifoam (0.25 milliliters per liter, mLlL), NaCI (1.0 g/L),
CaCI2 dihydrate (10 g/L), and NIT trace elements solution (10 mLlL). The
NIT trace elements solution contained citric acid monohydrate (10 g/L),
MnS04 hydrate (2 g/L), NaCI (2 g/L), FeS04 heptahydrate (0.5 g/L),
ZnS04 heptahydrate (0.2 g/L), CuS04 pentahydrate (0.02 g/L) and
NaMo04 dihydrate (0.02 g/L). Post sterilization additions included glucose
(12.5 g/L of a 50% w/w solution) and ampicillin (4 mLlL of a 25 mg/mL
stock solution).
Construction of glucosyltransferase (gtfJ) enzyme expression strain
A gene encoding the mature glucosyltransferase enzyme (gtfJ; EC
2.4.1.5; GENBANK® AAA26896.1, SEQ ID NO: 3) from Streptococcus
salivarius (ATCC 25975) was synthesized using codons optimized for
expression in E. coli (DNA 2.0, Menlo Park CA). The nucleic acid product
(SEQ ID NO: 1) was sub-cloned into pJexpress404® (DNA 2.0, Menlo
Park CA) to generate the plasmid identified as pMP52 (SEQ ID NO: 2).
The plasmid pMP52 was used to transform E. coli MG1655 (ATCC
47076™) to generate the strain identified as MG1655/pMP52. All
procedures used for construction of the glucosyltransferase enzyme
expression strain are well known in the art and can be performed by
individuals skilled in the relevant art without undue experimentation.
WO 20131101854
Production of recombinant gtfJ in fermentation
Production of the recombinant gtfJ enzyme in a fermenter was
initiated by preparing a pre-seed culture of the E. coli strain
MG1655/pMP52, expressing the gtfJ enzyme, constructed as described in
Example 1. A 10 mL aliquot of the seed medium was added into a 125 ml
disposable baffled flask and was inoculated with a 1.0 mL culture of E. coli
MG1655/pMP52 in 20% glycerol. This culture was allowed to grow at 37
°C while shaking at 300 revolutions per minute (rpm) for 3 hours.
A seed culture, for starting the fermenter, was prepared by charging a 2 L
shake flask with 0.5 L of the seed medium. 1.0 mL of the pre-seed culture
was aseptically transferred into 0.5 L seed medium in the flask and
cultivated at 37°C and 300 rpm for 5 hours. The seed culture was
transferred at optical density 550 nm (00550) >2 to a 14 L fermenter
(Braun, Perth Amboy, NJ) containing 8 L of the fermenter medium
described above at 37°C.
Cells of E. coli MG1655/pMP52 were allowed to grow in the
fermenter and glucose feed (50% w/w glucose solution containing 1 % w/w
MgS04·7H20) was initiated when glucose concentration in the medium
decreased to 0.5 g/L. The feed was started at 0.36 grams feed per minute
(g feed/min) and increased progressively each hour to 0.42, 0.49, 0.57,
0.66, 0.77, 0.90, 1.04, 1.21, 1.41 1.63, 1.92, 2.2 g feed/min respectively.
the rate was held constant afterwards by decreasing or temporarily
stopping the glucose feed when glucose concentration exceeded 0.1 g/L.
Glucose concentration in the medium was monitored using a YSI glucose
analyzer (YSI, Yellow Springs, Ohio).
Induction of glucosyltransferase enzyme activity was initiated, when
cells reached an 00550 of 70, with the addition of 9 mL of 0.5 M IPTG
(isopropyl 131-thiogalacto- pyranoside). The dissolved oxygen (~O)
concentration was controlled at 25% of air saturation. The DO was
controlled first by impeller agitation rate (400 to 1200 rpm) and later by
aeration rate (2 to 10 standard liters per minute, slpm). The pH was
controlled at 6.8. NH40H (14.5% weight/volume, w/v) and H2S04 (20%
WO 20131101854
w/v) were used for pH control. The back pressure was maintained at 0.5
bars. At various intervals (20, 25 and 30 hours), 5 ml of Suppressor 7153
antifoam was added into the fermenter to suppress foaming. Cells were
harvested by centrifugation 8 hours post IPTG addition and were stored at
-80°C as a cell paste.
Preparation of gtfJ crude enzyme extract from cell paste
The cell paste obtained above was suspended at 150 g/L in 50 mM
potassium phosphate buffer pH 7.2 to prepare a slurry. The slurry was
homogenized at 12,000 psi (Rannie-type machine, APV-1 000 or APV
16.56) and the homogenate chilled to 4°C. With moderately vigorous
stirring, 50 g of a floc solution (Aid rich no. 409138, 5% in 50 mM sodium
phosphate buffer pH 7.0) was added per liter of cell homogenate. Agitation
was reduced to light stirring for 15 minutes. The cell homogenate was then
clarified by centrifugation at 4500 rpm for 3 hours at 5-1 O°C. Supernatant,
containing crude gtfJ enzyme extract, was concentrated (approximately
5X) with a 30 kilo Dalton (kDa) cut-off membrane. The concentration of
protein in the gftJ enzyme solution was determined by the bicinchoninic
acid (BCA) protein assay (Sigma Aldrich) to be 4-8 g/L.
Preparation of poly(o(1 ~3) glucan)
All materials were obtained from VWR or Sigma Aldrich. In a 150
gallon glass lined reactor with stirring and temperature control
approximately 394kg of an aqueous solution was prepared by combining
75kg sucrose (VWR #BDH8029), Dextran T-10 500g (Sigma #09260),3.4
kg potassium phosphate buffer adjusted to pH 7.0 using 10 kg of 10%
KOH(aq.). All of the ingredients are added in the amount listed in table 1.
The solution was then charged with 32 units/liter of enzyme prepared as
described herein followed by an additional 1 L of de-ionized water and
mixed mildly at 25°C for 72 hours. The resulting glucan solids was
transferred to a Zwag filter with the mother liquor removed. The cake was
washed via displacement with water 3 times with approximately 150kg of
WO 20131101854
water. Finally two additional displacement washes with 1 OOL of methanol
were carried out. The material was dried under vacuum with a 60°C
jacket. Yield: 6.6 kg white flaky solids. The poly(a(1 ~3) glucan) polymer
so prepared is herein designated polymer P1.
Solutions of poly(a(1 ~3) glucan) polymer
Ionic liquids 1-butylmethylimidazolium acetate and 1-ethyl
methylimidazolium acetate were obtained from BASF. Ionic liquid 1-hexyl-
3-methylimidazolium chloride and 1-ethylmethylimidazolium chloride
were obtained from Sigma-Aldrich. Ionic liquid 1-butyl
methylimidazolium chloride was obtained from Fluka.
Example 1
In a glove box a 20 ml glass vial was charged with 1.99g of 1 ethyl,
3-methyl imidazolium acetate (EMIMAc). The vial was removed from the
glove box and 0.20 g of polymer P1 was added, bringing the solids level to
9.3 wt-%. The container was fitted with a cap through which a
polypropylene stirring rod had been fitted through a septum. The contents
were manually mixed with the plastic stirrer and placed in a
ReactiThermTM Heating and Stirring Module (Pierce, Rockford, IL) with an
inlet of nitrogen inserted through a needle through the septum. The
Reacti-Therm hereinafter shall be referred to as "the heating block." The
sample was stirred at room temperature for approximately 15 minutes.
The set point temperature of the heating block was then increased to 50
°C. After about 60 minutes, the set-point temperature was raised to 80 QC.
After about an additional 60 minutes, some solubility was observed. The
set-point temperature was then increased to 100°C. After an additional
120 minutes P1 was dissolved at the completion of the experiment. Upon
cooling, P1 remained in solution.
WO 20131101854
Example 2
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 1 were repeated except that 1.96 g of
EMIMAc and 0.27 g of polymer P1 were added. The solids level was 12.0
wt-%. After stirring at room temperature for approximately 15 minutes, the
set-point temperature of the heating block was then increased to 50°C.
After 50 minutes, an increase in viscosity was observed. The set-point
temperature was then raised to 80 QC. After an additional 55 minutes,
some solubility was observed. The set-point temperature was then
increased to 100°C. After an additional 180 minutes, polymer P1 was
dissolved. Upon cooling, the P1 remained in solution.
Example 3
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 1 were repeated except that 2.0 g of
EMIMAc and 0.35 g of polymer P1 were added. The solids level was 15.0
wt-%. After stirring at room temperature for approximately 15 minutes, the
set-point temperature of the heating block was then increased to 50°C.
After 50 minutes, an increase in viscosity was observed. The set-point
temperature was then raised to 80 QC. After an additional 55 minutes,
some solubility was observed. The set-point temperature was then
increased to 100°C. After an additional 230 minutes, polymer P1 was
dissolved. Upon cooling, the P1 remained in solution.
Example 4
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 3 were repeated except that 1.79 g of
EMIMAc was added. 0.27 g of polymer P1 together with 0.19 g of
deionized water were added. The solids level was 12.1 wt-%. After
stirring at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 50°C. After 40
minutes the set-point temperature was then raised to 80 QC. After an
WO 20131101854
additional 50 minutes, some solubility was observed. The set-point
temperature was then increased to 100°C. After an additional 70
minutes, polymer P1 was dissolved.
Example 5
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 3 were repeated except that 1.79 g of
EMIMAc was added. 0.35 g of polymer P1 together with 0.19 g of
deionized water were added. The solids level was 14.9 wt-%. After
stirring at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 50°C. After 40
minutes the set-point temperature was then raised to 80 QC. After an
additional 50 minutes, some solubility was observed. The set-point
temperature was then increased to 100°C. After an additional 70
minutes, polymer P1 was dissolved.
Example 6
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 3 were repeated except that 1.62 g of
EMIMAc was added. 0.22 g of polymer P1 together with 0.42 g of
deionized water were added. The solids level was 10.0 wt-%. After
stirring at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 50°C. After 40
minutes the set-point temperature was then raised to 80 QC. After an
additional 65 minutes, some solubility was observed. The set-point
temperature was then increased to 100°C. After an additional 75
minutes, polymer P1 was dissolved.
Example 7
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 3 were repeated except that 1.41 g of
EMIMAc was added. 0.27 g of polymer P1 together with 0.61 g of
WO 20131101854
deionized water were added. The solids level was 11.9 wt-%. After
stirring at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 50°C. After 45
minutes an increase in viscosity was observed. The set-point temperature
was then raised to 80 QC. After an additional 60 minutes, some solubility
was observed. The set-point temperature was then increased to 100°C.
After an additional 145 minutes, polymer P1 was dissolved.
Example 8
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 3 were repeated except that 1.40 g of
EMIMAc was added. 0.36 g of polymer P1 together with 0.59 g of
deionized water were added. The solids level was 15.2 wt-%. After
stirring at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 50°C. After 45
minutes an increase in viscosity was observed. The set-point temperature
was then raised to 80 QC. After an additional 60 minutes, some solubility
was observed. The set-point temperature was then increased to 100°C.
After an additional 145 minutes, the mixture so prepared was cooled to
room temperature and kept at room temperature for about 15 hours. The
mixture was then reheated to 80°C for 180 minutes, after which the
polymer P1 was observed to have dissolved.
Example 9
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 3 were repeated except that 1.41 g of
EMIMAc was added. 0.23 g of polymer P1 together with 0.63 g of
deionized water were added. The solids level was 10.0 wt-%. After
stirring at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 50°C. After 50
minutes an increase in viscosity was observed. The set-point temperature
was then raised to 80 QC. After an additional 55 minutes, some solubility
WO 20131101854
was observed. The set-point temperature was then increased to 100°C.
After an additional 80 minutes, polymer P1 was dissolved.
Comparative Example A
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 1 were repeated except that 2.0 g of 1-
butyl, 3-methyl imidazolium acetate (BMIMAc) was added instead of the
EMIMAc. 0.21 g of polymer P1 was added. The solids level was 9.3 wt
%. After stirring at room temperature for approximately 15 minutes, the
set-point temperature of the heating block was then increased to 50°C.
After 60 minutes the set-point temperature was then raised to 80 QC. After
an additional 60 minutes, the set-point temperature was then increased to
100°C. After an additional 120 minutes, polymer P1 was observed to not
have dissolved.
Comparative Example B
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Comparative Example A were repeated except that
2.0g of 1-ethyl, 3-methyl imidazolium chloride (EMIMCI) was added
instead of the BMIMAc. 0.22 g of polymer P1 was added. The solids level
was 10.0 wt-%. After stirring at room temperature for approximately 15
minutes, the set-point temperature of the heating block was then
increased to 50°C. After 40 minutes, the set-point temperature was then
raised to 80 QC. After an additional 50 minutes, the EMIMCI was observed
to have melted. The set-point temperature was then increased to 100°C.
After an additional 240 minutes, polymer P1 was observed to not have
dissolved.
Example 10
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Comparative Example A were repeated except that
2.0 g of 1-butyl, 3-methyl imidazolium chloride (BMIMCI) was added
WO 20131101854
instead of the BMIMAc. 0.23 g of polymer P1 was added. The solids level
was 10.1 wt-%. After stirring at room temperature for approximately 3
minutes, the set-point temperature of the heating block was then
increased to 50°C. After 40 minutes the set-point temperature was then
raised to 80 QC. After an additional 50 minutes, the set-point temperature
was then increased to 100°C. After an additional 80 minutes, some
increase in viscosity was observed. After 240 minutes at 100°C polymer
P1 had partially dissolved.
Example 11
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 1 were repeated except that 40.1 g of
EMIMAc and 5.5 g of polymer P1 were added. The solids level was 12.1
wt-%. After stirring at room temperature for approximately 15 minutes, the
set-point temperature of the heating block was then increased to 100°C.
After 240 minutes, the heat was turned off. The resultant solution was
cooled to room temperature overnight while remaining in the heating
block. Particulate matter was observed in the thus cooled solution. The
solution was reheated to 100°C. After 90 minutes, the polymer was
observed to have dissolved. The thus formed solution was again cooled
to room temperature.
Example 12
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 11 were repeated except that 36.05 g of
EMIMAc was added. 5.44 g of polymer P1 and 4.04 g of deionized water
were added to the EMIMAc. The solids level was 11.9 wt-%. After stirring
at room temperature for approximately 15 minutes, the set-point
temperature of the heating block was then increased to 100°C. After 240
minutes, the heat was turned off. The resultant solution was cooled to
room temperature overnight while remaining in the heating block. The
polymer was observed to have dissolved.
WO 20131101854
Examples 13-15
solution prepared in Example 11, using
Fibers were spun from the
the spinning apparatus shown in Figure 1 with the driven roll, 10, removed
from the filament pathway. The apparatus depicted in Figure 1 was
modified by removal of the driven roll, 10, and the second liquid bath, 11,
from the filament pathway. Spin stretch was attained by running the
windup faster than the jet velocity at the spinneret. The spin pack was
provided with a filter assembly consisting of 100 and 325 mesh screens.
The spinneret consisted of a single circular hole having a diameter of
0.005 in .. The spinneret hole had an LID ration of 6.000. The filament
was spun directly into glacial acetic acid with the air gap shown in Figure 1
set to a minimum. The glacial acetic acid coagulation bath was 4.4 feet in
length. The coagulated fiber was directed to to a speed controlled wind-up
with a traversing guide, and wound on bobbins at wind-up speeds shown
in Table 1. The fiber bobbins were soaked overnight in the media shown
in Table 1 and then removed and allowed to air dry before the fibers were
subjected to physical measurements. Table 1 gives the spinning
conditions that were used for the fibers prepared in Examples 15-17.
These include the pumping rate of the spinning solution to the spinneret,
the jet velocity of the spinning solution exiting the spinneret hole, the
length of the air gap, the temperature of the spinning solution, the wind-up
speed, and the spin stretch factor (SSF) which is the ratio of the wind-up
speed to the jet velocity.
Physical properties such as tenacity, elongation and initial modulus
were measured using methods and instruments conforming to ASTM
Standard Methods 03822 and 01577 (Option C), except that the test
specimen length was 10 inches. Reported results are averages for 3 to 5
individual yarn tests.
Table 1 shows the properties of the thus prepared filaments. These
include the denier of the fiber produced, and the physical properties such
as tenacity (T) in grams per denier (gpd), elongation to break (E, %), and
initial modulus (M) in gpd.
WO 20131101854
Example 16
Fiber was spun in the manner of Examples 13 - 15 but using the
spinning solution of Example 12. Spinning conditions and fiber properties
are shown in Table 1.
Table 1
Example 13 Example 14 Example 15 Example 16
Solvent: EMIMoAC EMIMoAC EMIMoAC EMIMoAC/water
(90: 1 0 wUwt)
% solids 12 12 12 12
Pump rate 40
80 80 80
(mLlmin)
Jet velocity 20 20 10 20
(ft/min)
112" 1/2" 7/16" 1/2"
Air gap
Temp CC) 24 24 23 24
Wind up speed 14.5 20.0 12.0 34
S.S.F. 0.7 1.0 1.2 1.7
Tenacity (gpd) 0.50 0.51 0.58 0.32
Enlongation 4.3 2.5 5.1 2.6
Modulus (gpd) 34 40 36 36
Denier (g) 86 58 34 49
10ne hole - diameter = 0.005; LID = 6.000
Example 17
The apparatus, materials, and procedures for charging the 20 ml
glass vial employed in Example 1 were repeated except that 2.74 g of 1-
hexyl, 3-methyl imidazolium chloride (HMIMCI) was added instead of the
BMIMAc, and 0.23 g of polymer P1 was added. The solids level was 10
wt-%. After stirring at room temperature for approximately 15 minutes, the
set-point temperature of the heating block was then increased to 50°C.
After 60 minutes, the set-point temperature was then raised to 80 QC.
After an additional 60 minutes, the set-point temperature was then
increased to 100°C. After an additional 30 minutes, an increase in
WO 20131101854
viscosity and some dissolution of P1 was observed. After 120 minutes at
100°C no further dissolution appeared to have occurred.
Example 18
In a glove box a 20 ml glass vial was charged with 0.75g of
EMIMAc and 0.25g BMIMAc then mixed by swirling the vial. Next, outside
of the glove box 0.12g of polymer P1 was added. The solids content was
11.0 wt-%. The vial was fitted with a cap through which a polypropylene
stirring rod had been fitted through a septum. The contents were manually
mixed with the plastic stirrer and placed in the heating block with an inlet
of nitrogen inserted through a needle through the septum. The sample
was stirred at room temperature for approximately 15 minutes. The
temperature set-point on the heating block was then increased to 50°C.
After about 60 minutes, the temperature set-point was raised to 80 QC.
After about 60 additional minutes, some solubility was observed. The
temperature set-point was then increased to 100°C. After an additional
120 minutes the polymer was observed to have dissolved.
Example 19
The apparatus, materials, and procedures of Example 18 were
replicated, except that 1.5 g of EMIMAC and 0.5 g of BMIMAc were added
and mixed. 0.36 g of polymer P1 was then added. The solids content was
.2 wt-%. After stirring for 15 minutes at room temperature, the
temperature set-point of the heating block was set to 50°C. After 40
minutes, the set-point was raised to 80 QC. After 55 additional minutes
some solubility was observed. The set-point was then raised to 100°C.
After an additional 120 minutes the polymer was observed to have
dissolved.
Example 20
The apparatus, materials, and procedures of Example 1 were
replicated except that 2.0 g of EMIMAc was added in place of the
WO 20131101854
BMIMAc. 0.50 g of polymer P1 was added. The solids content was 20
wt-%. Partial dissolution of the polymer was observed to have occurred at
the completion of the heating cycle as described in Example 1.
Comparative Example C
In a glove box a 20 ml glass vial was charged with 1 .Og of
EMIMOAc and 1.0g BMIMOAc then mixed by swirling the vial. Next
outside of the glove box 0.23g of polymer P1 was added bringing the
solids level to 10 wt %. The container was fitted with a cap through which
a polypropylene stirring rod had been fitted through a septum. The
contents were manually mixed with the plastic stirrer and placed in a
reactor block with an inlet of nitrogen inserted through a needle through
the septum. The sample was stirred at room temperature for
approximately 15 minutes. The temperature set-point of the heating block
was then increased to 50°C. After about 60 minutes, the set-point
temperature was raised to 80 QC. After another approximately 60 minutes,
some dissolution of the polymer was observed. The temperature was
then increased to 100°C. After an additional 120 minutes the polymer
remained partially dissolved.
WO 20131101854
Claims (13)
1. A solution comprising poly(a(1-73) glucan) and an ionic liquid comprising a cation selected from the group consisting of 1-ethyl, 3-methyl 5 imidazolium; 1-butyl, 3-methyl imidazolium, 1-hexyl, 3-methyl imidazolium, and mixtures thereof; and, a halide or carboxylate counterion.
2. The solution of Claim 1 wherein the ionic liquid comprises a carboxylate counterion.
3. The solution of Claim 2 wherein the ionic liquid is 1-ethyl, 3-methyl 10 imidazolium carboxylate.
4. The solution of Claim 3 wherein the ionic liquid is 1-ethyl, 3-methyl imidazolium acetate.
5. The solution of Claim 1 further comprising a concentration of non- solvent up to 30 % on a weight basis of the total weight of solvent plus 15 non-solvent.
6. The solution of Claim 1 wherein the poly(a(1-73) glucan) is present at a solids content of from about 5 weight percent to about 20 weight-%.
7. A process for spinning a fiber from a solution of poly(a(1-73) glucan) in an ionic liquid, the process comprising the steps: 20 a) forming a mixture by combining (i) an ionic liquid comprising a cation selected from the group consisting of 1-ethyl, 3-methyl imidazolium; 1-butyl, 3-methyl imidazolium, 1-hexyl, 3-methyl imidazolium, and mixtures thereof; and, a halide or carboxylate counterion; and, (ii) poly(a(1---+3) glucan); said solution having a 25 solids content of 5 to 25% by weight; b) heating said mixture under agitation to a temperature below the boiling point of the ionic liquid to obtain a glucan spinning solution; c) causing said spinning solution to flow through a spinneret, thereby forming a fibrous strand; 30 d) causing said fibrous strand to contact a coagulating liquid characterized by a pH in the range of 1 to 7, thereby forming a poly(a(1 ~3) glucan) fiber. WO 20131101854
8. The process of Claim 7 wherein the ionic liquid comprises a carboxylate counterion.
9. The process of Claim 8 wherein the ionic liquid is 1-ethyl, 3-methyl imidazolium carboxylate. 5
10. The process of Claim 9 wherein the ionic liquid is 1-ethyl, 3-methyl imidazolium acetate.
11. The process of Claim 7 wherein the solution further comprises up to 30 weight percent of a non-solvent that is water or an ionic liquid, on the basis of the total weight of solvent plus non-solvent. 10
12. The process of Claim 7 wherein the the poly(a(1-73) glucan) is present in the solution at a solids content of from about 5 weight percent to about 20 weight-%.
13. The process of Claim 7 wherein the coagulating liquid is glacial acetic acid.