Abstract

599750 A primary laminate continuous sheet 1b comprises a seal laminate 1 comprising a metal foil layer 5, a heat sealable layer 4 and a support layer 7, the heat sealable layer 4 being on one side of the foil 5 and the support layer 7 being on the opposite side of the foil 5, and a tab laminate comprising a continuous plastic sheet 10 formed of a transparent material and having first and second surfaces and several strips of longitudinal continuous tabstock 8 arranged intermittently across the primary laminate continuous sheet 1b. The tab laminate overlies the seal laminate 1 and the tabstock 8 is adhered to the plastic sheet 10 on the first sheet surface, being the surface facing the seal laminate 1. The plastic sheet 10 is adhered to the support layer between the tabstock strips 8 via an adhesive, where the break-in value of the adhesive bond is greater than 16 N/12.5 mm at 330 mm/min at 180°. Either surface of the plastic sheet 10 carries a printed pattern 11 of cured ink, the plastic sheet 10 is opaque in the region overlying the tabstock 8, and the printed pattern 11 is in registration with the strips of tabstock 8. The plastic sheet 10 is provided with a narrow longitudinally extending transparent band. A registration strip or tabstock 8 is provided underlying the transparent band that is visible through the band, is at a fixed position across the laminate relative to the said strips of tabstock 8 and provides a registration means for longitudinal slitting of the primary laminate continuous sheet 1b. mprising a continuous plastic sheet 10 formed of a transparent material and having first and second surfaces and several strips of longitudinal continuous tabstock 8 arranged intermittently across the primary laminate continuous sheet 1b. The tab laminate overlies the seal laminate 1 and the tabstock 8 is adhered to the plastic sheet 10 on the first sheet surface, being the surface facing the seal laminate 1. The plastic sheet 10 is adhered to the support layer between the tabstock strips 8 via an adhesive, where the break-in value of the adhesive bond is greater than 16 N/12.5 mm at 330 mm/min at 180°. Either surface of the plastic sheet 10 carries a printed pattern 11 of cured ink, the plastic sheet 10 is opaque in the region overlying the tabstock 8, and the printed pattern 11 is in registration with the strips of tabstock 8. The plastic sheet 10 is provided with a narrow longitudinally extending transparent band. A registration strip or tabstock 8 is provided underlying the transparent band that is visible through the band, is at a fixed position across the laminate relative to the said strips of tabstock 8 and provides a registration means for longitudinal slitting of the primary laminate continuous sheet 1b.

Description

PATENTS FORM NO. 5 Our ref: JB 234028NZPR NEW ZEALAND S ACT 1953 COMPLETE SPECIFICATION Coloured tabbed container closure liners We, Selig Sealing Products, Inc. a corporation organised under the laws of the State of Delaware of 342 East Wabash Street, Forrest, Illinois 61741, United States of America hereby declare the invention, for which we pray that a patent may be granted to us and the method by which it is to be performed, to be particularly described in and by the following ent: (followed by page 1a) Coloured Tabbed ner e Liners The present invention relates to a method of making a laminate which is used in container closure systems. The laminate ed is a primary laminate sheet including a tab stock. The te has a coloured top surface. The laminate is slit and punched to produce container closure liners which are sealed to the mouth of containers. The coloured top surface of the container closure liner is visible once the liner has been sealed to the mouth of the container.

It is common place in the packaging of a wide variety of materials ranging from pharmaceutical products to instant coffee that a closure is provided in the form of a seal connected to the mouth of a container. Often the closure is such that the underside of the seal has a heat sensitive adhesive coating or a meltable plastic layer covered by a metal foil. The metal foil can provide the substrate of the seal or may include a separate substrate formed from plastic material or paper. The seal closure is placed against the mouth of the container and sandwiched t it typically by an applied screw cap or snap on cap. An induction heat s heats the metal foil and in turn activates the heat sensitive adhesive layer or melts the plastic layer so that on cooling the seal closes the mouth of the container. Alternatively, the seal may be applied to the container without the means of a cap by direct ation and induction sealed in place. A snap on or screw cap can then be fitted or the seal can be accessible if required.

Containers used in the packaging ry are often provided with a screw cap so that once the seal has been opened the container can be temporarily closed again.

The caps of said containers and the containers themselves are often made out of a variety materials and are often a different colour, density or substance to each other. A difficulty encountered after the container has been emptied is that the container and cap have to be separated so that they can be recycled effectively. In many cases, the exclusion of a cap would leave just a seal laminate. in most cases this does not provide enough protection to the contents of the container as it could be easily pierced. It also eliminates the ability of the container to be ary resealed by the cap. (followed by page 2) In n cases, if the cap is transparent and is formed using the same material and density as the container, then this would not be acceptable in certain industrial circumstances as the cap is often used to y instructions, a logo or be identifiable by the end user. For example, in the milk industry, the colour of the screw cap is used by the consumer to identify the grade of the product in terms of fat content.

Another difficulty often encountered by eventual users is the removal of such container closure liners from the container. ts have thus far been made to incorporate a tab extending side ways from the mouth of the ner not within the circumference of the container so that the consumer can grip this to facilitate the removal of the ner closure liner.

EP1935636 describes a method of producing a primary laminate including a tabstock. The y laminate comprises a seal laminate, a foil layer and a top foam layer, a tabstock and a plastic film. The method in EP1935636 produces a y laminate wherein the tabstock strips are visible to the end user. This makes the procedure for slitting the laminate into rolls for punching out container closure liners simple as the operator can align the slitting machinery with the visible tabstock. if the ck were to be obscured it would be ible to determine where to slit the continuous sheet using the method disclosed in EP1935636.

EP2032460 discloses the use of coloured adhesive layer used in the formation of coloured sealing inserts for screw caps of containers. The introduction of ink into the adhesive could render these sealing inserts unsuitable as a container closure with a ck. The ink could decrease the strength of the adhesive layer of the primary laminate. This weakens the structural integrity of the container closures so that they are not able to be removed by pulling the tab. Instead the container closure liner would remain on the container mouth.

The method employed in EP2032460 only provides a method for producing a sealing insert with a single, solid colour. This does not allow for a pattern or non-solid colour to be visible to the end user. EP2032460 also highlights the difficulty of incorporating a d top layer on a sealing insert manufactured using the same methods to produce g inserts having a transparent top layer. it is suggested that the production of sealing inserts with a printed top layer is uneconomical due to high printing costs and high wastage.

GBZ443185 discloses a transparent cap and visible container closure liners for use in the milk industry. The container closure liner does not have a tab. 682443185 describes the use of a transparent cap to overcome the problem of container closure failure not being apparent to the consumer at the point of purchase. This is easily identified by the end user h the use of transparent screw caps. There is no disclosure of a method of making such container closure liners.

In one aspect, the present invention provides a primary laminate continuous sheet comprising a) a seal laminate comprising a metal foil layer, a heat sealable layer and a support layer, the heat sealable layer being on one side of the foil and the support layer being on the opposite side of the foil; and b) a tab laminate comprising a continuous plastic sheet formed of a transparent material and having first and second surfaces and several strips of udinal continuous tabstock arranged intermittently across the y laminate continuous sheet, wherein the tab laminate overlies the seal laminate and the tabstock is adhered to the plastic sheet on the first sheet surface, being the surface facing the seal te, and wherein the plastic sheet is adhered to the support layer between the tabstock strips via an adhesive, whereby the in value of the adhesive bond is greater than 16 N/12.5 mm at 330 mm/min at 180°, wherein either surface of the plastic sheet carries a d pattern of cured ink, the plastic sheet is opaque in the region overlying the tabstock, and the printed n is in registration with the strips of tabstock, wherein the plastic sheet is provided with a narrow longitudinally extending transparent band, and wherein a ration strip or tabstock is provided underlying the transparent band that is e through the band, is at a fixed position across the laminate ve to the said strips of tabstock and provides a registration means for longitudinal slitting of the primary laminate continuous sheet.

The present invention also provides methods of making the y laminate continuous sheet ing to the invention.

The present invention also provides a product comprising a) a container containing ible product; b) a container closure liner to be heat sealed around the mouth of the container; and in a preferred embodiment c) a transparent cap, which is removable from and replaceable onto the container, characterised in that the ink pattern can be seen through the cap; and that the arent cap is the same material and of similar density to the material used in the container.

The final t uses the ink pattern to obscure the foil and tabstock layers of the container closure and preferably the container and cap are made from the same materials so that they can be recycled together without the need to separate the cap from the ner. The invention is further illustrated in the drawings and Examples.

Also disclosed is a primary laminate continuous sheet comprising a) a seal laminate comprising a metal foil layer, a heat le layer and a support layer, the heat sealable layer being on one side of the foil and the support layer being on the opposite side of the foil; and b) a tab laminate comprising a uous plastic sheet having first and second surfaces and several strips of longitudinal continuous tabstock arranged intermittently across the primary laminate continuous sheet, wherein the tab laminate overlies the seal laminate and the ck is adhered to the plastic sheet on the first sheet surface, being the e facing the seal laminate, and wherein the plastic sheet is adhered to the support layer between the tabstock strips via an adhesive, whereby the break-in value of the adhesive bond is greater than 16 N/12.5 mm at 330 mm/min at 180°, terised in that either surface of the plastic sheet carries a d pattern of cured ink, the plastic sheet is opaque, and the printed pattern is in registration with the strips of tabstock.

Liners for closing containers are cut from the primary laminate so as to comprise tabs lying wholly within the circumference of the, usually circular liner.

The foil and heat sealable layer of the seal laminate are conventional for induction g systems. The heat sealable is suitable to form an adhesive seal to a food or beverage (i.e. comestible) container. (followed by page 4a) The support layer of the seal laminate may be a plastic sheet and is selected from the group consisting polyester, ably hylene terephthalate, polyamide, polypropylene or a composite, most preferably the support layer is polyethylene terephthalate.

The support layer of the seal laminate can comprise a foam layer. The foam may comprise several layers e.g. of coextruded materials having surface layers selected for compatibility with adjacent surfaces. The foam is preferably formed of lower alkene polymers and copolymers, preferably of ne and/or propylene. Foam formed from blended polymers may be used.

As noted above, an essential feature of the primary laminate is the inclusion of a tabstock so that the container closure liner will have a free tab. In the primary seal laminate produced, while the relative dimensions of the tab are not limited, it may be preferable that, for example the tab lies wholly within the circumference of the neck of the ner onto which the liner will be attached and typically the tab occupies about 50% of the seal area, where the primary laminate has a diameter of less than 36 mm. The tab stock may be 10-100 mm wide. The tab is provided by adhering a tab stock to the top plastic sheet of the primary laminate. The tabstock is narrower in width than the heat sealable laminate.

Preferably the ck is formed of a polyester, more ably polyethylene terephthalate. In one embodiment of the present invention, the bottom surface of the tabstock which is ultimately in contact with the t layer of the heat sealable laminate may be coated with a release material, for [FOLLOWED BY PAGE 5] example, silicone. This minimises the possibility, when the finished primary seal laminate is d to a container by induction heat sealing, of the tabstock sticking to the top support layer. Such release coatings are not typically necessary.

The adhesive needs to be one that has iently high surface energy to adhere to plastic materials such as PET but which will not damage the metallic rollers used. The adhesive should be of high enough peel strengths that low storage temperatures and at room temperature to avoid de-lamination of the container closure liner during removal from the sealed container using the adhered tab. The adhesive is based on a polymeric material, preferably an extrudable polymer. Materials with melt points (astm D3418) in the range 70- 100°C and ies (astm D792) in the range 0920-0955 g/cm3, for ce around 0940-0945 g/cm3 are suitable. Copolymer of ethylene with 01-12 alkyl (alk)acry|ate esters (e.g. acrylate or methacrylate esters), especially 01-4 alkyl esters, preferably of acrylic acid, especially butyl acrylate or methyl acrylate, may be used. The copolymers are random copolymers, for instance with molar proportions of acrylates of 05-25%, especially in the range 1-20%. ably the polymeric material has a melt flow index (astm D1238) of about 2 dg/min (190°C, 2.16 kg). A particularly preferred polymeric adhesive is the ethylene acrylate copolymer which has a melt flow index value of approximately 2 dg/min, a density of 0.94 g/cm3 and a melting point of 91°C.

The top layer of the tab laminate is a continuous plastic sheet which is made at least in part opaque by the covering ink. The covering ink can be printed so as to provide a pattern or a solid colour. In a red embodiment the printed plastic sheet is also coated with a lacquer when the pattern is carried on the second e which is used to protect the ink and the printed pattern and also t ink from contacting the comestible product.

It is important for the printed pattern on the top c sheet layer to be aligned with the tabstock underneath. In one embodiment the top sheet may have a n designed to provide relevant information for the consumer, e.g. “pull here” which would need to be aligned and ly on top of the tabstock.

Preferably the plastic sheet is formed of a material selected from the group consisting of polyester, preferably hylene terephthalate, polyamide, polypropylene or a ite. Most preferably the plastic sheet is polyethylene terephthalate.

Preferably the thickness of the plastic sheet is at least 20 ,um. More preferably the thickness of the plastic sheet is in the range from 20-40 ,um. In a preferred embodiment of the present invention, where the c sheet is PET preferably it has a surface layer with improved ve ties for instance formed by coextrusion.

Also disclosed is a method of forming container closures each comprising a transparent cap for fitting around the mouth of a container and a heat le liner within the cap for heat sealing to the mouth, wherein the liners are cut from a longitudinally extending laminate product sheet and positioned into the cap, the laminate product sheet comprising a) a seal laminate comprising a metal for a layer, a heat le layer and a support layer, the heat sealable layer being on one side of the foil and the support layer being on the opposite side of the foil; and b) a tab laminate comprising a product plastic sheet and at least one ribbon of tabstock extending longitudinally partially across the laminate continuous sheet, wherein the tab laminate es the seal laminate and the tabstock is adhered to the plastic sheet on the first sheet surface, being the surface facing the seal laminate, wherein the plastic sheet is adhered to the support layer between the strips of tabstock by an adhesive wherein the break-in value of the adhesive bond is greater than 16 N/12.5 mm at 330 mm/min at 180°, and wherein either surface of the plastic sheet carries a printed pattern of cured ink, the plastic sheet is , and the printed pattern is in registration with at least one ribbon of ck, wherein the liners are cut by a punch from the product sheet through the laminate including the tabstock such that a hinged tab is formed on each liner which lies over a proportion of the perimeter of the liner and liftable from the edge of the liner to form a hinge across the liner, terised in that the punching is aligned with the printed pattern of the cured ink, whereby the tab is visibly identifiable as a tab, and in that in the container e the cured ink is visible through the cap when using a transparent cap.

The container to which the container closure liner is attached may be made of glass or plastic material such as polyethylene, polyester, polyvinyl chloride, polypropylene or acrylonitrile-butadiene-styrene polymer.

A transparent screw cap equipped with a container closure liner as described above may be d on to the open neck of a container thus sandwiching the container closure liner between the open neck of the container and the top of the cap. ln a preferred embodiment, the screw cap is the same material, density and colour as the ner. The container closure liner is then adhered via the heat sealable on the lower surface of the te to the open neck of the container by induction heating.

As stated previously, the method of manufacturing the primary te and container closure liners of the present invention uses the main equipment which es previous products with minimal adaptation. The primary laminate can be made using a similar laminating station to that used in previous Application EP1935636 which es a coating of adhesive extruded between the plastic film stock and the top face of the primary substrate. A problem arises in attempting to align the tabstock underlayers on the primary laminate sheet with a printed pattern on top of the plastic sheet.

The apparatus required for the method of manufacture must have separate unwind stations for the laminate feeds that are arranged to enable simultaneous unwinding. The laminate feeds are fed to a lamination station comprising a nip between two rollers. At this point the feeds are adhered to each other to produce the primary laminate including a tabstock. The adhesive is applied vertically rds as a n into the nip where the feed rollers are in contact. The speed of the feed rollers which form the nip should be faster than the rate of application of adhesive to avoid build up of the molten adhesive in the nip which might result in an uneven coating. The adhesive is applied ly from the die head of an extruder.

Prior to reaching the laminating station, the bottom face of the ck and the t layer of the seal laminate are brought into contact. There is no adhesion between the two feeds. The two feeds are fed in contact with one another to the ting station. in order to achieve this, the two feeds must ch the laminating station from the same side relative to the extruder. The combination of the seal laminate and tabstock in contact with each other is referred to as a primary substrate as they are passed to the laminating station together. As the tabstock is necessarily narrower in width than the seal laminate, the top face of the primary substrate presented to the laminating station is formed partly of the top face of the tabstock and partly of the top layer of the seal laminate. The width of this plastic sheet is the same as or a little narrower than the width of the heat sealable laminate. lnk can be printed onto the plastic sheet so that it has been rendered opaque before the manufacture of the continuous primary laminate sheet.

The curtain of adhesive should not extend beyond the edge of the plastic sheet, and the edge portion which forms a thicker bead is ted between the edges of the plastic sheet and the support layer for trimming and removal. When pre- coated with printed ink, there is a narrow margin of uncoated PET sheet which provides means for registering the edge of the plastic sheet in order to overlay the print pattern correctly in line with the tabstock.

Registration of the d pattern or solid colour coated plastic sheet with the prepositioned tabstock means that the manufacturing process provides a method for making closures which obscure or completely hide the tabstock.

In the ting station, the primary substrate is t into t with the top plastic sheet which is fed aneously to the laminating station but from the opposite side of the curtain of adhesive. At the point where the top face of the primary ate is in contact with the bottom surface of the top plastic sheet, the polymeric adhesive is uously extruded between the two surfaces. The result is that the top plastic sheet is adhered over the entire surface area of the top face of the primary substrate. This means that over part of the width, the top plastic sheet will be adhered to the support of the seal laminate and over the remaining width, the top plastic sheet will be adhered to the top face of the ck. In a preferred embodiment where the primary laminate is cut, the result is that a tab portion is formed which lies wholly within the circumference of the seal.

Preferably the plastic sheet is corona treated on the e which ends up as the lowermost surface in the product, this treatment taking place upstream of the laminating station. This is done in order to ensure that the bond formed to the ric adhesive is sufficiently strong.

In one embodiment of the manufacturing process, the feed of tabstock comprises a plurality of narrow cks arranged across the machine at rly spaced apart intervals. In this way, a continuous sheet of primary laminate including a tabstock may be formed which can then be slit as required (in line or in subsequent operations) thus improving the efficiency of the system.

The primary laminate is slit into narrower continuous strips. The slitting of the primary laminate into narrower strips needs to be done with precision in order to ensure that the cuts are made at the correct positions to produce the tabs of the required size when punched so that they are functional. These er strips can then be punched or cut to form a container closure liner ready to be placed in the screw cap of the container. Punching or cutting may be carried out in a procedure and/or location te to the method of making the primary laminate. Alternatively the slit Primary laminate can be used in direct application where the seal liner is punched/cut and induction sealed directly onto the container in a uous process without the use of a cap. The ability of being able to correctly position the primary laminate on the equipment for slitting is of great importance in order that the tab within the slit tape is correctly positioned so that when d the tab within the punched liner is of the correct size and correctly positioned so that the tab is consistent and the tabbed portion is appropriately located to be capable of being grabbed at the point of opening. The difficulty arises as the strips of tabstock are not visible uously through the ink of the top plastic sheet.

In one embodiment of the method of manufacture involving slitting,one method for aligning the d top plastic sheet and the underlying ck during laminating of the product es that a narrow band of transparent top plastic sheet is left unprinted within the printed area. A registration strip at a fixed position ve to the tabstock ribbons/strips is laminated into the primary laminate continuous sheet.

During the laminating process the position of the printed top plastic sheet can be adjusted so that the band of clear transparent top plastic sheet aligns centrally about the registration tabbing strip. This s that the printed pattern aligns correctly with the hidden ck ribbons laminated within primary laminate.

A second method is the fitting of an optical sensor close to the point of lamination to detect the edge of the printed surface on the top plastic sheet, and via a drive system to laterally move the top plastic sheet unwind unit to control the position of the top plastic sheet, so that the band of clear transparent top plastic sheet aligns centrally about the registration tabbing strip within primary laminate.

The ability of being able to correctly position the primary te on the ent for slitting relative to the ng cutters is of great importance to ensure that the position of the tabstock within the slit tapes is tly position.

During slitting the registration print edge of the printed top plastic sheet on the primary laminate is monitored by an optical sensor, and via a drive system to laterally move the primary laminate unwind unit, so that the printed pattern and the ck within the primary te are correctly aligned to the slitting cutters. This ensures that the printed pattern and ck are correctly positioned on the slit tapes.

The primary te or continuous slit strips including a tabstock maybe uently wound onto a final roll after slitting.

The bond formed between the support layer of the seal laminate and the plastic film sheet must have an break-in value greater than 16 N/12.5 mm at 330 mm/min at 180° when the tab formed of tabstock and plastic sheet is pulled from the seal laminate at 90° to the longitudinal edge of the tab (which is the machine direction of the manufacturing apparatus) with an angle of separation of from the seal te 180°. This is in order to ensure that when using the tab to remove the seal from a container, the tab plastic sheet remains adhered to the primary laminate upon application of a pulling force to the tab.

The peel test is suitably carried out using a Hounsfield Tensile Tester.

Each test is carried out on three samples. The samples are cut from a strip 12.5 mm wide taken across a sample of primary laminate or slit strip of sufficient size.

The sample should be at least the length of the gap between two strips of tabstock. One end of the sample should be cut through the tabstock close to one longitudinal edge, allowing the tab comprising tabstock and plastic sheet to be separated from the seal laminate. The tabstock is d in one jaw of the Tensile Tester, with the seal laminate being fixed into the other jaw. The jaws te at an angle of 180°. A 50 N load cell is utilised for the test. The apparatus is set so as to allow an extension of at least 25 mm, with a speed of 330 mm per minute.

The s recorded include the “break-in force”, the force ed to overcome the initial resistance to tab de—lamination. uently the “running force” is measured, that is the force required to continue to separate the tab from the seal laminate. The running force is generally substantially constant. For the present product, the break-in force is the more important, since provided this is higher than the force required to peel the seal from the top of the container to which it is attached, the tab/plastic sheet will remain adhered to the seal as peeling starts, the force needed to continue this g being lower as the seal is peeled from the container.

Figure 1 is a cross section through an example of the primary laminate including a tabstock as formed according to the method of the present invention of a vertical dimension greatly exaggerated.

Figure 2 is a cross section through the screw cap container closure in place.

Figure 3 is a perspective view showing the seal closure in place on the neck of the ner.

Figure 4 is a schematic diagram of the laminating apparatus used in the method of the present invention.

Figure 5 is a ctive view of part of the apparatus rated in Figure 4 with a close up view of the transparent margin and visible registration mark.

Figure 6 is a cross sectional view through a sample of the primary laminate being subjected to the 180°C peel test to check the strength of the extruded adhesive.

EXAMPLE A primary laminate (1b) comprising a seal laminate (1) comprising a metal foil layer (5), a heat le layer (4), and a support layer (7). The seal laminate (1) is rolled onto the first feed roll (13) in the laminating apparatus.

The second unwind feed rollers (14) in the laminating apparatus is the source of the tabstock, which in this case, is a layer of polyethylene terephthalate (8). The width of the layer of polyethylene terephthalate (8) is typically in the range of 10—100 mm. A third feed roll (15) is loaded with the printed top c sheet, in this case a PET sheet (10). The thickness of the PET sheet (10) is in the range from 23—36 pm. The PET sheet (10) used is coextruded PET material with a surface layer which ensures optimal on to the adjacent support layer of the seal laminate. The PET sheet (10) also carries a printed pattern layer (11) which can be on either side of the PET sheet. The ink pattern renders the PET sheet opaque apart from an unprinted transparent band. The ink layer on the second surface can be further coated with a lacquer if ary.

The seal laminate (1), the tabstock (8) and PET stock (10) are aneously fed to the laminating station (6), the seal laminate (1) and the tabstock (8) are brought into contact to form a primary substrate (1a).

Ethylene methyl acrylate copolymer (9) with a melt flow index of 2 dg/min (190°C, 2.16 kg (astm D1238» is then extruded continuously as a curtain from the extruder (17) between the top face of the primary laminate (1a) and the bottom face of the PET sheet (10). The height of the die head above the nip was about 20 cm. The extrusion conditions, i.e. the weight of adhesive being extruded, its speed and extruder ature, were such that a temperature of greater than about 200°C, for instance as much as about 250°C is obtained at the nip for on. Roller (18) is a chilled stainless steel roller, while (19) has a Teflon coated e with Shore A hardness of 70. The rollers (18) and (19) are moving at a speed of 60 to 100 m/min relative to the speed of ation of the adhesive, the pressure between them selected to avoid the curtain creasing at the nip.

The bottom face of the plastic sheet (10) and the resulting primary laminate (1b) including the tabstock (8) is passed with the top face of the c sheet (10) in contact with the chilled roller (18) at a temperature of about 23°C to be rolled onto a final product roll (32). This process is illustrated schematically in Figure 4.

A registration tabbing strip (12a) is positioned on the primary substrate (1b) so that it can be seen through the transparent band (12b) of the top plastic sheet (1c) confirming that tabstock alignment is correct. This ration tabbing strip is ve to the position of the tabstock (8) of the primary substrate and the printed pattern (11) of the top plastic sheet. This system allows for accurate lamination of the tabstock (8) within the uous primary laminate relative to the printed patterns of the top plastic sheet and subsequent slitting of the continuous primary laminate into rolls of primary laminate with aligned tabstock and printed patterns.

In another embodiment, an al sensor (40) can be used to detect the edge of the printed pattern on the top plastic sheet and can control the lateral position of the top plastic sheet relative to the tabstock on the y substrate.

This can be seen schematically in Figure 5.

The in peel strength was measured as explained above and illustrated in Figure 6. The seal laminate comprising a support layer (7), foil (5) and heat sealable layer (4) were positioned into the lowerjaw (31) of the tensile tester. The plastic sheet (10), the tabstock (8) and ed ethylene methacrylate polymer (9) were mounted in the top jaw (31). The jaws were then moved apart in the direction of the arrow, with the force required to separate the materials at an angle of 180° being recorded. The break-in value was greater than 16 N/cm at 330 mm/min. The Figure is a schematic with the ess heavily exaggerated.

The primary laminate continuous sheet (1b) was then slit into narrow . During slitting, the edge of the printed top plastic sheet on the seal te was monitored by an optical , and via a drive system that laterally moved the seal laminate unwind unit, so that the printed n and the tabstock within the seal laminate were correctly aligned to the slitting cutters the web was slit. This ensured that the printed pattern and tabstock were corrected positioned on the slit tapes. From these slit tapes of seal laminate, seal liners were punched. The seal laminate liners were inserted inside transparent screw cap (20) which is made from the same material, is the same density and the same colour as the container. The screw cap (20) equipped with the container closure liners is then screwed onto the open neck of the bottle (24). The screw cap (20) and bottle (24) are then subjected to an induction heating process in which the toll is heated around its periphery by the ion process, which, in turn, melts the heat sealable layer (4) to bond the container closure liners to the open neck of the bottle.

Claims (25)

WHAT IS CLAIMED IS

1. A primary laminate continuous sheet comprising a) a seal laminate comprising a metal foil layer, a heat sealable layer and a support layer, the heat sealable layer being on one side of the foil and the support layer being on the opposite side of the foil; and b) a tab laminate comprising a continuous c sheet formed of a transparent material and having first and second es and several strips of udinal continuous tabstock arranged intermittently across the primary laminate continuous sheet, wherein the tab te overlies the seal laminate and the tabstock is adhered to the plastic sheet on the first sheet surface, being the surface facing the seal te, and wherein the c sheet is adhered to the t layer between the tabstock strips via an adhesive, whereby the break-in value of the adhesive bond is greater than 16 N/12.5 mm at 330 mm/min at 180°, wherein either surface of the plastic sheet s a printed pattern of cured ink, the plastic sheet is opaque in the region overlying the tabstock, and the printed n is in registration with the strips of tabstock, wherein the plastic sheet is ed with a narrow longitudinally extending transparent band, and wherein a registration strip or tabstock is provided underlying the transparent band that is visible through the band, is at a fixed position across the laminate relative to the said strips of tabstock and provides a registration means for longitudinal slitting of the primary laminate continuous sheet.

2. A continuous sheet according to claim 1, wherein the said adhesive is provided as a continuous layer across the said first sheet surface of the plastic sheet, whereby it adheres the plastic sheet to the tabstock strips and the support layer of the laminate.

3. A continuous sheet according to claim 2, n the said adhesive is an ed adhesive.

4. A continuous sheet according to claim 3, wherein the extruded adhesive is selected from the group consisting of polyethylene, polyethylene vinyl acetate, maleic anhydride/acrylate ester/polyethylene copolymer, ethylene methylacrylate copolymer and acid functional copolymer.

5. A continuous sheet according to any one of the previous claims, wherein only the second surface of the plastic sheet s a printed pattern of cured ink.

6. A continuous sheet according to claim 5, wherein the second surface of the plastic sheet is further coated over the ink with a lacquer that prevents ink migration.

7. A continuous sheet according to any one of claims 1 to 4, wherein only the first surface of the plastic sheet carries a printed n of cured ink.

8. A continuous sheet according to any one of the previous claims, in which the plastic sheet comprises polyester.

9. A continuous sheet according to claim 8, n the polyester is PET.

10. A continuous sheet according to any one of the previous claims, in which the support layer comprises a support layer and/or a foam layer.

11. A method of making a primary laminate continuous sheet according to claim 1, wherein several strips of udinal continuous tabstock and ration tabstock are ed intermittently across a seal laminate as defined in part (a) of claim 1, and are laminated to the first e of a plastic sheet, wherein the plastic sheet carries a cured printed pattern on either surface, by passing a curtain of adhesive between the seal te and the plastic sheet wherein during lamination the on of the plastic sheet is adjusted laterally relative to the on of the registration tabstock so that the printed n is in registration with the strips of tabstock.

12. A method according to claim 11 wherein an optical sensor is positioned close to the point of lamination of the primary laminate to detect the printed pattern of the plastic sheet and the registration tabstock and adjusts the lateral position of the top plastic sheet via a drive system.

13. A slitting method in which a primary laminate continuous sheet according to claim 1 or made according to the method of claim 11 or 12, is longitudinally slit to form two or more longitudinally extending product sheets by means of one or more cutters aligned in relation to the strips of tabstock by means of the registration tabstock, whereby each product sheet carries one or more tabstock strips.

14. A method according to claim 13, wherein the cutters are aligned by means of an l sensor which senses a single longitudinal slitting registration mark provided on the primary laminate continuous sheet.

15. A method of forming container closures each comprising a heat sealable liner for heat sealing to a mouth of a container, wherein the liners are cut from a longitudinally extending laminate product sheet produced by the slitting method of claim 13 or 14 and then formed by ng through the laminate including the tabstock such that a hinged tab is formed on each liner which lies over a proportion of the perimeter of the liner and liftable from the edge of the liner to form a hinge across the liner, n the punching is aligned with the printed pattern of the cured ink, whereby the tab is y identifiable as a tab, and in the container closure the cured ink is visible.

16. A method according to claim 15, wherein the container closure further comprises a cap for fitting around the mouth of a container, and wherein the heat-sealable liners are positioned within the cap.

17. A method according to claim 16 wherein the cap is transparent and the cured ink is visible through the cap.

18. A product comprising a) a container containing comestible products; b) a container closure produced according to the method of claim 15, n the heat le liner thereof is to be heat sealed around the mouth of the ner.

19. A product ing to claim 18, wherein the t further comprises a cap, which is ble from and replaceable onto the container.

20. A product according to claim 18 or 19, wherein the cap is transparent and the ink pattern can be seen through the cap.

21. A product according to any one of claims 18 to 20, wherein the cap is a similar thermoplastic material of a similar density and of a similar colour or transparency to the thermoplastic material used for the container.

22. A product according to any one of claims 18 to 21 wherein the ink pattern obscures the foil and tabstock.

23. A product according to any one of claims 18 to 22, wherein the container and cap are made from able materials.

24. A product according to claim 23, wherein the recyclable material is high density polyethylene.

25. A continuous sheet according to claim 1, substantially as herein described with reference to the Example and/or any one of the