NZ514718A - Forming a low molecular weight emulsion using polyacrylate, reaction stabilised with a hydrophobe and a catalytic chain transfer (cobaloxime) forming droplet size in the range of 30-120 nm - Google Patents

Abstract

A method of forming a polymer comprising: a) forming a mini-emulsion including i) a vinylic or acrylic monomer, ii) a non-aqueous solution including a cobalt-containing chain transfer agent, and iii) an aqueous solution; and b) reacting the mini-emulsion in the presence of an initiator for a time sufficient to form the polymer. The method is characterised in a separation of the chain transfer agent from a primary initiator radical by operating the chain transfer agent under polymerisation reaction under mini-emulsion conditions. The preferred embodiment describes the cobalt containing chain transfer agent being tetraphenyl cobaloxime boron fluoride (CoPhBF). A hydrophobe selected from alkanes and fatty alcohols is used to stabilise the formed mini-emulsion.

Description

Polymerisation reactions under mini-emulsion conditions Technical Field The present invention relates to a method for the formation of polymers by emulsion polymerisation and in particular to the formation of polymers under mini-emulsion conditions.

Background Art Emulsion polymerisation is widely used as a commercial process to produce a variety of latexes for a range of industries. Emulsion polymerisation processes are typically used to produce high molecular weight polymers, however, in recent times the advantage of generating much lower molecular weights for specific product applications has become evident. Catalytic chain transfer has been shown to be a highly effective synthetic tool for reducing molecular weight in free-radical solution/bulk polymerisation and emulsion polymerisation.

Limitations to the use of catalytic chain transfer agents in emulsion polymerisation reactions have been identified in the prior art. Firstly, such polymerisation reactions result in a loss of catalytic activity with time. This has, for example, been noted where cobaloximes are used as catalytic chain transfer agents. In addition, it has been noted that initiators which form oxygen centred peroxide radicals have a detrimental effect on the reaction, causing destruction of the catalyst. Similar behaviour has also been seen for oxygen centred persulfate radicals. This latter problem is highly inconvenient for commercial application of the technology, as persulfates are often the initiator of choice.

The present inventors have surprisingly found that one way of addressing the problem in the prior art is to separate the chain transfer agent from the primary initiator radicals by operating the chain transfer polymerisation reaction under mini-emulsion conditions.

In mini-emulsion polymerisation, the initial monomer droplet size, of about 100 nm is much smaller than conventional emulsion polymerisation, which is about 1 |j.m in size. Due to this size difference, particle nucleation occurs predominantly in the monomer droplets as opposed to creating a new particle phase. intellectual property office of n.z. 1 3 DEC 2001 received Disclosure of Invention In a first aspect, the present invention consists in a method of forming a polymer, the method comprising: a) forming a mini-emulsion including i) a vinylic or acrylic monomer, ii) a non-aqueous solution including a cobalt-containing chain transfer agent, and iii) an aqueous solution; and b) reacting the mini-emulsion in the presence of an initiator for a time sufficient to form the polymer.

Throughout the specification, the droplet size of the "mini-emulsion" formed according to the present invention will be understood to be in the range of about 30-120 nm.

The initiator for the polymerisation reaction can be included in the reaction prior to the formation of the mini-emulsion or in the mini-emulsion.

A variety of vinylic or acrylic monomers may be used in the present invention, including methacrylate derivatives, acrylate derivatives, acrylic acid, a-hydroxymethylacrylates, methacrylonitrile, a-hydroxymethylacrylonitrile, styrene and styrene derivatives. Methacrylate derivatives maybe selected from, methyl methacrylate (MMA), ethyl methacrylate, n-butyl methacrylate, i-butyl methacrylate, benzyl methacrylate, methacrylic acid and 2-hydroxyethyl methacrylate. Preferably the styrene derivative is a-methyl styrene. It will be appreciated, however, that the present invention is not limited to these monomers.

A variety of cobalt-containing chain transfer agents with varying hydrophobicity may be employed in the present invention. Suitable chain transfer agents are ones that are able to partition equally between the oil and water phase or those that reside primarily in the oil phase. An example of a suitable cobalt-containing chain transfer agent able to reside equally between the oil and water phase is cobaloxime boron fluoride (COBF) (Figure 1). A suitable chain transfer agent able to reside exclusively in the oil phase is tetraphenyl cobaloxime boron fluoride (COPhBF) (Figure 1). Preferably, the catalyst is present in a concentration of between 1 to 25 ppm.

The aqueous solution may consist of a surfactant in deionised water. A variety of surfactants selected from anionic, cationic and non-ionic intellectual property office of n.z. 1 3 DEC 2001 received surfactants may be used in the present invention either singularly or in combination. Preferably, the surfactant is sodium dodecylsulfate (SDS).

An initiator is included in the reaction either prior to the formation of the mini-emulsion or in the mini-emulsion. A variety of initiators capable of 5 generating free radicals in an aqueous or organic phase may be used in the present invention. Suitable initiators include peroxides, persulfates, azo initiators and redox initiator systems. Preferable persulfate initiators include potassium persulfate (KPS), ammonium persulfate, sodium persulfate Preferable azo initiators include azobisisobutyronitrile (AIBN), 10 azobiscyanovaleric acid and azobis(2-amidinopropane)dihydrochloride (Vazo V50™). Preferable redox initiators include a redox couple from which each member is selected from iron catalysts, sodium metabisulfite and sodium formaldehyde sulfonate. Particularly preferred are initiators that generate oxygen centred radicals such as, persulfates and peroxides. 15 The concentration of the initiator used will depend on many variables including temperature, monomer and other reaction conditions. The appropriate concentrations to be used falls within the skill of a formulator of polymers.

AIBN produces carbon-centred radicals while KPS produces oxygen 20 centred radicals. When AIBN is used as initiator, it is preferably added to the aqueous phase, prior to the formation of the mini-emulsion, while KPS is preferably predissolved in water and added in the mini-emulsion at the reaction temperature.

The mini-emulsion may be stabilised by the presence of a highly water-25 insoluble compound (hydrophobe). A possible role of the hydrophobe is to minimise the Ostwald ripening effect (diffusion of the oil phase from small to large droplets to reduce the interfacial free energy of the system). The hydrophobe is preferably contained in the non-aqueous solution. The hydrophobe may be selected from a variety of alkanes and fatty alcohols, 30 however, it will be appreciated that a suitable hydrophobe can be selected from a wide variety of other species. Preferably the alkane is hexadecane and the fatty alcohol is cetyl alcohol An advantage of mini-emulsion polymerisation is that highly water insoluble ingredients are present directly in the monomer droplets which are 35 the locus of polymerisation, whereas in conventional emulsion polymerisation, monomer and other reaction components need to diffuse intellectual property office of n.z. 1 3 DEC 2001 received 4 from the droplets via the water phase to the locus of the reaction (the particles). This can be exploited by dissolving highly water insoluble chain transfer agents directly into the monomer droplets, the loci of the reaction.

A mini-emulsion can be formed in a variety of ways. Preferably it is 5 formed from an emulsion by ultrasonification or high shear mixing at room temperature. In order to provide optimum polymerisation conditions, care should be taken at all steps to exclude oxygen from the system as the chain transfer agents are generally sensitive to oxygen once in solution. Typically, the cobalt-containing chain transfer agent is dissolved in the non-aqueous 10 solution comprising the monomer which were preferably degassed by freeze-pump-thaw cycles, usually about three cycles. The monomer solution is transferred via a cannula to the aqueous solution, which has preferably been deoxygenated by purging with an inert gas, for example argon, for one hour, and initial emulsification is achieved using, for example, a magnetic stirrer. 15 The mini-emulsion may be generated by, for example, ultrasonification of the emulsion for approximately fifteen minutes using an ultrasonic bath.

Typically, reaction of the mini-emulsion occurs in the same vessel in which the mini-emulsion is formed.

The reactions may take place at any suitable temperature. A 20 temperature range of about 40 to 80°C has been found to be particularly suitable. In a particularly preferred form, the reaction is controlled isothermally at about 65°C and ambient pressure in a flask fitted with a nitrogen purge and a magnetic stirrer. Samples may be removed periodically for conversion (by gravimetry) and molecular weight analyses. Typically, 25 reaction times are two to four hours. It will be appreciated, however, that the reaction time will vary depending on the polymer being formed.

In a second aspect, the present invention consists in a polymer prepared by the method according to the first aspect of the present invention.

Throughout this specification, unless the context requires otherwise, 30 the word "comprise", or variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated element or integer or group of elements or integers but not the exclusion of any other element or integer or group of elements or integers.

In order that the present invention may be more clearly understood, 35 preferred forms will be described with reference to the following examples and accompanying drawings. intellectual property office of N.Z. 1 3 DEC 2001 received Brief Description of the Figures Figure 1 shows structures of the chain transfer agents cobaloxime boron fluoride (COBF) and tetraphenyl cobaloxime boron fluoride (COPhBF).

Figure 2 is a graph showing dependence of Mj, vs conversion on the concentration of catalyst (COBF and COPhBF) for AIBN initiated runs.

Figure 3 is a graph showing dependence of conversion vs time on the concentration of catalyst (COBF and COPhBF) for AIBN initiated runs.

Figure 4 is a graph showing dependence of M^ vs conversion on the concentration of catalyst (COBF and COPhBF) for KPS initiated runs.

Figure 5 is a graph showing dependence of conversion vs time on the concentration of catalyst (COBF and COPhBF) for KPS initiated runs.

Modes for Carrying Out the Invention The following Examples further illustrate the present invention. Six examples of mini-emulsion polymerisation of methyl methacrylate using two different initiators (AIBN and KPS) and two different cobalt-containing chain transfer agents (COBF and COPhBF) have been described. The recipes for the mini-emulsion polymerisation reactions carried out according to Examples 2 to 5 and 7 to 8 are outlined in Tables 1 and 2.

Table 1: Typical recipe for mini-emulsion polymerisation reactions Component Mass/g water 80 sodium dodecylsulfate 0.80 methyl methacrylate hexadecane 0.50 initiator: AIBN or KPS 0.20 Catalyst: COBF or COPhBF see Table 2 General procedure Typically, the mini-emulsion was formed by the following procedure. The surfactant, sodium dodecylsulfate (SDS), was dissolved in deionised 25 water that was previously deoxygenated by purging with argon for one hour. The cobalt-containing chain transfer agent was dissolved in a non-aqueous solution comprising methyl methacrylate (MMA) and the hydrophobe (hexadecane), that were previously degassed by three freeze-pump-thaw intellectual property office of n.z. 1 3 DEC 2001 received cycles. The monomer solution was transferred via a cannula to the aqueous solution and initial emulsification was achieved using a magnetic stirrer. The mini-emulsion was generated by ultrasonification of the emulsion for fifteen minutes using an ultrasonic bath.

When AIBN was used as initiator, it was added to the aqueous phase with the SDS, prior to the formation of the emulsion. When KPS was used as the initiator, it was predissolved in water prior to the mini-emulsion at room temperature.

All reactions were performed in batch. The reactions were controlled 10 isothermally at 65°C in a flask fitted with a nitrogen purge and a magnetic stirrer. Samples were removed periodically for conversion (by gravimetry) and molecular weight analyses.

Molecular weight distributions may be measured by size exclusion chromatography (SEC) on a modular system, comprising an autoinjector, 15 guard column, two mixed bed columns (60 cm mixed C and 30 cm mixed E, Polymer Laboratories) and a differential refractive index detector. The eluent may be tetrahydrofuran at 1 mL/min, Final latex particle size distributions were measured using capillary hydrodynamic fractionation on a Matec Applied Sciences CHDF-1100 particle 20 size analyser, calibrated with polystyrene latex standards.

Comparative Testing In Examples 1 to 8, methyl methacrylate is polymerised under mini-emulsion conditions in a series of experiments designed to show the advantages of cobalt-containing chain transfer agents in mini-emulsion 25 polymerisation. Mini-emulsion polymerisation reactions with compositions as defined in Examples 2 to 5 and 7 to 8 (Tables 1 and 2) were compared with control polymerisation reactions containing no chain transfer agent, as seen in Examples 1 and 6. A summary of the runs conducted can be seen in Table 2. intellectual property office of n z. 1 3 DEC 2001 received 7 Table 2: Summary of Runs Examples Run Initiator Catalyst Concentration8' 1 Al AIBN - - 2 A2 AIBN COBF 3.0 3 A3 AIBN COBF 18 4 A4 AIBN COPhBF 2.0 A5 AIBN COPhBF 9.3 6 Kl KPS - - 7 K2 KPS COBF 17 8 K3 KPS COPhBF 2.0 a) ppm mol/mol, equivalent to [S]/[M] x 106, where [S] is the concentration of catalytic chain transfer agent and [M] is the monomer concentration.

Results from azobisisobutyronitrile (AIBN) Initiated Polymerisation The influence of cobalt containing chain transfer agents on the mini-emulsion polymerisation of MMA initiated by AIBN can be seen in Figures 2 and 3. The control polymerisation (run Al with no chain transfer agent) produces a number average molecular weight, in the order of 106 which is 10 typical of a mini-emulsion polymerisation. Upon the addition of 3.0 and 18 ppm COBF the molecular weight of PMMA is drastically reduced to 87.0xl03 and 4.41xl03 respectively. A similar trend is noted for the COPhBF mediated reactions with an even greater reduction in molecular weight to 18.4xl03 and 1.10x10s for a slightly lower concentrations of 2.0 and 9.3 ppm. 15 The first significant feature is that COPhBF appears to be a more effective catalyst than COBF under these conditions. This can easily be explained by the relative solubilities of the chain transfer agents in the two phases. It has been shown that COBF partitions approximately equally between the oil and water phase. Thus for the same overall catalyst 20 concentration, the COBF concentration in the locus of polymerisation is less than the COPhBF concentration which resides exclusively in the oil phase.

Another important point to make is that all these reactions were performed in batch and in the case of COPhBF mediated polymerisation (run A4) the efficiency of the transfer process was maintained throughout the 25 reaction to high conversion. This contrasts with previous emulsion studies where the transfer efficiency rapidly waned, and effective molecular weight intellectual property office of n.z. 1 3 DEC 2001 received control could only be maintained by the steady feed of catalyst throughout the reaction. Clearly the present inventors have been successful in utilising mini-emulsion polymerisation for effective compartmentalisation of the catalyst, preventing its contamination and degradation in the aqueous phase.

Results of the reaction initiated with AIBN are given in Table 3.

Results from Potassium Persulfate (KPS) Initiated Polymerisation The results for the KPS initiated polymerisation reactions of MMA are shown in Figures 4 and 5. The control polymerisation (Kl), without a cobalt-containing chain transfer agent, produced very similar results to the 10 corresponding AIBN run (Al) indicating no specific influence of initiator type on the reaction in the absence of cobalt containing chain transfer agents.

Upon the addition of 3.0 ppm COPhBF the molecular weight is reduced from 900xl03 to 17xl03 which is comparable to the molecular weight reduction in the corresponding AIBN initiated reaction (run A4 where Mn=18.4xl03). 15 This correlation shows that COPhBF maintains its efficiency as a chain transfer agent even in the presence of oxygen centred radicals. In the case of the COBF mediated reaction (K2) the molecular weight is reduced to 157xl03 a much smaller effect than the corresponding AIBN initiated run (A3) which produced a molecular weight of 4.41 xlO3 for similar catalyst concentrations. 20 It is quite clear that in the case of COBF with KPS initiation there is a significant reduction in catalyst performance. intellectual property office of nz. 1 3 DEC 2001 received Table 3: Summary of final properties from each run Molecular weight Particle size Distribution Distribution Averages Averages (PSD)a (MWD) (nm) Run Convb Mn Mw PDi Dn Dw PDi Nc Al 0.94 828xl03 2.12x10® 2.6 81 96 1.19 6.14 A2 0.65 87.0xl03 171xl03 96 135 1.41 3.69 A3 0.34 4.14xl03 .8xl03 2.4 - - - - A4 0.92 18.4xl03 116xl03 6.3 85 125 4.47 .23 A5 0.20 1.10x10s 3.76xl03 3.4 - - - - Kl 0.99 900xl03 2.3xl06 2.6 77 86 1.12 7.15 K2 0.96 157xl03 436xl03 2.8 71 76 1.07 9.12 K3 0.93 17.0xl03 52.3xl03 3.1 77 84 1.09 7.15 a Omitted samples did not go to high enough conversion to be measured by CHDF b Conversion of final sample taken Mn Number average molecular weight Mw Weight average molecular weight PDi Polydispersity Dn Number average diameter in nm Dw Weight average diameter in nm Nc Concentration of latex particles in L1 It will be appreciated by persons skilled in the art that numerous 15 variations and/or modifications may be made to the invention as shown in the specific embodiments without departing from the spirit or scope of the invention as broadly described. The present embodiments are, therefore, to be considered in all respects as illustrative and not restrictive. intellectual property office of n'. 1 3 DEC 2001 received

Claims (23)

Claims

1. A method of forming a polymer comprising: a) forming a mini-emulsion including i) a vinylic or acrylic monomer, ii) a non-aqueous solution including a cobalt-containing chain transfer agent, and iii) an aqueous solution; and b) reacting the mini-emulsion in the presence of an initiator for a time sufficient to form the polymer.

2. The method according to claim 1 wherein the vinyilc or acrylic monomer is selected from the group consisting methacrylate derivatives, acrylate derivatives, acrylic acid, a-hydroxymethylacrylates, methacrylonitrile, a-hydroxymethylacrylonitrile, styrene and styrene derivatives.

3. The method according to claim 2 wherein the methacrylate derivatives are selected from the group consisting of methyl methacrylate (MMA), ethyl methacrylate, 27-butyl methacrylate, i-butyl methacrylate, benzyl methacrylate, methacrylic acid, and 2-hydroxyethyl methacrylate.

4. The method according to claim 2 wherein the styrene derivative is a-methyl styrene.

5. The method according to any one of claims 1 to 4 wherein the mini-emulsion is stabilised by a hydrophobe.

6. The method according to claim 5 wherein the hydrophobe is included in the non-aqueous solution.

7. The method according to claim 5 or 6 wherein the hydrophobe is selected from alkanes and fatty alcohols.

8 The method according to claim 7 wherein the alkane is hexadecane and the fatty alcohol is cetyl alcohol.

9. The method according to any one of claims 1 to 8 wherein the cobalt-containing chain transfer agent partitions equally between the non-aqueous and aqueous solutions.

10. The method according to claim 9 wherein the cobalt-containing chain transfer agent is cobaloxime boron fluoride (COBF).

11. The method according to any one of claims 1 to 8 wherein the cobalt-containing chain transfer agent resides primarily in the non-aqueous solution. intellectual property office of n.z. 1 3 DEC 2001 received \ 11

12. The method according to claim 11 wherein the cobalt containing chain transfer agent is tetraphenyl cobaloxime boron fluoride (COPhBF).

13. The method according to any one of claims 1 or 12 wherein the initiator is included prior to formation of the mini-emulsion. 5

14. The method according to any one of claims 1 or 12 wherein the initiator is included after formation of the mini-emulsion.

15. The method according to any one of claims 1 or 14 wherein the initiator is selected from the group consisting of peroxides, persulfates, azo initiators, and redox initiators. 10

16. The method according to claims 15 wherein the persulfate initiator is selected from the group consisting of potassium persulfate (KPS), ammonium persulfate, and sodium persulfate.

17 The method according to claim 15 wherein the azo initiator is selected from the group consisting of azobisisobutyronitrile (AIBN), 15 azobiscyanovaleric acid, and azobis(2-amidinopropane)dihydrochloride.

18. The method according to claim 15 wherein the redox initiator is selected from the group consisting of iron catalysts, sodium metabisulfate and sodium formaldehyde sulfonate.

19. The method according to any one of claims 1 to 18 wherein the 20 aqueous solution includes of one or more surfactants.

20. The method according to claim 19 wherein the surfactants are selected from the group consisting of anionic, cationic and non-ionic surfactants.

21. The method according to claim 20 wherein the surfactant is sodium dodecylsulfate (SDS). 25

22. The method according to any one of claims 1 or 21 wherein the reaction is controlled isothermally at 65°C and ambient pressure.

23. A polymer prepared by the method according to any one of claims 1 to 22. END OF CLAIMS intellectual property office of nz. 1 3 DEC 2001 received