NO116994B - - Google Patents

Download PDF

Info

Publication number
NO116994B
NO116994B NO148694A NO14869463A NO116994B NO 116994 B NO116994 B NO 116994B NO 148694 A NO148694 A NO 148694A NO 14869463 A NO14869463 A NO 14869463A NO 116994 B NO116994 B NO 116994B
Authority
NO
Norway
Prior art keywords
approx
pressure
minutes
hot pressing
period
Prior art date
Application number
NO148694A
Other languages
Norwegian (no)
Inventor
Eugene Smits
Original Assignee
Eugene Smits
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from BE617809A external-priority patent/BE617809A/en
Application filed by Eugene Smits filed Critical Eugene Smits
Publication of NO116994B publication Critical patent/NO116994B/no

Description

Fremgangsmåte til fremstilling av nye konstruksjonsmaterialer. Procedure for the production of new construction materials.

Foreliggende oppfinnelse angår en fremgangsmåte til å frem-stille nye konstruksjonsmaterialer som er fordelaktige både på grunn av deres spesielle struktur og på grunn av deres overor-dentlige mange anvendelsesmuligheter. The present invention relates to a method for producing new construction materials which are advantageous both because of their special structure and because of their exceedingly many application possibilities.

Ved hjelp av oppfinnelsen settes der til disposisjon for fagfolk materialer som kan anvendes til konstruksjon av yttervegger og innervegger, av stasjonære eller flyttbare skillevegger og som kan utgjore en del av bunnbekledninger, raurverkskonstruksjoner, gulv og andre bygningsdeler. With the help of the invention, materials are made available to professionals which can be used for the construction of external walls and internal walls, of stationary or movable partitions and which can form part of floor coverings, masonry constructions, floors and other building parts.

På grunn av sin sammensetning og struktur er disse materialer samtidig relativt lette, har god motstandsdyktighet mot trykk og boyning, mot flammer og mot dimensjonsforandringer. Due to their composition and structure, these materials are at the same time relatively light, have good resistance to pressure and boyning, to flames and to dimensional changes.

Som en særlig original egenskap, istand til å medfdre et be-tydelig fremskritt på bygningsindustriens område, nevnes at disse nye produkter kan sages, spikres, at deler av samme kan skrues sammen med andre deler bestående av produktene eller av andre konstruksjonsmaterialer, perforeres, hovles, freses osv. uten at det brister eller sprekker eller får andre feil. As a particularly original feature, able to bring about significant progress in the area of the construction industry, it is mentioned that these new products can be sawn, nailed, that parts of the same can be screwed together with other parts consisting of the products or of other construction materials, perforated, planed , milled etc. without it cracking or cracking or getting other defects.

Man kan således feste konstruksjonsdeler fremstilt ved fremgangsmåten ifolge oppfinnelsen, ved meget enkle og dkonomiske mid-ler. Man kan likeledes foreta hvilke som helst nbdvendige uttag-ninger i et hvilket som helst oyeblikk og på et hvilket som helst sted. Men den mest originale egenskap er utvilsomt at produktene fra fremgangsmåten ifolge oppfinnelsen kan freses så at man på en okonomisk, rask og bekvem måte kan frembringe hvilke som helst ut-tagninger over hele konstruksjonselementets lengde, f. eks. for anordning av kanaler. One can thus fasten structural parts produced by the method according to the invention, by very simple and economical means. You can also make any necessary withdrawals at any time and in any place. But the most original feature is undoubtedly that the products from the method according to the invention can be milled so that in an economical, fast and convenient way, any recesses can be produced over the entire length of the construction element, e.g. for arrangement of channels.

Videre er produktene fra fremgangsmåten ifolge oppfinnelsen på en viss måte selv-sveisbare, således at de tillater en rask og fullstendig utforelse av enhver reparasjon og utfylning av hulrom, slik at de reparerte eller utfylte partier har noyaktig samme struktur som selve elementet. Således kan man efter å ha uttatt en renne og anbragt en ledning i denne, utfylle denne renne med det samme materiale som elementet består av, uten at denne utfylning blir Furthermore, the products from the method according to the invention are in a certain way self-weldable, so that they allow a quick and complete execution of any repair and filling of cavities, so that the repaired or filled parts have exactly the same structure as the element itself. Thus, after taking out a channel and placing a wire in it, you can fill this channel with the same material that the element is made of, without this filling being

synlig.visible.

Homogeniteten av konstruksjonselementene ifolge oppfinnelsen, selv efter utfylning av hulrom i samme eller efter utforelse av reparasjoner, er av meget stor viktighet for elementenes anvendelse særlig for en stor holdbarhet av overtrekk som påfdres ele-mentene, som malinger og lignende overtrekk. The homogeneity of the construction elements according to the invention, even after filling in cavities in the same or after carrying out repairs, is of very great importance for the use of the elements, especially for a high durability of coatings that are applied to the elements, such as paints and similar coatings.

Oe konstruksjonsmaterialer som fremstilles ved fremgangsmåten ifolge oppfinnelsen, omfatter sagmugg, et bindemiddel bestående av Oe construction materials which are produced by the method according to the invention, comprise sawdust, a binder consisting of

- en urea-formaldehydharpiks, et aluminiumsilikat som f. eks. kaolin, vann, et herdningsmiddel, og fortrinsvis et ytterligere fyllstoff, og det karakteristiske hovedtrekk ved oppfinnelsen er at roan blander de ovenfor nevnte stoffer, underkaster den erholdte blanding en forpresning i kold tilstand inntil den har en tykkelse på ca. 7 cm, hvorpå man underkaster det herved erholdte materiale et fbr-ste varmpresningstrin ved et trykk på ca. 60 kg/cm i et tidsrom på ca. 5 minutter og ved en temperatur på 50 - 60°C og derpå et - a urea-formaldehyde resin, an aluminum silicate such as kaolin, water, a hardening agent, and preferably a further filler, and the characteristic main feature of the invention is that Roan mixes the above-mentioned substances, subjects the resulting mixture to cold pressing until it has a thickness of approx. 7 cm, after which the material thus obtained is subjected to a first hot-pressing step at a pressure of approx. 60 kg/cm in a period of approx. 5 minutes and at a temperature of 50 - 60°C and then a

ytterligere varmpresningstrin ved et trykk fra 150 til 175 kg/cm<2>further hot pressing step at a pressure of 150 to 175 kg/cm<2>

i et tidsrom på ca.20 minutter og ved en temperatur på ca. 100°C, hvorved man mellom nevnte varmpresningstrin avlaster trykket ved å la presseanordningen stå åpen i ca» 1 minutt. in a period of approx. 20 minutes and at a temperature of approx. 100°C, whereby the pressure is relieved between the aforementioned hot pressing steps by leaving the pressing device open for approx. 1 minute.

Som katalysator kan man anvende aluminiumsilikater eller blandinger inneholdende sådanne, og ifolge en viktig utforelsesform for oppfinnelsen anvender man blandinger av aluminiumsilikater, f. eks. i form av leire og, i særdeleshet, i form av kaoling. Aluminum silicates or mixtures containing such can be used as a catalyst, and according to an important embodiment of the invention, mixtures of aluminum silicates are used, e.g. in the form of clay and, in particular, in the form of kaolin.

Den som organisk fyllstoff anvendte sagmugg er fortrinsvis harpiksholdig. The sawdust used as organic filler is preferably resinous.

I tilfelle hvor et ytterligere fyllstoff anvendes, kan man som sådant bruke ethvert materiale som er istand til å gi produktet onskede egenskaper, særlig gjore det meget lett. Med henblikk på dette kan man f. eks. anvende vermiculit, ekspanderte syntetiske harpikser eller visse syntetiske skumprodukter. In the case where an additional filler is used, any material capable of giving the product the desired properties, in particular making it very light, can be used as such. With a view to this, one can e.g. use vermiculite, expanded synthetic resins or certain synthetic foam products.

Det er en bemerkelsesverdig fordel ved fremgangsmåten ifolge oppfinnelsen at den tillater fremstilling av produkter med i ut-strakt grad forskjellige egenskaper på en slik måte at fagfolk meget lett kan bestemme mengdeforhold av og egenskaper hos de forskjellige bestanddeler med henblikk på den anvendelse av produktene som tilsiktes. It is a notable advantage of the method according to the invention that it allows the production of products with largely different properties in such a way that professionals can very easily determine the ratio of quantities and properties of the various components with a view to the intended use of the products .

I det folgende angis som eksempler noen sammensetninger av de blandinger som kan anvendes som utgangsmaterialer i fremgangsmåten ifolge oppfinnelsen, samt fremstilling av produktene fra disse blandinger. In the following, some compositions of the mixtures which can be used as starting materials in the method according to the invention, as well as the production of the products from these mixtures, are given as examples.

Eksempel 1Example 1

Eksempel 2 Example 2

Eksempel 3 Eksempel 4 Eksempel 5 Example 3 Example 4 Example 5

De stoffer som er angitt i ovenstående eksempler, med unntagelse av den polymeriserbare harpiks, blandes intimt i et tidsrom på f. eks. ca. 15 minutter. Derefter tilsetter man lang-somt den polymeriserbare harpiks mens blandingsoperasjonen fort-settes. Man lar denne foregå inntil man får en fullstendig homo-gen masse, hva der krever ca. 5 minutter. The substances indicated in the above examples, with the exception of the polymerizable resin, are intimately mixed for a period of e.g. about. 15 minutes. The polymerizable resin is then slowly added while the mixing operation continues. This is allowed to take place until a completely homogeneous mass is obtained, which requires approx. 5 minutes.

Derpå anbringes denne homogene blanding i en form hvis overflater er smutt med fett. Massen fordeles jevnt i formen, dens tykkelse kontrolleres og likeledes at den utfyller alle hjor-ner. Massen utsettes derpå for en forste trykkbehandling i kold tilstand slik at dens dimensjoner blir litt storre enn dens sluttelige dimensjoner, nemlig ca. 7 cm. This homogeneous mixture is then placed in a mold whose surfaces are smeared with grease. The mass is distributed evenly in the form, its thickness is checked and likewise that it fills all corners. The mass is then subjected to a first pressure treatment in a cold state so that its dimensions become slightly larger than its final dimensions, namely approx. 7 cm.

Denne behandling varer i kort tid, f. eks. ca. 5 minutter. Derpå utsetter man massen for innvirkning av trykk i varm tilstand ved en temperatur på 50 - 6o°C i ca. 5 minutter. Det trykk som herved påsettes, er ca. 60 kg/cm og er i alminnelighet halvparten av det sluttelige trykk. Derpå avlastes trykket ved at man lar presseanordningen stå åpen i ca. 1 minutt. Sluttelig påsetter man det maksimale trykk som ligger mellom 150 og 175 kg/cm ved en temperatur som ligger omkring 1Q0°C, og i et tidsrom på ca. 20 minutter. This treatment lasts for a short time, e.g. about. 5 minutes. The mass is then exposed to pressure in a hot state at a temperature of 50 - 6o°C for approx. 5 minutes. The pressure thereby applied is approx. 60 kg/cm and is generally half of the final pressure. The pressure is then relieved by leaving the press device open for approx. 1 minute. Finally, the maximum pressure is applied, which is between 150 and 175 kg/cm at a temperature of around 1Q0°C, and for a period of approx. 20 minutes.

Det trykk innenfor de angitte grenser som anvendes i detteThe pressure within the specified limits is used herein

siste trin er direkte en funksjon av naturen av den anvendte polymeriserbare harpiks og likeledes av tykkelsen eller dimensjonene av de elementer som skal fremstilles. the last step is directly a function of the nature of the polymerizable resin used and likewise of the thickness or dimensions of the elements to be produced.

Derefter tas produktet ut av formen og man påbegynner opera-The product is then taken out of the mold and the operation begins

sjonen påny med en ytterligere mengde blanding.again with a further amount of mixture.

Konstruksjonselementer man har fått på denne måte ved anvend-Construction elements that have been obtained in this way by using

else av mengdeforhold som angitt i eksempel 5 ovenfor, blev under-calculation of quantity ratios as stated in example 5 above, was under-

kastet forskjellige provninger i Laboratoires d'£ssais des Con-structions du Génie Civil et d'Hydraulique Fluviale, i Institut du Génie Civil de 1<1>Univerisité de Liége. threw various tests in the Laboratoires d'£ssais des Con-structions du Génie Civil et d'Hydraulique Fluviale, in the Institut du Génie Civil de 1<1>Univerisité de Liége.

Tre prbvestykker i form av terninger med dimensjoner 7x7x7Three test pieces in the form of cubes with dimensions 7x7x7

cm ble herved i en 10 tonns Amslerpresse utsatt for et trykk påcm was thereby subjected to a pressure of in a 10 tonne Amsler press

6 tonn. Til tross for at provestykkets spesifikke vekt ikke var storre enn ca. 0,450, steg belastningen for sprekkdannelse inntraff til ca. 15O0 kg og maksimalbelastningen til 1765 kg. 6 tons. Despite the fact that the specific weight of the sample was not greater than approx. 0.450, the load for cracking to occur increased to approx. 15O0 kg and the maximum load to 1765 kg.

En så hoy mekanisk styrke ved den ovenfor angitte lave spesi-Such a high mechanical strength at the above-mentioned low spec-

fikke vekt må sies å være temmelig overraskende.gained weight must be said to be rather surprising.

Prøvestykker av samme materiale og med dimensjoner 33 x IO x 7Test pieces of the same material and with dimensions 33 x 10 x 7

cm ble utsatt for bbyningspåkjenninger i et Amslerapparat for IOcm was subjected to bending stresses in an Amsler apparatus for IO

tonns trykk, ved et trykk på 500 kg. Prøvestykkene var understøt-tons of pressure, at a pressure of 500 kg. The test pieces were supported

tet på punkter hvis avstand mellom hverandre var 25 cm. Brudd-belastningen var 285 kg, hva der likeledes er bemerkelsesverdig for et slikt lett materiale. close at points whose distance between each other was 25 cm. The breaking load was 285 kg, which is also remarkable for such a light material.

Videre ble motstandsdyktigheten efter innvirkning av flammerFurthermore, the resistance was after the impact of flames

på materialet bestemt med prbvestykker hvis dimensjoner var 25 x 47 x 7 cm, likeledes i et Amslerapparat på 60 tonn, ved opp til on the material determined with test pieces whose dimensions were 25 x 47 x 7 cm, likewise in an Amsler apparatus of 60 tonnes, at up to

6 tonn. Den fundne maksimalbelastning var 4220 kg.6 tons. The maximum load found was 4220 kg.

Av disse provninger fremgår at man har for hånden et produktThese tests show that you have a product at hand

som kan anvendes i halvbærende konstruksjonselementer av enhver art. Således er det fullt ut tilfredsstillende for alle arter stasjonære which can be used in semi-supporting construction elements of any kind. Thus it is fully satisfactory for all stationary species

eller flyttbare innervegger, for yttervegger som stbtter seg til en bærende konstruksjon og likeledes for gulv og tak med rimelig storrelse, relativt stor tykkelse og som på sidene er understbttet av en passende bærende konstruksjon. or removable internal walls, for external walls that are supported by a load-bearing structure and likewise for floors and ceilings of reasonable size, relatively thick and that are supported on the sides by a suitable load-bearing structure.

Konstruksjonselementene som fremstilles ved fremgangsmåtenThe construction elements produced by the method

ifolge oppfinnelsen, kan gis enhver form og praktisk talt enhver according to the invention, can be given any shape and practically any

dimensjon, således kan de være i form av blokker, massive eller hule vegger eller i form av elementer som er profilert i overens-stemmelse med deres anvendelse. Dessuten kan de anvendes ved fremstilling av stive eller bbyelige konstruksjonselementer som even-tuelt kan være satt under forspenning. dimension, thus they can be in the form of blocks, solid or hollow walls or in the form of elements that are profiled in accordance with their application. Furthermore, they can be used in the production of rigid or flexible structural elements which may possibly be pre-stressed.

Claims (1)

Fremgangsmåte til fremstilling av konstruksjonsmaterialer som omfatter sagmugg, en urea-formaldehydharpiks, et aluminiumsilikat som f. eks. kaolin, vann, et herdningsmiddel, og fortrinsvis et ytterligere fyllstoff, karakterisert ved at man blander de ovenfor nevnte stoffer, underkaster den erholdte blanding en forpresning i kold tilstand inntil den har en tykkelse på ca. 7 cm, hvorpå man underkaster det herved erholdte materiale et forste varmpresningstrin ved et trykk på o ca. 60 kg/cm 2 i et tidsrom på ca. 5 minutter og ved en temperatur på 50 - 60°C og derpå et ytterligere varmpresningstrin ved ét trykk fra 150 til 175 kg/cm i et tidsrom på ca. 20 minutter og ved en temperatur på ca. 100°C, hvorved man mellom nevnte varmpresningstrin avlaster trykket ved å la presseanordningen stå åpen i ca. 1 minutt.Process for the production of construction materials comprising sawdust, a urea-formaldehyde resin, an aluminum silicate such as kaolin, water, a hardening agent, and preferably a further filler, characterized by mixing the above-mentioned substances, subjecting the resulting mixture to cold pressing until it has a thickness of approx. 7 cm, after which the material thus obtained is subjected to a first hot pressing step at a pressure of approx. 60 kg/cm 2 in a period of approx. 5 minutes and at a temperature of 50 - 60°C and then a further hot pressing step at a pressure of 150 to 175 kg/cm for a period of approx. 20 minutes and at a temperature of approx. 100°C, whereby between the aforementioned hot pressing steps the pressure is relieved by leaving the pressing device open for approx. 1 minute.
NO148694A 1962-05-18 1963-05-16 NO116994B (en)