NL8400625A - ARTISTS OF PAINTING ON THE BASIS OF SILICONES AND METHOD FOR THE PREPARATION THEREOF. - Google Patents
ARTISTS OF PAINTING ON THE BASIS OF SILICONES AND METHOD FOR THE PREPARATION THEREOF. Download PDFInfo
- Publication number
- NL8400625A NL8400625A NL8400625A NL8400625A NL8400625A NL 8400625 A NL8400625 A NL 8400625A NL 8400625 A NL8400625 A NL 8400625A NL 8400625 A NL8400625 A NL 8400625A NL 8400625 A NL8400625 A NL 8400625A
- Authority
- NL
- Netherlands
- Prior art keywords
- silicone
- paint
- paint according
- binder
- methyl
- Prior art date
Description
- 1 -- 1 -
Kunstschildersverf op basis van siliconen en werkwijze voor de bereiding ervan.Silicone painters based on silicone and method for its preparation.
De uitvinding beeft betrekking op kunstschildersverf, alsmede op een werkwijze voor de bereiding ervan. De kunstschildersverf volgens de uitvinding bevat organische polysiloxanpolymeren, die lak, hars of koud vulcaniserende 5 condensatie- of additiesiliconerubberpolymere bindmiddelen kunnen zijn.The invention relates to painters' paints and to a method for their preparation. The artist's paint according to the invention contains organic silicone polymers, which may be lacquer, resin or cold vulcanizing condensation or addition silicone rubber polymeric binders.
De olieverven, die gedurende honderden jaren alom zijn gebruikt, zijn bereid uit plantaardige drogende oliën (lijnzaadolie), geschikte pigmenten, toevoegsels (mastix) en 10 verdunners (terpentijn) volgens recepten, die zijn uitgewerkt aan de hand van de lange praktijk (Kiplik: Maltechnik, Meus-chel Edition, Berlijn, 1934).The oil paints, which have been widely used for hundreds of years, are prepared from vegetable drying oils (linseed oil), suitable pigments, additives (mastix) and 10 thinners (turpentine) according to recipes, which have been elaborated on the basis of long practice (Kiplik: Maltechnik, Meus-chel Edition, Berlin, 1934).
Deze bekende kunstschildersverven op organische basis bezitten - naast hun vele voordelen - ook nadelen. De 15 organische bestanddelen zijn onderhevig aan veroudering ten gevolge van oxidatieprocessen, die plaatsvinden ten gevolge van warmte, licht, enz., waarbij de verflaag desintegreert, afbreekt en afschilfert van de ondergrond als gevolg van der structieprocessen, of verandert de kleur (Schramm: Historische 2Q Malmaterialien, Dresden, 1971).In addition to their many advantages, these well-known organic-based painters also have disadvantages. The 15 organic components are subject to aging due to oxidation processes, which take place due to heat, light, etc., whereby the paint layer disintegrates, degrades and flakes off the substrate as a result of the construction processes, or changes the color (Schramm: Historisch 2Q Malmaterialien, Dresden, 1971).
In het bijzonder zijn de schilderijen op linnen-of houtbasis gevoelig, in de eerste plaats voor warmte en vochtgehalte van de lucht. Deze schilderijen kunnen in geval van een niet doelmatige opslag beschadigd worden, zelfs irre-25 versibel. Restauratie en opslag onder geschikte omstandigheden zijn grote hedendaagse problemen.In particular, the linen- or wood-based paintings are sensitive, primarily to heat and moisture content of the air. These paintings can be damaged in case of ineffective storage, even irre-versatility. Restoration and storage under suitable conditions are major contemporary problems.
De uitvinding beoogt de boven genoemde problemen op te lossen onder verschaffing van verven op siliconebasis, die bestand zijn tegen de boven genoemde effecten. De verven 30 volgens de uitvinding bevatten organische polysiloxanen als bindmiddelen, terwijl de pigmenten poedervormige kleurstoffen van minerale of synthetische origine’"zijn, bijv. Ti02, Fe2C>2, Cr2°3, cds' CoO, ZnO, enz.The object of the invention is to solve the above-mentioned problems by providing silicone-based paints that are resistant to the above-mentioned effects. The paints according to the invention contain organic polysiloxanes as binders, while the pigments are powdered dyes of mineral or synthetic origin, eg TiO2, Fe2C> 2, Cr2 ° 3, cds' CoO, ZnO, etc.
De verven volgens de uitvinding kunnen de volgen- / 8400625 -2- * .The paints according to the invention can follow the / 8400625 -2- *.
de bestanddelen bevattenj.the ingredients contain j.
variant 1: 20-80 gew.% siliconerubberbindmiddel met een vis-kositeit van 1000-20000 mPa.s. met polysiloxanen erin, die 5 zijn opgebouwd uit dimethyl- en in een geringere hoeveelheid uit methyl-vinyl-siloxy-eenheden met als eindstandige groepen dimethyl-hydroxy-silyl of dimethyl-vinyl-silyleengroepen; en bij voorkeur 80-20 gew.% van een pigment geschikt voor de artistieke doeleinden.variant 1: 20-80 wt.% silicone rubber binder with a viscosity of 1000-20000 mPa.s. containing polysiloxanes composed of dimethyl and in a minor amount of methyl vinyl siloxy units terminated with dimethyl hydroxy silyl or dimethyl vinyl silylene groups; and preferably 80-20% by weight of a pigment suitable for the artistic purposes.
10 Variant 2;10 Variant 2;
Alkydbindmiddel gecombineerd met aan de lucht drogende plantaardige oliën, gemodificeerd door siliconehars-tussenprodukten en pigmenten.Alkyd binder combined with air drying vegetable oils modified by silicone resin intermediates and pigments.
Variant 3: 15 Oplossing van aan de lucht drogende siliconelak- ken, met daarin alkyl-, aryl- en/of alkenyl-siloxy-eenheden, in hoofdzaak in hun trifunctionele eenheidsvorm, bij voorkeur methyl-, ^methyl-, fenyl?- en ^methyl-, fenyl-, vinyl7slloxy-eenheden, resp. gecombineerd met pigmenten.Variant 3: 15 Solution of air-drying silicone lacquers containing alkyl, aryl and / or alkenyl siloxy units, mainly in their trifunctional unit form, preferably methyl, methyl, phenyl and ^ methyl, phenyl, vinyl7slloxy units, respectively. combined with pigments.
20 De boven genoemde verven kunnen bovendien andere hulpstoffen bevatten, die gewoonlijk worden gebruikt bij de bereiding van verven, zoals plastificeermiddelen e.d.The above-mentioned paints may additionally contain other auxiliaries commonly used in the preparation of paints, such as plasticizers, etc.
tt
Volgens de onderhavige uitvinding kunnen de pigmenten worden gemengd met de onder varianten 1-3 beschreven 25 bindmiddelen volgens bekende verfbereidingstechnologieën (mechanische weg), of kan de kunstschilder de gewenste kleur bereiden door tijdens het schilderen de componenten met elkaar te vermengen.According to the present invention, the pigments can be mixed with the binders described under variants 1-3 according to known paint preparation technologies (mechanical route), or the painter can prepare the desired color by mixing the components together during painting.
Bij het bereiden van de boven genoemde verven 30 wordt 20-80 gew.% van het pigment met een deeltjesgrootte niet groter dan 5 jx gemengd met het bindmiddel. Het genoemde pigment kan worden gehydrofobiseerd met verschillende oppervlak-te-actieve siliconetussenprodukten, bijv. hexamethyl-disila-zan of het mengsel van dimethyl-dichloor-silaan en methyl-35 trichloor-silaan e.d. Vanzelfsprekend kan het genoemde pigment worden gebruikt zonder het te hydrofobiseren. Desgewenst kan er 1-5 gew.% van een verknopende katalysator en 0-40 gew.% van een vulmiddel of smeermiddel worden toegevoegd.In the preparation of the above-mentioned paints, 20-80% by weight of the pigment with a particle size no greater than 5 µm is mixed with the binder. The said pigment can be hydrophobized with various surfactant silicone intermediates, e.g. hexamethyl-disilazan or the mixture of dimethyl-dichlorosilane and methyl-trichlorosilane, etc. Of course, said pigment can be used without hydrophobizing . If desired, 1-5 wt% of a cross-linking catalyst and 0-40 wt% of a filler or lubricant can be added.
8400625 i * - 3 -8400625 i * - 3 -
Door toevoeging van de al dan niet vooraf behandelde pigmenten en smeermiddelen, alsmede hulpstoffen, aan het polysiloxanbindmiddel kunnen er verf pasta's worden bereid met een consistentie die overeenkomt met de klassieke olie-5 verven. De nieuwe anorganische verven op plasticbasis kunnen worden gebruikt voor het bekleden van verscheidene oppervlakken, bijv. textielglas, linnen, glas, hout, houtvezel, papier, beton, alsmede wandoppervlakken, bereid uit krasdeklaag, gips e.d. en derhalve voor het componeren van kunstwerken.By adding the pre-treated or non-treated pigments and lubricants, as well as auxiliaries, to the silicone binder, paint pastes can be prepared with a consistency similar to the classic oil-5 paints. The new inorganic plastic-based paints can be used for coating various surfaces, e.g. textile glass, linen, glass, wood, wood fiber, paper, concrete, as well as wall surfaces prepared from scratch coating, plaster, etc. and thus for composing works of art.
10 De uitvinding verschaft, verscheidene verven voor verschillende traditionele kunstschilderstechnieken, zoals olieverven, temperkleuren, aquarel e.d. De boven genoemde siliconeverffamilie voldoet aan de vereisten van alle boven genoemde kunstschildertechnieken.The invention provides various paints for different traditional painting techniques, such as oil paints, temper colors, watercolor etc. The above silicone family meets the requirements of all of the above painting techniques.
15 Wanneer de verf op basis van het siliconerubber- bindmiddel volgens variant 1 op linnen of textielglas wordt aangebracht, resulteert dit in schilderijen, die soortgelijk of identiek zijn aan schilderijen, die verkregen zijn door toepassing van traditionele olieverven. Evenzo wanneer gebruik 20 wordt gemaakt van de alkydhars gecombineerd met plantaardige olie en gemodificeerd met aan de lucht drogende siliconetus-senprodukten, d.w.z. verven volgens variant 2, komt dit overeen in algemene termen met een schilderstechniek, identiek aan die van olieverven. Deze laatste verf kan worden gebruikt voor 25 linnen, hout, houtvezel, glas, metaal en andere dragers. De aan de lucht drogende siliconelak volgens variant 3 kan in de eerste plaats worden gebruikt voor het maken van schilderijen op poreuze oppervlakken, bijv. papier, hout, gips, cement, krascoating e.d. · 30 Thans volgt een meer uitvoerige bespreking van de boven genoemde varianten.When the paint based on the silicone rubber binder according to variant 1 is applied to linen or textile glass, this results in paintings which are similar or identical to paintings obtained by using traditional oil paints. Likewise, when the alkyd resin is used in combination with vegetable oil and modified with air-drying silicone fluids, i.e. paints of variant 2, this corresponds in general terms to a painting technique identical to that of oil paints. The latter paint can be used for linen, wood, wood fiber, glass, metal and other supports. The air-drying silicone varnish according to variant 3 can primarily be used for painting on porous surfaces, eg paper, wood, plaster, cement, scratch coating, etc. 30 A more detailed discussion of the above-mentioned variants will now follow. .
Variant IsVariant Is
De eigenschappen van het koud vulcaniserende bindmiddel zijn als volgts 35 in chemisch opzicht zijn de boven genoemde poly- siloxanen opgebouwd uit methyl-, of methyl-fenyl-, of methyl-vinyl-siloxy-eenheden, terwijl de genoemde polysiloxanketens als eindstandige groepen reactieve groepen bevatten zoals / 8400625 4 \ » - 4 - hydroxy- of vinylgroepen.The properties of the cold vulcanizing binder are as follows chemically, the above-mentioned polysiloxanes are made up of methyl, or methyl-phenyl, or methyl-vinyl-siloxy units, while said polysiloxane chains are end groups of reactive groups such as / 8400625 contain 4 \ 4 -hydroxy or vinyl groups.
De polymerisatiegraad van de boven genoemde poly-siloxanen ligt tussen 100 en 10000/ terwijl de viskositeit ervan ligt tussen 1000 en 200000 mPa.s., bij voorkeur tussen 5 2000 en 100.000 mPa.s.The degree of polymerization of the above-mentioned polysiloxanes is between 100 and 10000 m, while its viscosity is between 1000 and 200000 mPa.s., preferably between 2000 and 100,000 mPa.s.
In de,boven genoemde verven kunnen bijv. de volgende koud vulcaniserende siliconerubbers worden gebruikt: één-component-siliconerubbers, die kunnen worden verknoopt onder toepassing van een katalysator die hydrolyse 10 mogelijk maakt ten gevolge van het vochtgehalte van de lucht en die alkyl-acyloxy-, alkyl-aminogroepen e.d. bevatten.For example, in the above-mentioned paints, the following cold vulcanizing silicone rubbers can be used: one-component silicone rubbers, which can be cross-linked using a catalyst that allows hydrolysis due to the moisture content of the air and that alkyl acyloxy alkyl, amino groups, etc.
Twee-componenten koud vulcaniserende silicone-rubbers, die gebruikt kunnen worden samen met een katalysator, die gebruikt wordt voor het verknopen van koud vulcaniserende 15 rubbers, die gekozen worden overeenkomstig de gewenste vulca-nisatietijd.Two-component cold vulcanizing silicone rubbers, which can be used in conjunction with a catalyst, which is used to crosslink cold vulcanizing rubbers, which are selected according to the desired vulcanization time.
Twee-componenten koud vulcaniserende rubbers, waarin iên van de componenten methyl-vinyl-polysiloxan is en de andere methyl-waterstof-polysiloxan en die verknoopt kan 20 zijn door additiereactie in aanwezigheid van geschikte katalysatoren, bijv. H^PtClg e.d,Two-component cold vulcanizing rubbers, in which one of the components is methyl-vinyl-polysiloxane and the other methyl-hydrogen-polysiloxane and which can be cross-linked by addition reaction in the presence of suitable catalysts, eg H ^ PtClg and the like,
De actieve vulmiddelen in de verven volgens variant 1 zijn in de eerste plaats de onbehandelde of opper- vlakte-behandelde aerosils met een soortelijk oppervlak van 2 25 100-400 m /g (witte koolstof). De genoemde vulmiddelen kunnen in de verf aanwezig zijn in een hoeveelheid van 0-36 gew.%.The active fillers in the paints of variant 1 are primarily the untreated or surface-treated aerosils with a surface area of 2 100-400 m / g (white carbon). The said fillers may be present in the paint in an amount of 0-36% by weight.
Inactieve vulmiddelen zijn kwartsmeel, Celite, diatomeeënaarde, kaoliniet, aluminiumhydraat e.d. De hoeveelheid ervan in de verf bedraag tussen 0 en 20 gew.%.Inactive fillers are quartz flour, Celite, diatomaceous earth, kaolinite, aluminum hydrate, etc. The amount of it in the paint is between 0 and 20% by weight.
30 Het silicone-olieplastificeermiddel is een methyl- en resp. methyl-fenyl-silicone-olie met een viskositeit van 10-1000 mPa.s., bij voorkeur 10-50 mPa.s.The silicone oil plasticizer is a methyl and resp. methyl phenyl silicone oil with a viscosity of 10-1000 mPa.s., preferably 10-50 mPa.s.
Als pigmenten worden bij voorkeur de wel bekende poedervormige kleurstoffen van meestal anorganische origine 35 gebruikt, welke bestand zijn tegen warmte (tenminste vanaf 100 tot 500°C), UV-straling, licht en storm en die niet reageren met verontreinigingen uit de lucht, bijv. CO, C02, H2S, S02, N02 e.d.Preferred pigments are the well-known powdery dyes of mostly inorganic origin, which are resistant to heat (at least from 100 to 500 ° C), UV radiation, light and storm and which do not react with air pollutants, eg CO, CO2, H2S, SO2, NO2 ed
8400625 ' r * - 5 -8400625 'r * - 5 -
De verfpasta kan worden verdund met diverse niet-polaire organische oplosmiddelen, zoals terpentine, benzeen, tolueen, xyleen, gechloreerde koolwaterstoffen e.d., alsmede met methyl-oligosiloxanvloeistoffen, bijv. hexamethyl-5 disilazan, octamethyl-cyclotetrasiloxan e.d. De hoeveelheid van het oplosmiddel kan variëren tussen 0 en 50 gew.%, Hexa-methyl-disiloxan verdient als oplosmiddel de meeste voorkeur.The paint paste can be diluted with various non-polar organic solvents, such as turpentine, benzene, toluene, xylene, chlorinated hydrocarbons, etc., as well as with methyl oligosiloxane liquids, eg hexamethyl-5 disilazan, octamethyl cyclotetrasiloxane, etc. The amount of the solvent can vary between 0 and 50% by weight, Hexa-methyl-disiloxane is the most preferred solvent.
De boven genoemde koud vulcaniseerbare silicone-rubberverven kunnen worden aangebracht op op de juiste wijze 10 van primer voorzien textiel, hout, glas, metaaloppervlak e.d. onder studio- en open-luchtcondities.The above mentioned cold vulcanizable silicone rubber paints can be applied to properly primed textiles, wood, glass, metal surface, etc. under studio and open air conditions.
De verftechniek is als volgt: op canvas, die onbehandeld dan wel voorbehandeld kan zijn met siliconehydrofobiserend materiaal, wordt een 15 verfpasta met daarin wit pigment (TiC^) en na te zijn verdund met hexamethyl-disiloxan aangebracht met behulp van een pasta-apparaat, waarna de laag met een katalysator wordt verknoopt.The painting technique is as follows: on canvas, which may be untreated or pretreated with silicone hydrophobizing material, a paint paste containing white pigment (TiCl 3) is applied and after being diluted with hexamethyl-disiloxane using a paste device, after which the layer is cross-linked with a catalyst.
De siliconeverven van verschillende kleur volgens de uitvinding kunnen op deze ondergrond worden aangebracht 20 waarna de laag wordt besproeid met een geschikte katalysator. Door keuze van dé katalysator kan de vulcanisatietijd binnen ruime grenzen worden gevarieerd.The silicone paints of different colors according to the invention can be applied to this substrate, after which the layer is sprayed with a suitable catalyst. By choosing the catalyst, the vulcanization time can be varied within wide limits.
Het aanbrengen van de verf kan ook plaatsvinden door inmengen van de verknopende katalysator in de verf, voor-25 afgaande aan het verven en de toepassing. De verf wordt verdund tot de gewenste consistentie tijdens schilderen.The application of the paint can also be effected by mixing the crosslinking catalyst into the paint prior to dyeing and application. The paint is thinned to the desired consistency during painting.
In dit geval wordt de verf gefixeerd ten gevolge van de werking van de verknopende katalysator. Deze laatste methode heeft het nadeel, dat de met de verknopende katalysa-30 tor vermengde verf slechts binnen de vulcanisatietijd (pot-tijd) kan worden gebruikt, hetgeen betekent dat het schilders-werk binnen een vooraf bepaalde tijd moet zijn voltooid. Deze tijd kan echter binnen ruime grenzen worden gevarieerd. Veranderingen op een dergelijk schilderij kunnen slechts door het 35 aanbrengen van een andere laag worden uitgevoerd.In this case, the paint is fixed due to the action of the cross-linking catalyst. The latter method has the drawback that the paint mixed with the crosslinking catalyst can only be used within the vulcanization time (pot time), which means that the painting work must be completed within a predetermined time. However, this time can be varied within wide limits. Changes to such a painting can only be made by applying another layer.
De êên-component-uitvoeringsvorm van de siliconeverven hebben de boven genoemde eigenschappen. Dit êên-compo-nentsysteem heeft het voordeel dat de verfpasta niet behoeft 3400625 / « * * ' - 6 - te worden gefixeerd met behulp van de verknopende katalysator. Bij het uitpersen van de verf oefent de daarin aanwezige katalysator een verknopende werking uit als resultaat van het contact met het vochtgehalte van de lucht, waarbij de eindcon-5 sistentie bereikt wordt in ca. 24 uur.The one-component embodiment of the silicone paints have the above-mentioned properties. This one-component system has the advantage that the paint paste does not need to be fixed 3400625 / * * '- 6 - using the cross-linking catalyst. When the paint is squeezed out, the catalyst contained therein exerts a cross-linking effect as a result of contact with the moisture content of the air, the final consistency being reached in about 24 hours.
Als katalysator voor het twee-componentensysteem wordt het mengsel van resp. tetraalkoxy- en alkyl-trialkoxy-silanen en dialkyl-diacyloxytin gebruikt. Een voorbeeld van deze katalysator is een mengsel van tetraethoxy-silaan en 10 dibutyl-dilauraattin.As a catalyst for the two-component system, the mixture of resp. tetraalkoxy and alkyl trialkoxy silanes and dialkyl diacyloxytin. An example of this catalyst is a mixture of tetraethoxy silane and dibutyl dilaurate tin.
Voor het ëén-componentsysteera worden methyl-tri-acetoxysilaan, methyl-trialkyl-aminosilanen e.d. gebruikt.For the one-component system, methyl triacetoxysilane, methyl trialkyl amino silanes and the like are used.
Als verdere katalysatoren worden genoemd de boorzure esters, alsmede tetraalkoxy-titaanverbindingen.Boric acid esters and tetraalkoxy-titanium compounds are mentioned as further catalysts.
15 Variant 2:15 Variant 2:
De eigenschappen van met alkyd geverniste gecombineerde met aan de lucht drogende plantaardige oliën en gemodificeerd door siliconeharstussenprodukten zijn als volgt; in chemisch opzicht is deze verf een lijnzaad-20 olie, sojaboonolie of een andere alkydhars met onverzadigde groepen erin, die gecombineerd kunnen worden door hun hydro-xygroepen door condensatie met siliconeharstussenprodukten met laag molecuulgewicht en voorzien van methoxy- of hydroxygroe-pen, bijv. Dow Corning Z-6018 of Z-6188 of Wacker SY-308 door 25 middel van de reactieve hydroxygroepen daarvan, onder oplevering van een bindmiddel van hoge stabiliteit, waterbestendigheid en daarnaast het vermogen in aanwezigheid of afwezigheid van lucht drogende siccativen te drogen.The properties of alkyd varnished combined with air drying vegetable oils and modified by silicone resin intermediates are as follows; chemically, this paint is a linseed oil, soybean oil or other alkyd resin with unsaturated groups therein, which can be combined by their hydroxy groups by condensation with low molecular weight silicone resin intermediates and provided with methoxy or hydroxy groups, e.g. Dow Corning Z-6018 or Z-6188 or Wacker SY-308 by their reactive hydroxy groups to provide a binder of high stability, water resistance and additionally the ability to dry in the presence or absence of air drying siccatives.
Bij voorkeur bevat het bindmiddel een oplosmiddel 30 met een hoog kookpunt in een hoeveelheid van 10-40 gew.%. Deze oplosmiddelen kunnen bijv. zijn petroleumether, xyleen, tetra-line, decaline e.d.Preferably, the binder contains a high boiling point solvent 30 in an amount of 10-40% by weight. These solvents can be, for example, petroleum ether, xylene, tetraline, decalin and the like.
Het pigmentmateriaal wordt in het gerede bindmiddel opgenomen overeenkomstig de bekende verfbereidingsmethoden. 35 De aldus verkregen verfpasta kan worden verdund met oplosmiddelen met hoog kookpunt. Desgewenst kan het drogen worden bevorderd onder toepassing van siccativen, bijv. Co,The pigment material is incorporated into the finished binder in accordance with known paint preparation methods. The paint paste thus obtained can be diluted with high boiling point solvents. If desired, drying can be promoted using siccatives, e.g. Co,
Mn, Zn e.d.Mn, Zn etc.
8400625 ar · - 7 -8400625 ar - - 7 -
De boven beschreven verf kan worden aangebracht op elk willekeurig oppervlak, waarop ook de traditionele olieverven kunnen worden gebruikt, bijv. textiel, hout, glas, metaal, houtvezel, houtvezelplaten bedekt met plastic e.d.The paint described above can be applied to any surface, on which traditional oil paints can also be used, e.g. textile, wood, glass, metal, wood fiber, wood fiber boards covered with plastic etc.
5 De toegepaste verfmethode correspondeert met de traditionele olieverftechnieken.5 The applied painting method corresponds to the traditional oil painting techniques.
Op het oppervlak, dat al dan niet van een verflaag bereid uit het boven genoemde bindmiddel is voorzien, kan de verf worden aangebracht. Desgewenst wordt de verf verdund 10 met een oplosmiddel met een hoog kookpunt en vervolgens in een gegeven geval gesiccateerd. De gerede verf wordt binnen één of twee dagen poederdroog.The paint can be applied to the surface, which may or may not be coated with a paint prepared from the above-mentioned binder. If desired, the paint is diluted with a high boiling point solvent and then, in a given case, siccated. The finished paint becomes powder dry within one or two days.
Variant 3; bij deze variant zijn de polysiloxanen die welke 15 aan de lucht drogen en onder afsplitsing van water condenseren en die methyl-, ^methyl-, fenyl7“ en/of ^methyl-, fenyl-, vinyl7~siloxy-eenheden bevatten, in het algemeen ^alkyl-, aryl-, alkenyl7-siloxy, en bij voorkeur trisiloxy-eenheden, welke bij drogen een vérnislaag vormen.Variant 3; in this variant, the polysiloxanes are those which air dry and condense under water splitting and which contain methyl, methyl, phenyl7 and / or methyl, phenyl, vinyl7, siloxy units, generally alkyl, aryl, alkenyl7-siloxy, and preferably trisiloxy units, which form a varnish layer upon drying.
20 Bij voorkeur dient de siliconehars oplosbaar te zijn in oplosmiddelen met een hoog kookpunt. De concentratie van vernis kan liggen tussen 20 en 70 gew.%. Geschikte oplosmiddelen zijns butylacetaat, tolueen, xyleen, tetraline, deca-line e.d.Preferably, the silicone resin should be soluble in high boiling point solvents. The concentration of varnish can be between 20 and 70% by weight. Suitable solvents are butyl acetate, toluene, xylene, tetraline, decal line and the like.
25 In de aldus verkregen vernisoplossing wordt het pigmentmateriaal volgens bekende methoden gedispergeerd. De verf kan dus zodanig zijn bereid dat deze direct geschikt is voor toepassing dan wel kan de verf door de artiest worden bereid uit het pigmentpoeder en de vernisoplossing tijdens 30 het schilderen. De schildermethode komt overeen met de traditionele aquarel- of tempertechnieken.The pigment material is dispersed according to known methods in the varnish solution thus obtained. Thus, the paint may be prepared to be directly suitable for use or the artist may prepare the paint from the pigment powder and varnish solution during painting. The painting method corresponds to the traditional watercolor or tempering techniques.
Deze variant is in het bijzonder geschikt voor het beschilderen van poreuze oppervlakken, zoals beton, kras-coating, papier, hout, gips e.d.This variant is particularly suitable for painting porous surfaces, such as concrete, scratch coating, paper, wood, plaster, etc.
35 De dispersie-aquarelverf, bereid onder toepassing van siliconevernisbindmiddel, is in het bijzonder geschikt voor het verkrijgen van schilderijen op papierbasis, alsmede voor het verkrijgen van objecten van het frescotype.The dispersion watercolor paint, prepared using silicone varnish binder, is particularly suitable for obtaining paper-based paintings, as well as obtaining fresco type objects.
8400625 • \ ο - 8 -8400625 • \ ο - 8 -
Na het aanbrengen droogt de dispersieverf lang-* zaam of snel, afhankelijk van de vluchtigheid van het oplos middel. De droogperiode kan worden gereguleerd door de keuze van het geschikte oplosmiddel..After application, the dispersion paint dries slowly or quickly, depending on the volatility of the solvent. The drying period can be controlled by selecting the appropriate solvent.
5 De voordelen van de boven genoemde verven op siliconebasis volgens varianten 1, 2 en 3 zijn als volgt: a) bij toepassing van de twee-componentenverf volgens variant 1 is de consistentie van de verfpasta constant, er vindt geen droging plaats bij blootstelling aan de lucht, 10 terwijl de consistentie niet verandert, zelfs niet bij opslag gedurende een langere periode; b) overeenkomstig de schildertechniek kan de verfpasta verdund worden met oplosmiddelen tot elke gewenste graad. Tijdens het schilderen kan het materiaal al naar gelang 15 de behoefte in dunne dan wel in dikke lagen worden aangebracht; c) bij toepassing van de verf volgens variant 1 kunnen de details van een schilderij worden gefixeerd door behandeling met de katalysator. Zoals vermeld hangt de vulcani-satietijd bij omgevingstemperatuur slechts af van de kwaliteit 20 en kwantiteit van de katalysator en kan plaatsvinden in een interval van enkele minuten tot 24 uur»The advantages of the above silicone-based paints according to variants 1, 2 and 3 are as follows: a) when using the two-component paint according to variant 1, the consistency of the paint paste is constant, no drying takes place when exposed to the air, 10 while the consistency does not change even when stored for an extended period of time; b) in accordance with the painting technique, the paint paste can be diluted with solvents to any desired degree. During painting, the material can be applied in thin or thick layers according to need; c) when using the paint according to variant 1, the details of a painting can be fixed by treatment with the catalyst. As mentioned, the vulcanization time at ambient temperature depends only on the quality and quantity of the catalyst and can take place in an interval of a few minutes to 24 hours »
De schilderijen die verkregen zijn door toepassing van siliconeverven volgens de uitvinding hebben de volgende voorkeurseigenschappen: 25 a) bestendigheid tegen chemische invloeden en beschadigingen vanuit de omgeving, bijv.o^lfl^' ^S, NH^, zuur, alsmede basische dampen en gassen, ψ b) geen beschadiging ten gevolge van waterdamp en water, 30 c) op grond van het hydrofobe oppervlak blijkt zelfs hydrofiele stof niet te hechten, hetgeen betekent dat het schilderij geen affiniteit voor vuil heeft en door wassen met water kan worden schoongemaakt, d) bestendigheid tegen fotochemische invloeden, 35 aangezien de siloxanbinding geen lichtquanta absorbeert met een golflengte groter dan 100 nm, e) de aangebrachte laag bestand is tegen warmte en kou. Het verglazingspunt verandert niet tussen -60°C en 180°C. Gebleken is, dat het materiaal bewaard kan worden bij 8^00625 - 9 - omgevingsomstandigheden (tussen -25°C en +50°C) en wel gedurende ongelimiteerde tijd voor zover de gebruikte poederverven onder deze omstandigheden niet veranderen, f) op grond van de boven genoemde eigenschappen 5 de bewaring van de artistieke voorwerpen geen speciale maatregelen vereist, zoals airconditioning e.d., g) de siliconeverf kan worden aangebracht op textiel, papier, cement, krascoating, glas, aardewerk en keramische oppervlakken, aangezien - desgewenst na geschikte voor- 10 behandeling - hechting gewaarborgd wordt. Op de gefixeerde coating kan de volgende laag gestadig worden aangebracht, waarbij de hechting wederom goed is, hetgeen betekent dat het schilderij verder kan worden ontwikkeld en gewijzigd indien dit gewenst is.The paintings obtained by the use of silicone paints according to the invention have the following preferred properties: a) resistance to chemical influences and environmental damage, eg, acid, NH, acid, as well as basic vapors and gases , ψ b) no damage due to water vapor and water, 30 c) because of the hydrophobic surface, even hydrophilic dust appears not to adhere, which means that the painting has no affinity for dirt and can be cleaned by washing with water, d ) resistance to photochemical influences, since the silicone bond does not absorb light quanta with a wavelength greater than 100 nm, e) the applied layer is resistant to heat and cold. The vitrification point does not change between -60 ° C and 180 ° C. It has been found that the material can be stored at ambient conditions (between -25 ° C and + 50 ° C) for an unlimited time, provided that the powder paints used do not change under these conditions, f) due to the abovementioned properties 5 the preservation of the artistic objects does not require any special measures, such as air conditioning, etc., g) the silicone paint can be applied on textile, paper, cement, scratch coating, glass, pottery and ceramic surfaces, since - if desired after suitable pre-treatment 10 treatment - adhesion is guaranteed. The next layer can be applied steadily to the fixed coating, the adhesion again being good, which means that the painting can be further developed and modified if desired.
15 De verfpasta's volgens de uitvinding kunnen be reid worden volgens in de verf- en vernisindustrie bekende methodes.The paint pastes according to the invention can be prepared by methods known in the paint and varnish industry.
Bereiding van de siliconeverven volgens de uitvinding.Preparation of the silicone paints according to the invention.
20 Bereiding van twee-componentenpastars volgens varianten 1 en 2sPreparation of two-component pastars according to variants 1 and 2s
De actieve en inactieve vulmaterialen alsmede de benodigde poedervormige pigmentmaterialen worden opgenomen in het gemalen materiaal, welk malen plaatsvindt in een Z-slag- 25 mesmenger of kogelmolen, zodat een volledig homogene vetachtige verfpasta wordt verkregen. De gerede verfpasta's worden overgebracht in tubes of potten.The active and inactive filler materials as well as the necessary powdered pigment materials are incorporated into the milled material, which grinding takes place in a Z-impact knife mixer or ball mill, so that a completely homogeneous fat-like paint paste is obtained. The finished paint pastes are transferred to tubes or jars.
De katalysatoren, die wat betreft hun hardings-tijd en verknopingsmechanisme van elkaar verschillen, kunnen 30 in de vorm van aerosols in flessen of druppelhouders worden gebruikt of in pasta's samen met verdikkers of kunnen de katalysatoren in tubes worden ondergebracht.The catalysts, which differ in their curing time and cross-linking mechanism, can be used in the form of aerosols in bottles or dropper containers, or in pastes together with thickeners, or can be placed in tubes.
Bereiding van êin-componentpasta's volgens variant 1ï 35 Bij de bereiding van êén-componentpasta' s wordt de geschikte katalysator gemengd met de andere component en vervolgens in tubes ondergebracht in afwezigheid van lucht in een inerte atmosfeer of onder vacuum met behulp van een ge- 8400625 * c - 10 - schikt vulapparaat.Preparation of one-component pastes according to variant 1i In the preparation of one-component pastes, the suitable catalyst is mixed with the other component and then placed in tubes in the absence of air in an inert atmosphere or under vacuum using 8400625 * c - 10 - suitable filling device.
Bereiding *van een dispersie-aquarelverf volgens variant 3:Preparation * of a dispersion watercolor paint according to variant 3:
Het gewenste verfpoeder wordt gedispergeerd in de 5 geconcentreerde oplossing van een siliconevernis in een snelle menginrichting of worden de verfpoeders, bindmiddelen en oplosmiddelen afzonderlijk gebruikt of aan de artiest verkocht in de vorm van eenheidsverpakkingen.The desired paint powder is dispersed in the concentrated solution of a silicone varnish in a rapid mixer or the paint powders, binders and solvents are used individually or sold to the artist in unit packs.
De volgende voorbeelden dienen ter nadere toe-10 lichting van de uitvoeringsvormen volgens de uitvinding. VOORBEELD IThe following examples serve to illustrate the embodiments of the invention. EXAMPLE I
Bereiding van twee-componentenverfset l.l.a. Bereiding van verfpasta zonder toevoegsel erin i 15 ComponentA (pigement + bindmiddel)Preparation of two-component paint set l.l.a. Preparation of paint paste without additive in it i 15 ComponentA (pigment + binder)
Wanneer als basis dimethyl-polysiloxan-a,ω-diol met een viskositeit van 10000 mPa.s. wordt gebruikt en wanneer gemalen pasta's met verschillende kleur worden bereid, worden de in de onderstaande tabel vermelde pigmentmaterialen opge-20 nomen.When as a basis dimethyl-polysiloxan-α, di-diol with a viscosity of 10000 mPa.s. is used and when ground pastes of different color are prepared, the pigments listed in the table below are included.
Voor het verkrijgen van een betere opname van het pigment en de siliconerubberbasis, dient het oppervlak van de pigmentpoeders te worden voorbehandeld met siliconen. Deze voorbehandeling kan worden uitgevoerd met een 10 gew. % ben-25 zeen-, tolueen of koolstoftetrachloride-oplossing van het mengsel van dimethyldichloorsilaan en methyltrichloorsilaan of met een 10 gew.% benzeenoplossing van hexamethyldisilazan.To obtain a better absorption of the pigment and the silicone rubber base, the surface of the pigment powders must be pretreated with silicone. This pretreatment can be performed with a 10 wt. 25% benzene, toluene or carbon tetrachloride solution of the mixture of dimethyldichlorosilane and methyltrichlorosilane or with a 10 wt% benzene solution of hexamethyldisilazan.
Het oppervlak dat is voorbehandeld, gedroogd en evt. gemalen pigment is opgenomen in de siliconerubberbasis 30 met behulp van een geschikte molen.The surface that has been pretreated, dried and if necessary. ground pigment is incorporated into the silicone rubber base 30 using a suitable mill.
Aan de aldus verkregen dichte massa wordt het oplosmiddel voor het verschaffen de optimale consistentie van elke verfpasta (bijv. terpentijn) toegevoegd in een geschikt apparaat, bijv. een Z^slagmesmenger. De hoeveelheid toe te 35 voegen oplosmiddel is in de onderstaande tabel aangegeven.To the dense mass thus obtained, the solvent is provided to provide the optimum consistency of each paint paste (e.g. turpentine) in a suitable device, e.g. a Z-beat mixer. The amount of solvent to be added is shown in the table below.
Het roeren wordt zolang voortgezet tot de pasta volledig homogeen is.Stirring is continued until the paste is completely homogeneous.
Voor het verkrijgen van een gemakkelijke hante- 8400625 » Jfc - 11 - ring van de aldus verkregen pasta wordt deze in tubes onder-gebraciit.To obtain an easy handling of the paste thus obtained, it is under-braced in tubes.
Component B (fixeermateriaal)Component B (fixing material)
Deze component is de katalysator die in de vorm 5 van een aerosol wordt gebruikt voor het fixeren door ver-sproeien. Als katalysator kan elk type katalysator worden gebruikt, die geschikt is voor het verknopen van twee-componen-ten-koud-vulcaniserende siliconerubbers en die een vulcanisa-tietijd van 1-10 uur waarborgt* Als katalysator wordt een 67-33 10 gew.% mengsel van tetra-ethoxysilaan en dibutyldilauraattin gebruikt (handelsmerk "Szilorka K-l").This component is the aerosol catalyst used for spray fixing. Any type of catalyst suitable for cross-linking two-component cold-vulcanizing silicone rubbers and ensuring a vulcanization time of 1-10 hours can be used as the catalyst. * As the catalyst, a 67-33 10 wt% mixture of tetraethoxysilane and dibutyl dilaurate tin (trademark "Szilorka Kl").
l.l.b. Bereiding van twee-componentenverf pasta met een smeermiddel erin (afgesloten eindigende silicone-olie met een viskositeit van 20 mPa.s.).l.l.b. Preparation of two-component paint paste with a lubricant in it (sealed ending silicone oil with a viscosity of 20 mPa.s.).
15 Component A15 Component A
Als bindmiddel wordt dimethyl-polysiloxan-α,ω-diol gebruikt.As a binder, dimethyl polysiloxane-α, ω-diol is used.
TABELTABLE
optimale hoeveelheid hoeveelheid 20 naam van het pigment gew.dl/100 smeermiddel gew.optimal amount quantity 20 name of the pigment parts by weight / 100 lubricant wt.
pigmentpoeder gew.dln rubber dl/100 gew.dln.pigment powder parts by weight of rubber parts / 100 parts by weight.
....... rubber__ 18.QQQ· mPa.s. ' cadmiumrood 125 10 titaanwit 125 12,5 25 gebrande sienna ' 125 25 ultramarijn blauw 125 25 13.000 mPa.s........ rubber__ 18.QQQ · mPa.s. 'cadmium red 125 10 titanium white 125 12.5 25 burnt sienna' 125 25 ultramarine blue 125 25 13,000 mPa.s.
titaanwit 188 10 cobaltblauw 163 10 30 cadmiumgeel 160 50 meekrap 63 12,5 ultramarijn blauw 120 14titanium white 188 10 cobalt blue 163 10 30 cadmium yellow 160 50 madder 63 12.5 ultramarine blue 120 14
De pigmenten werden niet gehydrofobiseerd. De massa werd grondig gemalen in mortier of molen en vervolgens 35 ondergebracht in tubes.The pigments were not hydrophobized. The mass was thoroughly ground in mortar or grinder and then placed in tubes.
8400625 - 12 -8400625 - 12 -
Component BComponent B
De gebruikte katalysator is dezelfde als in voorbeeld 1.1. a.The catalyst used is the same as in example 1.1. a.
1.1.c. Bereiding van twee-componenten-verfpasta's 5 met vulmaterialen erin:1.1.c. Preparation of two-component paint pastes 5 with fillers in them:
Component AComponent A
Bij de bereiding van de boven genoemde component worden de volgende bestanddelen gebruikt: 100 gew.dln. dimethyl-polysiloxaan-a,ω-diol 10 (viskoslteit: 35 tot 40000 mPa.s.) 50 gew.dln. celite (geïnactiveerd Si02) 10 gew.dln. aerosil (Degussa R 972) 32 gew.dln. cadmium oranje pigment (CdS).In the preparation of the above-mentioned component, the following ingredients are used: 100 parts by weight. dimethyl-polysiloxane-α, ω-diol 10 (viscosity: 35 to 40000 mPa.s.) 50 parts by weight. celite (inactivated SiO2) 10 parts. aerosil (Degussa R 972) 32 parts by weight. cadmium orange pigment (CdS).
Als hydrofobiseermateriaal werd een 10 % benzeen-15 oplossing van hexamethyl-disilazan gebruikt, waarbij het pigment wordt geïmpregneerd, gevolgd door drogen van de massa bij 80°C en dan vermalen.As the hydrophobizing material, a 10% benzene-15 solution of hexamethyl-disilazan was used, impregnating the pigment, then drying the mass at 80 ° C and then grinding.
Component AComponent A
Een andere variant voor de component A wordt be-20 reid uit een rubberbasis van lagere viskositeit en onder gebruikmaking van de volgende bestanddelen: 100 gew.dln. dimethyl-polysiloxan-a,ω-diol (viskositeit: 20-35.000 mPa.s.) 15 gew.dln. aerosil (Wacker HDK H-2000) 25 40 gew.dln. kwartsmeel 31 gew.dln. cadmium oranje pigment (CdS).Another variant for the component A is prepared from a rubber base of lower viscosity and using the following ingredients: 100 parts by weight. dimethyl-polysiloxane-α-di-diol (viscosity: 20-35,000 mPa.s.) 15 parts by weight. aerosil (Wacker HDK H-2000) 25 40 parts by weight. quartz flour 31 parts by weight. cadmium orange pigment (CdS).
Voor het hydrofobiseren van het pigment werd gebruik gemaakt van een 10 gew. % oplossing van het 1 : 1 molaire mengsel van dimethyldichloorsilaan en methyltrichloorsilaan in 30 koolstoftetrachloride.A 10 wt.% Was used to hydrophobize the pigment. % solution of the 1: 1 molar mixture of dimethyldichlorosilane and methyltrichlorosilane in carbon tetrachloride.
De mengsels bereid in de boven genoemde compositie, worden gehomogeniseerd in een molen. Desgewenst wordt de geschikte consistentie bereid door toevoeging van een oplosmiddel, bijv. terpentijn e.d. Na homogeniseren werd het pro-35 dukt overgebracht in tubes.The mixtures prepared in the above-mentioned composition are homogenized in a mill. If desired, the appropriate consistency is prepared by adding a solvent, eg turpentine, etc. After homogenization, the product was transferred to tubes.
Bij toepassing kan de verf op een geschikte wijze worden verdund met een oplosmiddel, bijv. terpentijn en wel op het palet.When used, the paint can be suitably diluted with a solvent, e.g. turpentine, on the palette.
8400625 - 13 -8400625 - 13 -
Component BComponent B
De katalysator die gebruikt wordt kan dezelfde zijn als in voorbeeld l.l.a.The catalyst used can be the same as in Example 1.l.a.
1.1. d. Bereiding van twee-componentenverfpasta 5 met vulmateriaal erin.1.1. d. Preparation of two-component paint paste 5 with filler material in it.
Component AComponent A
De bij de bereiding van de boven genoemde component gebruikte ingrediënten zijn als volgt:The ingredients used in the preparation of the above component are as follows:
30 gew.dln. dimethyl-polysiloxaan-α,ω-diol 10 (viskositeit: 13000 mPa.s.J30 parts by weight. dimethyl-polysiloxane-α, ω-diol 10 (viscosity: 13000 mPa.s.J
7 gew.dln. aerosil (Wacker HDK H-2000) 2 gew.dln. hexamethyldisilazan (hydrofobiserend middel) 18 gew.dln. terpentijn (oplosmiddel) 15 11 gew.dln. chroomoxide groen pigment.7 parts by weight. aerosil (Wacker HDK H-2000) 2 parts. hexamethyldisilazan (hydrophobizing agent) 18 parts. turpentine (solvent) 15 11 parts by weight. chromium oxide green pigment.
Het boven genoemde mengsel werd gehomogeniseerd onder gebruikmaking van een geschikte molen. Na homogeniseren werd het produkt overgebracht in tubes. Bij gebruik van de verf kan deze verder worden verdund door mengen met een ver-20 dunningsmiddel, bijv. terpentijn, op het palet.The above mixture was homogenized using a suitable mill. After homogenization, the product was transferred to tubes. When using the paint, it can be further diluted by mixing with a diluent, eg turpentine, on the palette.
Component BComponent B
De gebruikte katalysator kan dezelfde zijn als in voorbeeld 1.1.a.The catalyst used can be the same as in example 1.1.a.
1.2. Bereiding van een ëën-componentverfpasta: 25 De pasta's volgens voorbeelden l.l.a., l.l.b., 1.1.c. en l.l.d. kunnen eveneens in de vorm van een êên-com-ponent worden gebruikt, namelijk door gebruik te maken van niet-zure katalysatoren onder uitsluiting van vocht uit de lucht. Geschikte niet-zure katalysatoren zijn boorzure esters, 30 tetraalkoxy-titaanderivaten, silylaminen e.d.1.2. Preparation of one-component paint paste: The pastes according to Examples 1.1.a., 1.1.b., 1.1.c. and l.l.d. can also be used in the form of a single component, namely by using non-acidic catalysts with the exclusion of moisture from the air. Suitable non-acidic catalysts are boric acid esters, tetraalkoxy-titanium derivatives, silylamines and the like.
Een geschikte ëén-componentverfpasta werd bereid uit de volgende bestanddelen: 98 gew.dln. verfpasta met chroomoxide groen pigment erin, volgens voorbeeld l.l.d., 35 2 gew.dln. boorzuurtriisopropylester (kataly sator) .A suitable one-component paint paste was prepared from the following ingredients: 98 parts by weight. paint paste with chromium oxide green pigment in it, according to example 1.l.d., 35 2 parts. boric triisopropyl ester (catalyst).
In een gesloten homogeniseerinrichting, voorzien van een roerder werd de absoluut droge verfpasta en katalysator onder stikstofgas gehomogeniseerd en vervolgens in tubes 8400625 ^ 1 "Vi - 14 - overgebracht met behulp van een vulapparaat, dat op de inrichting is aangesloten.In a closed homogenizer equipped with a stirrer, the absolutely dry paint paste and catalyst were homogenized under nitrogen gas and then transferred into tubes 8400625 ^ 1 "Vi-14 - using a filling device connected to the device.
Er dient voorzichtigheid in acht te worden genomen bij gebruikmaking van de één-componentverf in verband met 5 het beginnen van de verknoping van de verf onder invloed van het watergehalte van de lucht,, afhankelijk van de hoeveelheid % *Caution should be exercised when using the one-component paint in connection with the initiation of the cross-linking of the paint under the influence of the water content of the air, depending on the amount of% *
en kwaliteit van de katalysator. Dit betekent dus dat de toepassing van êên-componentpasta’s in de tijd beperkt is. VOORBEELD IIand quality of the catalyst. This therefore means that the application of one-component pastes is limited in time. EXAMPLE II
10 Bereiding van verven uit alkydvernissen gecombi neerd met aan de lucht drogende plantaardige oliën en gemodificeerd door siliconeharstussenprodukten volgens variant 2.Preparation of paints from alkyd varnishes combined with air drying vegetable oils and modified by silicone resin intermediates according to variant 2.
2.1. Bindmiddel bereid met sojaboonvetzuur:2.1. Binder prepared with soybean fatty acid:
Voor de bereiding van het boven genoemde bindmid-15 del werd gebruik gemaakt van de volgende bestanddelen; 19,2 vol.dln. Dow Corning Z-6018-tussenprodukt 7,5 vol.dln. pentaerythritol (mono) 1,4 vol.dln. glycerol 9,8 vol.dln. ftaalzuuranhydride 20 26,7 vol.dln. sojaboonvetzuur 35,4 vol.dln. xyleen.The following ingredients were used for the preparation of the above binder; 19.2 parts by volume. Dow Corning Z-6018 intermediate 7.5 parts by volume. pentaerythritol (mono) 1.4 parts by volume. glycerol 9.8 parts by volume. phthalic anhydride 20 26.7 parts by volume. soybean fatty acid 35.4 parts by volume. xylene.
De alkydhars werd bereid volgens bekende methoden en vervolgens gekookt met een Z-60l8-tussenprodukt bij een temperatuur van 165-170°C in een apparaat, dat was voorzien 25 van een Markusson-inrichting, totdat alles was opgelost.The alkyd resin was prepared according to known methods and then cooked with a Z-6018 intermediate at a temperature of 165-170 ° C in an apparatus equipped with a Markusson device until everything was dissolved.
2.2. Dow Corning El-3044-copolymeer: siliconegehalte 30 % (Z-6018 of Wacker SY- .308) ftaalzuuranhydride 16,1 % 30 sojaboonolie 43,8 % hydroxygehalte in de hars; 2,2 % oplosmiddel; petroleumether, xyleen of tetraline.2.2. Dow Corning El-3044 copolymer: silicone content 30% (Z-6018 or Wacker SY-.308) phthalic anhydride 16.1% soybean oil 43.8% hydroxy content in the resin; 2.2% solvent; petroleum ether, xylene or tetraline.
Het extractgehalte wordt bij voorkeur ingesteld op 60-80 %.The extract content is preferably set at 60-80%.
35 2.3. Dow Corning El-3046-copolymeer: Z-6018 of SY-308-gehalte 25 % ftaalzuuranhydride 17,4 % lijnzaadolie 43,6 % oplosmiddel; petroleumether, xyleen of tetraline.35 2.3. Dow Corning El-3046 copolymer: Z-6018 or SY-308 content 25% phthalic anhydride 17.4% linseed oil 43.6% solvent; petroleum ether, xylene or tetraline.
8400625 - 15 -8400625 - 15 -
Het extractgehalte wordt bij voorkeur ingesteld op 60-90 %.The extract content is preferably set at 60-90%.
2.4. Het volgende preparaat werd bereid in een 1 liter-rondbodemkolf, voorzien van een Markusson-inrichting, 5 koeler, gasinlaatbuis en thermometer. Hierbij werd gebruik gemaakt van de volgende bestanddelenί A 200,0 g sojaboonvetzuur B 73,5 g ftaalzuuranhydride C 56,2 g pentaerythrite 10 D 12,0 g glycerol (87 %) E 43,4 g xyleen F 98,5 g xyleen G 143,8 g SY-308-siliconetussenprodukt H 167,5 g xyleen.2.4. The following preparation was prepared in a 1 liter round bottom flask equipped with a Markusson apparatus, cooler, gas inlet tube and thermometer. Use was made of the following constituents A 200.0 g soybean fatty acid B 73.5 g phthalic anhydride C 56.2 g pentaerythrite 10 D 12.0 g glycerol (87%) E 43.4 g xylene F 98.5 g xylene G 143.8 g of SY-308 silicone intermediate H 167.5 g of xylene.
15 De componenten A,B, C, D en E werden overge bracht in een kolf. De temperatuur werd geleidelijk opgevoerd tot 220-230°C. Het tijdens de reactie verkregen water werd via azeotrope destillatie verwijderd. Door regeling van de hoeveelheid xyleen dat met het water werd afgedestilleerd, 20 werd de temperatuur van de kolfinhoud onder continu koken tot terugvloeiing op 220-230°C gehouden.Components A, B, C, D and E were transferred to a flask. The temperature was gradually raised to 220-230 ° C. The water obtained during the reaction was removed via azeotropic distillation. By controlling the amount of xylene distilled with the water, the temperature of the flask contents was maintained at 220-230 ° C under continuous boiling until reflux.
Elke 30 minuten werden er monsters getrokken, teneinde de zuurwaarde te bepalen. De alkydcomponent is per-fekt wanneer de zuurwaarde onder 10 ligt. Dan werd het mengsel 25 afgekoeld tot 13Q-140°C, waarna het xyleen F werd toegevoegd. Onder verder afkoelen werd het siliconetus'senprodukt G toegevoegd bij een temperatuur van 80-100°C. Het mengsel werd vervolgens verhit tot 160°C, waarbij de condensatie van het tus-senprodukt en het alkydpolymeer plaatsvond. Het gevormde water 30 werd verwijderd via azeotrope destillatie.Samples were taken every 30 minutes to determine the acid value. The alkyd component is perfect when the acid value is below 10. Then the mixture was cooled to 140-140 ° C, after which the xylene F was added. With further cooling, the silicone fetus product G was added at a temperature of 80-100 ° C. The mixture was then heated to 160 ° C, the condensation of the intermediate and the alkyd polymer taking place. The water formed was removed via azeotropic distillation.
Tijdens de reactie werd de co-condensatie gevolgd door het nemen van druppelmonsters. Wanneer een druppelmonster op een glasplaat bij een temperatuur van 150-l60°C transparant is wordt de reactie als voltooid beschouwd.During the reaction, the co-condensation was followed by droplet samples. When a drop sample on a glass plate at a temperature of 150-160 ° C is transparent, the reaction is considered complete.
35 De co-condensatie vindt plaats in ca. 1 uur.35 The co-condensation takes place in approx. 1 hour.
Na beëindiging van de reactie werd het systeem afgekoeld en met xyleen H verdund. De reactie werd bij voor-* , keur uitgevoerd in een C02- of stikstofatmosfeer. Het extract- 8400625 - 16 - gehalte van het verkregen produkt ligt tussen 60 en 70 %.After the completion of the reaction, the system was cooled and diluted with xylene H. The reaction was preferably conducted in a CO2 or nitrogen atmosphere. The extract 8400625-16 content of the product obtained is between 60 and 70%.
Aan de alkydhars, bereid volgens voorbeelden 2.1., 2.2. en 2.3., meer in het bijzonder volgens voorbeeld 2.4., bereid onder toepassing van sojaboonolie en Z-6018 of Wacker 5 SY-308 werden de volgende poederverven toegevoegd (de hoeveelheid ervan is betrokken op 100 g hars): 112.0 g titaanwit (Tii^) 125.0 g ijzeroxide rood 33.0 g chroomoxide groen 10 100,0 g cadmium rood 125.0 g cadmium geel 125.0 g Thenard's blauw 125.0 g Berlijn blauw 125.0 g cobaltblauw 15 33,0 g krap 33.0 g acetyleenzwart 100.0 g nikkeltitaangeel 66.0 g ultramarijn blauw 114.0 g gebrande sienna.To the alkyd resin prepared according to examples 2.1., 2.2. and 2.3., more particularly according to example 2.4., prepared using soybean oil and Z-6018 or Wacker 5 SY-308, the following powder paints were added (the amount is based on 100 g resin): 112.0 g titanium white (Tii ^) 125.0 g iron oxide red 33.0 g chromium oxide green 10 100.0 g cadmium red 125.0 g cadmium yellow 125.0 g Thenard's blue 125.0 g Berlin blue 125.0 g cobalt blue 15 33.0 g tight 33.0 g acetylene black 100.0 g nickel titanium yellow 66.0 g ultramarine blue 114.0 g burnt sienna.
20 Bij het schilderen wordt het canvas bij voorkeur voorzien van een laag van titaanwit.When painting the canvas is preferably provided with a layer of titanium white.
De verf kan desgewenst worden verdund met tetra-line of decaline of worden gesiccateerd met cobalt of mangaan-houdende materialen. De hoeveelheid siccatieven bedraagt bij 25 voorkeur 0,00001-0,01 %.The paint can optionally be diluted with tetraline or decalin or siccated with cobalt or manganese-containing materials. The amount of siccatives is preferably 0.00001-0.01%.
VOORBEELD I'IIEXAMPLE I'II
Bereiding van aan de lucht drogende verven, verkregen uit alkyl-alkenyl-aryl-polysiloxanhars:Preparation of air drying paints obtained from alkyl-alkenyl-aryl-polysiloxane resin:
Als bindmiddelen kunnen de volgende commerciëel 30 beschikbare harsen worden genoemd, zonder beperking van de omvang van de bescherming van deze materialen:As binders, the following commercially available resins can be mentioned, without limiting the scope of protection of these materials:
Wacker Silikonharz MKWacker Silikonharz MK
Wacker Silikonharz-Lösung RF6Wacker Silikonharz-Lösung RF6
Wacker Silikonharz H 44.Wacker Silikonharz H 44.
35 3.1. Bereiding van een dispersieverfbindmiddel:35 3.1. Preparation of a dispersion paint binder:
Er werden 5000 g methyltrichloorsilaan en 6250 g fenyltrichloorsilaan opgelost in 80 1 butylacetaat, waarna het mengsel werd toegevoegd aan een mengsel van 200 1 water 8400625 - 17 - en 147 1 butylacetaat onder koelen gedurende 3,5-4 uur. Het roeren werd gedurende nog eens 0,5-1 uur voortgezet, waarna het mengsel vier keer werd gewassen telkens met 200 liter water tot zuurvrij, terwijl het water na roeren en elke keer 5 wassen na 2 uur bewaren werd afgezonderd. De afgezonderde butylacetaatharsoplossing werd azeotroop gedroogd bij 110-125°C. Dan werd de oplossing ingedampt tot 60-70 % van het originele volume bij 450-650 Hg mm en 115-120°C. Na indamping werd het residu opgelost in xyleen onder oplevering van een 10 60 % oplossing.5000 g of methyltrichlorosilane and 6250 g of phenyltrichlorosilane were dissolved in 80 l of butyl acetate, after which the mixture was added to a mixture of 200 l of water 8400625-17 and 147 l of butyl acetate under cooling for 3.5-4 hours. Stirring was continued for an additional 0.5-1 hour, after which the mixture was washed four times with 200 liters of water until acid-free, while the water was separated after stirring and each time after washing for 2 hours. The separated butyl acetate resin solution was azeotropically dried at 110-125 ° C. Then the solution was evaporated to 60-70% of the original volume at 450-650 Hg mm and 115-120 ° C. After evaporation, the residue was dissolved in xylene to yield a 60% solution.
Voor de bereiding van dispersieverven bleek het boven genoemde methyl-fenylvernis het geschiktst te zijn.The above-mentioned methyl phenyl varnish was found to be the most suitable for the preparation of dispersion paints.
3.2. Aan.de xyleenoplossing van de in 3.1. beschreven methyl-fenylsiliconehars werd pigment (titaanwit, 15 ijzeroxide wit, chroomoxide groen, cadmiumrood, Thenards’s blauw, Berlijns blauw, cobaltblauw, krap, gebrande sienna e.d.) bijgemengd tot er een dichte pasta werd verkregen, die desgewenst met xyleen werd verdund en op een bepaald oppervlak werd aangebracht (papier, hout, gips, cement, enz.).3.2. To the xylene solution of the in 3.1. described methyl phenyl silicone resin, pigment (titanium white, iron oxide white, chromium oxide green, cadmium red, Thenards's blue, Berlin blue, cobalt blue, tight, burnt sienna, etc.) was mixed until a dense paste was obtained, which was optionally diluted with xylene and placed on a certain surface was applied (paper, wood, plaster, cement, etc.).
20 Desgewenst kan de gerede verf worden gevernist met behulp van een kleurloze vernisoplossing.If desired, the finished paint can be varnished using a colorless varnish solution.
3.3. Er werd geschilderd met de 30 % oplossing van de vernisoplossing, zoals beschreven onder 3.1. van verf-tabletten volgens de techniek, die overeenkwam met die van 25 waterverf. Het voordeel is dat na drogen de verf niet met water kan worden afgewassen.3.3. The 30% solution of the varnish solution was painted as described under 3.1. of paint tablets according to the technique, which corresponded to that of watercolor. The advantage is that after drying the paint cannot be washed off with water.
3.4. Er werden 100 ml 30 % oplossing van Wacker MK, RF-6 of H 44 én het siliconevernis volgens 3.1., 30-40 g poedervormige kleurstof gedispergeerd en vervolgens overge- 30 bracht en bewaard in verfpotten met wijde hals. Bij het schilderen wordt de dispersieverf geroerd of geschud, terwijl het verven wordt uitgevoerd onder gebruikmaking van een penseel.3.4. 100 ml 30% solution of Wacker MK, RF-6 or H 44 and the silicone varnish according to 3.1., 30-40 g of powdered dye were dispersed and then transferred and stored in wide-necked paint pots. In painting, the dispersion paint is stirred or shaken, while dyeing is performed using a brush.
35 840062535 8400625
Claims (16)