NL8101505A - Converting sludge-like materials into sievable prods. - by mixing with moisture binding agent with pozzolan properties, esp. fly-ash - Google Patents

Converting sludge-like materials into sievable prods. - by mixing with moisture binding agent with pozzolan properties, esp. fly-ash Download PDF

Info

Publication number
NL8101505A
NL8101505A NL8101505A NL8101505A NL8101505A NL 8101505 A NL8101505 A NL 8101505A NL 8101505 A NL8101505 A NL 8101505A NL 8101505 A NL8101505 A NL 8101505A NL 8101505 A NL8101505 A NL 8101505A
Authority
NL
Netherlands
Prior art keywords
moisture
compound
composition
bound
mixing
Prior art date
Application number
NL8101505A
Other languages
Dutch (nl)
Original Assignee
Pelt & Hooykaas
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pelt & Hooykaas filed Critical Pelt & Hooykaas
Priority to NL8101505A priority Critical patent/NL8101505A/en
Publication of NL8101505A publication Critical patent/NL8101505A/en

Abstract

Conversion of a moisture-contg. esp. sludge-like material into a workable compsn. comprises mixing the material with a cpd. having pozzolan properties, in such an amt. that all the moisture in the material is bound by the cpd., with the proviso that the amt. of water to be bound is not more than 30 wt.% w.r.t. the wt. of the cpd., esp. 15-25 wt.% and partic. ca. 20%. The material with pozzolan properties is esp. fly ash (I). Process uses cheap materials such as (I) and gives a sievable prod. rather than a solid material as in previous processes, so that the prod. can be sieved to recover useful materials such as metal particles.

Description

« V«V

815Ó33/vdV/kd815Ó33 / vdV / kd

Korte aanduiding: Werkwijze voor het ontzetten van een vochthouden- de samenstelling in een verwerkbare samenstelling.Short designation: Method for removing a moisture-containing composition in a processable composition.

De uitvinding, heeft betrekking op een werkwijze voor het omzetten van een vochthoudende samenstelling, in het bijzonder slibachtige samenstelling, in een verwerkbare samenstelling door toevoegen van een vochtbindend middel.The invention relates to a method for converting a moisture-containing composition, in particular a sludge-like composition, into a processable composition by adding a moisture-binding agent.

5 Bij verschillende werkwijzen komen moeilijk verwerkbare vochthoudende samenstellingen, in het bijzonder slibachtige samenstellingen vrij. Vooral wanneer in deze slibachtige samenstellingen waardevolle produkten aanwezig zijn zoals metaaldeeltjes, is het zeer moeilijk om deze terug te winnen. Men kan weliswaar de fijne-10 re delen van het slibachtige materiaal uitwassen, waarbij dan de waardevolle bestanddelen achterblijven, maar een dergelijke wasbewerking brengt met zich mee dat de andere bestanddelen van de samenstelling in het waswater terecht komen en meestal in de omgeving waar zij ongewenst zijn vooral wanneer in de samenstelling schade— 15 lijke stoffen aanwezig zijn, zoals bijvoorbeeld zware metalen.Various processes release difficult-to-process moisture-containing compositions, in particular sludge-like compositions. Especially when valuable products such as metal particles are present in these sludge-like compositions, it is very difficult to recover them. Although the fine parts of the sludge-like material can be washed out, leaving the valuable components behind, such a washing operation entails that the other components of the composition end up in the washing water and usually in the environment where they are undesired. especially when harmful substances are present in the composition, such as, for example, heavy metals.

Het binden van het vocht met behulp van hydraulische bindmiddelen zoals cement is niet mogelijk daar dit leidt tot vorming van vaste massa's die niet verwerkbaar zijn door afzeven. Anderzijds zijn andere droogmiddelen voor dit doel te duur.The binding of the moisture using hydraulic binders such as cement is not possible, as this leads to the formation of solid masses that cannot be processed by sieving. On the other hand, other drying agents are too expensive for this purpose.

20 De uitvinding beoogt nu een werkwijze van het bovengenoem de type te verschaffen waarbij deze nadelen niet optreden door het gebruik van een goedkoop gemakkelijk beschikbaar droogmiddel.The invention now aims at providing a method of the above-mentioned type in which these drawbacks do not arise through the use of an inexpensive readily available desiccant.

Dit oogmerk wordt volgens de uitvinding bereikt doordat men de vochthoudende samenstelling mengt met een verbinding met puz-25 zolane eigenschappen in een zodanige hoeveelheid dat alle in de samenstelling door de genoemde verbinding te binden vocht door deze verbinding gebonden wordt, doch de door de verbinding gebonden hoeveelheid vocht niet meer bedraagt dan 30$ berekend op het cpwicht van de verbinding.This object is achieved according to the invention in that the moisture-containing composition is mixed with a compound with puz-zolane properties in such an amount that all the moisture to be bound in the composition by said compound is bound by this compound, but the compound bound by the compound amount of moisture does not exceed $ 30 based on the weight of the compound.

BAD ORIGINALBAD ORIGINAL

81015 0 5 - 2 -81015 0 5 - 2 -

« V«V

Door mengen van een vochthoudende samenstelling met een verbinding met puzzolane eigenschappen onder aanhouden van de genoemde voorwaarden, kan het vocht afgebonden worden onder vorming van een verwerkbare samenstelling, die zeer gemakkelijk verwerk-5 baar is.By mixing a moisture-containing composition with a compound with pozzolanic properties under the conditions mentioned, the moisture can be bound off to form a workable composition which is very easy to process.

Bovendien kan men op deze wijze de op grote schaal bij verbrandingsprocessen vrijkomende hoeveelheden verbindingen met pussolane eigenschappen (vliegas) doelmatig verwerken.Moreover, it is possible in this way to efficiently process the amounts of compounds with pussolane properties (fly ash) released during combustion processes on a large scale.

Als men werkt met een aan de verbinding met puzzolane 10 eigenschappen gebonden hoeveelheid vocht van meer dan 30/£, gaat de verbinding met puzzolaaneigenschappen tezamen met het vocht over in een vloeiende massa die zich niet gemakkelijk laat verwerken.When working with an amount of moisture bound to the compound with pozzolanic properties of more than 30%, the compound with pozzolanic properties, together with the moisture, turns into a flowing mass which is not easy to process.

Wanneer men er echter voor zorgt dat na het mengen de hoeveelheid vocht die gebonden is aan de verbinding met puzzolaaneigenschappen niet boven 30J& stijgt, voorkomt men dat de verbinding met puzzolaan 13 eigenschappen tezamen met het vocht overgaat in een vloeiende massa en derhalve een samenstelling ontstaat die gemakkelijk verwerkt kan worden, bijvoorbeeld door zeven. Tijdens het zeven kunnen waar-devolle bestanddelen uit dergelijke samenstellingen teruggewonnen kunnen worden, in het bijzonder geldt dit voor metaaldeeltjes wel-20 ke voorkomen in dergelijke vochthoudende of slibachtige samenstellingen.However, if one ensures that after mixing, the amount of moisture bound to the compound with pozzolanic properties does not rise above 30J, the compound with pozzolanic 13 properties is prevented from merging into a fluid mass together with the moisture and thus results in a composition which can be easily processed, for example by sieving. During sieving valuable components can be recovered from such compositions, in particular this applies to metal particles which occur in such moisture-containing or sludge-like compositions.

Doelmatig bedraagt de hoeveelheid vocht die aan de verbinding met puzzolaaneigenschappen gebonden is na mengen 15 tot 25%, bij voorkeur ongeveer 20 gew.%.Advantageously, the amount of moisture bound to the pozzolanic compound after mixing is 15 to 25%, preferably about 20% by weight.

25 Opgemerkt wordt dat de na het mengen verkregen samenstel ling op zichzelf meer dan 30^ vocht kan bevattend, doch dit meerdere vocht is dan zodanig aan andere bestanddelen gebonden dat het niet gebonden kan worden door de verbinding met puzzolane eigenschappen.It is noted that the composition obtained after mixing can contain more than 30% moisture per se, but this more moisture is then bound to other ingredients such that it cannot be bound by the compound having pozzolanic properties.

De verbinding met puzzolaaneigenschappen is doelmatig 30 vliegas.The connection with pozzolan properties is effective fly ash.

Om in een vochthoudende samenstelling aanwezicf waardevolle BAD ORIGINAL ATo provide valuable BAD ORIGINAL A in a moisture-containing composition

8101 5 0 58101 5 0 5

« '.VV

- 3 - bestanddelen terug te winnen, zoals metaaldeeltjes onderwerpt men de na mengen met de verbinding met puzzolaaneigenschappen verkregen samenstelling aan een zeefbewerking waardoor men waardevolle bestanddelen in deeltjes vorm gemakkélijk terug kan winnen.To recover components, such as metal particles, the composition obtained after mixing with the compound with pozzolanic properties is subjected to a sieving process, whereby valuable components in particulate form can be easily recovered.

In het voorgaande zijn de percentages gegeven als gewichts-percentages.In the foregoing, the percentages are given as weight percentages.

De uitvinding zal nu worden toegelicht aan de hand van een uitvoeringsvoorbeeld.The invention will now be elucidated on the basis of an exemplary embodiment.

VOORBEELD IEXAMPLE I

100 kg vliegas voegt men onder roeren toe aan een haven-slib tot in de uiteindelijk samenstelling 20 gew.% vocht berekend ten opzichte van het vliegas aan het vliegas gebonden is. Het vochtgehalte van de gehele samenstelling bedraagt 3Q% maar 1Q% vocht wordt zodanig vastgehouden dat het niet gebonden kan worden aan het vliegas.100 kg of fly ash are added with stirring to a harbor sludge until in the final composition 20% by weight of moisture, calculated relative to the fly ash, is bound to the fly ash. The moisture content of the entire composition is 3Q%, but 1Q% moisture is retained in such a way that it cannot be bound to the fly ash.

Bij een goede menging verkrijgt men een rulle massa die ge-makkelijk gezeefd kan worden en verder verwerkt door bijvoorbeeld omzetten in voorwerpen door bakken.When mixed well, a free-flowing mass is obtained which can be easily sieved and further processed by, for example, converting into articles by baking.

Eenzelfde bewerking waarbij men echter het aan het vliegas gebonden yochtgehalte in de uiteindelijke samenstelling laat stijgen tot 35 gew.%, geeft een vloeiende massa die niet verwerkbaar is.The same operation, however, in which the yocht content bound to the fly ash is increased to 35% by weight in the final composition, gives a flowing mass which cannot be processed.

VOORBEELD IIEXAMPLE II

Aan een slibachtige samenstelling met fijne koperdeeltjes, wordt 100 kg vliegas toggevoegd onder zorgvuldig mengen, zodanig dat in de uiteindelijke samenstelling 20 gew.% vocht aan het vliegas gebonden is.To a sludge-like composition with fine copper particles, 100 kg of fly ash is added with careful mixing, such that in the final composition 20% by weight of moisture is bound to the fly ash.

Men verkrijgt een rulle massa met een totaal vochtgehalte van 25% die gemakkelijk gezeefd kan worden, waarbij de koperdeeltjes op de zeef achterblijven.A free-flowing mass with a total moisture content of 25% is obtained which is easy to sieve, leaving the copper particles on the sieve.

VOORBEELD IIIEXAMPLE III

BAD ORIGINAL Men herhaalt voorbeeld II waarbij zich echter in de uitein- 81015 05BAD ORIGINAL Example II is repeated, but in the end 81015 05

« V«V

- 4 - delijke samenstelling 15 gew.$ vocht aan het vliegas gebonden is.- 4 - composition 15% wt. Moisture is bound to the fly ash.

Men verkrijgt ook weer een rulle massa met een totaal vochtgehalte van 20$ die zich goed laat zeven voor het terugwinnen van waarde-volle metaaldeeltjes in de vorm van koperdeeltjes.A free-flowing mass with a total moisture content of 20% is again obtained, which is easy to sieve for the recovery of valuable metal particles in the form of copper particles.

5 VOORBEELD IVEXAMPLE IV

Men mengt een ijzerertsdeeltjes bevattende pasta-achtige massa met een hoeveelheid vliegas waarbij in de gerede rulle massa 25$ vocht dan het vliegas gebonden is. De verkregen rulle massa laat zich goed verwerken en bevat in totaal 32$ vocht.An iron ore-containing paste-like mass is mixed with an amount of fly ash, the moisture being bound in the finished free-flowing mass, then the fly ash. The free-flowing mass obtained is easy to process and contains a total of $ 32 in moisture.

BAD ORIGINALBAD ORIGINAL

81015 0581015 05

Claims (6)

1. Werkwijze voor het omzetten von een vochthoudende, in het bijzonder slibachtige, somenstelling in een verwerkbare samenstelling door toevoegen van een vochtbindend middel, met het kenmerk, dat men de vochthoudende samenstelling mengt met een verbinding 5 met puzzolane eigenschappen in een zodanige hoeveelheid, dat alle in de samenstelling door de genoemde verbinding te binden vocht door deze verbinding gebonden wordt, doch de door verbinding gebonden hoeveelheid vocht niet meer bedraagt dan 30% berekend op het gewicht van de verbinding*Method for converting a moisture-containing, in particular sludge-like, composition into a processable composition by adding a moisture-binding agent, characterized in that the moisture-containing composition is mixed with a compound 5 with pozzolanic properties in such an amount that all moisture to be bound in the composition by said compound is bound by this compound, but the amount of moisture bound by compound does not exceed 30% by weight of the compound * 2. Werkwijze volgens conclusie 1, met het kenmerk, dat na het mengen de hoeveelheid vocht die gebonden is ten opzichte van de genoemde verbinding met puzzolaaneigenschappen 15 tot 25% bedraagt.Method according to claim 1, characterized in that after mixing the amount of moisture bound to said compound with pozzolanic properties is 15 to 25%. 3. Werkwijze volgens conclusie 1 of 2, met het kenmerk, dat -.....— na het mengen de hoeveelheid vocht die gebonden is ten opzichte van 15de genoemde verbinding met puzzolaaneigenschappen ongeveer 2Q£ bedraagt.3. Process according to claim 1 or 2, characterized in that - after mixing - the amount of moisture bound with respect to said compound with pozzolanic properties is approximately 20%. 4. Werkwijze volgens een of meer der voorgaande conclusies, met het kenmerk, dat de verbinding met puzzolaaneigenschappen vliegas is.Method according to one or more of the preceding claims, characterized in that the compound with pozzolanic properties is fly ash. 5. Werkwijze volgens een of meer der voorgaande conclusies, met het kenmerk, dat men uit de samenstelling afzeefbare bestanddelen terugwint door zeven van de na mengen verkregen samenstelling.Process according to one or more of the preceding claims, characterized in that sievable components can be recovered from the composition by sieving the composition obtained after mixing. 6. Werkwijze volgens conclusie 5, met het kenmerk, dat men na het mengen van de samenstelling met de verbinding met puzzolaan-25 eigenschappen metaaldeeltjes terugwint, in het bijzonder door afzeven. BAD ORIGINAL 81015 056. Process according to claim 5, characterized in that after mixing the composition with the compound with pozzolan properties, metal particles are recovered, in particular by sieving. BAD ORIGINAL 81015 05
NL8101505A 1981-03-26 1981-03-26 Converting sludge-like materials into sievable prods. - by mixing with moisture binding agent with pozzolan properties, esp. fly-ash NL8101505A (en)