NL8005128A - Artificial brick or stone wall covering strips - made from a mixt. of cement, sand, glass fibre, resin binder and pigment - Google Patents

Artificial brick or stone wall covering strips - made from a mixt. of cement, sand, glass fibre, resin binder and pigment Download PDF

Info

Publication number
NL8005128A
NL8005128A NL8005128A NL8005128A NL8005128A NL 8005128 A NL8005128 A NL 8005128A NL 8005128 A NL8005128 A NL 8005128A NL 8005128 A NL8005128 A NL 8005128A NL 8005128 A NL8005128 A NL 8005128A
Authority
NL
Netherlands
Prior art keywords
cement
binder
coating strip
reinforcement material
parts
Prior art date
Application number
NL8005128A
Other languages
Dutch (nl)
Original Assignee
Ordelman August Albert
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ordelman August Albert filed Critical Ordelman August Albert
Priority to NL8005128A priority Critical patent/NL8005128A/en
Publication of NL8005128A publication Critical patent/NL8005128A/en

Abstract

Coating strips for walls, ceilings, floors, etc., are made from a mixt. of cement, fine sand, opt. cement pigments and a fibrous or granular reinforcing material, bonded together with a synthetic resin binder. Suitable reinforcing materials are e.g. glass fibres, glass mat, stone gravel, wood fibres or wood pulp. The binder is pref. an acrylic adhesive. The dry components are mixed with the liq. binder to form a paste which is spread onto a non-adhesive substrate to give parts of the required thickness and dimensions, and allowed to harden. Used esp. in the prodn. of decorative articifical brick coverings for walls, ceilings and floors. The materials are cheaper and easier to make than real brick and stone coverings for walls etc., and can be made in a wide variety of shapes, dimensions and colours without a baking stage.

Description

* - ι - ί —* - ι - ί -

Bekledingsstrip, alsmede werkwijze voor het vervaardigen daarvan.Coating strip, as well as method for manufacturing it.

De uitvinding heeft betrekking op een bekledingsstrip voor muren, daken, vloeren, enz.The invention relates to a covering strip for walls, roofs, floors, etc.

Het is bekend om kale muren te voorzien van zgn. bekledingsstrips, die naar buiten toe een "baksteen"-5 configuratie hebben, waardoor de muur wordt verlevendigd en verfraaid. Het verdient de voorkeur, dat dergelijke zgn. steenstrips zijn vervaardigd uit natuurlijke minerale materialen, maar dit heeft het nadeel, dat de afzonderlijke strips relatief dik zijn, en daardoor minder gemakkelijk 10 aan te brengen, terwijl de vervaardiging ervan door middel van bakken enz. relatief duur is, en de consequentie heeft, dat de verkregen produkten relatief kwetsbaar zijn.It is known to provide bare walls with so-called cladding strips, which have an outwardly "brick" -5 configuration, which enlivens and embellishes the wall. It is preferable that such so-called brick slips are made of natural mineral materials, but this has the drawback that the individual strips are relatively thick, and therefore less easy to apply, while their manufacture is by means of baking etc. is relatively expensive, and has the consequence that the products obtained are relatively fragile.

Een andere oplossing is het gebruik van dunne kunststoflagen, maar dit laatste heeft het bezwaar, dat 15 een aldus beklede muur een onnatuurlijke aanblik biedt.Another solution is the use of thin plastic layers, but the latter has the drawback that a wall thus coated offers an unnatural appearance.

Het is nu het doel van de uitvinding bekledingsstrips, zoals steenstrips, alsmede een werkwijze voor de vervaardiging daarvan, te verschaffen, die de bovengenoemde nadelen niet vertoont, en waarbij hoofdzakelijk 20 uit minerale bestanddelen opgebouwde strips kunnen worden vervaardigd in elke gewenste dikte en afmeting.It is now the object of the invention to provide coating strips, such as brick slips, as well as a method of manufacturing them, which does not show the above-mentioned drawbacks, and which strips of mainly mineral constituents can be manufactured in any desired thickness and size.

Daartoe heeft de uitvinding het kenmerk, dat de strip is samengesteld uit een mengsel van cement en fijn zand, al dan niet onder toevoeging van een cement-25 pigment, en samen met een vezelig of korrelig wapenings-materiaal, welke materialen zijn gebonden door een kunststofbindmiddel.To this end, the invention is characterized in that the strip is composed of a mixture of cement and fine sand, with or without the addition of a cement-pigment, and together with a fibrous or granular reinforcement material, which materials are bonded by a plastic binder.

Volgens de uitvinding gaat men in principe uit van minerale grondstoffen, aangezien deze het meest 30 geschikt zijn voor het geven van een gewenst natuurlijk uiterlijk aan de strips. Evenwel is bij het binden van de materialen afgezien van het gebruikelijke bakprocëdê, maar maakt men in plaats daarvan gebruik van een geschikt kunststofbindmiddel, terwijl een geschikt wapenings-35 materiaal zorgt, dat een goede samenhang gewaarborgd blijft.According to the invention, in principle, mineral raw materials are used, since these are most suitable for giving the strips a desired natural appearance. However, in the bonding of the materials, the usual baking process is dispensed with, but a suitable plastic binder is used instead, while a suitable reinforcement material ensures that good cohesion is guaranteed.

Het vervaardigen van dergelijke strips kan op 8005128 ν' «. ** - 2 - eenvoudige wijze geschieden door de samenstellende vaste materialen innig te vermengen met een in vloeibare vorm verterend kunststofbindmiddel, tot een pasta, die kan worden uitgestreken op een glad niet-hechtend oppervlak 5 tot een strip van de gewenste dikte en afmeting, welke men vervolgens laat drogen. Het grote voordeel is, dat men op uiterst eenvoudige wijze strips van elke gewenste dikte, formaat, struktuur, kleur enz., al naar gelang de gewenste toepassing, kan vervaardigen.The manufacture of such strips can be done at 8005128. ** - 2 - Simply done by intimately mixing the constituent solid materials with a liquid-digesting plastic binder into a paste that can be spread on a smooth non-adhesive surface 5 to a strip of the desired thickness and size, which is then allowed to dry. The great advantage is that strips of any desired thickness, size, structure, color, etc. can be manufactured in an extremely simple manner, depending on the desired application.

10 Voor het vervaardigen van relatief dunne steen strips met een betrekkelijk fijne struktuur kan daarbij het wapeningsmiddel doelmatig bestaan uit fijngemalen glasvezel. Voor een grotere sterkte of voor zeer dunne strips kan de wapening ook worden gevormd door glasvezelmat.For the manufacture of relatively thin stone strips with a relatively fine structure, the reinforcing agent can expediently consist of finely ground glass fiber. For greater strength or for very thin strips, the reinforcement can also be formed by glass fiber mat.

15 Bij het vervaardigen van dikkere steenstrips, die een wat ruwer uiterlijk moeten bezitten, is het doelmatig gebleken om het materiaal te wapenen met steengrint.In the manufacture of thicker stone strips, which must have a somewhat rougher appearance, it has proved effective to reinforce the material with stone gravel.

Met behulp van bovengenoemde materialen kan men alle soorten steenstrips vervaardigen, maar ook bijv.All kinds of brick slips can be manufactured using the above materials, but also e.g.

20 plafondtegels, dakplaten, en diverse soorten wandbekleding.20 ceiling tiles, roof plates, and various types of wall coverings.

Men kan evenwel in plaats van glas of glasvezel, ook als bindmiddel gebruik maken van houtvezel of houtpulp. Indien dit in voldoende hoeveelheid aan het minerale mengsel wordt toegevoegd, kan men strips krijgen, die 25 het uiterlijk van houtplaten bezitten, die kunnen worden gebruikt, bijv. voor vloerbelegging. Op deze wijze is het mogelijk om op relatief goedkope wijze een vloer te maken, die het uiterlijk heeft van een parketvloer.However, instead of glass or glass fiber, it is also possible to use wood fiber or wood pulp as a binder. When added in sufficient quantity to the mineral mixture, strips can be obtained which have the appearance of wood panels which can be used, eg for floor covering. In this way it is possible to make a floor in a relatively inexpensive manner, which has the appearance of a parquet floor.

Als gevolg van het feit, dat het kunststofmiddel 30 vloeibaar door en door met het minerale mengsel wordt gemengd, zijn de verkregen strips goed water-afdichtend, zodat zij te gebruiken zijn voor vochtwerende afdekkingen.Due to the fact that the plastic agent 30 is thoroughly mixed with the mineral mixture, the strips obtained are well water-sealing, so that they can be used for moisture-resistant covers.

Zo kunnen bijv. dakplaten worden vervaardigd, al dan niet van een extra isolatie in de vorm van bijv. polystyreen-35 schuim.For example, roofing sheets can be manufactured, with or without additional insulation in the form of, for example, polystyrene-35 foam.

Hoewel bij de uitvinding elk kunststofbindmiddel, dat vloeibaar kan worden gemengd met de minerale bestanddelen, en dat na opdrogen voldoende bindkracht, c.q. vernetting geeft, is gebleken, dat in het bijzonder acrylaatbasislijmen 40 goed voldoen. Onder acrylaatbasislijmen worden die lijmen 80 05 1 28 V* · - ^ - 3 - bedoeld, waarvan acrylaat of acrylzuur het uitgangspunt vormt. Voorbeelden zijn polyacrylzuur en polymethacrylzuur, acrylonitril, en ABS.Although in the invention any plastic binder, which can be mixed in liquid form with the mineral constituents, and which, after drying, provides sufficient binding force or cross-linking, it has been found that in particular acrylic base adhesives 40 are satisfactory. Acrylic base adhesives are those adhesives 80 05 1 28 V * · - ^ - 3 - of which acrylic or acrylic acid is the starting point. Examples are polyacrylic acid and polymethacrylic acid, acrylonitrile, and ABS.

In het onderstaande is een voorbeeld gegeven 5 van de bereiding van steenstrip. Daarbij zijn alle delen volumedelen.An example of the preparation of brick slips is given below. In addition, all parts are volume parts.

VOORBEELDEXAMPLE

Men mengde 5 delen fijn gemalen grijze cement met 3 delen fijn zilverzand. Aan dit mengsel werden 3/4 delen 10 fijngemalen glasvezel toegevoegd tot een zo homogeen mogelijk mengsel.5 parts of finely ground gray cement were mixed with 3 parts of fine silver sand. 3/4 parts of 10 finely ground glass fiber were added to this mixture to make the mixture as homogeneous as possible.

De verkregen samenstelling werd innig gemengd met 3-3,5 delen acrylaatlijm, waardoor een pasta werd verkregen, waaraan men vervolgens een niet-alkalisch aan-15 tastende rode kleurpigment (cementpigment) toevoegde, totdat deze pasta de bruin-rode kleur van steen had verkregen.The resulting composition was intimately mixed with 3-3.5 parts of acrylic adhesive to yield a paste, to which a non-alkaline affecting red color pigment (cement pigment) was then added until this paste had the brown-red color of stone. obtained.

Dit mengsel werd vervolgens uitgestreken op een glasplaat tot een laag van 2 mm dik, die men verdeelde in een gewenst formaat voor steenstrip. Na drogen konden 20 de verkregen steenstrips zonder moeite van de glasplaat worden verwijderd, en boden deze het natuurlijke uiterlijk van baksteen. De verkregen strips konden met een geschikte lijmsoort (bijv. acrylaatlijm) gemakkelijk worden bevestigd op een te bekleden muur.This mixture was then spread on a glass plate to a layer of 2 mm thick, which was divided into a desired size for brick slips. After drying, the resulting brick slips could be effortlessly removed from the glass plate, providing the natural appearance of brick. The strips obtained could be easily attached to a wall to be coated with a suitable type of glue (e.g. acrylic glue).

25 Hoewel de uitvinding in het bovenstaande is beschreven en toegelicht aan de hand van ëén voorbeeld, zal het duidelijk zijn, dat er tal van verdere mogelijkheden bestaan, die alle liggen binnen het kader van de uitvinding.Although the invention has been described above and illustrated by means of one example, it will be apparent that there are numerous further possibilities, all of which lie within the scope of the invention.

Zo is het bijv. mogelijk om het samenstellende 30 mengsel uit te breiden met een brandwerend vulmiddel, waardoor brandwerende platen kunnen worden verkregen in alle maten en diktes.For example, it is possible to expand the constituent mixture with a fire-resistant filler, so that fire-resistant plates can be obtained in all sizes and thicknesses.

Bovendien is het mogelijk om in plaats van platen of strips ook ronde vormen te maken, bijv. sierlijsten, goten, dakranden enz. Het een en ander zal de vakman na 35 kennisname van het bovenstaande duidelijk zijn.In addition, it is possible to make round shapes instead of plates or strips, eg decorative frames, gutters, eaves, etc. All this will be clear to the skilled person after having knowledge of the above.

-conclusies - 80 0 5 1 28conclusions - 80 0 5 1 28

Claims (8)

1. Bekledingsstrip voormuren, daken, vloeren enz., met het kenmerk, dat de strip is samengesteld uit een mengsel van cement en fijn zand, al dan niet onder toevoeging van een cementpigment, en samen met 5 een vezelig of korrelig wapeningsmateriaal, welke materialen zijn gebonden door een kunststofbindmiddel.Coating strip for walls, roofs, floors, etc., characterized in that the strip is composed of a mixture of cement and fine sand, with or without the addition of a cement pigment, and together with a fibrous or granular reinforcement material, which materials are bound by a plastic binder. 2. Bekledingsstrip volgens conclusie 1, m e t het kenmerk, dat het wapeningsmateriaal fijn gemalen glasvezel is.2. Coating strip according to claim 1, characterized in that the reinforcement material is finely ground glass fiber. 3. Bekledingsstrip volgens conclusie 1, m e t het kenmerk, dat het wapeningsmateriaal glasvezel- mat is. 'Coating strip according to claim 1, characterized in that the reinforcement material is glass fiber mat. ' 4. Bekledingsstrip volgens conclusie 1, m e t het kenmerk, dat het wapeningsmateriaal bestaat 15 uit fijn steengrint.Coating strip according to claim 1, characterized in that the reinforcement material consists of fine stone gravel. 5. Bekledingsstrip volgens conclusie 1, m e t het kenmerk, dat het wapeningsmateriaal bestaat uit houtvezel of houtpulp.Coating strip according to claim 1, characterized in that the reinforcement material consists of wood fiber or wood pulp. 6. Bekledingsstrip volgens êën der conclusies 1-5, 20 met het kenmerk, dat het bindmiddel een lijm- op-acrylaatbasis is.Coating strip according to any one of claims 1 to 5, 20, characterized in that the binder is a glue-on-acrylic base. 7. Werkwijze voor het vervaardigen van een bekledingsstrip volgens êën der voorgaande conclusies, met het kenmerk, dat men de samenstellende vaste materialen 25 en het in vloeibare vorm verkerende bindmiddel innig vermengd tot een pasta, die men uitstrijkt op een glad, niet hechtend oppervlak tot een strip van gewenste dikte en afmeting, die men vervolgens laat drogen.7. A method of manufacturing a coating strip according to any one of the preceding claims, characterized in that the constituent solid materials and the binder in liquid form are intimately mixed into a paste, which is spread on a smooth, non-adhesive surface to a strip of desired thickness and size, which is then allowed to dry. 8. Werkwijze volgens conclusie 7, m e t het 30 kenmerk, dat men 5 delen witte of grijze cement maalt en innig vermengt met 3 delen fijn zilverzand, 8005128 - 5 - " ' 0,75 delen glasvezel, 3-3,5 delen vloeibare acrylaatlijm, en een aangepaste hoeveelheid cementpigment tot een uit-strijkbare pasta. 80 0 5 1 288. Process according to claim 7, characterized in that 5 parts of white or gray cement are ground and intimately mixed with 3 parts of fine silver sand, 8005128-5.5 parts of glass fiber, 3-3.5 parts of liquid acrylic glue. , and an appropriate amount of cement pigment to a spreadable paste 80 0 5 1 28
NL8005128A 1980-09-11 1980-09-11 Artificial brick or stone wall covering strips - made from a mixt. of cement, sand, glass fibre, resin binder and pigment NL8005128A (en)