NL2032426B1 - Steel composition for expandable tubular products, expandable tubular article having this steel composition, manufacturing method thereof and use thereof - Google Patents
Steel composition for expandable tubular products, expandable tubular article having this steel composition, manufacturing method thereof and use thereof Download PDFInfo
- Publication number
- NL2032426B1 NL2032426B1 NL2032426A NL2032426A NL2032426B1 NL 2032426 B1 NL2032426 B1 NL 2032426B1 NL 2032426 A NL2032426 A NL 2032426A NL 2032426 A NL2032426 A NL 2032426A NL 2032426 B1 NL2032426 B1 NL 2032426B1
- Authority
- NL
- Netherlands
- Prior art keywords
- steel composition
- composition according
- expandable tubular
- expandable
- tubular
- Prior art date
Links
- 239000000203 mixture Substances 0.000 title claims abstract description 47
- 229910000831 Steel Inorganic materials 0.000 title claims abstract description 44
- 239000010959 steel Substances 0.000 title claims abstract description 44
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 13
- 239000012535 impurity Substances 0.000 claims abstract description 10
- 238000000034 method Methods 0.000 claims abstract description 7
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims abstract description 5
- 229910000734 martensite Inorganic materials 0.000 claims description 18
- 229910001563 bainite Inorganic materials 0.000 claims description 13
- 238000005496 tempering Methods 0.000 claims description 12
- 229910000859 α-Fe Inorganic materials 0.000 claims description 11
- 229910052719 titanium Inorganic materials 0.000 claims description 8
- 229910001562 pearlite Inorganic materials 0.000 claims description 7
- 238000009863 impact test Methods 0.000 claims description 5
- 238000010791 quenching Methods 0.000 claims description 4
- 230000000171 quenching effect Effects 0.000 claims description 4
- 229910052799 carbon Inorganic materials 0.000 abstract description 6
- 239000000047 product Substances 0.000 description 27
- PXHVJJICTQNCMI-UHFFFAOYSA-N nickel Substances [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 22
- 239000010955 niobium Substances 0.000 description 22
- 239000010936 titanium Substances 0.000 description 16
- 239000011651 chromium Substances 0.000 description 15
- 239000011572 manganese Substances 0.000 description 11
- 229910001566 austenite Inorganic materials 0.000 description 9
- 238000001816 cooling Methods 0.000 description 9
- 239000010949 copper Substances 0.000 description 9
- 229910052758 niobium Inorganic materials 0.000 description 9
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 8
- 229910052750 molybdenum Inorganic materials 0.000 description 8
- 229910052759 nickel Inorganic materials 0.000 description 8
- 239000003921 oil Substances 0.000 description 8
- 229910052720 vanadium Inorganic materials 0.000 description 8
- 239000007789 gas Substances 0.000 description 7
- 230000001965 increasing effect Effects 0.000 description 7
- 229910052804 chromium Inorganic materials 0.000 description 6
- 238000005098 hot rolling Methods 0.000 description 6
- 230000015572 biosynthetic process Effects 0.000 description 5
- 238000005755 formation reaction Methods 0.000 description 5
- 150000004767 nitrides Chemical class 0.000 description 5
- 229910052757 nitrogen Inorganic materials 0.000 description 5
- 230000008569 process Effects 0.000 description 5
- 238000012360 testing method Methods 0.000 description 5
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 4
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 description 4
- 230000000052 comparative effect Effects 0.000 description 4
- 239000011733 molybdenum Substances 0.000 description 4
- 230000009466 transformation Effects 0.000 description 4
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 description 4
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 3
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 3
- 238000005275 alloying Methods 0.000 description 3
- 229910052796 boron Inorganic materials 0.000 description 3
- 229910052802 copper Inorganic materials 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 239000012530 fluid Substances 0.000 description 3
- 150000001247 metal acetylides Chemical class 0.000 description 3
- 238000001556 precipitation Methods 0.000 description 3
- 238000007670 refining Methods 0.000 description 3
- 238000005204 segregation Methods 0.000 description 3
- 238000002791 soaking Methods 0.000 description 3
- 239000007787 solid Substances 0.000 description 3
- 238000009628 steelmaking Methods 0.000 description 3
- 239000000126 substance Substances 0.000 description 3
- ZOXJGFHDIHLPTG-UHFFFAOYSA-N Boron Chemical compound [B] ZOXJGFHDIHLPTG-UHFFFAOYSA-N 0.000 description 2
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 2
- 229910001209 Low-carbon steel Inorganic materials 0.000 description 2
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 description 2
- 239000005864 Sulphur Substances 0.000 description 2
- 239000004411 aluminium Substances 0.000 description 2
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 2
- 229910052782 aluminium Inorganic materials 0.000 description 2
- 238000005266 casting Methods 0.000 description 2
- 238000010622 cold drawing Methods 0.000 description 2
- 239000012467 final product Substances 0.000 description 2
- BHEPBYXIRTUNPN-UHFFFAOYSA-N hydridophosphorus(.) (triplet) Chemical compound [PH] BHEPBYXIRTUNPN-UHFFFAOYSA-N 0.000 description 2
- 239000000314 lubricant Substances 0.000 description 2
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium atom Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 description 2
- 238000010899 nucleation Methods 0.000 description 2
- 230000006911 nucleation Effects 0.000 description 2
- 230000008092 positive effect Effects 0.000 description 2
- 230000001737 promoting effect Effects 0.000 description 2
- 230000035945 sensitivity Effects 0.000 description 2
- 229910052710 silicon Inorganic materials 0.000 description 2
- 238000005482 strain hardening Methods 0.000 description 2
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 1
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 description 1
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 1
- UCKMPCXJQFINFW-UHFFFAOYSA-N Sulphide Chemical compound [S-2] UCKMPCXJQFINFW-UHFFFAOYSA-N 0.000 description 1
- 230000002411 adverse Effects 0.000 description 1
- 230000003679 aging effect Effects 0.000 description 1
- 229910045601 alloy Inorganic materials 0.000 description 1
- 239000000956 alloy Substances 0.000 description 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- 230000008901 benefit Effects 0.000 description 1
- 239000004568 cement Substances 0.000 description 1
- 238000005097 cold rolling Methods 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 230000001010 compromised effect Effects 0.000 description 1
- 230000007423 decrease Effects 0.000 description 1
- 238000013461 design Methods 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 239000006185 dispersion Substances 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 238000002474 experimental method Methods 0.000 description 1
- 239000001257 hydrogen Substances 0.000 description 1
- 229910052739 hydrogen Inorganic materials 0.000 description 1
- 229910052742 iron Inorganic materials 0.000 description 1
- 229910052748 manganese Inorganic materials 0.000 description 1
- 239000000463 material Substances 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 239000003129 oil well Substances 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 238000004881 precipitation hardening Methods 0.000 description 1
- 238000002360 preparation method Methods 0.000 description 1
- 238000001953 recrystallisation Methods 0.000 description 1
- 230000009467 reduction Effects 0.000 description 1
- 238000003303 reheating Methods 0.000 description 1
- 238000007789 sealing Methods 0.000 description 1
- 150000004760 silicates Chemical class 0.000 description 1
- 239000010703 silicon Substances 0.000 description 1
- 239000007921 spray Substances 0.000 description 1
- 239000003381 stabilizer Substances 0.000 description 1
- 230000035882 stress Effects 0.000 description 1
- 238000009849 vacuum degassing Methods 0.000 description 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 1
- 238000003466 welding Methods 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/10—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of tubular bodies
- C21D8/105—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of tubular bodies of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/009—Pearlite
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/20—Ferrous alloys, e.g. steel alloys containing chromium with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
Claims (18)
1. Staalssamenstelling voor expandeerbare buisvormige producten, omvattende, in massa%, GC: 0,03 - 0,12; Mn: 05-15; Si: >0and 0,5; Cr: 0,1-1,0; Mo: 01-1,0; Ni >Oands 1,0; V: 0-0,20; Nb: 0-0,10; IJzer (Fe) en onvermijdelijke onzuiverheden onder de voorwaarde dat V+Nb20,01.
2. Staalsamenstelling volgens conclusie 1, verder omvattende Ti: 0-0,10; Al: 0-0,10.
3. Staalsamenstelling volgens conclusie 1 of conclusie 2, waarin Pr = 90, waarin Pr = 485 V + 130 Mo + 4In(Mo) + 18In(Cr) + 12In(Si) + 67; en/of Al/1,9 + Ti/3,4 + Nb/6,6 + V/3,6 = N.
4. Staalsamenstelling volgens een van de voorgaande conclusies, waarin de onvermijdelijke onzuiverheden omvatten Cu: 0-1,0; B: 0-0,010; N: 0 - 0,030; P: 0 - 0,030; S: 0 - 0,030.
5. Staalsamenstelling volgens een van de voorgaande conclusies, waarin C: 0,05 - 0,10; Mn: 0,7-1,2; Si: 0,1-0,5; Ni: 0,1-0,7; Cr: 0,2-0,9;
Mo: 02-07; V: 0,02 - 0,12; Nb: 0,01 - 0,06; Ti: 0-0,05; Al 0-0,05; N: 0-0,015.
6. Staalsamenstelling volgens een van de voorgaande conclusies, waarin C: 0,06 - 0,09; Mn: 08-11; Si: 0,1-0,3; Ni: 0,2 - 0,7, bij voorkeur 0,3 - 0,6 Cr: 04-08; Mo: 0,25- 0,60; V: 0,03 - 0,08; Nb: 0,02 - 0,04; Ti: 0-0,04; Al: 0-0,04; N: 0 - 0,008.
7. Staalsamenstelling volgens een van de voorgaande conclusies, waarin V + Nb 2 0,02, bij voorkeur V + Nb = 0,05.
8. Staalsamenstelling volgens een van de voorgaande conclusies, waarin B: 0 - 0,0050; bij voorkeur O - 0,0030.
9. Staalsamenstelling volgens een van de voorgaande conclusies, waari P: 0 - 0,020, bij voorkeur O - 0,015; S: 0 - 0,020, bij voorkeur O - 0,015.
10. Staalsamenstelling volgens een van de voorgaande conclusies 3-9, waarin: P+ 2 100, bij voorkeur Pr = 110.
11. Staalsamenstelling volgens een van de voorgaande conclusies 3-10, waarin: Paz 20, bij voorkeur Py = 24, meer bij voorkeur Py 2 27, waarin Pu = f* [C + Ni/41 + Cu/35 + Si/21 + Mn/16 + Cr/12 + Mo/10 +V/8] *100, waarin als B <0,0010;f=1, anders f= 3,5.
12. Werkwijze voor het vervaardigen van een uitzetbaar buisvormig voorwerp, omvattende de stappen van: a) het leveren van een buisvormig onderdeel; b) het austenitiseren van de buisvormige component bij een temperatuur in het bereik van Ac3-1000 °C; c) het afschrikken van de geaustenitiseerde buisvormige component uit stap b); d) het temperen van de afgeschrikte buisvormige component uit stap Cc); waarbij de buisvormige component een samenstelling heeft volgens een van de voorgaande conclusies 1-11.
13 Uitzetbaar buisvormig voorwerp met een samenstelling volgens een van de voorgaande conclusies 1-11.
14. Uitzetbaar buisvormig voorwerp volgens conclusie 13, vervaardigd volgens de werkwijze zoals gedefinieerd in conclusie 12.
15. Uitzetbaar buisvormig voorwerp volgens conclusie 13 met een microstructuur omvattende: som van martensiet en bainiet: 2 90 vol.%; ferriet en/of perliet: < 10%.
16. Voorwerp volgens een van de voorgaande conclusies 13-15 met ten minste een van de eigenschappen gekozen uit de groep bestaande uit: Vloeigrens (YS): = 620 MPa (90 ksi), bij voorkeur = 689 MPa (100 ksi); Totale rek: = 18%, bij voorkeur = 20%; Charpy slagtest: geabsorbeerde energie bij -20 °C: = 80 J, bij voorkeur 2 100 J; Laterale expansie: = 1,8 mm, bij voorkeur 2 2,0 mm; Afschuifoppervlak: = 85%, bij voorkeur 100% taai tot -40 °C, bij voorkeur tot -60 °C, meer bij voorkeur tot -80 °C.
17. Voorwerp volgens conclusie 16 met een vloeigrens (YS) van = 620 MPa (90 ksi), bij voorkeur = 689 MPa (100 ksi) en ten minste één van de andere eigenschappen vermeld in conclusie 12, bij voorkeur een Charpy slagtest: geabsorbeerde energie bij -20 °C: 2 80 J, bij voorkeur = 100 J.
18. Gebruik van een uitzetbaar voorwerp volgens een van de voorgaande conclusies 13 - 17 als een uitzetbare voering bij het opnieuw breken van een olie- of gasbron.