NL1010329C2 - Composite construction material sheet, laminated glass construction material column, and method of manufacturing such a column. - Google Patents

Composite construction material sheet, laminated glass construction material column, and method of manufacturing such a column. Download PDF

Info

Publication number
NL1010329C2
NL1010329C2 NL1010329A NL1010329A NL1010329C2 NL 1010329 C2 NL1010329 C2 NL 1010329C2 NL 1010329 A NL1010329 A NL 1010329A NL 1010329 A NL1010329 A NL 1010329A NL 1010329 C2 NL1010329 C2 NL 1010329C2
Authority
NL
Netherlands
Prior art keywords
column
glass
construction material
elements
base
Prior art date
Application number
NL1010329A
Other languages
Dutch (nl)
Inventor
Fredericus Albertus Veer
Original Assignee
Univ Delft Tech
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Univ Delft Tech filed Critical Univ Delft Tech
Priority to NL1010329A priority Critical patent/NL1010329C2/en
Priority to AU62341/99A priority patent/AU6234199A/en
Priority to PCT/NL1999/000639 priority patent/WO2000023265A2/en
Application granted granted Critical
Publication of NL1010329C2 publication Critical patent/NL1010329C2/en

Description

Plaat van composiet constructiemateriaal, kolom van gelami neerd glazen constructiemateriaal, en werkwijze voor het ver vaardigen van een dergelijke kolomComposite construction material plate, laminated glass construction material column, and method of manufacturing such a column

De uitvinding heeft betrekking op een plaat van composiet materiaal omvattende elementen van glas en een aan het glas gehechte thermoplastisch polymeer.The invention relates to a composite sheet comprising glass elements and a thermoplastic polymer adhered to the glass.

Een dergelijke plaat is bekend uit de Japanse oc-5 trooiaanvrage JP-A-92247650. Het uit deze Japanse octrooiaanvrage bekende materiaal betreft een transparant laminaat dat bruikbaar is als veiligheidsglas. Het bekende laminaat is echter niet bruikbaar voor constructiedoeleinden.Such a plate is known from Japanese patent application JP-A-92247650. The material known from this Japanese patent application relates to a transparent laminate which can be used as safety glass. However, the known laminate cannot be used for construction purposes.

Het is nu doelstelling van de uitvinding om een 10 plaat van de in de aanhef bedoelde soort te verschaffen, welke als constructiemateriaal verwerkt kan worden zonder dat daarbij vereist is om ten behoeve van de sterkte of de constructieve veiligheid metalen of andersoortige constructie-materialen toe te passen. Het constructiemateriaal volgens de 15 uitvinding leidt tot een verhoogde architectonische waarde van de met dit materiaal vervaardigde gebouwen. Tevens is het materiaal volgens de uitvinding beter geschikt voor veilig-heidsvragende toepassingen, zoals in automobielen of hogere snelheidsvoertuigen.It is now an object of the invention to provide a plate of the type referred to in the preamble, which can be processed as a construction material without this requiring the addition of metals or other construction materials for the sake of strength or structural safety. to fit. The construction material according to the invention leads to an increased architectural value of the buildings manufactured with this material. The material according to the invention is also better suited for safety-demanding applications, such as in automobiles or higher speed vehicles.

20 Volgens de uitvinding wordt het composiet construc tiemateriaal erdoor gekenmerkt, dat het glas gehard is en de plaat is samengesteld uit naastliggende en elkaar althans ten dele overlappende en onderling verlijmde elementen. De samenstelling uit afzonderlijke elementen maakt de vervaardiging 25 van relatief grote platen mogelijk, die nochtans bruikbaar zijn voor constructiedoeleinden. Het materiaal volgens de uitvinding is constructief veilig, en behoudt het vermogen om na overbelasting of beschadiging constructieve krachten op te nemen.According to the invention, the composite construction material is characterized in that the glass is hardened and the plate is composed of adjacent and at least partly overlapping and mutually glued elements. The composition of separate elements allows the manufacture of relatively large plates, which are nevertheless useful for construction purposes. The material according to the invention is structurally safe and retains the ability to absorb constructional forces after overload or damage.

30 Opgemerkt wordt dat uit US-A-4.774.143 een transpa rant gelamineerd materiaal bekend is, waarbij het materiaal een continue binnenlaag van thermoplastisch materiaal omvat, en een buitenlaag van onderling gescheiden glazen segmenten, waarbij in de ruimten tussen de naastliggende segmenten een 1010329 2 lijm wordt toegepast. Het laminaat volgens US-A-4.774.143 is bruikbaar als veiligheidsmateriaal, maar heeft geen overlappende elementen en staat geen toepassing als constructiemate-riaal toe.It is noted that US-A-4,774,143 discloses a transparent laminated material, the material comprising a continuous inner layer of thermoplastic material, and an outer layer of mutually separated glass segments, wherein in the spaces between the adjacent segments a 1010329 2 glue is applied. The laminate according to US-A-4,774,143 is useful as a safety material, but has no overlapping elements and does not allow use as a construction material.

5 Voor het verkrijgen van optimale constructie-eigen- schappen is het wenselijk dat het glas gehard is tot ten minste het dubbele van de sterkte van ongehard glas en ten hoogste 50 % van de maximale sterkte van gehard glas.To obtain optimum construction properties, it is desirable that the glass is cured to at least double the strength of unhardened glass and at most 50% of the maximum strength of tempered glass.

Architectonisch worden met de plaat volgens de uit-10 vinding de beste resultaten verkregen in de uitvoering waarin de elementen zijn verlijmd met een transparante lijm waarbij de dikte van de lijmlaag minder dan 25 μτη bedraagt. De dikte van de toe te passen lijmlaag is afhankelijk van de grootte van de onderling verlijmde elementen. Wanneer relatief kleine 15 elementen worden gebruikt, dient de lijmlaag dunner uitgevoerd te worden, bijvoorbeeld in het bereik 4-8 μτη.Architecturally, with the plate according to the invention, the best results are obtained in the embodiment in which the elements are glued with a transparent glue, the thickness of the glue layer being less than 25 μτη. The thickness of the adhesive layer to be used depends on the size of the glued elements. When relatively small elements are used, the adhesive layer should be thinner, for example in the range 4-8 μτη.

Het is voorts wenselijk dat het glas zo dun mogelijk is uitgevoerd, en bij voorkeur een dikte heeft van ten hoogste 5 % van de kleinste lengte- of breedtemaat van een ele-2 0 ment.It is further desirable that the glass is as thin as possible, and preferably has a thickness of at most 5% of the smallest length or width of an element.

De uitvinding heeft tevens betrekking op een kolom van gelamineerd glazen constructiemateriaal. Volgens de uitvinding is een dergelijke kolom erdoor gekenmerkt, dat deze voorzien is van een aan het glazen constructiemateriaal ge-25 lijmde voet, en dat het constructiemateriaal rust op in verhouding tot het constructiemateriaal zacht materiaal, met een vloeigrens in het bereik 5-30 MPa. Voor het zachte materiaal wordt bij voorkeur lood genomen. Dit biedt het voordeel dat de basis van de kolom tijdens belasting ontlast blijft, zodat 30 onregelmatigheden in de structuur van het constructiemateriaal bij belasting van de kolom geen lokale spanningsconcen-traties opleveren.The invention also relates to a column of laminated glass construction material. According to the invention, such a column is characterized in that it is provided with a base glued to the glass construction material, and that the construction material rests on soft material in relation to the construction material, with a yield point in the range 5-30 MPa . Lead is preferably used for the soft material. This offers the advantage that the base of the column remains unloaded during loading, so that irregularities in the structure of the construction material when loaded on the column do not produce local stress concentrations.

Verder is wenselijk dat in de voet van de kolom een kogelscharnier is opgenomen. Hiermee worden bij belasting van 35 de kolom buigende momenten voorkomen, tengevolge waarvan de belastbaarheid van de kolom wordt vergroot.It is further desirable that a ball joint is included in the base of the column. This prevents bending moments when the column is loaded, as a result of which the load capacity of the column is increased.

De uitvinding is voorts nog belichaamd in een werkwijze voor het vervaardigen van een dergelijke kolom. In de werkwijze volgens de uitvinding wordt de kolom gevormd door p1 0 10 3 2 9 3 twee glazen buizen in elkaar te passen, waarbij tussen de buitendiameter van de binnenbuis en de binnendiameter van de buitenbuis een ringvormige opening overblijft die wordt gevuld met een monomeer, welk monomeer vervolgens onder invloed 5 van licht wordt gepolymeriseerd waarbij een lamp vanaf de voet van de kolom naar boven wordt bewogen. Op deze wijze wordt de invloed van krimp effectief tegengegaan.The invention is further embodied in a method of manufacturing such a column. In the method according to the invention, the column is formed by fitting two glass tubes together, leaving an annular opening filled with a monomer between the outer diameter of the inner tube and the inner diameter of the outer tube, which monomer is then polymerized under the influence of light with a lamp being moved upward from the base of the column. In this way, the influence of shrinkage is effectively counteracted.

In het bijzonder wanneer één lamp wordt toegepast, is het wenselijk dat bij het naar boven bewegen van de lamp 10 gelijktijdig de kolom om haar lengteas wordt geroteerd. VOORBEELDParticularly when one lamp is used, it is desirable that when the lamp 10 is moved upwards, the column is simultaneously rotated about its longitudinal axis. EXAMPLE

Elementen van glas zijn chemisch gehard ter verkrijging van een verhoogde sterkte die ten minste het dubbele bedraagt van ongehard glas, en ten hoogste 50 % van de 15 maximale sterkte. Vervolgens is dit geharde glas verlijmd met een duetiele polymeer, in het bijzonder polycarbonaat. De toegepaste lijm is een transparante handelskwaliteit van de firma DELO uit Duitsland, en wel een blauwlicht uithardende fotokatalytische lijm op acrylaat-basis die in een dikte van 20 circa 4-8 μιη is aangebracht. Overigens zijn ook andere oplos-middelvrije en transparante lijmen toepasbaar die gecontroleerd kunnen uitharden. Hiermee is een composiet constructie-materiaal verkregen met een sterkte en E-modulus vergelijkbaar met die van gehard glas, echter met een taaiheid verge-25 lijkbaar met die van een metaal. Deze elementen zijn vervolgens samengesteld tot een grote plaat door de elementen naast en over elkaar te leggen en onderling op dezelfde als de hierboven aangegeven wijze te verlijmen. Hiermee is bereikt dat een composiet constructiemateriaal is verschaft met een 30 grote oppervlaktemaat, maar met nochtans een grote mate van integriteit van het geheel, ook bij belasting van de con-structieplaat. Bij belasting kan een enkel element bezwijken, terwijl de naastliggende en overlappende elementen onaangetast blijven.Elements of glass are chemically hardened to provide an increased strength that is at least double that of unhardened glass, and at most 50% of the maximum strength. Subsequently, this hardened glass is glued with a duetile polymer, in particular polycarbonate. The adhesive used is a transparent commercial quality from DELO from Germany, namely a blue-light-curing acrylic-based photocatalytic adhesive which is applied in a thickness of approximately 4-8 μιη. Incidentally, other solvent-free and transparent adhesives can also be used that can cure in a controlled manner. This provides a composite construction material with a strength and E-modulus comparable to that of tempered glass, but with a toughness comparable to that of a metal. These elements are then assembled into a large sheet by placing the elements next to and over each other and gluing them together in the same manner as indicated above. This achieves that a composite construction material is provided with a large surface area, but with a high degree of integrity of the whole, even under load on the construction plate. A single element can collapse under load, while the adjacent and overlapping elements remain unaffected.

35 De uitvinding zal nu nader worden toegelicht onder verwijzing naar de tekening, waarin schetsmatig in fig. 1 de kolom volgens de uitvinding in een eerste uitvoeringsvorm wordt getoond; en *1 0 103 29 4 in fig. 2 de kolom volgens de uitvinding in een tweede uitvoeringsvorm wordt getoond.The invention will now be further elucidated with reference to the drawing, in which in Fig. 1 the column according to the invention is shown in sketch in a first embodiment; and * 1 0 103 29 4 shows in Fig. 2 the column according to the invention in a second embodiment.

In fig. 1 wordt een kolom 1 van gelamineerd glazen constructiemateriaal getoond, welke is voorzien van een aan 5 het glazen constructiemateriaal van de kolom 1 gelijmde voet 2. Met verwijzingscijfer 3 is de lijmlaag aangeduid. Het constructiemateriaal van de kolom 1 rust op in verhouding tot het constructiemateriaal zacht materiaal 4, te weten lood.Fig. 1 shows a column 1 of laminated glass construction material, which is provided with a base 2 glued to the glass construction material of column 1. Reference number 3 indicates the adhesive layer. The construction material of the column 1 rests in proportion to the construction material soft material 4, namely lead.

In fig. 2 wordt een dergelijke kolom van glazen con-10 structiemateriaal getoond, waarbij de voet 2 is samengesteld uit een kop 2' van de voet, en een basis 2'' van de voet. Tussen de kop en de basis van de voet is een kogelgewricht 5 opgenomen, welke een alzijdig scharnier biedt aan de kolom l, zodat buigmomenten voorkomen worden.In Fig. 2, such a column of glass construction material is shown, the base 2 being composed of a head 2 'of the base, and a base 2' 'of the base. A ball joint 5 is provided between the head and the base of the foot, which provides an all-round hinge to the column 1, so that bending moments are prevented.

15 De uitvinding is niet beperkt tot de in het voor gaande beschreven uitvoeringsvoorbeelden. Binnen het kader van de uitvinding, zoals bepaald door de navolgende conclusies, kan op deze uitvoeringsvoorbeelden gevarieerd worden zonder dat daarbij de uitvindingsgedachte verlaten wordt.The invention is not limited to the exemplary embodiments described above. Within the scope of the invention, as defined by the following claims, these embodiments can be varied without leaving the inventive idea.

1 0 1 o 3 2 91 0 1 o 3 2 9

Claims (9)

1. Plaat van composiet constructiemateriaal omvattende elementen van glas en een aan het glas gehechte thermoplastisch polymeer, met het kenmerk, dat het glas gehard is en de plaat is samengesteld uit naastliggende en elkaar al- 5 thans ten dele overlappende en onderling verlijmde elementen.1. Composite construction material plate comprising elements of glass and a thermoplastic polymer adhered to the glass, characterized in that the glass is hardened and the plate is composed of adjoining and partly overlapping and glued elements. 2. Plaat volgens conclusie 1, met het kenmerk, dat het glas gehard is tot ten minste het dubbele van de sterkte van ongehard glas en ten hoogste 50 % van de maximale sterkte van gehard glas.Plate according to claim 1, characterized in that the glass is hardened to at least double the strength of unhardened glass and at most 50% of the maximum strength of hardened glass. 3. Plaat volgens conclusie 1 of 2, met het kenmerk, dat de elementen zijn verlijmd met een transparante lijm waarbij de dikte van de lijmlaag minder dan 25 μιη bedraagt.Plate according to claim 1 or 2, characterized in that the elements are glued with a transparent adhesive, the thickness of the adhesive layer being less than 25 µ. 4. Plaat volgens een der conclusies 1-3, met het kenmerk, dat het glas een dikte heeft van ten hoogste 5 % van 15 de kleinste lengte- of breedtemaat van een element.Plate according to any one of claims 1-3, characterized in that the glass has a thickness of at most 5% of the smallest length or width of an element. 5. Kolom van gelamineerd glazen constructiemateriaal, met het kenmerk, dat deze voorzien is van een aan het glazen constructiemateriaal gelijmde voet, en dat het constructiemateriaal rust op in verhouding tot het constructie- 20 materiaal zacht materiaal, met een vloeigrens in het bereik 5-30 MPa.5. Column of laminated glass construction material, characterized in that it is provided with a base glued to the glass construction material, and that the construction material rests on soft material in relation to the construction material, with a yield strength in the range 5- 30 MPa. 6. Kolom volgens conclusie 5, met het kenmerk, dat het zachte materiaal lood is.Column according to claim 5, characterized in that the soft material is lead. 7. Kolom volgens conclusie 5 of 6, met het kenmerk, 25 dat in de voet van de kolom een kogelscharnier is opgenomen.Column according to claim 5 or 6, characterized in that a ball joint is incorporated in the base of the column. 8. Werkwijze voor het vervaardigen van een kolom volgens conclusie 5, 6 of 7, met het kenmerk, dat deze wordt gevormd door twee glazen buizen in elkaar te passen, waarbij tussen de buitendiameter van de binnenbuis en de binnendiame- 30 ter van de buitenbuis een ringvormige opening overblijft die wordt gevuld met een monomeer, welk monomeer vervolgens onder invloed van licht wordt gepolymeriseerd waarbij een lamp vanaf de voet van de kolom naar boven wordt bewogen.8. A method of manufacturing a column according to claim 5, 6 or 7, characterized in that it is formed by fitting two glass tubes together, between the outer diameter of the inner tube and the inner diameter of the outer tube. an annular opening remains which is filled with a monomer, which monomer is then polymerized under the influence of light, with a lamp being moved upwards from the base of the column. 9. Werkwijze volgens conclusie 8, met het kenmerk, 35 dat bij het naar boven bewegen van de lamp de kolom gelijktijdig wordt geroteerd om haar lengteas. *10103299. Method according to claim 8, characterized in that when the lamp is moved upwards, the column is rotated simultaneously about its longitudinal axis. * 1010329
NL1010329A 1998-10-16 1998-10-16 Composite construction material sheet, laminated glass construction material column, and method of manufacturing such a column. NL1010329C2 (en)