NL1007444C2 - Contaminated soil containing clay is converted to building product - Google Patents

Contaminated soil containing clay is converted to building product Download PDF

Info

Publication number
NL1007444C2
NL1007444C2 NL1007444A NL1007444A NL1007444C2 NL 1007444 C2 NL1007444 C2 NL 1007444C2 NL 1007444 A NL1007444 A NL 1007444A NL 1007444 A NL1007444 A NL 1007444A NL 1007444 C2 NL1007444 C2 NL 1007444C2
Authority
NL
Netherlands
Prior art keywords
soil
binder
agglomeration agent
building material
contaminated
Prior art date
Application number
NL1007444A
Other languages
Dutch (nl)
Inventor
Karel Henquet
Original Assignee
Stevin Wegenbouw
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Stevin Wegenbouw filed Critical Stevin Wegenbouw
Priority to NL1007444A priority Critical patent/NL1007444C2/en
Application granted granted Critical
Publication of NL1007444C2 publication Critical patent/NL1007444C2/en

Abstract

A building compound is prepared by soil, that is possibly contaminated and preferably contains clay e.g. as mud or spoil, is adjusted for sand and water content and is combined with a binding or agglomeration agent. Also claimed is the use of a binding or agglomeration agent in the preparation of a building compound from contaminated soil.

Description

Werkwijze voor het vervaardigen van een bouwstof, bouwstof verkregen met die werkwijze, met die bouwstof vervaardigd produkt, toepassing van een bind- of agglomeratiemiddel, werkwijze voor de vervaardiging van een constructie.Method for manufacturing a building material, building material obtained by that method, product manufactured with that building material, use of a binding or agglomerating agent, method for manufacturing a construction.

55

Tot nu toe werd verontreinigde grond zoals bijvoorbeeld verontreinigd bagger of baggerslib beschouwd als milieugevaarlijke stof, welke gecontroleerd moesten worden gestort en opgeslagen.Until now, contaminated soil, such as contaminated dredged material or dredging sludge, has been regarded as an environmentally hazardous substance, which had to be dumped and stored in a controlled manner.

10 De uitvinding beoogt een verwerking van verontreinigde grond, bij voorkeur kleihoudende grond, zoals bijvoorbeeld bagger of baggerslib, teneinde daaraan een economisch nuttige bestemming te kunnen geven.The object of the invention is to process contaminated soil, preferably clay-containing soil, such as for instance dredging or dredging sludge, in order to be able to give it an economically useful destination.

Daartoe wordt voorgesteld, grond, bij voorkeur kleihoudende 15 grond, zoals bagger of baggerslib zodanig te behandelen, dat een grove korrelgehalte, zoals zandgehalte van ongeveer 20-40%, bij voorkeur ongeveer 30% en een watergehalte van ongeveer 15-25% wordt bereikt, en om daaraan toe te voegen een middel om de uitloging van verontreinigende stoffen daaruit te 20 beperken tot een voorafgekozen niveau. Bij voorkeur geschiedt de behandeling zodanig, dat een fijne korrelgehalte, zoals een slib- of kleigehalte van ongeveer 10-30%, bij voorkeur ongeveer 20% wordt bereikt.To this end, it is proposed to treat soil, preferably clay-containing soil, such as dredge or dredging sludge, such that a coarse grain content, such as sand content, of about 20-40%, preferably about 30% and a water content of about 15-25% is achieved. , and to add thereto a means to limit the leaching of pollutants therefrom to a preselected level. Preferably, the treatment is carried out such that a fine grain content, such as a sludge or clay content of about 10-30%, preferably about 20%, is achieved.

Aan de uitvinding ligt het inzicht ten grondslag, dat grond 25 waarvan het gehalte van één of meer verontreinigende stoffen boven een grens ligt waarboven die grond niet of niet zonder beschermende maatregelen zoals inpakken in folie gebruikt mag worden als bouwstof, door behandeling met een geschikt chemisch middel een uitloging vertoont die wezenlijk lager is 30 dan het gehalte van die ene of meer verontreinigende stoffen zou doen vermoeden, zodat de grond dan wel mag worden toegepast. Bijvoorbeeld kan daarmee de verontreinigende grond worden gebracht op een verontreinigingsniveau beneden de streefwaarden zoals bijvoorbeeld vermeld in de laatste verzie 35 van het Bouwstoffenbesluit van de Nederlandse Wet Bouwbesluit, zoals van kracht voor de prioriteitsdatum van deze octrooiaanvrage .The invention is based on the insight that soil of which the content of one or more pollutants is above a limit above which said soil may not be used as building material without protective measures such as wrapping in foil, by treatment with a suitable chemical shows a leaching which is substantially lower than the content of that one or more pollutants would suggest, so that the soil may then be used. For example, the polluting soil can hereby be brought to a contamination level below the target values, as stated, for example, in the latest version of the Building Materials Decree of the Dutch Building Act, as in force before the priority date of this patent application.

Ook beoogt de uitvinding een werkwijze waarbij grond op verontreinigingen wordt gekeurd en bij vaststelling van 1007444 - 2 - overschrijding van één of meer streefwaarden voor de verontreiniging wordt behandeld met een stof teneinde die ene of meer streefwaarden niet meer te overschrijden.It is also an object of the invention to provide a method in which soil is inspected for contaminants and, if one or more target values for the contamination are exceeded, it is treated with a substance in order to no longer exceed said one or more target values.

Een middel ter beperking van de uitloging kan zijn een 5 (chemisch) bindmiddel, maar ook een agglomeratie-middel, zoals een oppervlakte-aktieve stof, om aan de gronddeeltjes aanhechtend en/of zich in de poriën van die gronddeeltjes bevindend water irreversibel te verdrijven. Een dergelijk agglomeratie-middel is bijvoorbeeld Consolid, verkrijgbaar bij 10 de gelijknamige onderneming te Olsberg, Duitsland. Bij voorkeur bevat het agglomeratie-middel ten minste 3% organische stoffen, en daarnaast meer dan ongeveer 80% zeer fijnkorrelig cement en kalkhydraat. Bij voorkeur zorgt het bind- of agglomeratie-middel voor een aanzienlijke verlaging 15 van de wateropname-capaciteit van de aldus bewerkte grond, zoals bagger of baggerslib. Het gewenste watergehalte kan bijvoorbeeld worden bereikt door bagger of baggerslib te ontwateren (bijvoorbeeld door persen, zuigen, verhitten). Het gewenste grove korrelgehalte, zoals zandgehalte kan 20 bijvoorbeeld worden bereikt door bijmengen van zand. In plaats van zand, kan bijvoorbeeld een equivalent zoals vergruisd of gefreesd asfalt of beton worden gebruikt. Ook mengsels van bijvoorbeeld zand, vergruisd asfalt en/of beton zijn denkbaar. Het aldus verkregen mengsel kan worden ingezet voor verwerking 25 in bijvoorbeeld een wegfundering. Ook is aanwending als afdekgrond voor deponiën, en als onderdeel van ophogingen en geluidswallen en waterkerende constructies beoogd.An agent to limit the leaching can be a (chemical) binder, but also an agglomeration agent, such as a surfactant, to irreversibly expel water adhering to the soil particles and / or in the pores of those soil particles. . Such an agglomeration agent is, for example, Consolid, available from the eponymous company in Olsberg, Germany. Preferably, the agglomeration agent contains at least 3% organics, in addition more than about 80% very fine-grained cement and lime hydrate. Preferably, the binder or agglomeration agent considerably reduces the water absorption capacity of the soil worked in this way, such as dredging or dredging sludge. The desired water content can be achieved, for example, by dewatering dredging or dredging sludge (for example, by pressing, suctioning, heating). The desired coarse grain content, such as sand content, can be achieved, for example, by adding sand. For example, instead of sand, an equivalent such as crushed or milled asphalt or concrete can be used. Mixtures of, for example, sand, crushed asphalt and / or concrete are also conceivable. The mixture thus obtained can be used for processing in, for example, a road foundation. Use is also intended as a covering ground for deposits, and as part of embankments and noise barriers and water-retaining structures.

In het hiernavolgende wordt de uitvinding toegelicht aan de hand van een aantal experimenten. Hoewel de experimenten 1 en 30 2 gericht zijn op baggerslib klasse IV, zal het duidelijk zijn dat de uitvinding zich daartoe niet beperkt. Ook zal het duidelijk zijn, dat met de uitvinding een bouwstof kan worden vervaardigd uit bij voorkeur kleihoudende grond, zoals bagger of baggerslib, die niet of slechts beperkt is verontreinigd.In the following, the invention is illustrated by means of a number of experiments. Although experiments 1 and 2 are aimed at class IV dredging sludge, it will be clear that the invention is not limited thereto. It will also be clear that with the invention a building material can be manufactured from preferably clay-containing soil, such as dredge or dredging sludge, which is not or only slightly contaminated.

35 Experiment 135 Experiment 1

Van een hoeveelheid vrijkomend materiaal van het werk ten behoeve van de nieuwe sluis te Belfeld (Nederland) aan de Maas 1 007444 - 3 - werd een drietal slibmonster (klasse IV slib) getrokken, die eerst werden onderworpen aan een periode van droging ("rijping") aan de lucht, om een vochtgehalte van 16% te bereiken. Aan twee van de monsters werd vervolgens 30% zand 5 toegevoegd, alsmede het Consolidsysteem in een dosering van ongeveer 1 resp. 2 % "Solidry" en de daardoor bepaalde dosering vloeistof "C444". Vervolgens werd van alle drie monsters de initiële CBR waarde bepaald, en ook de verzadigde CBR waarde (d.w.z. de CBR waarde na onderdompeling in water 10 gedurende 28 dagen). De resultaten zijn weergegeven in Tabel 1. De verzadigde CBR waarde begroeg voor het niet met Consolid behandelde monster ong. 50% van de initiële CBR waarde. Het monster met 1% Consolid gaf een ong. 200%, het monster met 2% Consolid gaf een ong. 600% hogere verzadigde CBR waarde t.o.v. 15 de initiële CBR waarde. Het met 2% Consolid behandelde monster kan worden gekenschetst als een goed draagkrachtige grondsoort, die bruikbaar is als goed ophoogmateriaal met de kwaliteiten van een redelijk funderingsmateriaal.Three samples of sludge (class IV sludge) were taken from an amount of material released from the work for the new lock in Belfeld (the Netherlands) on the Maas 1 007444 - 3, which was first subjected to a period of drying ("maturing ") in the air, to achieve a moisture content of 16%. To two of the samples, 30% sand 5 was then added, as well as the Consolid system at a dose of about 1 resp. 2% "Solidry" and the thereby determined liquid dosage "C444". Subsequently, the initial CBR value of all three samples was determined, as well as the saturated CBR value (i.e. the CBR value after immersion in water for 28 days). The results are shown in Table 1. The saturated CBR value for the non-Consolid treated sample was approximately 50% of the initial CBR value. The sample with 1% Consolid gave an approx. 200%, the sample with 2% Consolid gave an approx. 600% higher saturated CBR value compared to the initial CBR value. The sample treated with 2% Consolid can be characterized as a good load-bearing soil type, which can be used as a good embankment material with the qualities of a reasonable foundation material.

Ondanks dat het hier gaat om klasse IV slib (het bevat o.a. 20 relatief veel zink en cadmium), is uit onderzoek conform NEN 7345 aan de beide met Consolid behandelde en voorverdichte monsters gebleken, dat de diffusie van stoffen niet de grenswaarden uit het bouwstoffenbesluit en de categorie-1 grenswaarden van het IPO-interimbeleid overschrijdt. Dit 25 ongeacht de wijze van toepassing (geïsoleerd, continu of discontinu bevochtigd).Although this concerns class IV sludge (it contains 20 relatively much zinc and cadmium), research in accordance with NEN 7345 on the two samples treated and pre-densified with Consolid has shown that the diffusion of substances does not meet the limit values from the Building Materials Decree and exceeds the category-1 limits of the IPO interim policy. This regardless of the method of application (insulated, continuously or discontinuously wetted).

Experiment 2Experiment 2

Slib van dezelfde bron als in Experiment 1 werd gedroogd tot 16% vochtgehalte en gemengd met 2% "Solidry" en de daardoor 30 bepaalde dosering vloeistof "C444". Dit proefstuk werd verdicht in een proctormal, en daarna onderworpen aan een waterdoorlatendheidstest in een zgn. DIN-test. Daarbij wordt om het monster een membraan aangebracht, waarna een waterkolom van 2 meter (0,2 bar) wordt opgebracht. Na een 35 verzadigingsperiode van 1 week werd geen vervorming van het ong. 60 mm. hoge proefstuk waargenomen. De berekende k-waarde bedroeg 2*10'8m/s. Vermoed wordt, dat het met 2% Consolid 1007444 - 4 - behandelde monster uit Experiment 1, een berekende k-waarde van ten minste 7*10"^* zal opleveren.Sludge from the same source as in Experiment 1 was dried to 16% moisture and mixed with 2% "Solidry" and the thereby dosed liquid "C444". This test piece was compacted in a proctor mold, and then subjected to a water permeability test in a so-called DIN test. A membrane is placed around the sample, after which a water column of 2 meters (0.2 bar) is applied. After a 1 week saturation period, no deformation of the approx. 60 mm. high test piece observed. The calculated k value was 2 * 10-8m / s. It is believed that the sample of Experiment 1 treated with 2% Consolid 1007444-4 will yield a calculated k value of at least 7 * 10%.

Experiment 3Experiment 3

Een stuk van de provinciale weg N361 tussen Mensingeweer en 5 Ranum (Nederland) werd gereconstrueerd door een ong. 500 mm dikke wegfundering te maken door de oude asfaltconstructie en fundering weg te frezen en dit freesproduct te mengen met klei en te stabiliseren met Consolid. Op de nieuwe fundering werd een 190 mm dikke asfaltlaag aangebracht. De nieuwe 10 wegfundering bleek een gemiddelde stijfheidsmodulus te hebben die vergelijkbaar is met puingranulaat/mengranulaat.A part of the provincial road N361 between Mensingeweer and 5 Ranum (Netherlands) was reconstructed by making an approx. 500 mm thick road foundation by milling away the old asphalt construction and foundation and mixing this milling product with clay and stabilizing it with Consolid. A 190 mm thick asphalt layer was applied to the new foundation. The new road foundation was found to have an average stiffness modulus comparable to rubble granulate / mix granulate.

10074441007444

Claims (9)

1. Werkwijze voor het vervaardigen van een bouwstof, waarbij een eventueel verontreinigde grondsoort, bij voorkeur kleihoudende grond, zoals bijvoorbeeld verontreinigd bagger of 5 baggerslib wordt verzameld, daarvan het zand- en watergehalte op een voor de bouwstof gewenst niveau wordt gebracht, en een bind- of agglomeratiemiddel wordt toegevoegd.1. A method for manufacturing a building material, in which a possibly contaminated soil type, preferably clay-containing soil, such as for instance contaminated dredging material or dredging sludge, is collected, the sand and water content of which is brought to a level desired for the building material, and a binding - or agglomeration agent is added. 2. Werkwijze volgens conclusie 1, waarbij het bind- of agglomeratie-middel het aan grondkorrels aanhangende en/of 10 zich in poriën van grondkorrels bevindend water verdrijft en/of waarbij het bind- of agglomeratie-middel verhindert, dat water aan grondkorrels kan gaan aanhangen en/of in poriën van grondkorrels kan binnendringen.2. A method according to claim 1, wherein the binder or agglomeration agent expels the water adhering to soil grains and / or pores of soil grains and / or wherein the binder or agglomeration agent prevents water from going to soil grains adhering and / or penetrating into pores of soil grains. 3. Bouwstof verkregen met de werkwijze volgens conclusie 1 of 15 2, of anders met die bouwstof vervaardigd produkt.3. Building material obtained with the method according to claim 1 or 15, or else product manufactured with said building material. 4. Werkwijze volgens conclusies 1 of 2, waarbij het bind- of agglomeratie-middel ten minste ongeveer 3% organische stoffen bevat.The method of claims 1 or 2, wherein the binder or agglomeration agent contains at least about 3% organics. 5. Werkwijze volgens conclusie 1, 2 of 4, waarbij het bind- of 20 agglomeratiemiddel meer dan ongeveer 80% zeer fijnkorrelig cement en kalkhydraat bevat.A method according to claim 1, 2 or 4, wherein the binder or agglomeration agent contains more than about 80% of very fine-grained cement and lime hydrate. 6. Werkwijze volgens conclusie 1, 2, 4 of 5, waarbij het bind-of agglomeratiemiddel uit een vaste en een vloeibare component bestaat.A method according to claim 1, 2, 4 or 5, wherein the binding or agglomerating agent consists of a solid and a liquid component. 7. Werkwijze volgens conclusie 1, 2, 4, 5 of 6, waarbij de grond zodanig verontreinigd is, dat deze zonder behandeling één of meer streefwaarden voor verontreinigende stoffen volgens het Bouwstoffenbesluit (Nederlandse Wet Bouwbesluit) overschrijdt of volgens het Bouwstoffenbesluit niet vrij 30 toepasbaar is.7. Method according to claim 1, 2, 4, 5 or 6, wherein the soil is so contaminated that without treatment it exceeds one or more target values for pollutants according to the Building Materials Decree (Dutch Building Act) or not freely applicable according to the Building Materials Decree. is. 8. Werkwijze voor het vervaardigen van een weg, afdeklaag voor een deponie, geluidwal, ophoging en dergelijke constructie waarbij een of meer grondlagen worden aangebracht, en waarbij de grond wordt vervaardigd volgens de werkwijze volgens 35 conclusie 1, 2, 4, 5, 6 of 7.8. Method for manufacturing a road, covering layer for a deposit, noise barrier, embankment and the like construction in which one or more soil layers are applied, and in which the soil is manufactured according to the method according to claim 1, 2, 4, 5, 6 or 7. 9. Toepassing van een bind- of agglomeratiemiddel bij het vervaardigen van een bouwstof uit verontreinigde grond. 10074449. Use of a binder or agglomeration agent in the manufacture of a building material from contaminated soil. 1007444
NL1007444A 1996-11-04 1997-11-04 Contaminated soil containing clay is converted to building product NL1007444C2 (en)