MX2018009236A - Lamina de acero galvanizado de alta resistencia, miembro de alta resistencia, y metodo para producir lamina de acero galvanizado de alta resistencia. - Google Patents
Lamina de acero galvanizado de alta resistencia, miembro de alta resistencia, y metodo para producir lamina de acero galvanizado de alta resistencia.Info
- Publication number
- MX2018009236A MX2018009236A MX2018009236A MX2018009236A MX2018009236A MX 2018009236 A MX2018009236 A MX 2018009236A MX 2018009236 A MX2018009236 A MX 2018009236A MX 2018009236 A MX2018009236 A MX 2018009236A MX 2018009236 A MX2018009236 A MX 2018009236A
- Authority
- MX
- Mexico
- Prior art keywords
- high strength
- steel sheet
- plated steel
- zinc plated
- production method
- Prior art date
Abstract
Se proporcionan una lámina de acero galvanizado de alta resistencia que tiene resistencia al impacto mejorada posterior al trabajo, un método para producir la lámina de acero galvanizado de alta resistencia, y un miembro de alta resistencia producido usando una lámina de acero. La lámina de acero galvanizado de alta resistencia incluye una lámina de acero que tiene una composición específica y una microestructura incluyendo ferrita y bainita sin carburo, martensita y bainita que contiene carburo, y austenita retenida, la fracción del área total de ferrita y bainita sin carburo siendo 0% a 55%, la fracción del área total de martensita y bainita que contiene carburo siendo 45% a 100%, y la fracción del área de austenita retenida siendo 0% a 5%, y una capa de galvanización dispuesta en la lámina de acero. La densidad de las brechas que cortan a través del grosor entero de la capa de galvanización en una sección transversal de la capa de galvanización que se toma en la dirección de grosor para ser perpendicular a la dirección de laminación es de 10 brechas/mm o más.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2016015358 | 2016-01-29 | ||
PCT/JP2017/002615 WO2017131054A1 (ja) | 2016-01-29 | 2017-01-26 | 高強度亜鉛めっき鋼板、高強度部材及び高強度亜鉛めっき鋼板の製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2018009236A true MX2018009236A (es) | 2018-09-03 |
Family
ID=59398395
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2018009236A MX2018009236A (es) | 2016-01-29 | 2017-01-26 | Lamina de acero galvanizado de alta resistencia, miembro de alta resistencia, y metodo para producir lamina de acero galvanizado de alta resistencia. |
Country Status (7)
Country | Link |
---|---|
US (1) | US11447852B2 (es) |
EP (1) | EP3409806B1 (es) |
JP (1) | JP6274360B2 (es) |
KR (1) | KR102148739B1 (es) |
CN (1) | CN108603264B (es) |
MX (1) | MX2018009236A (es) |
WO (1) | WO2017131054A1 (es) |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110121568B (zh) * | 2016-12-27 | 2021-02-19 | 杰富意钢铁株式会社 | 高强度镀锌钢板及其制造方法 |
KR102020412B1 (ko) | 2017-12-22 | 2019-09-10 | 주식회사 포스코 | 충돌특성 및 성형성이 고강도 강판 및 이의 제조방법 |
WO2019130713A1 (ja) * | 2017-12-27 | 2019-07-04 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP7047517B2 (ja) * | 2018-03-22 | 2022-04-05 | 日本製鉄株式会社 | 高張力鋼板用スラブの冷却方法、高張力熱延鋼板の製造方法、高張力溶融亜鉛めっき鋼板の製造方法及び高張力合金化溶融亜鉛めっき鋼板の製造方法 |
WO2019189849A1 (ja) * | 2018-03-30 | 2019-10-03 | Jfeスチール株式会社 | 高強度亜鉛めっき鋼板、高強度部材およびそれらの製造方法 |
CN113614256B (zh) * | 2019-04-11 | 2023-03-21 | 日本制铁株式会社 | 钢板及其制造方法 |
CN110184537B (zh) * | 2019-05-24 | 2020-10-30 | 武汉钢铁有限公司 | 一种低碳含钴高强度桥索钢及生产方法 |
Family Cites Families (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH1013081A (ja) | 1996-06-26 | 1998-01-16 | Nkk Corp | マイクロ波吸収材 |
JPH10130801A (ja) * | 1996-10-25 | 1998-05-19 | Sumitomo Metal Ind Ltd | 表面品質に優れた溶融めっき鋼板の製造方法 |
JP3525812B2 (ja) | 1999-07-02 | 2004-05-10 | 住友金属工業株式会社 | 衝撃エネルギー吸収性に優れた高強度鋼板およびその製造方法 |
DE10023312C1 (de) | 2000-05-15 | 2001-08-23 | Thyssenkrupp Stahl Ag | Galvannealed-Feinblech und Verfahren zum Herstellen von derartigem Feinblech |
KR100700473B1 (ko) | 2003-01-15 | 2007-03-28 | 신닛뽄세이테쯔 카부시키카이샤 | 고강도 용융 아연 도금 강판 및 그 제조 방법 |
CN102639739B (zh) * | 2009-11-30 | 2014-09-10 | 新日铁住金株式会社 | 耐氢脆化特性优异的最大拉伸强度为900MPa以上的高强度钢板及其制造方法 |
JP5432802B2 (ja) * | 2010-03-31 | 2014-03-05 | 株式会社神戸製鋼所 | 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板 |
JP5136609B2 (ja) | 2010-07-29 | 2013-02-06 | Jfeスチール株式会社 | 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
KR101597473B1 (ko) * | 2011-07-29 | 2016-02-24 | 신닛테츠스미킨 카부시키카이샤 | 굽힘성이 우수한 고강도 아연 도금 강판 및 그 제조 방법 |
MX2014001118A (es) * | 2011-07-29 | 2014-02-27 | Nippon Steel & Sumitomo Metal Corp | Capa de revestimiento de zinc por inmersion en caliente aleada, lamina de acero que tiene la misma y metodo para producir la misma. |
JP6314520B2 (ja) * | 2014-02-13 | 2018-04-25 | 新日鐵住金株式会社 | 引張最大強度1300MPa以上を有する成形性に優れた高強度鋼板、高強度溶融亜鉛めっき鋼板、及び、高強度合金化溶融亜鉛めっき鋼板とそれらの製造方法 |
US10113223B2 (en) | 2014-11-05 | 2018-10-30 | Nippon Steel & Sumitomo Metal Corporation | Hot-dip galvanized steel sheet |
-
2017
- 2017-01-26 KR KR1020187021607A patent/KR102148739B1/ko active IP Right Grant
- 2017-01-26 EP EP17744284.5A patent/EP3409806B1/en active Active
- 2017-01-26 MX MX2018009236A patent/MX2018009236A/es unknown
- 2017-01-26 US US16/072,904 patent/US11447852B2/en active Active
- 2017-01-26 JP JP2017525421A patent/JP6274360B2/ja active Active
- 2017-01-26 WO PCT/JP2017/002615 patent/WO2017131054A1/ja active Application Filing
- 2017-01-26 CN CN201780008501.6A patent/CN108603264B/zh active Active
Also Published As
Publication number | Publication date |
---|---|
EP3409806A4 (en) | 2019-02-20 |
EP3409806B1 (en) | 2021-03-10 |
CN108603264B (zh) | 2020-10-30 |
US20190040511A1 (en) | 2019-02-07 |
US11447852B2 (en) | 2022-09-20 |
WO2017131054A1 (ja) | 2017-08-03 |
KR102148739B1 (ko) | 2020-08-27 |
EP3409806A1 (en) | 2018-12-05 |
JPWO2017131054A1 (ja) | 2018-02-01 |
CN108603264A (zh) | 2018-09-28 |
KR20180095699A (ko) | 2018-08-27 |
JP6274360B2 (ja) | 2018-02-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2018009236A (es) | Lamina de acero galvanizado de alta resistencia, miembro de alta resistencia, y metodo para producir lamina de acero galvanizado de alta resistencia. | |
MX2019007728A (es) | Lamina de acero galvanizado de alta resistencia y metodo para producir la misma. | |
MX2016000266A (es) | Lamina de acero chapado de alta resistencia que tiene propiedades superiores de chapado, capacidad de manipulacion, y resistencia a la fractura retardada, y metodo de produccion la misma. | |
MX2019009513A (es) | Lamina de acero galvanizada de alta resistencia y metodo para producir la misma. | |
MX2016011756A (es) | Chapa de acero laminado en frio de alta resistencia y chapa de acero galvanizado de alta resistencia que tienen una excelente ductilidad y capacidad de flexion, y metodos para su produccion. | |
MA39075A1 (fr) | Acier à haute résistance et procédé de fabrication | |
MX2016007948A (es) | Lamina de acero galvanizada por inmersion de caliente de alta resistencia y metodo para la produccion de la misma. | |
MX2017009015A (es) | Lámina de acero chapado de alta resistencia que tiene excelentes propiedades de chapado, trabajabilidad y mayor resistencia a las fracturas, y método para su producción. | |
MX2016007954A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
MX2020005475A (es) | Chapa de acero galvanizada de alta resistencia y metodo para fabricar la misma. | |
MX2017001529A (es) | Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia. | |
MX2017015333A (es) | Lamina de acero rolada en frio de alta resistencia, lamina de acero recubierta de alta resistencia, metodo para fabricar lamina de acero rolada en frio de alta resistencia, y metodo para fabricar lamina de acero recubierta de alta resistencia. | |
MX2017001106A (es) | Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia. | |
MX2017001105A (es) | Lamina de acero galvanizada de alta resistencia y metodo de produccion de la misma. | |
MX2012002450A (es) | Lamina de acero galvanizada en caliente por inmersion, de alta resistencia, y proceso para producir la misma. | |
MX2019001828A (es) | Lamina de acero y metodo para la fabricacion de la misma. | |
MX2018014261A (es) | Lamina de acero recubierta o chapada y metodo para producir la misma. | |
MX2018006419A (es) | Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia. | |
MX2017001720A (es) | Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia. | |
MX2018009164A (es) | Lamina de acero galvanizado de alta resistencia y alta relacion de rendimiento y metodo para producir la misma. | |
MX2017009021A (es) | Lámina de acero chapado de alta resistencia y método para su producción. | |
MX2016013771A (es) | Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia. | |
MX2015016367A (es) | Placa de acero laminada en frio, placa de acero laminada en frio galvanizada, y metodo para manufacturar las placas. | |
MX356970B (es) | Acero al cromo con bajo contenido de carbono, reducido en vanadio y alta resistencia a la corrosión, y métodos de fabricación. | |
MX2018011778A (es) | Chapa de acero, chapa de acero revestida, metodo para producir chapa de acero laminada en caliente, metodo para producir chapa de acero muy dura laminada en frio, metodo para producir chapa de acero y metodo para producir chapa de acero revestida. |