LU500086B1 - Polyolefin blend with barrier and mechanical properties - Google Patents
Polyolefin blend with barrier and mechanical properties Download PDFInfo
- Publication number
- LU500086B1 LU500086B1 LU500086A LU500086A LU500086B1 LU 500086 B1 LU500086 B1 LU 500086B1 LU 500086 A LU500086 A LU 500086A LU 500086 A LU500086 A LU 500086A LU 500086 B1 LU500086 B1 LU 500086B1
- Authority
- LU
- Luxembourg
- Prior art keywords
- polyethylene
- ranging
- polyolefin blend
- measured
- iso
- Prior art date
Links
- 239000000203 mixture Substances 0.000 title claims abstract description 174
- 229920000098 polyolefin Polymers 0.000 title claims abstract description 154
- 230000004888 barrier function Effects 0.000 title description 11
- 239000004698 Polyethylene Substances 0.000 claims abstract description 410
- 229920000573 polyethylene Polymers 0.000 claims abstract description 409
- -1 polyethylene Polymers 0.000 claims abstract description 230
- 239000000155 melt Substances 0.000 claims abstract description 62
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 claims abstract description 34
- 239000001301 oxygen Substances 0.000 claims abstract description 34
- 229910052760 oxygen Inorganic materials 0.000 claims abstract description 34
- 230000035699 permeability Effects 0.000 claims abstract description 33
- 230000005540 biological transmission Effects 0.000 claims abstract description 28
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Chemical compound O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims abstract description 28
- 229920001903 high density polyethylene Polymers 0.000 claims description 32
- 239000004700 high-density polyethylene Substances 0.000 claims description 32
- VGGSQFUCUMXWEO-UHFFFAOYSA-N Ethene Chemical compound C=C VGGSQFUCUMXWEO-UHFFFAOYSA-N 0.000 claims description 24
- 239000005977 Ethylene Substances 0.000 claims description 24
- 229920000092 linear low density polyethylene Polymers 0.000 claims description 24
- 239000004707 linear low-density polyethylene Substances 0.000 claims description 23
- 238000002844 melting Methods 0.000 claims description 21
- 230000008018 melting Effects 0.000 claims description 21
- LIKMAJRDDDTEIG-UHFFFAOYSA-N 1-hexene Chemical compound CCCCC=C LIKMAJRDDDTEIG-UHFFFAOYSA-N 0.000 claims description 20
- 229920001577 copolymer Polymers 0.000 claims description 16
- 239000004702 low-density polyethylene Substances 0.000 claims description 16
- 238000000113 differential scanning calorimetry Methods 0.000 claims description 15
- 229920001684 low density polyethylene Polymers 0.000 claims description 15
- 238000002834 transmittance Methods 0.000 claims description 12
- 229920010126 Linear Low Density Polyethylene (LLDPE) Polymers 0.000 claims description 10
- 238000003860 storage Methods 0.000 claims description 10
- 239000011347 resin Substances 0.000 claims description 9
- 229920005989 resin Polymers 0.000 claims description 9
- 235000013365 dairy product Nutrition 0.000 claims description 6
- 235000013305 food Nutrition 0.000 claims description 6
- 238000004806 packaging method and process Methods 0.000 claims description 4
- 239000004566 building material Substances 0.000 claims description 3
- 230000006835 compression Effects 0.000 claims description 3
- 238000007906 compression Methods 0.000 claims description 3
- 238000010411 cooking Methods 0.000 claims description 3
- 230000035622 drinking Effects 0.000 claims description 3
- 239000004744 fabric Substances 0.000 claims description 3
- 239000000835 fiber Substances 0.000 claims description 3
- 238000000034 method Methods 0.000 description 25
- 229920000642 polymer Polymers 0.000 description 17
- 239000004711 α-olefin Substances 0.000 description 16
- 229940099514 low-density polyethylene Drugs 0.000 description 14
- 230000008569 process Effects 0.000 description 13
- 238000012360 testing method Methods 0.000 description 13
- 230000015556 catabolic process Effects 0.000 description 11
- 238000006731 degradation reaction Methods 0.000 description 11
- 229920013716 polyethylene resin Polymers 0.000 description 11
- QQONPFPTGQHPMA-UHFFFAOYSA-N propylene Natural products CC=C QQONPFPTGQHPMA-UHFFFAOYSA-N 0.000 description 10
- 238000004519 manufacturing process Methods 0.000 description 9
- 229920001519 homopolymer Polymers 0.000 description 8
- 238000002156 mixing Methods 0.000 description 8
- 125000004805 propylene group Chemical group [H]C([H])([H])C([H])([*:1])C([H])([H])[*:2] 0.000 description 8
- 238000001228 spectrum Methods 0.000 description 8
- PBKONEOXTCPAFI-UHFFFAOYSA-N TCB Natural products ClC1=CC=C(Cl)C(Cl)=C1 PBKONEOXTCPAFI-UHFFFAOYSA-N 0.000 description 7
- 229920001038 ethylene copolymer Polymers 0.000 description 7
- VXNZUUAINFGPBY-UHFFFAOYSA-N 1-Butene Chemical compound CCC=C VXNZUUAINFGPBY-UHFFFAOYSA-N 0.000 description 6
- KWKAKUADMBZCLK-UHFFFAOYSA-N 1-octene Chemical compound CCCCCCC=C KWKAKUADMBZCLK-UHFFFAOYSA-N 0.000 description 6
- 238000005227 gel permeation chromatography Methods 0.000 description 6
- YWAKXRMUMFPDSH-UHFFFAOYSA-N pentene Chemical compound CCCC=C YWAKXRMUMFPDSH-UHFFFAOYSA-N 0.000 description 6
- 238000005259 measurement Methods 0.000 description 5
- 125000002496 methyl group Chemical group [H]C([H])([H])* 0.000 description 5
- 230000003287 optical effect Effects 0.000 description 5
- 238000006116 polymerization reaction Methods 0.000 description 5
- 238000001542 size-exclusion chromatography Methods 0.000 description 5
- 238000009864 tensile test Methods 0.000 description 5
- AFFLGGQVNFXPEV-UHFFFAOYSA-N 1-decene Chemical compound CCCCCCCCC=C AFFLGGQVNFXPEV-UHFFFAOYSA-N 0.000 description 4
- CRSBERNSMYQZNG-UHFFFAOYSA-N 1-dodecene Chemical compound CCCCCCCCCCC=C CRSBERNSMYQZNG-UHFFFAOYSA-N 0.000 description 4
- GQEZCXVZFLOKMC-UHFFFAOYSA-N 1-hexadecene Chemical compound CCCCCCCCCCCCCCC=C GQEZCXVZFLOKMC-UHFFFAOYSA-N 0.000 description 4
- HFDVRLIODXPAHB-UHFFFAOYSA-N 1-tetradecene Chemical compound CCCCCCCCCCCCC=C HFDVRLIODXPAHB-UHFFFAOYSA-N 0.000 description 4
- WSSSPWUEQFSQQG-UHFFFAOYSA-N 4-methyl-1-pentene Chemical compound CC(C)CC=C WSSSPWUEQFSQQG-UHFFFAOYSA-N 0.000 description 4
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 4
- 238000005033 Fourier transform infrared spectroscopy Methods 0.000 description 4
- 102100021792 Gamma-sarcoglycan Human genes 0.000 description 4
- 101000616435 Homo sapiens Gamma-sarcoglycan Proteins 0.000 description 4
- 125000001931 aliphatic group Chemical group 0.000 description 4
- FFUAGWLWBBFQJT-UHFFFAOYSA-N hexamethyldisilazane Chemical compound C[Si](C)(C)N[Si](C)(C)C FFUAGWLWBBFQJT-UHFFFAOYSA-N 0.000 description 4
- 239000000463 material Substances 0.000 description 4
- 239000000178 monomer Substances 0.000 description 4
- VAMFXQBUQXONLZ-UHFFFAOYSA-N n-alpha-eicosene Natural products CCCCCCCCCCCCCCCCCCC=C VAMFXQBUQXONLZ-UHFFFAOYSA-N 0.000 description 4
- CCCMONHAUSKTEQ-UHFFFAOYSA-N octadec-1-ene Chemical compound CCCCCCCCCCCCCCCCC=C CCCMONHAUSKTEQ-UHFFFAOYSA-N 0.000 description 4
- 239000000126 substance Substances 0.000 description 4
- 238000001644 13C nuclear magnetic resonance spectroscopy Methods 0.000 description 3
- 238000005481 NMR spectroscopy Methods 0.000 description 3
- 238000004364 calculation method Methods 0.000 description 3
- 238000011156 evaluation Methods 0.000 description 3
- VLKZOEOYAKHREP-UHFFFAOYSA-N n-Hexane Chemical compound CCCCCC VLKZOEOYAKHREP-UHFFFAOYSA-N 0.000 description 3
- TVMXDCGIABBOFY-UHFFFAOYSA-N n-Octanol Natural products CCCCCCCC TVMXDCGIABBOFY-UHFFFAOYSA-N 0.000 description 3
- 238000002360 preparation method Methods 0.000 description 3
- 230000000007 visual effect Effects 0.000 description 3
- 229940106006 1-eicosene Drugs 0.000 description 2
- FIKTURVKRGQNQD-UHFFFAOYSA-N 1-eicosene Natural products CCCCCCCCCCCCCCCCCC=CC(O)=O FIKTURVKRGQNQD-UHFFFAOYSA-N 0.000 description 2
- 229910000661 Mercury cadmium telluride Inorganic materials 0.000 description 2
- 238000000071 blow moulding Methods 0.000 description 2
- MCMSPRNYOJJPIZ-UHFFFAOYSA-N cadmium;mercury;tellurium Chemical compound [Cd]=[Te]=[Hg] MCMSPRNYOJJPIZ-UHFFFAOYSA-N 0.000 description 2
- 239000012159 carrier gas Substances 0.000 description 2
- 238000005266 casting Methods 0.000 description 2
- 239000003054 catalyst Substances 0.000 description 2
- 230000008859 change Effects 0.000 description 2
- 150000001875 compounds Chemical class 0.000 description 2
- 238000000748 compression moulding Methods 0.000 description 2
- 230000003750 conditioning effect Effects 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 229940069096 dodecene Drugs 0.000 description 2
- 238000001125 extrusion Methods 0.000 description 2
- 238000010096 film blowing Methods 0.000 description 2
- 238000002347 injection Methods 0.000 description 2
- 239000007924 injection Substances 0.000 description 2
- 238000001746 injection moulding Methods 0.000 description 2
- 229920001179 medium density polyethylene Polymers 0.000 description 2
- 239000004701 medium-density polyethylene Substances 0.000 description 2
- 229910052757 nitrogen Inorganic materials 0.000 description 2
- 239000002861 polymer material Substances 0.000 description 2
- 239000000843 powder Substances 0.000 description 2
- 239000002904 solvent Substances 0.000 description 2
- 230000003595 spectral effect Effects 0.000 description 2
- 238000012546 transfer Methods 0.000 description 2
- RELMFMZEBKVZJC-UHFFFAOYSA-N 1,2,3-trichlorobenzene Chemical compound ClC1=CC=CC(Cl)=C1Cl RELMFMZEBKVZJC-UHFFFAOYSA-N 0.000 description 1
- 239000004793 Polystyrene Substances 0.000 description 1
- 238000002835 absorbance Methods 0.000 description 1
- 230000032683 aging Effects 0.000 description 1
- 238000013019 agitation Methods 0.000 description 1
- 150000001335 aliphatic alkanes Chemical class 0.000 description 1
- 239000012080 ambient air Substances 0.000 description 1
- 238000004458 analytical method Methods 0.000 description 1
- UHOVQNZJYSORNB-MZWXYZOWSA-N benzene-d6 Chemical compound [2H]C1=C([2H])C([2H])=C([2H])C([2H])=C1[2H] UHOVQNZJYSORNB-MZWXYZOWSA-N 0.000 description 1
- WXCZUWHSJWOTRV-UHFFFAOYSA-N but-1-ene;ethene Chemical compound C=C.CCC=C WXCZUWHSJWOTRV-UHFFFAOYSA-N 0.000 description 1
- 125000004432 carbon atom Chemical group C* 0.000 description 1
- 239000000306 component Substances 0.000 description 1
- 238000013329 compounding Methods 0.000 description 1
- 230000001143 conditioned effect Effects 0.000 description 1
- 238000012937 correction Methods 0.000 description 1
- 230000003247 decreasing effect Effects 0.000 description 1
- 238000010828 elution Methods 0.000 description 1
- ALSOCDGAZNNNME-UHFFFAOYSA-N ethene;hex-1-ene Chemical compound C=C.CCCCC=C ALSOCDGAZNNNME-UHFFFAOYSA-N 0.000 description 1
- 230000014509 gene expression Effects 0.000 description 1
- UQEAIHBTYFGYIE-UHFFFAOYSA-N hexamethyldisiloxane Chemical compound C[Si](C)(C)O[Si](C)(C)C UQEAIHBTYFGYIE-UHFFFAOYSA-N 0.000 description 1
- 229910052738 indium Inorganic materials 0.000 description 1
- 238000002329 infrared spectrum Methods 0.000 description 1
- 239000004615 ingredient Substances 0.000 description 1
- 229920002521 macromolecule Polymers 0.000 description 1
- 239000002245 particle Substances 0.000 description 1
- 238000005453 pelletization Methods 0.000 description 1
- 229920005638 polyethylene monopolymer Polymers 0.000 description 1
- 229920002959 polymer blend Polymers 0.000 description 1
- 230000000379 polymerizing effect Effects 0.000 description 1
- 229920005606 polypropylene copolymer Polymers 0.000 description 1
- 229920002223 polystyrene Polymers 0.000 description 1
- 238000003825 pressing Methods 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 238000010926 purge Methods 0.000 description 1
- 238000004611 spectroscopical analysis Methods 0.000 description 1
- 230000006641 stabilisation Effects 0.000 description 1
- 238000011105 stabilization Methods 0.000 description 1
- 229920001897 terpolymer Polymers 0.000 description 1
- 229920006029 tetra-polymer Polymers 0.000 description 1
- 238000012795 verification Methods 0.000 description 1
- 239000002699 waste material Substances 0.000 description 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/18—Manufacture of films or sheets
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
- C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
- C08L23/04—Homopolymers or copolymers of ethene
- C08L23/08—Copolymers of ethene
- C08L23/0807—Copolymers of ethene with unsaturated hydrocarbons only containing four or more carbon atoms
- C08L23/0815—Copolymers of ethene with unsaturated hydrocarbons only containing four or more carbon atoms with aliphatic 1-olefins containing one carbon-to-carbon double bond
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2323/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
- C08J2323/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
- C08J2323/04—Homopolymers or copolymers of ethene
- C08J2323/08—Copolymers of ethene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2423/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
- C08J2423/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
- C08J2423/04—Homopolymers or copolymers of ethene
- C08J2423/08—Copolymers of ethene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2201/00—Properties
- C08L2201/10—Transparent films; Clear coatings; Transparent materials
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2201/00—Properties
- C08L2201/14—Gas barrier composition
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2203/00—Applications
- C08L2203/16—Applications used for films
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2207/00—Properties characterising the ingredient of the composition
- C08L2207/20—Recycled plastic
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Manufacturing & Machinery (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Compositions Of Macromolecular Compounds (AREA)
Claims (27)
1. Un mélange de polyoléfines comprenant : - de 2 % en poids à 49 % en poids d'un premier polyéthylène PE1 sur la base du poids total du mélange de polyoléfines ; le premier polyéthylène PE1 étant un polyéthylène haute densité avec une densité d'au moins 0,940 g/cm’ telle que déterminée selon ISO 1183 à une température de 23 °C ; et un indice de fusion (MI2) d'au plus 500,0 g/10 min tel que déterminé selon ISO 1133-1:2011 à une température de 190 °C et sous une charge de 2,16 kg ; et - de 51 % en poids à 98 % en poids d'un deuxième polyéthylène PE2 sur la base du poids total du mélange de polyoléfines ; le deuxième polyéthylène PE2 ayant une densité allant de 0,890 à moins de 0,940 g/cm’ telle que déterminée selon ISO 1183 à une température de 23 °C ; et un indice de fusion (MI2) allant de 0,1 à 20,0 2/10 min tel que déterminé selon ISO 1133-1:2011 à une température de 190 °C et sous une charge de 2,16 kg ; dans lequel le rapport de l'indice de fusion du premier polyéthylène PE1 par rapport au deuxième polyéthylène PE2 est égal ou supérieur à 1,0 ;et dans lequel le mélange de polyoléfines a un coefficient de perméabilité à l'oxygène (PO») allant de 2,04 x 10716 à 9,18 x 107! mol'm/m*s-Pa tel que mesuré par ASTM D3985-17 et/ou un taux de transmission de vapeur d'eau (WVTR) d'au plus 10,42 x 107° g/(m°.s) tel que mesuré par ASTM F1249-20.
2. Le mélange de polyoléfines selon la revendication 1, dans lequel le mélange de polyoléfines a un coefficient de perméabilité à l'oxygène (PO) allant de 2,55 x 107!° à 7,14 x 107! mol-m/m*-s-Pa tel que mesuré par ASTM D3985-17.
3. Le mélange de polyoléfines selon la revendication 1 ou 2, dans lequel le mélange de polyoléfines a un taux de transmission de vapeur d'eau (WVTR) d'au plus 9,26 x 107° g/(m°.s), tel que mesuré par ASTM F1249-20.
4. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 3, dans lequel le mélange de polyoléfines a un indice de fusion (MI2) d'au plus 25 g/10 min tel que déterminé selon ISO 1133-1:2011 à une température de 190 °C et sous une charge de
2,16 kg. LU500086
5. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 4, dans lequel le rapport de l'indice de fusion du premier polyéthylène PE1 par rapport au deuxième polyéthylène PF2 est compris entre 1,1 et 100.
6. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 5, dans lequel le mélange de polyoléfines comprend entre 8 et 30 % en poids du premier polyéthylène PF1 sur la base du poids total du mélange de polyoléfines, et entre 70 et 92 % en poids du deuxième polyéthylène PE2.
7. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 6, dans lequel au moins un élément sélectionné parmi le premier polyéthylène PE1 et le deuxième polyéthylène PE2 a un Mw/Mn allant de 1,5 à 6,0 comme déterminé par GPC.
8. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 7, dans lequel au moins un élément sélectionné parmi le premier polyéthylène PE1 et le deuxième polyéthylène PE2 est un copolymère d'éthylène et de 1-hexène.
9. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 8, dans lequel le premier polyéthylène PE1 comprend un ou plusieurs des éléments suivants : - une densité allant de 0,945 à 0,965 g/cm’ telle que déterminée selon ISO 1183 à une température de 23 °C ; - un indice de fusion allant de 1,0 à 100,0 g/10 min tel que déterminé selon ISO 1133-1:2011 à une température de 190 °C et sous une charge de 2,16 kg ; - une température de fusion d'au moins 120 °C telle que mesurée par ISO 11357 ; et/ou - une teneur plus commune exprimée en nombre de ramifications courtes (SCB) pour 1000 carbones totaux allant de O ramification/1000 C à
3,0 ramifications/1 000 C. LU500086
10.Un mélange de polyoléfines selon l'une quelconque des revendications 1 à 9, le deuxième polyéthylène PE2 comprenant un ou plusieurs des éléments suivants : - une densité allant de 0,910 à 0,935 g/cm’ telle que déterminée selon ISO 1183 à une température de 23 °C ; - un indice de fusion allant de 0,8 à 8,0 g/10 min tel que déterminé selon ISO 1133- 1:2011 à une température de 190 °C et sous une charge de 2,16 kg ; - une température de fusion Tm d'au plus 118 °C telle que mesurée par ISO 11357 ; et/ou - une teneur en polyéthylène basse densité linéaire LLDPE d'au moins 70 % en poids du poids total du deuxième polyéthylène PE2.
11. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 10, dans lequel un ou plusieurs éléments sélectionnés parmi le premier polyéthylène PE1 et le deuxième polyéthylène PE2 sont catalysés par un métallocène.
12. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 11, dans lequel le deuxième polyéthylène PE2 est un ou plusieurs éléments sélectionnés parmi le polyéthylène basse densité linéaire (LLDPE) et le polyéthylène basse densité (LDPE).
13. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 12, dans lequel un ou plusieurs éléments sélectionnés parmi le premier polyéthylène PE1 et le deuxième polyéthylène PE2 est une résine post-consommation.
14. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 13, dans lequel le mélange de polyoléfines comprend un ou plusieurs éléments parmi : - un module d'élasticité (E) allant de 180 à 500 MPa, tel que mesuré par ISO 527-3 à 23 °C;
- une résistance a la traction à la rupture allant de 15 à 100 MPa telle que mesurée LU500086 conformément à ASTM D638 ; - un allongement à la rupture allant de 300 à 800% tel que mesuré selon ASTM D638 ; et/ou - une transmittance d'au moins 10 % lorsqu'elle est mesurée à 450 nm sur un échantillon d'une épaisseur de 350 um.
15. Le mélange de polyoléfines selon l'une quelconque des revendications 1 à 14, dans lequel le mélange de polyoléfines a une capacité thermique spécifique (AHn) allant de 90 à 150 J/g telle que mesurée par calorimétrie différentielle à balayage (DSC).
16. Un article comprenant le mélange de polyoléfines selon l'une quelconque des revendications 1 à 15.
17. L'article selon la revendication 16, dans lequel l'article est sélectionné parmi un récipient de stockage alimentaire de produits ménagers, un ustensile de cuisine, une assiette, une tasse, un plateau à cavité, un gobelet, un verre mesureur, une passoire, une poire à dinde, un récipient de stockage non alimentaire, un classeur, une armoire à tiroirs, un article de stockage général, un organisateur, un fourre-tout, une boîte de pull, un emballage rigide, une boîte de charcuterie, un couvercle de boîte de charcuterie, une boîte de produits laitiers, un couvercle de boîte de produits laitiers, une bouteille et un pot de produits de soins personnels, un meuble, un composant de meuble, un matériau de construction, des composants de conteneur de construction, du film, une feuille, de la fibre, un sac, du fil et un sachet en tissu, ou une coquille.
18. L'article selon la revendication 16 ou 17, dans lequel l'article est choisi parmi un article extrudé, un article moulé par soufflage, un article moulé par injection ou un article moulé par compression.
19. L'article selon la revendication 16, dans lequel l'article est une feuille thermoformée LU500086 d'une épaisseur d'au moins 1 mm.
20. L'article selon la revendication 16, dans lequel l'article est un film d'une épaisseur allant de 2 um à 2,0 mm.
21.Un film comprenant le mélange de polyoléfines selon l'une quelconque des revendications 1 à 15.
22. Le film selon la revendication 21, dans lequel le film a une épaisseur allant de m 2 um à 2,0 mm.
23. Le film selon la revendication 21 ou la revendication 22, dans lequel le film a un coefficient de perméabilité à l'oxygène (PO) allant de 2,55 x 107° à 7,14 x 107!° mol-m/m°-s-Pa tel que mesuré par ASTM D3985-17 .
24. Le film selon l'une quelconque des revendications 21 à 23, dans lequel le film a un taux de transmission de vapeur d'eau (WVTR) d'au plus 9,26 x 107° g/(m° s), tel que mesuré par ASTM F1249-20.
25. Le film selon l'une quelconque des revendications 21 à 24, dans lequel le film a un indice de fusion (MI2) d'au plus 25 g/10 min tel que déterminé selon ISO 1133-1:2011 à une température de 190 °C et sous une charge de 2,16 kg.
26. Le film selon l'une quelconque des revendications 21 à 25, dans lequel le film comprend un ou plusieurs éléments parmi: - un module d'élasticité (E) allant de 180 à 500 MPa, tel que mesuré par ISO 527-3 à 23 °C;
- une résistance a la traction a la rupture allant de 15 à 100 MPa telle que mesurée LU500086 conformément à ASTM D638 ; - un allongement à la rupture allant de 300 à 800 % tel que mesuré selon ASTM D638 ; et/ou - une transmittance d'au moins 10 % lorsqu'elle est mesurée à 450 nm sur un échantillon d'une épaisseur de 350 um.
27. Le film selon l'une quelconque des revendications 21 à 26, dans lequel le film a une capacité thermique spécifique (AHnm) allant de 90 à 150 J/g telle que mesurée par calorimétrie différentielle à balayage (DSC).