KR970061803A - Crystallized glass for building materials with natural marble pattern and its manufacturing method - Google Patents

Crystallized glass for building materials with natural marble pattern and its manufacturing method Download PDF

Info

Publication number
KR970061803A
KR970061803A KR1019970006524A KR19970006524A KR970061803A KR 970061803 A KR970061803 A KR 970061803A KR 1019970006524 A KR1019970006524 A KR 1019970006524A KR 19970006524 A KR19970006524 A KR 19970006524A KR 970061803 A KR970061803 A KR 970061803A
Authority
KR
South Korea
Prior art keywords
crystallized glass
manufacturing
building materials
natural marble
marble pattern
Prior art date
Application number
KR1019970006524A
Other languages
Korean (ko)
Other versions
KR100385371B1 (en
Inventor
요시오 하시베
Original Assignee
모리 데쯔지
닛뽄 덴끼 가라스 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 모리 데쯔지, 닛뽄 덴끼 가라스 가부시끼가이샤 filed Critical 모리 데쯔지
Publication of KR970061803A publication Critical patent/KR970061803A/en
Application granted granted Critical
Publication of KR100385371B1 publication Critical patent/KR100385371B1/en

Abstract

본 발명의 결정화 유리는 청정제로서 황산나트륨을 사용하며, 중량백분률로 SiO245~77%, Al2O31~25%, CaO 2~25%, ZnO 0~18%, BaO 0~20%, Na2O 1~15%, K2O 0~7%, Li2O 0~5%, B2O30~1.5%, CeO20.01~0.5%, SO30.01~0.5%의 조성을 가지도록 조합한 유리원료를 용융 및 성형한 후, 결정화시켜 제조한다. 본 발명의 결정화 유리는 As2O3및 Sb2O3를 함유하지 않지만, 용해성이 우수하여 생산효율이 좋을 뿐만아니라 종래의 제품과 동등하거나 그 이상의 백색도를 가진다.The crystallized glass of the present invention uses sodium sulfate as a detergent, and by weight percentage, SiO 2 45-77%, Al 2 O 3 1-25%, CaO 2-25%, ZnO 0-18%, BaO 0-20% , Na 2 O 1-15%, K 2 O 0-7%, Li 2 O 0-5%, B 2 O 3 0-1.5%, CeO 2 0.01-0.5%, SO 3 0.01-0.5% The glass raw materials so combined are melted and molded, and then crystallized. The crystallized glass of the present invention does not contain As 2 O 3 and Sb 2 O 3 , but is excellent in solubility and has good production efficiency, and has a whiteness equivalent to or higher than that of a conventional product.

Description

천연 대리석 무늬를 갖는 건축 재료용 결정화 유리 및 그 제조방법Crystallized glass for building materials with natural marble pattern and its manufacturing method

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.

Claims (2)

중량백분률로 SiO245~77%, Al2O31~25%, CaO 2~25%, ZnO 0~18%, BaO 0~20%, Na2O 1~15%, K2O 0~7%, Li2O 0~5%, B2O30~1.5%, CeO20.01~0.5%, SO30.01~0.5%의 조성을 가지며, 주결정으로서-규회석을 석출하여 이루지는 것을 특징으로 하는 결정화 유리.By weight percentage SiO 2 45 ~ 77%, Al 2 O 3 1-25%, CaO 2-25%, ZnO 0-18%, BaO 0-20%, Na 2 O 1-15%, K 2 O 0 ~ 7%, Li 2 O 0-5%, B 2 O 3 0-1.5%, CeO 2 0.01-0.5%, SO 3 0.01-0.5%, as a main crystal Crystallized glass, characterized in that it is formed by depositing wollastonite. 청정제로서 황산나트륨을 사용하고, 중량백분률로 SiO245~77%, Al2O31~25%, CaO 2~25%, ZnO 0~18%, BaO 0~20%, Na2O 1~15%, K2O 0~7%, Li2O 0~5%, B2O30~1.5%, CeO20.01~0.5%, SO30.01~0.5%의 조성이 되도록 조합한 유리원료를 용융 및 성형한 후, 결정화시키는 것을 특징으로 하는 결정화 유리의 제조방법.Sodium sulfate is used as a cleaning agent, and by weight percentage, SiO 2 45-77%, Al 2 O 3 1-25%, CaO 2-25%, ZnO 0-18%, BaO 0-20%, Na 2 O 1 ~ 15%, K 2 O 0 ~ 7%, Li 2 O 0 ~ 5%, B 2 O 3 0 ~ 1.5%, CeO 2 0.01 ~ 0.5%, SO 3 0.01 ~ 0.5% After melting and molding, it crystallizes. The manufacturing method of the crystallized glass characterized by the above-mentioned. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019970006524A 1996-02-28 1997-02-28 Crystallized glass for building material having natural marbly pattern and manufacturing method thereof KR100385371B1 (en)