KR970043151A - Manufacturing method of thick plate steel for storage tank with excellent high temperature material characteristics - Google Patents
Manufacturing method of thick plate steel for storage tank with excellent high temperature material characteristics Download PDFInfo
- Publication number
- KR970043151A KR970043151A KR1019950049562A KR19950049562A KR970043151A KR 970043151 A KR970043151 A KR 970043151A KR 1019950049562 A KR1019950049562 A KR 1019950049562A KR 19950049562 A KR19950049562 A KR 19950049562A KR 970043151 A KR970043151 A KR 970043151A
- Authority
- KR
- South Korea
- Prior art keywords
- manufacturing
- storage tank
- high temperature
- thick plate
- excellent high
- Prior art date
Abstract
본 발명은 석유화학 저장탱크용 소재로 사용되는 후판강재의 제조방법에 관한 것이며, 그 목적은 고온(217℃)에서는 재질열화가 발생되지 않는 후판강재의 제조방법에 관한 것이다.The present invention relates to a method for producing a thick steel plate used as a material for a petrochemical storage tank, the object of the present invention relates to a method for manufacturing a thick plate steel material does not occur at high temperatures (217 ℃).
본 발명은 중량%로, C: 0.07-0.10%, Si: 0.30-0.40%, Mn: 1.30-1.50%, P: 0.020% 이하, S: 0.010%이하, Mo: 0.25-0.35%, Nb: 0.02-0.04%, V: 0.04-0.06%, 나머지 Fe 및 기타불가피한 불순물로 조성되는 강슬라브를 통상의 방법으로 열간압연한 후 870-890℃의 온도에서 (1.0t + 5분 - 1.3t + 5분)(t: 압연된 소재 두께)동안 소준처리한 다음, 600-650℃의 온도 범위에서 1.9t(1.9+20)분 동안 소려함을 포함하여 구성되는 고온재질 특성이 우수한 저장탱크용 후판강재의 제조방법에 관한 것을 그 기술적 요지로 한다.In the present invention, by weight%, C: 0.07-0.10%, Si: 0.30-0.40%, Mn: 1.30-1.50%, P: 0.020% or less, S: 0.010% or less, Mo: 0.25-0.35%, Nb: 0.02 -0.04%, V: 0.04-0.06%, steel slab composed of the remaining Fe and other unavoidable impurities, hot-rolled in a conventional manner, at a temperature of 870-890 ° C. (1.0t + 5 min-1.3t + 5 min (t: rolled material thickness), followed by annealing for 1.9 t (1.9 + 20) minutes in the temperature range of 600-650 ° C. The technical subject matter is a manufacturing method.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
Claims (1)