KR970001022B1

KR970001022B1 - Apparatus and method for producing a thermos cover of pipe

Info

Publication number: KR970001022B1
Application number: KR1019890008663A
Authority: KR
Inventors: 이봉두
Original assignee: 주식회사 금강; 박가경
Priority date: 1989-06-22
Filing date: 1989-06-22
Publication date: 1997-01-25
Also published as: KR910001309A

Abstract

A cover for warming pipe wherein plural V grooves(16) are formed on the surface of an inorganic fiber slab plate(1') and on an adhesive paper(6) is bonded to the opposite surface of the plate(1'): a manufacturing method thereof comprising the step cutting the plate(1') as feeding it ; the step spraying adhesive of the opposite surface to bond the adhesive paper; the step fixing the plate to form plural V grooves; and the step repeating the steps : and a manufacturing apparatus thereof having a cutting edge(3) in upstream of a conveyer belt(2); an adhesive spraying nozzle(4), a winding roll(5), a press roll(7) and a guide roll(8) in downstream of the cutting edge(3); a pressing means having a press rollers(9,10) and a press plate(11) contacted to the rear end of the conveyer belt(2); supporting plates(13,13'); and a rotation edge(14) swiveled between the supporting plates(13,13'); are disclosed.

Description

Manufacturing method and apparatus for piping insulation cover

제1도는 본 발명에 의하면 제조된 보온용 카바 및 그 시공상태를 보인 사시도.1 is a perspective view showing the insulation cover manufactured according to the present invention and its construction.

제2도는 본 발명에 의한 보온용 카바의 제조방법을 설명하기 위한 공정도.Figure 2 is a process chart for explaining the manufacturing method of the cover for thermal insulation according to the present invention.

제3도는 본 발명에 의한 보온용 카바의 제조장치를 예시한 사시도.3 is a perspective view illustrating an apparatus for manufacturing a thermal insulation cover according to the present invention.

제4도는 본 발명에 의한 보온용 카바의 V형홈 삭설을 위한 수단을 예시한 시시도.4 is a view illustrating a means for removing the V-shaped groove of the thermal insulation cover according to the present invention.

제5도는 본 발명에 의한 보온용 카바의 V형홈 삭설각도에 따른 구체적인 시공예를 설명하기 위한 설명도.Figure 5 is an explanatory view for explaining a specific construction example according to the angle of V-shaped groove cutting of the thermal insulation cover according to the present invention.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1,1' : 슬라브판체 2 : 콘베이어벨트1,1 ': slab plate body 2: conveyor belt

3 : 절단톱 4 : 접착제분사노즐3: cutting saw 4: adhesive spray nozzle

5 : 권취롤 6 : 접착지5: winding roll 6: adhesive paper

7 : 압압롤 8 : 안내롤7: press roll 8: guide roll

9,10 : 압압롤러 11 : 압압판9,10: press roller 11: press plate

13,13' : 받침대 14 : 회전도13,13 ': pedestal 14: degree of rotation

16 : V형홈16: V-shaped groove

본 발명은, 열연화성 무기물질을 용융시키고 섬유화하며 이때 섬유간의 상호결합력을 부여하기 위하여 분사된 열경화성 섬유표면처리제가 경화되도록 하기 위하여 건조장치에 통과시켜 건조시키고 성형하며, 재단을 완료한 상태의 슬라브판체를 이용하여 두께의 조정이 용이하며, 다양한 규격의 배관에 고루 사용이 가능할 뿐만 아니라, 생산능률을 대폭 증대시킬 수 있는 배관 보온용 카바의 제조방법 및 제조장치에 관한 것이다.The present invention, the slab of the heat-softening inorganic material is melted and fiberized, and passed through a drying apparatus for drying and shaping the sprayed thermosetting fiber surface treatment agent in order to harden the fibers to impart the mutual bonding force between the fibers, and finished cutting It is easy to adjust the thickness by using a plate body, and can be used evenly for pipes of various standards, and relates to a manufacturing method and apparatus for manufacturing a pipe insulation cover that can greatly increase the production efficiency.

종래에서 각종 배관을 보온시켜 줌으로써 에너지 손실을 방지하고자 하였으며, 이를 위하여 무기섬유 제조공정에서 생산된 블랑켓트상의 매트를 콘베이어벨트 위에 전개시켜 이송시키되 인력이나 기계를 이용하여 심봉에 콘베이어벨트 위에서 이송되는 매트를 권취하고 건조시킨 후 재단가공하여 배관 보온용 카바를 완성하였던 것이므로 무기섬유 제조공정에서 흔히 발생하는 부위별 집면밀도의 불균일 현상에 의하여 심봉의 현상으로 권취되어 성형건조된 보온용 카바의 진원상태가 불량하게 되고 무기섬유 제조공정중 섬유간 상호결합을 위하여 분사된 열경화성 섬유표면처리제의 경화를 위한 건조공정중 수축 혹은 변형을 일으켜 보온용 카바의 진직상태가 저하될 뿐만 아니라, 시공시에 보온용 카바가 배관 외주면을 감싸지 못하게 되어 일부가 노출되므로 보온효과가 저조하게 될 뿐만 아니라 제조된 보온용 카바는 한가지 규격에 배관에만 사용할 수 있으므로 호환성이 전무하여 생산 비축할 수 없고 주문에 따라 소요수량을 공급할 수밖에 없으므로 제품의 신속한 적기공급이 불가능하게 되고 매트를 심봉에 일일이 맡아 제조하여야 하는 것이므로 품질의 균일이 이루어지지 않는 문제점이 있는 것이다.In order to prevent energy loss by keeping various pipes in the related art, for this purpose, the mat on the blanket produced in the inorganic fiber manufacturing process is deployed on the conveyor belt, and transferred, but the mat is transferred on the conveyor belt to the mandrel using manpower or a machine. After winding, drying, and cutting to complete the pipe insulation cover, the rounded shape of the cover was dried by the phenomenon of core rods due to the nonuniformity of the collection density for each part, which is common in the inorganic fiber manufacturing process. It becomes poor and shrinks or deforms during the drying process for curing the thermosetting fiber surface treatment agent sprayed for inter-fiber inter-bonding during the inorganic fiber manufacturing process, thereby decreasing the straight state of the insulating cover, Can't cover the outer circumference of the pipe The exposed thermal cover is not only low, but the manufactured thermal cover can only be used for pipes in one standard, so there is no compatibility, so it is not possible to stockpile and supply the required quantity according to the order. And there is a problem that the uniformity of the quality is not made because the mat is to be entrusted to the mandrel one by one.

또한 직경이 큰 배관 보온용 카바는 그 수요량이 적으므로 업체에서 그에 맞는 별도의 카바를 생산치 않고 있어서 대개 슬라브상의 판재를 적절히 절단하여 외주에 씌워 시공하였던 것이며, 그 결과 시공시 외주에 각 판재의 모서리가 벌어져 이곳으로 열의 집중적인 이동이 이루어지므로 원하는 보온효과를 얻지 못하게 되었다.In addition, large diameter pipe insulation cover has a small demand, so the company did not produce a separate cover, so the slab plate was properly cut and covered with an outer circumference. Opening the corners, the heat is concentrated here, so the desired thermal effect is not achieved.

본 발명은 이상에서 팔표본 바와같은 종래의 배관 보온용 카바가 안고 있는 문제점들을 해결하기 위하여 제조되는 배관 보온용 카바의 두께를 임의로 정확하게 조정할 수 있게 하고 높은 진원도나 진적도를 유지할수 있게 함과 동시에 여러 가지 규격의 배관에 고루 사용할 수 있어서 많은 수요의 발생에도 규격이 다양한 제품을 신속하게 공급할 수 있으며, 대량 제조가 가능하여 생산성이 높은 배관 보온용 카바의 제조방법 및 제조장치를 제공함을 목적으로 하는 것이다.The present invention enables to accurately and accurately adjust the thickness of the pipe insulation cover to be manufactured in order to solve the problems of the conventional pipe insulation cover as shown in the arm sample above, while maintaining high roundness or integrity It can be used evenly in various sizes of pipes, so it is possible to supply various products quickly even if a lot of demands occur, and it is possible to manufacture a large quantity of pipes for the production of piping insulation cover with high productivity. will be.

이러한 본 발명의 목적은 배관 보온용 카바로써 필요한 두께보다 두껍게 된 건조, 성형, 재단이 끝단 소정밀도의 무기섬유 슬라브판체를 필요한 두께로 절단하면서 이면에 접착지를 접착하고 표면에 일정간격으로 V형홈을 삭설하여 줌으로써 달성될 수 있는 것으로, 이를 상세히 설명하면 다음과 같다.The purpose of the present invention is to cover the back of the adhesive fiber on the back and to form a V-shaped groove on the surface while cutting, cutting and cutting the inorganic fiber slab plate body having a predetermined density at the end of the drying, forming, and cutting, which is thicker than the required thickness as a pipe insulation cover. It can be achieved by cutting off, which will be described in detail as follows.

먼저 본 발명에서 적정두께 및 집면밀도를 가진 슬라브판체(1)는 건조성형 재단공정을 마친 완제춤을 의미하며 적정 두께란 용도에 따라 변화되는 보온용 카바의 두께 최고치보다 2배 이상 두터운 것을 말하며 집면밀도란 각종의 용도에 고루 사용될 수 있는 것을 의미하는 것이다.First, in the present invention, the slab plate body (1) having a proper thickness and surface density means a finished dance after finishing the drying molding process, and an appropriate thickness refers to a thickness two times thicker than the maximum thickness of the insulation cover that varies depending on the application. Surface density means that it can be used for various uses.

이어서 준비된 슬라브판체(1)를 콘베이어벨트(2)에 재치하여 이동시키면서 절단톱(3)에 의하여 절단하여 하방의 절단된 슬라브판체(1')의 두께가 현재 원하는 것으로 되도록 하고, 상반의 절단된 슬라브판체(1)는 들어내어 제거하도록 함으로써 하방의 전달된 슬라브판체(1')만이 콘베이어벨트(2)에 의하여 계속 이용되도록 하되, 이때 이송되는 슬라브판체(1')는 후술되는 V형홈간의 간격만큼 이송된 후 정지되는 동작을 반복하도록 콘베이어벨트(2)의 회동을 조절하여야 한다.Subsequently, the prepared slab plate body 1 is placed on the conveyor belt 2 and moved while being cut by the cutting saw 3 so that the thickness of the lower cut slab plate body 1 'is now desired, and the upper half of the slab plate body 1 is cut. The slab plate body 1 is lifted and removed so that only the lowered slab plate body 1 'is continuously used by the conveyor belt 2, but the slab plate body 1' to be transported is spaced between the V-shaped grooves to be described later. Rotation of the conveyor belt (2) is to be adjusted to repeat the stop operation after the transfer.

아울러, 이송되는 슬라브판체(1')의 상방에 분사장치에 의하여 접착제가 분사되는 것이며, 이러한 분사장치는 노즐(4) 및 펌프 그리고 접착제 저장탱크 및 자동제어기(도면에 도시하지 않음)로 구성되어 있는 것이어서, 후술되는 V형홈의 절삭작업 시행시에는 노즐(4)에 의한 접착제 분사가 증지되도록 되어 있는 것이다.In addition, the adhesive is injected by the injection device above the slab plate body (1 ') to be transported, this injection device is composed of a nozzle (4) and a pump, and an adhesive storage tank and an automatic controller (not shown) When the cutting operation of the V-shaped grooves to be described later is carried out, the adhesive spray by the nozzle 4 is to be deposited.

이어서 그 상부에 권취롤(5)로부터 접착지(6)가 공급되도록 되어 있으며, 적당한 압력을 가하여 접착상태를 개선하기 위한 압압롤(7) 및 안내롤(8)이 설치되어 있어서, 슬라브판체(1')이면에는 분사된 접착제에 의하여 접착지(6)가 접착되면서 V형홈 가공을 위해 이송되는 것이다.Subsequently, the adhesive paper 6 is supplied from the take-up roll 5 to an upper portion thereof, and a pressing roll 7 and a guide roll 8 are installed to apply an appropriate pressure to improve the adhesion state. 1 ') is to be transported for the V-shaped groove while the adhesive paper 6 is bonded by the sprayed adhesive.

즉, 콘베이어벨트(2)에 의하여 이송되는 슬라브판체(1')가 V형홈간의 간격만큼 이송된 후 정지한 다음 노즐(4)에 의한 접착제의 분사가 중지되도록 하며, 압압롤러(9),(10) 및 압압판(11)이 탄설된 압압수단과 하부의 받침대(13)(13')와의 상호작용에 따라 접착지(6)가 접착된 슬라브판체(1')가 안정된 상태로 고정되는 것이며, 이러한 상태에서 받침대(13)(13')사이의 공간으로 회전도(14)가 습동하면서 슬라브판체(1')의 표면에 V형홈(16)을 삭설하게 되는 것이고, 이러한 회전도(14)는 일예로서 모우터(M)에 의한 다수의 이빨을 가진 둥근 칼날로 된 것을 사용할 수 있는 것이며, 이 경우에는 실린더(15)에 의하여 모우터(M)을 습동시켜 줌으로써 회전도(14)가 받침대(13)(13')사이의 공간으로 습동되도록 할 수 있는 것이다.That is, the slab plate body 1 'conveyed by the conveyor belt 2 is stopped after being transferred by the interval between the V-shaped grooves, and then the injection of the adhesive by the nozzle 4 is stopped, and the pressure roller 9, ( 10) and the slab plate body 1 'on which the adhesive paper 6 is bonded is fixed in a stable state according to the interaction between the pressing means in which the pressing plate 11 is installed and the pedestal 13, 13' of the lower part. In this state, while the rotational speed 14 slides into the space between the pedestals 13 and 13 ', the V-shaped groove 16 is cut on the surface of the slab plate body 1'. As an example, a round blade having a plurality of teeth by the motor M may be used. In this case, the rotational speed 14 is supported by sliding the motor M by the cylinder 15. It can be slid into the space between (13) and (13 ').

이와같이 하여 습동 및 회전되는 회전도(14)에 의하여 V형홈(16)이 삭설된 후에는 콘베이이벨트(2)를 회동시킴과 동시에 노즐(4)에 의한 접착제의 분사가 이루어지도록하며, 이러한 상태로 슬라브판체(1')가 다시 V형홈(16)간의 간격만큼 이송된 후, 재차 콘베이어벨트(2)를 정지시키고, 노즐(4)에 의한 접착제의 분사를 중지시키며, 회전도(14)가 회전, 습동하면서 연속적을 V형홈(16)이 일정간격으로 삭설되고 이면에는 접착지(6)가 접착된 슬라브판체(1')가 되며, 배관의 직경에 따라 필요한 길이만큼씩 끊어낸 후 이로써 배관의 외주를 감싸고 보온테이프나 기타 결착띠등으로 고정시키면 시공이 완료될 수 있는 것이다.In this way, after the V-shaped groove 16 is removed by the rotational and sliding rotation 14, the conveyor belt 2 is rotated and the adhesive is sprayed by the nozzle 4, and in this state, After the furnace slab plate body 1 'is again transferred by the interval between the V-shaped grooves 16, the conveyor belt 2 is again stopped, and the injection of the adhesive by the nozzle 4 is stopped, and the rotational speed 14 is While rotating and sliding, the V-shaped groove 16 is continuously cut at regular intervals and the slab plate body 1 'is bonded to the backing paper 6 on the back side, and cut by the required length according to the diameter of the pipe. If you wrap the outer periphery and fix it with insulation tape or other binding band, the construction can be completed.

이때 제5도에 도시된 바와같이 V형홈(16)의 각도(θ')은 그림에서 보여주듯이 한번 접게되면 각도(θ)와 같이 각도가 없어지면서 배관(17)의 외주표면에 접촉이 되며 이때 θ₁+θ의 각도는 θ가 없어져 θ₁이 되고 또다시 θ만큼 접게되면 θ₂가 되게 되는 것이다.At this time, as shown in FIG. 5, the angle θ 'of the V-shaped groove 16 is folded as shown in the figure, and when the angle θ is lost, the angle θ disappears as shown in the angle θ. The angle of θ ₁ + θ becomes θ ₁ due to the disappearance of θ and becomes θ ₂ when folded by θ again.

이러한 작업을 반복하여 시공하면 정밀하게 감싸진 상태로 시공을 완료할 수 있게 되는 것이며, 이러한 V형홈의 각도와 그 개수오의 관계식을 유도하여 보면 다음과 같다.Repeated construction of this work will be able to complete the construction in a precisely wrapped state, and if you derive the relationship between the angle of the V-shaped groove and its number is as follows.

가 되고 그러므로 θn이 0°가 되도록 하면 시공이 완료되는 것이므로 θ'=360°n이 되는 것이다.(여기서 θ'은 V형홈(16)의 각도이고, n은 V형홈(16)의 총 갯수이다.)Therefore, when θn is 0 °, construction is completed, so θ '= 360 ° n. (Where θ' is the angle of the V-shaped groove 16, and n is the total number of V-shaped grooves 16). .)

또한, 이러한 본 발명에서도 소정의 두께로 전달하여 들어낸 상방의 절단된 슬라브판체(1)는 그 두께가 원하는 목적 두께보다 아직도 두꺼우므로 다시 콘베이어벨트(2)위에 올려주어 절단톱(3)을 통과하도록 하면 목적두께로 절단된 상태가 되어 전술한 바와같은 과정으로 배관 보온용 카바를 생산할 수 있게 되는 것이다.In addition, in the present invention, the upper cut slab plate body 1 that has been delivered to a predetermined thickness and lifted up is placed on the conveyor belt 2 again through the cutting saw 3 because its thickness is still thicker than the desired target thickness. If it is to be cut to the target thickness is to be able to produce a pipe insulation cover for the process as described above.

이와같이 함으로써 소정의 정확한 두께를 가진 보온용 카바를 생산하면서도 절단으로 인한 그 손실량은 매우 적게되는 것이며, 그 손실량을 모아 두었다가 무기섬유 제조공정에 투입하여 재생할 수 있음은 물론이다.By doing this, the loss of cutting due to the cutting of the insulation cover having a predetermined thickness is very small, and the amount of the loss can be collected and recycled into the inorganic fiber manufacturing process.

또한 본 발명에서의 절단톱(3)의 일예로서 이음매가 없는 환형으로 되어 있어서 교환이 용이한 형태의 것을 보이고 있으며, 이는 콘베이어벨트(2) 상부면과의 간격을 조절할 수 있도록 하여야 하는 것이며, 또한 회전도(14)에 의한 V형홈(16)이 형성작업중 발생되는 분진은 포집후드(18)에 의하여 집진장치(도면에 도시하지 않음)로 흡인되는 것이어서 작업환경이 악화되는 일은 없게 된다.In addition, as an example of the cutting saw 3 in the present invention is shown in the form of an easy to replace the round shape, which is to be able to adjust the distance from the upper surface of the conveyor belt (2), The dust generated during the forming operation of the V-shaped groove 16 by the rotational degree 14 is sucked into the dust collector (not shown in the drawing) by the collecting hood 18 so that the working environment is not deteriorated.

아울러 본 발명에서는 여러 가지 규격으로 회전도(14)를 다수 준비하여 필요에 따라 교체시켜 가면서 사용함으로써 V형홈(16)의 각도를 임의 조절하여 설정된 배관규격에 다각형의 변의 수를 조절하여 적절하게 사용할 수 있게 되는 것이다.In addition, in the present invention, by adjusting the number of the rotation 14 to various standards and using as needed, by changing the angle of the V-shaped groove (16) arbitrarily adjust the number of sides of the polygon to the set pipe size to use properly It will be possible.

아울러 배관 보온용 카바는 그 용도에 따라 특정한 밀도가 지정되는 경우가 있으며, 이 경우에는 주문에 따라 특정한 밀도를 갖는 슬라브판체를 선택하면 되므로 다양한 밀도의 제품생산이 가능하게 되는 것이며, 이상에서 살펴본 바와같은 본 발명에 의한 보온용 카바는 그 밀도가 두께 편차가 거의 없이 이미 건조성형재단된 슬라브판체를 가공하여 보온용 카바로 사용하는 것이므로 진원도 및 진직도가 대단히 우수하게 되는 것이고, 따라서 시공후 배관 외주면을 완전히 감싸게 되어 보온성능이 탁월하게 되는 것이며, 연속적인 생산이 가능하고, 본 발명에 의하여 제조된 보온용 카바는 배관의 직경에 따라 임의 절단하여 사용하면 되므로 특정 규격의 갑작스런 대량 주문에도 신속한 적기공급이 가능하게 되는 것이면서도 신속한 시공이 가능하게 되는 등의 유용한 효과가 있다.In addition, the pipe insulation cover may be specified a specific density according to the purpose, in this case, since the slab plate body having a specific density can be selected according to the order, it is possible to produce products of various densities. Insulation cover according to the present invention is to use the slab plate body is already dry-molded slab with a density of almost no thickness variation, so that the roundness and straightness is very excellent, so the pipe outer peripheral surface after construction It is completely wrapped to be excellent thermal insulation performance, continuous production is possible, and the thermal insulation cover manufactured by the present invention can be used by cutting arbitrarily according to the diameter of the pipe, so that timely supply even for sudden large orders of a certain standard It becomes possible, but it is possible to construct quickly Has a beneficial effect, such as.

Claims

The slab plate body 1 'is cut to a certain thickness while transferring the slab plate body 1' to obtain a slab plate body 1 'having a desired thickness, sprayed with adhesive on the back side thereof, and then the adhesive is attached and the transfer is stopped to fix the position. A method for manufacturing a pipe insulation cover for releasing the fixed position after cutting and transporting the slab plate body (1 ') to continuously repeat the above-described process.

A cutting saw 3 is installed above the conveyor belt 2, and an adhesive spray nozzle 4, a winding roll 5, a guide roll 8 is installed at the rear of the conveyor belt 2, and is connected to the rear end of the conveyor belt 2. There is a pressing means in which the pressing rollers 9, 10 and the pressing plate 11 are installed, and below the pedestal 13, 13 'is installed but separated and rotated in the gap (14). Apparatus for manufacturing a pipe insulation cover that is configured to slide.