Claims (10)
a) 비스페놀A타입의 에폭시 수지에 아크릴산을 부가 반응시킨 후 분자내에 형성된 하이드록실그룹과 일반식(2)로 표시되는 편말단 에폭시 변성 실록산 폴리머를 산 촉매로 반응하여 제조한 일반식 (1)로 표시되는 실란변성 에폭시아크릴레이트 올리고머 5~90중량%; b) 반응성모너머 5~80중량%; c) 광개시제 0.1~20중량%; d) 레벨링제 0~10중량%; e) 소량의 첨가제:로 구성되는 자외선 경화형 도료 조성물.a) After addition reaction of acrylic acid to a bisphenol A type epoxy resin, general formula (1) prepared by reacting a hydroxyl group formed in a molecule with a single-terminal epoxy modified siloxane polymer represented by formula (2) with an acid catalyst 5 to 90% by weight of the silane-modified epoxy acrylate oligomer represented; b) 5 to 80% by weight of reactive monomer; c) 0.1-20% by weight of photoinitiator; d) 0 to 10% by weight leveling agent; e) UV curable coating composition consisting of a small amount of additives:
여기서, R1은 수소원자 또는 메틸기, R2은 카본수가 3~8인 불포화된 아크릴로일옥시 또는 메타크릴로옥시기, R3은 실록산화합물이고, n은 0~20인 정수이다.Wherein R 1 is a hydrogen atom or a methyl group, R 2 is an unsaturated acryloyloxy or methacrylooxy group having 3 to 8 carbon atoms, R 3 is a siloxane compound, and n is an integer of 0 to 20.
여기서, R4는 메틸기 또는 페닐기이고, m은 1~40 사이의 정수이다.Here, R <4> is a methyl group or a phenyl group, m is an integer between 1-40.
제1항에 있어서, 실란변성 에폭시 아크릴레이트 올리고머가 에폭시아크릴레이트 1당량에 대하여 에폭시 변성 실록산 폴리머 0.1~6당량비로 반응시킨 자외선 경화형 도료 조성물.The ultraviolet curable coating composition according to claim 1, wherein the silane-modified epoxy acrylate oligomer is reacted with 0.1 to 6 equivalents of epoxy-modified siloxane polymer with respect to 1 equivalent of epoxy acrylate.
제1항에 있어서, 일반식 (2)의 폴리머가 편말단 에폭시 변성 디메틸실록산폴리머, 편말단 에폭시변성페닐 메틸실록산폴리머, 편말단 에폭시 변성디페닐실록산폴리머에서 선택된 1종인 자외선 경화형 도료 조성물.The ultraviolet curable coating composition according to claim 1, wherein the polymer of the general formula (2) is one selected from a single-ended epoxy-modified dimethylsiloxane polymer, a single-ended epoxy-modified phenyl methylsiloxane polymer, and a single-ended epoxy-modified diphenylsiloxane polymer.
제1항 내지 제3항 중 어느 한 항에 있어서, 편말단 에폭시 변성 실록산 폴리머의 분자량이 250~3000인 자외선 경화형 도료 조성물.The ultraviolet curable coating composition according to any one of claims 1 to 3, wherein the single-ended epoxy-modified siloxane polymer has a molecular weight of 250 to 3,000.
제1항에 있어서, 반응성모노모가 단관능 모노머로서 2-에틸헥실아크릴레이트, 옥틸데실아크릴레이트, 이소데실아크릴레이트, 트리데실메타크릴레이트, 2-페녹시에틸아크릴레이트, 노닐페놀에톡시레이크모노아크릴레이트, 테트라하이드로퍼푸릴레이트, 에톡시에틸아크릴레이트, 하이드록시에틸아크릴레이트, 하이드록시에틸메타아크릴레이트, 하이드록시프로필아크릴레이트, 하이드록시프로필메타아크릴레이트, 하이드록시부틸아크릴레이트, 하이드록시부틸메타아크릴레이트에서 선택된 1종인 자외선 경화형 도료 조성물.The method of claim 1, wherein the reactive mono-monomer is 2-ethylhexyl acrylate, octyldecyl acrylate, isodecyl acrylate, tridecyl methacrylate, 2-phenoxyethyl acrylate, nonyl phenol ethoxy lake as monofunctional monomer Monoacrylate, tetrahydroperfuryl, ethoxyethyl acrylate, hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, hydroxybutyl acrylate, hydroxy UV curable coating composition selected from oxybutyl methacrylate.
제1항에 있어서, 반응성모노머가 2관능모노모로서, 1,3-부탄디올디아크릴레이트,, 1,4-부탄디올디아크릴레이트, 1,6-헥산디올디아크릴레이트, 디에틸렌글리콜디아크릴레이트, 트리에틸렌글리콜디메타크릴레이트, 네오펜틸글리콜디아크릴레이트, 에틸렌글리콜디메타크릴레이트, 테트라에틸렌글리콜디메타크리레이트, 폴리에틸렌글리콜디메타크릴레이트, 트리프로필렌글리콜디아크릴레이트, 1,6-헥산디올디아크릴레이트에서 선택된 1종인 자외선 경화형 도료조성물.The method of claim 1, wherein the reactive monomer is a bifunctional monomer, 1,3-butanediol diacrylate, 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, diethylene glycol diacrylate , Triethylene glycol dimethacrylate, neopentyl glycol diacrylate, ethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol dimethacrylate, tripropylene glycol diacrylate, 1,6-hexane UV curable paint composition selected from diol diacrylate.
제1항에 있어서, 반응성모노머가 3관능 모노머로서 트리메틸올프로판트리아크릴레이트, 트리메틸올프로판트리메타크릴레이트, 펜타에리스리톨트리아크릴레이트, 글리시딜펜타트리아크릴레이트, 글리시딜펜타트리아크릴레이트에서 선택된 1종인 자외선 경화형 도료 조성물.The method according to claim 1, wherein the reactive monomer is selected from trimethylolpropanetriacrylate, trimethylolpropanetrimethacrylate, pentaerythritoltriacrylate, glycidylpentatriacrylate, and glycidylpentatriacrylate as trifunctional monomers. UV curable coating composition selected.
제1항에 있어서, 반응성모노머가 다관능 모노모로서 1,6-산디올디아크릴레이트, 트리프로필렌글리콜디아크릴레이트, 트리메틸올프로판트리아크릴레이트 또는 펜타에리스리톨테트라아크릴레이트에서 선택된 1종인 자외선 경화성 도료 조성물.The UV curable coating composition according to claim 1, wherein the reactive monomer is one selected from 1,6-acid diol diacrylate, tripropylene glycol diacrylate, trimethylolpropane triacrylate, or pentaerythritol tetraacrylate as a polyfunctional monomole. .
제1항에 있어서, 광개시제가 벤조페논계, 벤질디메딜케탈계, 아세토페논계, 안트라퀴논제, 티옥소잔톤계에서 선택된 1종인 자외선 경화형 도료조성물.The ultraviolet curable coating composition according to claim 1, wherein the photoinitiator is one selected from benzophenone series, benzyldimedyl ketal series, acetophenone series, anthraquinones, and thioxoxanthone series.
제1항의 자외선 경화형 도료 조성물을 코팅한 플라스틱, 금속 및 비금속 성형품.Plastic, metal and nonmetallic molded article coated with the UV-curable coating composition of claim 1.