KR940021745A - Method of manufacturing wear resistant steel sheet - Google Patents
Method of manufacturing wear resistant steel sheet Download PDFInfo
- Publication number
- KR940021745A KR940021745A KR1019930005319A KR930005319A KR940021745A KR 940021745 A KR940021745 A KR 940021745A KR 1019930005319 A KR1019930005319 A KR 1019930005319A KR 930005319 A KR930005319 A KR 930005319A KR 940021745 A KR940021745 A KR 940021745A
- Authority
- KR
- South Korea
- Prior art keywords
- temperature
- steel sheet
- resistant steel
- wear
- temperature range
- Prior art date
Abstract
본 발명은 토목, 건축 및 광산 등의 각종 산업기계에 적용될 수 있는 내마용 강판의 제조방법에 관한 것으로서, 본 발명은 저합금강 슬라브를 1150-1300℃의 온도범위로 가열한 후, 마무리 압연온도를 900℃ 이하로 하고 900℃ 이하인 온도에서의 전체압하율을 30% 이상으로 하여 열간압연을 실시한 다음, 120초 이내에서 상온까지 7℃/sec 이하인 온도에서의 전체압하율을 30% 이상으로 하여 열간압연을 실시한 다음, 120초 이내에서 상온까지 7℃/sec 이상의 평균냉각속도로 담금질한 후 200-350℃의 온도범위에서 뜨임처리하여 내마모용 강판을 제조하는 방법을 그 요지로 한다.The present invention relates to a method for producing a wear-resistant steel sheet that can be applied to various industrial machinery such as civil engineering, construction and mining, the present invention is to heat the low-alloy steel slab to a temperature range of 1150-1300 ℃, and then finish rolling temperature Hot rolling is carried out at a temperature of 900 ° C. or lower and a total reduction rate at a temperature of 900 ° C. or lower at 30% or more. After rolling, it is quenched at an average cooling rate of 7 ° C./sec or more from 120 seconds to room temperature, and then tempered at a temperature range of 200-350 ° C. to produce a wear-resistant steel sheet.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.
제1도는 마무리 압연온도 및 압하율에 따른 경도값 변화를 나타내는 그래프이다.1 is a graph showing the change in hardness value according to the finish rolling temperature and the reduction ratio.
Claims (1)