KR940011506A - 내후성 내충격성 무광택 열가소성 수지 제조방법 - Google Patents
내후성 내충격성 무광택 열가소성 수지 제조방법 Download PDFInfo
- Publication number
- KR940011506A KR940011506A KR1019920021499A KR920021499A KR940011506A KR 940011506 A KR940011506 A KR 940011506A KR 1019920021499 A KR1019920021499 A KR 1019920021499A KR 920021499 A KR920021499 A KR 920021499A KR 940011506 A KR940011506 A KR 940011506A
- Authority
- KR
- South Korea
- Prior art keywords
- parts
- weight
- monomer
- thermoplastic resin
- acrylonitrile
- Prior art date
Abstract
본 발명은 내후성이 우수한 내충격성 무광택 아크릴계고무-스티렌-아크릴로니트릴 수지의 제조방법에 관한 것이다.
본 발명은 2단계 공정을 거쳐 제조된 가교 아크릴계 고무 라텍스 10 내지 60중량부(a)에 스티렌 33 내지 14중량부(b), 아크릴로니트릴 14 내지 4중량부(c)를 그라프트 중합시킨 1차 그라프트 중합체에, 스티렌 34.5 내지 16중량부(b′)와, 아크릴로니트릴 11.5 내지 6중량부(c′)를 프리에멀젼 상태로 만든 후 연속 투입하여 2차 그라프트 중합시키는 것을 특징으로 한다.
본 발명의 방법에 의하여 제조된 수지는 내후성과 무광택성이 요구되는 전기, 전자제품, 자동차용 부품, 농기구등 일광노출이 많은 외장 부품 등에 사용될 수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (4)
- 2단계 공정을 거쳐 제조된 가교 아크릴계 고무 라텍스 10 내지 60중량부(a)에 스티렌 33 내지 14중량부(b), 아크릴로니트릴 14 내지 4중량부(c)를 그라프트 중합시킨 1차 그라프트 중합체에, 스티렌 34.5 내지 16중량부(b′)와, 아크릴로니트릴 11.5 내지 6중량부(c′)를 프리에멀젼 상태로 만든 후 연속 투입하여 2차 그라프트 중합시키는 것을 특징으로 하는 열가소성 수지의 제조방법.
- 제1항에 있어서, 가교 아크릴계 고무 라텍스(a)의 제조방법이 하기 2단계 공정을 가지는 것을 특징으로 하는 열가소성 수지의 제조방법.1) 제1단계탄소수 1-13개의 알킬기를 가지는 아크릴산 에스테르 단량체 30∼70부와, 상기 단량체와 공중합 가능한 2개 이상의 관능기를 가지고 있는 다관능성 모노머 0.05∼1.5부와, 음이온성 유화제 1.0∼3.5부와, 이온교환수의 존재하에 중합 개시제 0.1∼0.45부를 혼합, 중합하여 입자크기 0.1∼0.15 마이크론인 고무질 라텍스를 제조하는 공정.2) 제2단계제1단계에서 제조된 고무질 라텍스에 아크릴산 에스테르 단량체 단량체 70∼30부, 상기 단량체와 공중합 가능한 2개 이상의 관능기를 가지고 있는 다관능성 모노머 0.5∼2.8부, 음이온성 유화제 0.4∼2.0부와 이온교환수를 교반 가능한 용기에 넣고, 프리에멀젼 상태로 만든 후 연속투입하여 입자크기를 0.15∼1.2 마이크론으로 성장시켜 최종 고무질 라텍스를 제조하는 공정.
- 제1항에 있어서, 제2단계의 최종 고무질 라텍스의 평균 입도가 0.47 내지 0.54 마이크론인 것을 특징으로 하는 열가소성 수지의 제조방법.
- 제2항에 있어서, 제2단계의 최종 고무질 라텍스의 겔 함유량이 70∼95중량%인 것을 특징으로 하는 열가소성 수지의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.