Abstract

pouring evenly the kneaded mixture composed of 70 % of silicone (R.T.V), 20 % of pigment, 0.5 % of surfactant, 0.1 % of straight chain alkyl benzene, 0.1 % of alpha olefin, 0.2 % of anioic alcohol, 0.1 % of nonionic fatty oil and 3 % of water into the depressed grooves of the known frame; heating at 100 deg.C under a low pressure for 10 sec. after bonding the fabric on the frame to join and cure the fabric; and seaparating the fabric from the frame. The label made by this method retains durable and original form even after laundering, steaming or ironing because of the heat-resistance and soft touch of silicone when it is applied to a garment.

Description

Manufacturing method of label which bonded silicon of cloth

첨부도면은 본 발명의 제조공정 설명도.The accompanying drawings are explanatory views of the manufacturing process of the present invention.

본 발명은 실리콘(R.T.V.)을 주재로 하여 천에 접착하는 라벨의 제조방법에 관한 것이다.The present invention relates to a method for producing a label that is adhered to a cloth based on silicone (R.T.V.).

종래 P.V.C.를 주재로 하여 천에 접착하는 라벨의 제조법은 이미 공지된 바이다.The manufacturing method of the label which adheres to a cloth based on conventional P.V.C. is already known.

이러한 종래의 방법은 공개특허번호 87-10472호에 기재된 바와 같이, P.V.C.분말에 안정제(DOP)와 안료를 적당량 첨가하여 반죽한 반죽물을 도형 또는 문자가 새겨진 형틀의 요홈에 주입한 다음 상온에서 24시간 정도 경과시켜 형틀의 요홈에 주입된 P.V.C. 반죽물이 경화되면 그 위에 나일론 직물과 같이 열에 용착되는 천을 그 위에 대고 고주파접착하여 떼어내면 경화된 P.V.C.와 천이 접착되어 빠져나오므로 천상에 형틀에 새겨진 도형 또는 문자가 깨끗하게 돌출형태로 나타나는 것이었다.This conventional method is, as described in Korean Patent No. 87-10472, injecting a dough kneaded by adding an appropriate amount of stabilizer (DOP) and a pigment to a PVC powder into a groove of a figure or letter engraved mold, and then at room temperature 24 PVC injected into the mold groove after the passage of time When the dough was cured, the fabric welded on the heat, such as nylon fabric, was applied on it, and the high-frequency adhesive was removed to remove the hardened P.V.C. and the fabric.

이와 같이 P.V.C.로 제조되는 라벨은 나일론섬유직물과 같은 열용융성 천을 반듯이 사용하여야 하고 P.V.C. 자체도 열에 잘 녹기 때문에 P.V.C.로 제조된 라벨을 의류에 부착할 경우 다림질을 할 수 없고 또, P.V.C.는 경질이기 때문에 촉감이 불량할 뿐만 아니라 잘 떨어지는 결점이 있으며 제조시에 고주파 접착과정에서 천의 섬유질이 녹아 붙어 표면이 거칠어져서 양질의 제품을 기대할 수 없는 결점이 있었다.As such, the labels made of P.V.C. must be used with a heat-melting cloth such as nylon fiber fabric. Because it is also very soluble in heat, it can't be ironed when a label made of PVC is attached to clothing, and because PVC is hard, it is not only poor in touch but also has a flaw that can fall off. There was a defect that this melted surface was rough and the quality product could not be expected.

이상과 같은 종래 P.V.C. 라벨이 가지고 있는 문제점을 해결하기 위하여 오랜기간 연구끝에 내열성 실리콘(R.T.V.)을 섬유질에 구애없이 모두 견고하게 접착 성형할 수 있는 제조법을 창출하므로서 실리콘 자체가 가지는 부드러운 촉감과 내열성을 부여하여 의류에 붙여서 세탁하거나 삶거나 다림질을 하여도 라벨의 변형없이 오랜기간 원형을 유지할 수 있는 의류용 라벨을 제공할 수 있다.The conventional P.V.C. as described above. In order to solve the problem of the label, after a long period of research, we created a manufacturing method that can heat-resistant silicone (RTV) to be firmly bonded and formed regardless of fibers. It is possible to provide a label for clothing that can maintain its original shape for a long time without deformation of the label even if it is cooked, boiled or ironed.

이를 제조공정별로 상술하면 다음과 같다.This will be described in detail for each manufacturing process as follows.

[제1공정][Step 1]

직물 표면에 섬유가 솟아나 있는 천의 일측면에 재봉하기 좋게 얇은 비닐지를 접착하거나 가열시 의류에 열접착되는 접착매체층을 형성하여 이 라벨의 기지를 준비한다. 이때의 천의 섬유질은 내열성 섬유질이 좋으며 기모형태가 짧고 많을수록 좋다.The base of this label is prepared by gluing thin plastic paper to sew on one side of the fabric with the fibers on the fabric surface or by forming an adhesive medium layer that is heat-bonded to the garment when heated. At this time, the fiber of the fabric is good heat-resistant fiber, the shorter the brushed form, the more the better.

[제2공정][Step 2]

임의의 도형 또는 문자가 새겨진 형틀은 첨부도면에는 하나의 형틀만이 도시되어 있지만 넓은 형틀에 동일 라벨도형 또는 문자를 일정한 간격으로 다수 배설하면 일시에 많은 량의 라벨을 얻을 수 있다.Only one template is shown in the attached drawing of an arbitrary figure or letter, but a large amount of labels can be obtained at a time by disposing a large number of identical label shapes or characters at regular intervals in a wide template.

[제3공정][Step 3]

실리콘(R.T.V.) 70부70 parts of silicon (R.T.V.)

안료 20부20 parts pigment

계면활성제 0.5부0.5 parts surfactant

직쇄알킬벤젠계 0.1부0.1 parts of linear alkylbenzene system

알파올레핀계 0.1부Alphaolefin 0.1 part

알코올(음이온) 0.2부Alcohol (anion) 0.2 part

지방실계(비이온) 0.1부Aliphatic system (non-ion) 0.1 part

수분 3부Moisture part 3

이를 교반하여 물은 실리콘 반죽물을 얻는다.By stirring this, the water obtains a silicone dough.

위의 혼합비는 색상, 촉감의 요구에 따라 다소 변동될 수 있다.The above mixing ratio may vary slightly depending on the needs of color and touch.

[제4공정][Step 4]

제2공정의 형틀위에 새겨진 도형 또는 문자의 요홈에만 실리콘 반죽물을 주입하고 그 위에 천의 기모면을 대고 가열 압착한다.The silicone paste is injected only into the grooves of figures or letters engraved on the mold of the second process, and the surface is pressed with a raised surface of the fabric.

이때의 압력은 천이 형틀면에 밀착될 정도의 약한 압력이며 가열온도는 100℃에서 약 10초간 수행된다.At this time, the pressure is weak enough to be in close contact with the transition mold surface, and the heating temperature is performed at 100 ° C. for about 10 seconds.

가열압착 과정에서 일어나는 현상은 천의 섬유가닥이 실리콘 반죽물속에 매입되면서 단시간 내에 경화되며 실리콘 반죽물 속에 함유된 수분이 완전 증발하면서 형틀로부터의 이형을 용이하게 한다.The phenomenon occurring during the hot pressing process is to cure in a short time as the fiber strands of the cloth is embedded in the silicone dough, and the moisture contained in the silicone dough is evaporated to facilitate the release from the mold.

[제5공정][Step 5]

제4공정에서 접착된 천을 형틀에서 떼어내면 천에 실리콘층의 도형 또는 문자가 붙어나오며 기모부분이 눌린 부분을 접착테이프로 붙였다 떼었다 하면서 다시 원상복귀시켜 미려한 표면을 만든다.If the fabric bonded in the fourth step is removed from the mold, the figure or character of the silicon layer is attached to the fabric, and the part where the brushed part is pressed is attached with the adhesive tape.

이상과 같이 본 발명은 실리콘에 계면활성제와 수분등을 혼합하여 이 형성이 양호한 반죽물을 얻어 내열성 천의 기모를 반죽물에 심어서 접착하므로서 의류에 부착하여 세탁, 다림질을 할때에 라벨의 변형이 없고, 실리콘 자체의 부드러운 촉감으로 보다 진보된 고급 제품의 라벨을 제조하는 것이다.As described above, the present invention obtains a good dough by mixing a surfactant and moisture in silicone, and obtains a good dough, and attaches the brush of the heat-resistant cloth to the dough, and then adheres to the garment so as to deform the label when washing and ironing. It is a product that makes a label of more advanced products with the soft touch of silicone itself.

또한, 제4공정에서의 열접착에 의한 경화접착은 대량의 라벨을 단시간내에 양산할 수 있어 제품가를 저렴하게 하는 장점도 가진다.In addition, the curing adhesion by thermal bonding in the fourth step has the advantage of mass production of a large number of labels in a short time to reduce the product price.

Claims

As described above, 70 parts of silicone (RTV), 20 parts of pigment, 0.5 part of surfactant, 0.1 part of linear alkylbenzene type, 0.1 part of alpha olefin type, 0.2 part of alcohol, 0.1 part of aliphatic type, and 3 parts of moisture Injecting water evenly into the groove of a well-known mold, apply the cloth to it, and heat the temperature of 100 ° C. for 10 seconds at acupressure for about 10 seconds to bond and cure to separate the cloth and the mold, characterized in that the silicone-bonded label of the fabric .