KR930000579B1

KR930000579B1 - Shadow mask support structure for flat color picture tube and manufacturing method

Info

Publication number: KR930000579B1
Application number: KR1019900014741A
Authority: KR
Inventors: 이재호
Original assignee: 삼성전관 주식회사; 김정배
Priority date: 1990-09-14
Filing date: 1990-09-14
Publication date: 1993-01-25
Also published as: KR920007052A

Abstract

The shadow mask support for a plane color braun tube is manufactured by (a) welding an aluminium tilled steel-shadow mask material to a perlite cast iron-frame composed of 3.56 % C, 2.7 % Si, 0.39 % Mn and residual Fe, and (b) heating the welded frame in the heating furnace at a rate of 70-100 deg.C/min and a peak temp. of 500-800 deg.C, and then rapidly cooling it at a rate of 300-400 deg.C/min to grow it and to bond the mask material to it.

Description

Shadow mask support for flat color CRT and manufacturing method

제1도는 본 발명의 새도우마스크의 적용한 평면 칼라 브라운관의 단면도.1 is a cross-sectional view of a flat color CRT applied to the shadow mask of the present invention.

제2도는 본 발명의 주요부 새도우마스크 지지체를 나타내는 사시도.2 is a perspective view showing the main portion shadow mask support of the present invention.

제3도는 본 발명 새도우마스크 지지체를 구성하는 주철의 온도와 반복회수에 따른 신장률을 나타내는 그래프.3 is a graph showing the elongation rate according to the temperature and the repetition frequency of the cast iron constituting the shadow mask support of the present invention.

제4도는 종래의 평면 칼라 브라운관의 단면 구조도.4 is a cross-sectional structural view of a conventional flat color CRT.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1 : 페이스 2 : 외주벽1: face 2: outer wall

3 : 스터드핀 4 : 새도우마스크소재3: stud pin 4: shadow mask material

5 : 프레임5: frame

본 발명은 음극선관용 새도우마스크 지지체에 관한 것으로, 특히 주철의 열 성장성을 이용하여 새도우마스크를 인장시켜 장착하는 평면 칼라 브라운관용 새도우마스크 지지체와 그 제조방법에 관한 것이다.The present invention relates to a shadow mask support for a cathode ray tube, and more particularly to a shadow mask support for a flat color CRT tube and a method for manufacturing the shadow mask support using the thermal growth of cast iron.

칼라 브라운관에서 새도우마스크는 전자총에서 주사되는 전자비임이 R,G,B형광체 상에 정확하게 랜딩될 수 있게 제어하여 주는 주요부품의 하나로서,평면 칼라 브라운관에서는 제4도에 도시한 바와같이 새도우 마스크(8)는 적당한 기계장치에 의해 상하 좌우로 약 3mm가량 늘어나게 인장된 상태로 Q레일(R)에 선용접되고, 전기한 Q레일 (R)은 프리트를 접착제로 하여 평판상의 페이스(F)에 접합 고정된 구조로 되어 있다.In the color CRT, the shadow mask is one of the main components that controls the electron beam injected from the electron gun to be accurately landed on the R, G, and B phosphors. In the plane CRT, the shadow mask is shown in FIG. 8) is pre-welded to the Q rail (R) in a stretched state of about 3mm in up, down, left, and right by a suitable mechanism, and the Q rail (R), which is described above, is bonded to the flat face (F) using frit as an adhesive It is a fixed structure.

여기서 새도우마스크(S)가 인장된 상태에서 선용접되는 이유는, 전자비임이 새도우마스크(S)에 충돌하여 발생하는 열로 인해 팽창하는 소위 도우밍현상이 생기지 않게 하기 위함이다.Here, the reason that the shadow mask S is pre-welded in the tensioned state is to prevent the so-called domming phenomenon from expanding due to the heat generated by the electron beam colliding with the shadow mask S.

그런데, 상술한 평면 칼라 브라운관의 구조는 Q레일(R)이 일단 페이스(F)에 부착되면, 그 위치조정이 거의 불가능하기 때문에 위치정밀도를 ±10㎛이내로 해야하는 까다로운 면이 있고, 또 Q레일(R)은 페이스(F)와 거의 같은 열팽창계수를 갖는 값비싼 카펜터 금속이나,426합금과 같은 고가의 재료를 사용해야하므로 제조 원가가 비싸게 되는 문제를 안고 있다.By the way, the structure of the flat color CRT described above has a difficult aspect that the positioning accuracy should be within ± 10 μm because the positioning of the Q rail R once attached to the face F is almost impossible, and the Q rail ( R) has a problem in that the manufacturing cost is high because expensive Carpenter metals having a coefficient of thermal expansion almost equal to the face F or expensive materials such as 426 alloy must be used.

본 발명은 상기한 문제점을 해소하고자, 종래의 곡면형 칼라 브라운관에서 볼 수 있는 새도우마스크 지지체와 유사한 방식으로 설치될 수 있는 평면형 칼라 브라운관용 새도우마스크 지지체와 그 제조방법을 제공하여, 오차범위를 넓히고 값싼 주철재의 활용을 도모함에 있다.The present invention to solve the above problems, by providing a shadow mask support for the flat type color tube can be installed in a similar manner to the shadow mask support that can be seen in the conventional curved color tube, and widening the error range It is aimed at utilizing inexpensive cast iron materials.

상기 목적에 따라 본 발명은 C 3.56%, Si 2.70%, Mn 0.39%, 기타 불가피한 성분 및 철로 이루어진 퍼얼라이트계 주철로 된 프레임에 알루미늄킬드강으로 된 새도우마스크 소재를 선용접하고, 전기한 프레임을 열성장시켜서 새도우마스크소재가 인장되게 한 새도우마스크 지지체를 제안하고, 또 이와같은 새도우마스크 지지체를 제조하기에 적합한 방법으로서, 알루미늄 킬드강제 새도우마스크소재가 선용접된 주철재 프레임을 가열로에서 분당 70~100℃의 승온속도로 피이크온도 500~800℃로 가열하고, 분당 300~400℃의 강온속도로 급속냉각시켜서 주철재 프레임이 열성장되게 하여 알루미늄 킬드강제 새도우마스크 소재가 인장되게 하는 평면 킬라 브라운관용 새도우마스크 지지체의 제조방법을 제안한다.According to the above object, the present invention pre-welds the shadow mask material of aluminum-kilted steel to a frame made of C.56%, Si 2.70%, Mn 0.39%, other inevitable components and iron-based cast iron, and heats the electric frame. Suggested shadow mask support by growing the shadow mask material to grow, and also suitable for manufacturing such shadow mask support, cast iron frame pre-welded aluminum-kilted steel shadow mask material in the furnace 70 ~ For the flat Kila Brown tube, which is heated to a peak temperature of 500 ~ 800 ℃ at 100 ℃ heating rate and rapidly cooled at a temperature of 300 ~ 400 ℃ per minute, the cast iron frame is thermally grown to tension the aluminum-kilted shadow mask material. We propose a method of preparing a shadow mask support.

주철은 특정의 온도로 가열과 급냉을 반복할 때, 가열에 의해 팽창된 신장율이 급냉에 의한 수축율보다 높게 나타나서, 처음의 길이보다 신장되는 열성장성을 가지고 있는 물질의 하나로 알려져 있으며, 제3도는 온도와 반복회수에 따른 열성장성의 관계를 나타낸다.Cast iron is known to be one of the materials that have a thermal growth property that extends more than the initial length because the elongation of expansion caused by heating is higher than the shrinkage rate due to rapid cooling when heating and quenching are repeated at a specific temperature. And the relationship of thermal growth according to the number of iterations.

이 그래프를 보아 알 수 있는 바와같이, 주철은 가열-급냉의 반복으로 1%의 신장률을 보이고, 30회를 상한점로 반복을 거듭할 수록 신장율이 높아지는 것으로 나타난다.As can be seen from this graph, the cast iron shows an elongation rate of 1% by heating and quenching repetition, and the elongation rate increases as the repetition is repeated 30 times as the upper limit.

본 발명을 이러한 주철의 열성장성을 평면 칼라 브라운관용 새도우마스크 지지체에 교묘히 적용하려는 것으로서, 이를 첨부도면에 따라 바람직한 실시예로 설명하면 다음과 같다.The present invention intends to artfully apply the thermal growth of the cast iron to the shadow mask support for the flat color CRT, which will be described as a preferred embodiment according to the accompanying drawings.

제1도는 본 발명 새도우마스크 지지체가 적용된 평면 칼라 브라운관의 단면도로서, 페이스(1)은 통상의 곡면형 브라운관과 마찬가지로 외주면이 광축방향으로 약간 연장된 외부벽(2)를 가진 형태로 되어 있고, 이 외주벽(2)의 내측에는 스터드핀(3)이 부착되어 새도우마스크소재(4)가 선용접된 프레임(5)를 현수할 수 있게 되어 있다.1 is a cross-sectional view of a flat color CRT tube to which the present invention shadowmask support is applied, and the face 1 has a shape having an outer wall 2 whose outer circumferential surface extends slightly in the optical axis direction as in a conventional curved CRT. The stud pin 3 is attached to the inner side of the outer circumferential wall 2 to suspend the frame 5 on which the shadow mask material 4 is pre-welded.

본 발명의 주요부로 되는 새도우마스크 지지체는 제2도의 소디와 같이 주철제 프레임(5)에 알루미늄킬드 강제 새도우마스크소재(4)를 펼친 상태로 선용접하여 놓은 것으로서, 이 프레임(5)의 주위에는 상기한 외주벽(2)의 스터드핀(3)에 현수되기 위한 스프링(6)이 소정부위에 부착되어 있다.The shadow mask supporter, which is the main part of the present invention, is pre-welded in a state where the aluminum-killed shadow mask material 4 is unfolded in the cast iron frame 5 as shown in FIG. A spring 6 for hanging on the stud pin 3 of the outer circumferential wall 2 is attached to a predetermined portion.

이러한 구성은 외관상 종래의 곡면형 새도우마스크 지지체와 동일하게 보이지만, 본 발명은 새도우마스크소재(4)가 선용접된 프레임(5)를 가열로에 넣고, 가열과 급냉을 반복하여 열성장시키므로써 프레임(5)상에 새도우마스크소재(4)가 인장된 상태로 부착되게 하는 점에 그 특징이 있다.This configuration looks the same as the conventional curved shadow mask supporter in appearance, but the present invention is to put the frame (5) in which the shadow mask material (4) is pre-welded in a heating furnace, the frame by heating and quenching repeatedly to heat growth (5) is characterized in that the shadow mask material 4 is attached in a tensioned state.

다음에 주철제 프레임(5)를 열성장시키는 공정을 설명한다.Next, a process of thermally growing the cast iron frame 5 will be described.

주철재 프레임(5)에 알루미늄킬드강제새도우마스크소재(4)를 자연스럽게 펼쳐 선용접하여 부착시킨 다음 이를 가열로에 넣고 분당 70~100℃의 승온속도로, 피이크온도 500~800℃가 되게 가열시키고, 즉시 분300~400℃의 강온속도로 급냉시키면 프레임(5)는 가열과 반복회수에 따라 최소 0.01에서 최대 0.014의 신장률로 성장하게 된다.Aluminum-kilted steel shadow mask material (4) is naturally spread on the cast iron frame (5), and then welded to the cast iron frame (5). Immediately quenching at a temperature-falling rate of 300-400 ° C., the frame 5 grows at an elongation rate of at least 0.01 up to 0.014 depending on heating and repetition times.

한편, 평면형 칼라 브라운관에서 새도우마스크소재(4)의 필요 인장량은 3mm이므로 15인치용 새도우마스크 지지체를 예로들면, 프레임(5)의 규격이 가로 세로 330× 250곱으로 되어 가열 냉각을 1회 반복하면 2.5∼4.6mm 더 신장된 결과를 얻을 수 있다.On the other hand, since the required amount of tension of the shadow mask material 4 in the flat color CRT is 3 mm, the shadow mask support for 15 inches is taken as an example. The size of the frame 5 is 330 × 250 times, and the heating and cooling are repeated once. If it is, the result can be extended by 2.5 to 4.6 mm.

따라서 본 발명에서 새도우마스크소재(4)는 프레임(5)의 열성장량만큼 강제인장되기 때문에 동작시에 도우밍을 일으킬 염려가 없게 되는 것이다.Therefore, in the present invention, since the shadow mask material 4 is forcibly tensioned by the amount of thermal growth of the frame 5, there is no fear of causing domming during operation.

이상과 같이 본 발명은 주철제프레임을 열성장시켜서 새도우마스크소재를 강제인장된 상태로 유지되게 함으로써, 이 새도우마스크 지지체를 통상의 곡면형 칼라 브라운관에서와 같이 페이스의 외주벽에 고착된 스터드핀으로 현수할 수 있게 조립이 간편해지고 값싼 재료를 활용할 수 있는 등의 이점을 나타내는 것이다.As described above, the present invention heat-grows the cast iron frame so that the shadow mask material is kept in the tensioned state, and thus the shadow mask support is suspended with stud pins fixed to the outer peripheral wall of the face as in a conventional curved color CRT. This makes it easier to assemble and use cheaper materials.

Claims

C 3.56%, Si 2.70%, Mn 0.39% Other unavoidable components and the iron-ride cast iron frame is welded with a shadow mask material of aluminum-kilted steel and heat-grown the electric frame to make the shadow mask material tensile. Shadowmask support for flat color CRTs.

2. The shadow mask support for flat color CRT tubes according to claim 1, wherein the support has a suspension spring attached to a predetermined peripheral portion thereof.

Cast-iron frame with pre-welded aluminum-kilted steel shadow mask material is heated in a heating furnace at a heating rate of 70 to 100 ° C per minute, to a peak temperature of 500 to 800 ° C, and rapidly cooled at a temperature of 300 to 400 ° C per minute A method for producing a shadow mask support for a flat color CRT tube, which causes the thermal growth to cause the aluminum-kilted shadow mask material to be tensioned.