KR870002080B1 - Permanent pleat processing method of animal fabric

Info

Publication number: KR870002080B1
Application number: KR1019850007169A
Authority: KR
Inventors: 노희연
Original assignee: 주식회사 일신산업; 유열
Priority date: 1985-09-28
Filing date: 1985-09-28
Publication date: 1987-12-03
Also published as: KR870003261A

Abstract

In processing animal fiber fabrics for permanent pleating and for reinforcing clothe forms, a composition of L-systein hydrochloride 0.1-6% and stabilized citrates 0.1-6% is dissolved in water or alcohol or solvent with or without addition of thioglycolic acid 0.01-6% and is adjusted to pH 4-9. The prepared composition is sprayed on the subject fabric to apply steam press or steam iron to press-set pleats or forms. The preparation presents no health hazard and is long preservative for ready use without particular equipments.

Description

Permanent pleat processing of animal fibers

본 발명은 동물성 섬유 이를테면 모직물이나 견직물등과 같은 순모 직물에 영구 주름(pleat)을 부여할 수 있게한 동물성 섬유의 영구 주름 가공방법 및 그의 조성물에 관한 것이다.FIELD OF THE INVENTION The present invention relates to a method for permanently wrinkling animal fibers and to compositions thereof which makes it possible to impart permanent pleats to woolen fabrics such as wool or silk fabrics.

구체적으로는 동물성 섬유의 뛰어난 성질을 손상 시킴이 없이, 그 특성에 변화를 갖게하므로서 간단하게 주름을 형성하여 착용시에 있어서나, 물에 젖거나 또 세탁을 행할지라도 변형이 되지 않는 영구적인 주름을 손쉽게 부여할 수 있게한 신규의 조성물과 이 조성물에 의해서 이루어지는 가공방법에 관한 것이다.Specifically, it is possible to form permanent wrinkles by changing the properties of the fibers without damaging the excellent properties of the animal fibers, so that the permanent wrinkles that are not deformed at the time of wearing, even when wet or washed with water are washed. It relates to a novel composition which can be easily given and a processing method made of the composition.

주지하는 바와같이, 양모 섬유는 특이한 탄성을 갖고 있어, 순모직물에 인위적인 구김을 행한다 할지라도 그대로 복원되어 주름잡기가 매우 어려움은 잘 알려진 사실이다.As is well known, wool fibers have an unusual elasticity, and even though artificial wrinkles are performed on the wool fabric, it is well known that the wool fibers are restored and are very difficult to wrinkle.

즉, 순모의복 예컨데, 신사바지나 슬랙스(Slacks)등의 주름 또는 스커트 등의 주름등에 있어서, 일반적으로 스티임 프레스(Steam press)와 같은 가공방법으로 주름을 행하고 있으나, 착용하고 있으면, 서서히 퍼지거나 물에 젖으면 금방 퍼져버리는 원인으로 되고 있다.That is, in woolen clothes, for example, wrinkles such as men's pants or slacks or wrinkles such as skirts, the wrinkles are generally processed by a processing method such as steam press, but if worn, they gradually spread or water When it gets wet, it becomes the cause which spreads out quickly.

종전의 기술에 의하면, 내구적인 주름을 잡는 가공법이라고 하여, 오스트렐리아의 연방산업 연구 기구(C.S.I.R.O)가 연구 개발한 시로 셋트(Si-Ro-Set) 가공법이 문헌에서 알려진바 있다.According to the conventional technique, the Si-Ro-Set processing method researched and developed by the Federal Industrial Research Organization of Australia (C.S.I.R.O), known as the durable creasing processing method, is known from the literature.

이 시로 셋트 가공 방법에 관하여, 국제양모 사무국에서 발행한 "순모 바지에 내구적인 주름을 만드는 시로셋트 가공 MEAS-Steam press법" (Clothing Information No. 15 1980. 5)의 기재 내용에 의하면 바지, 스커트 등에 열프레스로 예비구김을 행하고 이에 2~4%의 티오글리 콜산과 암모니아수의 혼합 수용액을 처리물(원단)중량의 40%정도 분무한뒤, 호프만 프레스기에서 18.16㎏/㎠이상의 수증기를 20초 동안 통과시켜 20초 동안 방치한 다음, 진공 펌프로 외기를 뽑아내어 냉각하므로서 구김(주름)을 행하는 것이라고 밝히고 있다.According to the description of the method of processing the shiro set, according to the description of the "Siloset processing MEAS-Steam press method for making durable wrinkles on wool trousers" issued by the International Wool Secretariat (Clothing Information No. 15 1980. 5) After pre-wrinkling with a heat press on the back, spray a mixed aqueous solution of 2-4% thioglycolic acid and ammonia water about 40% of the weight of the treated material (fabric), and steam over 18.16㎏ / ㎠ for 20 seconds in a Hoffman press. After allowing it to pass through for 20 seconds, it is revealed that wrinkles are performed by removing the outside air with a vacuum pump and cooling.

그러나 이 방법은 가공 조건이 매우 까다로워 고도의 숙련 기술을 요할뿐 아니라 일정한 시설이 없는 소기업 특히 일반 대중들이 간편하게 활용할 수 없는 결점이 있어, 현재 국내의 사용에 있어서는 전무한 실정에 있다.However, this method is very demanding in terms of processing conditions and requires not only highly skilled skills, but also has a shortcoming that is not readily available to small enterprises without a certain facility, especially the general public.

이 방법에서는 양모 섬유의 내부에 화학적, 물리적인 변화를 가하여 의복류에 주름을 유지하게 하는 성질을 부여하는 것으로서 드라이 클라닝 후에 다시 주름을 잡을 필요가 없다고 밝히고 있어 매우 바람직한 방법이기는 하나,This method imparts chemical and physical changes to the inside of the wool fiber to impart wrinkles to the garments, and it is a very desirable method because it does not need to be wrinkled again after dry cleaning.

첫째, 상기 셋트(Set) 제인 혼합 수용액중 티오글리 콜산은 철, 동등의 금속을 부식시키는 인체 유해물질 일뿐 아니라 용액이 접촉하는 의복의 면직물 부분(예 : 주머니, 심재, 라이닝 등)이 쉽게 손상되고,First, thioglycolic acid in the mixed solution of Set Jane is not only a human harmful substance that corrodes iron and equivalent metals, but also a cotton fabric portion (for example, a pocket, a core material, a lining, etc.) of the garment contacted with the solution is easily damaged. ,

둘째, 상기 셋트제인 혼합 수용액을 처리물(원단) 중량의 40% 정도 분무하여야 하므로 셋트제의 소비량이 매우 많아, 소규모 량의 작업시에는 경제적으로 불리한 점이 있으며,Second, since the mixed aqueous solution of the set agent should be sprayed about 40% of the weight of the treated material (fabric), the consumption of the set agent is very large, and there is an economic disadvantage in the case of a small amount of work.

셋째, 프레스 작업을 할때, 내구적인 주름을 부여하고자 하는 부위를 정확하게 프레스 하도록 주의하지 않으면 안될뿐 아니라 물이나 세재용액 속에서 심하게 비비든지 하면 펠트 수축이 발생하여 세탁은 반드시 드라이 클라닝에 국한되는 불편이 뒤따르고,Third, when press work, care must be taken to accurately press the area to be endured, and if it is rubbed heavily in water or detergent solution, felt shrinkage occurs and washing is limited to dry cleaning. Discomfort follows,

넷째, 특히, 콘프렛샤의 압축공기를 1.2~1.5㎏/㎝로 감압 분무해야 하는등의 소정의 대단위적 설비를 요하므로, 소규모 특히 일반 가정들에서는 활용할 수 없는 결점등이 있다.Fourth, in particular, because it requires a certain large-scale equipment, such as pressure-reduced compressed air of compressed air at 1.2 ~ 1.5kg / cm, there are disadvantages that can not be utilized in small, especially ordinary households.

본 발명자는, 이같은 시로 셋트 가공법에 관하여 예의 연구 검토한 결과, 모든 동물성 모(毛)에서 필수아미노산을 축출할 수 있다는 사실에 주목하여, 울(wool) 및 동물성 원단에 필요한 영양소를 공급하면 양모의 특이한 탄성에 변화를 부여할 수 있음을 발견하고, 본 발명을 완성하기에 이르렀다.As a result of earnestly researching and studying such a silo set processing method, the present inventors pay attention to the fact that essential amino acids can be extracted from all animal hairs. It has been found that a change can be given to the specific elasticity, and the present invention has been completed.

따라서, 본 발명은, 소기업은 물론 일반 서민층에서도, 간단한 스티임프레스 가공법등(아이론 등)에 의해 동물성 섬유에 영구적인 주름을 부여할 수 있는 신규의 조성물을 제공하고자 함에 주요 목적이 있다.Therefore, the present invention has a main object to provide a novel composition capable of imparting permanent wrinkles to animal fibers by a simple steam press method or the like (iron, etc.) as well as small businesses.

본 발명의 다른 목적은, 본 발명에 의한 조성물을 이용하여 간편, 용이하게 영구 주름을 부여하거나 형(型)의 지속적인 보강이 가능하게 한 모직물들의 가공 방법에 있다.Another object of the present invention is a method for processing woolen fabrics which allows the use of the composition according to the present invention to simply and easily impart permanent pleats or enable continuous reinforcement of a mold.

본 발명의 기타 목적과 장점은 이하의 명세서에서 명백히 설명되고 그 실시예에서 확실히 알 수 있을 것이다.Other objects and advantages of the invention will be apparent from the following description, and will be apparent from the examples.

본 발명의 특징적인 요소로서는, 고도의 안정성과 보관성을 가짐과 동시에 소기업 특히 일반 대중들이 간편, 용이하게 활용할 수 있을 뿐만 아니라 세탁성이 우수하고 영구적인 주름 및 형(型)의 보강을 지속적으로 유지하면서 인체무해성을 상승효과로 나타낼 수 있게한 것이다.As a characteristic element of the present invention, it has a high degree of stability and storage, and can be easily and easily utilized by small businesses, especially the general public, and has excellent launderability and permanent reinforcement of permanent wrinkles and shapes. While maintaining the harmless human body can be shown as a synergistic effect.

이같은 본 발명을 구체적으로 설명하면 다음과 같다.The present invention will be described in detail as follows.

실크(本絹) 및 울(wool)등 동물성 섬유 제품에 영구 주름을 부여하거나 상의류의 형(型) 보강 및 모직물을 가공함에 있어서, 엘 시스테인 염산염의 엘시스틴류 0.1~6%, 안정제 구연산류 0.1~6%의 혼합물을 물 및 알콜 또는 용제에 용해하고 이에 티오글리콜산 0.01~6%를 첨가하거나 또는 첨가하지 않은 혼합물을 pH4~9로 조절하여 본 발명의 조성물로 한다.When adding permanent wrinkles to animal textile products such as silk and wool, or reinforcing the shape of upper garments and processing wool, 0.1 to 6% of elcistine of stabilized hydrochloride, stabilizer citric acid 0.1 A mixture of ˜6% is dissolved in water and an alcohol or a solvent, and 0.01-6% of thioglycolic acid is added thereto or the mixture is not added to adjust the pH of the composition to pH 4-9.

이같은 본 발명에 있어서, 엘시스테인 염산염(HClH O)을 단독으로 한 시료 (1)일 경우 그 사용 결과는 표 Ⅰ과 같았다.In the present invention as described above, in the case of the sample (1) using only elcysteine hydrochloride (HClH O), the results of the use were as shown in Table I.

[표 Ⅰ]TABLE I

위 표 Ⅰ에서와 같이 엘시스테인 염산염을 단독으로 한 시료(1)을 물에 용해하여 사용한 결과는 비교적 양호하나 pH가 1이상이므로 산(酸)에 약한 면직물(주머니, 심재, 라이닝 등)에 접촉되어 고열 가압시에 쉽게 손상되는 취약점이 있다. 동시에, 시료 (1)을 밀폐되지 않은 용기에 저장할 경우 2시간 정도후부터 침전물이 생겨 이후, 분사, 사용이 힘들게 된다.As shown in Table I above, the result of dissolving the sample (1) using solely the cysteine hydrochloride in water was relatively good, but the pH was above 1, so it was in contact with a cotton fabric (pouch, core, lining, etc.) which is weak to acid. There is a vulnerability that is easily damaged during high temperature pressurization. At the same time, when the sample (1) is stored in an unsealed container, a precipitate is formed after about 2 hours, and then, spraying and use are difficult.

따라서, 엘시스테인 염삼염에 구연산 20%중량(엘시스테인比)을 가하여 시료 (2)를 조성한 것을 사용하였을 때는 그 처리 결과가 상기 표Ⅰ와 같이 비교적 양호 하였으나 pH가 1이상이므로 산에 약한 면직물과의 관계에서 취약점이 있는 반면, 밀폐되지 않은 용기에 장기 보관하더라도 침전물이 생기지 않아 분무사용이 용이함을 알 수 있었다.Therefore, when the sample (2) was prepared by adding 20% weight of citric acid (elcistein ratio) to the elcysteine salt salt, the treatment result was relatively good as shown in Table I. However, since the pH was 1 or more, On the other hand, there is a weak point, but even if it is stored for a long time in an unsealed container, it is easy to use spray because no sediment is formed.

또, 시료(2)의 조성물에 수산화나트륨, 암모니아수등으로 중화하여 시료(3)을 형성하였을 경우 그 사용 결과의 처리물에 대한 주름의 개각 각도는 각%마다 10도 정도 열리는 우수한 효과를 나타내었으나 보관시에 있어 24시간 밀폐되지 않은 상태에서는 앙금이 생겨 장기 보관이 불가능함을 알 수 있었고, 또한 모직물에 분사하여 자연 건조하였을때 오염현상이 나타남을 발견하였다.In addition, when the sample 3 was formed by neutralizing the composition of the sample 2 with sodium hydroxide, ammonia water or the like, the opening angle of the wrinkles on the treated product of the use resulted in about 10 degrees for each%. During storage, it was found that sediment was not possible for long-term storage because it was not sealed for 24 hours. Also, it was found that contamination occurred when sprinkled with natural wool.

그리하여, 본 발명에서는 단기 사용을 목적으로한 조성물로서는 상기의 시료 (1)~(3)들을 채택한다.Therefore, in this invention, said sample (1)-(3) is employ | adopted as a composition for the short term use.

바람직하게는, 엘시스테인 비(比)의 구연산 20%, 엘시스테인 0.5~4%, 티오글리콜산 20%(엘시스테인比)의 물질들을 충분히 용해하여 수산화 나트륨(NaOH)로 pH4~9로 조절한 시료(4)의 조성물을 저장성과 안정성이 높은 상품으로 사용한다. 이때의 시료(4)는 무색무취에서 연분홍의 색깔로 변화된 액상의 물질이다.Preferably, a solution of citric acid 20%, elcysteine 0.5-4% and thioglycolic acid 20% (cysteine ratio) of elcysteine ratio is sufficiently dissolved and adjusted to pH 4-9 with sodium hydroxide (NaOH). The composition of the sample 4 is used as a product with high storage stability. At this time, the sample 4 is a liquid substance changed from colorless odorless to pale pink color.

이와같은 본 발명에 있어서의 "엘시스테인" 물질은, 순모직물등에 영구주름을 부여함에 있어 양모의 주조성물인 게라틴 성분중의 "시스틴"과 결합하여 Set효과를 얻는 것으로 추정된다.Such "elcysteine" material in the present invention is assumed to obtain a Set effect by combining with "cystine" in the gelatin component, which is a cast product of wool, in imparting permanent wrinkles to a wool fabric or the like.

즉 시스틴 1-S-S-1의 유황( S )분자와 ( S )분자 사이에 엘시스테인으로 환원하면 1-S-

-S-1 수소(H)의 분자가 시스틴 분자를 절단(혹은 과잉 시스틴 분자가 절단)되고, 이때 모직물의 형 및 주름을 구성하면서, 가열 가압하면 물이 증열되면서 산소(O) 분자를 주어 H₂O가 빠져 나오면서 산화되어 성형된 상태

로 분자 배열이 고정되는 것으로 생각된다In other words, if it is reduced to elcysteine between sulfur (S) and (S) molecules of cystine 1-SS-1, 1-S-

-S-1 Hydrogen (H) molecule cuts cystine molecule (or excess cystine molecule is cut), and forms the form and wrinkle of wool, and heat pressurizes water to give oxygen (O) molecule to give H ₂ O is oxidized and molded

It is believed that the molecular arrangement is fixed

이와같은 본 발명에 의한 시료는, 일반 가정에서 부터 세탁소, 봉제공장에 이르기 까지 다양하게 사용할 수 있다.Such a sample according to the present invention can be used in various ways from a general household to a laundry and a sewing factory.

가) 가공조건A) Processing condition

모직물 실크등의 원단에 디자인상 필요 부위에 선주름 및 성형을 하고 그 부위에 시료를 분무하여 스티임 프레스 및 아이론으로 가압 건조하면 주름 및 성형부위가 영구 보형된다.Wrinkles and moldings are required on the design-needed part of the fabric such as woolen silk, and the sample is sprayed onto the parts by press-drying with a steam press and iron to permanently shape the wrinkles and the molded part.

나) 변퇴색과 오염기타 부작용B) discoloration and other side effects

농도가 강하면 변퇴색 위험이 있으나 본 시료 단일로 사용시 변퇴색 및 오염의 부작용이 없는 완전한 중성이며 인체에 아무런 해가 없다.If the concentration is strong, there is a risk of discoloration, but when used as a single sample, it is completely neutral without any side effects of discoloration and contamination, and there is no harm to the human body.

다) 냄 새C) smell

본 시료를 모직물에 분무할때는 전혀 냄새가 없고 건조시 모직물에서 나는 황( S ) 분자의 취기를 약간 느낄 수 있다. 인체에는 아무런 해가 없다.When spraying the sample on the woolen fabric, there is no smell at all, and the smell of sulfur (S) molecules from the woolen cloth can be felt slightly. There is no harm to the human body.

라) 촉 감D) touch

촉감변화는 보통 동물성 섬유와 같게 쾌적하다. 부드럽게 처리하고자 할 경우는 본 발명에 의한 시료의 pH를 7~8정도 조절하고, 까실까실하고 힘이 있게 하기 위해서는 pH 4~5정도 조절함이 좋다.Tactile changes are usually as comfortable as animal fibers. If you want to treat gently, the pH of the sample according to the present invention is adjusted to about 7 to 8, in order to be tight and strong, it is good to adjust the pH 4 to 5 or so.

본 발명에 의한 조성물로 15온스 100%을 개버딘(Wool Gaberdine)에 부여한 영구 주름에 대한 시험결과는 아래 표 Ⅱ와 같았다.Test results for permanent wrinkles given 15oz 100% gabardine (Wool Gaberdine) with the composition according to the present invention are shown in Table II below.

[표 Ⅱ]TABLE II

* 1% 중성세제 비누물에 6시간 이상 침수 후의 측정도임.* Measured after immersion in 1% neutral detergent soap water for 6 hours or more.

위 표에서와 같이 2%)이상의 사용은 전연 필요 없음을 알 수 있다.As shown in the above table, the use of more than 2%) does not require leading edge.

또, 본 발명에 의한 조성물로 8온스 및 14온스의 100%을 개버딘의 영구 주름을 성형한 시험결과는 아래 표 Ⅲ와 같았다.In addition, the test results of molding the permanent wrinkles of gabardine from 100% of 8oz and 14oz with the composition according to the present invention was as Table III below.

[표 Ⅲ]TABLE III

* 1% 중성세제에 6시간 이상 침수후 침수 상태에서 개각 각도를 측정한 것임.* Opening angle was measured after immersion in 1% neutral detergent for more than 6 hours.

위 표에서와 같이 3% 이상 사용할 때는 오염의 우려성은 있으나 원단에 미치는 인열, 인장강도 및 촉감의 변화는 전연 없으며, 통기성, 흡습성 및 보온성에도 전연 영향을 미치지 않음이 확인되었다.When using more than 3% as shown in the table above, there is a risk of contamination, but there is no change in tearing, tensile strength and touch on the fabric, and it has been confirmed that there is no influence on breathability, hygroscopicity and heat retention.

그리고, 위 표들에 있어서의 시험구로 사용한 100% Wool Gabardine은 양모중 가장 치밀한 조직이며 봉재시 성형하기가 가장 어려웁고 오염도가 높은 대상물을 선택하였다.In addition, 100% Wool Gabardine, which was used as the test tool in the above tables, selected the most dense structure of wool and the most difficult and highly contaminated object to be molded when sewing.

상술과 같이, 본 발명에 의한 조성물은 자연 용기속에서 장기간 보관할 수 있는 상품으로서 인체에 무해하고 타섬유에 손상이 없음이 물론, 오염, 변퇴등의 부작용도 전연 없음이 확인 되었다.As described above, it was confirmed that the composition according to the present invention is a product that can be stored in a natural container for a long time, harmless to the human body, and there is no damage to other fibers, as well as no side effects such as contamination and change.

또한, 본 발명 조성물에 의하여 부여된 주름이 잘못되었을 경우, 시료를 다시 분사하여 다시 주름을 사으면 되므로 사용상 극히 편리한 점이 있다.In addition, when the wrinkles imparted by the composition of the present invention is wrong, it is very convenient in use since the sample is sprayed again to buy the wrinkles again.

Claims

In the permanent reinforcement of animal products, such as silk and wool, or the reinforcement of woolen fabrics, or spraying a composition based on elcysteine hydrochloride, it is applied to steam presses, steam irons and irons. Permanent wrinkle processing method of animal fibers, characterized in that the pressure drying (Set).

In performing permanent reinforcement of silk and wool products or mold reinforcement or wool processing, a mixture of 0.1 to 6% of elcysteine and 0.01 to 6% of stabilizer citric acid is dissolved in water and alcohol or solvent. 0.01 to 6% of thioglycolic acid is added or not added to the composition for permanent share processing of animal fibers, characterized in that by adjusting the pH to 4-9.