Abstract

The nail lacquer is consisted of fine glass powder 85, diatomite 10 and glycerine 5 wt.% and makes the nails to have glistening luster by polishing them with lacquer-smeared leather. The external form of each glass powder shown through a magnifier is sharp broken piece so the mixt. of lacquer composition makes the surface texture of the nail brilliantly.

Description

Friction Varnish Composition for Nails

본 발명은 인체의 케라틴성 조직인 손톱이 항시 대기(大氣)에 노출되면서 광택성(光澤性)이 유지될 수 있게 한 손톱용 마찰식 광택제 조성물에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a rubbing varnish composition for nails in which nails, which are keratinous tissues of the human body, are kept exposed to the atmosphere at all times.

종래 인체의 손톱에 사용 되어온 광택제로는 광택 반사성(光澤反射性)이나 속건 도포식(速乾塗布式) 등의 액체를 사용하여 왔으나, 이 도포식 액체를 손톱 위에 도포하면 손톱 부위는 완전 기밀성(完全氣密'性) 피막(被膜)이 형성되여 피부 조직이 대기(大氣)로부터 완전 차단(遮斷)되게 하는 것이어서 이를 장기간 사용할 시는 손톱의 노출성(露出性)을 유지해야 되는 인체조직이 생기를 상실하게 되어 흑색으로 변색되는 등의 비위생적인 결점을 초래하였다.Conventional varnishes used in human nails have been used liquids such as gloss reflectivity or quick-drying coating. However, when the coating liquid is applied onto the nail, the nail area is completely airtight (完全氣密 'sexual coating is formed, so that the skin tissue is completely blocked from the air, so long-term use of human tissue that should maintain the nail's exposure Loss of vitality resulted in unsanitary defects such as discoloration in black.

본 발명은 손톱의 광택제에 관하여, 종래와 같은 도포식 광택액체를 사용하는 것이 아니고 본 발명과 같은 마찰식 광택제를 사용되게 하므로서 전기한 바와 같은 손톱광택제에 관한 결점을 제거되게 한 발명에 관한 것으로서, 이하 본 발명의 요지를 상세히 설명하면 다음과 같다.The present invention relates to a nail polish, which does not use a conventional coating varnish liquid, but to use the friction varnish as described in the present invention to remove the defects related to the nail polish as described above, Hereinafter, the gist of the present invention will be described in detail.

유리의 미세분말 85%(중량비), 규조토 10%(중량비), 그리세링 5%(중량비)을 골고루 혼합하여 본 발명의 손톱용 마찰식 광택제를 조성한다.Fine powder 85% (weight ratio), diatomaceous earth 10% (weight ratio), and 5% (weight ratio) of the grinding ring are evenly mixed to form a rubbing varnish for nails of the present invention.

본 발명에 의한 유리가루의 미세분말은 그 입자를 매우 미세하게 분쇄하여, 먼지 상태로 형성하는 것이어서, 그 입자의 개별적인 형태를 높은 비율로 확대하여 보면, 그 외형은 모두 예리한 미세각이 인체 손톱의 표면 조직을 광택되게 하는 것이고, 이와 같은 유리의 미세물에 규조토(硅燥土) 및 그리세링을 혼합하면, 규조토는 그 입자(粒子)가 역시 매우 미세한 것이어서, 미세 유리분말 사이에 혼합 충전됨과 동시에 그리세링과 더불어 미세유리 분말을 규조토와 같이 습윤 상태로 만들어 광택제로 사용되게 하는 성질을 갖게끔 조성물로 조성하는 것이다.The fine powder of the glass powder according to the present invention is that the particles are pulverized very finely and are formed in a dust state, and when the individual forms of the particles are enlarged at a high rate, the appearance is sharp all the fine angles of the human nail. When the surface structure is polished, and when diatomaceous earth and glacering are mixed with such glass fine particles, the diatomaceous earth is also very fine particles, which are mixed and filled between the fine glass powders. Together with the griesling, the microglass powder is formulated into a composition such that the microglass powder is wetted, such as diatomaceous earth, to be used as a polishing agent.

상기와 같은 본 발명의 광택제를 사용할 시는 먼저 손톱의 부위를 깨끗하게 한 다음 본 발명에 의한 광택제를 가죽의 내면에 약간량만을 묻혀서 손톱 위에 조금만 문질러도 손톱들의 표면은 곧 아름다운 광택이 발생하게 되는 것이다.When using the varnish of the present invention as described above, first cleans the area of the nail and then the surface of the nails will soon generate a beautiful luster even if only a small amount of the varnish according to the present invention on the inner surface of the leather rubbed on the nail .

본 발명의 실시는 인체의 손톱을 종래와 같은 기밀성 피막을 조성하여 왔던 도포식 광택제와는 달리 그 결점에서 탈피하여 용이한 방법으로 손톱의 광택을 가벼운 마찰로 유지되게 함과 동시 손톱부위 인체의 조직을 항시 위생적으로 대기에 의한 것이어서 인체조직의 보건에 유용하게 사용되는 것이다.In the practice of the present invention, unlike the applied varnish that has been forming a conventional hermetic coating on the nails of the human body to avoid the defects to maintain the luster of the nails in a light manner in an easy way and at the same time the tissue of the human body Since it is always hygienically caused by the atmosphere, it is useful for the health of human tissues.

Claims

Friction varnish composition for powdery nails, characterized in that the mixture of glass fine powder 85%, diatomaceous earth 10%, griesling 5%, weight ratio.