KR820000418B1

KR820000418B1 - Fishing rod made of fiber reinforced synthetic resin

Info

Publication number: KR820000418B1
Application number: KR7702317A
Authority: KR
Inventors: 겐이찌 히구찌
Original assignee: 후지이 도시다카; 후지이 하루유끼; 겐이찌 히구찌
Priority date: 1977-10-04
Filing date: 1977-10-04
Publication date: 1982-04-01

Abstract

This invented patent is related to the fishing rod made of synthetic resin, especially for the improvement of fishing rod made of fiber re-inforced synthetic resin. The fishing rod is composed of multiple layer made from fiber-reinforced artificial resin, and is set porous layer between inner most layer and outer most layer.

Description

Synthetic fishing rod

제1도는 본 발명의 1예를 보인 적층구조를 보인 투시도.1 is a perspective view showing a laminated structure showing an example of the present invention.

제2도는 공극보유층의 1예를 보인 확대도.2 is an enlarged view showing one example of the void retaining layer.

제3도는 종래의 낚시대에 있어서 굴곡모멘트가 작용한 경우의 설명도.3 is an explanatory diagram when the bending moment acts in the conventional fishing rod.

제4도는 본 발명에 의한 낚시대의 굴곡모멘트가 작용한 경우의 설명도.4 is an explanatory diagram when the bending moment of the fishing rod according to the present invention is applied.

본 발명은 합성수지제 낚시대, 특히 섬유강화 합성수지제 낚시대의 개량에 관한 것이다.The present invention relates to an improvement in synthetic fishing rods, in particular fiber reinforced synthetic fishing rods.

섬유 강화 합성수지제 낚시대는 종래부터 공지이나, 이런 공지의 낚시대는 테이퍼(taper)상태의 심금(芯金) 외면에 수지를 함침시킨 직포를 여러층 밀착시켜 감아 붙인 뒤, 수지를 경화하여 심금을 빼내어 제조하는 것이 보통이다.Fiber-reinforced synthetic resin fishing rods have been known in the past, but such known fishing rods have a tapered outer surface of tapered impregnated woven fabric in close contact with multiple layers, and then the resin is cured to remove the core. It is common to manufacture.

따라서 종래와 같은 낚시대는 적층된 관재료에 외부힘이 작용하면 낚시대 본체의 흐트러짐이 비교적 작은 동안은 단면은 원형을 유지하고, 둥근관으로서의 단면계수를 유지하고 있으나, 외부힘이 증대하여 굴곡의 흐트러짐이 점차 크게 되는데 따라 단면은 제3도에 도시하는 바와 같이 둥근원으로부터 타원형에 가까운 형태로 변화되어 단면계수를 감소한다. 뿐만 아니라, 단면형상의 변형에 따라 발생하는 접선방향의 인장응력을 일으켜 낚시대가 쪼개지기 쉬운 결점이 있다.Therefore, the conventional fishing rod maintains a circular cross section and maintains a cross-sectional coefficient as a round pipe while the fishing rod main body is relatively small when the external force is applied to the laminated tubing material. As this gradually increases, the cross section changes from a round circle to an elliptical shape as shown in FIG. 3, thereby decreasing the cross-sectional coefficient. In addition, there is a drawback that the fishing rod is easily broken due to tangential tensile stress caused by deformation of the cross-sectional shape.

때문에 섬유방향이 낚시대관 본체와 평행이 아니고 각도를 가지고 있는 섬유들로된 부가적인 직포층을 사용하거나 특히 강화된 직포의 층을 여유있게 사용하는 것도 실시되고 있으나, 이런 경우는 낚시대의 중량을 증가시키는 결점이 있으므로 좋지가 못한 것이다.For this reason, it is also possible to use an additional layer of woven fabric with a fiber direction whose angle is not parallel to the body of the fishing canal, or in particular using a layer of reinforced woven fabric. It is not good because there is a fault.

본 발명은 이와 같은 종래의 결점을 제거하고, 경량으로 강도가 높은 성능을 갖는 낚시대를 제공하고자 하는 것이다. 즉 본 발명은 섬유강화 인조 수지로된 다수의 층으로 구성되며, 이들층의 가장 안쪽층과 가장 바깥층 사이에 공극(空隙)보유층을 설치한 것을 특징으로 하는 낚시대를 제공하는 것이다.The present invention is to eliminate the above-mentioned drawbacks, and to provide a fishing rod having high strength and light weight performance. That is, the present invention is to provide a fishing rod comprising a plurality of layers made of fiber-reinforced artificial resin, wherein a void retaining layer is provided between the innermost layer and the outermost layer of these layers.

이하 실시상태를 도면에 따라서 설명한다.Embodiments will be described below with reference to the drawings.

제1도는 낚시대관의 적층구성의 일예를 설명적으로 도시한 투시도로, (1)은 내층으로 평직 또는 주자직(朱子織)등의 유리섬유 직포나 상품명 게브랄-49(KEVLAR-49, 미국듀퐁사제 방향족 포리 아미드 계섬유)의 직포 또는 유리섬유와 게브랄-49와의 교직포를 사용한 푸리프레그(Piepreg) 시이트(sheet)를 사용한 것이다. (2)는 공극 보유층으로 예를 들면 제2도에서 확대하여 도시한 바와 같이 비교적 직목(織目)이 크며 두께가 두껍고 단위면적당 중량이 작은 직포로서 여기에 수지를 함침시킨 것이다. 그러나 직목의 공극(空隙)(6)부분에 공극을 잔존 형성시킨 점이 종래의 방법에 대해 특이한 특징을 갖는 것이다. 사용하는 섬유는 전기한 내층(1)에 사용하는 것과 같아도 좋다.1 is a perspective view showing an example of the laminated structure of the fishing pipe explanatory, (1) is the inner layer of glass fiber woven fabrics such as plain weave or runner weaving or trade name Gebral-49 (KEVLAR-49, US A woven fabric made of DuPont's aromatic polyamide-based fiber) or a woven fabric made of glass cloth and a cross-woven fabric of gebral-49 is used. (2) is a pore-retaining layer, for example, as shown in an enlarged view in FIG. 2, which is relatively woven and has a thick thickness and a small weight per unit area, in which resin is impregnated. However, the fact that the voids remain in the voids 6 of the direct wood has a characteristic unique to the conventional method. The fiber to be used may be the same as that used for the inner layer 1 described above.

이러한 공극 보유층(2)의 외측에는 낚시대 본체와 평행방향(긴쪽방향을 따라)으로 당겨져서 정리된 강화섬유층(중간층)(3)이 만들어져 있다. 이 강화섬유층(3)에 사용되는 섬유는 높은 항장력, 높은 탄성계수를 갖는 재료가 적당하며, 예를들어 전기한 게브랄-49의 섬유와 같은 수지함침된 섬유 또는 탄소섬유나 이들의 혼합물등이 사용될 수 있다(4)는 가장 바깥층으로, 예를 들면 전술한 재료나 유니온 직물로 만들어진 단독직포 또는 교직포로서 평직 기타로 짠 푸리프레그시이트로 구성되어 있다.On the outside of the void retaining layer 2, a reinforcing fiber layer (intermediate layer) 3 which is pulled and arranged in parallel with the fishing rod body (along the longitudinal direction) is formed. The fiber used in the reinforcing fiber layer 3 is preferably a material having high tensile strength and high modulus of elasticity. For example, resin-impregnated fibers such as the aforementioned Gebral-49 fibers, carbon fibers or mixtures thereof may be used. (4) may be used as the outermost layer, for example, consisting of a single-ply fabric made of the aforementioned material or a union fabric, or of a plain prep woven into plain weave or the like as a teaching cloth.

통상 이상의 순서로 테이퍼상태의 심금 외면에 권착하여 적층구조를 형성한 뒤, 수지를 경화함에 의해 적층구조의 중간에 다수의 작은 공극(6)을 감싸는 공극보유층(2)이 일체적으로 있도록 한 본 발명의 낚시대가 얻어진다.After forming the laminated structure by winding on the outer surface of the tapered core in the above-described order, the resin is cured so that the void retaining layer 2 which covers the plurality of small voids 6 in the middle of the laminated structure is integrally formed. The fishing rod of this invention is obtained.

또 도면에 있어서 (5)는 가장 바깥층의 도장부를 도시한다.In the drawing, reference numeral 5 denotes the outermost coating part.

본 발명의 낚시대는 이와 같이 구성되어 있으므로 공극을 함유시킨만큼 높이를 늘리고, 동일 중량의 경우 종래의 낚시대관에 비교하여 관의 벽 두께를 증가시킬 수가 있다. 그러나 중요한 것은 제4도에 도시한 바와 같이, 이 관에 굴곡모멘트 M가 작용하는 경우 제3도의 종래의 것에 비교하여 종단면의 변형이 거의 발생하지 않고 둥근 그대로 유지될 수가 있다.Since the fishing rod of the present invention is configured in this manner, the height can be increased by containing voids, and in the case of the same weight, the wall thickness of the pipe can be increased as compared with the conventional fishing rod. Importantly, however, as shown in FIG. 4, when the bending moment M acts on this tube, the deformation of the longitudinal section is hardly generated and can be kept round as compared with the conventional one of FIG.

즉, 단면의 변형비

That is, the strain ratio of the cross section

굴절에 의한 흐트러짐 c′＜ cDisturbance due to refraction c '<c

따라서 굴곡모멘트에 의한 흐트러짐을 감소하고, 가볍고, 강성(剛性)이 큰 뛰어난 낚시대가 얻어진다.This reduces the disturbance caused by the bending moment and obtains an excellent fishing rod that is light and has high rigidity.

또 전술한 실시예에서는 대표적인 일예로서 여기에 한정되는 것이 아니고 적층수나 수지재료는 필요에 따라 공지의 방법 내지는 임의로 결정하여 실시할 수가 있다.Moreover, in the above-mentioned embodiment, it is not limited to this as a typical example, A lamination number and a resin material can be performed by a well-known method or arbitrarily determined as needed.

적층수를 늘린 경우에는 공극 보유층은 내층과 외층의 임의의 위치에 배치할 수가 있다. 또 이들 공극 보유층은 한층에만 국한하지 않고 여러층으로 만들어도 좋다.When the number of stacked layers is increased, the void retaining layer can be disposed at any position of the inner layer and the outer layer. Moreover, these void holding layers may be made not only in one layer but in several layers.

요는 다수의 작은 공극을 보유하는 층이 다른 적층 사이에 존재하는 것이다. 또 이런 작은 공극보유층으로서 작은 공극의 형성수단은 제2도의 이에 한정되는 것이 아니고 다른 방법으로 직조한 직포, 또는 직포 외에, 예를 들면 망, 또는 다수의 작은 구멍을 천설한 시이트, 허니컴(hanly comb)구조체등을 사용해도 좋음은 물론이다.The idea is that a layer containing a number of small voids is present between the different stacks. The means for forming the small voids as the small void retaining layer is not limited to the one shown in FIG. 2, but in addition to the woven fabric or the woven fabric of another method, for example, a sheet or a honeycomb fabricated with a web or a plurality of small holes comb) structure may be used, of course.

Claims

As described above in the text and shown in the drawings, a synthetic resin fishing rod comprising a plurality of layers made of fiber-reinforced artificial resin and having a void retaining layer provided between the innermost and outermost layers of these layers. .