KR20240062108A - 직조된 홀로그램 필름 원단 - Google Patents
직조된 홀로그램 필름 원단 Download PDFInfo
- Publication number
- KR20240062108A KR20240062108A KR1020230147107A KR20230147107A KR20240062108A KR 20240062108 A KR20240062108 A KR 20240062108A KR 1020230147107 A KR1020230147107 A KR 1020230147107A KR 20230147107 A KR20230147107 A KR 20230147107A KR 20240062108 A KR20240062108 A KR 20240062108A
- Authority
- KR
- South Korea
- Prior art keywords
- fabric
- weight
- parts
- layer
- film
- Prior art date
Abstract
본 발명의 홀로그램 필름 원단은 홀로그램 필름이나 빛을 받으면 색상이 변하는 오로라필름(레인보우필름)을 미세하게 가는 실 처럼 절단한 다음 이를 원사와 그물망처럼 직조하여 필름원단을 제직하여 보다 다양한 입체감을 나타내는 3차원의 빛 반사를 가능하도록 하고, 표면에 잉크젯 프린터로 디자인이나 사진을 인쇄할 수 있도록, 세로줄인 날실과 가로줄인 씨실 2개를 직각으로 서로 교차하도록 반복적으로 엮어 직조한 홀로그램 직물을 생산하여 홀로그램 원단과, 상기 홀로그램 원단 사이사이와 표면에 열가소성 아크릴계통 수지를 열 융착시켜 접착하는 인쇄층과, 상기 홀로그램 원단 하부에 배경이 표현되는 수지를 열융착시켜 접착하는 배경층과, 상기 배경층의 하부에 핫멜트를 코팅시키는 접착층으로 이루어져, 잉크젯 인쇄성이 좋고 세탁 견뢰도가 뛰어난 효과가 있다.
Description
본 발명은 홀로그램 필름 원단에 관한 것으로서, 더욱 상세하게 는 홀로그램 필름이나 빛을 받으면 색상이 변하는 오로라필름(레인보우필름)을 미세하게 가는 실 처럼 절단한 다음 이를 원사와 그물망처럼 직조하여 필름원단을 제직하여 보다 다양한 입체감을 나타내는 3차원의 빛 반사를 가능하도록 하고, 표면에 잉크젯 프린터로 디자인이나 사진을 인쇄할 수 있도록 한 직조된 홀로그램 필름 원단에 관한 것이다.
일반적인 열전사지는 스포츠웨어의 백넘버나 팀 로고, 티셔츠의 캐릭터나 글자, 사진 등을 붙이는 용도로 사용하고 있다.
기존의 3D 입체감을 주는 열전사지는 일반적으로 필름 위에 이형제층, 무늬층, 입체감을 주기 위한 발포층, 및 기재와 접착하기 위한 접착층으로 구성되어 있다. 이러한 열전사지의 접착층을 기재와 맞대어 열과 압력을 가하여 접착시킨 후, 일련의 냉각 공정을 거쳐, 이형제층 위의 필름을 제거하면, 기재에 무늬층, 발포층, 접착층이 남게 되어 무늬가 형성되며, 입체감은 열과 압력이 가해질 때 발포층의 발포에 의해 구현되게 된다. 입체감을 잘 살리기 위해 발포층을 다층으로 한 것도 제안되어 있으며, 의류에 전사된 패턴의 입체감을 살리기 위해서 투명 잉크층 위에 옵셋 인쇄층을 형성하고, 인쇄층 위에 세탁견뢰도 및 은폐력 보강을 위한 2개의 보강층을 형성한 전사 필름도 제안되어 있다.
그런데 입체감이 잘 구현되더라도 니트 등의 편물류, 메쉬 원단과 같은 표면 밀도가 낮은 직물 원단, 부직포 등의 접촉 면적이 작은 기재는 접착력이 낮아서, 열전사 후, 입체감이 구현된 무늬층의 탈락이 쉽게 일어나는 문제점이 있다. 또한, 무늬층, 발포층, 접착층에 사용되는 소재들이 열에 약한 폴리우레탄(PU)이나 폴리프로필렌(PP)계일 경우에는, 열전사시 열과 압력에 의해 변형되어 무늬층의 표면에 기재 표면의 형태가 나타나, 무늬 표면이 매끈하지 못하고 변형되는 문제점이 있다.
위와 같은 기능을 수행하는 종래기술은 대한민국 공개특허 제2004-0037291호에서 보는 바와 같이, 직조원단의 표면에 스크린인쇄를 하는 단계; 상기 스크린인쇄를 한 표면에 홀로그램 필름을 열전사하는 단계;를 포함한다.
이때, 섬유원단은 표면이 거칠고, 잉크가 원단 속으로 스며들어버려 화상 표현이 어렵다. 더불어, 섬유원단은 컷팅을 하면 컷팅된 단면에서 실이 한올 한올 풀리게 되고 이 상태로 세탁을 하면 원단 올이 다 풀려버리는 문제점이 있다.
따라서 원단용 입체 열전사 필름에 있어서, 원단과 무늬층의 접착력이나 무늬층의 형태 안정성에 대한 개선이 요구되고 있는 실정이다.
상기와 같은 문제점을 해소하기 위한 본 발명의 홀로그램 필름 원단은 홀로그램 필름이나 빛을 받으면 색상이 변하는 오로라필름(레인보우필름)을 미세하게 가는 실 처럼 절단한 다음 이를 원사와 그물망처럼 직조하여 필름원단을 제직하여 보다 다양한 입체감을 나타내는 3차원의 빛 반사를 가능하도록 하고, 표면에 잉크젯 프린터로 디자인이나 사진을 인쇄할 수 있도록 하는 데 있다.
상기와 같은 목적을 달성하기 위한 본 발명의 홀로그램 필름 원단은 세로줄인 날실과 가로줄인 씨실 2개를 직각으로 서로 교차하도록 반복적으로 엮어 직조한 홀로그램 직물을 생산하여 홀로그램 원단과, 상기 홀로그램 원단 사이사이와 표면에 열가소성 아크릴계통 수지를 열 융착시켜 접착하는 인쇄층과, 상기 홀로그램 원단 하부에 배경이 표현되는 수지를 열융착시켜 접착하는 배경층과, 상기 배경층의 하부에 핫멜트를 코팅시키는 접착층으로 이루어진 것을 그 기술적 기본 특징으로 한다.
본 발명에 따르면, 상기 인쇄층은, 폴리우레탄 수지 40 내지 60중량부, 희석용제 메칠에칠케톤 20 내지 40중량부, 폴리에스터 수지 15 내지 25중량부, 폴리아크릴 수지 4 내지 6중량부, 실리카 파우더 4 내지 6중량부, 첨가제 0.05 내지 0.15중량부로 혼합된 것을 특징으로 한다.
본 발명에 따르면, 상기 배경층은, 폴리에스터 수지 40 내지 60중량부, 희석용제 메칠에칠케톤 20 내지 40중량부, 폴리우레탄 수지 5 내지 15중량부, 경화제 5 내지 15중량부, 촉매 1 내지 3중량부로 혼합된 것을 특징으로 한다.
본 발명에 따르면, 상기 접착층은, 폴리에스터계, 폴리우레탄계, 에틸렌비닐아세테이트계, 폴리올레핀계, 폴리아마이드계로 이루어진 군에서 1 이상을 선택적으로 적용할 수 있는 것을 특징으로 한다.
상기와 같은 본 발명의 홀로그램 필름 원단은 홀로그램 필름이나 빛을 받으면 색상이 변하는 오로라필름(레인보우필름)을 미세하게 가는 실 처럼 절단한 다음 이를 원사와 그물망처럼 직조하여 필름원단을 제직하여 보다 다양한 입체감을 나타내는 3차원의 빛 반사를 가능하도록 하고, 표면에 잉크젯 프린터로 디자인이나 사진을 인쇄할 수 있도록, 세로줄인 날실과 가로줄인 씨실 2개를 직각으로 서로 교차하도록 반복적으로 엮어 직조한 홀로그램 직물을 생산하여 홀로그램 원단과, 상기 홀로그램 원단 사이사이와 표면에 열가소성 아크릴계통 수지를 열 융착시켜 접착하는 인쇄층과, 상기 홀로그램 원단 하부에 배경이 표현되는 수지를 열융착시켜 접착하는 배경층과, 상기 배경층의 하부에 핫멜트를 코팅시키는 접착층으로 이루어져, 잉크젯 인쇄성이 좋고 세탁 견뢰도가 뛰어난 효과가 있다.
또한, 인쇄층을 라미네이팅을 하고 라미네이팅 반대면에 접착층을 코팅하여 인쇄성과 섬유원단에의 접착성을 모두 개선하는 효과가 있다.
도 1은 본 발명의 직조된 홀로그램 필름 원단을 나타낸 단면도.
도 2는 본 발명의 직조된 홀로그램 필름 원단을 나타낸 평면도.
도 2는 본 발명의 직조된 홀로그램 필름 원단을 나타낸 평면도.
우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 동일한 참조부호로 나타내고 있음에 유의하여야 한다.
본 발명을 설명함에 있어, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않기 위하여 생략한다.
본 명세서에서 사용되는 정도의 용어 "약","실질적으로" 등은 언급된 의미에고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접 한의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적이니 수치가 언급된개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.
도 1은 본 발명의 직조된 홀로그램 필름 원단을 나타낸 단면도이고, 도 2는 본 발명의 직조된 홀로그램 필름 원단을 나타낸 평면도이다.
본 발명은 입체감을 나타내는 홀로그램 필름이나 빛을 받으면 색상이 변하는 오로라필름(또는 레인보우필름)을 미세하게, 즉 가는 실처럼 절단한 다음, 이를 원사와 그물망처럼 직조하여 홀로그램원단 110을 제직한다.
그리고 홀로그램원단 110 표면에 인쇄층 120, 배경층 130, 접착층 140이 적층되는 직조된 홀로그램 필름 원단 100을 제안한다.
즉, 본 발명에서 전술한 홀로그램 필름이나 오로라 필름을 원사와 직조한 이유는, 상기 홀로그램 필름이나 오로라필름은 다른 재질(우레탄계열의 소재)과 접착이되지 않기 때문에 본 발명에서는 상기 필름을 미세하게 절단한 후 이를 원사와 직조한 것이다.
이때, 직조는 세로줄인 날실 111과 가로줄인 씨실 113을 직각으로 서로 교차하도록 반복적으로 엮는다.
다시 말해, 직조된 홀로그램 필름 원단 100은 홀로그램 필름 또는 오로라 필름을가는 실처럼 절단하여 실사 111, 113를 만든 다음, 상기 실사와 화학 섬유 또는 천연섬유 재질로 형성된 직물인 원사를 상호 그물망의 형상으로 엮어서 직조하여 홀로그램 원단 110을 제직한다.
또한, 상기 홀로그램 원단 110 사이사이와 표면에 열가소성 아크릴계통 수지인 인쇄층 120을 열 융착시켜 접착한다. 이때, 인쇄층 120은 섬유원단 ROLL TO ROLL 코팅으로 제작한다.
특히, 인쇄층 120은 인쇄가 가능하면서 열접착력이 있는 열가소성 아크릴계통 수지(PMMA, PMA, PEMA, PEA, PBMA, PBA 등), 폴리에스터 계통 수지, 폴리아마이드 계통 수지, 폴리우레탄 계통 수지, 고무계 수지 등을 배합하여 사용한다.
그리고 인쇄층 120은 다양한 첨가제를 사용하여 인쇄성과 접착성, 표면 블록킹 방지성, 내세탁성 등을 확보한다. 이때, 첨가제는 실리카 파우더, 잉크정착제, 경화제, 레벨링제, 소포제, 대전방지제, 점도조절제, 필러, 안료, 염료로 이루어진 군에서 1 이상을 선택적으로 적용한다.
나아가, 상기 인쇄층 120은 폴리우레탄 수지 40 내지 60중량부, 희석용제 메칠에칠케톤 20 내지 40중량부, 폴리에스터 수지 15 내지 25중량부, 폴리아크릴 수지 4 내지 6중량부, 실리카 파우더 4 내지 6중량부, 첨가제 0.05 내지 0.15중량부로 혼합되어 있다.
더불어, 인쇄층 120의 코팅 두께는 0.01미크론 내지 50미크론으로 상부면은 인쇄가 용이하도록 돌출이 없도록 한다.
한편, 상기 홀로그램 원단 110 하부에 배경이 표현되는 수지를 열융착시켜 접착하는 배경층 130을 적층한다.
상기 배경층 130은 폴리에스터 수지 40 내지 60중량부, 희석용제 메칠에칠케톤 20 내지 40중량부, 폴리우레탄 수지 5 내지 15중량부, 경화제 5 내지 15중량부, 촉매 1 내지 3중량부로 혼합된다.
또한, 배경층 130은 아크릴 계통 수지, 폴리우레탄 계통 수지, 폴리아마이드 계통 수지, 폴리에스터 계통 수지, 비닐 관능기 보유 수지, 고무계통 수지, 에폭시 수지, 페놀계통 수지 등을 배합하여 사용한다. 이러한, 수지들은 단독 혹은 혼합으로 사용가능하고, 열가소성 상태로 사용하거나 경화제를 사용하여 경화형태로 사용할 수 있다.
이때, 경화제는 이소시아네이트계, 아미노수지계, 에폭시 수지계, 아지리딘계, 킬레이트계, UV 경화제 등 시중에서 일반적으로 사용하는 경화제 코팅액은 위의 기본 수지를 여러가지 사용하여 배합하고, 다양한 첨가제를 사용하여 접착성, 블록킹 방지성, 내세탁성 등을 확보한다.
더불어, 배경층 130의 코팅방식은 ROLL TO ROLL 코팅으로 두께는 1 미크론 내지 100미크론으로 섬유 내부에 충분히 스며들어서 인쇄층 120과 접착성이 나오면서 핫멜트층과의 접착력도 나오는 수준의 두께이다.
나아가, 배경층 130은 흰색 또는 컬러를 혼합하여 홀로그램 원단 110 및 인쇄층 120을 부각시는 기능을 수행한다.
한편, 상기 배경층 130의 하부에 핫멜트를 코팅시키는 접착층 140을 적층한다.
이때, 접착층 140은 폴리에스터계, 폴리우레탄계, 에틸렌비닐아세테이트계, 폴리올레핀계, 폴리아마이드계로 이루어진 군에서 1 이상을 선택적으로 적용할 수 있다.
이러한, 접착층 140은 티셔츠나 스포츠웨어 등 장식할 대상에 열프레스기나 다리미를 이용하여 고온 고압에서 열프레스를 하면 접착층 140이 녹아서 장식할 대상에 접착이 된다.
상기, 접착층 140의 코팅방식은 ROLL TO ROLL 코팅으로 두께 1 내지 200미크론 메칠에칠케톤으로 녹인 액상 폴리에스터계 핫멜트이다.
한편, 접착층 140의 하부를 보호하는 이형층 200이 접착된 상태로 제조되고 사용시 이형층 200을 제거한 후 사용한다.
결국, 본 발명의 홀로그램 필름 원단 100은 홀로그램 필름이나 빛을 받으면 색상이 변하는 오로라필름(레인보우필름)을 미세하게 가는 실 처럼 절단한 다음 이를 원사와 그물망처럼 직조하여 필름원단을 제직하여 보다 다양한 입체감을 나타내는 3차원의 빛 반사를 가능하도록 하고, 표면에 잉크젯 프린터로 디자인이나 사진을 인쇄할 수 있도록하여, 잉크젯 인쇄성이 좋고 세탁 견뢰도가 뛰어난 효과가 있다.
또한, 인쇄층 120을 라미네이팅을 하고 라미네이팅 반대면에 접착층 140을 코팅하여 인쇄성과 섬유원단에의 접착성을 모두 개선하는 효과가 있다.
이상과 같이, 본 명세서와 도면에는 본 발명의 바람직한 실시예에 대하여 개시하였으며, 비록 특정 용어들이 사용되었으나, 이는 단지 본 발명의 기술내용을 쉽게 설명하고 발명의 이해를 돕기 위한 일반적인 의미에서 사용된 것이지, 본 발명의 범위를 한정하고자 하는 것은 아니다. 여기에 개시된 실시예외에도 본 발명의 기술적 사상에 바탕을 둔 다른 변형예들이 실시 가능하다는 것은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 자명한 것이다.
100 : 홀로그램 필름 원단
110 : 홀로그램 원단 111: 날실
113 : 씨실 120 : 인쇄층
130 : 배경층 140 : 접착층
110 : 홀로그램 원단 111: 날실
113 : 씨실 120 : 인쇄층
130 : 배경층 140 : 접착층
Claims (4)
- 세로줄인 날실과 가로줄인 씨실 2개를 직각으로 서로 교차하도록 반복적으로 엮어 직조한 홀로그램 직물을 생산하여 홀로그램 원단과,
상기 홀로그램 원단 사이사이와 표면에 열가소성 아크릴계통 수지를 열 융착시켜 접착하는 인쇄층과,
상기 홀로그램 원단 하부에 배경이 표현되는 수지를 열융착시켜 접착하는 배경층과,
상기 배경층의 하부에 핫멜트를 코팅시키는 접착층으로 이루어진 것을 특징으로 하는 직조된 홀로그램 필름 원단.
- 제1항에 있어서,
상기 인쇄층은,
폴리우레탄 수지 40 내지 60중량부, 희석용제 메칠에칠케톤 20 내지 40중량부, 폴리에스터 수지 15 내지 25중량부, 폴리아크릴 수지 4 내지 6중량부, 실리카 파우더 4 내지 6중량부, 첨가제 0.05 내지 0.15중량부로 혼합된 것을 특징으로 하는 직조된 홀로그램 필름 원단.
- 제1항에 있어서,
상기 배경층은,
폴리에스터 수지 40 내지 60중량부, 희석용제 메칠에칠케톤 20 내지 40중량부, 폴리우레탄 수지 5 내지 15중량부, 경화제 5 내지 15중량부, 촉매 1 내지 3중량부로 혼합된 것을 특징으로 하는 직조된 홀로그램 필름 원단.
- 제1항에 있어서,
상기 접착층은,
폴리에스터계, 폴리우레탄계, 에틸렌비닐아세테이트계, 폴리올레핀계, 폴리아마이드계로 이루어진 군에서 1 이상을 선택적으로 적용할 수 있는 것을 특징으로 하는 직조된 홀로그램 필름 원단.