KR20230153296A - Nickel with permanent oxidation resistance by silicon-coated surface and manufacturing method for nickel with permanent oxidation resistance by silicon-coated surface - Google Patents
Nickel with permanent oxidation resistance by silicon-coated surface and manufacturing method for nickel with permanent oxidation resistance by silicon-coated surface Download PDFInfo
- Publication number
- KR20230153296A KR20230153296A KR1020230054704A KR20230054704A KR20230153296A KR 20230153296 A KR20230153296 A KR 20230153296A KR 1020230054704 A KR1020230054704 A KR 1020230054704A KR 20230054704 A KR20230054704 A KR 20230054704A KR 20230153296 A KR20230153296 A KR 20230153296A
- Authority
- KR
- South Korea
- Prior art keywords
- silicon
- nickel
- coated
- oxidation
- oxygen
- Prior art date
Abstract
본 발명은 실리콘이 코팅된 산화방지용 니켈 및 실리콘이 코팅된 산화방지용 니켈 제조방법에 관한 것으로, 더욱 상세하게는 실리콘(Si)를 증착하여 실리콘(Si)-산소(O)-니켈(Ni) 혼합층 보호막을 형성하여 전기적인 특성을 그대로 유지하면서 산화에 대한 저항성을 갖는 실리콘(Si)이 코팅된 표면을 포함하는 산화방지용 니켈에 관한 것이다.
본 발명인 실리콘이 코팅된 산화방지용 니켈은 니켈층(100); 상기 니켈층(100) 상단에 실리콘(Si)-산소(O)-니켈(Ni)이 혼합되어 형성된 사이닉스층(200); 상기 사이닉스층(200) 상단에 형성된 제 1 실리콘(Si)-산소(O) 혼합층(300); 및 상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 상단에 형성된 제 2 실리콘(Si)-산소(O) 혼합층(400);으로 구성되는 것을 특징으로 한다.
본 발명인 실리콘이 코팅된 니켈 제조방법은 실리콘(Si)을 스퍼터링(sputtering) 단일 공정으로 증착시킨 것을 특징으로 한다.The present invention relates to silicon-coated anti-oxidation nickel and a method for manufacturing silicon-coated anti-oxidation nickel, and more specifically, to deposit silicon (Si) to form a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer. It relates to nickel for preventing oxidation, which includes a surface coated with silicon (Si), which has resistance to oxidation while maintaining electrical properties by forming a protective film.
The present invention, silicon-coated nickel for oxidation prevention, includes a nickel layer (100); A cynix layer 200 formed by mixing silicon (Si)-oxygen (O)-nickel (Ni) on top of the nickel layer 100; A first silicon (Si)-oxygen (O) mixed layer 300 formed on top of the cynics layer 200; and a second silicon (Si)-oxygen (O) mixed layer 400 formed on top of the first silicon (Si)-oxygen (O) mixed layer 300.
The present invention's silicon-coated nickel manufacturing method is characterized by depositing silicon (Si) through a single sputtering process.
Description
본 발명은 실리콘이 코팅된 산화방지용 니켈 및 실리콘이 코팅된 산화방지용 니켈 제조방법에 관한 것으로, 더욱 상세하게는 실리콘(Si)를 증착하여 실리콘(Si)-산소(O)-니켈(Ni) 혼합층 보호막을 형성하여 전기적 및 자기적인 특성을 그대로 유지하면서 산화에 대한 저항성을 갖는 실리콘(Si)이 코팅된 표면을 포함하는 산화방지용 니켈에 관한 것이다.The present invention relates to silicon-coated anti-oxidation nickel and a method for manufacturing silicon-coated anti-oxidation nickel, and more specifically, to deposit silicon (Si) to form a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer. The present invention relates to nickel for preventing oxidation, which includes a surface coated with silicon (Si), which has resistance to oxidation while maintaining electrical and magnetic properties by forming a protective film.
일반적으로 금속재료는 주변 환경과의 상호작용에 의해 산화되면서 부식이 일어나 금속 자체의 내구성이 저하되게 된다. 종래에는 금속에 발생하는 부식을 방지하기 위한 방법으로 금속 자체에 다른 원소를 첨가하여 화학적으로 안정된 합금을 만드는 방법 및 금속의 표면을 코팅 등을 통해 처리하는 방법 등이 있다.In general, metal materials are oxidized and corrode due to interaction with the surrounding environment, thereby reducing the durability of the metal itself. Conventionally, methods for preventing corrosion occurring in metal include a method of making a chemically stable alloy by adding other elements to the metal itself, and a method of treating the surface of the metal through coating, etc.
상기 표면을 코팅하는 방법은 금속의 특성과 용도, 주변 환경에 따라 코팅 물질을 선택하여 사용할 수 있으며, 내부식성을 향상시킬 수 있다는 장점이 있으나, 고온에서의 사용이 제한된다는 단점이 있다. The method of coating the surface can be used by selecting a coating material depending on the characteristics of the metal, its use, and the surrounding environment, and has the advantage of improving corrosion resistance, but has the disadvantage of limiting use at high temperatures.
따라서, 상기와 같은 문제를 해결하기 위해 공정이 단순하면서 산화 문제를 해결할 수 있는 금속의 표면코팅 방법이 필요하다.Therefore, in order to solve the above problems, a metal surface coating method that has a simple process and can solve the oxidation problem is needed.
본 발명은 상기와 같은 문제점을 해결하기 위해서 안출된 것으로, 본 발명의 목적은 Si 증착을 통해 Si-O-Ni 보호층을 형성하여 산화를 방지함과 동시에 고온에서도 산화에 안정적인 산화방지용 니켈 박막을 제조하는 방법을 제공하는 것이다.The present invention was devised to solve the above problems, and the purpose of the present invention is to prevent oxidation by forming a Si-O-Ni protective layer through Si deposition and at the same time provide an anti-oxidation nickel thin film that is stable against oxidation even at high temperatures. It provides a manufacturing method.
발명이 해결하고자 하는 기술적 과제들은 이상에서 언급한 기술적 과제들로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.The technical problems to be solved by the invention are not limited to the technical problems mentioned above, and other technical problems not mentioned will be clearly understood by those skilled in the art from the description below. You will be able to.
본 발명은 실리콘이 코팅된 산화방지용 니켈로, 실리콘(Si)을 증착시켜 실리콘(Si)-산소(O)-니켈(Ni) 혼합층인 사이닉스층(200)이 형성된 실리콘이 코팅된 산화방지용 니켈에 관한 것이다.The present invention is silicon-coated anti-oxidation nickel, in which silicon (Si) is deposited to form a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer (200). It's about.
또한, 상기 실리콘이 코팅된 니켈은, 상기 실리콘(Si)이 증착되지 않은 니켈과 유사한 전기저항을 가지는 것을 특징으로 한다.In addition, the silicon-coated nickel is characterized by having an electrical resistance similar to that of nickel on which the silicon (Si) is not deposited.
또한, 상기 실리콘이 코팅된 니켈은, 단결정 박막, 다결정 박막, 호일 또는 덩어리 인 것을 특징으로 한다.In addition, the silicon-coated nickel is characterized in that it is a single crystal thin film, a polycrystalline thin film, a foil, or a lump.
또한, 상기 실리콘이 코팅된 니켈이 단결정 박막인 경우, 300 내지 500 ℃로 20 내지 50 분 동안 열을 가하여도 산화가 방지되는 것을 특징으로 한다.In addition, when the silicon-coated nickel is a single crystal thin film, oxidation is prevented even when heat is applied at 300 to 500 ° C. for 20 to 50 minutes.
또한, 상기 실리콘이 코팅된 니켈이 다결정 박막, 호일 또는 덩어리인 경우, 300 내지 400 ℃로 열을 가하여도 산화가 방지되는 것을 특징으로 한다.In addition, when the silicon-coated nickel is a polycrystalline thin film, foil, or lump, oxidation is prevented even when heated at 300 to 400 ° C.
또한, 상기 실리콘이 코팅된 니켈은, 면저항이 6.2×10-4 내지 6.8×10-4 Ω/□인 것을 특징으로 한다.In addition, the silicon-coated nickel is characterized by a sheet resistance of 6.2×10 -4 to 6.8×10 -4 Ω/□.
또한, 상기 실리콘이 코팅된 니켈은, 니켈층(100); 상기 니켈층(100) 상단에 실리콘(Si)-산소(O)-니켈(Ni)이 혼합되어 형성된 사이닉스층(200); 상기 사이닉스층(200) 상단에 형성된 제 1 실리콘(Si)-산소(O) 혼합층(300);및 상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 상단에 형성된 실리콘(Si)층(400);으로 구성되는 것을 특징으로 한다.In addition, the silicon-coated nickel is formed into a nickel layer 100; A cynics layer 200 formed by mixing silicon (Si)-oxygen (O)-nickel (Ni) on top of the nickel layer 100; A first silicon (Si)-oxygen (O) mixed layer 300 formed on top of the cynics layer 200; and silicon (Si) formed on top of the first silicon (Si)-oxygen (O) mixed layer 300. It is characterized in that it consists of a layer (400).
또한, 상기 사이닉스층(200)은, 두께가 0.8 내지 1.2 nm인 것을 특징으로 한다.In addition, the cynics layer 200 is characterized by a thickness of 0.8 to 1.2 nm.
또한, 상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 및 상기 제 2 실리콘(Si)-산소(O) 혼합층(400)을 포함하는 실리콘(Si)-산소(O) 혼합층은, 두께가 5 내지 30 nm인 것을 인 것을 특징으로 한다.In addition, the silicon (Si)-oxygen (O) mixed layer including the first silicon (Si)-oxygen (O) mixed layer 300 and the second silicon (Si)-oxygen (O) mixed layer 400, It is characterized in that the thickness is 5 to 30 nm.
본 발명은 니켈(Ni)에 실리콘(Si)을 스퍼터링(sputtering) 단일 공정으로 증착시키는 실리콘이 코팅된 산화방지용 니켈 제조방법에 관한 것이다.The present invention relates to a method of manufacturing silicon-coated nickel for preventing oxidation by depositing silicon (Si) on nickel (Ni) through a single sputtering process.
또한, 상기 스퍼터링(sputtering)은, 아르곤 분위기 하에서 수행하는 것을 특징으로 한다.Additionally, the sputtering is characterized in that it is performed under an argon atmosphere.
또한, 상기 스퍼터링(sputtering)은, 상온 내지 350 ℃에서 1 내지 5 분 동안 수행하는 것을 특징으로 한다.In addition, the sputtering is characterized in that it is performed for 1 to 5 minutes at room temperature to 350 ° C.
상기 과제의 해결 수단에 의해, 본 발명은 산화에서 자유로운 니켈을 실리콘(Si) 증착만으로 제작하여 공정이 단순하고 제조 효율이 높으며, 니켈(Ni) 및 실리콘(Si)를 이용하여 경제적으로 높은 가치가 있는 산화방지용 니켈을 제공할 수 있다.As a means of solving the above problem, the present invention produces oxidation-free nickel only by depositing silicon (Si), so the process is simple and manufacturing efficiency is high, and it has high economic value by using nickel (Ni) and silicon (Si). Nickel for oxidation prevention can be provided.
또한, 본 발명은 실리콘(Si) 증착을 통해 실리콘(Si)-산소(O)-니켈(Ni) 보호막을 형성하여 전기적 특성을 그대로 유지하면서 산화에 대한 저항 특성을 갖는 니켈(Ni) 및 이의 제조방법을 제공할 수 있다.In addition, the present invention forms a silicon (Si)-oxygen (O)-nickel (Ni) protective film through silicon (Si) deposition, thereby maintaining the electrical properties and producing nickel (Ni) with resistance to oxidation properties and its production. A method can be provided.
또한, 본 발명은 제조방법이 매우 간편하고 가격이 저렴하면서 상온에서 반영구적으로 사용 가능한 니켈을 제공할 수 있다.In addition, the present invention can provide nickel that has a very simple manufacturing method, is inexpensive, and can be used semi-permanently at room temperature.
또한, 본 발명은 고온에서의 산화저항을 크게 증가시킨 산화방지용 니켈을 제공할 수 있다.Additionally, the present invention can provide anti-oxidation nickel with greatly increased oxidation resistance at high temperatures.
본 발명의 효과들은 이상에서 언급한 효과들로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 청구범위의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned will be clearly understood by those skilled in the art from the description of the claims.
도 1은 본 발명에 따른 순수한 니켈판 및 실리콘(Si)이 코팅된 니켈판의 열처리 전후의 사진이다.
도 2는 본 발명에 따른 순수한 니켈판 및 실리콘이 코팅된 니켈판의 열처리 전후의 XRD 측정 결과를 나타내는 그래프이다.
도 3은 본 발명에 따른 순수한 니켈판 및 실리콘이 코팅된 니켈판의 열처리 전후의 SEM 측정 결과를 나타내는 사진이다.
도 4는 본 발명에 따른 실리콘이 코팅된 니켈판의 (a) TEM 단면 측정, (b) 및 (c) 시료 표면에 대한 TEM 성분 분석 결과를 나타내는 사진 및 그래프이다.
도 5는 본 발명에 따른 순수한 니켈판 및 실리콘이 코팅된 니켈판의 열처리 전후의 면저항 측정 결과를 나타내는 그래프이다.
도 6은 본 발명에 따른 실리콘이 코팅된 니켈판의 Ni(초록색) 박막 위의 O(빨간색)와 Si(회색)의 분포 예상도로, (a) 측면도 및 (b) 평면도를 나타내는 사진이다.
도 7은 본 발명에 따른 순수한 니켈판 및 실리콘이 코팅된 니켈판의 침투 깊이에 따른 △E 및 원자 분포 예상도를 나타내는 그래프이다.Figure 1 is a photograph before and after heat treatment of a pure nickel plate and a nickel plate coated with silicon (Si) according to the present invention.
Figure 2 is a graph showing the XRD measurement results before and after heat treatment of a pure nickel plate and a silicon-coated nickel plate according to the present invention.
Figure 3 is a photograph showing SEM measurement results before and after heat treatment of a pure nickel plate and a silicon-coated nickel plate according to the present invention.
Figure 4 is a photograph and graph showing (a) TEM cross-section measurement of a silicon-coated nickel plate according to the present invention, and (b) and (c) TEM component analysis results for the sample surface.
Figure 5 is a graph showing the sheet resistance measurement results of a pure nickel plate and a silicon-coated nickel plate according to the present invention before and after heat treatment.
Figure 6 is a photograph showing the expected distribution of O (red) and Si (gray) on the Ni (green) thin film of the silicon-coated nickel plate according to the present invention, showing (a) a side view and (b) a top view.
Figure 7 is a graph showing the expected ΔE and atomic distribution according to the penetration depth of the pure nickel plate and the silicon-coated nickel plate according to the present invention.
본 명세서에서 사용되는 용어는 본 발명에서의 기능을 고려하면서 가능한 현재 널리 사용되는 일반적인 용어들을 선택하였으나, 이는 당 분야에 종사하는 기술자의 의도 또는 판례, 새로운 기술의 출현 등에 따라 달라질 수 있다. 또한, 특정한 경우는 출원인이 임의로 선정한 용어도 있으며, 이 경우 해당하는 발명의 설명 부분에서 상세히 그 의미를 기재할 것이다. 따라서 본 발명에서 사용되는 용어는 단순한 용어의 명칭이 아닌, 그 용어가 가지는 의미와 본 발명의 전반에 걸친 내용을 토대로 정의되어야 한다.The terms used in this specification are general terms that are currently widely used as much as possible while considering the function in the present invention, but this may vary depending on the intention or precedent of a person skilled in the art, the emergence of new technology, etc. In addition, in certain cases, there are terms arbitrarily selected by the applicant, and in this case, the meaning will be described in detail in the description of the relevant invention. Therefore, the terms used in the present invention should be defined based on the meaning of the term and the overall content of the present invention, rather than simply the name of the term.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by a person of ordinary skill in the technical field to which the present invention pertains. Terms defined in commonly used dictionaries should be interpreted as having a meaning consistent with the meaning in the context of the related technology, and unless clearly defined in the present application, should not be interpreted in an ideal or excessively formal sense. No.
수치 범위는 상기 범위에 정의된 수치를 포함한다. 본 명세서에 걸쳐 주어진 모든 최대의 수치 제한은 낮은 수치 제한이 명확히 쓰여 있는 것처럼 모든 더 낮은 수치 제한을 포함한다. 본 명세서에 걸쳐 주어진 모든 최소의 수치 제한은 더 높은 수치 제한이 명확히 쓰여 있는 것처럼 모든 더 높은 수치 제한을 포함한다. 본 명세서에 걸쳐 주어진 모든 수치 제한은 더 좁은 수치 제한이 명확히 쓰여 있는 것처럼, 더 넓은 수치 범위 내의 더 좋은 모든 수치 범위를 포함할 것이다.The numerical range includes the values defined in the range above. Any maximum numerical limit given throughout this specification includes all lower numerical limits as if the lower numerical limit were explicitly written out. Every minimum numerical limit given throughout this specification includes every higher numerical limit as if such higher numerical limit were expressly written out. All numerical limits given throughout this specification will include all better numerical ranges within the broader numerical range, as if the narrower numerical limits were clearly written.
실리콘이 코팅된 산화방지용 니켈Anti-oxidation nickel coated with silicon
본 발명은 실리콘이 코팅된 산화방지용 니켈에 관한 것으로, 실리콘을 증착시켜 실리콘(Si)-산소(O)-니켈(Ni) 혼합층인 사이닉스층(200)이 형성된 산화방지용 니켈에 관한 것이다.The present invention relates to anti-oxidation nickel coated with silicon, and to anti-oxidation nickel in which the cynics layer 200, which is a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer, is formed by depositing silicon.
상기 사이닉스층(200)이 형성된 산화방지용 니켈은 전기적 특성을 그대로 유지하면서 산화에 대한 저항 특성을 가지는 것일 수 있다.The anti-oxidation nickel on which the cynics layer 200 is formed may have resistance to oxidation while maintaining its electrical properties.
상기 사이닉스층이 생성되어 산화가 방지되고 고온에서의 산화 저항성이 나타나는 것일 수 있다. 상기 실리콘은 상기 니켈층 표면의 상기 산소와 결합하여 상기 니켈 표면 상에 고정하는 역할을 하는 것일 수 있으며, 이때 가장 기본적인 구조는 도 6과 같이 구성되는 것일 수 있다. 상기 도 6 (a)의 측면도 및 (b)의 평면도에 나타난 바와 같이 상기 산소가 상기 니켈 표면을 덮은 다음 상기 실리콘에 의해 고정이 되면 다른 산소들이 상기 니켈 내부로 들어가지 못하여 산화 저항성을 나타내는 것일 수 있다.The cynics layer may be created to prevent oxidation and exhibit oxidation resistance at high temperatures. The silicon may bind to the oxygen on the surface of the nickel layer and serve to fix it on the nickel surface. In this case, the most basic structure may be configured as shown in FIG. 6. As shown in the side view of FIG. 6 (a) and the top view of (b), when the oxygen covers the nickel surface and is fixed by the silicon, other oxygen cannot enter the nickel, showing oxidation resistance. there is.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈이 단결정 박막인 경우, 300 내지 500 ℃로 20 내지 50 분 동안 열을 가하여도 산화가 방지되는 것일 수 있다.In the present invention, when the silicon-coated nickel is a single crystal thin film, oxidation may be prevented even when heat is applied at 300 to 500° C. for 20 to 50 minutes.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈이 다결정 박막, 호일 또는 덩어리인 경우, 200 내지 400 ℃로 열을 가하여도 산화가 방지되는 것일 수 있다. 상기 다결정 박막, 호일 또는 덩어리인 경우 산화가 방지되어 상기와 같이 열처리를 진행하여도 육안으로 확인되는 색상, XRD 측정, SEM 측정 결과 변화가 나타나지 않는 것일 수 있다.In the present invention, when the silicon-coated nickel is a polycrystalline thin film, foil, or lump, oxidation may be prevented even when heated at 200 to 400 ° C. In the case of the polycrystalline thin film, foil, or lump, oxidation may be prevented and no change in color, XRD measurement, or SEM measurement can be observed with the naked eye even if heat treatment is performed as described above.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈은, 면저항값이 6.2×10-4 내지 6.8×10-4 Ω/□인 것일 수 있다. 상기 실리콘이 코팅된 니켈은 면저항값이 실리콘 코팅되지 않은 니켈과 유사한 면저항 값을 나타내는 것일 수 있으며, 상기 면저항 값은 열처리 후에도 급격한 상승이 나타나지 않는 것일 수 있다.In the present invention, the silicon-coated nickel may have a sheet resistance of 6.2×10 -4 to 6.8×10 -4 Ω/□. The silicon-coated nickel may have a sheet resistance value similar to that of nickel without silicon coating, and the sheet resistance value may not show a sharp increase even after heat treatment.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈은, 니켈층(100); 상기 니켈층(100) 상단에 실리콘(Si)-산소(O)-니켈(Ni)이 혼합되어 형성된 사이닉스층(200); 상기 사이닉스층(200) 상단에 형성된 제 1 실리콘(Si)-산소(O) 혼합층(300); 상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 상단에 형성된 제 2 실리콘(Si)-산소(O) 혼합층(400);으로 구성되는 것일 수 있다.In the present invention, the silicon-coated nickel includes a nickel layer 100; A cynics layer 200 formed by mixing silicon (Si)-oxygen (O)-nickel (Ni) on top of the nickel layer 100; A first silicon (Si)-oxygen (O) mixed layer 300 formed on top of the cynics layer 200; It may be composed of a second silicon (Si)-oxygen (O) mixed layer 400 formed on top of the first silicon (Si)-oxygen (O) mixed layer 300.
본 발명에 있어서, 상기 사이닉스층(200)은, 두께가 0.8 내지 1.2 nm 인 것일 수 있다.In the present invention, the cynics layer 200 may have a thickness of 0.8 to 1.2 nm.
본 발명에 있어서, 상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 및 상기 제 2 실리콘(Si)-산소(O) 혼합층(400)을 포함하는 실리콘(Si)-산소(O) 혼합층은, 두께가 5 내지 30 nm인 것일 수 있으며, 바람직하게는 8 내지 20 nm인 것일 수 있다. 상기 제 1 실리콘(Si)-산소(O) 혼합층(300)은 산소 함량이 니켈 함량보다 높은 것일 수있으며, 상가 제 2 실리콘(Si)-산소(O) 혼합층(400)은 니켈 함량이 산소 함량보다 높은 것일 수 있다.In the present invention, the silicon (Si)-oxygen (O) layer including the first silicon (Si)-oxygen (O) mixed layer 300 and the second silicon (Si)-oxygen (O) mixed layer 400. The mixed layer may have a thickness of 5 to 30 nm, preferably 8 to 20 nm. The first silicon (Si)-oxygen (O) mixed layer 300 may have an oxygen content higher than the nickel content, and the second silicon (Si)-oxygen (O) mixed layer 400 may have a nickel content higher than the oxygen content. It may be higher.
실리콘이 코팅된 산화방지용 니켈 제조방법Method for manufacturing silicon-coated anti-oxidation nickel
본 발명은 실리콘이 코팅된 산화방지용 니켈 제조방법에 관한 것이다.The present invention relates to a method for producing silicon-coated nickel for preventing oxidation.
본 발명의 실리콘이 코팅된 산화방지용 니켈은 실리콘을 증착시켜 실리콘(Si)-산소(O)-니켈(Ni) 혼합층인 사이닉스층(200)이 형성된 산화방지용 니켈에 관한 것이다.본 발명은 실리콘이 코팅된 산화방지용 니켈 제조방법에 관한 것이다.The silicon-coated anti-oxidation nickel of the present invention relates to anti-oxidation nickel in which a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer (200), which is a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer, is formed by depositing silicon. This relates to a method for producing coated nickel for preventing oxidation.
본 발명의 실리콘이 코팅된 산화방지용 니켈은 실리콘을 증착시켜 실리콘(Si)-산소(O)-니켈(Ni) 혼합층인 사이닉스층(200)이 형성된 산화방지용 니켈에 관한 것이다.The silicon-coated anti-oxidation nickel of the present invention relates to anti-oxidation nickel in which the cynics layer 200, which is a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer, is formed by depositing silicon.
상기 사이닉스층(200)이 형성된 산화방지용 니켈은 전기적 특성을 그대로 유지하면서 산화에 대한 저항 특성을 가지는 것일 수 있다.The anti-oxidation nickel on which the cynics layer 200 is formed may have resistance to oxidation while maintaining its electrical properties.
상기 사이닉스층이 생성되어 산화가 방지되고 고온에서의 산화 저항성이 나타나는 것일 수 있다. 상기 실리콘은 상기 니켈층 표면의 상기 산소와 결합하여 상기 니켈 표면 상에 고정하는 역할을 하는 것일 수 있으며, 이때 가장 기본적인 구조는 도 6과 같이 구성되는 것일 수 있다. 상기 도 6 (a)의 측면도 및 (b)의 평면도에 나타난 바와 같이 상기 산소가 상기 니켈 표면을 덮은 다음 상기 실리콘에 의해 고정이 되면 다른 산소들이 상기 니켈 내부로 들어가지 못하여 산화 저항성을 나타내는 것일 수 있다.The cynics layer may be created to prevent oxidation and exhibit oxidation resistance at high temperatures. The silicon may bind to the oxygen on the surface of the nickel layer and serve to fix it on the nickel surface. In this case, the most basic structure may be configured as shown in FIG. 6. As shown in the side view of FIG. 6 (a) and the top view of (b), when the oxygen covers the nickel surface and is fixed by the silicon, other oxygen cannot enter the nickel, showing oxidation resistance. there is.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈은, 상기 실리콘(Si)이 증착되지 않은 니켈과 유사한 전기저항을 가지는 것일 수 있다.In the present invention, the silicon-coated nickel may have an electrical resistance similar to that of nickel on which the silicon (Si) is not deposited.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈은, 단결정 박막, 다결정 박막, 호일 또는 덩어리인 것일 수 있다.In the present invention, the silicon-coated nickel may be a single crystal thin film, a polycrystalline thin film, a foil, or a lump.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈이 단결정 박막인 경우, 300 내지 500 ℃로 20 내지 50 분 동안 열을 가하여도 산화가 방지되는 것일 수 있다.In the present invention, when the silicon-coated nickel is a single crystal thin film, oxidation may be prevented even when heat is applied at 300 to 500° C. for 20 to 50 minutes.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈이 다결정 박막, 호일 또는 덩어리인 경우, 200 내지 400 ℃로 열을 가하여도 산화가 방지되는 것일 수 있다. 상기 다결정 박막, 호일 또는 덩어리인 경우 산화가 방지되어 상기와 같이 열처리를 진행하여도 육안으로 확인되는 색상, XRD 측정, SEM 측정 결과 변화가 나타나지 않는 것일 수 있다.In the present invention, when the silicon-coated nickel is a polycrystalline thin film, foil, or lump, oxidation may be prevented even when heated at 200 to 400 ° C. In the case of the polycrystalline thin film, foil, or lump, oxidation may be prevented and no change in color, XRD measurement, or SEM measurement can be observed with the naked eye even if heat treatment is performed as described above.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈은, 면저항값이 6.2×10-4 내지 6.8×10-4 Ω/□인 것일 수 있다. 상기 실리콘이 코팅된 니켈은 면저항값이 실리콘 코팅되지 않은 니켈과 유사한 면저항 값을 나타내는 것일 수 있으며, 상기 면저항 값은 열처리 후에도 급격한 상승이 나타나지 않는 것일 수 있다.In the present invention, the silicon-coated nickel may have a sheet resistance of 6.2×10 -4 to 6.8×10 -4 Ω/□. The silicon-coated nickel may have a sheet resistance value similar to that of nickel without silicon coating, and the sheet resistance value may not show a sharp increase even after heat treatment.
본 발명에 있어서, 상기 실리콘이 코팅된 니켈은, 니켈층(100); 상기 니켈층(100) 상단에 실리콘(Si)-산소(O)-니켈(Ni)이 혼합되어 형성된 사이닉스층(200); 상기 사이닉스층(200) 상단에 형성된 제 1 실리콘(Si)-산소(O) 혼합층(300); 상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 상단에 형성된 제 2 실리콘(Si)-산소(O) 혼합층(400);으로 구성되는 것일 수 있다.In the present invention, the silicon-coated nickel includes a nickel layer 100; A cynics layer 200 formed by mixing silicon (Si)-oxygen (O)-nickel (Ni) on top of the nickel layer 100; A first silicon (Si)-oxygen (O) mixed layer 300 formed on top of the cynics layer 200; It may be composed of a second silicon (Si)-oxygen (O) mixed layer 400 formed on top of the first silicon (Si)-oxygen (O) mixed layer 300.
본 발명에 있어서, 상기 사이닉스층(200)은, 두께가 0.8 내지 1.2 nm 인 것일 수 있다.In the present invention, the cynics layer 200 may have a thickness of 0.8 to 1.2 nm.
상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 및 상기 제 2 실리콘(Si)-산소(O) 혼합층(400)을 포함하는 실리콘(Si)-산소(O) 혼합층은, 두께가 5 내지 30 nm인 것일 수 있으며, 바람직하게는 8 내지 20 nm인 것일 수 있다. 상기 제 1 실리콘(Si)-산소(O) 혼합층(300)은 산소 함량이 니켈 함량보다 높은 것일 수 있으며, 상기 제 2 실리콘(Si)-산소(O) 혼합층(400)은 니켈 함량이 산소 함량보다 높은 것일 수 있다.The silicon (Si)-oxygen (O) mixed layer including the first silicon (Si)-oxygen (O) mixed layer 300 and the second silicon (Si)-oxygen (O) mixed layer 400 has a thickness of It may be 5 to 30 nm, preferably 8 to 20 nm. The first silicon (Si)-oxygen (O) mixed layer 300 may have an oxygen content higher than the nickel content, and the second silicon (Si)-oxygen (O) mixed layer 400 may have a nickel content higher than the oxygen content. It may be higher.
본 발명은 니켈(Ni)에 실리콘(Si)을 스퍼터링(sputtering) 단일 공정으로 증착시키는 실리콘이 코팅된 산화방지용 니켈 제조방법에 관한 것이다. 상기와 같이 단일 공정으로 진행되어 제조방법이 매우 간편하고 경제적일 수 있다.The present invention relates to a method of manufacturing silicon-coated nickel for preventing oxidation by depositing silicon (Si) on nickel (Ni) through a single sputtering process. As described above, the manufacturing method can be very simple and economical as it is carried out in a single process.
본 발명에 있어서, 상기 스퍼터링(sputtering)은, 아르곤 분위기 하에서 수행하는 것일 수 있다.In the present invention, the sputtering may be performed under an argon atmosphere.
본 발명에 있어서, 상기 스퍼터링(sputtering)은, 상온 내지 350 ℃에서 1 내지 5 분 동안 수행하는 것일 수 있으며, 바람직하게는 180 내지 200 ℃에서 70 내지 350 초 동안 수행하는 것일 수 있다. 상기 스퍼터링 수행 시, 온도 및 수행 시간 범위보다 높거나 낮으면 결정립계와 전위 등의 형성됨에 따라 결정성이 저하되므로 상기 온도 및 수행 시간 범위 내에서 수행하는 것이 바람직하다.In the present invention, the sputtering may be performed at room temperature to 350°C for 1 to 5 minutes, and preferably at 180 to 200°C for 70 to 350 seconds. When performing the sputtering, if it is higher or lower than the temperature and performance time range, crystallinity decreases due to the formation of grain boundaries and dislocations, so it is preferable to perform the sputtering within the above temperature and performance time range.
실시예Example
이하, 본 발명의 실시예를 상세히 기술하나, 하기 실시예에 의해 본 발명이 한정되지 아니함은 자명하다. Hereinafter, examples of the present invention will be described in detail, but it is obvious that the present invention is not limited to the following examples.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예들을 참조하면 명확해 질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 수 있으며, 단지 실시예들은 본 발명의 개시가 완전하도록 하고, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. The advantages and features of the present invention and methods for achieving them will become clear with reference to the embodiments described in detail below. However, the present invention is not limited to the embodiments disclosed below and may be implemented in various different forms, and only the embodiments are provided to ensure that the disclosure of the present invention is complete and that common knowledge in the technical field to which the present invention pertains is provided. It is provided to fully inform those who have the scope of the invention, and the present invention is only defined by the scope of the claims.
실시예 1. 실리콘이 코팅된 니켈판Example 1. Nickel plate coated with silicon
니켈(Ni)판 상에 아르곤 분위기 하에서 190 ℃에서 5분 동안 스퍼터링(sputtering)하여 실리콘(Si)를 20 nm 증착하여 실리콘이 코팅된 철판을 제조하였다.A silicon-coated steel plate was manufactured by depositing 20 nm of silicon (Si) on a nickel (Ni) plate by sputtering at 190°C for 5 minutes under an argon atmosphere.
비교예 1. 실리콘이 코팅되지 않은 니켈판Comparative Example 1. Nickel plate without silicon coating
실리콘을 코팅하지 않은 니켈판을 준비하였다.A nickel plate without silicon coating was prepared.
실험예 1. 열처리 후 산화 정도 관찰Experimental Example 1. Observation of oxidation degree after heat treatment
실시예 1 및 비교예 1에서 제조된 니켈판을 400 ℃에서 30 분간 열처리하여 열처리 전과 후를 관찰하고 이에 대한 결과를 도 1로 나타내었다.The nickel plates prepared in Example 1 and Comparative Example 1 were heat treated at 400° C. for 30 minutes and observed before and after heat treatment, and the results are shown in Figure 1.
도 1에 나타난 바와 같이, 비교예 1의 니켈판은 열처리 후 산화가 일어나 어둡게 변한 반면, 실시예 1에서 제조된 실리콘이 코팅된 니켈판은 열처리 후에도 원래의 색을 그대로 유지하였으며, 이를 통해 산화가 일어나지 않음을 확인하였다.As shown in Figure 1, the nickel plate of Comparative Example 1 was oxidized after heat treatment and turned dark, while the silicon-coated nickel plate manufactured in Example 1 maintained its original color even after heat treatment, which showed that oxidation occurred. It was confirmed that this did not occur.
상기와 같은 결과를 통해, 본 발명에 따른 실리콘이 코팅된 니켈은 산화에 대한 저항 특성을 나타내는 것을 확인하였다.Through the above results, it was confirmed that nickel coated with silicon according to the present invention exhibits resistance to oxidation.
실험예 2. XRD 측정Experimental Example 2. XRD measurement
실시예 1 및 비교예 1에서 제조된 니켈판을 400 ℃에서 30 분간 열처리하여 열처리 전과 후를 XRD로 측정하고, 이에 대한 결과를 도 2로 나타내었다.The nickel plates prepared in Example 1 and Comparative Example 1 were heat treated at 400°C for 30 minutes and measured by XRD before and after heat treatment, and the results are shown in Figure 2.
도 2에 나타난 바와 같이, 실시예 1에서 제조된 실리콘이 코팅된 니켈판은 열처리 전 및 열처리 후에도 Ni 이외의 피크가 나타나지 않았다. 또한, 결정 구조가 바뀌지 않았다. 이를 통해 상기 실리콘이 코팅된 철판은 열처리 후에 산화가 일어나지 않았음을 확인하였다. 반면, 비교예 1의 니켈판의 경우 열처리한 후에는 니켈 산화물 피크가 나타나 산화가 일어났음을 확인하였다.As shown in Figure 2, the silicon-coated nickel plate prepared in Example 1 showed no peaks other than Ni before and after heat treatment. Additionally, the crystal structure did not change. Through this, it was confirmed that the silicon-coated steel plate did not oxidize after heat treatment. On the other hand, in the case of the nickel plate of Comparative Example 1, a nickel oxide peak appeared after heat treatment, confirming that oxidation had occurred.
상기와 같은 결과를 통해, 본 발명에 따른 실리콘이 코팅된 니켈은 산화에 대한 저항 특성을 나타내는 것을 확인하였다.Through the above results, it was confirmed that nickel coated with silicon according to the present invention exhibits resistance to oxidation.
실험예 3. SEM 관찰Experimental Example 3. SEM observation
실시예 1 및 비교예 1에서 제조된 니켈판을 400 ℃에서 30 분간 열처리하여 열처리 전과 후를 SEM을 통해 10,000 배 확대하여 관찰하고, 이에 대한 결과를 도 3으로 나타내었다.The nickel plates prepared in Example 1 and Comparative Example 1 were heat treated at 400° C. for 30 minutes and observed before and after heat treatment through SEM at a magnification of 10,000 times, and the results are shown in Figure 3.
도 3에 나타난 바와 같이, 비교예 1의 니켈판은 열처리 후 표면에 변화가 나타난 반면, 실시예 1에서 제조된 실리콘이 코팅된 니켈판은 열처리 후에도 표면에 변화가 나타나지 않았다. 이를 통해, 상기 실시예 1에서 제조된 실리콘이 코팅된 산화방지용 니켈판에는 산화가 일어나지 않음을 확인하였다.As shown in Figure 3, the nickel plate of Comparative Example 1 showed changes in the surface after heat treatment, while the silicon-coated nickel plate prepared in Example 1 showed no changes in the surface even after heat treatment. Through this, it was confirmed that oxidation did not occur in the silicon-coated anti-oxidation nickel plate prepared in Example 1.
상기와 같은 결과를 통해, 본 발명에 따른 실리콘이 코팅된 니켈은 산화에 대한 저항 특성을 나타내는 것을 확인하였다.Through the above results, it was confirmed that nickel coated with silicon according to the present invention exhibits resistance to oxidation.
실험예 4. TEM 분석Experimental Example 4. TEM Analysis
실시예 1에서 제조된 실리콘이 코팅된 니켈판을 TEM으로 분석하고, 이에 대한 결과를 도 4로 나타내었다.The silicon-coated nickel plate prepared in Example 1 was analyzed by TEM, and the results are shown in Figure 4.
도 4에 나타난 바와 같이, 실리콘이 코팅된 니켈판은 니켈층, 상기 니켈층 상단에 실리콘(Si)-산소(O)-니켈(Ni)이 혼합되어 형성된 사이닉스층, 상기 사이닉스층 상단에 형성된 제 1 실리콘(Si)-산소(O) 혼합층, 상기 제 1 실리콘(Si)-산소(O) 혼합층 상단에 형성된 제 2 실리콘(Si)-산소(O) 혼합층의 순서로 박막 표면이 형성되어 있음을 확인하였다.As shown in Figure 4, the silicon-coated nickel plate has a nickel layer, a psonics layer formed by mixing silicon (Si)-oxygen (O)-nickel (Ni) on top of the nickel layer, and a psonics layer on top of the psonics layer. A thin film surface is formed in the order of the first silicon (Si)-oxygen (O) mixed layer formed, and the second silicon (Si)-oxygen (O) mixed layer formed on top of the first silicon (Si)-oxygen (O) mixed layer. It was confirmed that it exists.
상기 니켈층 상에 실리콘을 증착함에 따라 실리콘 원자들이 상기 니켈층 표면에 자유롭게 움직이는 산소들을 최적의 위치(site)에 고정시켜 Si-O-Ni 결합이 생성되었으며, 이로 인해 형성된 상기 사이닉스층은 산화를 막는 결정적인 역할을 하는 것으로 판단되었다.As silicon was deposited on the nickel layer, silicon atoms fixed oxygen moving freely on the surface of the nickel layer to an optimal site, creating a Si-O-Ni bond, and the resulting cyanix layer was oxidized. It was judged to play a decisive role in preventing.
상기와 같은 결과를 통해, 본 발명에 따른 실리콘이 코팅된 니켈은 니켈층 상에 Si-O-Ni 혼합층이 형성되어 산화가 방지되며 고온에서 산화 저항성을 나타낼 수 있는 것을 확인하였다.Through the above results, it was confirmed that the silicon-coated nickel according to the present invention is prevented from oxidation by forming a Si-O-Ni mixed layer on the nickel layer and can exhibit oxidation resistance at high temperatures.
실험예 5. 면저항 측정Experimental Example 5. Sheet resistance measurement
실시예 1 및 비교예 1에서 제조된 니켈판을 400 ℃에서 30 분간 열처리하여 열처리 전과 후의 면 저항을 측정하고, 이에 대한 결과를 도 5로 나타내었다.The nickel plates prepared in Example 1 and Comparative Example 1 were heat treated at 400°C for 30 minutes to measure sheet resistance before and after heat treatment, and the results are shown in Figure 5.
도 5에 나타난 바와 같이, 비교예 1의 니켈판의 경우 열처리 이후에 면저항값이 급격하게 증가한 반면, 실시예 1에서 제조된 실리콘이 코팅된 니켈판은 열처리 이후에도 큰 변화가 나타나지 않았다.As shown in Figure 5, in the case of the nickel plate of Comparative Example 1, the sheet resistance value rapidly increased after heat treatment, while the silicon-coated nickel plate manufactured in Example 1 did not show a significant change even after heat treatment.
상기와 같은 결과를 통해, 본 발명에 따른 실리콘이 코팅된 니켈은 전기적 특성을 유지하면서 산화에 대한 저항 특성을 나타내는 것을 확인하였다.Through the above results, it was confirmed that nickel coated with silicon according to the present invention exhibits resistance to oxidation while maintaining electrical properties.
실험예 6. 침투 깊이에 따른 산소 에너지 차이 측정Experimental Example 6. Measurement of oxygen energy difference according to penetration depth
실시예 1에서 제조된 실리콘이 코팅된 니켈판의 표면 밖에 있는 상태의 에너지를 기준으로 하여 산소가 니켈 속으로 침투할 때 표면으로부터의 깊이에 따라 에너지를 계산하고 산소가 시료의 표면에 있을 때 계산된 에너지와의 차이를 도 7로 나타내었다.Based on the energy outside the surface of the silicon-coated nickel plate prepared in Example 1, the energy is calculated according to the depth from the surface when oxygen penetrates into nickel, and calculated when oxygen is on the surface of the sample. The difference from the generated energy is shown in Figure 7.
도 7에 나타난 바와 같이, 상기 실시예 1에서 제조된 실리콘이 코팅된 니켈판의 경우 산소가 표면에서 Si-O-Ni 혼합층을 통과하기 위해서는 에너지 장벽을 넘어야 하는 것으로 나타났으며, 상기 에너지 장벽은 산화에 대한 저항을 의미한다.As shown in Figure 7, in the case of the silicon-coated nickel plate prepared in Example 1, it was found that oxygen must overcome an energy barrier in order to pass through the Si-O-Ni mixed layer at the surface, and the energy barrier is It means resistance to oxidation.
상기와 같은 결과를 통해, 본 발명에 따른 실리콘이 코팅된 니켈은 산화에 대한 저항 특성을 나타내는 것을 확인하였다.Through the above results, it was confirmed that nickel coated with silicon according to the present invention exhibits resistance to oxidation.
100. 니켈(Ni)층
200. 사이닉스층
300. 제 1 실리콘(Si)-산소(O) 혼합층
400. 제 2 실리콘(Si)-산소(O) 혼합층100. Nickel (Ni) layer
200. Cynics layer
300. First silicon (Si)-oxygen (O) mixed layer
400. Second silicon (Si)-oxygen (O) mixed layer
Claims (12)
Anti-oxidation nickel coated with silicon in which the cynics layer 200, which is a silicon (Si)-oxygen (O)-nickel (Ni) mixed layer, is formed by depositing silicon (Si).
상기 실리콘이 코팅된 니켈은,
상기 실리콘(Si)이 증착되지 않은 니켈과 유사한 전기저항을 가지는 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 1,
The silicon-coated nickel is,
Anti-oxidation nickel coated with silicon, characterized in that it has an electrical resistance similar to nickel without the silicon (Si) deposited on it.
상기 실리콘이 코팅된 니켈은,
단결정 박막, 다결정 박막, 호일 또는 덩어리인 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 1,
The silicon-coated nickel is,
Anti-oxidation nickel coated with silicon, characterized in that it is a single crystal thin film, a polycrystalline thin film, a foil, or a lump.
상기 실리콘이 코팅된 니켈이 단결정 박막인 경우,
300 내지 500 ℃로 20 내지 50 분 동안 열을 가하여도 산화가 방지되는 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 3,
When the silicon-coated nickel is a single crystal thin film,
Anti-oxidation nickel coated with silicon, characterized in that oxidation is prevented even when heated at 300 to 500 ° C. for 20 to 50 minutes.
상기 실리콘이 코팅된 니켈이 다결정 박막, 호일 또는 덩어리인 경우,
200 ℃ 내지 400 ℃로 열을 가하여도 산화가 방지되는 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 3,
When the silicon-coated nickel is a polycrystalline thin film, foil, or lump,
Anti-oxidation nickel coated with silicon, characterized in that oxidation is prevented even when heated at 200 ℃ to 400 ℃.
상기 실리콘이 코팅된 니켈은,
면저항이 6.2×10-4 내지 6.8×10-4 Ω/□ 인 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 1,
The silicon-coated nickel is,
Anti-oxidation nickel coated with silicon, characterized in that the sheet resistance is 6.2×10 -4 to 6.8×10 -4 Ω/□.
상기 실리콘이 코팅된 니켈은,
니켈층(100);
상기 니켈층(100) 상단에 실리콘(Si)-산소(O)-니켈(Ni)이 혼합되어 형성된 사이닉스층(200);
상기 사이닉스층(200) 상단에 형성된 제 1 실리콘(Si)-산소(O) 혼합층(300); 및
상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 상단에 형성된 제 2 실리콘(Si)-산소(O) 혼합층(400);으로 구성되는 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 1,
The silicon-coated nickel is,
Nickel layer (100);
A cynix layer 200 formed by mixing silicon (Si)-oxygen (O)-nickel (Ni) on top of the nickel layer 100;
A first silicon (Si)-oxygen (O) mixed layer 300 formed on top of the cynics layer 200; and
Anti-oxidation nickel coated with silicon, characterized in that it consists of a second silicon (Si)-oxygen (O) mixed layer (400) formed on top of the first silicon (Si)-oxygen (O) mixed layer (300).
상기 사이닉스층(200)은,
두께가 0.8 내지 1.2 nm 인 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 7,
The Cynics layer 200 is,
Anti-oxidation nickel coated with silicon, characterized in that the thickness is 0.8 to 1.2 nm.
상기 제 1 실리콘(Si)-산소(O) 혼합층(300) 및 상기 제 2 실리콘(Si)-산소(O) 혼합층(400)을 포함하는 실리콘(Si)-산소(O) 혼합층은,
두께가 5 내지 30 nm인 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈.
According to clause 7,
The silicon (Si)-oxygen (O) mixed layer including the first silicon (Si)-oxygen (O) mixed layer 300 and the second silicon (Si)-oxygen (O) mixed layer 400,
Anti-oxidation nickel coated with silicon, characterized in that the thickness is 5 to 30 nm.
A method of manufacturing silicon-coated nickel to prevent oxidation by depositing silicon (Si) on nickel (Ni) through a single sputtering process.
상기 스퍼터링(sputtering)은,
아르곤 분위기 하에서 수행하는 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈 제조방법.
According to clause 10,
The sputtering is,
A method for producing silicon-coated nickel for preventing oxidation, characterized in that it is carried out under an argon atmosphere.
상기 스퍼터링(sputtering)은,
상온 내지 350 ℃에서 1 내지 5 분 동안 수행하는 것을 특징으로 하는 실리콘이 코팅된 산화방지용 니켈 제조방법. According to clause 10,
The sputtering is,
A method for producing silicon-coated nickel for preventing oxidation, characterized in that it is carried out at room temperature to 350 ° C. for 1 to 5 minutes.