KR20230115486A - Mulching vinyl for agricultural having excellent insect resistance and method for preparing the same - Google Patents
Mulching vinyl for agricultural having excellent insect resistance and method for preparing the same Download PDFInfo
- Publication number
- KR20230115486A KR20230115486A KR1020220012030A KR20220012030A KR20230115486A KR 20230115486 A KR20230115486 A KR 20230115486A KR 1020220012030 A KR1020220012030 A KR 1020220012030A KR 20220012030 A KR20220012030 A KR 20220012030A KR 20230115486 A KR20230115486 A KR 20230115486A
- Authority
- KR
- South Korea
- Prior art keywords
- insect repellent
- resin
- mulching vinyl
- resin composition
- weight
- Prior art date
Abstract
본 발명에서는, 방충 성능이 우수함과 동시에 인장강도, 인열강도 등의 물성이 우수한, 농업용 멀칭비닐 및 이의 제조방법을 제공한다.In the present invention, an agricultural mulching vinyl and a manufacturing method thereof, which have excellent insect repellent performance and excellent physical properties such as tensile strength and tear strength, are provided.
Description
본 발명은 방충 성능이 우수한 농업용 멀칭비닐 및 이의 제조방법에 관한 것이다.The present invention relates to agricultural mulching vinyl with excellent insect repellent performance and a manufacturing method thereof.
농업에 적용되는 멀칭비닐은, 눈, 비, 바람, 햇빛, 먼지 등 외부의 자극으로부터 농작물을 보호하는 용도 또는 농작물을 고정 또는 지지하는 용도 등으로 주로 사용되며, 폴리에틸렌, 폴리프로필렌, 에틸렌비닐아세테이트 수지 등의 수지 성분으로 제조된 것이 주로 사용되고 있다.Mulching vinyl applied to agriculture is mainly used to protect crops from external stimuli such as snow, rain, wind, sunlight, dust, etc., or to fix or support crops. Polyethylene, polypropylene, ethylene vinyl acetate resin Those made of resin components such as are mainly used.
한편, 농작물은 불필요한 해충과 균에 노출되어 있어, 해충과 균에 의한 농작물의 성장 저해, 오염, 상품성 저하 등의 문제를 지속적으로 겪어왔다. 이러한 문제를 해결하기 위해, 최근에는 농업용 멀칭비닐에, 방충 성능을 부여하기 위한 다양한 시도들이 계속되고 있다.On the other hand, since crops are exposed to unnecessary pests and fungi, they have continuously suffered problems such as growth inhibition, contamination, and deterioration in marketability of crops caused by pests and fungi. In order to solve this problem, various attempts have recently been made to impart insect repellent performance to agricultural mulching vinyl.
일례로, 대한민국 등록특허 제10-1886020호에서는 항충 물질 준비 단계, 마스터 배치 칩 제조 단계, 마스터 배치 칩 100 내지 300 중량부 및 항충 물질을 5 내지 15 중량부로 혼합하여 혼합 칩을 제조하는 단계 및 혼합 칩을 이용하여, 항충 비닐을 제조하는 단계를 포함하는, 항충 비닐의 제조방법에 대해 개시하고 있다.For example, in Korean Patent Registration No. 10-1886020, preparation of anti-insect materials, preparation of master batch chips, preparation of mixed chips by mixing 100 to 300 parts by weight of master batch chips and 5 to 15 parts by weight of anti-insect materials, and mixing Using a chip, it discloses a method for producing an anti-insect vinyl, including the step of producing an anti-insect vinyl.
그러나, 상기 등록특허를 포함하여 현재까지 개발된, 다수의 방충 성능을 갖는 멀칭비닐은, 방충 성분이 균일하게 분산되지 못하여, 방충 성능이 미미할 뿐 아니라, 방충 성능이 일시적인 문제가 있었다. 또한, 방충 성분에 의해, 멀칭비닐 자체의 내구성과 강도가 저하되어, 사용성 및 수명이 저하되는 문제가 있었다.However, mulching vinyl having a plurality of insect repellent properties developed to date, including the registered patent, has a problem in that the insect repellent component is not uniformly dispersed, and the insect repellent performance is insignificant, as well as the insect repellent performance is temporary. In addition, due to the insect repellent component, the durability and strength of the mulching vinyl itself is lowered, and there is a problem in that usability and lifespan are lowered.
본 발명의 첫 번째 목적은 방충 성능이 우수함과 동시에 인장강도, 인열강도 등의 물성이 우수한, 농업용 멀칭비닐을 제공하는 데에 있다.A first object of the present invention is to provide agricultural mulching vinyl having excellent insect repellent performance and excellent physical properties such as tensile strength and tear strength.
본 발명의 두 번째 목적은 방충 성능이 우수함과 동시에 인장강도, 인열강도 등의 물성이 우수한, 농업용 멀칭비닐을, 단 시간 내에 간단한 방법으로 제조하는 방법을 제공하는 데에 있다.A second object of the present invention is to provide a method for producing agricultural mulching vinyl, which has excellent insect repellent performance and excellent physical properties such as tensile strength and tear strength, in a short time and by a simple method.
본 발명의 목적은 상기된 바와 같은 기술적 과제로 한정되지 않으며, 이하의 설명으로부터 또 다른 기술적 과제가 도출될 수 있다. The object of the present invention is not limited to the technical problem as described above, and another technical problem may be derived from the following description.
상기 첫 번째 목적을 달성하기 위하여, 본 발명은 베이스 수지; 방충 캡슐; 및 분산제;를 포함하는 수지 조성물을 필름 형태로 성형한 것이되, 상기 방충 캡슐은 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는, 방충 성능이 우수한 농업용 멀칭비닐을 제공한다.In order to achieve the above first object, the present invention is a base resin; insect repellent capsules; And a dispersing agent; doedoe molded in the form of a resin composition containing a film, the insect repellent capsule provides an agricultural mulching vinyl having excellent insect repellent performance, including a core containing an insect repellent component and a polymer shell surrounding the core.
상기 수지 조성물은 상기 수지 조성물 총 중량 기준으로 상기 베이스 수지 50 ~ 90 중량%, 상기 방충 캡슐 1 ~ 40 중량% 및 분산제 1 ~ 20 중량%를 포함할 수 있다.The resin composition may include 50 to 90% by weight of the base resin, 1 to 40% by weight of the insect repellent capsule, and 1 to 20% by weight of the dispersant based on the total weight of the resin composition.
상기 베이스 수지는 폴리에틸렌 수지, 폴리프로필렌 수지, 폴리스티렌 수지, 에틸렌비닐아세테이트 수지, 폴리에틸렌테레프탈레이트 수지, 폴리염화비닐 수지, PLA(Poly Lactic Acid) 수지, PBAT(Poly-Butylene Adipate Terephthalate) 수지 및 PBS(butylenesuccinate copolymer) 수지로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The base resin is a polyethylene resin, a polypropylene resin, a polystyrene resin, an ethylene vinyl acetate resin, a polyethylene terephthalate resin, a polyvinyl chloride resin, a poly lactic acid (PLA) resin, a poly-butylene adipate terephthalate (PBAT) resin, and a butylenesuccinate (PBS) resin. copolymer) may include one or more selected from the group consisting of resins.
상기 방충 성분은 피레스로이드계 성분, 유기인계 성분, 네오니코티노이드계 성분, 카바메이트계 성분, 니아신계 성분, 아바멕틴 및 에마멕틴 벤조에이트로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The insect repellent component may include at least one selected from the group consisting of pyrethroid-based components, organophosphorus-based components, neonicotinoid-based components, carbamate-based components, niacin-based components, abamectin, and emamectin benzoate.
상기 분산제는 폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The dispersant may include at least one selected from the group consisting of polystyrene sulfonic acid, polyvinyl sulfonic acid, and polyacrylamide methyl propane sulfonic acid.
상기 두 번째 목적을 달성하기 위하여, 본 발명에서는 베이스 수지; 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 방충 캡슐; 및 분산제;를 포함하는 수지 조성물을 준비하는 제1 단계; 및 상기 수지 조성물을 성형하여, 필름 형태의 멀칭비닐을 제조하는 제2 단계;를 포함하는, 방충 성능이 우수한 농업용 멀칭비닐의 제조방법을 제공한다.In order to achieve the second object, in the present invention, the base resin; An insect repellent capsule comprising a core containing an insect repellent component and a polymer shell surrounding the core; A first step of preparing a resin composition comprising; and a dispersing agent; And a second step of molding the resin composition to produce a mulching vinyl in the form of a film; it provides a method for producing agricultural mulching vinyl having excellent insect repellent performance.
상기 제2 단계에서는 10 아르(a) 당 5 ~ 1,000 그램(g) 농도의 방충 성분을 포함하도록 멀칭비닐을 제조할 수 있다.In the second step, mulching vinyl may be prepared to include an insect repellent component at a concentration of 5 to 1,000 grams (g) per 10 are (a).
본 발명에 따르면, 방충 성능이 우수함과 동시에 인장 강도, 인열 강도, 신장률 등의 물성이 우수한, 농업용 멀칭비닐을 제공할 수 있다. 이에 따라, 본 발명의 농업용 멀칭비닐은 사용성 및 사용 수명이 향상될 수 있다.According to the present invention, it is possible to provide agricultural mulching vinyl having excellent insect repellent performance and excellent physical properties such as tensile strength, tear strength, and elongation. Accordingly, the usability and service life of the agricultural mulching vinyl of the present invention can be improved.
또한, 본 발명에 따르면, 방충 성능, 인장 강도, 인열 강도, 신장률이 우수한 농업용 멀칭비닐을, 단 시간 내에 간단한 방법으로 제조할 수 있다.In addition, according to the present invention, agricultural mulching vinyl excellent in insect repellent performance, tensile strength, tear strength, and elongation can be produced in a short time by a simple method.
아래에서는 첨부한 도면을 참조하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예를 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였다.Hereinafter, embodiments of the present invention will be described in detail so that those skilled in the art can easily practice the present invention with reference to the accompanying drawings. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein. And in order to clearly explain the present invention in the drawings, parts irrelevant to the description are omitted.
본 발명의 명세서 및 청구범위에 사용된 용어 또는 단어는 통상적이거나 사전적인 의미로 한정 해석되지 아니하며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.Terms or words used in the specification and claims of the present invention are not limited to the usual or dictionary meaning, and the inventor can properly define the concept of the term in order to explain his/her invention in the best way. Based on the principle, it should be interpreted as a meaning and concept consistent with the technical idea of the present invention.
본 발명의 명세서 전체에 있어서, 어떤 부분이 어떤 구성 요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. Throughout the specification of the present invention, when a part "includes" a certain component, it means that it may further include other components, not excluding other components unless otherwise stated. .
본 발명의 명세서 전체에 있어서, "A 및/또는 B"는, A 또는 B, 또는 A 및 B를 의미한다.Throughout the specification of the present invention, "A and/or B" means A or B, or A and B.
이하에서 본 발명을 구체적으로 설명하였으나, 본 발명이 이에 제한되는 것은 아니다.Although the present invention has been specifically described below, the present invention is not limited thereto.
본 발명에서는 방충 성능이 우수한 농업용 멀칭비닐을 제공한다.In the present invention, an agricultural mulching vinyl having excellent insect repellent performance is provided.
본 발명의 일 실시예에서는 베이스 수지; 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 방충 캡슐; 및 분산제;를 포함하는 수지 조성물을 필름 형태로 성형한 것으로, 방충 성능이 우수함과 동시에 인장 강도, 인열 강도, 신장률 등의 물성이 향상된, 농업용 멀칭비닐을 제공한다.In one embodiment of the present invention, the base resin; An insect repellent capsule comprising a core containing an insect repellent component and a polymer shell surrounding the core; And a dispersant; by molding a resin composition containing a film form, excellent insect repellent performance and improved physical properties such as tensile strength, tear strength, elongation, etc., provides agricultural mulching vinyl.
이때, 상기 수지 조성물을 필름 형태로 성형하는 것은, 공지된 필름 제조 또는 성형법에 따라, 실시될 수 있다.At this time, molding the resin composition into a film form may be performed according to a known film manufacturing or molding method.
이하에서는 상기 수지 조성물에 대해 상세히 설명하도록 하겠다.Hereinafter, the resin composition will be described in detail.
본 실시예의 수지 조성물은 베이스 수지를 포함한다.The resin composition of this embodiment includes a base resin.
본 실시예의 베이스 수지는 폴리에틸렌 수지, 폴리프로필렌 수지, 폴리스티렌 수지, 에틸렌비닐아세테이트 수지, 폴리에틸렌테레프탈레이트 수지, 폴리염화비닐 수지, PLA(Poly Lactic Acid) 수지, PBAT(Poly-Butylene Adipate Terephthalate) 수지 및 PBS(butylenesuccinate copolymer) 수지로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The base resin of this embodiment is polyethylene resin, polypropylene resin, polystyrene resin, ethylene vinyl acetate resin, polyethylene terephthalate resin, polyvinyl chloride resin, PLA (Poly Lactic Acid) resin, PBAT (Poly-Butylene Adipate Terephthalate) resin and PBS (butylenesuccinate copolymer) may include one or more selected from the group consisting of resins.
본 실시예의 수지 조성물은 상기 수지 조성물 총 중량 기준으로 베이스 수지를 50 ~ 90 중량%, 구체적으로는 50 ~ 70 중량%, 더 구체적으로는 55 ~ 65 중량%로 포함할 수 있다. 특히, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 베이스 수지를 55 ~ 65 중량%로 포함할 때, 방충 성능이 우수하면서도 물성이 향상된, 농업용 멀칭비닐을 제공할 수 있다.The resin composition of this embodiment may include 50 to 90% by weight, specifically 50 to 70% by weight, more specifically 55 to 65% by weight of the base resin based on the total weight of the resin composition. In particular, when the resin composition of this embodiment includes 55 to 65% by weight of the base resin based on the total weight of the resin composition, it is possible to provide agricultural mulching vinyl with excellent insect repellent performance and improved physical properties.
만약, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 베이스 수지를 50 중량% 미만으로 포함할 경우, 베이스 수지를 50 ~ 90 중량%로 포함하는 경우 보다, 멀칭비닐의 물성이 저하될 수 있다. 반면, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 베이스 수지를 90 중량% 초과로 포함할 경우, 베이스 수지를 50 ~ 90 중량%로 포함하는 경우 보다, 방충 성능의 향상 정도가 미미할 수 있다.If the resin composition of this embodiment contains less than 50% by weight of the base resin based on the total weight of the resin composition, the physical properties of mulching vinyl may be lowered than when the base resin is included in 50 to 90% by weight. . On the other hand, when the resin composition of the present embodiment includes more than 90% by weight of the base resin based on the total weight of the resin composition, the degree of improvement in insect repellent performance may be insignificant compared to the case where the base resin is included in 50 to 90% by weight. .
본 실시예의 수지 조성물은 방충 캡슐을 포함한다.The resin composition of this embodiment includes an insect repellent capsule.
본 실시예의 수지 조성물은 방충 캡슐을 포함하되, 상기 방충 캡슐은 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 코어-쉘 구조로 형성된 것일 수 있다.The resin composition of this embodiment includes an insect repellent capsule, but the insect repellent capsule may be formed of a core-shell structure including a core containing an insect repellent component and a polymer shell surrounding the core.
이때, 상기 방충 캡슐을 기준으로 하여, 방충 캡슐에서 방충 성분을 포함하는 코어와 상기 코어를 감싸는 고분자 쉘의 함량은 특별히 제한되지 않으며, 최종 멀칭비닐에서 10 아르(a) 당 5 ~ 1,000 그램(g) 농도의 방충 성분이 포함될 수 있도록, 방충 성분과 고분자를 포함할 수 있다.At this time, based on the insect repellent capsule, the content of the core containing the insect repellent component in the insect repellent capsule and the polymer shell surrounding the core is not particularly limited, and 5 to 1,000 grams per 10 are (a) in the final mulching vinyl (g ) may contain insect repellent ingredients and polymers so that the concentration of insect repellent ingredients can be included.
예를 들어, 상기 방충 캡슐에서, 상기 방충 성분 및 상기 고분자는 0.00001 ~ 10 : 1, 0.0001 ~ 10 : 1, 0.001 ~ 10 : 1, 0.01 ~ 10 : 1, 0.1 ~ 10 : 1, 또는 1 ~ 10 : 1 의 중량비로 포함될 수 있으나, 이에 제한되지 않으며, 방충 캡슐에서 방충 성분의 함량을 제외한 나머지 함량은 모두 고분자 쉘의 함량을 의미할 수 있다.For example, in the insect repellent capsule, the insect repellent component and the polymer are 0.00001 to 10: 1, 0.0001 to 10: 1, 0.001 to 10: 1, 0.01 to 10: 1, 0.1 to 10: 1, or 1 to 10 : It may be included in a weight ratio of 1, but is not limited thereto, and all other contents except for the content of the insect repellent component in the insect repellent capsule may refer to the content of the polymer shell.
본 실시예의 방충 성분은 피레스로이드계 성분, 유기인계 성분, 네오니코티노이드계 성분, 카바메이트계 성분, 니아신계 성분, 아바멕틴 및 에마멕틴 벤조에이트로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The insect repellent component of this embodiment may include at least one selected from the group consisting of pyrethroid-based components, organophosphorus-based components, neonicotinoid-based components, carbamate-based components, niacin-based components, abamectin, and emamectin benzoate. there is.
이때, 상기 피레스로이드계 성분은 비펜트린, 에토펜프록스, 펜발러레이트, 델타메트린, 테플루트린, 사이플루트린 및 사이퍼메트린으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.In this case, the pyrethroid-based component may include at least one selected from the group consisting of bifenthrin, etofenprox, penvalerate, deltamethrin, tefluthrin, cyfluthrin, and cypermethrin, but is limited thereto It doesn't work.
상기 유기인계 성분은 터부포스, 카두사포스, 에토프로포스, 포스티아제이트 및 포레이트로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.The organophosphorus component may include one or more selected from the group consisting of terbufos, cardusaphos, etoprofos, phosthiazate, and phorate, but is not limited thereto.
상기 네오니코티노이드계 성분은 아세타미프리드, 디노테퓨란, 이미다클로프리드 및 티아메톡삼으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.The neonicotinoid-based component may include at least one selected from the group consisting of acetamiprid, dinotefuran, imidacloprid, and thiamethoxam, but is not limited thereto.
상기 카바메이트계 성분은 카보설판 및 벤퓨라카브로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.The carbamate-based component may include at least one selected from the group consisting of carbosulfan and benfuracarb, but is not limited thereto.
상기 니아신계 성분은 플로니카미드를 포함할 수 있으나, 이에 제한되지 않는다.The niacin-based component may include flonicamide, but is not limited thereto.
본 실시예에서, 상기 쉘을 형성하는 고분자는 아크릴계 고분자 및 우레탄계 고분자로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.In this embodiment, the polymer forming the shell may include at least one selected from the group consisting of acrylic polymers and urethane polymers, but is not limited thereto.
본 실시예의 수지 조성물은 상기 수지 조성물 총 중량 기준으로 방충 캡슐을 1 ~ 40 중량%, 구체적으로는 5 ~ 35 중량%, 더 구체적으로는 20 ~ 40 중량%로 포함할 수 있다. 특히, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 방충 캡슐을 20 ~ 40 중량%로 포함할 때, 방충 성능이 우수하면서도 물성이 향상된, 농업용 멀칭비닐을 제공할 수 있다.The resin composition of this embodiment may include 1 to 40% by weight, specifically 5 to 35% by weight, more specifically 20 to 40% by weight of the insect repellent capsule based on the total weight of the resin composition. In particular, when the resin composition of this embodiment includes 20 to 40% by weight of the insect repellent capsule based on the total weight of the resin composition, it is possible to provide agricultural mulching vinyl with excellent insect repellent performance and improved physical properties.
만약, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 방충 캡슐을 1 중량% 미만으로 포함할 경우, 방충 캡슐을 1 ~ 40 중량%로 포함하는 경우 보다, 방충 성능의 향상 정도가 미미할 수 있다. 반면, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 방충 캡슐을 40 중량% 초과로 포함할 경우, 방충 캡슐을 1 ~ 40 중량%로 포함하는 경우 보다, 물성이 저하될 수 있다.If the resin composition of this embodiment contains less than 1% by weight of the insect repellent capsule based on the total weight of the resin composition, the degree of improvement in insect repellent performance may be insignificant compared to the case of including 1 to 40% by weight of the insect repellent capsule. . On the other hand, when the resin composition of this embodiment includes more than 40% by weight of the insect repellent capsule based on the total weight of the resin composition, physical properties may be lowered than when the resin composition includes 1 to 40% by weight of the insect repellent capsule.
본 실시예의 수지 조성물은 분산제를 포함한다.The resin composition of this embodiment contains a dispersing agent.
본 실시예의 분산제는 폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산으로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.The dispersant of this embodiment may include at least one selected from the group consisting of polystyrene sulfonic acid, polyvinyl sulfonic acid, and polyacrylamide methyl propane sulfonic acid.
구체적으로, 본 실시예의 분산제는 폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산을 포함할 수 있으며, 이 경우, 본 실시예에 따르는 멀칭비닐의 방충 성능 및 물성은 더욱 향상될 수 있다.Specifically, the dispersant of this embodiment may include polystyrenesulfonic acid, polyvinylsulfonic acid, and polyacrylamidemethylpropanesulfonic acid, and in this case, the insect repellent performance and physical properties of the mulching vinyl according to this embodiment can be further improved.
더 구체적으로, 본 실시예의 분산제는 폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산을 1 : 0.1 ~ 1 : 7 ~ 15 의 중량비로 포함할 수 있으며, 이 경우, 본 실시예에 따르는 멀칭비닐의 방충 성능 및 물성은 더욱 우수할 수 있다.More specifically, the dispersant of the present embodiment may include polystyrenesulfonic acid, polyvinylsulfonic acid, and polyacrylamidemethylpropanesulfonic acid in a weight ratio of 1:0.1 to 1:7 to 15, in which case, the mulching vinyl according to the present embodiment The insect repellent performance and physical properties of may be more excellent.
가장 구체적으로, 본 실시예의 분산제는 폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산을 1 : 0.1 ~ 1 : 10 ~ 12 의 중량비로 포함할 수 있으며, 이 경우, 본 실시예에 따르는 멀칭비닐의 방충 성능 및 물성은 현저히 우수할 수 있다.Most specifically, the dispersant of this embodiment may include polystyrenesulfonic acid, polyvinylsulfonic acid, and polyacrylamidemethylpropanesulfonic acid in a weight ratio of 1:0.1 to 1:10 to 12, in which case, the mulching vinyl according to this embodiment The insect repellent performance and physical properties of can be remarkably excellent.
본 실시예의 수지 조성물은 상기 수지 조성물 총 중량 기준으로 분산제를 1 ~ 20 중량%, 구체적으로는 10 ~ 12 중량%로 포함할 수 있다. 특히, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 분산제를 10 ~ 12 중량%로 포함할 때, 방충 성능이 우수하면서도 물성이 향상된, 농업용 멀칭비닐을 제공할 수 있다.The resin composition of this embodiment may include 1 to 20% by weight, specifically 10 to 12% by weight of the dispersant based on the total weight of the resin composition. In particular, when the resin composition of this embodiment includes 10 to 12% by weight of the dispersant based on the total weight of the resin composition, it is possible to provide agricultural mulching vinyl with excellent insect repellent performance and improved physical properties.
만약, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 분산제를 1 중량% 미만으로 포함할 경우, 분산제를 1 ~ 20 중량%로 포함하는 경우 보다, 방충 캡슐의 분산성 향상 효과가 미미하여, 방충 성능의 향상 정도가 미미할 수 있다. 반면, 본 실시예의 수지 조성물이 상기 수지 조성물 총 중량 기준으로 분산제를 20 중량% 초과로 포함할 경우, 분산제를 1 ~ 20 중량%로 포함하는 경우 보다, 방충 성능 및 물성이 저하될 수 있다.If the resin composition of this embodiment contains less than 1% by weight of the dispersant based on the total weight of the resin composition, the effect of improving the dispersibility of the insect repellent capsule is insignificant compared to the case of containing 1 to 20% by weight of the dispersant, The degree of improvement in performance may be insignificant. On the other hand, when the resin composition of the present embodiment includes more than 20% by weight of the dispersant based on the total weight of the resin composition, the insect repellent performance and physical properties may be lowered than when the dispersant is included in 1 to 20% by weight.
본 실시예의 수지 조성물은 항균 성분을 더 포함할 수 있다.The resin composition of this embodiment may further include an antibacterial component.
예를 들어, 상기 향균 성분은 만코제브(mancozeb), 티아디닐(tianidil), 은 나노 입자 및 식물 유래의 항균성 폴리페놀계 화합물로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.For example, the antibacterial component may include at least one selected from the group consisting of mancozeb, tianidil, silver nanoparticles, and plant-derived antibacterial polyphenolic compounds, but is not limited thereto. don't
이때, 상기 식물 유래 항균성 폴리페놀계 화합물은 은행잎 추출물, 녹차 추출물, 커피콩 추출물, 편백나무추출물, 측백나무추출물, 노간주나무추출물, 삼나무추출물, 솔잎추출물, 당귀추출물, 천궁추출물, 산조인추출물, 쑥추출물, 계피추출물, 건강추출물, 상엽추출물, 죽엽추출물 및 숯으로 이루어진 군에서 선택되는 하나 이상을 포함하는 식물에서 유래된 것일 수 있으나, 이에 제한되지 않는다.At this time, the plant-derived antibacterial polyphenolic compound is ginkgo leaf extract, green tea extract, coffee bean extract, cypress extract, arborvitae extract, juniper extract, cedar extract, pine needle extract, angelica extract, cnidium extract, sanjoin extract, mugwort extract , cinnamon extract, health extract, leaf extract, bamboo leaf extract, and may be derived from plants containing at least one selected from the group consisting of charcoal, but is not limited thereto.
본 실시예의 수지 조성물은 공지의 첨가제를 더 포함할 수 있다.The resin composition of this embodiment may further include known additives.
예를 들어, 상기 첨가제는 소포제, 경화제, 경화보조제, 계면활성제, 피막형성제, 산화방지제, 노화방지제, 분산 안정제, 현탁화제, 불투명화제, 킬레이트제, 유기 용매, 물, 이형제, 안료 및 염료로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있으나, 이에 제한되지 않는다.For example, the additives include antifoaming agents, curing agents, curing aids, surfactants, film forming agents, antioxidants, antiaging agents, dispersion stabilizers, suspending agents, opacifying agents, chelating agents, organic solvents, water, release agents, pigments and dyes. It may include one or more selected from the group consisting of, but is not limited thereto.
또한, 본 발명에서는 방충 성능이 우수한 농업용 멀칭비닐의 제조방법을 제공한다.In addition, the present invention provides a method for manufacturing agricultural mulching vinyl having excellent insect repellent performance.
본 발명의 다른 실시예에서는 베이스 수지; 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 방충 캡슐; 및 분산제;를 포함하는 수지 조성물을 준비하는 제1 단계; 및 상기 수지 조성물을 성형하여, 필름 형태의 멀칭비닐을 제조하는 제2 단계;를 포함함에 따라, 간단한 방법으로 단 시간 내에, 방충 성능 및 물성이 우수한, 농업용 멀칭비닐의 제조방법을 제공한다.In another embodiment of the present invention, the base resin; An insect repellent capsule comprising a core containing an insect repellent component and a polymer shell surrounding the core; A first step of preparing a resin composition comprising; and a dispersing agent; And a second step of producing mulching vinyl in the form of a film by molding the resin composition; thereby providing a method for producing agricultural mulching vinyl with excellent insect repellent performance and physical properties in a short time by a simple method.
(a)수지 조성물을 준비하는 제1 단계(a) first step of preparing a resin composition
본 실시예의 제1 단계에서는 베이스 수지; 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 방충 캡슐; 및 분산제;를 포함하는 수지 조성물을 제조할 수 있다. 이때, 상기 수지 조성물은 상기된 농업용 멀칭비닐의 내용을 따른다.In the first step of this embodiment, the base resin; An insect repellent capsule comprising a core containing an insect repellent component and a polymer shell surrounding the core; And a dispersing agent; it is possible to prepare a resin composition comprising a. At this time, the resin composition follows the contents of the agricultural mulching vinyl described above.
(b)필름 형태의 멀칭비닐을 제조하는 제2 단계;(b) a second step of preparing a mulching vinyl in the form of a film;
본 실시예의 제2 단계에서는 상기 제1 단계에 따라 제조된 수지 조성물을, 공지의 방법으로 성형함으로써, 필름 형태의 멀칭비닐을 제조할 수 있다.In the second step of the present embodiment, the resin composition prepared in the first step may be molded by a known method, thereby producing a film-type mulched vinyl.
본 실시예의 수지 조성물에는 공지의 첨가제가 더 혼합될 수 있다. 이때, 공지의 첨가제는 항균제, 소포제, 경화제, 경화보조제, 계면활성제, 피막형성제, 산화방지제, 노화방지제, 분산 안정제, 현탁화제, 불투명화제, 킬레이트제, 유기 용매, 물, 이형제, 안료 및 염료로 이루어진 군에서 선택되는 하나 이상을 포함할 수 있다.Known additives may be further mixed in the resin composition of this embodiment. At this time, the known additives are antibacterial agents, antifoaming agents, curing agents, curing aids, surfactants, film forming agents, antioxidants, antiaging agents, dispersion stabilizers, suspending agents, opacifying agents, chelating agents, organic solvents, water, release agents, pigments and dyes. It may include one or more selected from the group consisting of.
본 실시예의 제1 단계 및 제2 단계에 따라, 멀칭비닐을 제조하되, 10 아르(a) 당 5 ~ 1,000 그램(g) 농도의 방충 성분을 포함하도록 멀칭비닐을 제조할 수 있다. 상기 방충 성분의 농도는 방충 캡슐 내 방충 성분의 함량 또는 수지 조성물 내 방충 캡슐의 함량을 조절하거나, 수지 조성물에 공지의 첨가제를 더 혼합함으로써, 조절될 수 있다.According to the first and second steps of this embodiment, mulching vinyl may be prepared, but the mulching vinyl may be prepared to include an insect repellent component at a concentration of 5 to 1,000 grams (g) per 10 are (a). The concentration of the insect repellent component may be adjusted by adjusting the content of the insect repellent component in the insect repellent capsule or the content of the insect repellent capsule in the resin composition, or by further mixing a known additive to the resin composition.
만약, 본 실시예의 제2 단계에서, 10 아르(a) 당 5 그램(g) 농도 미만의 방충 성분을 포함하도록 멀칭비닐을 제조할 경우에는, 방충 성능이 미미할 수 있다. 반면, 본 실시예의 제2 단계에서, 10 아르(a) 당 1,000 그램(g) 농도 초과의 방충 성분을 포함하도록 멀칭비닐을 제조할 경우에는, 물성이 저하되며, 환경에 유해할 수 있다.If, in the second step of this embodiment, when the mulching vinyl is manufactured to include an insect repellent component of less than 5 grams (g) per 10 are (a), the insect repellent performance may be insignificant. On the other hand, in the second step of this embodiment, when the mulching vinyl is prepared to include an insect repellent component of more than 1,000 grams (g) per 10 ares (a), physical properties are deteriorated and it may be harmful to the environment.
이하 실시예, 비교예, 및 실험예를 통하여 본 발명의 방충 성능이 우수한 농업용 멀칭비닐 및 이의 제조방법에 대해 구체적으로 설명하기로 한다. 이들 실시예는 단지 본 발명을 예시하기 위한 것이므로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다.Hereinafter, the agricultural mulching vinyl having excellent insect repellent performance and its manufacturing method will be described in detail through Examples, Comparative Examples, and Experimental Examples. Since these examples are intended to illustrate the present invention only, the scope of the present invention is not to be construed as being limited by these examples.
[ 실시예 ][Example]
실시예 1 내지 4Examples 1 to 4
표 1[단위 : 중량%]에 따라 각 성분을 혼합하되, 분산제는 표 2[단위 : 중량비]에 따라 폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산이 혼합된 것을 사용하였다.Each component was mixed according to Table 1 [unit: weight%], but the dispersant was a mixture of polystyrenesulfonic acid, polyvinylsulfonic acid and polyacrylamidemethylpropanesulfonic acid according to Table 2 [unit: weight ratio].
이어서, 상기 수지 조성물을 필름 형태로 성형하여, 10 아르(a) 당 100 그램(g) 농도의 방충 성분을 포함하는 멀칭비닐(두께 : 0.03 mm)을 제조하였다.Subsequently, the resin composition was molded into a film form to prepare mulching vinyl (thickness: 0.03 mm) containing an insect repellent component at a concentration of 100 grams (g) per 10 are (a).
표 1에서 베이스 수지는 PBAT(Poly-Butylene Adipate Terephthalate) 수지를 사용하였다.In Table 1, the base resin was PBAT (Poly-Butylene Adipate Terephthalate) resin.
또한, 상기 방충 캡슐은 비펜트린을 포함하는 코어 및 아크릴레이트/C10-30알킬아크릴레이트크로스폴리머로 형성된 쉘의 코어-쉘 구조로 형성된 것이되, 최종 멀칭비닐에서 10 아르(a) 당 100 그램(g) 농도의 방충 성분이 함유되도록, 비펜트린을 포함하는 것을 사용하였다. 이때, 상기 방충 캡슐에서, 방충 성분의 함량을 제외하고는 고분자 쉘의 함량을 의미한다.In addition, the insect repellent capsule is formed of a core-shell structure of a core containing bifenthrin and a shell formed of acrylate/C10-30 alkyl acrylate crosspolymer, and 100 grams per 10 are (a) in the final mulched vinyl. (g) To contain the insect repellent component of the concentration, one containing bifenthrin was used. At this time, in the insect repellent capsule, it means the content of the polymer shell except for the content of the insect repellent component.
[ 비교예 ][Comparative Example]
비교예 1 내지 6Comparative Examples 1 to 6
표 3[단위 : 중량%]에 따라 각 성분이 혼합된 수지 조성물을 사용한 것을 제외하고는, 실시예 2와 동일하게 실시하였다. 이때, 방충 캡슐 또한, 실시예 2의 것을 그대로 함량만 조절하여 사용하였다.It was carried out in the same manner as in Example 2, except that the resin composition in which each component was mixed according to Table 3 [unit: weight%] was used. At this time, the insect repellent capsule was also used by adjusting only the content of Example 2 as it is.
비교예 7 내지 9Comparative Examples 7 to 9
분산제로 하기 표 4에서 '○' 표기된 것만을 사용한 것을 제외하고는, 실시예 2와 동일하게 제조하였다.It was prepared in the same manner as in Example 2, except that only those marked with '○' in Table 4 were used as dispersants.
[ 실험예 ][Experimental example]
실험예 1 : 방충 성능 평가Experimental Example 1: Evaluation of insect repellent performance
농촌진흥청 고시 '농약의 등록기준 약효 및 약해 시험기준과 방법'에 따라, 방충 성능을 평가하고, 그 결과를 표 5[단위 : 개]에 나타내었다.In accordance with the Rural Development Administration notification, 'Efficacy and Weakness Test Criteria and Methods for Registration Criteria of Pesticides', the insect repellent performance was evaluated, and the results are shown in Table 5 [unit: pieces].
이때, 방충 성능은, 벼룩잎벌레에 대한 피해구멍수를 3회 반복한 평균값을 확인함으로써 평가하였으며, 피해구멍수가 적을수록 방충 성능이 우수함을 의미한다.At this time, the insect repellent performance was evaluated by checking the average value obtained by repeating the number of damaged holes against the flea leaf beetle three times, and the smaller the number of damaged holes, the better the insect repellent performance.
- 대상해충 : 벼룩잎벌레(Phyllotreta striolate)- Target pest: Flea leaf beetle ( Phyllotreta striolate )
- 시험작물(품종) : 배추(휘모리골드)- Test crop (variety): Cabbage (Hwimori Gold)
- 무처리 : 일반 멀칭비닐 사용- Untreated: use general mulching vinyl
- 대조군 : 디노테퓨란 입제(3kg/10a)를 토양에 처리한 후, 멀칭비닐 적용- Control group: After treating the soil with dinotefuran granules (3kg/10a), apply mulching vinyl
표 5를 보면, 본 실시예에 따를 경우, 벼룩잎벌레에 의한 피해구멍수가 현저히 줄어드는 바, 방충 성능이 우수함을 알 수 있다.Looking at Table 5, it can be seen that according to this embodiment, the number of holes damaged by flea leaf beetles is significantly reduced, and the insect repellent performance is excellent.
실험예 2 : 물성 평가Experimental Example 2: Evaluation of physical properties
SPS-KPS M 1001-0806 : 2018에 따라, 실시예 및 비교예의 인장 강도(N/cm2), 인열 강도(N/cm) 및 신장률(%)을 평가하고, 그 결과를 표 6에 나타내었다.According to SPS-KPS M 1001-0806: 2018, the tensile strength (N / cm 2 ), tear strength (N / cm) and elongation (%) of Examples and Comparative Examples were evaluated, and the results are shown in Table 6 .
표 6을 보면, 본 실시예에 따르는 실시예 2의 경우, 우수한 인열 강도, 인장 강도, 신장률을 보임을 알 수 있다.Looking at Table 6, it can be seen that in the case of Example 2 according to this embodiment, excellent tear strength, tensile strength, and elongation are exhibited.
전술한 바와 같이, 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 기술을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.As described above, the description of the present invention is for illustrative purposes, and those skilled in the art to which the present invention pertains can easily be modified into other specific forms without changing the technical spirit or essential features of the present invention. You will understand. Therefore, it should be understood that the embodiments described above are illustrative in all respects and not restrictive. For example, each component described as a single type may be implemented in a distributed manner, and similarly, components described as distributed may be implemented in a combined form.
본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is indicated by the following claims rather than the detailed description above, and all changes or modifications derived from the meaning and scope of the claims and equivalent concepts should be construed as being included in the scope of the present invention. do.
Claims (7)
상기 방충 캡슐은
방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐.
A resin composition comprising a base resin, an insect repellent capsule and a dispersant is molded into a film form,
The insect repellent capsule
An agricultural mulching vinyl with excellent insect repellent performance, characterized in that it comprises a core containing an insect repellent component and a polymer shell surrounding the core.
상기 수지 조성물은
상기 수지 조성물 총 중량 기준으로 상기 베이스 수지 50 ~ 90 중량%, 상기 방충 캡슐 1 ~ 40 중량% 및 분산제 1 ~ 20 중량%를 포함하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐.
According to claim 1,
The resin composition
Agricultural mulching vinyl with excellent insect repellent performance, characterized in that it comprises 50 to 90% by weight of the base resin, 1 to 40% by weight of the insect repellent capsule and 1 to 20% by weight of the dispersant based on the total weight of the resin composition.
상기 베이스 수지는
폴리에틸렌 수지, 폴리프로필렌 수지, 폴리스티렌 수지, 에틸렌비닐아세테이트 수지, 폴리에틸렌테레프탈레이트 수지, 폴리염화비닐 수지, PLA(Poly Lactic Acid) 수지, PBAT(Poly-Butylene Adipate Terephthalate) 수지 및 PBS(butylenesuccinate copolymer) 수지로 이루어진 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐.
According to claim 1,
The base resin is
Polyethylene resin, polypropylene resin, polystyrene resin, ethylene vinyl acetate resin, polyethylene terephthalate resin, polyvinyl chloride resin, PLA (Poly Lactic Acid) resin, PBAT (Poly-Butylene Adipate Terephthalate) resin, and PBS (butylenesuccinate copolymer) resin. Characterized in that it comprises at least one selected from the group consisting of, agricultural mulching vinyl with excellent insect repellent performance.
상기 방충 성분은
피레스로이드계 성분, 유기인계 성분, 네오니코티노이드계 성분, 카바메이트계 성분, 니아신계 성분, 아바멕틴 및 에마멕틴 벤조에이트로 이루어진 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐.
According to claim 1,
The insect repellent component
Insect repellent performance, characterized in that it comprises at least one selected from the group consisting of pyrethroid-based components, organophosphorus-based components, neonicotinoid-based components, carbamate-based components, niacin-based components, abamectin and emamectin benzoate This excellent agricultural mulching vinyl.
상기 분산제는
폴리스티렌술폰산, 폴리비닐술폰산 및 폴리아크릴아미드메틸프로판술폰산으로 이루어진 군에서 선택되는 하나 이상을 포함하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐.
According to claim 1,
The dispersing agent
Polystyrene sulfonic acid, polyvinyl sulfonic acid and polyacrylamide methyl propane sulfonic acid characterized in that it comprises at least one selected from the group consisting of, agricultural mulching vinyl with excellent insect repellent performance.
베이스 수지; 방충 성분을 포함하는 코어 및 상기 코어를 감싸는 고분자 쉘을 포함하는 방충 캡슐; 및 분산제;를 포함하는 수지 조성물을 준비하는 제1 단계; 및
상기 수지 조성물을 성형하여, 필름 형태의 멀칭비닐을 제조하는 제2 단계;를 포함하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐의 제조방법.
A method for producing the mulching vinyl according to claim 1,
base resin; An insect repellent capsule comprising a core containing an insect repellent component and a polymer shell surrounding the core; A first step of preparing a resin composition comprising; and a dispersing agent; and
A method for producing agricultural mulching vinyl having excellent insect repellent performance, comprising: a second step of molding the resin composition to produce a film-type mulching vinyl.
상기 제1 단계 및 상기 제2 단계에서는
10 아르(a) 당 5 ~ 1,000 그램(g) 농도의 방충 성분을 포함하도록 멀칭비닐을 제조하는 것을 특징으로 하는, 방충 성능이 우수한 농업용 멀칭비닐의 제조방법.
According to claim 6,
In the first step and the second step
A method for producing agricultural mulching vinyl having excellent insect repellent performance, characterized in that the mulching vinyl is prepared to contain an insect repellent component at a concentration of 5 to 1,000 grams (g) per 10 are (a).