KR20230094356A - Biodegradable hot-melt adhesive composition - Google Patents
Biodegradable hot-melt adhesive composition Download PDFInfo
- Publication number
- KR20230094356A KR20230094356A KR1020210183468A KR20210183468A KR20230094356A KR 20230094356 A KR20230094356 A KR 20230094356A KR 1020210183468 A KR1020210183468 A KR 1020210183468A KR 20210183468 A KR20210183468 A KR 20210183468A KR 20230094356 A KR20230094356 A KR 20230094356A
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive composition
- melt adhesive
- hot melt
- wax
- biodegradable
- Prior art date
Abstract
Description
본 발명은 생분해성 핫멜트 접착 조성물에 관한 것이다.The present invention relates to a biodegradable hot melt adhesive composition.
접착제는 물체와 물체를 접합하는 특수한 성질을 가진 고분자 물질이다. 이 중 핫멜트 접착제는 일회용 부직포 제품, 예를 들어 일회용 기저귀, 성인 요실금 제품 및 여성용 위생 제품뿐만 아니라, 감압 점착제, 목재의 접착, 식품용 필름 접착, 종이 제본 등 다양한 분야에서 다양한 용도로 널리 사용되고 있으며, 일반적으로 150 내지 250℃의 고온에서 가열하여 용융 상태로 기재에 적용한 후 냉각시킴에 따라 접착 성능을 나타내고, 간단한 공정으로 대량 생산이 용이한 장점을 가진다.Adhesives are polymeric substances with special properties that bond objects to objects. Among them, hot melt adhesives are widely used for various purposes in various fields such as disposable nonwoven products, such as disposable diapers, adult incontinence products, and feminine hygiene products, as well as pressure-sensitive adhesives, wood adhesion, food film adhesion, and paper binding. Generally, it is heated at a high temperature of 150 to 250 ° C., applied to a substrate in a molten state, and then cooled to show adhesive performance, and has the advantage of being easy to mass-produce through a simple process.
그러나, 기존의 핫멜트 접착제는 기재에 대해 우수한 접착성, 도포성 및 용융 특성을 가지기는 하나, 생분해성이 없는 에틸렌 비닐 아세테이트(Ethylene Vinyl Acetate, EVA)를 베이스 폴리머로 하는 경우가 대부분이므로 환경오염 문제를 야기할 수 있다. 한편, 오늘날 환경에 대한 관심이 계속 증가하고 있어, 친환경적인 일회용품 등을 제조하기 위해서는, 제품을 구성하는 기재는 물론, 이들 기재를 접착하는 접착 조성물 역시 생분해성을 가질 필요가 있다. However, existing hot melt adhesives have excellent adhesion to substrates, coating properties, and melting properties, but most of them use non-biodegradable ethylene vinyl acetate (EVA) as a base polymer, so environmental pollution problems are avoided. can cause On the other hand, as interest in the environment continues to increase today, in order to manufacture environmentally friendly disposable products, substrates constituting the product as well as adhesive compositions for bonding these substrates need to have biodegradability.
한편, 생분해성 고분자는 크게 천연물 합성계, 화학 합성계, 미생물 합성계의 3종류로 나뉘며, 식물체 등 천연물을 가소화, 단량체 및 축중합시키는 천연물 합성계 생분해성 고분자로는 PLA(Poly lactic acid), TPS(Thermo plastics starch), AP(Aliphatic polyester), CA(Cellulose acetate), CDA(Cellulose di acetate) 등이 있으며, 화학 합성계 생분해성 고분자로는 PBS(Poly butylene succinate), PCL(Poly capro lactone), PEU(Poly ester urethane), PGA(Ploy glycolic acid), PBAT (Polybutylene adipate terephthalate) 등이 있고, 미생물 합성계 생분해성 고분자로는 PHA(Poly hydroxy alkanoic acid), PHB(Poly 3-hydroxybutyrate), PHV(Poly 3-hydroxy valerate), Pullulan(풀루란) 등이 있다.On the other hand, biodegradable polymers are largely divided into three types: natural product synthesis, chemical synthesis, and microbial synthesis. Natural product synthesis biodegradable polymers that plasticize, monomer, and condensate natural products such as plants include PLA (Poly lactic acid) and TPS (Thermo plastics starch), AP (Aliphatic polyester), CA (Cellulose acetate), CDA (Cellulose di acetate), etc. Chemical synthetic biodegradable polymers include PBS (Poly butylene succinate), PCL (Poly capro lactone), PEU (Poly ester urethane), PGA (Ploy glycolic acid), PBAT (Polybutylene adipate terephthalate), and microbial synthetic biodegradable polymers include PHA (Poly hydroxy alkanoic acid), PHB (Poly 3-hydroxybutyrate), PHV (Poly 3-hydroxy valerate) and Pullulan.
이 중 석유 기반의 생분해성 고분자인 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephthalate, PBAT)는 지방족 글리콜로서의 1,4-BD(1,4-Butanediol dimethyl terephthalate)와 방향족 성분인 DMT(Dimethyl terephthalate)을 원료로 하여 에스테르반응과 축중합반응을 거쳐 얻어진 중합물로, 생분해성이 우수하다. Among them, polybutylene adipate terephthalate (PBAT), a petroleum-based biodegradable polymer, contains 1,4-BD (1,4-Butanediol dimethyl terephthalate) as an aliphatic glycol and dimethyl terephthalate (DMT) as an aromatic component. As a raw material, it is a polymer obtained through esterification and condensation polymerization, and has excellent biodegradability.
이에, 폴리부틸렌 아디페이트 테레프탈레이트를 생분해성 접착제의 주요 성분으로 포함시켜 생분해도를 향상시키고자 하는 시도들이 이어져 왔으나, PBAT의 강한 고분자 사슬간의 얽힘(entanglement)에 의한 높은 강성(stiffness)과 타 성분과의 상용성 등 문제로 인하여, 핫멜트 접착제로 활용하기 어려운 문제가 있다. Accordingly, attempts have been made to improve biodegradability by including polybutylene adipate terephthalate as a main component of biodegradable adhesives, but the high stiffness and other problems due to entanglement between strong polymer chains of PBAT have been continued. Due to problems such as compatibility with components, there is a problem that is difficult to utilize as a hot melt adhesive.
이에, 본 발명자들은, 강한 고분자 사슬간의 얽힘에 의한 높은 강성과 타 성분과의 상용성이 떨어지는 문제로 인해 핫멜트 접착 조성물로 활용이 어려운, 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene Adipate Terephtalate, PBAT)에 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC), 점착부여수지, 왁스 및 고무를 특정 중량부 비로 조합함으로써, KS M ISO 14855-1에 따른 생분해도가 80% 이상이면서 우수한 접착력과 접착 택타임 및 탄성을 나타내는 생분해성 핫멜트 접착 조성물을 제공하고자 한다.Therefore, the inventors of the present invention, to polybutylene adipate terephthalate (Polybutylene Adipate Terephthalate, PBAT), which is difficult to utilize as a hot melt adhesive composition due to problems of high stiffness due to entanglement between strong polymer chains and poor compatibility with other components By combining Acetyl Tributyl Citrate (ATBC), tackifying resin, wax and rubber in a specific weight part ratio, the biodegradability according to KS M ISO 14855-1 is 80% or more and excellent adhesive strength, adhesive tact time and It is intended to provide a biodegradable hot melt adhesive composition exhibiting elasticity.
본 발명이 해결하고자 하는 기술적 과제는 이상에서 언급한 기술적 과제로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다. The technical problem to be solved by the present invention is not limited to the above-mentioned technical problem, and other technical problems not mentioned will be clearly understood by those skilled in the art from the description below. You will be able to.
본 명세서에서, 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephtalate, PBAT); 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC); 송진(Rosin)계 및 테르펜(terpene)계 중 선택되는 1종 이상의 점착부여수지(tackifier resin); 왁스(wax); 및 고무(rubber)를 포함하는, 생분해성 핫멜트 접착 조성물을 제공한다.In the present specification, polybutylene adipate terephthalate (Polybutylene adipate terephtalate, PBAT); Acetyl Tributyl Citrate (ATBC); At least one tackifier resin selected from rosin-based and terpene-based; wax; And it provides a biodegradable hot melt adhesive composition comprising rubber (rubber).
일례로, 상기 접착 조성물은, 폴리부틸렌 아디페이트 테레프탈레이트 100 중량부를 기준으로, 아세틸 트리부틸 시트레이트 80 내지 120 중량부, 점착부여수지 1,300 내지 1,500 중량부, 왁스 80 내지 120 중량부 및 고무 280 내지 320 중량부를 포함하는 것일 수 있다. For example, the adhesive composition, based on 100 parts by weight of polybutylene adipate terephthalate, 80 to 120 parts by weight of acetyl tributyl citrate, 1,300 to 1,500 parts by weight of a tackifying resin, 80 to 120 parts by weight of wax and 280 rubber to 320 parts by weight.
일례로, 상기 왁스는 파라핀 왁스, 미세결정질 왁스(microcrystalline wax), 폴리에틸렌 왁스, 폴리프로필렌 왁스, 아마이드 왁스 및 피셔-트롭쉬 왁스(Fischer-Tropsch wax) 중 선택되는 1종 이상일 수 있다. For example, the wax may be at least one selected from paraffin wax, microcrystalline wax, polyethylene wax, polypropylene wax, amide wax, and Fischer-Tropsch wax.
일례로, 상기 접촉 조성물의 접착 택타임(Tact Time)은 1초 내지 180초일 수 있다. For example, the adhesion tact time of the contact composition may be 1 second to 180 seconds.
일례로, 상기 접착 조성물의 박리 강도는 350 내지 4,500 g/25㎜일 수 있다. For example, the peel strength of the adhesive composition may be 350 to 4,500 g/25 mm.
일례로, 상기 접착 조성물의 점도는 500 내지 20,000 cps일 수 있다. For example, the adhesive composition may have a viscosity of 500 to 20,000 cps.
본 명세서에서는, 제1 기재, 제2 기재 및 상기 제1 기재와 제2 기재의 계면에 형성되는 상기 생분해성 핫멜트 접착 조성물을 포함하는, 일회용 제품을 제공한다.In the present specification, a disposable product including a first substrate, a second substrate, and the biodegradable hot-melt adhesive composition formed on the interface between the first substrate and the second substrate is provided.
일례로, 상기 일회용 제품은 펄프 박스, 페트(PET)병용 라벨지, 접착 테이프, 기저귀, 여성용 위생 제품 및 의료용 밴드 중 선택되는 1종 이상의 제품일 수 있다. For example, the disposable product may be at least one product selected from a pulp box, a label for a PET bottle, an adhesive tape, a diaper, a feminine hygiene product, and a medical band.
본 명세서에서, a) 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephtalate, PBAT); 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC); 송진(Rosin)계 및 테르펜(terpene)계 중 선택되는 1종 이상의 점착부여수지(tackifier resin); 왁스(wax); 및 고무(rubber)를 혼합하여 생분해성 핫멜트 접착 조성물을 제조하는 단계; b) 상기 생분해성 핫멜트 접착 조성물을 제1 기재 상에 도포하는 단계; 및 c) 상기 생분해성 핫멜트 접착 조성물이 도포된 제1 기재 상에 제2 기재를 적층하고 열압착하여 접착시키는 단계; 를 포함하는, 일회용 제품의 제조방법을 제공한다. In the present specification, a) polybutylene adipate terephthalate (Polybutylene adipate terephtalate, PBAT); Acetyl Tributyl Citrate (ATBC); At least one tackifier resin selected from rosin-based and terpene-based; wax; And preparing a biodegradable hot melt adhesive composition by mixing rubber (rubber); b) applying the biodegradable hot melt adhesive composition on a first substrate; and c) laminating a second substrate on the first substrate coated with the biodegradable hot melt adhesive composition and bonding the second substrate by thermal compression bonding; It provides a method for manufacturing a disposable product comprising a.
일례로, 상기 생분해성 핫멜트 접착 조성물을 제1 기재 상에 도포하는 상기 b 단계는 80 내지 160℃ 온도 범위 내에서 수행되는 것일 수 있다. For example, step b of applying the biodegradable hot melt adhesive composition onto the first substrate may be performed within a temperature range of 80 to 160°C.
본 발명에 따르면, 생분해도는 높으나, 강한 고분자 사슬간의 얽힘에 의한 높은 강성과 타 성분과의 상용성이 떨어지는 문제로 인해 핫멜트 접착 조성물로 활용이 어려운, 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene Adipate Terephtalate, PBAT)에 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC), 점착부여수지, 왁스 및 고무를 특정 중량부 비로 조합함으로써, 생분해도, 접착력, 접착 택타임 및 탄성도가 우수한 생분해성 핫멜트 접착 조성물을 제공할 수 있다. According to the present invention, although biodegradability is high, polybutylene adipate terephthalate (Polybutylene Adipate Terephtalate), which is difficult to utilize as a hot melt adhesive composition due to high stiffness due to entanglement between strong polymer chains and poor compatibility with other components , PBAT) by combining Acetyl Tributyl Citrate (ATBC), tackifying resin, wax and rubber in a specific weight part ratio, a biodegradable hot melt adhesive composition with excellent biodegradability, adhesive strength, adhesive tact time and elasticity can provide.
본 발명에 따른 생분해성 핫멜트 접착 조성물은, KS M ISO 14855-1에 따른 생분해도가 80% 이상이면서 우수한 접착력과 접착 택타임 및 탄성을 나타낸다. 따라서, 환경오염 문제를 최소화하면서도 펄프 박스, 페트(PET)병용 라벨지, 접착 테이프, 기저귀, 여성용 위생 제품 및 의료용 밴드 등 다양한 1회용 제품 분야에서 널리 활용될 수 있다. The biodegradable hot melt adhesive composition according to the present invention has a biodegradability of 80% or more according to KS M ISO 14855-1 and exhibits excellent adhesive strength, adhesive tact time and elasticity. Therefore, it can be widely used in various disposable product fields such as pulp boxes, label paper for PET bottles, adhesive tapes, diapers, feminine hygiene products and medical bands while minimizing environmental pollution problems.
도 1은 본 발명의 일실시예에 따른 생분해성 핫멜트 접착 조성물 및 이를 이용하여 일회용 제품을 제조하는 방법을 개략적으로 도시한 것이다.
도 2는 본 발명의 일실시예에 따라 실제 제조된 생분해성 핫멜트 접착 조성물의 실제 사진을 나타낸 것이다. 1 schematically illustrates a biodegradable hot-melt adhesive composition according to an embodiment of the present invention and a method for manufacturing a disposable product using the same.
2 shows an actual photograph of a biodegradable hot-melt adhesive composition actually prepared according to an embodiment of the present invention.
이하, 본 발명에 대하여 보다 상세히 설명한다. 본 발명의 내용, 목적 및 효과는 하기의 설명에 의해서 자연스럽게 이해되거나 보다 분명해질 수 있으며, 하기의 기재만으로 본 발명의 내용, 목적 및 효과가 제한되는 것은 아니다.Hereinafter, the present invention will be described in more detail. The contents, objects and effects of the present invention can be naturally understood or more clearly understood by the following description, and the contents, objects and effects of the present invention are not limited only by the following description.
상술한 바와 같이, 일반적으로 종래 기술에 따른 핫멜트 접착제 조성물은 생분해성이 없는 에틸렌 비닐 아세테이트(Ethylene Vinyl Acetate, EVA)를 베이스 폴리머로 하여 제조됨으로써, 환경오염 문제에 취약한 문제가 있었다.As described above, hot-melt adhesive compositions according to the prior art are generally prepared using ethylene vinyl acetate (EVA), which is not biodegradable, as a base polymer, and thus have a problem of being vulnerable to environmental pollution.
이에, 본 발명자들은 생분해도가 낮은 EVA를 대체하기 위하여, 생분해도가 높은 폴리부틸렌 아디페이트 테레프탈레이트(PBAT)를 핫멜트 접착 조성물에 포함시키되, 강한 고분자 사슬간의 얽힘에 의한 높은 강성과 타 성분과의 상용성이 떨어지는 문제를 해결하기 위하여, 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC), 점착부여수지, 왁스 및 고무를 특정 중량부 비로 조합하는 경우, 생분해도가 높고, 피착체에 대한 우수한 접착력과 빠른 접착 택타임 및 탄성도를 가지는 생분해성 핫멜트 접착 조성물을 제조할 수 있다는 점을 실험을 통하여 확인하고, 본 발명을 완성하게 되었다. Therefore, in order to replace EVA with low biodegradability, the present inventors included polybutylene adipate terephthalate (PBAT), which has high biodegradability, in the hot melt adhesive composition, but has high stiffness and other components due to entanglement between strong polymer chains. In order to solve the problem of poor compatibility of acetyl tributyl citrate (ATBC), tackifying resin, wax and rubber in a specific weight part ratio, biodegradability is high and excellent for adherends. It was confirmed through experiments that a biodegradable hot-melt adhesive composition having adhesive strength, fast adhesive tact time, and elasticity could be prepared, and the present invention was completed.
이하, 본 발명의 구체적인 실시예에 따른 생분해성 핫멜트 접착 조성물에 대하여 보다 상세하게 설명하기로 한다. Hereinafter, a biodegradable hot melt adhesive composition according to a specific embodiment of the present invention will be described in more detail.
생분해성 핫멜트 접착 조성물Biodegradable Hot Melt Adhesive Composition
본 발명의 일실시예에 따른 생분해성 핫멜트 접착 조성물은, 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephtalate, PBAT); 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC); 송진(Rosin)계 및 테르펜(terpene)계 중 선택되는 1종 이상의 점착부여수지(tackifier resin); 왁스(wax); 및 고무(rubber)를 포함할 수 있다. A biodegradable hot melt adhesive composition according to an embodiment of the present invention includes polybutylene adipate terephthalate (PBAT); Acetyl Tributyl Citrate (ATBC); At least one tackifier resin selected from rosin-based and terpene-based; wax; and rubber.
폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephtalate, PBAT)는 화석연료 기반의 생분해성 폴리머 수지로서, 1,4-부탄디올(1,4-Butanediol), 아디프산(Adipic acid), 테레프탈산(Terephalic acid)의 공중합체이며, 생분해성이 우수하다. 구체적으로, 폴리부틸렌 아디페이트 테레프탈레이트는 우수한 인장 및 인열 강도, 일정기간 동안 내구성을 유지하는 특성 및 우수한 가공성을 가지며, 현재 폴리유산(PLA) 개질제, 쇼핑백, 쓰레기 종량제 봉투, 롤백, 종이컵 코팅, 명함, 멀칭 필름, 일회용 제품(위생장갑, 식탁보) 등 다양한 제품에 적용되고 있다. 폴리부틸렌 아디페이트 테레프탈레이트는 본 발명의 핫멜트 접착 조성물의 일 구성으로 포함되어, 종래 EVA를 대체하여 접착 조성물의 물성을 개선하는 한편, 생분해도를 향상시킨다. Polybutylene adipate terephthalate (PBAT) is a fossil fuel-based biodegradable polymer resin that contains 1,4-butanediol, adipic acid, and terephthalic acid. ), and has excellent biodegradability. Specifically, polybutylene adipate terephthalate has excellent tensile and tear strength, durability for a certain period of time, and excellent processability, and is currently used as a polylactic acid (PLA) modifier, shopping bags, garbage bags, rolls, paper cup coatings, It is applied to various products such as business cards, mulching films, and disposable products (sanitary gloves, tablecloths). Polybutylene adipate terephthalate is included as one component of the hot melt adhesive composition of the present invention, replacing conventional EVA to improve physical properties of the adhesive composition and improve biodegradability.
아세틸 트리부틸 시트레이트(Acetyl tributyl citrate, ATBC)는 무색 무향의 액체로, 물과 유기용매에 녹으며, 비닐 수지용 가소제, 유지 식품에 닿는 수지성 고분자 코팅, 종이/판지로 된 식품 접착 표면의 제조, 프탈레이트 대체 가소제, 식품 랩, 비닐 장난감, 의약품 부형제, 질산 셀룰로오스, 셀룰로오스 아세테이트, 폴리비닐 아세테이트의 가소제, 화장품 등 다양한 제품에 적용된다. 한편, 아세틸 트리부틸 시트레이트는 본 발명의 핫멜트 접착 조성물에 포함되는 폴리부틸렌 아디페이트 테레프탈레이트가 가진 강한 고분자 사슬간의 얽힘을 완화시키는 일종의 가소제로서 사용되는 것일 수 있다. 구체적으로, 아세틸 트리부틸 시트레이트가 상기 핫멜트 접착 조성물에 포함되는 경우, 고분자 사슬 간 거리를 넓혀 마이크로브라운(microbrownian motion) 운동을 일으키기 쉽게 하는 한편, 유리전이 온도를 낮추어 고분자에 유연성을 부여함으로써, 접착 조성물의 초기 도포 시 기재에 대한 초기 접착성을 증가시키는 역할도 수행할 수 있다. Acetyl tributyl citrate (ATBC) is a colorless, odorless liquid, soluble in water and organic solvents, used as a plasticizer for vinyl resins, as a resinous polymer coating for fats and oils, and for food adhesion surfaces made of paper/board. It is applied to various products such as manufacturing, phthalate substitute plasticizer, food wrap, vinyl toy, pharmaceutical excipient, cellulose nitrate, cellulose acetate, plasticizer of polyvinyl acetate, and cosmetics. Meanwhile, acetyl tributyl citrate may be used as a kind of plasticizer that relieves entanglement between strong polymer chains of polybutylene adipate terephthalate included in the hot melt adhesive composition of the present invention. Specifically, when acetyl tributyl citrate is included in the hot melt adhesive composition, the distance between polymer chains is widened to facilitate microbrownian motion, while the glass transition temperature is lowered to impart flexibility to the polymer, thereby providing adhesion It may also serve to increase the initial adhesion to the substrate when the composition is initially applied.
구체적으로, 본 발명에서 아세틸 트리부틸 시트레이트는 폴리부틸렌 아디페이트 테레프탈레이트 100 중량부를 기준으로, 80 내지 120 중량부, 상세하게는 90 내지 110 중량부, 더욱 상세하게는 100 중량부로 포함되는 것일 수 있다. 아세틸 트리부틸 시트레이트가 상기 중량부 범위로 포함되는 경우, 폴리부틸렌 아디페이트 테레프탈레이트 고분자 사슬 간 거리를 효과적으로 넓혀 강한 고분자 사슬간의 얽힘을 완화시켜줌으로써, 핫멜트 접착 조성물로 사용하기 적합한 수준의 강성(stiffness)을 갖도록 하는 한편, 초기 접착 강도 확보 측면에서 기여할 수 있다. Specifically, in the present invention, acetyl tributyl citrate is included in 80 to 120 parts by weight, specifically 90 to 110 parts by weight, and more specifically 100 parts by weight based on 100 parts by weight of polybutylene adipate terephthalate. can When acetyl tributyl citrate is included in the above parts by weight range, the distance between polybutylene adipate terephthalate polymer chains is effectively widened to relieve entanglement between strong polymer chains, thereby providing a level of stiffness suitable for use as a hot melt adhesive composition ( stiffness), while contributing to securing the initial adhesive strength.
한편, 본 발명의 점착부여수지(tackifier resin)는 접착 조성물의 접착 특성 발현 및 물성 조절을 위해 포함되는 것일 수 있으며, 일례로 로진(Rosin)계 및 테르펜(Terpene)계 수지 중 선택되는 1종 이상 일 수 있다.On the other hand, the tackifier resin of the present invention may be included for the expression of adhesive properties and control of physical properties of the adhesive composition, for example, at least one selected from rosin-based and terpene-based resins can be
로진(Rosin)은 소나무과의 나무가 손상을 입었을 때 분비되는 끈적끈적한 액체인 송진을 정제한 것으로서, 천연 로진은 통상적으로 7 또는 8 로진산 및 다른 부수적인 성분의 혼합물로 이루어지는 것일 수 있다. 로진은 아비에트산를 주성분으로 하며, 네오아비에트산·레포피마르산·히드로아비에트산·피마르산·덱스톤산 등 수지산(樹脂酸)을 함유할 수 있다. 로진은 상업적으로 입수 가능하고 올레오 수지의 분별 증류에 의해(검 로진), 소나무 그루터기의 추출에 의해(우드 로진) 또는 톨유의 분별 증류에 의해(톨유 로진) 얻을 수 있다. 일례로, 본 발명에 의한 생분해성 핫멜트 접착 조성물에 포함되는 로진은 상술한 검 로진, 우드 로진 및 톨유 로진 중 선택되는 1종 이상일 수 있다. 한편, 본 발명에서 로진계 수지는 젖음성(wettability)을 향상시켜, 부착도 및 흡착도를 증가시키므로, 접착 조성물의 접착력 및 접착 택타임을 보다 향상시킨다. Rosin is a purified rosin, which is a sticky liquid secreted when a tree of the Pinaceae family is damaged. Rosin has abietic acid as its main component, and may contain resin acids such as neoabietic acid, lepopimaric acid, hydroabietic acid, pimaric acid, and dextonic acid. Rosin is commercially available and can be obtained by fractional distillation of oleoresin (gum rosin), extraction of pine stumps (wood rosin) or fractional distillation of tall oil (tall oil rosin). For example, the rosin included in the biodegradable hot melt adhesive composition according to the present invention may be at least one selected from the above-described gum rosin, wood rosin, and tall oil rosin. On the other hand, in the present invention, since the rosin-based resin improves wettability and increases adhesion and adsorption, the adhesive strength and adhesion tact time of the adhesive composition are further improved.
테르펜(Terpene)은 동식물에 널리 분포되어 있는 가연성의 불포화 탄화수소로서, 일반식 (C5H8)n (n≥2)을 갖는 탄수화물 및 이들 유도체를 총칭한다. 한편, 구조 상으로는 이소프렌 분자가 기본 단위인 이소프렌 법칙을 따르고, 식물계에 널리 분포한다. 테르펜은 분자 내 이소프렌(C5H8) 단위체 수에 따라 분류하며, 모노테르펜(C10H16)은 2개, 세스퀴테르펜(C15H24)은 3개, 디테르펜(C20H32)은 4개, 트리테르펜(C30H48)은 6개, 테트라테르펜(C40H64)은 8개의 이소프렌 단위체를 각각 가진다. 테르펜은 향료의 원료나 의약품, 화학공업의 원료로 사용된다. 한편, 본 발명에서 테르펜계 수지는 접착 조성물의 용융 온도와 용융 점도를 감소시키는 한편, 접착 조성물 자체의 강도를 증가시키는 역할을 수행한다. Terpene (Terpene) is a combustible unsaturated hydrocarbon widely distributed in animals and plants, general formula (C 5 H 8 ) It is a general term for carbohydrates having n (n≥2) and their derivatives. On the other hand, in terms of structure, the isoprene molecule follows the isoprene law, which is the basic unit, and is widely distributed in the plant kingdom. Terpenes are classified according to the number of isoprene (C 5 H 8 ) units in the molecule. Monoterpenes (C 10 H 16 ) have two units, sesquiterpenes (C 15 H 24 ) three units, and diterpenes (C 20 H 32 units). ) has 4, triterpene (C 30 H 48 ) has 6, and tetraterpene (C 40 H 64 ) has 8 isoprene units, respectively. Terpenes are used as raw materials for spices, pharmaceuticals, and chemical industries. On the other hand, in the present invention, the terpene-based resin serves to reduce the melting temperature and melt viscosity of the adhesive composition, while increasing the strength of the adhesive composition itself.
구체적으로, 본 발명의 생분해성 핫멜트 접착 조성물에, 로진(Rosin)계 및 테르펜(Terpene)계 수지 중 선택되는 1종 이상의 점착부여수지(tackifier resin)를 포함함으로써, 젖음성 및 접착 강도를 향상시킬 수 있다. 또한, 상기 로진계 수지 또는 테르펜계 수지는 폴리부틸렌 아디페이트 테레프탈레이트와의 상용성이 뛰어나 균일 혼합이 가능하며, 이로 인해 본 발명에 따른 생분해성 핫멜트 접착 조성물이 기재에 도포될 때, 기재에 대한 밀착성 및 접착력이 향상될 수 있다. Specifically, by including one or more tackifier resins selected from rosin-based and terpene-based resins in the biodegradable hot-melt adhesive composition of the present invention, wettability and adhesive strength can be improved. there is. In addition, the rosin-based resin or terpene-based resin has excellent compatibility with polybutylene adipate terephthalate and can be uniformly mixed, so that when the biodegradable hot melt adhesive composition according to the present invention is applied to a substrate, Adhesion and adhesion may be improved.
본 발명에서 로진(Rosin)계 및 테르펜(Terpene)계 수지 중 선택되는 1종 이상의 점착부여수지(tackifier resin)는 폴리부틸렌 아디페이트 테레프탈레이트 100 중량부를 기준으로, 1,300 내지 1,500 중량부, 상세하게는 1,350 내지 1,450 중량부, 더욱 상세하게는 1,400 중량부 포함되는 것일 수 있으며, 점착부여수지가 상기 중량부 비로 포함되는 경우, 접착 조성물을 기재와의 접촉시켰을 때, 충분한 밀착력을 확보하는 동시에, 우수한 접착력 및 접착 택타임을 확보할 수 있게 된다. In the present invention, at least one tackifier resin selected from rosin-based and terpene-based resins is 1,300 to 1,500 parts by weight, based on 100 parts by weight of polybutylene adipate terephthalate, in detail may be included in 1,350 to 1,450 parts by weight, more specifically 1,400 parts by weight, and when the tackifying resin is included in the above weight part ratio, when the adhesive composition is brought into contact with the substrate, sufficient adhesion is secured, and excellent It is possible to secure adhesive strength and adhesive tact time.
한편, 본 발명의 왁스는 일종의 점도 조절제 역할을 수행할 수 있으며, 본 발명의 일실시예에 따른 왁스는, 파라핀 왁스, 미세결정질 왁스(microcrystalline wax), 폴리에틸렌 왁스, 폴리프로필렌 왁스, 아마이드 왁스 및 피셔-트롭쉬 왁스(Fischer-Tropsch wax) 중 선택되는 1종 이상일 수 있다. 구체적으로, 상기 왁스는 접착 조성물에 포함되는 기타 고분자 수지들의 용융 온도를 낮추는 동시에, 유동성과 습윤성을 향상시키고, 접착 조성물의 응고 속도를 조절하는 역할을 수행할 수 있다. On the other hand, the wax of the present invention may serve as a kind of viscosity modifier, and the wax according to an embodiment of the present invention includes paraffin wax, microcrystalline wax, polyethylene wax, polypropylene wax, amide wax, and Fischer wax. - It may be one or more selected from among Fischer-Tropsch waxes. Specifically, the wax may play a role of lowering the melting temperature of other polymer resins included in the adhesive composition, improving fluidity and wettability, and controlling the solidification rate of the adhesive composition.
본 발명에서 왁스는 폴리부틸렌 아디페이트 테레프탈레이트 100 중량부를 기준으로, 80 내지 120 중량부, 상세하게는 90 내지 110 중량부, 더욱 상세하게는 100 중량부 포함되는 것일 수 있다. 한편, 왁스가 상기 중량부 비로 포함되는 경우 접착 조성물을 기재와의 접촉시켰을 때, 유동성과 습윤성을 조절하여, 응고 속도를 기재 내지 접착 목적에 따라 조절할 수 있게 된다. In the present invention, the wax may be included in 80 to 120 parts by weight, specifically 90 to 110 parts by weight, and more specifically 100 parts by weight, based on 100 parts by weight of polybutylene adipate terephthalate. On the other hand, when the wax is included in the weight part ratio, when the adhesive composition is brought into contact with the substrate, fluidity and wettability are adjusted, so that the solidification rate can be adjusted according to the substrate or the purpose of adhesion.
한편, 고무(rubber)는 상온에서 고무상(狀) 탄성을 나타내는 사슬 모양의 고분자 물질이나 그 원료가 되는 고분자 물질을 가리키는 것으로, 크게 천연고무와 합성고무로 분류된다. 본 발명에 따른 접착제 조성물에 첨가되는 고무는 천연고무, 부타디엔고무 또는 스티렌 부타디엔 고무 등의 일반 고무를 단독으로 사용할 수도 있고, 또는 접착성 수지의 분산성을 향상시키기 위해 니트릴부타디엔고무, 아크릴 고무 또는 클로로술폰화 폴리에틸렌 고무 등의 극성고무를 병용하여 사용할 수도 있다. 일례로, 본 발명에서 사용되는 고무는 생분해도 향상을 위한 천연고무일 수 있다. 본 발명의 접착제 조성물에 있어서, 고무는 점착성을 개선하는 한편, 탄성도를 향상시켜 종이, 부직 웹, 직물 웹, 필름 및 탄성 스트랜드를 비롯한 각종 기재에 도포하여 접착 필름 또는 접착 테이프로 가공하기 용이하도록 물성을 개선한다. On the other hand, rubber (rubber) refers to a chain-shaped polymer material exhibiting rubber-like elasticity at room temperature or a polymer material that is a raw material thereof, and is largely classified into natural rubber and synthetic rubber. As the rubber added to the adhesive composition according to the present invention, general rubber such as natural rubber, butadiene rubber or styrene butadiene rubber may be used alone, or nitrile butadiene rubber, acrylic rubber or chloro A polar rubber such as sulfonated polyethylene rubber may be used in combination. For example, the rubber used in the present invention may be natural rubber for improving biodegradability. In the adhesive composition of the present invention, the rubber improves adhesion and improves elasticity so that it can be applied to various substrates including paper, nonwoven webs, woven webs, films and elastic strands to facilitate processing into adhesive films or adhesive tapes. improve physical properties
본 발명에서 고무는 폴리부틸렌 아디페이트 테레프탈레이트 100 중량부를 기준으로, 280 내지 320 중량부, 상세하게는 290 내지 310 중량부, 더욱 상세하게는 300 중량부 포함되는 것일 수 있다. 한편, 고무가 상기 중량부 비로 포함되는 경우 접착 필름 또는 접착 테이프로 가공하기가 보다 용이하다. In the present invention, the rubber may be included in 280 to 320 parts by weight, specifically 290 to 310 parts by weight, and more specifically 300 parts by weight, based on 100 parts by weight of polybutylene adipate terephthalate. On the other hand, when rubber is included in the weight part ratio, processing into an adhesive film or adhesive tape is easier.
한편, 본 발명에 따른 생분해성 핫멜트 접착 조성물은 산화방지제, 충전재(filler) 등 기타 물성 향상을 위한 추가적인 성분을 더 포함할 수 있다. Meanwhile, the biodegradable hot melt adhesive composition according to the present invention may further include additional components for improving other physical properties, such as antioxidants and fillers.
일례로, 접착 조성물이 페놀계 산화방지제, 방향족 아민계 산화방지제, 인계 산화방지제 및 유황계 산화방지제로부터 선택된 적어도 1종 이상의 산화방지제를 더 포함하는 경우, 고온 내지 빛에 의한 고분자 사슬 절단 또는 가교 반응을 방지하여, 접착 조성물의 열안정성을 개선할 수 있다. For example, when the adhesive composition further includes at least one or more antioxidants selected from phenol-based antioxidants, aromatic amine-based antioxidants, phosphorus-based antioxidants, and sulfur-based antioxidants, polymer chain cleavage or crosslinking reaction by high temperature or light By preventing this, it is possible to improve the thermal stability of the adhesive composition.
또 다른 일례로, 접착 조성물이 무기 충전재 내지 유기 충전재를 더 포함하는 경우, 일례로 실리카, 용융 실리카, 클레이, 석고, 탄산칼슘, 황산바륨, 산화알루미나, 산화베릴륨, 탄화규소, 질화규소 등 세라믹류, 알루미늄, 구리, 은, 금, 니켈, 크로뮴, 납, 주석, 아연, 팔라듐, 땜납 등 금속 내지 합금류, 카본 등으로 이루어지는 무기 분말을 1종 이상 사용하는 경우, 접착 조성물의 점도를 증가시켜, 초기 점착에 보다 유리할 수 있다. As another example, when the adhesive composition further includes an inorganic filler or an organic filler, for example, silica, fused silica, clay, gypsum, calcium carbonate, barium sulfate, alumina oxide, beryllium oxide, silicon carbide, ceramics such as silicon nitride, In the case of using one or more types of inorganic powder composed of metals or alloys such as aluminum, copper, silver, gold, nickel, chromium, lead, tin, zinc, palladium, solder, carbon, etc., the viscosity of the adhesive composition is increased, It may be more advantageous for adhesion.
이상으로 설명한, 본 발명에 따른 생분해성 핫멜트 접착 조성물은, KS M ISO 14855-1에 따른 생분해도가 80%, 상세하게는 90% 이상일 수 있고, 상기와 같은 높은 생분해 특성으로 인해 접착 조성물이 일정 기간 이후 미생물 등에 의해 자연 분해되므로, 매립, 소각 등 별도의 처리가 요구되지 않아 친환경적이다. As described above, the biodegradable hot melt adhesive composition according to the present invention may have a biodegradability of 80%, specifically 90% or more according to KS M ISO 14855-1, and due to the high biodegradability as described above, the adhesive composition is uniform. Since it is naturally decomposed by microorganisms after a period of time, it is eco-friendly because no separate treatment such as landfill or incineration is required.
한편, 상기 접착 조성물은 접착 택타임(Tact Time)이 1초 내지 180초, 상세하게는 1초 내지 60초일 수 있고, 인장강도 시험기를 이용한 박리 실험 시 박리 강도가 350 내지 4,000 g/25㎜ 범위를 가질 수 있다. 또한, 상기 본 발명에 따른 생분해성 핫멜트 접착 조성물의 점도는 500 내지 8,000 cps 범위를 나타내는 것일 수 있다. 한편, 접착 조성물이 상기와 같은 특성을 갖는 경우 핫멜트 접착 조성물로 활용하기 적합하다. On the other hand, the adhesive composition may have an adhesive tact time of 1 second to 180 seconds, specifically 1 second to 60 seconds, and a peel strength in a peel test using a tensile strength tester in the range of 350 to 4,000 g/25 mm. can have In addition, the viscosity of the biodegradable hot melt adhesive composition according to the present invention may be in the range of 500 to 8,000 cps. On the other hand, when the adhesive composition has the above properties, it is suitable for use as a hot melt adhesive composition.
한편, 본 발명에 따른 생분해성 핫멜트 접착 조성물은 위생재, 부직포, 포장재, 소비재, 섬유, 가죽, 신발, 가구, 목공재, 운송 제품, 전자 제품, 인쇄/제본 등 다양한 기술 분야에 제한없이 적용될 수 있다. 특히, 본 발명에 따른 접착 조성물은 뛰어난 탄성도를 가지고 있어, 접착 필름 또는 접착 테이프에 적용하기 적합하다. On the other hand, the biodegradable hot-melt adhesive composition according to the present invention can be applied without limitation to various technical fields such as sanitary materials, non-woven fabrics, packaging materials, consumer goods, textiles, leather, shoes, furniture, woodworking materials, transportation products, electronic products, and printing / bookbinding. there is. In particular, the adhesive composition according to the present invention has excellent elasticity and is suitable for application to adhesive films or adhesive tapes.
이상으로 설명한 본 발명에 따른 생분해성 핫멜트 접착 조성물의 하나의 사용예로서, 상기 생분해성 핫멜트 접착 조성물을 이용하여 제조한 일회용 제품에 대하여 아래에서 구체적으로 더 설명한다. As one use example of the biodegradable hot-melt adhesive composition according to the present invention described above, a disposable product manufactured using the biodegradable hot-melt adhesive composition will be described in detail below.
생분해성 핫멜트 접착 조성물을 이용한 일회용 제품Disposable products using biodegradable hot melt adhesive composition
본 발명에 따른 일회용 제품은 제1 기재, 제2 기재 및 상기 제1 기재와 제2 기재의 계면에 형성되는 상기 생분해성 핫멜트 접착 조성물을 포함하며, 상기 생분해성 핫멜트 접착 조성물은 상술한 바와 같다. The disposable product according to the present invention includes a first substrate, a second substrate, and the biodegradable hot-melt adhesive composition formed on the interface between the first substrate and the second substrate, and the biodegradable hot-melt adhesive composition is as described above.
제1 기재 및 제2 기재는 일회용 제품에서 사용되는 기재라면 특별히 제한되지 아니하나, 상기 기재는 일례로 신품 및 재생 크라프트(craft), 고밀도 및 저밀도 크라프트, 칩보드(chipoard), 폴리에틸렌, 마일러(mylar), 폴리프로필렌, 폴리비닐리덴 클로라이드, 에틸렌 비닐아세테이트, 폴리에틸렌 테레프탈레이트 등 재질일 수 있다. 한편, 본 명세서 내의 용어 "제1" 및 "제2" 등은 상호 구분을 위해 임의로 순번을 지정한 것으로 이해되어야 한다. The first substrate and the second substrate are not particularly limited as long as they are used in disposable products, but the substrates are, for example, new and recycled kraft, high-density and low-density kraft, chipboard, polyethylene, mylar ( mylar), polypropylene, polyvinylidene chloride, ethylene vinyl acetate, polyethylene terephthalate, and the like. Meanwhile, the terms "first" and "second" in this specification should be understood as randomly assigned order numbers for mutual distinction.
한편, 상기 일회용 제품은 산업용 작업복, 의료용 가운, 마스크, 배변 훈련용 팬츠, 수영복, 기저귀, 성인 요실금 제품, 여성용 위생 제품 및 의료용 밴드는 물론, 펄프 박스, 페트(PET)병용 라벨지, 접착 테이프 등일 수 있으며, 보다 상세하게는, 펄프 박스, 페트(PET)병용 라벨지, 접착 테이프, 기저귀, 여성용 위생 제품 및 의료용 밴드 중 선택되는 1종 이상의 제품일 수 있다. On the other hand, the disposable products may be industrial work clothes, medical gowns, masks, potty training pants, swimwear, diapers, adult incontinence products, feminine hygiene products and medical bands, as well as pulp boxes, PET bottle labels, adhesive tapes, and the like. And, more specifically, it may be one or more products selected from pulp boxes, label paper for PET bottles, adhesive tapes, diapers, feminine hygiene products, and medical bands.
생분해성 핫멜트 접착 조성물을 이용한 일회용 제품 제조방법Method for manufacturing disposable products using biodegradable hot melt adhesive composition
본 발명의 또 다른 일실시예에 따른, 일회용 제품의 제조방법은 a) 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephtalate, PBAT); 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC); 송진(Rosin)계 및 테르펜(terpene)계 중 선택되는 1종 이상의 점착부여수지(tackifier resin); 왁스(wax); 및 고무(rubber)를 혼합하여 생분해성 핫멜트 접착 조성물을 제조하는 단계; b) 상기 생분해성 핫멜트 접착 조성물을 제1 기재 상에 도포하는 단계; 및 c) 상기 생분해성 핫멜트 접착 조성물이 도포된 제1 기재 상에 제2 기재를 적층하고 열압착하여 접착시키는 단계; 를 포함할 수 있다. According to another embodiment of the present invention, a method for manufacturing a disposable product is a) polybutylene adipate terephthalate (Polybutylene adipate terephtalate, PBAT); Acetyl Tributyl Citrate (ATBC); At least one tackifier resin selected from rosin-based and terpene-based; wax; And preparing a biodegradable hot melt adhesive composition by mixing rubber (rubber); b) applying the biodegradable hot melt adhesive composition on a first substrate; and c) laminating a second substrate on the first substrate coated with the biodegradable hot melt adhesive composition and bonding the second substrate by thermal compression bonding; can include
상기 a 단계는 폴리부틸렌 아디페이트 테레프탈레이트(Polybutylene adipate terephtalate, PBAT); 아세틸 트리부틸 시트레이트(Acetyl Tributyl Citrate, ATBC); 송진(Rosin)계 및 테르펜(terpene)계 중 선택되는 1종 이상의 점착부여수지(tackifier resin); 왁스(wax) 및 고무(rubber)를 혼합하고, 니더 루더, 압출기, 믹싱 롤, 밴버리 믹서 등 공지의 혼합 장치를 이용하여 80 내지 160 ℃ 온도 범위 내에서 균일하게 혼합하여 수행될 수 있으나, 이에 제한되지 아니한다. Step a is polybutylene adipate terephthalate (Polybutylene adipate terephtalate, PBAT); Acetyl Tributyl Citrate (ATBC); At least one tackifier resin selected from rosin-based and terpene-based; It may be performed by mixing wax and rubber and uniformly mixing within a temperature range of 80 to 160 ° C. using a known mixing device such as a kneader rouder, extruder, mixing roll, Banbury mixer, etc., but limited thereto It doesn't.
다음으로, b 단계는 상기 제조된 핫멜트 접착 조성물을 연화점 이상으로 가열하여 용융된 상태로 제1 기재에 도포하는 것으로서, 80 내지 160 ℃ 온도 범위 내에서 수행될 수 있다. 한편, 상기 도포는 용융 상태로 핫멜트 접착 조성물을 분사하는 장치 내지 코팅하는 장치를 이용하여 수행될 수 있으며, 일례로, 글루건 등 분사하는 형태의 비접촉 방식으로 또는 슬롯 코터 등을 이용하여 기재 상에 직접 도포하는 접촉 방식으로 수행되는 것일 수 있으나, 이에 제한되지 아니한다. Next, step b is to heat the prepared hot-melt adhesive composition above its softening point and apply it to the first substrate in a molten state, which may be performed within a temperature range of 80 to 160 °C. Meanwhile, the coating may be performed using a device for spraying or coating the hot melt adhesive composition in a molten state, and for example, in a non-contact method in the form of spraying a hot melt adhesive composition such as a glue gun or the like, or directly on a substrate using a slot coater or the like. It may be performed in a contact method of applying, but is not limited thereto.
다음으로, c 단계는 상기 생분해성 핫멜트 접착 조성물이 도포된 제1 기재 상에 제2 기재를 적층하고 열압착하여 접착시켜 수행될 수 있으며, 구체적으로, 상기 b 단계의 도포 이후, 제2 기재를 도포된 접착 조성물 상에 적층하고 압착 롤러 등을 이용하여 압력을 가하거나, 냉각시킴으로써 접착 조성물을 경화시켜 수행될 수 있다. Next, step c may be performed by laminating a second substrate on the first substrate coated with the biodegradable hot melt adhesive composition and bonding the second substrate by thermal compression. Specifically, after the application of step b, the second substrate It may be performed by laminating on the applied adhesive composition and curing the adhesive composition by applying pressure using a pressure roller or the like or by cooling.
한편, 상술한 핫멜트 접착 조성물은 일례로 핫멜트 도공법, T 다이법, 인플레이션법, 캘린더 성형법, 및 라미네이션법 등을 이용하여 시트상이나, 필름상으로 제조한 후, 가열 용융하여 사용하는 것일 수 있으나, 이에 제한되지 아니한다. Meanwhile, the above-described hot melt adhesive composition may be prepared in the form of a sheet or film using, for example, a hot melt coating method, a T-die method, an inflation method, a calender molding method, and a lamination method, and then heat-melted and used. not limited thereto.
이하 발명의 구체적인 실시예를 통해 발명의 내용, 작용 및 효과를 보다 구체적으로 설명하기로 한다. 다만, 이는 발명의 예시로서 제시된 것으로 이에 의해 발명의 권리범위가 어떠한 의미로든 한정되는 것은 아니다. Hereinafter, the contents, actions and effects of the invention will be described in more detail through specific examples of the invention. However, this is presented as an example of the invention, and thereby the scope of the invention is not limited in any sense.
제조예manufacturing example
아래 표 1과 같은 조성(중량부 비)로 접착 조성물을 제조하였다. 구체적으로, 폴리부틸렌 아디페이트 테레프탈레이트(PBAT) 수지, 아세틸 트리부틸 시트레이트(ATBC) 수지, 점착부여수지로서 로진 수지 또는 테르펜 수지, 파라핀 왁스(Shell GTL Sarawax SX 105, EVONIK) 및 천연고무를 아래 조성비로 Brabender mixer에 첨가하여 160 ℃ 온도에서 2시간 혼합하여 접착 조성물을 제조하였다. An adhesive composition was prepared with the composition (part by weight ratio) shown in Table 1 below. Specifically, polybutylene adipate terephthalate (PBAT) resin, acetyl tributyl citrate (ATBC) resin, rosin resin or terpene resin as a tackifying resin, paraffin wax (Shell GTL Sarawax SX 105, EVONIK) and natural rubber The following composition ratio was added to a Brabender mixer and mixed at a temperature of 160 ° C. for 2 hours to prepare an adhesive composition.
[실험: 접착 조성물의 상세 물성 측정][Experiment: Measurement of detailed physical properties of adhesive composition]
1. 점도 측정1. Viscosity measurement
실시예 및 비교예에 따라 제조된 접착 조성물을 160 ℃ 온도에서 용융시켜 샘플을 채취한 후, BROOKFIELD DV TYPE 점도계를 사용하여 10rpm, 4spindle을 사용하여 점도를 측정하였다. 시료의 양은 200g으로 하여 측정에 사용하였다. After taking a sample by melting the adhesive composition prepared according to Examples and Comparative Examples at 160 ° C., the viscosity was measured using a BROOKFIELD DV TYPE viscometer at 10 rpm and 4 spindles. The amount of the sample was 200 g and used for the measurement.
2. 접착 택타임 측정2. Measurement of adhesion tact time
실시예 및 비교예에 따라 제조된 접착 조성물을 160 ℃ 온도에서 용융시켜 샘플을 채취한 후, glass 위에 약 5g 떨어뜨리고, 표면이 경화되는 시간을 측정하였다. 구체적으로 손끝으로 만져 손에 묻어나지 않는 시간을 표시하며, 분위기 조건은 온도 25 ℃, 습도 50% 조건에서 측정하였다. After taking a sample by melting the adhesive composition prepared according to Examples and Comparative Examples at a temperature of 160 ° C., about 5 g was dropped on glass, and the time for curing the surface was measured. Specifically, the time that does not stick to the hand by touching it with the fingertips is displayed, and the atmosphere conditions were measured under conditions of a temperature of 25 ° C and a humidity of 50%.
3. 수상 내 접착성3. Adhesion in aqueous phase
실시예 및 비교예에 따라 제조된 접착 조성물을 160 ℃ 온도에서 용융시켜 3 X 3 X 0.5 ㎝ 폴리에틸렌테레프탈레이트 재질의 제1 기재 및 제2 기재 사이에 도포 및 접착시켜 시편을 제조하고, 이를 물 500ml에 1시간 침지시킨 후, 꺼내여 기재의 박리정도를 육안 관찰하여 점수로 평가하였다. 총 100개의 시편을 시험하여, 박리되지 않은 제품의 개수를 나타내었다. The adhesive composition prepared according to Examples and Comparative Examples was melted at a temperature of 160 ° C. and applied and adhered between the first substrate and the second substrate made of 3 X 3 X 0.5 cm polyethylene terephthalate to prepare a specimen, which was mixed with 500 ml of water. After being immersed in for 1 hour, it was taken out and the degree of peeling of the substrate was visually observed and evaluated as a score. A total of 100 specimens were tested, and the number of non-peeled products was shown.
4. 박리 강도 측정4. Measurement of peel strength
실시예 및 비교예에 따라 제조된 접착 조성물을 160 ℃ 온도에서 용융시켜 크라프트 재질의 제1 기재 및 제2 기재 사이에 도포 및 접착시켜 시편을 제조하고, 인장 강도 시험기를 이용하여 25℃에서 박리 강도를 측정하였다. 인장 강도 시험기의 한 쪽 지그를 제조된 시편에 고정된 상태에서 지그를 300 ㎜/min의 속력으로 잡아당겨 가해지는 박리 강도를 10회 반복 측정하여 평균값을 구하였다. The adhesive composition prepared according to Examples and Comparative Examples was melted at a temperature of 160 ° C, coated and adhered between the first substrate and the second substrate made of kraft material to prepare a specimen, and peel strength at 25 ° C using a tensile strength tester. was measured. The peel strength applied by pulling the jig at a speed of 300 mm/min in a state where one jig of the tensile strength tester was fixed to the manufactured specimen was repeatedly measured 10 times to obtain an average value.
5. 도포 균일성 측정5. Measurement of application uniformity
실시예 및 비교예에 따라 제조된 접착 조성물을 160 ℃ 온도에서 용융시켜 크라프트 재질의 기재에 도포하여 시편을 제조하고, 핫멜트 접착 조성물이 기재에 균일하게 도포되는지 여부를 육안으로 관찰하여 도포 균일성을 평가하였다. 이 때, 총 100개의 크라프트 재질의 기재에 도포하여, 스프레이 공정 시 필라멘트 형성 없이 접착 조성물이 기재에 균일하게 도포된 크라프트 재질의 기재 개수를 나타내었다. The adhesive composition prepared according to Examples and Comparative Examples was melted at 160 ° C. and applied to a kraft substrate to prepare a specimen, and visually observed whether the hot melt adhesive composition was uniformly applied to the substrate to determine coating uniformity. evaluated. At this time, it was applied to a total of 100 kraft material substrates, and the number of kraft material substrates in which the adhesive composition was uniformly applied to the substrates without filament formation during the spray process was shown.
6. 생분해도 측정6. Biodegradability measurement
생분해도를 측정하기 위해 실시예 및 비교예들의 시편을 준비하고, KS M ISO 14855-1에 따라 60일 경과 후 생분해도를 측정하였다. In order to measure biodegradability, specimens of Examples and Comparative Examples were prepared, and biodegradability was measured after 60 days in accordance with KS M ISO 14855-1.
(cps)viscosity
(cps)
(s)adhesive tact time
(s)
(개)adhesiveness
(dog)
(g/25 ㎜)peel strength
(g/25 mm)
(개)uniformity of application
(dog)
(%)biodegradability
(%)
상기 표 2의 결과를 참조하면, 본 발명에 따른 실시예의 경우, 비교예들 대비 접착력, 접착 택타임 및 도포 균일성 등 여러가지 물성 측면에서 동등 내지 그 이상의 우수한 특성을 나타내는 것을 확인할 수 있었으며, 특히, 종래 사용하던 EVA를 대체함으로써, 생분해도 측면에서도 우수한 특성을 가지는 것을 확인할 수 있었다. 또한, 실시예의 경우, 접착 조성물 내에 고무를 포함함으로써, 우수한 탄성도를 가져, 접착 필름 또는 접착 테이프 제품에 활용하기 적합한 것을 확인할 수 있었다. Referring to the results of Table 2, in the case of the examples according to the present invention, it was confirmed that they exhibited equivalent or superior properties in terms of various physical properties, such as adhesive strength, adhesion tact time and coating uniformity, compared to comparative examples. In particular, By replacing the conventionally used EVA, it was confirmed that it had excellent characteristics in terms of biodegradability. In addition, in the case of the examples, it was confirmed that by including rubber in the adhesive composition, it has excellent elasticity and is suitable for use in adhesive film or adhesive tape products.
Claims (10)
상기 접착 조성물은,
폴리부틸렌 아디페이트 테레프탈레이트 100 중량부를 기준으로, 아세틸 트리부틸 시트레이트 80 내지 120 중량부, 점착부여수지 1,300 내지 1,500 중량부, 왁스 80 내지 120 중량부 및 고무 280 내지 320 중량부를 포함하는, 생분해성 핫멜트 접착 조성물. According to claim 1,
The adhesive composition,
Based on 100 parts by weight of polybutylene adipate terephthalate, 80 to 120 parts by weight of acetyl tributyl citrate, 1,300 to 1,500 parts by weight of tackifying resin, 80 to 120 parts by weight of wax and 280 to 320 parts by weight of rubber, biodegradable Sexual hot melt adhesive composition.
상기 왁스는 파라핀 왁스, 미세결정질 왁스(microcrystalline wax), 폴리에틸렌 왁스, 폴리프로필렌 왁스, 아마이드 왁스 및 피셔-트롭쉬 왁스(Fischer-Tropsch wax) 중 선택되는 1종 이상인, 생분해성 핫멜트 접착 조성물. According to claim 1,
The wax is at least one selected from paraffin wax, microcrystalline wax, polyethylene wax, polypropylene wax, amide wax and Fischer-Tropsch wax, biodegradable hot melt adhesive composition.
상기 접착 조성물의 접착 택타임(Tact Time)은 1초 내지 180초인, 생분해성 핫멜트 접착 조성물. According to claim 1,
The adhesive tact time of the adhesive composition is 1 second to 180 seconds, biodegradable hot melt adhesive composition.
상기 접착 조성물의 박리 강도는 350 내지 4,500 g/25㎜인, 생분해성 핫멜트 접착 조성물. According to claim 1,
The peel strength of the adhesive composition is 350 to 4,500 g / 25 mm, biodegradable hot melt adhesive composition.
상기 접착 조성물의 점도는 500 내지 20,000 cps인, 생분해성 핫멜트 접착 조성물. According to claim 1,
The viscosity of the adhesive composition is 500 to 20,000 cps, biodegradable hot melt adhesive composition.
상기 일회용 제품은 펄프 박스, 페트(PET)병용 라벨지, 접착 테이프, 기저귀, 여성용 위생 제품 및 의료용 밴드 중 선택되는 1종 이상의 제품인, 일회용 제품.According to claim 7,
The disposable product is one or more products selected from pulp boxes, label paper for PET bottles, adhesive tapes, diapers, feminine hygiene products, and medical bands.
b) 상기 생분해성 핫멜트 접착 조성물을 제1 기재 상에 도포하는 단계; 및
c) 상기 생분해성 핫멜트 접착 조성물이 도포된 제1 기재 상에 제2 기재를 적층하고 열압착하여 접착시키는 단계; 를 포함하는, 일회용 제품의 제조방법.a) polybutylene adipate terephthalate (PBAT); Acetyl Tributyl Citrate (ATBC); At least one tackifier resin selected from rosin-based and terpene-based; wax; And preparing a biodegradable hot melt adhesive composition by mixing rubber (rubber);
b) applying the biodegradable hot melt adhesive composition on a first substrate; and
c) laminating a second substrate on the first substrate coated with the biodegradable hot melt adhesive composition and bonding the second substrate by thermal compression; A method of manufacturing a disposable product comprising a.
상기 생분해성 핫멜트 접착 조성물을 제1 기재 상에 도포하는 상기 b 단계는 80 내지 160℃ 온도 범위 내에서 수행되는, 일회용 제품의 제조방법. According to claim 9,
Wherein step b of applying the biodegradable hot melt adhesive composition on the first substrate is performed within a temperature range of 80 to 160 ° C.