KR20220163541A - Self-adhesive silicone tape that changes color with temperature and its manufacturing method - Google Patents
Self-adhesive silicone tape that changes color with temperature and its manufacturing method Download PDFInfo
- Publication number
- KR20220163541A KR20220163541A KR1020210071272A KR20210071272A KR20220163541A KR 20220163541 A KR20220163541 A KR 20220163541A KR 1020210071272 A KR1020210071272 A KR 1020210071272A KR 20210071272 A KR20210071272 A KR 20210071272A KR 20220163541 A KR20220163541 A KR 20220163541A
- Authority
- KR
- South Korea
- Prior art keywords
- silicone
- pigment
- self
- fusing
- tape
- Prior art date
Abstract
Description
본 발명은 온도에 따라 변색되는 자기 융착 실리콘 테이프 및 이의 제조방법이다.The present invention is a self-fusing silicone tape that is discolored with temperature and a manufacturing method thereof.
시온 안료는 열에 따라 색상이 변하는 안료를 통칭하는 말로, 기준 온도 이하에서는 일정한 색상을 보이지만 온도가 상승하면 투명한 색으로 변색되는 안료를 지칭한다. 이러한 시온 안료는 온도의 하강에 의하여 원래 색상으로 돌아오는지 여부에 따라 가역성 시온 안료와 비가역성 시온 안료로 구분된다. 이러한 시온 안료는 고온으로 상승할수록 투명해짐에 따라 바탕색이 전면에 노출되어 색상이 변화하게 되며, 2~3종을 혼합하여 사용되는 경우 각 온도구간별로 상이한 색상을 나타내는 것도 가능하다.Zion pigment is a general term for pigments whose color changes with heat, and refers to pigments that show a constant color below a standard temperature but change to a transparent color when the temperature rises. These Zion pigments are classified into reversible Zion pigments and irreversible Zion pigments depending on whether or not the original color is returned by a decrease in temperature. As these Zion pigments become more transparent as the temperature rises, the background color is exposed to the front and the color changes. When two or three types are mixed and used, it is possible to show different colors for each temperature range.
한편, 일반적으로 전선을 연결하기 위해서 양측 전선의 피복층을 일부 제거한 후 결속하고, 외부로 노출된 전선의 결선부에 절연테이프를 감아서 전선 연결부분의 부식이나 누전, 합선 등으로 인한 화재, 감전 등의 안전사고를 미연에 방지하고 있다.On the other hand, in general, in order to connect wires, some of the coating layers of the wires on both sides are removed and bound, and insulation tape is wrapped around the connection parts of the wires exposed to the outside to prevent fire, electric shock, etc. safety accidents are prevented.
하지만 대부분의 테이프는 단순히 전선 결선부 등을 보호하는 것에 그치고 있으며 고온 또는 열변화를 가지는 현장에서의 사용은 제한되고 있어, 이러한 문제점을 해결하기 위한 기술이 필요한 실정이다.However, most of the tapes stop at simply protecting wire connection parts and the like, and their use in fields with high temperatures or thermal changes is limited. Therefore, a technology for solving these problems is required.
본 발명이 해결하고자 하는 과제는 색상이 가역적으로 변경되어 고온 또는 열변화를 가지는 현장에서 사용할 수 있고, 이에 따라 안전에 도움이 되는 자가 융착 테이프를 제공하는 것이다.The problem to be solved by the present invention is to provide a self-fusing tape that can be used in a field having a high temperature or thermal change because the color is reversibly changed, and thus is helpful in safety.
본 발명의 일 실시예는 실리콘, 안료 및 실리콘 오일을 포함하고, 온도에 따라 변색되는 자기 융착 실리콘 테이프이다.One embodiment of the present invention is a self-fusing silicone tape comprising silicone, pigment and silicone oil and discoloring with temperature.
상기 안료는 가역형 시온 안료일 수 있다.The pigment may be a reversible Zion pigment.
상기 안료의 함량은 상기 실리콘 100중량부 대비 0.5~1.5중량부일 수 있고, 상기 실리콘 오일의 함량은 상기 실리콘 100중량부 대비 0.1~1중량부일 수 있다.The content of the pigment may be 0.5 to 1.5 parts by weight based on 100 parts by weight of the silicone, and the content of the silicone oil may be 0.1 to 1 part by weight based on 100 parts by weight of the silicone.
상기 안료 및 실리콘 오일의 중량비는 1:0.1~1 일 수 있다.The weight ratio of the pigment and the silicone oil may be 1:0.1 to 1.
상기 자기 융착 실리콘 테이프는 인장강도가 85kgf/cm2 이상일 수 있다.The self-fusing silicon tape may have a tensile strength of 85 kgf/cm 2 or more.
본 발명의 다른 실시예는 실리콘 오일 및 안료를 혼합하여 안료 용액을 제조하는 단계; 및 상기 안료 용액에 실리콘을 혼합하는 단계;를 포함하는 자기 융착 실리콘 테이프 제조방법이다.Another embodiment of the present invention is to prepare a pigment solution by mixing the silicone oil and the pigment; and mixing silicone with the pigment solution.
상기 안료 용액은 상기 안료 및 실리콘 오일을 1:0.1~1 중량비로 혼합할 수 있다.The pigment solution may be mixed with the pigment and silicone oil in a weight ratio of 1:0.1 to 1.
본 발명에 따른 자기 융착 테이프는 시온 안료 및 실리콘 오일을 사용함으로써, 시온 안료의 혼합을 용이하게 할 수 있고, 공기 중에 흩어질 수 있는 시온 안료의 양을 최소화함으로써 경제성을 향상시킬 수 있다.The self-fusing tape according to the present invention can facilitate mixing of Zion pigments by using Zion pigments and silicone oil, and can improve economic feasibility by minimizing the amount of Zion pigments that can be dispersed in the air.
또한, 전용 배합기의 사용없이 일반 배합기로 용이하게 배합할 수 있다.In addition, it can be easily blended with a general blender without using a dedicated blender.
또한, 본 발명에 따른 자기 융착 테이프는 안료 및 실리콘 오일의 중량비를 한정함으로써 물성을 극대화하고, 혼합 효율을 극대화할 수 있다.In addition, the self-fusing tape according to the present invention can maximize physical properties and mixing efficiency by limiting the weight ratio of the pigment and the silicone oil.
또한, 본 발명에 따른 자기 융착 테이프는 안료 및 실리콘 오일의 함량을 한정함으로써 품질이 우수하고, 동시에 자기 융착 테이프의 물성이 저하되지 않을 수 있다.In addition, the quality of the self-fusing tape according to the present invention is limited by limiting the content of the pigment and the silicone oil, and at the same time, the physical properties of the self-fusing tape may not be deteriorated.
도 1은 본 발명의 일실시예인 자기 융착 실리콘 테이프를 나타낸 사진이다.
도 2는 본 발명의 일실시예인 자기 융착 실리콘 테이프가 열에 의해 변색된 모습을 나타낸 사진이다.
도 3은 본 발명의 일실시예인 자기 융착 실리콘 테이프가 열에 의해 변색된 후 되돌아온 모습을 나타낸 사진이다.1 is a photograph showing a self-fusing silicon tape as an embodiment of the present invention.
2 is a photograph showing a state in which a self-fusing silicon tape, which is an embodiment of the present invention, is discolored by heat.
3 is a photograph showing a state in which a self-fusing silicon tape, which is an embodiment of the present invention, is discolored by heat and then returned.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 구체적인 실시예를 통하여 보다 상세하게 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, specific embodiments of the present invention will be described in more detail so that those skilled in the art can easily implement the present invention. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein.
도 1은 본 발명의 일실시예인 자기 융착 실리콘 테이프를 나타낸 사진, 도 2는 본 발명의 일실시예인 자기 융착 실리콘 테이프가 열에 의해 변색된 모습을 나타낸 사진, 도 3은 본 발명의 일실시예인 자기 융착 실리콘 테이프가 열에 의해 변색된 후 되돌아온 모습을 나타낸 사진이다.1 is a photograph showing a self-fusing silicone tape, which is an embodiment of the present invention, FIG. 2 is a photograph showing a self-fusing silicon tape, which is an embodiment of the present invention, discolored by heat, and FIG. This is a picture showing the appearance of the fused silicone tape after it has been discolored by heat and then returned.
도 1 내지 3을 참조하면, 본 발명의 일 실시예는 실리콘, 안료 및 실리콘 오일을 포함하고, 온도에 따라 변색되는 자기 융착 실리콘 테이프이다.Referring to Figures 1 to 3, one embodiment of the present invention is a self-fusing silicone tape that includes silicone, pigment and silicone oil, and is discolored depending on temperature.
상기 실리콘은, 자기 융착 실리콘 테이프의 베이스 수지이고, 상기 안료는 자기 융착 실리콘 테이프가 온도에 따라 색이 변할 수 있도록 첨가되는 것으로, 시온 안료일 수 있으며, 바람직하게는 가역형 시온안료일 수 있다.The silicone is a base resin of the self-fusing silicone tape, and the pigment is added so that the self-fusing silicone tape can change color depending on the temperature, and may be a zion pigment, preferably a reversible zion pigment.
상기 가역형 시온안료는 특정 온도 이상 시 색이 변하고, 특정 온도 미만으로 내려가면 색이 다시 돌아오는 안료를 말한다.The reversible zion pigment refers to a pigment that changes color when the temperature exceeds a certain temperature and returns when the temperature drops below a certain temperature.
상기 실리콘 오일은 상기 실리콘과 안료의 혼합을 용이하게 하며, 상기 실리콘과 상기 안료를 혼합기 내에서 혼합 시 상기 안료가 혼합기 외부로 유출되는 것을 방지할 수 있다. The silicone oil facilitates mixing of the silicone and the pigment, and when mixing the silicone and the pigment in the mixer, it is possible to prevent the pigment from leaking out of the mixer.
구체적으로, 상기 안료는 분말 형태로서, 1~10㎛의 입자 크기일 수 있다. 상기 안료는 입자 크기가 매우 작기 때문에 혼합기 내 투입 시 외부로 쉽게 유실될 수 있으며, 유실 양은 약 1~5중량% 이상이다. Specifically, the pigment may be in powder form and have a particle size of 1 μm to 10 μm. Since the pigment has a very small particle size, it can be easily lost to the outside when it is introduced into the mixer, and the amount of loss is about 1 to 5% by weight or more.
본 발명은 상기 실리콘 오일을 사용함으로써, 안료의 유실 양을 0.1~1중량%로 최소화할 수 있으며, 상기 안료와 실리콘과의 혼합을 용이하게 하여 전용 배합기(리더기)를 사용하지 않고 일반 배합기(2롤 롤러 등)로도 배합을 용이하게 할 수 있다.In the present invention, by using the silicone oil, the loss amount of the pigment can be minimized to 0.1 to 1% by weight, and mixing of the pigment and silicone is facilitated, so that a general blender (2 A roll roller, etc.) can also facilitate mixing.
본 발명에서 상기 안료의 함량은 상기 실리콘 100중량부 대비 0.5~1.5중량부일 수 있고, 상기 실리콘 오일의 함량은 상기 실리콘 100중량부 대비 0.1~1중량부일 수 있으며, 바람직하게 상기 안료의 함량은 상기 실리콘 100중량부 대비 0.8~1.2중량부일 수 있고, 상기 실리콘 오일의 함량은 상기 실리콘 100중량부 대비 0.4~0.6중량부일 수 있다.In the present invention, the content of the pigment may be 0.5 to 1.5 parts by weight based on 100 parts by weight of the silicone, and the content of the silicone oil may be 0.1 to 1 part by weight based on 100 parts by weight of the silicone. It may be 0.8 to 1.2 parts by weight compared to 100 parts by weight of silicone, and the content of the silicone oil may be 0.4 to 0.6 parts by weight compared to 100 parts by weight of the silicone.
상기 안료의 함량이 상기 실리콘 100중량부 대비 0.5중량부 미만이면, 자기 융착 실리콘 테이프의 온도에 따른 색 변화가 용이하지 않고, 1.5 중량부를 초과하면 인장강도가 저하될 수 있다.If the content of the pigment is less than 0.5 parts by weight relative to 100 parts by weight of the silicone, the color change according to the temperature of the self-adhesive silicone tape is not easy, and if it exceeds 1.5 parts by weight, the tensile strength may be lowered.
또한, 상기 실리콘 오일의 함량이 상기 실리콘 100중량부 대비 0.1 중량부 미만이면, 배합 속도가 저조하고, 유실량이 많아 상기 안료와의 혼합이 용이하지 않고, 자기 융착 실리콘 테이프의 온도에 따른 색 변화가 용이하지 않으며, 1중량부를 초과하면 인장강도가 저하될 수 있다.In addition, when the content of the silicone oil is less than 0.1 parts by weight relative to 100 parts by weight of the silicone, the mixing speed is low and the amount of loss is large, so it is not easy to mix with the pigment, and the color change according to the temperature of the self-fusing silicone tape It is not easy, and if it exceeds 1 part by weight, the tensile strength may be lowered.
또한, 상기 안료 및 실리콘 오일의 중량비는 1:0.1~1일 수 있고, 바람직하게는 1:0.4~0.6일 수 있다. 상기 안료 및 실리콘 오일의 중량비가 1:0.1 미만이면 실리콘과의 혼합이 용이하지 않고, 1:1을 초과하면 실리콘 오일의 함량이 높아 자기 융착 실리콘 테이프의 인장강도가 저하될 수 있다.In addition, the weight ratio of the pigment and the silicone oil may be 1:0.1 to 1, preferably 1:0.4 to 0.6. When the weight ratio of the pigment and the silicone oil is less than 1:0.1, mixing with silicone is not easy, and when the weight ratio exceeds 1:1, the content of the silicone oil is high, and the tensile strength of the self-fusing silicone tape may decrease.
본 발명에 따른 자기 융착 실리콘 테이프는 인장강도가 85kgf/cm2 이상일 수 있으며, 바람직하게는 90kgf/cm2 이상일 수 있다. 상기 인장강도가 85kgf/cm2 미만이면, 현장에서 사용 시 쉽게 끊어져 품질이 저하될 수 있다.The self-fusing silicone tape according to the present invention may have a tensile strength of 85 kgf/cm 2 or more, preferably 90 kgf/cm 2 or more. If the tensile strength is less than 85 kgf/cm 2 , it may be easily broken when used in the field and the quality may deteriorate.
본 발명에서 상기 온도는 시온 안료에 따라 다양하게 조절될 수 있다.In the present invention, the temperature may be variously adjusted according to the Zion pigment.
도 1은 자기 융착 실리콘 테이프 제조방법이다.1 is a method for manufacturing a self-fusing silicon tape.
도 1을 참조하면, 본 발명의 다른 실시예는 안료 및 실리콘 오일을 혼합하여 안료 용액을 제조하는 단계; 및 상기 안료 용액에 실리콘을 혼합하는 단계;를 포함하는 자기 융착 실리콘 테이프 제조방법이다.Referring to Figure 1, another embodiment of the present invention is to prepare a pigment solution by mixing the pigment and silicone oil; and mixing silicone with the pigment solution.
상기 안료 및 실리콘 오일을 혼합하여 안료 용액을 제조하는 단계는 상기 안료와 실리콘과의 혼합이 용이하게 하고, 상기 안료의 유출을 방지하기 위한 것이다.The step of preparing a pigment solution by mixing the pigment and silicone oil is to facilitate mixing of the pigment and silicone and to prevent leakage of the pigment.
상기 안료 용액은 상기 안료 및 실리콘 오일을 1:0.1~1 중량비로 혼합하여 제조될 수 있고, 바람직하게는 1:0.4~0.6 중량비로 혼합하여 제조될 수 있다. 상기 안료 및 실리콘 오일의 중량비가 1:0.1 미만이면 실리콘과의 혼합이 용이하지 않고, 1:1을 초과하면 실리콘 오일의 함량이 높아 자기 융착 실리콘 테이프의 인장강도가 저하될 수 있다.The pigment solution may be prepared by mixing the pigment and the silicone oil at a weight ratio of 1:0.1 to 1, preferably at a weight ratio of 1:0.4 to 0.6. When the weight ratio of the pigment and the silicone oil is less than 1:0.1, mixing with silicone is not easy, and when the weight ratio exceeds 1:1, the content of the silicone oil is high, and the tensile strength of the self-fusing silicone tape may decrease.
이와 같이 본 발명에 따른 자기 융착 실리콘 테이프는 인장강도가 저하되지 않으면서도, 색 변화가 가능하여 현장에서 열로 인해 발생할 수 있는 사고를 방지할 수 있다.As described above, the self-fusing silicone tape according to the present invention can change color without deteriorating tensile strength, thereby preventing accidents that may occur due to heat in the field.
이하, 본 발명에 따른 구체적인 실시예를 들어 설명한다.Hereinafter, specific embodiments according to the present invention will be described.
실시예 1Example 1
시온 안료(Thermochromic Red 65) 10g 및 실리콘 오일 5g을 혼합하여 안료 용액을 제조한다. 상기 안료 용액 15g과 실리콘 1000g을 롤러를 이용하여 배합하였다. 이후, 압출기를 이용하여 폭5mm~1M, 두께 0.3T~1.5T의 규격에 압출 금형 크기를 맞추어 200~600℃ 및 30~70RPM으로, 자기 융착 실리콘 테이프를 제조 하였다.A pigment solution was prepared by mixing 10 g of Zion pigment (Thermochromic Red 65) and 5 g of silicone oil. 15 g of the pigment solution and 1000 g of silicone were mixed using a roller. Then, using an extruder, a self-fusing silicone tape was manufactured at 200 to 600 ° C and 30 to 70 RPM by adjusting the size of the extrusion mold to the specifications of 5 mm to 1 M in width and 0.3 T to 1.5 T in thickness.
실시예 2Example 2
상기 실시예 1에서 시온 안료의 함량을 50g으로 변경한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 자기 융착 실리콘 테이프를 제조하였다.A self-fusing silicone tape was manufactured in the same manner as in Example 1, except that the content of the Zion pigment was changed to 50 g in Example 1.
실시예 3Example 3
상기 실시예 1에서 시온 안료의 함량을 3g으로 변경한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 자기 융착 실리콘 테이프를 제조하였다.A self-fusing silicone tape was manufactured in the same manner as in Example 1, except that the content of Zion pigment was changed to 3 g in Example 1.
실시예 4Example 4
상기 실시예 1에서 시온 안료의 함량을 20g으로 변경한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 자기 융착 실리콘 테이프를 제조하였다.A self-fusing silicone tape was manufactured in the same manner as in Example 1, except that the content of the Zion pigment was changed to 20 g in Example 1.
실시예 5Example 5
상기 실시예 1에서 실리콘 오일의 함량을 1g으로 변경한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 자기 융착 실리콘 테이프를 제조하였다.A self-fusing silicone tape was manufactured in the same manner as in Example 1, except that the content of the silicone oil was changed to 1 g in Example 1.
실시예 6Example 6
상기 실시예 1에서 실리콘 오일의 함량을 10g으로 변경한 것을 제외하고는 상기 실시예 1과 동일한 방법으로 자기 융착 실리콘 테이프를 제조하였다.A self-fusing silicone tape was manufactured in the same manner as in Example 1, except that the content of the silicone oil was changed to 10 g in Example 1.
비교예 1Comparative Example 1
시온 안료(Thermochromic Red 65) 10g과 실리콘 1000g을 롤러를 이용하여 배합하였다. 이후, 압출기를 이용하여 폭5mm~1M, 두께 0.3T~1.5T의 규격에 압출 금형 크기를 맞추어 200~600℃ 및 30~70RPM으로, 자기 융착 실리콘 테이프를 제조 하였다.10 g of Zion pigment (Thermochromic Red 65) and 1000 g of silicone were mixed using a roller. Then, using an extruder, a self-fusing silicone tape was manufactured at 200 to 600 ° C and 30 to 70 RPM by adjusting the size of the extrusion mold to the specifications of 5 mm to 1 M in width and 0.3 T to 1.5 T in thickness.
비교예 2Comparative Example 2
실리콘 1000g을 압출기를 이용하여 폭5mm~1M, 두께 0.3T~1.5T의 규격에 압출 금형 크기를 맞추어 200~600℃ 및 30~70RPM으로, 자기 융착 실리콘 테이프를 제조 하였다.A self-fusing silicone tape was manufactured by using an extruder of 1000 g of silicone at 200 to 600 ° C and 30 to 70 RPM by adjusting the size of the extrusion mold to the specifications of 5 mm to 1 M in width and 0.3 T to 1.5 T in thickness.
실험예 1Experimental Example 1
상기 실시예 1 내지 6 및 비교예 1에서 제조된 자기 융착 실리콘 테이프를 130℃에서 200mm*200mm*2T 시편으로 제조하였으며, 시편의 외관을 하기 측정방법으로 측정하였고, 이에 대한 평균 결과를 하기 표 1에 나타내었다.The self-fusing silicone tapes prepared in Examples 1 to 6 and Comparative Example 1 were prepared as 200mm * 200mm * 2T specimens at 130 ° C., and the appearance of the specimens was measured by the following measurement method, and the average results thereof are shown in Table 1 below. shown in
[측정방법][How to measure]
외관 : 자기 융착 실리콘 테이프의 변화 전 외관과 85℃의 열을 가한 후의 외관을 육안으로 확인하여 고르게 동일한 색상을 나타내는 경우를 양호로, 색이 동일하지 않은 경우를 불량으로 표시함Appearance: Visually check the appearance of the self-fusing silicone tape before the change and after applying heat at 85℃, and if the color is uniformly the same, it is marked as good, and if the color is not the same, it is marked as defective.
상기 표 1을 참고하면, 안료 및 오일의 함량이 실리콘 100중량부 대비 1중량부 및 0.5중량부(실시예1)인 경우 변화 전 및 변화 후 외관의 색상이 고른 것을 확인할 수 있다.Referring to Table 1, when the content of the pigment and oil was 1 part by weight and 0.5 part by weight (Example 1) compared to 100 parts by weight of silicone, it could be confirmed that the color of the appearance before and after the change was even.
반면, 안료의 함량이 실리콘 100중량부 대비 0.3중량부인 경우(실시예 3), 실리콘 오일의 함량이 실리콘 100중량부 대비 0.1중량부인 경우(실시예 5) 및 실리콘 오일을 넣지 않은 경우(비교예 1)의 경우 변화 전 후의 외관의 색상이 고르지 않은 것을 확인할 수 있다.On the other hand, when the content of the pigment is 0.3 parts by weight relative to 100 parts by weight of silicone (Example 3), when the content of silicone oil is 0.1 part by weight relative to 100 parts by weight of silicone (Example 5) and when no silicone oil is added (Comparative Example) In the case of 1), it can be confirmed that the color of the exterior before and after the change is uneven.
또한, 안료의 함량이 실리콘 100중량부 대비 5중량부인 경우(실시예 2) 변화 후 외관의 색상이 고르지 않은 것을 확인할 수 있다.In addition, when the content of the pigment is 5 parts by weight compared to 100 parts by weight of silicone (Example 2), it can be seen that the color of the appearance after the change is uneven.
실험예 2Experimental Example 2
상기 실시예 1 내지 6, 비교예 1 및 2에서 제조된 자기 융착 실리콘 테이프를 130℃에서 200mm*200mm*2T 시편으로 제조하였으며, 시편의 인장강도를 하기 측정방법으로 3회 측정하였고, 이에 대한 평균 결과를 하기 표 1에 나타내었다.The self-fusing silicone tapes prepared in Examples 1 to 6 and Comparative Examples 1 and 2 were prepared as 200mm * 200mm * 2T specimens at 130 ° C, and the tensile strength of the specimens was measured three times by the following measurement method, and the average of these The results are shown in Table 1 below.
[측정방법][How to measure]
인장강도 : ASTM D412 시험법에 따라 진행하였다.Tensile strength: It was conducted according to the ASTM D412 test method.
상기 표 2를 참고하면, 안료의 함량이 실리콘 100중량부 대비 5중량부인 경우(실시예 2), 안료의 함량이 실리콘 100중량부 대비 2중량부인 경우(실시예 4), 실리콘 오일의 함량이 실리콘 100중량부 대비 1 중량부인 경우(실시예 6)의 경우 인장강도가 85(kgf/cm2) 미만인 것을 확인할 수 있고, 안료 및 실리콘 오일을 넣지 않은 경우(비교예 2)와 비교할 때, 매우 낮은 인장강도를 가지는 것을 확인할 수 있다.Referring to Table 2, when the content of the pigment is 5 parts by weight relative to 100 parts by weight of silicone (Example 2), when the content of the pigment is 2 parts by weight relative to 100 parts by weight of silicone (Example 4), the content of silicone oil In the case of 1 part by weight compared to 100 parts by weight of silicone (Example 6), it can be seen that the tensile strength is less than 85 (kgf / cm2), and compared to the case where no pigment and silicone oil are added (Comparative Example 2), very low It can be confirmed that it has tensile strength.
반면, 안료 및 오일의 함량이 실리콘 100중량부 대비 1중량부 및 0.5중량부(실시예1)인 경우는 안료 및 실리콘 오일을 넣지 않은 경우(비교예 2)와 비교할 때, 크게 저하되지 않은 것을 확인할 수 있다.On the other hand, when the content of the pigment and oil is 1 part by weight and 0.5 part by weight (Example 1) relative to 100 parts by weight of silicone, compared to the case where the pigment and silicone oil are not added (Comparative Example 2), it is not significantly reduced. You can check.
실험예 3Experimental Example 3
상기 실시예 1 내지 6 및 비교예 1에서 제조된 자기 융착 실리콘 테이프를 130℃에서 200mm*200mm*2T 시편으로 제조하였으며, 시편의 색상 변화 속도를 하기 측정방법으로 3회 측정하였고, 이에 대한 평균 결과를 하기 표 3에 나타내었다.The self-fusing silicone tapes prepared in Examples 1 to 6 and Comparative Example 1 were prepared as 200mm * 200mm * 2T specimens at 130 ° C, and the color change rate of the specimens was measured three times by the following measurement method, and the average result thereof are shown in Table 3 below.
[측정방법][How to measure]
색상 변화 속도 : 각각 폭을 25mm씩 일정하게 자른 뒤 수직 스탠드에 메달아 온도 85℃이상의 물에 수직으로 동시에 낙하 시킨 후, 색상의 변화를 확인 비교하였고, 이후, 변화 후 원상 회복되는 시간을 타이머로 측정하여 기록하였다.Color change speed: After cutting each width uniformly by 25mm, hanging it on a vertical stand and dropping it vertically into water with a temperature of 85℃ or higher at the same time, the color change was checked and compared, and then the recovery time after change was measured with a timer. Measured and recorded.
상기 표 3을 참조하면, 시온 안료가 첨가된 경우, 색상 변화 속도는 차이가 나지 않는 것을 확인할 수 있다.Referring to Table 3, when Zion pigment is added, it can be seen that there is no difference in color change rate.
이와 같이, 본 발명에 따라 제조된 자기 융착 테이프는 시온 안료 및 실리콘 오일을 사용함으로써, 시온 안료의 혼합을 용이하게 할 수 있고, 공기 중에 흩어질 수 있는 시온 안료의 양을 최소화함으로써 경제성을 향상시킬 수 있다.As such, the self-fusing tape manufactured according to the present invention can facilitate mixing of Zion pigments by using Zion pigments and silicone oil, and can improve economic feasibility by minimizing the amount of Zion pigments that can be dispersed in the air. have.
또한, 본 발명에 따른 자기 융착 테이프는 안료 및 실리콘 오일의 중량비를 한정함으로써 물성의 저하를 방지하고, 혼합 효율을 극대화할 수 있다.In addition, the self-fusing tape according to the present invention can prevent degradation of physical properties and maximize mixing efficiency by limiting the weight ratio of the pigment and the silicone oil.
또한, 본 발명에 따른 자기 융착 테이프는 안료 및 실리콘 오일의 함량을 한정함으로써 품질이 우수하고, 자기 융착 테이프의 물성이 저하되지 않을 수 있다.In addition, the quality of the self-fusing tape according to the present invention is limited by limiting the content of the pigment and the silicone oil, and the physical properties of the self-fusing tape may not be deteriorated.
이상으로 본 발명의 바람직한 실시예를 상세하게 설명하였다. 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다.Above, preferred embodiments of the present invention have been described in detail. The description of the present invention is for illustrative purposes, and those skilled in the art will understand that other specific forms can be easily modified without changing the technical spirit or essential features of the present invention.
따라서, 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미, 범위 및 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.Therefore, the scope of the present invention is indicated by the following claims rather than the above detailed description, and all changes or modifications derived from the meaning, scope and equivalent concept of the claims are included in the scope of the present invention. should be interpreted
Claims (7)
A self-fusing silicone tape that contains silicone, pigment and silicone oil, and is discolored with temperature.
상기 안료는 가역형 시온 안료인 것을 특징으로 하는 자기 융착 실리콘 테이프.
According to claim 1,
The self-fusing silicone tape, characterized in that the pigment is a reversible zion pigment.
상기 안료의 함량은 상기 실리콘 100중량부 대비 0.5~1.5중량부이고, 상기 실리콘 오일의 함량은 상기 실리콘 100중량부 대비 0.1~1중량부인 것을 특징으로 하는 자기 융착 실리콘 테이프.
According to claim 1,
The content of the pigment is 0.5 to 1.5 parts by weight based on 100 parts by weight of the silicone, and the content of the silicone oil is 0.1 to 1 part by weight based on 100 parts by weight of the silicone.
상기 안료 및 실리콘 오일의 중량비는 1:0.1~1인 것을 특징으로 하는 자기 융착 실리콘 테이프.
According to claim 1,
Self-fusing silicone tape, characterized in that the weight ratio of the pigment and silicone oil is 1: 0.1 to 1.
상기 자기 융착 실리콘 테이프는 인장강도가 85kgf/cm2 이상인 것을 특징으로 하는 자기 융착 실리콘 테이프.
According to claim 1,
The self-fusing silicone tape has a tensile strength of 85 kgf/cm 2 or more.
상기 안료 용액에 실리콘을 혼합하는 단계;
를 포함하는 자기 융착 실리콘 테이프 제조방법.
preparing a pigment solution by mixing a pigment and a silicone oil; and
mixing silicone with the pigment solution;
Self-fusing silicone tape manufacturing method comprising a.
상기 안료 용액은 상기 안료 및 실리콘 오일을 1:0.1~1 중량비로 혼합하는 것을 특징으로 하는 자기 융착 실리콘 테이프 제조방법.According to claim 6,
The pigment solution is a self-fusing silicone tape manufacturing method, characterized in that the pigment and silicone oil are mixed in a weight ratio of 1: 0.1 to 1.