KR20220040873A - Silicone artificial laether - Google Patents

Silicone artificial laether Download PDF

Info

Publication number
KR20220040873A
KR20220040873A KR1020200124129A KR20200124129A KR20220040873A KR 20220040873 A KR20220040873 A KR 20220040873A KR 1020200124129 A KR1020200124129 A KR 1020200124129A KR 20200124129 A KR20200124129 A KR 20200124129A KR 20220040873 A KR20220040873 A KR 20220040873A
Authority
KR
South Korea
Prior art keywords
silicone
layer
curing
coating solution
artificial leather
Prior art date
Application number
KR1020200124129A
Other languages
Korean (ko)
Other versions
KR102521018B1 (en
Inventor
신무현
Original Assignee
신무현
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 신무현 filed Critical 신무현
Priority to KR1020200124129A priority Critical patent/KR102521018B1/en
Publication of KR20220040873A publication Critical patent/KR20220040873A/en
Application granted granted Critical
Publication of KR102521018B1 publication Critical patent/KR102521018B1/en

Abstract

The present invention provides a silicone artificial leather to provide excellent surface texture due to slip properties. According to the present invention, the silicone artificial leather comprises: a first silicone layer formed by curing a first coating solution containing a silicone resin and a catalyst for accelerating curing of the silicone resin; a second silicone layer formed by curing a second coating solution containing the silicone resin, the catalyst, a retardant for delaying curing of the silicone resin at room temperature, and an inorganic pigment on the first silicone layer; a tertiary silicone layer formed by curing the second coating solution on the second silicone layer; and an inner skin layer which is a colored fabric laminated on the tertiary silicone layer and having elasticity, wherein the silicone resin is a maximizing of powdered silica, polydimethylsiloxane, and a curing agent is used for elasticity and surface slip properties of the first to third silicone layers.

Description

실리콘 인조 피혁{SILICONE ARTIFICIAL LAETHER}Silicone artificial leather {SILICONE ARTIFICIAL LAETHER}

본 발명은 실리콘 인조 피혁에 관한 것으로, 더욱 상세하게는 자동차 시트(seat)와 같은 내장재에 적용되기에 적합한 실리콘 인조 피혁에 관한 것이다. The present invention relates to artificial silicone leather, and more particularly, to silicone artificial leather suitable for application to interior materials such as automobile seats.

자동차 내장재, 예컨대 자동차 시트(seat)에는 고가의 천연 피혁이 사용되기도 하지만 대부분의 경우에는 생산이 용이하고 제조비용이 저렴한 인조 피혁이 사용되고 있다.Although expensive natural leather is sometimes used for automobile interior materials, for example, automobile seats, artificial leather, which is easy to produce and inexpensive to manufacture, is used.

자동차의 내장재로 사용되기 위한 인조 피혁의 일 예가 한국공개특허 10-2012-0133210호(자동차 내장재용 폴리우레탄 인조피혁 제조방법)에 개시되어 있다. 이 공개특허에서는 릴리즈페이퍼의 상면에 폴리우레탄 수지를 복수 회 반복적으로 도포 및 건조하는 단계를 통해 복수 층으로 적층된 표면층을 형성하고, 이후 표면층의 상면에 접착제를 도포하여 접착층을 형성하며, 마지막으로 접착층의 상면에 직물, 편물 또는 부직포를 접착하여 원단층을 형성한다.An example of artificial leather for use as an interior material of a vehicle is disclosed in Korean Patent Application Laid-Open No. 10-2012-0133210 (Method for manufacturing polyurethane artificial leather for interior material). In this publication, a surface layer laminated in multiple layers is formed through a step of repeatedly applying and drying a polyurethane resin a plurality of times on the upper surface of the release paper, and then an adhesive is applied to the upper surface of the surface layer to form an adhesive layer, and finally A fabric, knitted fabric or nonwoven fabric is adhered to the upper surface of the adhesive layer to form a fabric layer.

위 표면층을 형성하는 과정은 릴리즈페이퍼의 상면에 제 1폴리우레탄 수지를 도포 및 건조하여 가장 외부의 표면을 이루게 되는 제 1표면층을 형성하는 단계와, 제 1표면층의 상면에 제 2폴리우레탄 수지를 도포 및 건조하여 제 2표면층을 형성하는 단계와, 제 2표면층의 상면에 제 3폴리우레탄 수지 및 안료를 도포한 후 건조하여 색상을 발현시키는 제 3표면층을 형성하는 단계를 통해 이루어진다.The process of forming the upper surface layer includes the steps of applying and drying a first polyurethane resin on the upper surface of the release paper to form a first surface layer forming the outermost surface, and a second polyurethane resin on the upper surface of the first surface layer. Forming a second surface layer by coating and drying, and applying a third polyurethane resin and a pigment on the upper surface of the second surface layer, and then drying to form a third surface layer to express color.

인조 피혁을 사용할 때는 릴리즈페이퍼를 제거하고 사용한다. When using artificial leather, remove the release paper before use.

공개특허공보 제10-2012-0133210호(자동차 내장재용 폴리우레탄 인조피혁 제조방법)Laid-open Patent Publication No. 10-2012-0133210 (Method for manufacturing polyurethane artificial leather for automobile interior materials)

위 공개특허공보 제10-2012-0133210호에 개시된 종래 기술에서는 인조 피혁의 표면층이 폴리우레탄을 기반으로 한다. 그런데 폴리우레탄은 자외선에 취약하기 때문에 폴리우레탄을 기반으로 하는 위 공개특허공보의 인조 피혁은 자동차의 내장재로 사용될 경우 그 수명이 매우 짧은 문제를 갖는다. 또한, 위 공개특허공보의 인조 피혁에서는 제 3표면층과 원단층 간 결합에 접착제가 사용되기 때문에 제조 공정 및 제조 비용의 면에 있어서 그다지 효율적이지 않다.In the prior art disclosed in Patent Publication No. 10-2012-0133210, the surface layer of artificial leather is based on polyurethane. However, since polyurethane is vulnerable to UV rays, the artificial leather of the above publication based on polyurethane has a very short lifespan when used as an interior material of a vehicle. In addition, in the artificial leather of the above publication, since an adhesive is used for bonding between the third surface layer and the fabric layer, it is not very efficient in terms of manufacturing process and manufacturing cost.

따라서 본 발명은 위와 같은 종래 기술의 문제점을 해결할 수 있는 실리콘 인조 피혁을 제공하고자 한다.Accordingly, the present invention is to provide a silicone artificial leather that can solve the above problems of the prior art.

본 발명은, 실리콘 수지 및 상기 실리콘 수지의 경화를 촉진시키기 위한 촉매를 포함하는 1차 코팅액을 경화하여 형성한 1차 실리콘층; 상기 실리콘 수지, 상기 촉매, 상기 실리콘 수지의 상온 경화를 지연시키기 위한 지연제 및 유색 무기안료를 포함하는 2차 코팅액을 상기 1차 실리콘층 상에서 경화하여 형성한 2차 실리콘층; 상기 2차 코팅액을 상기 2차 실리콘층 상에서 경화하여 형성한 3차 실리콘층; 및 상기 3차 실리콘층 상에 적층된 유색 직물로서, 탄력성을 갖는 내피층;을 포함하는 실리콘 인조 피혁을 제공한다. 여기서, 상기 실리콘 수지로는 상기 1차 내지 3차 실리콘층의 탄력성 및 표면 슬립성을 위해 가루 형태의 실리카와, 폴리디메틸실록산과, 경화제를 혼합한 것이 사용된다.The present invention, a first silicone layer formed by curing a first coating solution containing a silicone resin and a catalyst for accelerating the curing of the silicone resin; a secondary silicone layer formed by curing a secondary coating solution including the silicone resin, the catalyst, a retarder for delaying room temperature curing of the silicone resin, and a colored inorganic pigment on the primary silicone layer; a tertiary silicone layer formed by curing the secondary coating solution on the secondary silicone layer; and an inner skin layer having elasticity as a colored fabric laminated on the tertiary silicone layer. Here, as the silicone resin, a mixture of silica powder, polydimethylsiloxane, and a curing agent is used for elasticity and surface slip properties of the primary to tertiary silicone layers.

상기 촉매로는 녹인 백금과 오가노폴리실록산을 혼합한 것이 사용된다.As the catalyst, a mixture of melted platinum and organopolysiloxane is used.

상기 내피층을 구성하는 유색 직물은 상기 무기안료가 용해된 용제에 함침시킨 폴리에스터 재질의 원사 및 스판 재질의 원사를 직조하여 형성된다.The colored fabric constituting the inner skin layer is formed by weaving a polyester yarn and a spandex yarn impregnated in a solvent in which the inorganic pigment is dissolved.

상기 내피층의 적층은 상기 2차 실리콘층에 도포된 상기 2차 코팅액에 상기 직물이 합쳐진 상태에서 상기 2차 코팅액이 경화됨으로써 이루어진다.Lamination of the inner skin layer is made by curing the secondary coating solution in a state in which the fabric is combined with the secondary coating solution applied to the secondary silicone layer.

상기 1차 코팅액은 고분자 수지 또는 종이 재질의 기재 시트에 도포된 후 경화되고, 그러면 상기 1차 실리콘층이 기재 시트 상에 형성된다. 실리콘 인조 피혁의 사용 시에는 기재 시트가 1차 실리콘층으로부터 제거된다. The first coating solution is applied to a base sheet made of a polymer resin or paper material and then cured, and then the first silicone layer is formed on the base sheet. When the silicone artificial leather is used, the base sheet is removed from the primary silicone layer.

상기 실리콘 인조 피혁의 사용 시, 상기 내피층은 가장 내측의 층을 구성하고, 상기 1차 실리콘층은 사용자에게 직접 노출되는 가장 외측의 층을 구성한다.When the silicone artificial leather is used, the inner skin layer constitutes the innermost layer, and the first silicone layer constitutes the outermost layer directly exposed to the user.

본 발명에 따른 실리콘 인조 피혁은 자외선에 강한 특성을 갖는 실리콘을 기반으로 하면서도 탄력성, 색상 및 내광성을 갖고, 외부에 노출되는 가장 외측의 1차 실리콘층의 표면이 슬립성을 갖는다. 따라서 상기 실리콘 인조 피혁은 자외선 노출이 잦은 자동차용 내장재로 장기간 사용될 수 있고, 탄력성으로 인해 자동차용 내장재로 사용하기가 매우 편리하며, 다양한 색상의 구현이 가능하여 고객의 색상 요구를 충족시킬 수 있고, 슬립성으로 인해 우수한 표면 질감을 갖는다.The silicone artificial leather according to the present invention has elasticity, color and light resistance while being based on silicon having strong UV-resistance, and the surface of the outermost primary silicone layer exposed to the outside has slip properties. Therefore, the silicone artificial leather can be used for a long time as an interior material for automobiles that are exposed to frequent UV rays, and is very convenient to use as an interior material for automobiles due to its elasticity. It has an excellent surface texture due to its slip properties.

또한, 본 발명에 따르면, 2차 실리콘층, 3차 실리콘층 및 내피층이 모두 색상을 가지므로 실리콘 인조 피혁의 색상이 확실하고 선명하게 구현되고, 3차 실리콘층과 내피층 간 결합에 접착제가 전혀 사용되지 않는다. In addition, according to the present invention, since the secondary silicone layer, the tertiary silicone layer, and the inner skin layer all have a color, the color of the silicone artificial leather is realized clearly and clearly, and the adhesive is applied to the bonding between the tertiary silicone layer and the inner skin layer. not used at all

도 1은 본 발명에 따른 실리콘 인조 피혁을 도시한 단면도이다.
도 2는 도 1의 실리콘 인조 피혁의 제조 과정을 도시한 공정도이다.1 is a cross-sectional view showing a silicone artificial leather according to the present invention.
FIG. 2 is a process diagram illustrating a manufacturing process of the silicone artificial leather of FIG. 1 .

이하, 본 발명에 따른 실리콘 인조 피혁의 바람직한 실시예들을 도면을 참조하여 상세하게 설명한다. 이하에서 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니되며, 발명자는 그 자신의 발명을 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야할 것이다. Hereinafter, preferred embodiments of the silicone artificial leather according to the present invention will be described in detail with reference to the drawings. The terms or words used below should not be construed as being limited to a conventional or dictionary meaning, and based on the principle that the inventor can appropriately define the concept of a term to explain his invention in the best way. It should be interpreted as meaning and concept consistent with the technical idea of the present invention.

본 발명에 따른 실리콘 인조 피혁(100)은 도 1에 도시된 바와 같이 1차 실리콘층(110)과, 2차 실리콘층(120)과, 3차 실리콘층(130)과, 내피층(140)을 포함한다.As shown in FIG. 1 , the silicone artificial leather 100 according to the present invention has a primary silicone layer 110 , a secondary silicone layer 120 , a tertiary silicone layer 130 , and an inner skin layer 140 . includes

1차 실리콘층(110)은 실리콘 수지 및 촉매를 혼합한 1차 코팅액을 경화시킨 층으로서, 탄력성 및 표면 슬립성을 갖는다. 실리콘 인조 피혁(100)을 사용할 때, 1차 실리콘층(110)은 가장 외측에 위치하여 사용자에게 직접 노출된다.The primary silicone layer 110 is a layer obtained by curing a primary coating solution in which a silicone resin and a catalyst are mixed, and has elasticity and surface slip properties. When the silicone artificial leather 100 is used, the primary silicone layer 110 is located at the outermost side and is directly exposed to the user.

위 1차 코팅액의 실리콘 수지는 가루 형태의 실리카와, 폴리디메틸실록산(PDMS, polydimethylsiloxane)과, 경화제를 혼합한 것이다. 위 실리카는 1차 실리콘층(110)의 표면에 슬립성(slip)을 부여하기 위해 사용되고, 폴리디메틸실록산은 1차 실리콘층(110)에 탄력성을 부여하기 위해 사용되며, 경화제는 1차 코팅액의 경화를 위해 사용된다.The silicone resin of the first coating solution is a mixture of silica powder, polydimethylsiloxane (PDMS, polydimethylsiloxane), and a curing agent. The above silica is used to impart slip properties to the surface of the first silicone layer 110, polydimethylsiloxane is used to impart elasticity to the first silicone layer 110, and the curing agent is the first coating solution. used for curing.

위 실리콘 수지 100 중량 대비 실리카는 10~40 중량 범위, 폴리디메틸실록산은 20~60 중량 범위, 경화제는 10~60 중량 범위 내에서 혼합되고, 실리카, 폴리디메틸실록산 및 경화제는 위 중량 범위 내에서 실리콘 수지가 100 중량이 되도록 적절히 혼합된다. 실리카의 함량이 너무 적고 폴리디메틸실록산의 함량이 너무 많으면 1차 실리콘층(110) 표면이 슬립성을 갖지 못하고 끈적거리는 문제가 생긴다. 그리고 실리카의 함량이 너무 많으면 1차 실리콘(110)을 늘렸을 때 표면 갈라짐이 발생하는 문제가 생기고, 폴리디메틸실록산의 함량이 너무 적으면 1차 실리콘층(110)의 탄력성(특히, 늘어난 후 다시 원래대로 축소되려는 복원력)이 저하되는 문제가 생긴다. 바람직한 함량 조합은 실리콘 수지 100 중량 대비 실리카 30 중량, 폴리디메틸실록산 45 중량, 경화제 25 중량 조합, 또는 실리콘 수지 100 중량 대비 실리카 25 중량, 폴리디메틸실록산 55 중량, 경화제 20 중량 조합이다. The silica, polydimethylsiloxane, and the curing agent are mixed within the range of 10 to 40 weight, the curing agent is mixed within the range of 10 to 60 weight, and the silica, polydimethylsiloxane and the curing agent are silicone within the above weight range relative to 100 weight of the silicone resin. The resin is mixed appropriately so that it becomes 100 weight. When the content of silica is too small and the content of polydimethylsiloxane is too large, the surface of the primary silicone layer 110 does not have slip property and becomes sticky. And if the content of silica is too large, a problem of surface cracking occurs when the primary silicon 110 is increased, and if the content of polydimethylsiloxane is too small, the elasticity of the primary silicone layer 110 (especially, after stretching again There is a problem that the resilience to be reduced to the original state) is reduced. A preferred content combination is a combination of 30 weights of silica, 45 weights of polydimethylsiloxane, and 25 weights of curing agent based on 100 weight of silicone resin, or 25 weight of silica, 55 weight of polydimethylsiloxane, and 20 weight of curing agent based on 100 weight of silicone resin.

위 1차 코팅액의 촉매는 실리콘 수지의 경화를 촉진하기 위한 것으로서, 백금을 녹여 오가노폴리실록산을 혼합한 것이다. 1차 코팅액의 촉매의 함량은 실리콘 수지 100 중량 대비 5~35 중량 범위 내가 적당하다. 촉매의 함량이 너무 적으면 1차 코팅액의 경화 속도가 느려 생산성이 저하되고, 너무 많으면 1차 코팅액의 경화가 너무 빨라 1차 실리콘층(110)에 갈라짐과 같은 문제가 발생할 수 있다. 바람직한 촉매 함량은 실리콘 수지 100 중량 대비 10 중량 정도이다.The catalyst of the first coating solution is to accelerate the curing of the silicone resin, and is a mixture of organopolysiloxane by dissolving platinum. The content of the catalyst in the primary coating solution is suitable in the range of 5 to 35 weight relative to 100 weight of the silicone resin. If the content of the catalyst is too small, the curing rate of the primary coating solution is slow and productivity is lowered. If the content of the catalyst is too small, problems such as cracking of the primary silicone layer 110 may occur because the curing of the primary coating solution is too fast. The preferred catalyst content is about 10 weight based on 100 weight of the silicone resin.

2차 실리콘층(120) 및 3차 실리콘층(130)은 실리콘 수지, 촉매, 지연제 및 무기안료를 혼합한 2차 코팅액을 경화시킨 층으로서, 2차 실리콘층(120)은 1차 실리콘층(110) 상에 적층되고, 3차 실리콘층(130)은 2차 실리콘층(120) 상에 적층된다.The secondary silicone layer 120 and the tertiary silicone layer 130 are layers obtained by curing a secondary coating solution in which a silicone resin, a catalyst, a retarder, and an inorganic pigment are mixed, and the secondary silicone layer 120 is a primary silicone layer. It is laminated on 110 , and the tertiary silicon layer 130 is laminated on the secondary silicon layer 120 .

2차 코팅액의 실리콘 수지 및 촉매는 1차 코팅액의 실리콘 수지 및 촉매와 동일하다. 따라서 2차 실리콘층(120) 및 3차 실리콘층(130)도 탄력성 및 표면 슬립성을 갖는다.The silicone resin and catalyst of the secondary coating solution are the same as the silicone resin and catalyst of the primary coating solution. Accordingly, the secondary silicon layer 120 and the tertiary silicon layer 130 also have elasticity and surface slip properties.

실리콘 인조 피혁(100)에서 1차 실리콘층(110)은 약 0.02mm 정도의 두께로 형성되고, 2차 실리콘층(120)은 약 0.2mm 정도의 두께로 형성되며, 3차 실리콘층(130)은 약 0.25mm 정도의 두께로 형성된다. 따라서 실리콘 인조 피혁(100)을 제조할 때는 1차 코팅액의 사용량보다 2차 코팅액의 사용량이 22.5배(0.45/0.02) 정도 많다. 이에 2차 코팅액에는 상온에서 실리콘 수지가 경화되는 것을 지연시키기 위해 지연제가 혼합된다. 지연제의 함량은 실리콘 수지 100 중량 대비 1~5 중량 정도가 적당하다.In the silicone artificial leather 100 , the primary silicone layer 110 is formed to a thickness of about 0.02 mm, the secondary silicone layer 120 is formed to a thickness of about 0.2 mm, and the tertiary silicone layer 130 . is formed to a thickness of about 0.25 mm. Therefore, when manufacturing the silicone artificial leather 100, the amount of the secondary coating solution is 22.5 times (0.45/0.02) more than the amount of the first coating solution. Accordingly, a retarder is mixed in the secondary coating solution to delay curing of the silicone resin at room temperature. The content of the retarder is suitably about 1 to 5 weight based on 100 weight of the silicone resin.

2차 코팅액에 무기안료가 혼합되면 실리콘 인조 피혁(100)이 색을 띠게 되어 미감을 가질 수 있고, 또한 유기안료가 사용된 경우에 비해 우수한 내광성(가시광선에 노출되었을 때 열화, 변색, 퇴색에 견디는 성질)도 가질 수 있다. 무기안료의 함량은 실리콘 인조 피혁(100)의 색상이 뚜렷하게 구현될 수 있는 선에서 적절하게 선택될 수 있는데, 실리콘 수지 100 중량 대비 3~15 중량 정도가 적당하다.When an inorganic pigment is mixed with the secondary coating solution, the silicone artificial leather 100 can be colored and have an aesthetic feeling, and also has superior light resistance (deterioration, discoloration, and fading when exposed to visible light) compared to the case where an organic pigment is used. tolerant properties). The content of the inorganic pigment may be appropriately selected from a line in which the color of the silicone artificial leather 100 can be clearly realized, and about 3 to 15 weight is suitable relative to 100 weight of the silicone resin.

상기 내피층(140)은 3차 실리콘층(130) 상에 적층된 층으로서, 실리콘 인조 피혁(100)의 사용 시 가장 내측에 위치하게 된다. 내피층(140)은 2차 코팅액의 무기안료와 동일한 무기안료가 용해된 용제(예컨대, 디메틸포름알데히드)에 함침한 원사를 직조한 직물(20, 도 2 참조) 형태로 구성된다. 그리고 원사로는 폴리에스터 재질의 원사와 탄력성을 부여하기 위한 스판 재질의 원사가 함께 사용된다. 스판 재질의 원사는 총 사용 원사 100 중량 대비 10~40 중량이 사용되고, 폴리에스터 재질의 원사가 나머지 중량으로 사용된다. 스판 재질의 원사가 너무 적게 사용되면 신율(늘어나는 정도)이 저하되고 너무 많이 사용되면 복원성이 저하된다. 바람직한 스판 재질 원사의 함량은 15 중량 정도이다. 이러한 내피층(140)은 탄력성 및 색상을 갖게 된다.The inner skin layer 140 is a layer stacked on the tertiary silicone layer 130 , and is located at the innermost side when the silicone artificial leather 100 is used. The inner skin layer 140 is configured in the form of a fabric (20, see FIG. 2) woven with yarn impregnated in a solvent (eg, dimethylformaldehyde) in which the same inorganic pigment as the inorganic pigment of the secondary coating solution is dissolved. And as the yarn, a polyester yarn and a spandex yarn to give elasticity are used together. For spandex yarn, 10-40 weight is used based on 100 weight of total yarn used, and polyester yarn is used for the remaining weight. If too little of the spanned yarn is used, the elongation (the degree of elongation) is lowered, and if too much is used, the stability is lowered. The content of the preferred span material yarn is about 15 weight. This endothelial layer 140 has elasticity and color.

이상과 같은 실리콘 인조 피혁(100)의 제조 방법을 도 2을 참조하여 설명하면 아래와 같다. A method of manufacturing the artificial silicone leather 100 as described above will be described with reference to FIG. 2 as follows.

실리콘 인조 피혁(100)의 제조 과정에서는 언와인딩롤(30)로부터 풀리면서 와인딩롤(40)에 감기는 방식으로 기재 시트(10)가 연속적으로 이동하고, 연속적으로 이동하는 기재 시트(10) 상에 1차 실리콘층(110)을 적층하는 과정, 2차 실리콘층(120)을 적층하는 과정, 그리고 3차 실리콘층(130) 및 내피층(140)을 동시에 적층하는 과정이 차례대로 이루어진다. 상기 기재 시트(10)로는 수지 필름(PET 필름 등), 종이 등이 사용될 수 있다.In the manufacturing process of the silicone artificial leather 100, the base sheet 10 continuously moves in such a way that it is wound on the winding roll 40 while being unwound from the unwinding roll 30, and on the continuously moving base sheet 10 The process of laminating the primary silicon layer 110 on the , the process of laminating the secondary silicon layer 120 , and the process of simultaneously laminating the tertiary silicon layer 130 and the inner skin layer 140 are sequentially performed. As the base sheet 10, a resin film (PET film, etc.), paper, or the like may be used.

1차 실리콘층(110)의 적층 과정에서는 기재 시트(10) 상에 1차 코팅액이 도포된 후 나이프(50)에 의해 고르게 펴지고, 이 상태로 기재 시트(10)가 오븐(60)을 통과하면, 1차 코팅액이 경화되어 1차 실리콘층(110)이 형성된다. 한편, 실리콘 인조 피혁(100)이 사용될 때는 기재 시트(10)가 1차 실리콘층(110)으로부터 제거된다.In the lamination process of the first silicone layer 110 , after the first coating solution is applied on the base sheet 10 , it is spread evenly by the knife 50 , and when the base sheet 10 passes through the oven 60 in this state, , the primary coating solution is cured to form the primary silicone layer 110 . Meanwhile, when the silicone artificial leather 100 is used, the base sheet 10 is removed from the primary silicone layer 110 .

2차 실리콘층(120)의 적층 과정에서는 1차 실리콘층(110) 상에 2차 코팅액이 도포된 후 나이프(50)에 의해 고르게 펴지고, 이 상태로 기재 시트(10)가 오븐(60)을 통과하면, 2차 코팅액이 경화되어 2차 실리콘층(120)이 형성된다.In the lamination process of the secondary silicone layer 120 , the secondary coating solution is applied on the primary silicone layer 110 and then evenly spread by the knife 50 , and in this state, the substrate sheet 10 is heated in the oven 60 . When passed, the secondary coating solution is cured to form the secondary silicone layer 120 .

3차 실리콘층(130) 및 내피층(140)을 동시에 적층하는 과정에서는 2차 실리콘층(120) 상에 2차 코팅액이 도포된 후 나이프(50)에 의해 고르게 펴지고, 이후 내피층(140)을 구성할 직물(20)이 2차 코팅액 상에 합쳐지며, 이 상태로 기재 시트(10)가 오븐(60)을 통과하면, 2차 코팅액이 직물(20)을 고정시키면서 경화되어 3차 실리콘층(130) 및 내피층(140)이 형성된다.In the process of simultaneously laminating the tertiary silicone layer 130 and the endothelial layer 140 , the secondary coating solution is applied on the secondary silicone layer 120 and then evenly spread by the knife 50 , and then the endothelial layer 140 . The fabric 20 to constitute is merged on the secondary coating solution, and in this state, when the base sheet 10 passes through the oven 60, the secondary coating solution is cured while fixing the fabric 20 and the tertiary silicone layer 130 and the endothelial layer 140 are formed.

한편, 투광성 탄력 커버(100)는 자외선에 강한 특성을 갖는 실리콘을 기반으로 하면서도 탄력성, 색상 및 내광성을 갖고, 외부에 노출되는 외곽층인 1차 실리콘층(110)의 표면이 슬립성을 갖는다. On the other hand, the light-transmitting elastic cover 100 has elasticity, color and light resistance while being based on silicon having strong UV-resistant properties, and the surface of the primary silicone layer 110, which is an outer layer exposed to the outside, has slip properties.

따라서 실리콘 인조 피혁(100)은 폴리우레탄을 기반으로 하는 종래 기술과 달리 자외선 노출이 잦은 자동차용 내장재로 장기간 사용될 수 있고, 그 외, 탄력성으로 인해 자동차용 내장재로 사용하기가 매우 편리하며, 다양한 색상의 구현이 가능하여 고객의 색상 요구를 충족시킬 수 있고, 슬립성으로 인해 우수한 표면 질감을 가지며, 2차 실리콘층, 3차 실리콘층 및 내피층이 모두 색상을 가지므로 실리콘 인조 피혁의 색상이 확실하고 선명하게 구현되고, 3차 실리콘층과 내피층 간 결합에 접착제가 전혀 사용되지 않아 제조 비용 및 제조 공정의 면에 있어서 효율적이다. Therefore, the silicone artificial leather 100 can be used for a long time as an interior material for automobiles exposed to frequent ultraviolet rays, unlike the prior art based on polyurethane, and in addition, it is very convenient to use as an interior material for automobiles due to its elasticity, and various colors It is possible to realize the color requirements of customers, it has an excellent surface texture due to slip property, and the color of the silicone artificial leather is certain because the secondary silicone layer, the tertiary silicone layer, and the inner skin layer all have color. And it is clearly implemented, and since no adhesive is used for bonding between the tertiary silicone layer and the inner skin layer, it is efficient in terms of manufacturing cost and manufacturing process.

이상과 같이, 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술사상과 아래에 기재될 청구범위의 균등범위 내에서 다양하게 수정 및 변형될 수 있고, 상술한 실시예들이 다양하게 조합될 수 있음은 물론이다.As described above, although the present invention has been described with reference to limited embodiments and drawings, the present invention is not limited thereto, and the technical idea of the present invention and the following by those skilled in the art to which the present invention pertains. It goes without saying that various modifications and variations can be made within the equivalent scope of the claims to be described, and the above-described embodiments can be variously combined.

100 : 실리콘 인조 피혁 110 : 1차 실리콘층
120 : 2차 실리콘층 130 : 3차 실리콘층
140 : 내피층
10 : 기재 시트 20 : 직물
30 : 언와인딩롤 40 : 와인딩롤
50 : 나이프 60 : 오븐100: silicone artificial leather 110: primary silicone layer
120: secondary silicon layer 130: tertiary silicon layer
140: endothelial layer
10: base sheet 20: fabric
30: unwinding roll 40: winding roll
50: knife 60: oven

Claims (6)

실리콘 수지 및 상기 실리콘 수지의 경화를 촉진시키기 위한 촉매를 포함하는 1차 코팅액을 경화하여 형성한 1차 실리콘층;
상기 실리콘 수지, 상기 촉매, 상기 실리콘 수지의 상온 경화를 지연시키기 위한 지연제 및 유색 무기안료를 포함하는 2차 코팅액을 상기 1차 실리콘층 상에서 경화하여 형성한 2차 실리콘층;
상기 2차 코팅액을 상기 2차 실리콘층 상에서 경화하여 형성한 3차 실리콘층; 및
상기 3차 실리콘층 상에 적층된 유색 직물로서, 탄력성을 갖는 내피층;을 포함하고,
상기 실리콘 수지로는 상기 1차 내지 3차 실리콘층의 탄력성 및 표면 슬립성을 위해 가루 형태의 실리카와, 폴리디메틸실록산과, 경화제를 혼합한 것이 사용되는 실리콘 인조 피혁.a first silicone layer formed by curing a first coating solution containing a silicone resin and a catalyst for accelerating curing of the silicone resin;
a secondary silicone layer formed by curing a secondary coating solution including the silicone resin, the catalyst, a retarder for delaying room temperature curing of the silicone resin, and a colored inorganic pigment on the primary silicone layer;
a tertiary silicone layer formed by curing the secondary coating solution on the secondary silicone layer; and
A colored fabric laminated on the tertiary silicone layer, including an inner skin layer having elasticity,
As the silicone resin, a mixture of silica powder, polydimethylsiloxane, and a curing agent is used for elasticity and surface slip properties of the primary to tertiary silicone layer. 제1항에 있어서,
상기 촉매는 녹인 백금과 오가노폴리실록산을 혼합한 것인 실리콘 인조 피혁.According to claim 1,
The catalyst is a silicone artificial leather that is a mixture of melted platinum and organopolysiloxane. 제1항에 있어서,
상기 내피층을 구성하는 유색 직물은 상기 무기안료가 용해된 용제에 함침시킨 폴리에스터 재질의 원사 및 스판 재질의 원사를 직조하여 형성된 실리콘 인조 피혁.According to claim 1,
The colored fabric constituting the inner skin layer is a silicone artificial leather formed by weaving a polyester yarn and a spandex yarn impregnated in a solvent in which the inorganic pigment is dissolved. 제1항에 있어서,
상기 내피층의 적층은 상기 2차 실리콘층에 도포된 상기 2차 코팅액에 상기 직물이 합쳐진 상태에서 상기 2차 코팅액이 경화됨으로써 이루어지는 실리콘 인조 피혁.According to claim 1,
The lamination of the inner skin layer is made by curing the secondary coating solution in a state in which the fabric is combined with the secondary coating solution applied to the secondary silicone layer. 제1항에 있어서,
상기 1차 코팅액은 고분자 수지 필름 또는 종이 재질의 기재 시트에 도포된 후 경화되는 실리콘 인조 피혁.According to claim 1,
The first coating solution is a silicone artificial leather that is cured after being applied to a base sheet made of a polymer resin film or paper material. 제1항 내지 제5항 중 어느 한 항에 있어서,
상기 내피층은 가장 내측의 층이고 상기 1차 실리콘층은 사용자에게 직접 노출되는 가장 외측의 층인 실리콘 인조 피혁.
6. The method according to any one of claims 1 to 5,
The inner skin layer is the innermost layer, and the first silicone layer is the outermost layer directly exposed to the user.
KR1020200124129A 2020-09-24 2020-09-24 Silicone artificial laether KR102521018B1 (en)