KR20210125252A - Method for manufacturing granular confinement honeycomb reinforcement - Google Patents
Method for manufacturing granular confinement honeycomb reinforcement Download PDFInfo
- Publication number
- KR20210125252A KR20210125252A KR1020200042707A KR20200042707A KR20210125252A KR 20210125252 A KR20210125252 A KR 20210125252A KR 1020200042707 A KR1020200042707 A KR 1020200042707A KR 20200042707 A KR20200042707 A KR 20200042707A KR 20210125252 A KR20210125252 A KR 20210125252A
- Authority
- KR
- South Korea
- Prior art keywords
- honeycomb
- manufacturing
- web
- constrained
- fiber sheet
- Prior art date
Abstract
Description
본 발명은 토립자 구속 벌집형 보강재의 제조방법에 관한 것으로서 보다 상세하게는 플렉스블하고 중량이 가벼워 이송 및 사용이 용이하며 제작이 간편하고 시트의 두께조절이 용이한 토립자 구속 벌집형 보강재의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a particle-constrained honeycomb reinforcing material, and more particularly, to a method for manufacturing a particle-constrained honeycomb reinforcing material that is flexible and light in weight, which is easy to transport and use, is simple to manufacture, and is easy to control the thickness of a sheet. it's about
일반적으로 사면, 호안은 강우와 유수에 의하여 침식 및 붕괴가 발생되기 쉬우며 연약지반은 구조물의 하중보다 기초지반의 지지력이 작아서 변형을 일으키는 지반이다. 이러한 사면 및 호안 제방을 축조할 경우 사면침식 및 붕괴가 발생하지 않도록 사면보호용 보강재를 설치하여야 하며, 연약지반 위에 제방이나 도로를 시공할 경우 지반의 지지력을 증대시키고 지반의 침하가 일어나지 않도록 보강구조물을 설치하여야 한다.In general, slopes and shorelines are prone to erosion and collapse due to rainfall and runoff, and soft ground is the ground that causes deformation because the bearing capacity of the base ground is smaller than the load of the structure. When constructing such slopes and shore embankments, reinforcing materials for slope protection must be installed to prevent slope erosion and collapse. should be installed
이러한 사면보호용 보강재의 종래 구조는 고밀도 폴리에틸렌재로 이루어져 소정의 길이로 형성된 띠 형상의 시트가 겹치어져 이루어지며 일부분에는 초음파 융착한 후 당기면 세포형의 망으로 형성한 토립자 구속 벌집형 보강재이다.The conventional structure of such a slope protection reinforcing material is made of a high-density polyethylene material and formed by overlapping band-shaped sheets formed with a predetermined length, and is a honeycomb-type reinforcing material constrained by soil particles formed into a cellular network when a portion is ultrasonically welded and pulled.
한편 부직포(Non-woven fabric)란 폴리프로필렌 또는 폴리에스터 등으로 된 미세사를 단독 또는 혼합한 상태로 압착처리하여 섬유재로 제조한 후 이를 열융착 또는 니들펀칭(Needle punching) 등의 방법으로 다수의 통공을 형성시킨 기능성 섬유를 말하는 것으로, 일반적으로 부직포가 갖는 투수기능을 이용하여 지반공사 등과 같은 대규모 토목공사시 토사 등과 같은 수분함유 고형물의 배수를 위한 필터링 등의 용도로서 널리 이용되고 있다.On the other hand, non-woven fabric is made of fiber material by compressing fine yarn made of polypropylene or polyester alone or in a mixed state, and then using a plurality of methods such as thermal fusion or needle punching. It refers to a functional fiber that has a through hole in it. Generally, it is widely used as filtering for drainage of water-containing solids such as earth and sand during large-scale civil works such as ground work using the water permeability function of nonwoven fabrics.
그러나 상기의 부직포는 구조적 특성상 일반 직물섬유와 비교하여 인장강도 등의 물리적 특성이 매우 약할 뿐만 아니라, 신율이 높아서 장기간의 공사 기간을 요하는 대규모의 공사시에는 토사 등과 같은 수분함유 고형물의 자체 하중에 의한 지속적인 응력 인가로 인하여 부직포가 쉽게 이완되어 변형되고, 아울러 부직포에 구성된 통수공의 구경이 확대됨으로서 효과적인 필터링이 이루어지지 못하게 되어 부직포의 기본 기능인 배수기능 등의 수리적 특성이 급격하게 저하되는 현상이 발생하였으며, 이와 같은 부직포의 수리적 특성 저하현상으로 인하여 공사시 설치한 부직포 구조물을 경우에 따라 다수회에 걸쳐 재설치하여야 하는 번거로움이 발생하였을 뿐만 아니라 공사 기간이 지연되고 공사 비용 또한 크게 증가함과 아울러 궁극적으로는 전반적인 공사품질을 크게 저하 시키는 문제점이 있었다.However, the nonwoven fabric has structural characteristics, compared to general textile fibers, in terms of physical properties such as tensile strength, and high elongation. The nonwoven fabric is easily relaxed and deformed due to continuous stress application by the Due to the deterioration of the hydraulic properties of the nonwoven fabric, the inconvenience of having to reinstall the nonwoven structure installed during construction several times in some cases occurred, as well as delaying the construction period, greatly increasing the construction cost, and ultimately As a result, there was a problem that significantly lowered the overall construction quality.
상기한 원재료의 문제로 인하여 첨부도면 도 1은 종래 토립자 구속 벌집형 보강재를 생산 시 별도의 천공기를 이용하여 통공(200)을 형성시키거나 또는 토립자 구속 벌집형 보강재를 생산 후 현장에서 후속공정 작업자가 시트(100)에 투수계수를 높이기 위하여 작업자가 펀칭기를 이용하여 통공(200)을 형성시키는 구조의 토립자 구속 벌집형 보강재를 사용하였다.Due to the problem of the above-mentioned raw materials, the attached drawing FIG. 1 shows that the
이와 같이 종래의 연약지반 보강재는 투수계수가 낮고, 채움재와의 마찰력이 낮으며, 생산시 고가의 설비가 필요하며 제조단가가 높고 뿌리 활착이 용이하지 않으며, 압축하중 시 시트가 변형이 일어나 지반이 변형되는 문제점이 있다.As such, the conventional soft ground reinforcing material has a low water permeability coefficient, low frictional force with the filling material, requires expensive equipment for production, has a high manufacturing cost and is not easy to establish roots, and the sheet is deformed under compressive load, causing the ground to deteriorate. There is a problem with transformation.
상기와 같은 종래 문제점을 감안하여 대한민국 특허등록 제834784호 "토립자 구속 벌집형 보강재"가 제안된 바 있다. 상기 대한민국 특허등록 제834784호는 첨부도면 도 2에 도시된 바와 같이 가로보강사와 세로보강사가 교차하면서 일정크기의 공극을 갖는 망상의 시트를 형성하고 이 시트를 폭 방향으로 일정간격 융착 연결 후 일측 방향으로 당기면 다수의 벌집형태의 셀망부를 형성하여 이루어진 구조이다.In consideration of the conventional problems as described above, Korean Patent Registration No. 834784, "reinforcing particle restraint honeycomb type" has been proposed. The Republic of Korea Patent Registration No. 834784, as shown in the accompanying drawings, forms a mesh sheet having a certain size of voids while crossing the horizontal reinforcement and the vertical reinforcement, and after fusion splicing the sheet at a predetermined interval in the width direction, one direction It is a structure made by forming a plurality of honeycomb-shaped cell networks when pulled.
상기한 종래 "토립자 구속 벌집형 보강재"는 가로보강사와 세로보강사가 일정한 두께와 강도를 갖고 있어 롤 형태로 권취가 불가능하고 전체 중량이 무거우며 폴리에틸렌재로 이루어진 가로보강사와 세로보강사로 이루어진 셀망부가 딱딱하여 파손되는 경우도 있으며 이에 따라 제품 자체가 플렉시블하지 못한 문제점이 있다.The above-mentioned conventional "grain-constrained honeycomb reinforcing material" has a horizontal reinforcing yarn and a vertical reinforcing yarn having a certain thickness and strength, so it is impossible to wind it in a roll form, and the overall weight is heavy. There is a case where it is hard and damaged, and thus there is a problem that the product itself is not flexible.
또한 제품의 전체중량이 무거워 이송 및 설치가 용이하지 못하고 가로보강사와 세로보강사로 이루어진 셀망부의 끝단이 날카로워 작업자의 신체가 긁혀 상처가 발생하는 등의 문제점도 있다.In addition, since the total weight of the product is heavy, it is not easy to transport and install, and the end of the cell mesh part made of horizontal reinforcement and vertical reinforcement is sharp, so there is a problem that the body of the operator is scratched and wounds occur.
상기한 종래 문제점을 감안하여 안출한 본 발명의 목적은 플렉시블하여 롤 형태로 권취가 가능하고 전체 중량이 가벼워 이동 및 설치가 용이하며 파손의 위험이 적으며 작업자의 신체 훼손이 방지되며 제작이 간편하고 시트의 두께조절이 용이함 및 인장강도 향상 및 배수성능 향상 등의 이점이 있는 토립자 구속 벌집형 보강재의 제조방법을 제공하는데 있다.The object of the present invention, which was devised in view of the above-mentioned problems of the prior art, is that it is flexible and can be wound in a roll form, and the overall weight is light, so it is easy to move and install, the risk of breakage is small, damage to the body of the operator is prevented, and the production is simple. An object of the present invention is to provide a method for manufacturing a honeycomb reinforcing material constrained by soil particles, which has advantages such as ease of sheet thickness control, improvement of tensile strength, and improvement of drainage performance.
이러한 본 발명은 토립자 구속 벌집형 보강재의 제조방법에 있어서, 단섬유를 개섬하고 적층하여 웹을 형성시키는 웹성형공정과; 상기 웹성형공정에 의해 형성된 웹을 가압하여 일정한 두께로 형성시키는 두께 및 밀도를 조절하는 물성조절공정과; 상기 물성조절공정에 의해 생성된 단섬유적층체를 니들펀칭하는 펀칭공정과; 상기 펀칭공정 후 인장강도를 향상시키기 위하여 표면을 가열가압하는 열처리공정과; 상기 열처리공정에 의해 생성된 띠형의 단섬유 시트를 저주파융착기에 공급하는 준비공정과; 상기 준비공정에 의해 저주파융착기에 단섬유 시트가 배열되면 저주파융착기를 작동시켜 띠형의 단섬유 시트를 일정한 간격으로 전·후, 좌·우 연속되게 접합시키는 접합공정에 의해 제조되는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.The present invention provides a method for manufacturing a particle-constrained honeycomb reinforcing material, comprising: a web forming process of opening and laminating short fibers to form a web; a physical property control process of controlling the thickness and density of pressing the web formed by the web forming process to form a constant thickness; a punching process of needle-punching the single fiber laminate produced by the physical property control process; a heat treatment process of heating and pressing the surface to improve tensile strength after the punching process; a preparation step of supplying the band-shaped short fiber sheet produced by the heat treatment process to a low frequency welding machine; When the short fiber sheets are arranged in the low frequency fusing machine by the above preparation process, the low frequency fusing machine is operated to bond the strip-shaped short fiber sheets forward, backward, left and right at regular intervals, characterized in that it is manufactured by a bonding process. It is achieved by a method for manufacturing a constrained honeycomb reinforcing material.
상기 본 발명의 다른 실시예의 제조방법으로는 토립자 구속 벌집형 보강재의 제조방법에 있어서,In the manufacturing method of another embodiment of the present invention, in the manufacturing method of the particle-constrained honeycomb reinforcing material,
단섬유를 개섬하고 적층하여 웹을 형성시키는 웹성형공정과; 상기 웹성형공정에 의해 형성된 단섬유적층체를 니들펀칭하는 펀칭공정과; 상기 펀칭공정 후 인장강도를 향상시키기 위하여 표면을 가열가압하는 열처리공정과; 상기 열처리공정에 의해 생성된 띠형의 단섬유 시트를 저주파융착기에 공급하는 준비공정과; 상기 준비공정에 의해 저주파융착기에 단섬유 시트가 배열되면 저주파융착기를 작동시켜 띠형의 단섬유 시트를 일정한 간격으로 전·후, 좌·우 연속되게 접합시키는 접합공정에 의해 제조되는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.A web forming process of opening and laminating short fibers to form a web; a punching process of needle punching the short fiber laminate formed by the web forming process; a heat treatment process of heating and pressing the surface to improve tensile strength after the punching process; a preparation step of supplying the band-shaped short fiber sheet produced by the heat treatment process to a low frequency welding machine; When the short fiber sheets are arranged in the low frequency fusing machine by the above preparation process, the low frequency fusing machine is operated to bond the strip-shaped short fiber sheets forward, backward, left and right at regular intervals, characterized in that it is manufactured by a bonding process. It is achieved by a method for manufacturing a constrained honeycomb reinforcing material.
상기 접합공정은 초음파 접합장치가 일정한 간격으로 전후좌우 연속 반복하여 설치되되 홀수열 또는 짝수열은 인접하는 행열의 초음파 접합장치의 사이에 초음파 접합장치가 위치되도록 설치하여 띠형의 단섬유 시트를 초음파 접합장치가 다수개 설치되어 한 행열을 형성하는 초음파 접합장치에 2장의 시트를 통과시키되 띠형의 단섬유 시트가 짝수열-홀수열-짝수열 또는 홀수열-짝수열-홀수열이 반복되게 경유하도록 하여 접합하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.In the bonding process, the ultrasonic bonding device is installed repeatedly, back and forth, left and right, at regular intervals, and in odd or even rows, the ultrasonic bonding device is installed so that the ultrasonic bonding device is positioned between the ultrasonic bonding devices in adjacent rows, thereby ultrasonically bonding the band-shaped single fiber sheet. Two sheets are passed through an ultrasonic bonding device in which a plurality of devices are installed to form a row, and the strip-shaped single-fiber sheet is repeatedly passed through even-numbered-odd-numbered-even-numbered or odd-numbered-even-numbered-odd columns. It is achieved by a method for manufacturing a particle-constrained honeycomb reinforcing material, characterized in that bonding.
상기 접합공정은 초음파 접합장치가 일정한 간격으로 설치되어 단섬유 시트에 접합부를 형성하여 한 줄 형태의 셀단위 보강재를 형성시키고 상기 접합부와 접합부 사이에 초음파 접합장치가 위치하도록 초음파 접합장치 또는 셀단위 보강재를 이동시켜 공급되는 새로운 단섬유 시트를 접합시키고 다시 셀단위 보강재를 원위치하여 공급되는 단섬유 시트를 접합시키는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.In the bonding process, the ultrasonic bonding device is installed at regular intervals to form a bonding portion on the short fiber sheet to form a cell unit reinforcement in the form of a single line, and an ultrasonic bonding device or a cell unit reinforcement material so that the ultrasonic bonding device is positioned between the bonding portion and the bonding portion It is achieved by a method of manufacturing a honeycomb-type reinforcing material constrained by particles, characterized in that the new short-fiber sheet is moved by moving the supply, and the single-fiber sheet supplied by moving the reinforcing material in the cell unit to its original position is bonded again.
상기 열처리공정 후 펀칭공정을 실시하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.It is achieved by a method of manufacturing a particle-constrained honeycomb reinforcing material, characterized in that a punching process is performed after the heat treatment process.
상기 접합공정 후 최외각의 시트에 + 형의 절취선을 형성시켜 조각편이 일체로 형성되며 상기 + 형의 절취선에 의해 형성된 조각편을 외부 쪽으로 절첩하면 통공을 형성하는 절취선을 형성하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.After the bonding process, a +-type perforation line is formed on the outermost sheet to form a piece piece integrally, and when the piece piece formed by the + type perforation line is folded toward the outside, a perforation line forming a through hole is formed. This is achieved by a method for manufacturing a honeycomb reinforcing material.
상기 웹성형공정 후 적층된 웹에 인장력을 보강하기 위한 보강사가 설치되는 보강사설치공정을 더 포함하여 이루어진 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.It is achieved by the method for manufacturing a reinforcing particle constrained honeycomb reinforcing material, characterized in that it further comprises a reinforcing yarn installation step in which reinforcing yarns for reinforcing tensile force are installed in the laminated web after the web forming step.
상기 단섬유 시트는 한 장을 반으로 절첩 또는 2장이 적층되어 인장력을 향상시킨 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법에 의하여 달성된다.The short fiber sheet is achieved by a method of manufacturing a honeycomb reinforcing material constraining grains, characterized in that one sheet is folded in half or two sheets are laminated to improve the tensile force.
상기한 제조방법에 의하여 제조된 토자 구속 벌집형 보강재는 단섬유로 이루어지며 니들펀칭되고 표면이 열처리되어 투수성과 인장력이 향상된 띠형의 단섬유 시트를 일정한 간격으로 좌우, 전후 연속반속되게 저주파융착하여 이루어진 것을 특징으로 하는 토립자 구속 벌집형 보강재에 의하여 달성된다.The earthen constraint honeycomb reinforcing material manufactured by the above manufacturing method is made of short fibers, needle punched, and heat-treated on the surface to form a band-shaped single fiber sheet with improved water permeability and tensile strength at regular intervals, left and right, front and rear, and low-frequency fusion at regular intervals. It is achieved by the particle restraint honeycomb reinforcement, characterized in that.
상기 단섬유 시트에 + 형의 절취선을 형성시켜 조각편이 일체로 형성되며 상기 + 형의 절취선에 의해 형성된 조각편을 내부 또는 외부 쪽으로 절첩하면 통공을 형성하는 것을 특징으로 하는 토립자 구속 벌집형 보강재.The fragments are integrally formed by forming a +-type perforation line on the short fiber sheet, and when the fragment formed by the +-type perforation line is folded inside or outside, a through hole is formed.
또한 상기 단섬유 시트에 봉재 가공하여 고정사가 더 설치되어 이루어진 것을 특징으로 하는 토립자 구속 벌집형 보강재에 의하여 달성된다.In addition, it is achieved by a honeycomb-type reinforcing material constraining grains, characterized in that the fixed yarn is further installed by processing the bar on the short fiber sheet.
이와 같은 본 발명은 플렉시블하여 절첩이 용이하여 취급이 쉽고 또한 롤 형태로 권취가 가능하고 전체 중량이 가벼워 이동 및 설치가 용이하며 파손의 위험이 적으며 작업자의 신체 훼손이 방지되며 제작이 간편하고 시트의 두께조절이 용이한 등의 효과가 있는 매우 유용한 발명이다.As described above, the present invention is flexible and easy to fold, so it is easy to handle, and it can be wound in a roll form, and the overall weight is light, so it is easy to move and install, the risk of breakage is small, damage to the body of the worker is prevented, manufacturing is simple, and the sheet It is a very useful invention that has effects such as easy thickness control.
도 1 및 도 2는 종래 토립자 구속 벌집형 보강재의 구조를 보여주는 사시도.
도 3은 본 발명의 기술이 적용된 토립자 구속 벌집형 보강재의 제조방법을 보여주는 제조공정도.
도 4는 본 발명의 기술이 적용된 토립자 구속 벌집형 보강재의 구조를 보여주는 사시도.
도 5는 본 발명의 다른 제조방법을 보여주는 제조공정도.
도 6 내지 도 7은 본 발명의 기술적 요지인 접합공정의 접합방법을 보여주는 예시도.
도 8은 본 발명의 또 다른 토립자 구속 벌집형 보강재의 제조방법을 보여주는 제조공정도.
도 9는 도 8의 제조방법에 의해 제조된 토립자 구속 벌집형 보강재의 구조를 보여주는 사시도.
도 10은 본 발명의 실시예인 웹에 보강사를 설치하는 모습을 보여주는 사진.
도 11a 내지 도 11b는 본 발명의 기술의 요부인 단섬유 시트의 구조를 보여주는 단면도.
도 12는 시트에 고정사를 봉재하여 설치한 구조를 보여주는 단면도.1 and 2 are perspective views showing the structure of a conventional soil particle restraint honeycomb reinforcement.
Figure 3 is a manufacturing process diagram showing a manufacturing method of the particle-constrained honeycomb reinforcing material to which the technology of the present invention is applied.
Figure 4 is a perspective view showing the structure of the particle restraint honeycomb reinforcement to which the technology of the present invention is applied.
5 is a manufacturing process diagram showing another manufacturing method of the present invention.
6 to 7 are exemplary views showing a bonding method of the bonding process, which is the technical gist of the present invention.
8 is a manufacturing process diagram showing a manufacturing method of another particle-constrained honeycomb reinforcing material of the present invention.
9 is a perspective view showing the structure of the particle-constrained honeycomb reinforcing material manufactured by the manufacturing method of FIG.
10 is a photograph showing a state of installing a reinforcing yarn on the web, which is an embodiment of the present invention.
11A to 11B are cross-sectional views showing the structure of a short fiber sheet, which is an essential part of the technology of the present invention.
12 is a cross-sectional view showing a structure installed by sealing a fixing thread to a sheet;
이하 본 발명의 바람직한 실시예를 첨부된 도면에 의거하여 상세히 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail based on the accompanying drawings.
첨부도면 도 3은 본 발명의 기술이 적용된 토립자 구속 벌집형 보강재의 제조방법을 보여주는 제조공정도이고, 도 4는 본 발명의 기술이 적용된 토립자 구속 벌집형 보강재의 구조를 보여주는 사시도로써 이에 따른 본 발명은 단섬유를 개섬하고 적층하여 웹을 형성시키는 웹성형공정(S100)과, 상기 웹성형공정(S100)에 의해 형성된 웹을 가압하여 일정한 두께로 형성시키는 두께 및 밀도를 조절하는 물성조절공정(S200)과, 상기 물성조절공정(S200)에 의해 생성된 단섬유적층체를 니들펀칭하는 펀칭공정(S300)과, 상기 펀칭공정(S300) 후 인장강도를 향상시키기 위하여 표면을 가열가압하는 열처리공정(S400)과, 상기 열처리공정(S400)에 의해 생성된 띠형의 단섬유 시트(10)를 저주파융착기에 거치하는 준비공정(S500)과, 상기 준비공정(S500)에 의해 저주파융착기에 단섬유 시트(10)가 배열되면 저주파융착기를 작동시켜 띠형의 단섬유 시트(10)를 일정한 간격으로 전·후, 좌·우 연속되게 접합시키는 접합공정(S600)에 의한 제조 순으로 제조되는 것에 특징이 있다.3 is a manufacturing process diagram showing a manufacturing method of a particle-constrained honeycomb reinforcement to which the technology of the present invention is applied, and FIG. 4 is a perspective view showing the structure of a particle-constrained honeycomb reinforcement to which the technology of the present invention is applied. A web forming process (S100) of opening and laminating short fibers to form a web, and a physical property control process (S200) of controlling the thickness and density of pressing the web formed by the web forming process (S100) to form a constant thickness (S200) And, a punching process (S300) of needle punching the short fiber laminate produced by the physical property control process (S200), and a heat treatment process (S400) of heating and pressing the surface to improve tensile strength after the punching process (S300) ) and a preparation process (S500) of mounting the band-shaped
상기 웹성형공정(S100)은 융점이 서로 다른 저융점 단섬유와 고융점 단섬유를 개섬수단을 이용하여 새털 같은 원사로 개섬하고 개섬된 섬유를 일정한 두께와 폭을 갖는 카딩수단을 이용하여 웹을 형성한다.In the web forming process (S100), low-melting short fibers and high-melting short fibers having different melting points are opened into yarn like feathers using an opening means, and the opened fibers are opened using carding means having a certain thickness and width to form a web. to form
상기 카딩수단에 의하여 형성된 웹을 이송벨트 상에 골고루 펼쳐지게 깔고 일정한 두께를 형성하도록 웹적층수단을 이용하여 웹을 수회 적층하여 수평상태의 조직을 갖는 웹을 형성시킨다. The web formed by the carding means is spread evenly on the conveying belt, and the web is laminated several times using a web laminating means to form a constant thickness to form a web having a horizontal structure.
상기 웹성형공정(S100)에 의해 일정한 두께로 웹 형성이 완료되면 웹을 히팅장치가 구비되어 있는 가압수단을 이용하여 웹을 가압하여 일정한 두께 및 밀도를 조절하는 물성조절공정(S200)을 수행한다.When the web is formed to a constant thickness by the web forming process (S100), the web is pressurized using a pressing means equipped with a heating device to adjust a constant thickness and density by pressing the web to perform a physical property control process (S200). .
상기 물성조절공정(S200)은 단섬유로 이루어진 웹을 수회 적층하여 예컨대 적층 두께를 100mm 적층하였다면 상기 적층된 100mm의 단섬유 적층체를 가압하여 형성하고자 하는 두께 즉 1mm 또는 30mm 등으로 제조하는 것이다.In the physical property control process (S200), if the web made of short fibers is laminated several times and, for example, the laminate thickness is 100 mm, the thickness to be formed by pressing the laminated short fiber laminate of 100 mm, that is, 1 mm or 30 mm, etc. is manufactured.
상기 웹 적층물을 가압하여 두께를 조절하는 이유는 밀도도 자연적으로 조절되기 때문이며 상기 밀도는 투수성에 미치는 영향이 크기 때문이다. 따라서 상기 물성조절공정(S200)에 의해 생성된 단섬유적층체를 니들펀칭하는 펀칭공정(S300)을 수행한다. 상기 펀칭공정(S300)은 단섬유적층체를 결속시켜 인장력을 향상시키는 효과도 있으나 투수성을 향상시키는 효과가 있다.The reason for controlling the thickness by pressing the web laminate is because the density is also naturally controlled, and the density has a large effect on water permeability. Therefore, a punching process (S300) of needle-punching the short fiber laminate produced by the physical property control process (S200) is performed. The punching process (S300) has the effect of improving the tensile force by binding the short fiber laminate, but also has the effect of improving the water permeability.
한편 상기 펀칭공정(S300) 후 인장강도를 향상시키기 위하여 표면을 가열 가압하는 열처리공정(S400)을 수행한다. 이때 상기 열처리공정(S400)의 방법으로는 60~120℃의 범위의 히팅열을 갖는 로울러 사이를 통과되면서 수행하며, 열처리온도가 60℃ 이하일 경우 열처리 효과가 일어나지 않아 인장강도가 향상되지 않으며, 더불어 단섬유 적층체의 표면 정리 효과가 일어나지 않는다. Meanwhile, after the punching process (S300), a heat treatment process (S400) of heating and pressing the surface is performed in order to improve the tensile strength. At this time, as the method of the heat treatment process (S400), it is performed while passing between the rollers having a heating heat in the range of 60 to 120 ° C. When the heat treatment temperature is 60 ° C or less, the heat treatment effect does not occur and the tensile strength is not improved, The surface cleaning effect of the short fiber laminate does not occur.
상기 열처리온도가 120℃ 이상일 경우 단섬유 적층체를 형성하는 단섬유가 용융되어 투수성이 떨어지는 문제가 있다. 본 발명에서는 상기 열처리공정(S400) 전에 펀칭공정(S300)을 실시하는 것으로 설명하고 있으나 작업의 흐름상 펀칭공정(S300)을 열처리공정(S400) 후에 실시할 수도 있다. When the heat treatment temperature is 120° C. or more, the short fibers forming the short fiber laminate are melted and there is a problem in that water permeability is deteriorated. Although the present invention has been described as performing the punching process (S300) before the heat treatment process (S400), the punching process (S300) may be performed after the heat treatment process (S400) in the flow of work.
본 발명에서는 물성조절공정(S200)과 열처리공정(S400)을 각각 구분하고 있으나 첨부도면 도 5에 도시된 바와 같이 상기 물성조절공정(S200)을 생략하고 열처리공정(S400) 만을 수행할 수도 있다. 상기 열처리공정(S400)은 반드시 수행하여야 한다. 그 이유는 인장력을 향상시키기 위함이며 열처리공정(S400)을 하지 않을 때에는 인장력이 현저히 떨어지기 때문이다.In the present invention, although the physical property control process (S200) and the heat treatment process (S400) are respectively separated, the physical property control process (S200) may be omitted and only the heat treatment process (S400) may be performed as shown in FIG. 5 . The heat treatment process (S400) must be performed. The reason is to improve the tensile force, and when the heat treatment process (S400) is not performed, the tensile force is significantly reduced.
상기와 같이 열처리공정(S400)이 완료되면 일정한 폭을 형성하도록 절단을 하여 띠 형의 시트(10)를 형성시킨다. 상기 시트 준비가 완료되면 상기 띠형의 단섬유 시트(10)를 저주파융착기에 공급하는 준비공정(S500)을 수행 후 상기 준비공정(S500)에 의해 저주파융착기에 단섬유 시트가 배열되면 저주파융착기를 작동시켜 띠형의 단섬유 시트를 일정한 간격으로 전·후, 좌·우 연속되게 접합시키는 접합공정(S600)을 수행하여 토립자 구속 벌집형 보강재를 제조한다.When the heat treatment process (S400) is completed as described above, the band-shaped
상기 접합공정(S600)을 수행하여 접합된 시트(10)는 접합부(20)를 형성하며 접합부(20)와 접합부(20) 사이에 토립자 구속할 수 있는 공간(30)이 형성되어 이루어진 구조이며 상기 접합부(20)와 공간(30)이 전후, 좌우 연속반복되게 형성된 구조이다.The
상기 접합공정(S600)의 방법으로는 첨부도면 도 6에 도시된 바와 같이 고정자와 유동자 2개가 1조로 이루어진 초음파 접합장치(T)가 일정한 간격으로 전후좌우 연속 반복하여 설치되되 홀수열 또는 짝수열은 인접하는 행열의 초음파 접합장치(T)의 사이에 초음파 접합장치(T)가 위치되도록 설치하여 띠형의 단섬유 시트(10)를 초음파 접합장치가 다수개 설치되어 한 행열을 형성하는 초음파 접합장치(T)에 2장의 시트(10)를 통과시키되 띠형의 단섬유 시트(10)가 짝수열-홀수열-짝수열 또는 홀수열-짝수열-홀수열이 반복되게 경유하도록 하여 전체를 한 번에 접합한다.As a method of the bonding process (S600), as shown in the accompanying drawings, an ultrasonic bonding device (T) consisting of two stators and a mover in one set is repeatedly installed back and forth, left and right, at regular intervals, in odd or even rows. Ultrasonic bonding apparatus for forming a single row by installing a plurality of ultrasonic bonding apparatuses for a band-shaped
본 발명의 다른 접합공정(S600)은 첨부도면 도 7에 도시된 바와 같이 초음파 접합장치(T)가 일정한 간격으로 설치되어 단섬유 시트(10)에 접합부(20)를 형성하여 한 줄 형태의 셀단위 보강재를 형성시키고 상기 접합부(20)와 접합부(20) 사이에 초음파 접합장치가 위치하도록 초음파 접합장치 또는 셀단위 보강재를 이동시켜 공급되는 새로운 단섬유 시트(10)를 접합시키고 다시 셀단위 보강재를 원위치하여 공급되는 단섬유 시트(10)를 접합시켜 제조한다.In another bonding process (S600) of the present invention, as shown in the accompanying drawings, the ultrasonic bonding apparatus (T) is installed at regular intervals to form the
첨부도면 도 8은 본 발명의 또 다른 토립자 구속 벌집형 보강재의 제조방법을 보여주는 제조공정도이며 도 9는 도 8의 제조방법에 의해 제조된 토립자 구속 벌집형 보강재의 구조를 보여주는 사시도로써 열처리공정(S400) 후 펀칭공정(S700)을 수행하여 토립자 구속 벌집형 보강재를 제조할 수 있다. 8 is a manufacturing process diagram showing another method of manufacturing the particle-constrained honeycomb reinforcement according to the present invention, and FIG. 9 is a perspective view showing the structure of the particle-constrained honeycomb reinforcement manufactured by the manufacturing method of FIG. ) and then a punching process (S700) may be performed to manufacture the particle-constrained honeycomb reinforcing material.
상기 펀칭공정(S700)은 펀칭기를 이용하여 시트(10)에 + 형의 절취선(50)을 형성시켜 조각편(51)이 일체로 형성되며 상기 + 형의 절취선(50)에 의해 형성된 조각편(51)을 내부 또는 외부 쪽으로 절첩하면 통공이 만들어지는 절취선을 형성하는 방법이다. 상기 조각편(51)을 내부 또는 외부 쪽으로 절첩하면 조각편(51)은 고정력을 향상시키는 이점을 갖게 된다.In the punching process (S700), a +-
상기 본 발명에 있어서 인장력을 향상시키는 방법으로는 전자에서 열처리공정을 수행하는 것으로 설명하고 있으나 첨부도면 도 10에 도시된 바와 같이 형성된 웹을 이동시키면서 웹의 일면에 일정 간격으로 보강사를 공급하는 보강사공급단계(S800)을 수행한다. 상기 보강사는 길이방향으로 설치되며 보강사의 종류로는 PE사, PP사, 유리섬유사, 탄소섬유사 중 어느 하나를 선택하여 사용할 수 있다.In the present invention, the method for improving the tensile force is described as performing a heat treatment process in the former, but as shown in the accompanying drawings, a beam is supplied with reinforcing yarn at regular intervals on one side of the web while moving the formed web. Instructor supply step (S800) is performed. The reinforcing yarn is installed in the longitudinal direction, and as a kind of reinforcing yarn, any one of PE yarn, PP yarn, glass fiber yarn, and carbon fiber yarn can be selected and used.
또한 상기 본 발명에 있어서 인장력을 향상시키는 방법으로는 첨부도면 도 11a 및 도 11b에 도시된 바와 같이 시트(10)를 넓게 형성시키고 반을 접어 2중으로 형성시키거나 또는 2장의 시트를 겹쳐지게 하여 사영할 수 있으며 이때 상기 시트에 상기 단섬유 시트에 있어서, 첨부도면 도 12에 도시된 바와 같이 봉재를 하여 고정사(70)를 형성시켜 투수성 향상과 인장력을 향상을 얻을 수 있다.In addition, as a method of improving the tensile force in the present invention, as shown in FIGS. 11a and 11b of the accompanying drawings, the
상기 고정사(70)는 인장력 향상과 공간 내측에 위치한 물을 외부로 배출시 수분이 흘러가는 수로 역할을 한다. 상기 본 발명에 있어서 인장력을 향상시키는 또 다른 방법으로는 상기 웹성형공정 후 적층된 웹에 인장력을 보강하기 위한 일표면에 접착 필름 또는 접착용 파우더를 도포하여 사용할 수도 있다.The fixing
이와 같은 본 발명은 플렉시블하여 절첩이 용이하여 취급이 쉽고 또한 롤 형태로 권취가 가능하고 전체 중량이 가벼워 이동 및 설치가 용이하며 파손의 위험이 적으며 작업자의 신체 훼손이 방지되며 제작이 간편하고 시트의 두께조절이 용이한 등의 효과가 있는 매우 유용한 발명이다.As described above, the present invention is flexible and easy to fold, so it is easy to handle, and it can be wound in a roll form, and the overall weight is light, so it is easy to move and install, the risk of breakage is small, damage to the body of the worker is prevented, manufacturing is simple, and the sheet It is a very useful invention that has effects such as easy thickness control.
10 : 시트
20 : 접합부
30 : 공간
50 : 절취선
51 : 조각편
70 : 고정사
S100 : 웹성형공정
S200 : 물성조절공정
S300 : 펀칭공정
S400 : 열처리공정
S500 : 준비공정
S600 : 접합공정
S700 : 펀칭공정
S800 : 보강사공급단계10: sheet 20: joint
30: space 50: perforated line
51: fragment 70: fixed yarn
S100: web forming process S200: property control process
S300: Punching process S400: Heat treatment process
S500: preparation process S600: bonding process
S700: Punching process S800: Reinforcing yarn supply stage
Claims (13)
단섬유를 개섬하고 적층하여 웹을 형성시키는 웹성형공정과;
상기 웹성형공정에 의해 형성된 웹을 가압하여 일정한 두께와 밀도를 조절하는 물성조절공정과;
상기 물성조절공정에 의해 생성된 단섬유적층체를 니들펀칭하는 펀칭공정과;
상기 펀칭공정 후 인장강도를 향상시키기 위하여 표면을 가열가압하는 열처리공정과;
상기 열처리공정에 의해 생성된 띠형의 단섬유 시트를 저주파융착기에 공급하는 준비공정과;
상기 준비공정에 의해 저주파융착기에 단섬유 시트가 배열되면 저주파융착기를 작동시켜 띠형의 단섬유 시트를 일정한 간격으로 전·후, 좌·우 연속되게 접합시키는 접합공정에 의해 제조되는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
In the manufacturing method of the particle-constrained honeycomb reinforcing material,
A web forming process of opening and laminating short fibers to form a web;
a physical property control process of controlling a certain thickness and density by pressing the web formed by the web forming process;
a punching process of needle-punching the single fiber laminate produced by the physical property control process;
a heat treatment process of heating and pressing the surface to improve tensile strength after the punching process;
a preparation step of supplying the band-shaped short fiber sheet produced by the heat treatment process to a low frequency welding machine;
When the short fiber sheets are arranged in the low frequency fusing machine by the preparation process, the low frequency fusing machine is operated to bond the strip-shaped short fiber sheets forward, backward, left and right at regular intervals, characterized in that they are manufactured by a bonding process A method for manufacturing a constrained honeycomb reinforcement.
단섬유를 개섬하고 적층하여 웹을 형성시키는 웹성형공정과;
상기 웹성형공정에 의해 형성된 단섬유적층체를 니들펀칭하는 펀칭공정과;
상기 펀칭공정 후 인장강도를 향상시키기 위하여 표면을 가열가압하는 열처리공정과;
상기 열처리공정에 의해 생성된 띠형의 단섬유 시트를 저주파융착기에 거치하는 준비공정과;
상기 준비공정에 의해 저주파융착기에 단섬유 시트가 배열되면 저주파융착기를 작동시켜 띠형의 단섬유 시트를 일정한 간격으로 전·후, 좌·우 연속되게 접합시키는 접합공정에 의해 제조되는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
In the manufacturing method of the particle-constrained honeycomb reinforcing material,
A web forming process of opening and laminating short fibers to form a web;
a punching process of needle punching the short fiber laminate formed by the web forming process;
a heat treatment process of heating and pressing the surface to improve tensile strength after the punching process;
a preparation step of mounting the band-shaped short fiber sheet produced by the heat treatment process on a low-frequency welding machine;
When the short fiber sheets are arranged in the low frequency fusing machine by the above preparation process, the low frequency fusing machine is operated to bond the strip-shaped short fiber sheets forward, backward, left and right at regular intervals, characterized in that it is manufactured by a bonding process. A method for manufacturing a constrained honeycomb reinforcement.
상기 접합공정은 초음파 접합장치가 일정한 간격으로 전후좌우 연속 반복하여 설치되되 홀수열 또는 짝수열은 인접하는 행열의 초음파 접합장치의 사이에 초음파 접합장치가 위치되도록 설치하여 띠형의 단섬유 시트를 초음파 접합장치가 다수개 설치되어 한 행열을 형성하는 초음파 접합장치에 2장의 시트를 통과시키되 띠형의 단섬유 시트가 짝수열-홀수열-짝수열 또는 홀수열-짝수열-홀수열이 반복되게 경유하도록 하여 접합하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
The method of claim 1,
In the bonding process, the ultrasonic bonding apparatus is installed repeatedly, front and rear, left and right, at regular intervals, and in odd or even rows, the ultrasonic bonding apparatus is installed so that the ultrasonic bonding apparatus is positioned between the ultrasonic bonding apparatuses in adjacent rows, thereby ultrasonically bonding the band-shaped single fiber sheet. Two sheets are passed through an ultrasonic bonding device in which a plurality of devices are installed to form a row, but the strip-shaped single-fiber sheet is repeatedly passed through even-numbered-odd-numbered-even-numbered or odd-numbered-even-numbered-odd columns. A method of manufacturing an earthen particle restraint honeycomb reinforcing material, characterized in that bonding.
상기 접합공정은 초음파 접합장치가 일정한 간격으로 설치되어 단섬유 시트에 접합부를 형성하여 한 줄 형태의 셀단위 보강재를 형성시키고 상기 접합부와 접합부 사이에 초음파 접합장치가 위치하도록 초음파 접합장치 또는 셀단위 보강재를 이동시켜 공급되는 새로운 단섬유 시트를 접합시키고 다시 셀단위 보강재를 원위치하여 공급되는 단섬유 시트를 접합시키는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
The method of claim 1,
In the bonding process, the ultrasonic bonding device is installed at regular intervals to form a bonding portion on the short fiber sheet to form a cell unit reinforcement in the form of a single line, and an ultrasonic bonding device or a cell unit reinforcement material so that the ultrasonic bonding device is positioned between the bonding portion and the bonding portion A method of manufacturing a particle constrained honeycomb reinforcing material, characterized in that the new short fiber sheet supplied by moving is joined, and the single fiber sheet supplied by moving the cell unit reinforcing material back to its original position is joined.
상기 열처리공정 후 펀칭공정을 실시하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
The method of claim 1,
A method of manufacturing an earthen particle constrained honeycomb reinforcing material, characterized in that a punching process is performed after the heat treatment process.
상기 펀칭공정은 시트에 + 형의 절취선을 형성시켜 조각편이 일체로 형성되며 상기 + 형의 절취선에 의해 형성된 조각편을 내부 또는 외부 쪽으로 절첩하면 통공을 형성하는 절취선을 형성하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
6. The method of claim 5,
The punching process forms a perforation line of + type on the sheet to form a piece piece integrally, and when the piece piece formed by the + type perforation line is folded inside or outside, a perforation line forming a through hole is formed. A method for manufacturing a mold reinforcement.
상기 웹성형공정 후 적층된 웹에 인장력을 보강하기 위한 보강사가 설치되는 보강사설치공정을 더 포함하여 이루어진 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
The method of claim 1,
and a reinforcing yarn installation step in which reinforcing yarns for reinforcing tensile force are installed in the laminated web after the web forming step.
상기 단섬유 시트는 한 장을 반으로 절첩 또는 2장이 적층되어 인장력을 향상시킨 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
The method of claim 1,
The single fiber sheet is a method of manufacturing a honeycomb constrained grain reinforcing material, characterized in that one sheet is folded in half or two sheets are laminated to improve the tensile force.
상기 단섬유 시트에 있어서, 봉재를 하여 고정사를 형성시켜 투수성 향상과인장력을 향상시키 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
The method of claim 1,
In the short-fiber sheet, the method for producing a grain-constrained honeycomb reinforcing material, characterized in that by forming a fixed yarn by using a bar to improve water permeability and tensile strength.
상기 웹성형공정 후 적층된 웹에 인장력을 보강하기 위한 일표면에 접착 필름 또는 접착용 파우더를 도포하는 것을 특징으로 하는 토립자 구속 벌집형 보강재의 제조방법.
9. The method of any one of claims 1 or 6 to 8,
After the web forming process, an adhesive film or an adhesive powder is applied to one surface for reinforcing tensile force on the laminated web.
단섬유로 이루어지며 니들펀칭되고 표면이 열처리되어 투수성과 인장력이 향상된 띠형의 단섬유 시트를 일정한 간격으로 좌우, 전후 연속반속되게 저주파융착하여 이루어진 것을 특징으로 하는 토립자 구속 벌집형 보강재.
In the particle-constrained honeycomb reinforcing material,
Reinforcing grain constraint honeycomb, characterized in that it is made of short fibers, needle punched, and heat-treated on the surface to form a band-shaped short-fiber sheet with improved water permeability and tensile strength at regular intervals and low-frequency fusion at regular intervals in a continuous semi-continuous front and rear.
상기 단섬유 시트에 + 형의 절취선을 형성시켜 조각편이 일체로 형성되며 상기 + 형의 절취선에 의해 형성된 조각편을 내부 또는 외부 쪽으로 절첩하면 통공을 형성하는 것을 특징으로 하는 토립자 구속 벌집형 보강재.
11. The method of claim 10,
The fragment is integrally formed by forming a +-type perforation line on the short fiber sheet, and a through hole is formed when the fragment formed by the +-type perforation line is folded toward the inside or the outside.
상기 단섬유 시트에 봉재 가공하여 고정사가 더 설치되어 이루어진 것을 특징으로 하는 토립자 구속 벌집형 보강재.13. The method according to any one of claims 11 to 12,
Reinforcing grain constrained honeycomb, characterized in that the fixed yarn is further installed by processing the bar on the short fiber sheet.