KR20210007519A - A mortar composition using industrial by-products be used to form rego type hollow wall block for wall construction and the rego type hollow wall block using thereof - Google Patents
A mortar composition using industrial by-products be used to form rego type hollow wall block for wall construction and the rego type hollow wall block using thereof Download PDFInfo
- Publication number
- KR20210007519A KR20210007519A KR1020190084135A KR20190084135A KR20210007519A KR 20210007519 A KR20210007519 A KR 20210007519A KR 1020190084135 A KR1020190084135 A KR 1020190084135A KR 20190084135 A KR20190084135 A KR 20190084135A KR 20210007519 A KR20210007519 A KR 20210007519A
- Authority
- KR
- South Korea
- Prior art keywords
- hollow
- lego
- block
- fitting
- type concrete
- Prior art date
Abstract
Description
본 발명은 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물 및 이를 이용한 속빈 레고형 콘크리트 블록에 관한 것으로, 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되어 시멘트 모르타르 접착시공없이도 상하좌우 견고하게 적층될 수 있는 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물 및 이를 이용한 속빈 레고형 콘크리트 블록에 관한 것이다.The present invention relates to a mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using industrial by-products, and a hollow Lego-type concrete block using the same, and one or two or more fittings integrally with the block body on the upper part of the block body A protrusion is formed, and one or two or more hollow fitting grooves of the same shape as the one or more fitting protrusions are formed inside the block body, so that the fitting protrusion is inserted into the hollow fitting groove to be integrated and bound without a gap, thereby forming a cement mortar. It relates to a mortar composition for forming hollow Lego-type concrete blocks for civil engineering and building wall construction using industrial by-products that can be firmly stacked up and down, left and right without adhesive construction, and a hollow Lego-type concrete block using the same.
일반적으로 직육면체로 제조되는 콘크리트 블록은 건축용 또는 토목용 벽체 또는 옹벽축조에 주로 쓰이며, 기타 칸막이 공사 등의 간이공사에도 많이 사용하고 있다. 이러한 콘크리트 블록은 모르타르로 접합시켜서 쌓아 올려 소망하는 벽체를 만들게 된다. In general, concrete blocks manufactured in a rectangular parallelepiped are mainly used for building or civil engineering walls or retaining wall construction, and are often used for simple construction such as other partition works. These concrete blocks are bonded with mortar and stacked to create the desired wall.
상기와 같은 일반적인 건축용 또는 토목용 벽체 또는 옹벽축조의 대표적인 종래 시공 방법을 살펴보면, 콘크리트 블록의 상단에 시멘트 모르타르(mortar)를 도포하고, 그 상단에 다시 콘크리트 블록을 조적하는 방법으로 벽체를 시공한 후, 벽체면을 시멘트 모르타르를 이용하여 미장처리를 하였다. Looking at the typical conventional construction method of the general building or civil engineering wall or retaining wall construction as described above, after applying the cement mortar to the top of the concrete block, and then constructing the wall by masonry again on the top of the concrete block. , The wall surface was plastered using cement mortar.
그러나, 상기의 경우 콘크리트 블록을 조적함에 있어서, 건물의 바닥면에 대하여 수직으로 벽체를 축조하기 위해서는 숙련된 작업자의 상당한 주의를 요하며, 콘크리트 블록의 상단에 시멘트 모르타르(mortar)를 도포하여 조적하는 작업에 많은 작업 시간과 노동력을 필요로 하여, 공사기한의 지연 및 시공비가 증대되는 등 비효율적인 문제점이 있었다.However, in the case of masonry in the above case, in order to construct a wall vertically with respect to the floor surface of a building, considerable attention is required by a skilled worker, and a cement mortar is applied to the top of the concrete block to masonry. Since the work requires a lot of work time and labor, there are inefficient problems such as delay in the construction period and increase in construction cost.
상기한 종래 문제점들을 해결하기 위하여, 최근에는 조립식으로 콘크리트 블록을 조적하는 기술들이 개발되었는데, 한국등록실용신안 20-0273410(등록일자 2002년04월15일)에 양 사이드(12a)와 마구리(12b), 그리고 상면(12c)과 하면(12d)의 직육면체로 이루어진 블록몸체(12)과, 상기 상면 (12c)과 하면(12d)의 중앙 길이방향으로 서로 대응되게 형성되어 블록몸체(12)를 각홈이음(tongue and groove joint)으로 조립할 수 있게 하는 돌출레일(14) 및 오목레일(16)과, 상기 양 마구리(12b)에 수직되게 형성되어 각 블록 몸체(12)를 모르타르로 고정할 수 있는 모르타르 홈(18)과, 상기 양 마구리(12b)를 관통하여 매설되어 블록몸체(12)를 단열시키는 제 1단열재(20) 및 제 2단열재(22)를 포함하여 구성된 것에 있어서, 상기 제 1단열재(20) 및 제 2단열재(22)는 서로 대향되는 경사면(20a)(22a)이 형성되고, 그 사이에 보강블록(12e) 이 블록몸체(12)와 일체로 연결된 것을 특징으로 하는 조립식 콘크리트 단열블록이 공지되어 있다.In order to solve the above-described conventional problems, technologies for masonry of concrete blocks in a prefabricated manner have recently been developed. In Korea Utility Model 20-0273410 (Registration Date April 15, 2002), both sides 12a and Maguri 12b ), and a block body 12 made of a rectangular parallelepiped of the upper surface 12c and the lower surface 12d, and the block body 12 is formed to correspond to each other in the central longitudinal direction of the upper surface 12c and the lower surface 12d. A protruding rail 14 and a concave rail 16 that can be assembled with a tongue and groove joint, and a mortar that is formed perpendicular to the both ends 12b to fix each block body 12 with a mortar. A groove 18 and a first insulating material 20 and a second insulating material 22 that are buried through the both ends 12b to insulate the block body 12, wherein the first insulating material ( 20) and the second insulating material 22 is a prefabricated concrete insulation block, characterized in that inclined surfaces 20a and 22a facing each other are formed, and a reinforcing block 12e is integrally connected with the block body 12 therebetween. This is known.
또한, 한국등록실용신안 20-0335136(등록일자 2003년11월25일)에는 건축 현장에서 일반적으로 사용되는 조적용 건축자재인 블록(2)과 벽돌(12)의 구조를 개량하여 상기 조적용 건축자재에 기능성을 갖는 물질을 내장시켜 열손실, 소음차단, 방수 등의 기능성을 제공하는 동시에 연결돌출부(4)와 연결결합부(10)를 구비하여 시멘트 몰탈의 접착없이도 상기 조적용건축자재의 연결돌출부(4)가 다른 조적용건축자재의 연결결합부(10)에 삽입되어 가로 연결시공이 간편하여 현장에서 모든 공정 에 효과를 제공하는 현저한 효과가 있게 되는 조립식 기능성 조적용 건축자재가 공지되어 있다.In addition, in the Korean Utility Model Registration 20-0335136 (registration date November 25, 2003), the structure of the blocks (2) and bricks (12), which are commonly used masonry materials in construction sites, has been improved. By embedding a functional material into the material, it provides functions such as heat loss, noise blocking, and waterproofing, and at the same time, it is provided with a connection protrusion (4) and a connection joint (10) to connect the building materials for construction without cement mortar adhesion. Prefabricated functional building materials for masonry are known that have a remarkable effect of providing effects to all processes in the field because the protrusions 4 are inserted into the connecting parts 10 of other masonry materials for easy horizontal connection construction. .
또한, 한국등록실용신안 20-0340941(등록일자 2004년01월28일)에는 주위의 환경과 친화적으로 형성될 수 있도록 조경용 식생공이 형성되고, 조경용 식생공이 형성된 블록을 이용하여 옹벽용 또는 어소용으로 사용하는 블록에 있어서, 일측에 블록(10)과 블록(10)이 결합될 수 있도록 돌기(11a)가 형성되고, 타측에는 결합홈(11b)이 형성된 결합부(11)와; 상기 블록(10)과 블록(10)을 적층시 철근을 끼워 연결할 수 있도록 양측에 다수 형성된 끼움공(16)과; 상기 양측에 형성된 끼움공(16) 사이에 저부가 막히고 옹벽블록으로 사용시 작은묘목, 화초를 선택적으로 심을 수 있도록 된 제1식생공(12)과; 상기 제1식생공(12) 후부에 어소 블록으로 사용시 고기의 휴식공간이 될 수 있도록 형성된 어소공(13)과; 상기 블록(10)과 블록(10)을 좌우로 연결시 제2식생공(13)이 형성되도록 전면 양측 모서리에 형성된 요홈(14)을 포함하는 구성으로 블록(10)이 이루어진 것을 특징으로 하는 옹벽블록 겸용 어소블록이 공지되어 있다.In addition, in the Korean Utility Model Registration 20-0340941 (registration date January 28, 2004), a vegetation hole for landscaping is formed so that it can be formed in a friendly manner with the surrounding environment, and a block with a vegetation hole for landscaping is used for retaining walls or for associates. In the used block, a protrusion 11a is formed so that the block 10 and the block 10 can be coupled to each other on one side, and a coupling portion 11 having a coupling groove 11b formed on the other side; A plurality of fitting holes 16 formed on both sides of the block 10 and the block 10 so that reinforcing bars can be inserted and connected when stacking the block 10 and the block 10; A first vegetation hole (12) for selectively planting small seedlings and flowers when the bottom is blocked between the fitting holes 16 formed on both sides and used as a retaining wall block; An associate hole 13 formed at the rear of the first vegetation hole 12 so as to become a resting area for meat when used as an associate block; Retaining wall, characterized in that the block 10 is formed in a configuration including grooves 14 formed at both front corners so that the second vegetation hole 13 is formed when the block 10 and the block 10 are connected to the left and right Block-combined associate blocks are known.
또한, 한국등록실용신안 20-0467656(등록일자 2013년06월20일)에는 몸체부; 상기 몸체부 내부에 포함되는 복수개의 단열재 충진부; 상기 몸체부의 일측면에 돌출 형성되는 돌출부; 및 상기 몸체부의 상기 돌출부가 형성된 면과 대향되는 면에 상기 몸체부의 내측으로 형성되는 삽입부;를 포함하고, 상기 삽입부는 상기 몸체부의 내측으로 삽입되는 모서리부에 모따기 구조의 단차부를 포함하고, 상기 돌출부는 상기 몸체부의 외측으로 돌출되는 모서리부에 모따기 구조의 단차부를 포함하는 것을 특징으로 하는 단열성 강화 블록이 공지되어 있다.In addition, the Korean Utility Model Registration 20-0467656 (registration date June 20, 2013) includes the body; A plurality of insulating material filling portions included in the body portion; A protrusion protruding from one side of the body portion; And an insertion portion formed inwardly of the body portion on a surface opposite to the surface where the protrusion portion of the body portion is formed, wherein the insertion portion includes a stepped portion having a chamfer structure at an edge portion inserted into the inner side of the body portion, and the A heat insulating reinforcing block is known, characterized in that the protrusion includes a stepped portion having a chamfer structure at a corner protruding outward of the body portion.
또한, 한국등록특허 10-0514086(등록일자 2005년09월02일)에는 친환경 구축력 옹벽에 있어서, 정면부(1')와, 측벽(3,3')과, 중앙측벽 (3'') 및 후면부(4')로 형성되며, 상기 정면부(1')와 후면부(4'), 2개의 측벽 (3,3') 및 중앙측벽(3'')이 연결되어 형성된 내부는 콘크리트로 메우거나 흙을 채워 넣어 블록 내부로 유입되는 물의 배수를 겸하면서 나무나 풀 등의 식재를 할 수 있는 공간부(5)가 형성되고, 상기 정면부(1')는 자연석문양이 형성되거나 자연석이 부착되고, 상기 정면부(1')에 나무나 풀, 꽃등의 재배되거나, 저목(작은나무) 등의 꺽꽂이 나무를 식재할 수 있도록 형성된 다수의 정면통공(2)이 형성되며, 상기 후면부(4')는 중앙에 형성된 배수공의 역할을 하는 후면통공 (7)과, 상기 후면통공(7)의 외측으로 돌출되어 형성된 다수의 앵커연결부(34)로 구성되며, 상기 정면부(1')와 후면부(4')의 상부면에 형성된 양측의 4개의 앵커홈 (33)과, 상기 정면부(1)와 후면부(3) 일측을 연결시키는 2개의 측벽(3,3') 및 하나의 중앙측벽(3'')으로 구성되어 있고, 상기 3개의 측벽(3,3',3'')은 상부에 형성된 다수의 상부돌출부(31)와, 상기 상부돌출부(31) 사이에 형성된 상부요홈부 (31')와, 상기 상부돌출부(31)와 상부요홈부(31')에 대응되도록 하부에 형성된 하부돌출부(32) 및 하부요홈부 (32')와, 상기 측벽(3,3')의 중앙부에 형성된 측면통공(6)으로 구성된 친환경 구축력 옹벽이 공지되어 있다.In addition, in the Korean Patent Registration 10-0514086 (registration date September 2, 2005), in the environmentally friendly building power retaining wall, the front part 1', the side walls 3, 3', the central side wall 3'', and It is formed as a rear part (4'), and the inside formed by connecting the front part (1') and the rear part (4'), two side walls (3, 3') and the central side wall (3'') is filled with concrete or Filling with soil and draining water flowing into the block, a space part 5 capable of planting trees or grass is formed, and the front part 1'has a natural stone pattern or natural stone attached thereto. , A plurality of front through holes 2 formed so as to cultivate trees, grass, flowers, etc., or to plant cut trees such as low trees (small trees) are formed in the front part 1 ′, and the rear part 4 ′ Is composed of a rear through hole 7 serving as a drain hole formed in the center, and a plurality of anchor connecting parts 34 protruding outward from the rear through hole 7, and the front part 1 ′ and the rear part 4 Four anchor grooves 33 on both sides formed on the upper surface of'), two side walls 3 and 3'connecting one side of the front portion 1 and the rear portion 3, and one central side wall 3' '), and the three sidewalls (3,3',3'') have a plurality of upper protrusions 31 formed thereon, and an upper concave groove 31 ′ formed between the upper protrusions 31 And, a lower protrusion 32 and a lower concave part 32 ′ formed at the lower portion to correspond to the upper protrusion 31 and the upper concave groove 31 ′, and a side surface formed at the center of the side walls 3 and 3 ′. An eco-friendly retaining wall composed of through holes 6 is known.
또한, 한국등록특허 10-0522174(등록일자2005년10월10일)에는 하부 양측으로 끼움돌기(20)가 형성되고, 상부로는 이에 대응되는 끼움홈(30)이 형성되어 상부 및 하부로 적층 가능하게 이루어지되, 상기 끼움홈(30)의 바닥면에서 상기 끼움돌기(20)까지 관통된 통공(31)이 된 직육면체의 몸체(10)로 이루어 지며, 상기 몸체(10)는 적층시 자유로운 굴곡이 가능하도록 양측이 둥글게 만곡된 "호" 형태를 갖으며, 전면으로는 각종식생물이 서식할 수 있도록 서로 다른 직경을 갖는 다수의 식생공(40)이 형성되는 것을 특징으로 하는 레고형 옹벽블럭이 공지되어 있다.In addition, in Korean Patent Registration 10-0522174 (registration date October 10, 2005), fitting protrusions 20 are formed on both sides of the lower side, and fitting grooves 30 corresponding thereto are formed on the upper side, and are stacked on top and bottom. It is made possible, but consists of a body 10 of a rectangular parallelepiped body having a through hole 31 penetrating from the bottom surface of the fitting groove 30 to the fitting protrusion 20, and the body 10 is bent freely when stacked Lego-type retaining wall block, characterized in that it has a shape of "arc" curved on both sides to enable this, and a plurality of vegetation holes 40 having different diameters are formed on the front side so that various vegetation can inhabit. This is known.
또한, 한국공개특허 10-2009-0084568(공개일자 2009년08월05일)에는 콘크리트 블록구조물(1)에 있어서, 상기 제 1 블록구조물(1)과 상기 제 1 블록구조물(1) 상에 수직 다단으로 결합되는 적어도 하나 이상의 제 2 블 록구조물(2)로 이루어지되, 상기 제 1 블록구조물(1)은 일측면에 다수의 측면 삽입홈(111)이 형성되고, 타측면에 상기 측면 삽입홈(111)에 대응되는 형상의 다수의 측면 돌출부(112)가 형성되며, 상부 삽입홈(113)이 형성된 다수의 제 1 단위블록(11)들로 구성되고, 각각의 이웃하는 제 1 단위블록(11)은 상기 측면 삽입홈(111)에 인접하는 측면 돌출부(112)가 삽입 결합되어 일체화되고, 상기 제 2 블록구조물(2)은 일측면에 다수의 측면 삽입홈(211)이 형성되고, 타측면에 상기 측면 삽입홈(211)에 대응되는 형상의 다수의 측면 돌출부(212)와 상부 삽입홈(213) 및 하부 돌출부(214)가 형성된 다수의 제 2 단위 블록(21)들로 구성되고, 각각의 이웃하는 제 2 단위블록(21)은 측면 삽입홈(211)에 인접하는 측면 돌출부(212)가 삽입 결합되어 일체화된 것을 특징으로 하는 토목 벽제 건설용 콘크리트 블록구조물이 공지되어 있다.In addition, Korean Patent Laid-Open Publication No. 10-2009-0084568 (published on Aug. 5, 2009) shows that in the concrete block structure (1), vertically on the first block structure (1) and the first block structure (1). Consisting of at least one or more second block structures (2) coupled in multiple stages, the first block structure (1) has a plurality of side insertion grooves 111 formed on one side thereof, and the side insertion grooves on the other side A plurality of side protrusions 112 having a shape corresponding to 111 are formed, and composed of a plurality of first unit blocks 11 having an upper insertion groove 113 formed therein, and each of the neighboring first unit blocks ( 11) The side protrusion 112 adjacent to the side insertion groove 111 is inserted and integrated, and the second block structure 2 has a plurality of side insertion grooves 211 formed on one side thereof, and the other Consisting of a plurality of second unit blocks 21 having a plurality of side protrusions 212 and an upper insertion groove 213 and a lower protrusion 214 having a shape corresponding to the side insertion groove 211 on the side, Each neighboring second unit block 21 is known as a concrete block structure for civil wall construction characterized in that the side protrusions 212 adjacent to the side insertion grooves 211 are inserted and integrated.
그러나, 상기 언급된 콘크리트 블록들은 수직방향으로 관통되어 수직방향으로 흙 또는 채움재로 채워져 고정되어 식생 또는 옹벽으로 사용되는 것들이며, 특히 종래 콘크리트 블록들은 상부 및 하부에 각각 결합돌기 및 결합홈이 형성되어 있기는 하나 횡방향 또는 종방향의 일방향으로만 외력변형에 대응력이 발생하여 다른 일방향에 대한 외력변형에 대응력이 취약한 문제점이 있었으며, 흙 또는 채움재로 채워져 고정되지 않으면 외력에 의하여 쉽게 붕괴되는 단점이 있었을 뿐만 아니라, 이를 보강하기 위하여 시멘트 모르타르 접착 시공이 반드시 필요한 문제점이 있었다.However, the above-mentioned concrete blocks are vertically penetrated and filled with soil or filling material in the vertical direction to be fixed to be used as vegetation or retaining walls.In particular, conventional concrete blocks have coupling protrusions and coupling grooves formed at the top and bottom, respectively. However, there was a problem that the response force to the external force deformation occurred only in one direction in the transverse or longitudinal direction, so that the ability to respond to the external force deformation in the other direction was weak.If it was not fixed by being filled with soil or filling material, it would have a disadvantage that it would easily collapse by external force. In addition, there is a problem in which cement mortar adhesion construction is required to reinforce this.
본 발명은 상기 종래 문제점들을 해결하기 위하여, 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되어 시멘트 모르타르 접착시공없이도 상하좌우 견고하게 적층될 수 있는 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물 및 이를 이용한 속빈 레고형 콘크리트 블록을 제공하는 것을 해결하고자 하는 과제로 한다.In the present invention, in order to solve the above problems, one or more fitting protrusions are formed integrally with the block body on an upper portion of the block body, and one or more of the same shape as the one or two or more fitting protrusions is formed inside the block body. Hollow lego for civil engineering and building wall construction using industrial by-products that can be firmly stacked up, down, left and right without cement mortar bonding by being integrated with two or more hollow fitting grooves, and the fitting protrusion is inserted into the hollow fitting groove. It is a problem to be solved to provide a mortar composition for forming a concrete block and a hollow Lego-type concrete block using the same.
본 발명은 상기 과제를 해결하기 위하여, 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되어 시멘트 모르타르 접착시공없이도 상하좌우 견고하게 적층될 수 있는 속빈 레고형 콘크리트 블록을 성형하기 위한 모르타르 조성물로서, 상기 모르타르 조성물은 천연잔골재와 동슬래그를 9 : 1의 중량비로 혼합한 혼합잔골재와, 보통시멘트와 고로슬래그분말을 7 : 3의 중량비로 혼합하고 여기에 상기 보통시멘트 사용량의 5중량% 비율로 폐유리를 분쇄한 폐유리분말을 첨가하여 혼합한 혼합시멘트를 조성하고, 상기 혼합시멘트와 상기 혼합잔골재를 1 : 6~8의 중량비로 혼합하고 물을 배합하여 조성한 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물을 과제의 해결수단으로 한다.In order to solve the above problems, the present invention has one or more fitting protrusions formed integrally with the block body on an upper portion of the block body, and one or two fitting protrusions having the same shape as the one or more fitting protrusions inside the block body As a mortar composition for forming a hollow Lego-type concrete block in which the above hollow fitting grooves are formed so that the fitting protrusions are inserted into the hollow fitting grooves so as to be integrally bonded without gaps and that can be firmly stacked up and down, left and right without cement mortar adhesion construction, The mortar composition is a mixed fine aggregate obtained by mixing natural fine aggregate and copper slag in a weight ratio of 9:1, and a mixture of ordinary cement and blast furnace slag powder in a weight ratio of 7:3. Civil engineering and building wall construction using industrial by-products formed by adding glass crushed waste glass powder to form a mixed cement, mixing the mixed cement and the mixed fine aggregate at a weight ratio of 1: 6 to 8 and mixing water A mortar composition for molding hollow Lego concrete blocks is used as a solution to the problem.
상기 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물은 압축강도 18MPa 이상인 것을 과제의 해결수단으로 한다. The mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using the industrial by-products is a means of solving the problem that the compressive strength is 18 MPa or more.
상기 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물로 성형된 콘크리트 블록으로서, 상기 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되므로 시멘트 모르타르 접착시공없이도 모든 방향의 외력에 대하여 견고하게 적층될 수 있는 속빈 레고형 콘크리트 블록을 과제의 해결수단으로 한다. A concrete block molded from a mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using the industrial by-product, wherein one or more fitting protrusions are formed integrally with the block body on the upper portion of the block body, and the One or two or more hollow fitting grooves of the same shape as the one or more fitting protrusions are formed inside the block body, so that the fitting protrusion is inserted into the hollow fitting groove and is integrally bonded without any gaps. Hollow Lego-type concrete blocks that can be firmly stacked against external force are used as a solution to the problem.
상기 속빈 레고형 콘크리트 블록은 길이방향으로 복수개 인접 연결시 상기 하나 또는 둘 이상의 끼움돌기와 하나 또는 둘 이상의 속빈 끼움홈의 간격이 동일하게 형성되어 상기 속빈 레고형 콘크리트 블록 적층시 지그재그형으로 적층되더라도 틈새없이 일체화 결속되는 것을 과제의 해결수단으로 한다.When a plurality of hollow Lego-type concrete blocks are connected adjacently in the longitudinal direction, the one or more fitting protrusions and one or more hollow fitting grooves have the same spacing, so that even if the hollow Lego-type concrete blocks are stacked in a zigzag shape, there is no gap. Unity and unity are the means of solving the problem.
상기 속빈 레고형 콘크리트 블록은 길이방향 일측면에는 측면끼움돌기가 형성되고, 길이방향 타측면에는 측면끼움홈이 형성되어 상기 측면끼움돌기가 인접된 속빈 레고형 콘크리트 블록의 측면끼움홈에 삽입되어 일자형으로 적층시 길이방향에 대한 수직방향의 외력에 대하여 견고하게 적층되는 것을 과제의 해결수단으로 한다.The hollow Lego-type concrete block has a side fitting protrusion formed on one side in the longitudinal direction, and a side fitting groove is formed on the other side in the longitudinal direction, and the side fitting protrusion is inserted into the side fitting groove of the adjacent hollow Lego-type concrete block. As a means of solving the problem, it is firmly laminated against an external force in the vertical direction with respect to the longitudinal direction.
본 발명의 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물로 성형된 콘크리트 블록은 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되어 시멘트 모르타르 접착시공없이도 상하좌우 견고하게 적층될 수 있는 우수한 효과가 있다.The concrete block formed of a mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using an industrial by-product of the present invention has one or more fitting protrusions formed integrally with the block body on the upper portion of the block body, and the One or two or more hollow fitting grooves of the same shape as the one or more fitting protrusions are formed inside the block body, so that the fitting protrusion is inserted into the hollow fitting groove to be integrated and bound without a gap, so that it is solid up, down, left, and right without cement mortar bonding. There is an excellent effect that can be stacked together.
뿐만 아니라, 본 발명은 시멘트 모르타르 접착시공을 생략할 수 있게 되어 그 결과 양생시간이 불필요하여 시공시간을 대폭 단축시키는 효과와 함께, 해체후 재사용이 가능하며, 조립이 매우 간단하여 훈련된 기능공이 필요없이 누구나 조립할 수 있어 인건비를 절감하는 우수한 효과가 있다.In addition, the present invention makes it possible to omit the cement mortar bonding construction, and as a result, the curing time is unnecessary and thus the construction time is greatly shortened, and it can be reused after disassembly, and the assembly is very simple, so a trained skilled worker is required. Anyone can assemble without it, so it has an excellent effect of reducing labor costs.
도 1은 본 발명의 속빈 레고형 콘크리트 블록 형태를 나타내는 사시도
도 2는 본 발명의 속빈 레고형 콘크리트 블록 연결상태를 나타내는 사시도
도 3은 본 발명의 속빈 레고형 콘크리트 블록 측면결합을 나타내는 사시도1 is a perspective view showing the form of a hollow Lego concrete block of the present invention
Figure 2 is a perspective view showing the connection state of the hollow Lego concrete block of the present invention
Figure 3 is a perspective view showing the side combination of the hollow Lego concrete block of the present invention
본 발명은, 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되어 시멘트 모르타르 접착시공없이도 상하좌우 견고하게 적층될 수 있는 속빈 레고형 콘크리트 블록을 성형하기 위한 모르타르 조성물로서, 상기 모르타르 조성물은 천연잔골재와 동슬래그를 9 : 1의 중량비로 혼합한 혼합잔골재와, 보통시멘트와 고로슬래그분말을 7 : 3의 중량비로 혼합하고 여기에 상기 보통시멘트 사용량의 5중량% 비율로 폐유리를 분쇄한 폐유리분말을 첨가하여 혼합한 혼합시멘트를 조성하고, 상기 혼합시멘트와 상기 혼합잔골재를 1 : 6~8의 중량비로 혼합하고 물을 배합하여 조성한 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물을 기술구성의 특징으로 한다.In the present invention, one or more fitting protrusions are formed integrally with the block body on an upper portion of the block body, and one or two or more hollow fitting grooves of the same shape as the one or more fitting protrusions are formed inside the block body As a mortar composition for forming a hollow Lego-type concrete block that can be firmly stacked up, down, left and right without a cement mortar adhesion construction by inserting the fitting protrusion into the hollow fitting groove and being integrated without a gap, the mortar composition is a natural fine aggregate Waste glass obtained by mixing vortex slag at a weight ratio of 9:1, and a mixture of ordinary cement and blast furnace slag powder at a weight ratio of 7:3 and pulverizing the waste glass at a ratio of 5% by weight of the amount of ordinary cement used. Hollow Lego-type concrete block for civil engineering and building wall construction using industrial by-products formed by adding powder to form mixed cement, mixing the mixed cement and the mixed fine aggregate at a weight ratio of 1: 6 to 8 and mixing water The mortar composition for molding is characterized by the technical configuration.
상기 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물은 압축강도 18MPa 이상인 것을 기술구성의 특징으로 한다.The mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using the industrial by-product is characterized in that the compressive strength is 18 MPa or more.
상기 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물로 성형된 콘크리트 블록으로서, 상기 블록 몸체의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기가 형성되고, 상기 블록 몸체의 내부에 상기 하나 또는 둘 이상의 끼움돌기와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈이 형성되어 상기 끼움돌기가 상기 속빈 끼움홈 내부에 삽입되어 틈새없이 일체화 결속되므로 시멘트 모르타르 접착시공없이도 모든 방향의 외력에 대하여 견고하게 적층될 수 있는 속빈 레고형 콘크리트 블록을 기술구성의 특징으로 한다.A concrete block molded from a mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using the industrial by-product, wherein one or more fitting protrusions are formed integrally with the block body on the upper portion of the block body, and the One or two or more hollow fitting grooves of the same shape as the one or more fitting protrusions are formed inside the block body, so that the fitting protrusion is inserted into the hollow fitting groove and is integrally bonded without any gaps. It features hollow Lego-type concrete blocks that can be firmly stacked against external forces.
상기 속빈 레고형 콘크리트 블록은 길이방향으로 복수개 인접 연결시 상기 하나 또는 둘 이상의 끼움돌기와 하나 또는 둘 이상의 속빈 끼움홈의 간격이 동일하게 형성되어 상기 속빈 레고형 콘크리트 블록 적층시 지그재그형으로 적층되더라도 틈새없이 일체화 결속되는 것을 기술구성의 특징으로 한다.When a plurality of hollow Lego-type concrete blocks are connected adjacently in the longitudinal direction, the one or more fitting protrusions and one or more hollow fitting grooves have the same spacing, so that even if the hollow Lego-type concrete blocks are stacked in a zigzag shape, there is no gap. It is a feature of the technical composition that it is integrated and bound.
상기 속빈 레고형 콘크리트 블록은 길이방향 일측면에는 측면끼움돌기가 형성되고, 길이방향 타측면에는 측면끼움홈이 형성되어 상기 측면끼움돌기가 인접된 속빈 레고형 콘크리트 블록의 측면끼움홈에 삽입되어 일자형으로 적층시 길이방향에 대한 수직방향의 외력에 대하여 견고하게 적층되는 것을 기술구성의 특징으로 한다.The hollow Lego-type concrete block has a side fitting protrusion formed on one side in the longitudinal direction, and a side fitting groove is formed on the other side in the longitudinal direction, and the side fitting protrusion is inserted into the side fitting groove of the adjacent hollow Lego-type concrete block. As a feature of the technology configuration, it is firmly laminated against an external force in the vertical direction with respect to the longitudinal direction during lamination.
이하에서는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 바람직한 실시예 또는 도면을 통하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, it will be described in detail through preferred embodiments or drawings of the present invention so that those of ordinary skill in the art can easily implement the present invention. However, the present invention may be implemented in various different forms and is not limited to the embodiments described herein.
본 발명의 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물은 천연잔골재와 동슬래그를 9 : 1의 중량비로 혼합한 혼합잔골재와, 보통시멘트와 고로슬래그분말을 7 : 3의 중량비로 혼합하고 여기에 상기 보통시멘트 사용량의 5중량% 비율로 폐유리를 분쇄한 폐유리분말을 첨가하여 혼합한 혼합시멘트를 조성하고, 상기 혼합시멘트와 상기 혼합잔골재를 1 : 6~8의 중량비로 혼합하고 물을 배합하여 조성된다.The mortar composition for forming hollow Lego concrete blocks for civil engineering and building wall construction using the industrial by-products of the present invention is a mixed fine aggregate obtained by mixing natural fine aggregate and copper slag in a weight ratio of 9: 1, and ordinary cement and blast furnace slag powder. Mixing at a weight ratio of 3 and adding waste glass powder obtained by pulverizing waste glass at a ratio of 5% by weight of the amount of normal cement used to form a mixed cement, and mixing the mixed cement and the mixed fine aggregate are 1:6~8 It is formulated by mixing in a weight ratio of and mixing water.
이때, 상기 동슬래그는 산업부산물로서 발생하는 것인데 종전에는 자원으로 활용되지 못하고, 추가 비용을 들여서 폐기하여야만 했다. 본 발명에서는 이러한 동슬래그를 재료로 활용함으로써, 비용 절감과 자원재활용에 의한 친환경성을 높이면서도, 본 발명의 조성물로 제작되는 속빈 레고형 콘크리트 블록이 고강도를 발휘하도록 한다.At this time, the copper slag is generated as an industrial by-product, but was not used as a resource in the past, and had to be disposed of at an additional cost. In the present invention, by using the copper slag as a material, the hollow Lego-type concrete block made of the composition of the present invention exhibits high strength while reducing cost and increasing eco-friendliness by recycling resources.
구체적으로 본 발명에서 천연잔골재와 동슬래그를 9 : 1의 중량비로 혼합하여 사용하는 것이 바람직한데, 동슬래그의 함유량 상기 중량비 미만인 경우에는 강도가 저하될 뿐만 아니라, 산업부산물의 재활용이라는 친환경적인 효과가 미미하고, 상기 중량비 초과시에는 천연잔골재와의 재료분리로 인하여 오히료 물성저하 우려가 있다.Specifically, in the present invention, it is preferable to use a mixture of natural fine aggregate and copper slag in a weight ratio of 9:1, but when the content of copper slag is less than the weight ratio, not only the strength decreases, but also the environmentally friendly effect of recycling industrial by-products is obtained. It is insignificant, and when the weight ratio is exceeded, there is a concern that physical properties may be deteriorated due to material separation from natural fine aggregate.
특히, 본 발명에서 사용되는 동슬래그는, 그 입경이 0.1 내지 5mm의 크기를 가지는 것이 좋으며, 동슬래그의 입경이 0.1mm 미만이면, 동슬래그 입자가 지나치게 작아져서 동슬래그 함유에 의한 강도향상효과가 미미하며, 반대로 입경이 5mm를 초과하면 동슬래그 입자가 너무 커져서 표면의 외관이 저하되는 문제점이 있다.In particular, the copper slag used in the present invention preferably has a particle diameter of 0.1 to 5 mm, and if the particle diameter of the copper slag is less than 0.1 mm, the copper slag particles become too small, resulting in the effect of improving the strength by containing the copper slag. It is insignificant, and on the contrary, when the particle diameter exceeds 5 mm, there is a problem that the copper slag particles become too large to deteriorate the appearance of the surface.
한편, 고로슬래그는 철강 산업 부산물로서 주성분이 CaO와 SiO2 등에 해당하여 시멘트와 그 조성이 유사하면서도 CO2를 발생시키지 않아 친환경 건설소재로 알려져 있다.On the other hand, blast furnace slag is a by-product of the steel industry, and its main components correspond to CaO and SiO2, so that its composition is similar to that of cement, but does not generate CO2, so it is known as an eco-friendly construction material.
따라서, 최근에는 아파트 등 건축공사에 사용하는 레미콘의 경우에는 고로슬래그를 일부 사용하고 있지만 고로슬래그는 시멘트와 달리 수화반응을 하지 않기 때문에, 충분한 초기 강도를 확보하기 어려워 고강도 콘크리트를 제조할 경우에는 사용이 제한되어 왔다Therefore, recently, in the case of ready-mixed concrete used for building construction such as apartments, some blast furnace slag is used, but since blast furnace slag does not undergo hydration reaction unlike cement, it is difficult to secure sufficient initial strength and is used when manufacturing high-strength concrete. This has been limited
따라서, 본 발명의 속이빈 레고형 콘크리트 블록에는 보통시멘트와 고로슬래그분말을 7 : 3의 중량비로 혼합하여 사용하는 것이 바람직하며, 고로슬래그의 사용 중량비가 상기 수치범위를 초과하면 강도가 저하되고, 미만 사용하면 보통시멘트의 대체제로서의 효과가 미미한 단점이 있다.Therefore, it is preferable to mix and use ordinary cement and blast furnace slag powder in a weight ratio of 7:3 in the hollow Lego-type concrete block of the present invention, and when the weight ratio of the blast furnace slag exceeds the above numerical range, the strength decreases, If used less than that, the effect as a substitute for ordinary cement is insignificant.
상기 폐유리를 분쇄한 폐유리분말은 폐유리를 분새할 때 발생되는 폐유리분말로서, SiO2가 90%이상 함유되어 있으므로 이를 시멘트에 대하여 5중량% 비율로 사용하게 되면 시멘트 대체제로서 뿐만 아니라 흡수율이 저하되는 효과가 있게 되는 장점이 있다.The waste glass powder obtained by pulverizing the waste glass is a waste glass powder generated when the waste glass is dispensed.SiO2 is contained more than 90%, so if it is used in a ratio of 5% by weight to cement, it is not only a cement substitute, but also has an absorption rate. There is an advantage of having a lowering effect.
본 발명의 모르타르 조성물은 상기 혼합시멘트와 상기 혼합잔골재를 1 : 6~8의 중량비로 혼합하고 물을 배합하여 조성하는데, 이렇게 조성된 모르타르 조성물은 블록으로 양생후, 압축강도 18MPa 이상을 나타낸다.The mortar composition of the present invention is composed by mixing the mixed cement and the mixed fine aggregate at a weight ratio of 1: 6 to 8 and mixing water, and the mortar composition thus constituted after curing with a block, exhibits a compressive strength of 18 MPa or more.
한편, [도 1] 내지 [도 3]을 참조하여 설명하면, 상기 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물로 제조되는 속빈 레고형 콘크리트 블록은, 상기 블록 몸체(100)의 상부에 상기 블록 몸체와 일체로 하나 또는 둘 이상의 끼움돌기(101)가 형성되고, 상기 블록 몸체(100)의 내부에 상기 하나 또는 둘 이상의 끼움돌기(101)와 동일한 형태의 하나 또는 둘 이상의 속빈 끼움홈(102)이 형성되어 상기 끼움돌기(101)가 상기 속빈 끼움홈(102) 내부에 삽입되어 틈새없이 일체화 결속되므로 시멘트 모르타르 접착시공없이도 모든 방향의 외력에 대하여 견고하게 적층될 수 있도록 구성된다.On the other hand, referring to [Figs. 1] to [Fig. 3], the hollow Lego-type concrete block made of a mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using the industrial by-products, the block body One or more
이때, [도 2]에 도시한 바와 같이, 상기 속빈 레고형 콘크리트 블록은 길이방향으로 복수개 인접 연결시 상기 하나 또는 둘 이상의 끼움돌기(101)와 하나 또는 둘 이상의 속빈 끼움홈(102)의 간격이 동일(D1=D2)하게 형성되어 상기 속빈 레고형 콘크리트 블록 적층시 지그재그형으로 적층되더라도 틈새없이 일체화 결속될 수 있는 것이 특징적 구성이다.At this time, as shown in [Fig. 2], when a plurality of the hollow Lego-type concrete blocks are connected adjacently in the longitudinal direction, the distance between the one or more
또한, [도 3]에 도시한 바와 같이, 상기 속빈 레고형 콘크리트 블록은 길이방향 일측면에는 측면끼움돌기(103)가 형성되고, 길이방향 타측면에는 측면끼움홈(104)이 형성되어 상기 측면끼움돌기(103)가 인접된 속빈 레고형 콘크리트 블록의 측면끼움홈(104)에 삽입되어 일자형으로 적층시 길이방향에 대한 수직방향의 외력에 대하여 견고하게 적층되도록 구성된다.In addition, as shown in [Fig. 3], the hollow Lego-type concrete block has a side
[본 발명의 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물 제조][Preparation of mortar composition for molding hollow Lego concrete block of the present invention]
천연잔골재와 동슬래그를 9 : 1의 중량비로 혼합한 혼합잔골재 100kg과, 보통시멘트와 고로슬래그분말을 7 : 3의 중량비로 혼합하고 여기에 상기 보통시멘트 사용량의 5중량% 비율로 폐유리를 분쇄한 폐유리분말을 첨가하여 혼합한 혼합시멘트 10kg를 조성하고, 상기 혼합시멘트 10kg에 대하여 상기 혼합잔골재를 1 : 7의 중량비로 혼합하고 적량의 물을 배합하여 모르타르 조성물을 제조하였다.100kg of mixed fine aggregate obtained by mixing natural fine aggregate and copper slag at a weight ratio of 9:1, and ordinary cement and blast furnace slag powder at a weight ratio of 7:3, and crushed waste glass at a ratio of 5% by weight of the amount of normal cement used. One waste glass powder was added to prepare 10 kg of mixed cement, and the mixed fine aggregate was mixed at a weight ratio of 1:7 with respect to 10 kg of the mixed cement, and an appropriate amount of water was added to prepare a mortar composition.
[본 발명의 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물의 물성측정][Measurement of Physical Properties of Mortar Composition for Molding Hollow Lego Concrete Block of the Invention]
상기 [실시예 1]에서 제조한 모르타르 조성물에 대하여, KS F 2405(콘크리트의 압축강도 시험방법), KS F 2408(콘크리트의 휨강도 시험방법)의 기준에 의거 시험을 실시하였으며, 그 결과를 다음 [표 1]에 나타내었다.For the mortar composition prepared in [Example 1], a test was conducted based on the standards of KS F 2405 (compressive strength test method of concrete) and KS F 2408 (bending strength test method of concrete), and the results are as follows [ It is shown in Table 1].
이상의 설명은 본 발명의 기술사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예 또는 도면들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예 또는 도면에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The above description is merely illustrative of the technical idea of the present invention, and those of ordinary skill in the art to which the present invention pertains will be able to make various modifications and variations without departing from the essential characteristics of the present invention. Accordingly, the embodiments or drawings disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain the technical idea, and the scope of the technical idea of the present invention is not limited by these embodiments or drawings. The scope of protection of the present invention should be interpreted by the following claims, and all technical ideas within the scope equivalent thereto should be interpreted as being included in the scope of the present invention.
100 : 블록 몸체
101 : 끼움돌기
102 : 속빈 끼움홈
103 : 측면끼움돌기
104 : 측면끼움홈100: block body 101: fitting protrusion 102: hollow fitting groove
103: side fitting protrusion 104: side fitting groove
Claims (5)
One or two or more fitting protrusions are formed integrally with the block body on an upper portion of the block body, and one or two or more hollow fitting grooves having the same shape as the one or more fitting protrusions are formed inside the block body, and the fitting protrusion As a mortar composition for forming a hollow Lego-type concrete block that can be firmly stacked up, down, left, and right without a cement mortar adhesion construction by being inserted into the hollow fitting groove and integrally bound without a gap, the mortar composition comprises natural fine aggregate and copper slag. Mix fine aggregate mixed at a weight ratio of 9: 1, ordinary cement and blast furnace slag powder at a weight ratio of 7: 3, and add waste glass powder obtained by pulverizing the waste glass at a ratio of 5% by weight of the amount of normal cement. Hollow Lego-type concrete block for civil engineering and building wall construction using industrial by-products, characterized in that the mixed cement is formed, the mixed cement and the mixed fine aggregate are mixed in a weight ratio of 1: 6 to 8, and water is mixed. Mortar composition for molding
상기 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물은 압축강도 18MPa 이상인 것을 특징으로 하는 산업부산물을 이용한 토목 및 건축 벽체 건설용 속빈 레고형 콘크리트 블록 성형용 모르타르 조성물
The method of claim 1,
The mortar composition for forming hollow Lego-type concrete blocks for civil engineering and building wall construction using the industrial by-products is a mortar composition for forming hollow Lego-type concrete blocks for civil engineering and building wall construction using industrial by-products, characterized in that the compressive strength is 18 MPa or more.
A concrete block molded from a mortar composition for forming a hollow Lego-type concrete block for civil engineering and building wall construction using an industrial by-product according to claim 1 or 2, wherein one or two are integrally formed with the block body on the upper part of the block body. Since more than one fitting protrusion is formed, and one or two or more hollow fitting grooves of the same shape as the one or more fitting protrusions are formed inside the block body, the fitting protrusion is inserted into the hollow fitting groove to be integrated without a gap. Hollow Lego concrete block, characterized in that it can be firmly laminated against external forces in all directions without cement mortar bonding.
상기 속빈 레고형 콘크리트 블록은 길이방향으로 복수개 인접 연결시 상기 하나 또는 둘 이상의 끼움돌기와 하나 또는 둘 이상의 속빈 끼움홈의 간격이 동일하게 형성되어 상기 속빈 레고형 콘크리트 블록 적층시 지그재그형으로 적층되더라도 틈새없이 일체화 결속되는 것을 특징으로 하는 속빈 레고형 콘크리트 블록
The method of claim 3,
When a plurality of hollow Lego-type concrete blocks are connected adjacently in the longitudinal direction, the one or more fitting protrusions and one or more hollow fitting grooves have the same spacing, so that even if the hollow Lego-type concrete blocks are stacked in a zigzag shape, there is no gap. Hollow Lego-type concrete block characterized by being integrated and bound
상기 속빈 레고형 콘크리트 블록은 길이방향 일측면에는 측면끼움돌기가 형성되고, 길이방향 타측면에는 측면끼움홈이 형성되어 상기 측면끼움돌기가 인접된 속빈 레고형 콘크리트 블록의 측면끼움홈에 삽입되어 일자형으로 적층시 길이방향에 대한 수직방향의 외력에 대하여 견고하게 적층되는 것을 특징으로 하는 속빈 레고형 콘크리트 블록The method of claim 3,
The hollow Lego-type concrete block has a side fitting protrusion formed on one side in the longitudinal direction, and a side fitting groove is formed on the other side in the longitudinal direction, and the side fitting protrusion is inserted into the side fitting groove of the adjacent hollow Lego-type concrete block. Hollow Lego-type concrete block, characterized in that it is firmly laminated against external force in the vertical direction with respect to the longitudinal direction when stacked with