KR20200144631A - Hot melt adhesive composition - Google Patents

Hot melt adhesive composition Download PDF

Info

Publication number
KR20200144631A
KR20200144631A KR1020190072464A KR20190072464A KR20200144631A KR 20200144631 A KR20200144631 A KR 20200144631A KR 1020190072464 A KR1020190072464 A KR 1020190072464A KR 20190072464 A KR20190072464 A KR 20190072464A KR 20200144631 A KR20200144631 A KR 20200144631A
Authority
KR
South Korea
Prior art keywords
melt adhesive
adhesive composition
hot
styrene
block copolymer
Prior art date
Application number
KR1020190072464A
Other languages
Korean (ko)
Other versions
KR102261405B1 (en
Inventor
홍사의
Original Assignee
(주) 대양산업
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 대양산업 filed Critical (주) 대양산업
Priority to KR1020190072464A priority Critical patent/KR102261405B1/en
Priority to PCT/KR2019/015960 priority patent/WO2020256235A1/en
Priority to CN201911180124.1A priority patent/CN112094608B/en
Publication of KR20200144631A publication Critical patent/KR20200144631A/en
Application granted granted Critical
Publication of KR102261405B1 publication Critical patent/KR102261405B1/en

Abstract

The present invention relates to a hot melt adhesive composition and, more specifically, to a hot melt adhesive composition for adhering pure cotton having excellent adhesion to pure cotton fibers and maintaining adhesion even when in contact with water, and to a hot melt adhesive pure cotton product comprising the same. The hot melt adhesive composition for adhering pure cotton comprises: an olefin resin; a hydrogenated styrene-based block copolymer; and a hydrocarbon-based adhesive resin.

Description

핫멜트 접착제 조성물{HOT MELT ADHESIVE COMPOSITION}Hot melt adhesive composition {HOT MELT ADHESIVE COMPOSITION}

본 발명은 핫멜트 접착제 조성물에 관한 것으로, 보다 구체적으로 순면 섬유에 우수한 접착력을 가지며, 물과 접촉하여도 접착력을 유지하는 효과가 뛰어난 순면 접착용 핫멜트 접착제 조성물 및 이를 포함하는 핫멜트 접착식 순면 제품에 관한 것이다.The present invention relates to a hot-melt adhesive composition, and more specifically, to a hot-melt adhesive composition for pure cotton adhesion having excellent adhesion to pure cotton fibers and maintaining adhesion even in contact with water, and a hot melt adhesive pure cotton product comprising the same .

핫멜트 접착제는 제품의 조립 및 포장 등 다양한 용도로 널리 이용되고 있으며, 일반적으로 150 ~ 250 ℃의 고온에서 가열하여 용융 상태로 기재에 적용한 후 냉각시킴에 따라 접착성능을 나타내어 간단한 공정으로 대량생산이 용이한 장점을 가진다.Hot melt adhesives are widely used for various purposes such as assembly and packaging of products. Generally, they are heated at a high temperature of 150 ~ 250 ℃, applied to a substrate in a molten state, and then cooled to show adhesive performance, making mass production easy with a simple process. It has one advantage.

이러한 핫멜트 접착제는 일회용 부직포 제품, 예를 들어 일회용 기저귀, 성인 요실금 제품 및 여성용 위생 제품 등에 오랫동안 적용되어왔다. 상기 일회용 부직포 제품은 폴리에틸렌 시트와 폴리프로필렌 부직포로 이루어져 있으며, 이러한 제품은 핫멜트 접착제를 이용하여 상기 시트와 부직포를 접착시켜 제조된다.Such hot melt adhesives have long been applied to disposable nonwoven products such as disposable diapers, adult incontinence products and feminine hygiene products. The disposable nonwoven product is made of a polyethylene sheet and a polypropylene nonwoven, and such a product is manufactured by bonding the sheet and the nonwoven using a hot melt adhesive.

한편, 최근 여성용 위생 제품인 생리대에서 발암물질이 검출되어 논란이 일면서, 친환경적이며 인체에 무해한 유기농 순면 생리대를 찾는 소비자가 대폭 증가하였다. 종래 유해물질을 다량 포함하는 생리대의 경우, 피부가 민감한 사용자에게 피부자극, 가려움증, 알레르기 및 피부염 등 각종 부작용을 유발할 뿐만 아니라, 생분해가 되지 않아 폐기 후 매립에 따른 환경오염을 야기하는 문제점이 있었다.Meanwhile, as carcinogens have been recently detected in sanitary napkins, which are feminine hygiene products, controversy has arisen, and as a result, the number of consumers seeking eco-friendly and harmless organic cotton sanitary napkins has increased significantly. In the case of a sanitary napkin containing a large amount of harmful substances in the related art, it causes various side effects such as skin irritation, itchiness, allergies and dermatitis to users with sensitive skin, and there is a problem that it is not biodegradable, causing environmental pollution due to landfill after disposal.

이에 반해, 유기농 순면 생리대는 유전자 변형을 거치지 않은 목화 솜 씨앗을 사용하여 합성비료, 살충제 및 농약 사용 없이 재배한 목화 솜을 생리대에 적용한 것으로서, 민감한 피부를 가진 사용자도 부작용 없이 사용 가능하며, 통기성, 촉감 및 착용감이 뛰어난 장점이 있다.On the other hand, organic cotton sanitary napkins are cotton pads grown without the use of synthetic fertilizers, pesticides, and pesticides, using cotton wool seeds that have not undergone genetic modification, and can be used by users with sensitive skin without side effects. It has the advantage of being excellent in touch and fit.

그러나, 상기 유기농 목화 솜, 즉 순면 섬유를 생리대에 적용하기 위해서는 순면 섬유를 부직포에 접착시켜야 하는데, 종래 핫멜트 접착제는 순면 섬유에 대한 접착력이 매우 약한 문제점이 있다.However, in order to apply the organic cotton wool, that is, the pure cotton fiber to the sanitary napkin, the pure cotton fiber must be bonded to the nonwoven fabric, but the conventional hot melt adhesive has a problem that the adhesion to the pure cotton fiber is very weak.

특히, 생리대를 사용함에 따라 순면 섬유 내부로 흡수된 수분으로 인하여 핫멜트 접착제가 접착력을 잃으면서, 순면 섬유와 부직포 간의 분리뿐만 아니라, 부직포와 시트 간의 분리를 야기한다.In particular, as the sanitary napkin is used, the hot melt adhesive loses adhesion due to moisture absorbed into the pure cotton fiber, causing not only separation between the pure cotton fiber and the nonwoven fabric, but also separation between the nonwoven fabric and the sheet.

이러한 문제점으로 인해 순면 섬유를 실제 생리대에 적용하기 어려우나, 현재까지 핫멜트 접착제의 낮은 순면 접착력 및 물에 대한 내구성 문제를 해결할 수 있는 방법이 없으며, 이를 대체할 접착제의 개발 또한 어려워 사용자들이 불편함을 호소하고 있는 실정이다.Due to these problems, it is difficult to apply pure cotton fibers to actual sanitary napkins, but there is no way to solve the problems of low pure cotton adhesion and water durability of hot melt adhesives, and it is difficult to develop adhesives to replace them, complaining of inconvenience to users. It is a situation.

이에, 순면 섬유에 대한 접착력이 우수하며, 물에 접촉하여도 접착력을 유지함에 따라 뛰어난 내구성을 갖는 접착제의 개발이 요구되고 있다.Accordingly, it is required to develop an adhesive having excellent durability as it has excellent adhesion to pure cotton fibers and maintains adhesion even in contact with water.

대한민국 공개특허공보 10-2018-0130522호 (2018.12.07.)Korean Patent Application Publication No. 10-2018-0130522 (2018.12.07.)

본 발명의 목적은 순면 섬유에 우수한 접착력을 나타내며, 물과 접촉하여도 높은 접착력을 유지하는 핫멜트 접착제 조성물 및 이를 포함하는 순면 제품을 제공하는 것이다.It is an object of the present invention to provide a hot melt adhesive composition that exhibits excellent adhesion to pure cotton fibers and maintains high adhesion even in contact with water, and a pure cotton product comprising the same.

상기 목적을 달성하기 위한 본 발명은 순면 접착용 핫멜트 접착제 조성물을 제공하며, 융점이 70 내지 120 ℃인 프로필렌 반복단위를 포함하는 올레핀계 수지; 수소화 스티렌계 블록 공중합체; 및 탄화수소계 점착성 수지를 포함한다.The present invention for achieving the above object provides a hot-melt adhesive composition for bonding a pure surface, an olefin-based resin comprising a propylene repeating unit having a melting point of 70 to 120 ℃; Hydrogenated styrene block copolymer; And a hydrocarbon-based adhesive resin.

본 발명의 일 양태에서, 상기 순면 접착용 핫멜트 접착제 조성물은 올레핀계 수지 1 내지 20 중량%, 수소화 스티렌계 블록 공중합체 5 내지 40 중량% 및 탄화수소계 점착성 수지 40 내지 80 중량%를 포함하는 것일 수 있다.In one aspect of the present invention, the hot melt adhesive composition for pure surface bonding may include 1 to 20% by weight of an olefin-based resin, 5 to 40% by weight of a hydrogenated styrene-based block copolymer, and 40 to 80% by weight of a hydrocarbon-based adhesive resin. have.

본 발명의 일 양태에서, 상기 올레핀계 수지는 프로필렌 반복단위 함량이 50 내지 95 몰%인 것일 수 있다.In one aspect of the present invention, the olefin-based resin may have a propylene repeating unit content of 50 to 95 mol%.

본 발명의 일 양태에서, 상기 올레핀계 수지 및 수소화 스티렌계 블록 공중합체의 중량비는 1 : 1 내지 2인 것일 수 있다.In one aspect of the present invention, the weight ratio of the olefin-based resin and the hydrogenated styrene-based block copolymer may be 1:1 to 2.

본 발명의 일 양태에서, 상기 수소화 스티렌계 블록 공중합체는 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체(SEBS), 스티렌-에틸렌-프로필렌-스티렌 블록 공중합체(SEPS), 스티렌-에틸렌-프로필렌 블록 공중합체(SEP), 스티렌-에틸렌-에틸렌-프로필렌-스티렌 블록 공중합체(SEEPS) 및 스티렌-부틸렌-부타디엔-스티렌 블록 공중합체(SBBS)에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 것일 수 있다.In one aspect of the present invention, the hydrogenated styrene-based block copolymer is a styrene-ethylene-butylene-styrene block copolymer (SEBS), a styrene-ethylene-propylene-styrene block copolymer (SEPS), and a styrene-ethylene-propylene block. Copolymer (SEP), styrene-ethylene-ethylene-propylene-styrene block copolymer (SEEPS), and styrene-butylene-butadiene-styrene block copolymer (SBBS) may be any one or a mixture of two or more selected from.

본 발명의 일 양태에서, 상기 탄화수소계 점착성 수지는 수첨 탄화수소계 점착성 수지인 것일 수 있다.In one aspect of the present invention, the hydrocarbon-based adhesive resin may be a hydrogenated hydrocarbon-based adhesive resin.

본 발명의 일 양태에서, 상기 순면 접착용 핫멜트 접착제 조성물은 연화점이 130 ℃ 이하인 것일 수 있다.In one aspect of the present invention, the hot-melt adhesive composition for pure surface bonding may have a softening point of 130° C. or less.

본 발명의 일 양태에서, 상기 순면 접착용 핫멜트 접착제 조성물은 윤활제, 왁스, 가소제 및 산화 방지제에서 선택되는 어느 하나 또는 둘 이상의 혼합물을 더 포함하는 것일 수 있다.In one aspect of the present invention, the hot-melt adhesive composition for pure surface bonding may further include any one or a mixture of two or more selected from lubricants, waxes, plasticizers, and antioxidants.

또한 본 발명은 제1기재; 제2기재; 및 상기 제1기재와 제2기재의 계면에 형성되는 순면 접착용 핫멜트 접착제 조성물;을 포함하는 일회용 제품을 제공한다.In addition, the present invention is a first base; Second description; And a hot melt adhesive composition for pure surface bonding formed at the interface between the first and second substrates.

본 발명의 일 양태에서, 상기 일회용 제품은 기저귀, 성인 요실금용 제품, 여성용 위생 제품 및 의료용 밴드에서 선택되는 것일 수 있다.In one aspect of the present invention, the disposable product may be selected from diapers, adult incontinence products, feminine hygiene products, and medical bands.

본 발명의 일 양태에서, 상기 제1기재 및 제2기재 중 적어도 어느 하나 이상이 순면 섬유인 것일 수 있다.In one aspect of the present invention, at least one or more of the first and second substrates may be pure cotton fibers.

또한 본 발명은 상기 일회용 제품의 제조방법을 제공하며, 융점이 70 내지 120 ℃인 프로필렌 반복단위을 포함하는 올레핀계 수지, 수소화 스티렌계 블록 공중합체 및 탄화수소계 점착성 수지를 포함하는 핫멜트 접착제 조성물을 가온하는 단계; 제1기재에 상기 가온된 핫멜트 접착제 조성물을 도포하는 단계; 및 상기 핫멜트 접착제 조성물이 도포된 제1기재 상에 제2기재를 적층하고 열압착하여 접착시키는 단계;를 포함한다.In addition, the present invention provides a method of manufacturing the disposable product, and heating a hot melt adhesive composition comprising an olefin resin, a hydrogenated styrene block copolymer, and a hydrocarbon-based adhesive resin comprising a propylene repeating unit having a melting point of 70 to 120 °C. step; Applying the heated hot melt adhesive composition to a first substrate; And laminating a second substrate on the first substrate to which the hot-melt adhesive composition is applied, and bonding by thermocompression bonding.

본 발명의 일 양태에서, 상기 핫멜트 접착제 조성물을 도포하는 단계는 80 내지 150 ℃에서 수행되는 것일 수 있다.In one aspect of the present invention, the step of applying the hot melt adhesive composition may be performed at 80 to 150 °C.

본 발명의 일 양태에서, 상기 일회용 제품은 순면 섬유를 포함하는 것일 수 있다.In one aspect of the present invention, the disposable product may include pure cotton fibers.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물은 순면 섬유에 우수한 접착력을 가질 뿐만 아니라, 물과 접촉하여도 높은 접착력을 유지하는 장점을 가진다.The hot-melt adhesive composition for pure cotton bonding according to the present invention not only has excellent adhesion to pure cotton fibers, but also has the advantage of maintaining high adhesion even in contact with water.

또한, 본 발명에 따른 순면 접착용 핫멜트 접착제 조성물을 포함하는 순면 제품은 기재 간의 분리 없이 우수한 내구성을 나타내는 장점이 있다.In addition, the pure cotton product including the hot melt adhesive composition for pure cotton bonding according to the present invention has the advantage of showing excellent durability without separation between substrates.

또한, 본 발명에 따른 순면 제품은 비교적 낮은 온도에서 간단한 공정만으로 제조가 가능한 장점이 있다.In addition, the pure cotton product according to the present invention has the advantage that it can be manufactured only by a simple process at a relatively low temperature.

이하 첨부된 도면들을 포함한 구체예 또는 실시예를 통해 본 발명을 더욱 상세히 설명한다. 다만 하기 구체예 또는 실시예는 본 발명을 상세히 설명하기 위한 하나의 참조일 뿐 본 발명이 이에 한정되는 것은 아니며, 여러 형태로 구현될 수 있다.Hereinafter, the present invention will be described in more detail through specific examples or examples including the accompanying drawings. However, the following specific examples or examples are only one reference for describing the present invention in detail, and the present invention is not limited thereto, and may be implemented in various forms.

본 발명의 명세서에서 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다.Technical terms and scientific terms used in the specification of the present invention have the meanings commonly understood by those of ordinary skill in the art, unless otherwise defined, and the present invention in the following description and accompanying drawings Descriptions of known functions and configurations that may unnecessarily obscure the gist of are omitted.

또한 본 발명의 명세서에서 사용되는 단수 형태는 문맥에서 특별한 지시가 없는 한 복수 형태도 포함하는 것으로 의도할 수 있다. In addition, the singular form used in the specification of the present invention may be intended to include the plural form unless otherwise indicated in the context.

또한 본 발명의 명세서에서 특별한 언급 없이 사용된 단위는 중량을 기준으로 하며, 일 예로 % 또는 비의 단위는 중량% 또는 중량비를 의미한다.In addition, units used in the specification of the present invention are based on weight, and as an example, the unit of% or ratio means weight% or weight ratio.

또한 본 발명의 명세서에서 사용되는 수치 범위는 하한치와 상한치와 그 범위 내에서의 모든 값, 정의되는 범위의 형태와 폭에서 논리적으로 유도되는 증분, 이중 한정된 모든 값 및 서로 다른 형태로 한정된 수치 범위의 상한 및 하한의 모든 가능한 조합을 포함한다. 일례로서 분자량이 100 내지 10,000이고, 구체적으로 500 내지 5,000으로 한정된 경우 500 내지 10,000 또는 100 내지 5,000의 수치범위도 본 발명의 명세서에 기재된 것으로 해석되어야 한다. 본 발명의 명세서에서 특별한 정의가 없는 한 실험 오차 또는 값의 반올림으로 인해 발생할 가능성이 있는 수치범위 외의 값 역시 정의된 수치범위에 포함된다.In addition, the numerical range used in the specification of the present invention includes the lower limit and the upper limit and all values within the range, increments that are logically derived from the shape and width of the defined range, all of the limited values, and the numerical ranges limited to different forms. Includes all possible combinations of upper and lower limits. As an example, when the molecular weight is 100 to 10,000, and specifically limited to 500 to 5,000, a numerical range of 500 to 10,000 or 100 to 5,000 should also be interpreted as described in the specification of the present invention. Unless otherwise defined in the specification of the present invention, values outside the numerical range that may occur due to experimental errors or rounding of values are also included in the defined numerical range.

또한 본 발명의 명세서에서, “포함한다”는 표현은 “구비한다”, “함유한다”, “가진다” 또는 “특징으로 한다” 등의 표현과 등가의 의미를 가지는 개방형 기재이며, 추가로 열거되어 있지 않은 요소, 재료 또는 공정을 배제하지 않는다. 또한 “실질적으로…로 구성된다”는 표현은 특정된 요소, 재료 또는 공정과 함께 열거되어 있지 않은 다른 요소, 재료 또는 공정이 발명의 적어도 하나의 기본적이고 신규한 기술적 사상에 허용할 수 없을 만큼의 현저한 영향을 미치지 않는 양으로 존재할 수 있는 것을 의미한다. 또한 “구성된다”는 표현은 기재된 요소, 재료 또는 공정만이 존재하는 것을 의미한다.In addition, in the specification of the present invention, the expression "includes" is an open-type substrate having a meaning equivalent to expressions such as "have", "include", "have" or "feature", and are further listed. It does not exclude elements, materials or processes that do not exist. Also, “Practically… The expression “consist of” means that the specified element, material or process does not have an unacceptably significant effect on at least one basic and novel technical idea of the invention by another element, material or process not listed. It means something that can exist as a quantity. Also, the expression “consisting of” means that only the described elements, materials or processes are present.

또한 본 발명의 명세서에서, 고분자의 “분자량”은 별다른 정의가 없는 한 “중량평균분자량”을 의미하며, 중량평균분자량 및 분자량 분포도(중량평균분자량/수평균분자량)는 젤투과 크로마토그래피(Gel Permeation Chromatography)로 측정된 것을 의미한다.In addition, in the specification of the present invention, the “molecular weight” of a polymer means “weight average molecular weight” unless otherwise defined, and the weight average molecular weight and molecular weight distribution (weight average molecular weight/number average molecular weight) are determined by gel permeation chromatography. It means what was measured by Chromatography.

순면 접착용 핫멜트 접착제 조성물Hot melt adhesive composition for pure surface bonding

본 발명의 제1양태는 순면에 뛰어난 접착력을 가지며, 물과 접촉하여도 접착력이 그대로 유지되는 순면 접착용 핫멜트 접착제 조성물에 관한 것이다.A first aspect of the present invention relates to a hot-melt adhesive composition for pure surface bonding that has excellent adhesion to pure cotton and maintains the adhesion even when contacted with water.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물은 융점이 70 내지 120℃인 프로필렌 반복단위을 포함하는 올레핀계 수지; 수소화 스티렌계 블록 공중합체; 및 탄화수소계 점착성 수지를 포함한다.The hot-melt adhesive composition for pure surface bonding according to the present invention includes an olefin-based resin comprising a propylene repeating unit having a melting point of 70 to 120°C; Hydrogenated styrene block copolymer; And a hydrocarbon-based adhesive resin.

본 발명에 따른 핫멜트 접착제 조성물은 상기의 올레핀계 수지를 수소화 스티렌계 블록 공중합체 및 탄화수소계 접착성 수지와 함께 사용함에 따라 순면에 대한 접착력이 현저히 향상되는 효과가 있다.The hot-melt adhesive composition according to the present invention has the effect of remarkably improving adhesion to pure cotton by using the olefin-based resin together with a hydrogenated styrene-based block copolymer and a hydrocarbon-based adhesive resin.

구체적으로, 상기 올레핀계 수지는 프로필렌 반복단위를 필수적으로 포함하며, 융점이 70 내지 120℃, 구체적으로 80 내지 110℃, 보다 구체적으로 90 내지 100℃일 수 있다. 상기 범위의 융점을 가짐에 따라 제조되는 핫멜트 접착제 조성물이 고온에서 혼화성이 우수하며, 순면 섬유를 포함한 다양한 기재에 대한 접착력이 뛰어난 효과가 있다.Specifically, the olefin-based resin essentially includes a propylene repeating unit, and may have a melting point of 70 to 120°C, specifically 80 to 110°C, and more specifically 90 to 100°C. The hot melt adhesive composition prepared by having a melting point in the above range has excellent miscibility at high temperatures, and has excellent adhesion to various substrates including pure cotton fibers.

상기 올레핀계 수지로서 바람직하게는, 상기 범위의 융점을 가지는 폴리프로필렌 호모중합체 및 에틸렌-프로필렌 공중합체에서 선택되는 어느 하나 또는 이들의 혼합물을 사용하는 것일 수 있다. 상기 폴리프로필렌 호모중합체로서 바람직하게 메탈로센 촉매 하에 제조된 폴리프로필렌(메탈로센 폴리프로필렌, Metallocene polypropylene, m-PP)일 수 있다.As the olefin-based resin, preferably, any one selected from a polypropylene homopolymer and an ethylene-propylene copolymer having a melting point in the above range, or a mixture thereof may be used. The polypropylene homopolymer may be preferably polypropylene (metallocene polypropylene, metallocene polypropylene, m-PP) prepared under a metallocene catalyst.

또한, 상기 올레핀계 수지는 구체적으로 프로필렌 반복단위를 고분자 주쇄에 포함하는 탄성 폴리프로필렌계 수지일 수 있으며, 바람직하게 상기 탄성 폴리프로필렌계 수지는 탄성 에틸렌-프로필렌 랜덤 공중합체일 수 있으나, 이에 제한되는 것은 아니다.In addition, the olefin resin may specifically be an elastic polypropylene resin including a propylene repeating unit in the polymer main chain, and preferably, the elastic polypropylene resin may be an elastic ethylene-propylene random copolymer, but is limited thereto. It is not.

또한, 상기 올레핀계 수지의 중량평균분자량으로서 제한하는 것은 아니나, 10,000 내지 1,000,000 g/mol, 구체적으로 20,000 내지 500,000 g/mol, 보다 구체적으로 50,000 내지 300,000 g/mol인 것일 수 있다.In addition, the weight average molecular weight of the olefin-based resin is not limited, but may be 10,000 to 1,000,000 g/mol, specifically 20,000 to 500,000 g/mol, and more specifically 50,000 to 300,000 g/mol.

상기 올레핀계 수지의 밀도는 25 ℃에서 0.92 g/cm3 이하, 바람직하게 0.91 g/cm3 이하일 수 있으며, 보다 바람직하게 0.905 g/cm3 이하일 수 있다. 상기 올레핀계 수지의 밀도의 하한은 0.80 g/cm3 이상일 수 있다.The density of the olefin-based resin may be 0.92 g/cm 3 or less, preferably 0.91 g/cm 3 or less, and more preferably 0.905 g/cm 3 or less at 25°C. The lower limit of the density of the olefin-based resin may be 0.80 g/cm 3 or more.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물의 일 양태에서, 상기 올레핀계 수지의 프로필렌 반복단위 함량은 50 내지 95 몰%, 구체적으로 65 내지 93 몰%, 보다 구체적으로 75 내지 90 몰%인 것일 수 있다. 상기 범위의 프로필렌 반복단위를 포함함에 따라 상기 올레핀계 수지와 수소화 스티렌계 블록 공중합체가 균질하게 혼합되며 순면에 대한 접착력이 현저히 향상될 수 있다. 특히 순면 섬유를 포함하는 기저귀 및 여성용 위생 제품 등에 접착제로 적용되어 제품을 이루는 기재와 순면 섬유간의 우수한 접착력 및 내구성을 부여하는 효과가 우수하다.In one aspect of the hot melt adhesive composition for pure surface bonding according to the present invention, the content of the propylene repeating unit of the olefin-based resin may be 50 to 95 mol%, specifically 65 to 93 mol%, more specifically 75 to 90 mol% have. By including the propylene repeating unit in the above range, the olefin-based resin and the hydrogenated styrene-based block copolymer are homogeneously mixed, and the adhesion to the pure cotton may be remarkably improved. In particular, it is applied as an adhesive to diapers including pure cotton fibers and feminine hygiene products, and has excellent effect of imparting excellent adhesion and durability between the base material forming the product and the pure cotton fibers.

또한, 상기 수소화 스티렌계 블록 공중합체는 공지의 스티렌계 블록 공중합체를 수소화한 것이라면 제한 없이 사용할 수 있으며, 구체적으로 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체(styrene-ethylene-butylene-styrene, SEBS), 스티렌-에틸렌-프로필렌-스티렌 블록 공중합체(styrene-ethylene-propylene-styrene, SEPS), 스티렌-에틸렌-프로필렌 블록 공중합체(styrene-ethylene-propylene, SEP), 스티렌-에틸렌-에틸렌-프로필렌-스티렌 블록 공중합체(styrene-ethylene-ethylene-propylene-styrene, SEEPS) 및 스티렌-부틸렌-부타디엔-스티렌 블록 공중합체(SBBS)에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있다. 상기 수소화 스티렌계 블록 공중합체의 바람직한 일 구체예로, 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체(styrene-ethylene-butylene-styrene, SEBS) 또는 스티렌-에틸렌-프로필렌-스티렌 블록 공중합체(styrene-ethylene-propylene-styrene, SEPS)일 수 있다.In addition, the hydrogenated styrene-based block copolymer may be used without limitation as long as it is hydrogenated of a known styrene-based block copolymer, and specifically, styrene-ethylene-butylene-styrene (SEBS) ), styrene-ethylene-propylene-styrene block copolymer (styrene-ethylene-propylene-styrene, SEPS), styrene-ethylene-propylene block copolymer (styrene-ethylene-propylene, SEP), styrene-ethylene-ethylene-propylene- It may be any one or a mixture of two or more selected from a styrene block copolymer (styrene-ethylene-ethylene-propylene-styrene, SEEPS) and a styrene-butylene-butadiene-styrene block copolymer (SBBS). As a preferred embodiment of the hydrogenated styrene-based block copolymer, styrene-ethylene-butylene-styrene block copolymer (styrene-ethylene-butylene-styrene, SEBS) or styrene-ethylene-propylene-styrene block copolymer (styrene- ethylene-propylene-styrene, SEPS).

또한, 상기 수소화 스티렌계 블록 공중합체 내 스티렌의 함량으로 특별히 제한하는 것은 아니나, 5 내지 50 중량%, 구체적으로 12 내지 35 중량%일 수 있다.In addition, although it is not particularly limited to the content of styrene in the hydrogenated styrene-based block copolymer, it may be 5 to 50% by weight, specifically 12 to 35% by weight.

상기의 수소화 스티렌계 블록 공중합체를 70 내지 120℃의 융점을 가지며 프로필렌 반복단위을 포함하는 올레핀계 수지 및 탄화수소계 점착성 수지와 함께 사용함에 따라, 순면에 대한 우수한 접착력뿐만 아니라 물에서도 우수한 접착력을 유지하는 유지력이 뛰어난 효과가 있다.As the hydrogenated styrene block copolymer has a melting point of 70 to 120°C and is used with an olefinic resin and a hydrocarbon-based adhesive resin containing a propylene repeating unit, it maintains excellent adhesion to pure cotton as well as water. It has an excellent retention effect.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물의 바람직한 일 양태에서, 상기 프로필렌 반복단위를 포함하는 올레핀계 수지는 에틸렌-프로필렌 공중합체 수지일 수 있으며, 바람직하게 에틸렌-프로필렌 탄성 공중합체 수지일 수 있고, 상기 수소화 스티렌계 블록 공중합체는 에틸렌을 반복단위로 포함하는 수소화 스티렌계 블록 공중합체일 수 있다. 상기 에틸렌-프로필렌 탄성 공중합체 수지와 상기 에틸렌을 반복단위로 포함하는 수소화 스티렌계 블록 공중합체가 에틸렌을 공통된 반복단위로 포함함에 따라 핫멜트 접착제 조성물은 우수한 상용성을 나타낼 수 있으며, 순면에 대한 접착력이 현저히 향상되어, 수분에 접촉되어도 순면 섬유와 부직포 간의 분리를 야기하지 않는다.In a preferred embodiment of the hot-melt adhesive composition for pure surface adhesion according to the present invention, the olefin-based resin including the propylene repeating unit may be an ethylene-propylene copolymer resin, preferably an ethylene-propylene elastomer resin, The hydrogenated styrene-based block copolymer may be a hydrogenated styrene-based block copolymer containing ethylene as a repeating unit. As the ethylene-propylene elastic copolymer resin and the hydrogenated styrene-based block copolymer containing ethylene as a repeating unit contain ethylene as a common repeating unit, the hot-melt adhesive composition can exhibit excellent compatibility, and the adhesion to pure cotton is It is remarkably improved and does not cause separation between the pure cotton fiber and the non-woven fabric even when contacted with moisture.

구체적으로, 기저귀와 같은 위생 제품은 수분 흡수체를 포함하는 제1기재와, 수분을 외부로 방출하지 않도록 방수 기능을 갖춘 제2기재로 구성되는데, 순면 섬유를 위생 제품에 적용할 경우, 착용 후 수분이 내부에 저장되면서 제품으로부터 순면 섬유가 분리되어 제품이 파손되고 그 기능을 상실하는 문제점이 있다. 이는 종래 위생 제품에 적용되는 핫멜트 접착제가 순면 섬유에 대한 낮은 접착력을 가질 뿐만 아니라, 수분과 접촉하여 접착력을 잃기 때문인데, 본 발명에 따른 핫멜트 접착제 조성물은 순면에 대한 접착력이 우수한 동시에 물에 대한 내구성이 향상되어, 장시간 착용하여도 수분에 의한 접착력 저하 없이 우수한 접착력을 유지하는 효과가 뛰어나다.Specifically, hygiene products such as diapers are composed of a first base material including a moisture absorber and a second base material with a waterproof function so as not to release moisture to the outside. When pure cotton fibers are applied to hygiene products, moisture after wearing There is a problem in that the pure cotton fiber is separated from the product while it is stored inside the product, and the product is damaged and its function is lost. This is because the hot melt adhesive applied to conventional hygiene products not only has low adhesion to pure cotton fibers, but also loses adhesion due to contact with moisture.The hot melt adhesive composition according to the present invention has excellent adhesion to pure cotton and durability against water This is improved, and even if worn for a long time, the effect of maintaining excellent adhesion without deterioration due to moisture is excellent.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물의 일 양태에서, 올레핀계 수지 및 수소화 스티렌계 블록 공중합체의 중량비는 1 : 0.1 내지 10, 구체적으로 1 : 1 내지 5, 보다 구체적으로 1 : 1 내지 2인 것일 수 있다. 상기 범위로 올레핀계 수지와 수소화 스티렌계 블록 공중합체를 사용함에 따라, 우수한 박리강도를 가지는 동시에 물에 대한 내구성이 현저히 향상되어 수분과 접촉하여도 우수한 접착력을 나타낸다. 이에 따라, 상기의 순면 제품뿐만 아니라, 방수성을 요하는 다양한 제품에 접착제로 사용될 수 있는 장점이 있다.In one aspect of the hot-melt adhesive composition for pure surface adhesion according to the present invention, the weight ratio of the olefin-based resin and the hydrogenated styrene-based block copolymer is 1: 0.1 to 10, specifically 1: 1 to 5, more specifically 1: 1 to 2 It can be. As the olefin-based resin and the hydrogenated styrene-based block copolymer are used in the above range, excellent peel strength and durability against water are remarkably improved, thereby exhibiting excellent adhesion even in contact with moisture. Accordingly, there is an advantage that it can be used as an adhesive for not only the pure cotton products but also various products requiring waterproofness.

상기 탄화수소계 점착성 수지는 핫멜트 접착제 조성물에 점착성을 부여하는 것으로서, 예를 들어 방향족 탄화수소계 수지, 지방족 탄화수소계 수지, 고리식 탄화수소계 수지, 테르펜 및 이를 반복단위로 포함하는 테르펜계 공중합체 수지 등을 들 수 있으며, 바람직하게는 공지의 수소첨가 반응을 통해 제조된 수첨 탄화수소계 수지일 수 있다.The hydrocarbon-based adhesive resin is to impart tackiness to the hot melt adhesive composition, for example, an aromatic hydrocarbon-based resin, an aliphatic hydrocarbon-based resin, a cyclic hydrocarbon-based resin, a terpene, and a terpene-based copolymer resin including the same as a repeating unit. And, preferably, a hydrogenated hydrocarbon-based resin prepared through a known hydrogenation reaction.

상기의 수첨 탄화수소계 점착성 수지를 사용하는 경우, 올레핀계 수지 및 수소화 스티렌계 블록 공중합체와 상용성이 우수하며, 순면 접착력 및 물에 대한 내구성이 동시에 향상되며, 특이취가 발생하지 않는 효과가 뛰어나다.When the above-described hydrogenated hydrocarbon-based adhesive resin is used, it is excellent in compatibility with olefin-based resins and hydrogenated styrene-based block copolymers, and the net surface adhesion and durability against water are improved at the same time, and the effect of not generating a peculiar odor is excellent. .

또한, 상기 수첨 탄화수소계 점착성 수지를 본 발명의 올레핀계 수지 및 수소화 스티렌계 블록 공중합체와 함께 용융시킨 후 분사하여 기재에 도포하는 경우, 필라멘트의 형성 없이 기재에 고르게 도포되는 효과가 우수하여, 순면 접착용 핫멜트 접착제 조성물의 도포 균일성을 현저히 향상시킨다.In addition, when the hydrogenated hydrocarbon-based adhesive resin is melted together with the olefin-based resin and hydrogenated styrene-based block copolymer of the present invention, sprayed and applied to a substrate, the effect of being evenly applied to the substrate without forming a filament is excellent. Remarkably improves the coating uniformity of the hot melt adhesive composition for adhesion.

상기 수첨 탄화수소계 점착성 수지의 바람직한 예로, 스티렌계 단량체 및 다환 방향족 단량체를 반복단위로 포함하는 탄화수소계 수지를 수첨하여 얻어진 것이 바람직할 수 있다. 구체적인 일 예로, 스티렌계 단량체로는 스티렌 또는 메틸스티렌일 수 있으며, 다환 방향족 단량체로는 인덴일 수 있다. 예를 들어, 메틸스티렌 및 인덴 공중합체 수지를 수첨하여 얻어진 수첨 탄화수소계 수지가 바람직한 점착성 수지로 예시될 수 있다.As a preferred example of the hydrogenated hydrocarbon-based adhesive resin, it may be preferably obtained by hydrogenating a hydrocarbon-based resin containing a styrene-based monomer and a polycyclic aromatic monomer as a repeating unit. As a specific example, the styrene-based monomer may be styrene or methylstyrene, and the polycyclic aromatic monomer may be indene. For example, a hydrogenated hydrocarbon-based resin obtained by hydrogenating a methylstyrene and indene copolymer resin may be exemplified as a preferred adhesive resin.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물의 일 양태에서, 상기 순면 접착용 핫멜트 접착제 조성물은 올레핀계 수지 1 내지 20 중량%, 수소화 스티렌계 블록 공중합체 5 내지 40 중량% 및 탄화수소계 점착성 수지 40 내지 80 중량%일 수 있다. 상기 핫멜트 접착제 조성물은 구체적으로 올레핀계 수지 2 내지 15 중량%, 수소화 스티렌계 블록 공중합체 10 내지 30 중량% 및 탄화수소계 점착성 수지 50 내지 70 중량%를 포함하는 것일 수 있으나, 이에 제한되는 것은 아니다.In one aspect of the hot-melt adhesive composition for pure surface bonding according to the present invention, the hot-melt adhesive composition for pure surface bonding is 1 to 20% by weight of an olefin resin, 5 to 40% by weight of a hydrogenated styrene-based block copolymer, and 40 to 40% by weight of a hydrocarbon-based adhesive resin. It may be 80% by weight. The hot melt adhesive composition may specifically include 2 to 15% by weight of an olefin-based resin, 10 to 30% by weight of a hydrogenated styrene-based block copolymer, and 50 to 70% by weight of a hydrocarbon-based adhesive resin, but is not limited thereto.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물의 일 양태에서, 상기 순면 접착용 핫멜트 접착제 조성물은 연화점이 130℃ 이하, 구체적으로 110℃ 이하, 보다 구체적으로 75 내지 105℃인 것일 수 있으나, 이에 제한되는 것은 아니다. 종래 핫멜트 접착제 조성물은 일반적으로 150 내지 250℃의 고온에서 용융시켜 기재에 적용하는 것과 비교하여, 본 발명에 따른 핫멜트 접착제 조성물은 상기 범위의 연화점을 가짐에 따라 150℃ 이하의 비교적 낮은 온도에서 용융시켜 접착 공정이 수행될 수 있어 기재의 손상을 방지하는 효과가 있다.In one aspect of the hot-melt adhesive composition for pure surface bonding according to the present invention, the hot-melt adhesive composition for pure surface bonding may have a softening point of 130° C. or less, specifically 110° C. or less, and more specifically 75 to 105° C., but is limited thereto. It is not. Compared to the conventional hot melt adhesive composition generally melted at a high temperature of 150 to 250°C and applied to a substrate, the hot melt adhesive composition according to the present invention is melted at a relatively low temperature of 150°C or less as it has a softening point in the above range. Since the bonding process can be performed, there is an effect of preventing damage to the substrate.

또한, 본 발명에 따른 순면 접착용 핫멜트 접착제 조성물은 60 내지 90℃의 온도 범위에서는 UCST(Upper Critical Solution Temperature)를 가질 수 있으며, 바람직하게 60 내지 80℃의 온도 범위에서 UCST를 가질 수 있다. 상기 UCST 이하의 온도에서 혼화성이 낮아지면서 핫멜트 접착제 조성물이 미세 상분리된 상태로 존재할 수 있다. 상기 미세 상분리된 핫멜트 접착제 조성물은 상온에서 안정된 미세 상분리 구조를 유지할 수 있으며, 미세 상분리 구조는 순면 섬유와 부직포 간의 우수한 접착성을 바람직하게 유도할 수 있다.In addition, the hot-melt adhesive composition for pure surface bonding according to the present invention may have an Upper Critical Solution Temperature (UCST) in a temperature range of 60 to 90°C, and may have a UCST in a temperature range of 60 to 80°C. As the miscibility is lowered at a temperature below the UCST, the hot melt adhesive composition may be present in a state of fine phase separation. The fine phase-separated hot melt adhesive composition may maintain a stable fine phase-separated structure at room temperature, and the fine phase-separated structure may preferably induce excellent adhesion between the pure cotton fiber and the nonwoven fabric.

본 발명에 따른 순면 접착용 핫멜트 접착제 조성물의 일 양태에서, 상기 순면 접착용 핫멜트 접착제 조성물은 공지의 윤활제, 왁스, 가소제 및 산화 방지제에서 선택되는 어느 하나 또는 둘 이상의 혼합물을 더 포함할 수 있다.In one aspect of the hot melt adhesive composition for pure surface bonding according to the present invention, the hot melt adhesive composition for pure surface bonding may further include any one or a mixture of two or more selected from known lubricants, waxes, plasticizers, and antioxidants.

상기 윤활제로서 제한하는 것은 아니나, 구체적으로 예를 들면 파라핀계 오일 및 나프텐계 오일 등을 들 수 있으며 바람직하게 파라핀 오일일 수 있다. 상기 윤활제는 순면 접착용 핫멜트 접착제 조성물 총 중량에 대하여 1 내지 30 중량%로 포함될 수 있으며, 바람직하게 10 내지 30 중량%로 포함될 수 있으나 이에 제한받지 않는다.Although not limited as the lubricant, specifically, for example, paraffinic oil and naphthenic oil may be mentioned, and preferably paraffinic oil. The lubricant may be included in an amount of 1 to 30% by weight, preferably 10 to 30% by weight, based on the total weight of the hot-melt adhesive composition for pure surface bonding, but is not limited thereto.

또한, 상기 왁스로서 제한하는 것은 아니나, 구체적으로 예를 들면 파라핀 왁스 및 미세결정질 왁스(microcrystalline wax) 등을 들 수 있으며 바람직하게 파라핀 왁스일 수 있다. 상기 왁스는 순면 접착용 핫멜트 접착제 조성물 총 중량에 대하여 1 내지 10 중량%로 포함될 수 있으며, 바람직하게 2 내지 8 중량%로 포함될 수 있으나 이에 제한받지 않는다.In addition, the wax is not limited, but specifically, for example, paraffin wax, microcrystalline wax, and the like may be exemplified, and paraffin wax may be preferred. The wax may be included in an amount of 1 to 10% by weight, preferably 2 to 8% by weight, based on the total weight of the hot melt adhesive composition for pure surface bonding, but is not limited thereto.

또한, 상기 가소제로서 제한하는 것은 아니나, 구체적으로 예를 들면 글리세린, 글리세린디아세테이트, 펜타에리쓰리톨, 솔비톨 및 에틸렌글리콜 등을 들 수 있으며, 상기 순면 접착용 핫멜트 접착제 조성물 총 중량에 대하여 1 내지 10 중량%로 포함될 수 있으나 이에 제한받지 않는다.In addition, the plasticizer is not limited, but specifically, for example, glycerin, glycerin diacetate, pentaerythritol, sorbitol, and ethylene glycol, etc., and 1 to 10 based on the total weight of the hot-melt adhesive composition for pure surface bonding. It may be included in weight percent, but is not limited thereto.

또한, 상기 산화 방지제로서 제한하는 것은 아니나, 구체적으로 예를 들면 티오에스테르, 포스페이트, 방향족 아민, 힌더드 페놀, 테트라키스(메틸렌-3-(3′,5′-디-t-부틸-4′-하이드록시페닐)프로피오네이트)메탄, 2,2'-에틸리덴 비스(4,6-디-tert-부틸 페놀), 1,1-트리스(2-메틸-4-하이드록시-5-t-부틸 페닐) 부탄, 1,3,5-트리메틸-2,4,6-트리스(3,5-tert-부틸-4-하이드록시벤질) 벤젠, 디라우릴 티오디프로피오네이트, 펜타에리트리톨 테트라키스(β-라우릴 티오프로피오네이트) 폴리포스페이트 및 티오 아인산염 등을 들 수 있으며, 상기 순면 접착용 핫멜트 접착제 조성물 총 중량에 대하여 1 내지 5 중량%로 포함될 수 있으나 이에 제한받지 않는다.In addition, the antioxidant is not limited, but specifically, for example, thioester, phosphate, aromatic amine, hindered phenol, tetrakis (methylene-3-(3',5'-di-t-butyl-4' -Hydroxyphenyl)propionate)methane, 2,2'-ethylidene bis(4,6-di-tert-butyl phenol), 1,1-tris(2-methyl-4-hydroxy-5-t) -Butyl phenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5-tert-butyl-4-hydroxybenzyl) benzene, dilauryl thiodipropionate, pentaerythritol tetra Kiss (β-lauryl thiopropionate) polyphosphate and thiophosphite may be mentioned, and may be included in an amount of 1 to 5% by weight based on the total weight of the hot-melt adhesive composition for pure surface bonding, but is not limited thereto.

핫멜트 접착제 조성물을 포함하는 일회용 제품Disposable product containing hot melt adhesive composition

또한 본 발명의 제2양태는 상기의 순면 접착용 핫멜트 접착제 조성물을 포함하는 일회용 제품을 제공한다.In addition, a second aspect of the present invention provides a disposable product comprising the hot-melt adhesive composition for pure surface bonding.

상기 일회용 제품은 제1기재; 제2기재; 및 상기 제1기재와 제2기재의 계면에 형성되는 핫멜트 접착제 조성물;을 포함한다.The disposable product includes a first substrate; Second description; And a hot melt adhesive composition formed at the interface between the first and second substrates.

상기 제1기재 및 제2기재는 일회용 제품에 사용되는 기재라면 제한 없이 사용될 수 있으며, 구체적으로 예를 들면 신품 및 재생 크라프트(craft), 고밀도 및 저밀도 크라프트, 칩보드(chipboard), 폴리에틸렌, 마일러(mylar), 폴리프로필렌, 폴리비닐리덴 클로라이드 및 에틸렌 비닐아세테이트 등을 들 수 있다.The first and second substrates may be used without limitation as long as they are used for disposable products, and specifically, for example, new and regenerated kraft, high density and low density kraft, chipboard, polyethylene, mylar (mylar), polypropylene, polyvinylidene chloride, ethylene vinyl acetate, and the like.

또한, 상기 일회용 제품으로서 예를 들면 산업 작업복, 의료용 가운, 마스크, 배변 훈련용 팬츠, 수영복, 기저귀, 성인 요실금용 제품, 여성용 위생 제품 및 의료용 밴드 등을 들 수 있으며, 바람직하게는 순면 섬유를 포함하는 기저귀, 성인 요실금용 제품, 여성용 위생 제품 및 의료용 밴드에서 선택되는 것일 수 있다.In addition, as the disposable products, for example, industrial work clothes, medical gowns, masks, bowel training pants, swimsuits, diapers, adult incontinence products, feminine hygiene products and medical bands, and the like, preferably include pure cotton fibers. It may be selected from diapers, adult incontinence products, feminine hygiene products, and medical bands.

본 발명의 일 양태에서, 상기 제1기재 및 제2기재 중 적어도 어느 하나 이상은 순면 섬유인 것일 수 있다.In an aspect of the present invention, at least one or more of the first and second substrates may be pure cotton fibers.

상기의 일회용 제품 중에서도 특히 기저귀, 성인 요실금용 제품, 여성용 위생 제품 및 의료용 밴드는 국소부위의 피부와 직접 접촉함에 따라 민감한 사용자의 경우 피부자극, 가려움증, 알레르기 및 피부염 등 각종 부작용을 유발하는 문제점이 있다.Among the above disposable products, especially diapers, products for adult incontinence, feminine hygiene products, and medical bands, there are problems that cause various side effects such as skin irritation, itching, allergies, and dermatitis in the case of sensitive users as they directly contact the skin of the local area. .

그러나, 본 발명의 순면 접착용 핫멜트 접착제 조성물을 포함하는 일회용 제품은 상기 순면 섬유를 기재로 포함함에 따라 우수한 통기성을 나타낼 뿐만 아니라, 사용자에게 우수한 촉감 및 착용감을 부여할 수 있다.However, the disposable product including the hot-melt adhesive composition for pure cotton bonding of the present invention may exhibit excellent breathability as well as provide excellent touch and fit to a user by including the pure cotton fiber as a substrate.

핫멜트 접착제 조성물을 이용하는 일회용 제품의 제조방법Method for manufacturing disposable products using hot melt adhesive composition

또한 본 발명의 제3양태는 상기의 순면 접착용 핫멜트 접착제 조성물을 이용한 일회용 제품의 제조방법을 제공한다. 보다 구체적으로, 융점이 70 내지 120℃인 프로필렌 반복단위을 포함하는 올레핀계 수지, 수소화 스티렌계 블록 공중합체 및 탄화수소계 점착성 수지를 포함하는 핫멜트 접착제 조성물을 가온하는 단계; 제1기재에 상기 가온된 핫멜트 접착제 조성물을 도포하는 단계;및 상기 핫멜트 접착제 조성물이 도포된 제1기재 상에 제2기재를 적층하고 열압착하여 접착시키는 단계;를 포함하는 일회용 제품의 제조방법에 관한 것이다.In addition, a third aspect of the present invention provides a method of manufacturing a disposable product using the hot melt adhesive composition for pure surface bonding. More specifically, heating a hot-melt adhesive composition comprising an olefin-based resin, a hydrogenated styrene-based block copolymer, and a hydrocarbon-based adhesive resin including a propylene repeating unit having a melting point of 70 to 120°C; Applying the heated hot-melt adhesive composition to a first substrate; And laminating a second substrate on the first substrate to which the hot-melt adhesive composition is applied, and bonding by thermocompression bonding; In a method for manufacturing a disposable product comprising About.

상기 핫멜트 접착제 조성물의 가온 단계는 상기 핫멜트 접착제 조성물의 연화점 이상으로 가온하여 균일한 용액을 제조하는 단계이다. 균일한 용액을 제조하는 단계를 구체적으로 예를 들면, 상기 핫멜트 접착제 조성물을 니더 루더, 압출기, 믹싱 롤, 밴버리 믹서 등 공지의 혼합 장치를 사용하여 80 내지 160 ℃에서 균일하게 혼합하는 것일 수 있으나 이에 제한하는 것은 아니다.The heating step of the hot melt adhesive composition is a step of preparing a uniform solution by heating above the softening point of the hot melt adhesive composition. Specifically, for example, the step of preparing a uniform solution may be uniformly mixing the hot melt adhesive composition at 80 to 160°C using a known mixing device such as a kneader luder, an extruder, a mixing roll, and a Banbury mixer. It is not limiting.

이어서, 상기 핫멜트 접착제 조성물 도포 단계는 앞서 혼합된 핫멜트 접착제 조성물을 연화점 이상으로 가열하여 용융 상태로 제1기재에 도포하는 단계이다. 구체적으로, 상기 도포하는 단계는 80 내지 180℃, 구체적으로 130 내지 160℃에서 수행되는 것일 수 있다.Subsequently, in the step of applying the hot-melt adhesive composition, the hot-melt adhesive composition is heated above the softening point and applied to the first substrate in a molten state. Specifically, the applying step may be performed at 80 to 180°C, specifically 130 to 160°C.

또한, 상기 도포 방법으로 구체적인 예를 들면, 상기 온도 범위에서 용융된 핫멜트 접착제 조성물을 공지의 분사 장치 또는 코팅 장치를 이용하여 기재에 도포하는 것일 수 있다. 보다 구체적으로, 분사 장치를 이용하여 핫멜트 접착제 조성물을 기재 상에 분사하는 비접촉식 방법 또는 슬롯 코터 등을 이용하여 기재 상에 핫멜트 접착제 조성물을 도포하는 접촉식 방법을 들 수 있다. In addition, as a specific example of the coating method, a hot melt adhesive composition melted in the temperature range may be applied to a substrate using a known spraying device or a coating device. More specifically, a non-contact method of spraying the hot-melt adhesive composition onto the substrate using a spraying device, or a contact method of applying the hot-melt adhesive composition onto the substrate using a slot coater or the like may be mentioned.

바람직한 일 양태로, 본 발명에 따른 핫멜트 접착제 조성물은 비접촉식 방법으로 코팅될 수 있으며 비접촉식 방법으로 기재 상에 분사함으로써 기재 상에 균일한 접착층을 형성할 수 있다. 비접촉식 방식의 구체적으로 예로는 공지의 분사장치, 예를 들어 Nordson 사의 분사 장치를 이용하여 노즐로부터 용융시킨 핫멜트 접착제 조성물을 분사하여 기재에 도포하는 것일 수 있으나, 상기 방법으로 제한되는 것은 아니다. 한편 도포 균일성이 떨어지는 핫멜트 접착제 조성물의 경우 접촉식 방식으로 기재 상에 도포되어 접착층을 형성하는 것도 본 발명에 따른 일 양태에 포함된다.In a preferred embodiment, the hot melt adhesive composition according to the present invention may be coated by a non-contact method, and a uniform adhesive layer may be formed on the substrate by spraying on the substrate by a non-contact method. A specific example of the non-contact method may be spraying a hot-melt adhesive composition melted from a nozzle using a known spraying device, for example, a spray device of Nordson, and applying it to a substrate, but is not limited thereto. On the other hand, in the case of a hot melt adhesive composition having poor application uniformity, it is also included in one aspect according to the present invention to form an adhesive layer by being applied on a substrate in a contact method.

이어서, 상기 핫멜트 접착제 조성물이 도포된 제1기재 상에 제2기재를 적층하고 열압착하여 접착시키는 단계는, 핫멜트 접착제 조성물을 제1기재와 제2기재의 계면에 적용하여 이들을 접착시키는 단계이다. 구체적으로, 상기 제1기재 상에 용융 상태로 도포된 핫멜트 접착제 조성물에 제2기재를 적층한 후 냉각시킴으로써, 핫멜트 접착제 조성물이 경화되어 두 기재가 접착될 수 있다. 또는, 상기 적층 이후에 공지의 압착롤 등을 이용하여 압착시킨 후 냉각하여 기재를 접착시킬 수 있으나, 이에 제한되는 것은 아니다.Subsequently, the step of laminating a second base material on the first base material to which the hot-melt adhesive composition is applied and bonding by heat compression is a step of applying the hot-melt adhesive composition to the interface between the first base material and the second base material to adhere them. Specifically, the hot-melt adhesive composition is cured and the two substrates can be bonded by laminating the second substrate to the hot-melt adhesive composition applied in a molten state on the first substrate and then cooling it. Alternatively, after the lamination, the substrate may be adhered by compressing it using a known press roll or the like and then cooling it, but is not limited thereto.

본 발명에 따른 일회용 제품의 제조방법의 일 양태에서, 상기의 제조방법으로 제조된 일회용 제품은 순면 섬유를 포함하는 것일 수 있다. 구체적으로, 제1기재 및 제2기재 중 적어도 어느 하나 이상이 순면 섬유인 순면 일회용 제품일 수 있다.In one aspect of the method for manufacturing a disposable product according to the present invention, the disposable product manufactured by the above manufacturing method may include pure cotton fibers. Specifically, at least one of the first substrate and the second substrate may be a pure cotton disposable product including pure cotton fibers.

또한, 본 발명에 따른 순면 접착용 핫멜트 접착제 조성물은 예를 들어 핫멜트 도공법, T 다이법, 인플레이션법, 캘린더 성형법 및 라미네이션법 등을 이용하여 시트상이나 필름상의 형상으로 제조한 후, 가열 용융하여 사용할 수 있다.In addition, the hot-melt adhesive composition for pure surface bonding according to the present invention is prepared in a sheet or film shape using, for example, a hot melt coating method, a T-die method, an inflation method, a calendering method, and a lamination method, and then used by heating and melting. I can.

이하 실시예 및 비교예를 바탕으로 본 발명을 더욱 상세히 설명한다. 다만 하기 실시예 및 비교예는 본 발명을 더욱 상세히 설명하기 위한 하나의 예시일 뿐, 본 발명이 하기 실시예 및 비교예에 의해 제한되는 것은 아니다. Hereinafter, the present invention will be described in more detail based on Examples and Comparative Examples. However, the following Examples and Comparative Examples are only one example for describing the present invention in more detail, and the present invention is not limited by the following Examples and Comparative Examples.

(평가)(evaluation)

1. 수상 내 접착성1. Adhesion in water

제조된 일회용 순면 제품을 물 500 mL에 1 시간 침지한 후 꺼내어 순면 시트의 박리정도를 육안으로 관찰하여 점수로 평가하였다. 총 100 개의 일회용 순면 제품을 시험하여, 박리되지 않은 일회용 순면 제품의 개수를 나타내었다.The prepared disposable cotton product was immersed in 500 mL of water for 1 hour, then taken out, and the degree of peeling of the cotton sheet was visually observed and evaluated by score. A total of 100 disposable pure cotton products were tested, and the number of disposable pure cotton products that were not peeled off was indicated.

2. 박리강도2. Peel strength

인장강도시험기를 이용하여 25℃에서 박리강도를 측정하였다. 인장강도시험기의 한 쪽 지그를 제조된 일회용 순면 제품에 고정시킨 상태에서 지그를 300 mm/min의 속력으로 잡아당겨 가해지는 박리강도를 10 회 반복 측정하여 평균값을 구하였다. Peel strength was measured at 25°C using a tensile strength tester. The average value was obtained by repeatedly measuring the peel strength applied by pulling the jig at a speed of 300 mm/min while fixing one jig of the tensile strength tester to the manufactured disposable cotton product.

3. 도포 균일성3. Application uniformity

핫멜트 접착제 조성물의 스프레이 도포 시, 핫멜트 접착제 조성물이 기재에 균일하게 도포되는지 여부를 육안으로 관찰하여 도포 균일성을 평가하였다. 이 때, 총 100 개의 일회용 순면 제품을 제조하여, 스프레이 공정 시 필라멘트의 형성 없이 핫멜트 접착제 조성물이 기재에 균일하게 도포된 일회용 순면 제품의 개수를 나타내었다.When spray-coating the hot-melt adhesive composition, whether or not the hot-melt adhesive composition was uniformly applied to the substrate was visually observed to evaluate the coating uniformity. At this time, a total of 100 disposable pure cotton products were manufactured, and the number of disposable pure cotton products in which the hot melt adhesive composition was uniformly applied to the substrate without forming a filament during the spraying process was shown.

하기 실시예 1 내지 7 및 비교예 1 내지 4의 핫멜트 접착제 조성물의 구체적인 함량을 하기 표 1에 나타내었다.Specific contents of the hot melt adhesive composition of Examples 1 to 7 and Comparative Examples 1 to 4 are shown in Table 1 below.

[실시예 1][Example 1]

융점이 100℃이고 중량평균분자량이 78,910 g/mol(분자량 분포도: 8.24)인 메탈로센-폴리프로필렌(m-PP) 7 중량부, 중량평균분자량이 68,999 g/mol(분자량 분포도: 3.45)이며 스티렌 함량이 30.5 중량%인 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체(SEBS) 10 중량부 및 방향족 변성 테르펜 수지(YS POLYSTER T145, 야스하라 케미컬) 56 중량부, 파라핀 왁스(Shell GTL Sarawax SX 105, EVONIK) 5 중량부, 파라핀 오일(Kixx LP 600, GS 칼텍스) 21 중량부 및 산화 방지제(테트라키스(메틸렌-3-(3′,5′-디-t-부틸-4′-하이드록시페닐)프로피오네이트)메탄) 1 중량부를 Brabender mixer에 첨가하여 160℃에서 2 시간 혼합하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 90℃인 것을 확인하였다.7 parts by weight of metallocene-polypropylene (m-PP) with a melting point of 100°C and a weight average molecular weight of 78,910 g/mol (molecular weight distribution: 8.24), a weight average molecular weight of 68,999 g/mol (molecular weight distribution: 3.45) 10 parts by weight of styrene-ethylene-butylene-styrene block copolymer (SEBS) having a styrene content of 30.5% by weight and 56 parts by weight of an aromatic modified terpene resin (YS POLYSTER T145, Yasuhara Chemical), paraffin wax (Shell GTL Sarawax SX 105) , EVONIK) 5 parts by weight, paraffin oil (Kixx LP 600, GS Caltex) 21 parts by weight and an antioxidant (tetrakis (methylene-3-(3′,5′-di-t-butyl-4′-hydroxyphenyl)) ) 1 part by weight of propionate) methane) was added to a Brabender mixer and mixed at 160° C. for 2 hours to prepare a hot melt adhesive composition for bonding pure cotton, and it was confirmed that the softening point of the prepared composition was 90° C.

이어서, 폴리에틸렌 필름과 폴리프로필렌 스펀본드가 순차적으로 적층 및 접착된 기재 상에 제조된 순면 접착용 핫멜트 접착제 조성물을 분사노즐을 통해 130℃에서 용융 상태로 스프레이(Nordson) 도포한 후, 순면 시트를 적층하고 압착롤로 접착시켜 일회용 순면 제품을 제조하였다. 제조된 제품의 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.Subsequently, a hot melt adhesive composition for pure cotton bonding prepared on a substrate in which a polyethylene film and a polypropylene spunbond were sequentially laminated and bonded was applied by spraying (Nordson) in a melted state at 130°C through a spray nozzle, and then the pure cotton sheet was laminated. And adhered with a pressing roll to prepare a disposable pure cotton product. Table 2 shows the evaluation of adhesion, peel strength, and coating uniformity of the prepared product.

[실시예 2][Example 2]

상기 실시예 1에서 방향족 변성 테르펜 수지를 방향족 탄화수소 수지(HIKOTACK P-90, 코오롱인더스트리)로 대체한 것을 제외하고는 실시예 1과 동일하게 실시하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 95℃인 것을 확인하였다. 이어서, 실시예 1과 동일한 방법으로 일회용 순면 제품을 제조하여 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.A hot melt adhesive composition for pure surface bonding was prepared in the same manner as in Example 1, except that the aromatic modified terpene resin in Example 1 was replaced with an aromatic hydrocarbon resin (HIKOTACK P-90, Kolon Industries). It was confirmed that the softening point of was 95°C. Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 1, and the adhesion in the water phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[실시예 3][Example 3]

상기 실시예 1에서 방향족 변성 테르펜 수지를 수첨 탄화수소계 점착성 수지인 수첨 메틸스티렌-인덴 공중합체 수지(SUKOREZ SU-100S, 코오롱인더스트리)로 대체한 것을 제외하고는 실시예 1과 동일하게 실시하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 94℃인 것을 확인하였다. 이어서, 실시예 1과 동일한 방법으로 일회용 순면 제품을 제조하여 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.Pure surface bonding in the same manner as in Example 1, except that the aromatic modified terpene resin in Example 1 was replaced with a hydrogenated hydrocarbon-based adhesive resin, a hydrogenated methylstyrene-indene copolymer resin (SUKOREZ SU-100S, Kolon Industries). A hot melt adhesive composition was prepared, and it was confirmed that the softening point of the prepared composition was 94°C. Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 1, and the adhesion in the water phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[실시예 4][Example 4]

상기 실시예 3에서 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체를 양봉 분포를 가지며 스티렌 함량이 13.0 중량%인 스티렌-에틸렌-프로필렌-스티렌 블록 공중합체(SEPS)로 대체한 것을 제외하고는 실시예 3과 동일하게 실시하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 91℃인 것을 확인하였다. 상기 양봉 분포를 보이는 SEPS의 제1분율은 중량평균분자량이 38,404 g/mol 및 분자량 분포도가 2.24이었으며, 제2분율은 중량평균분자량이 207,184 g/mol 및 분자량 분포도가 1.02이었으며, 제1분율은 39.4 중량%를 차지하며 제2분율은 60.5중량%를 차지하였다.Examples except that the styrene-ethylene-butylene-styrene block copolymer in Example 3 was replaced with a styrene-ethylene-propylene-styrene block copolymer (SEPS) having a beekeeping distribution and a styrene content of 13.0% by weight. In the same manner as in 3, a hot melt adhesive composition for pure surface bonding was prepared, and it was confirmed that the softening point of the prepared composition was 91°C. The first fraction of SEPS showing the beekeeping distribution had a weight average molecular weight of 38,404 g/mol and a molecular weight distribution of 2.24, the second fraction had a weight average molecular weight of 207,184 g/mol and a molecular weight distribution of 1.02, and the first fraction was 39.4 It occupied% by weight and the second fraction accounted for 60.5% by weight.

이어서, 실시예 3과 동일한 방법으로 일회용 순면 제품을 제조하여 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 3, and the adhesion in the water phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[실시예 5][Example 5]

상기 실시예 3에서 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체를 15 중량부, 수첨 메틸스티렌-인덴 공중합체 수지를 51 중량부로 사용한 것을 제외하고는 실시예 3과 동일하게 실시하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 91℃인 것을 확인하였다. 이어서, 실시예 3과 동일한 방법으로 일회용 순면 제품을 제조하여 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.In Example 3, except that 15 parts by weight of a styrene-ethylene-butylene-styrene block copolymer and 51 parts by weight of a hydrogenated methylstyrene-indene copolymer resin were used, a hot melt for pure surface adhesion An adhesive composition was prepared, and it was confirmed that the softening point of the prepared composition was 91°C. Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 3, and the adhesion in the water phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[실시예 6][Example 6]

상기 실시예 3에서 메탈로센-폴리프로필렌을 융점이 97℃이고 프로필렌 반복단위 함량이 90 몰%인 중량평균분자량 207,331 g/mol(분자량 분포도: 10.61)의 탄성 에틸렌-프로필렌 랜덤 공중합체로 대체한 것을 제외하고는 실시예 3과 동일하게 실시하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 92℃인 것을 확인하였다. 이어서, 실시예 3과 동일한 방법으로 일회용 순면 제품을 제조하여 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.In Example 3, metallocene-polypropylene was replaced with an elastic ethylene-propylene random copolymer having a weight average molecular weight of 207,331 g/mol (molecular weight distribution: 10.61) with a melting point of 97°C and a propylene repeating unit content of 90 mol%. Except that, a hot melt adhesive composition for pure surface bonding was prepared in the same manner as in Example 3, and it was confirmed that the softening point of the prepared composition was 92°C. Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 3, and the adhesion in the water phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[실시예 7][Example 7]

상기 실시예 6에서 탄성 에틸렌-프로필렌 랜덤 공중합체를 3.5 중량부로 하여 융점이 100℃이고 중량평균분자량이 78,910 g/mol(분자량 분포도: 8.24)인 메탈로센-폴리프로필렌(m-PP) 3.5 중량부와 함께 사용한 것을 제외하고는 실시예 6과 동일하게 실시하여 순면 접착용 핫멜트 접착제 조성물을 제조하였으며, 제조된 조성물의 연화점이 93℃인 것을 확인하였다. 이어서, 실시예 6과 동일한 방법으로 일회용 순면 제품을 제조하여 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.3.5 parts by weight of metallocene-polypropylene (m-PP) having a melting point of 100°C and a weight average molecular weight of 78,910 g/mol (molecular weight distribution: 8.24) using 3.5 parts by weight of the elastic ethylene-propylene random copolymer in Example 6 A hot melt adhesive composition for pure surface bonding was prepared in the same manner as in Example 6, except that it was used together with a part, and it was confirmed that the softening point of the prepared composition was 93°C. Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 6, and the adhesion in the aqueous phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[비교예 1][Comparative Example 1]

상기 실시예 3에서 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체를 스티렌-부타디엔-스티렌 블록 공중합체(SBS, TAIPOL® SBS-3206, TSRC)로 대체한 것을 제외하고는 실시예 3과 동일하게 실시하여 일회용 순면 제품을 제조하였다. 제조된 제품의 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.The same procedure as in Example 3, except that the styrene-ethylene-butylene-styrene block copolymer in Example 3 was replaced with a styrene-butadiene-styrene block copolymer (SBS, TAIPOL ® SBS-3206, TSRC). Thus, a disposable pure cotton product was manufactured. Table 2 shows the evaluation of adhesion, peel strength, and coating uniformity of the prepared product.

[비교예 2][Comparative Example 2]

상기 실시예 3에서 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체를 스티렌-이소프렌-스티렌 블록 공중합체(SIS, 4114N, TSRC)로 대체한 것을 제외하고는 실시예 3과 동일하게 실시하여 일회용 순면 제품을 제조하였다. 제조된 제품의 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.Disposable cotton product in the same manner as in Example 3, except that the styrene-ethylene-butylene-styrene block copolymer in Example 3 was replaced with a styrene-isoprene-styrene block copolymer (SIS, 4114N, TSRC). Was prepared. Table 2 shows the evaluation of adhesion, peel strength, and coating uniformity of the prepared product.

[비교예 3][Comparative Example 3]

융점이 97℃이고 프로필렌 반복단위 함량이 90 몰%인 중량평균분자량 207,331 g/mol(분자량 분포도: 10.61)의 탄성 에틸렌-프로필렌 랜덤 공중합체 7 중량부, 수첨 메틸스티렌-인덴 공중합체 수지(SUKOREZ SU-100S, 코오롱인더스트리) 56 중량부, 파라핀 왁스(DNW-110S, 동남유화) 15 중량부, 파라핀 오일(Kixx LP 600, GS 칼텍스) 21 중량부 및 산화 방지제(ADK STAB AO-60, 아데카코리아) 1 중량부를 Brabender mixer에 첨가하여 160℃에서 2 시간 혼합하여 핫멜트 접착제 조성물을 제조하였다.7 parts by weight of an elastic ethylene-propylene random copolymer having a weight average molecular weight of 207,331 g/mol (molecular weight distribution: 10.61) with a melting point of 97°C and a propylene repeating unit content of 90 mol%, hydrogenated methylstyrene-indene copolymer resin (SUKOREZ SU -100S, Kolon Industries) 56 parts by weight, paraffin wax (DNW-110S, Dongnam Petrochemical) 15 parts by weight, paraffin oil (Kixx LP 600, GS Caltex) 21 parts by weight and antioxidant (ADK STAB AO-60, Adeka Korea) ) 1 part by weight was added to the Brabender mixer and mixed at 160°C for 2 hours to prepare a hot melt adhesive composition.

이어서, 실시예 1과 동일한 방법으로 일회용 순면 제품을 제조하고 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.Subsequently, a disposable pure cotton product was prepared in the same manner as in Example 1, and the adhesion in the aqueous phase, peel strength, and coating uniformity were evaluated, and are shown in Table 2.

[비교예 4][Comparative Example 4]

상기 실시예 3에서 메탈로센-폴리프로필렌를 사용하지 않고, 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체를 17 중량부로 사용한 것을 제외하고는 실시예 3과 동일하게 실시하여 일회용 순면 제품을 제조하였다. 제조된 제품의 수상 내 접착성, 박리강도 및 도포 균일성을 평가하여 표 2에 나타내었다.In Example 3, a disposable cotton product was prepared in the same manner as in Example 3, except that the metallocene-polypropylene was not used and the styrene-ethylene-butylene-styrene block copolymer was used in 17 parts by weight. Table 2 shows the evaluation of adhesion, peel strength, and coating uniformity of the prepared product.

조성(중량부)Composition (parts by weight) 올레핀계
수지
Olefin
Suzy
수소화 스티렌계 블록 공중합체Hydrogenated Styrene Block Copolymer 탄화수소계 점착성 수지Hydrocarbon adhesive resin 왁스Wax 윤활제slush 산화방지제Antioxidant
실시예 1Example 1 m-PP(7)m-PP(7) SEBS(10)SEBS(10) 방향족 변성 테르펜 수지(56)Aromatic Modified Terpene Resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
테트라키스(메틸렌-3-(3′,5′-디-t-부틸-4′-하이드록시페닐)프로피오네이트)메탄(1)Tetrakis (methylene-3-(3′,5′-di-t-butyl-4′-hydroxyphenyl)propionate)methane (1)
실시예 2Example 2 m-PP(7)m-PP(7) SEBS(10)SEBS(10) 방향족 탄화수소 수지(56)Aromatic Hydrocarbon Resin(56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
실시예 3Example 3 m-PP(7)m-PP(7) SEBS(10)SEBS(10) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
실시예 4Example 4 m-PP(7)m-PP(7) SEPS(10)SEPS(10) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
실시예 5Example 5 m-PP(7)m-PP(7) SEBS(15)SEBS(15) 수첨 탄화수소계 점착성 수지(51)Hydrocarbon-based adhesive resin (51) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
실시예 6Example 6 에틸렌-프로필렌 랜덤공중합체(7)Ethylene-propylene random copolymer (7) SEBS(10)SEBS(10) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
실시예 7Example 7 에틸렌-프로필렌 랜덤공중합체(3.5)
m-PP(3.5)
Ethylene-propylene random copolymer (3.5)
m-PP(3.5)
SEBS(10)SEBS(10) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
비교예 1Comparative Example 1 m-PP(7)m-PP(7) SBS(10)SBS(10) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
비교예 2Comparative Example 2 m-PP(7)m-PP(7) SIS(10)SIS(10) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)
비교예 3Comparative Example 3 에틸렌-프로필렌 랜덤공중합체(7)Ethylene-propylene random copolymer (7) -- 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀 왁스(15)Paraffin Wax(15) 파라핀
오일(21)
paraffin
Oil(21)
비교예 4Comparative Example 4 -- SEBS(17)SEBS(17) 수첨 탄화수소계 점착성 수지(56)Hydrocarbon-based adhesive resin (56) 파라핀
왁스(5)
paraffin
Wax(5)
파라핀
오일(21)
paraffin
Oil(21)

수상 내 접착성(개)Adhesion in water (pcs) 박리강도
(g/25 mm)
Peeling strength
(g/25 mm)
도포 균일성(개)Coating uniformity (pcs)
실시예 1Example 1 9191 182.0±7.2182.0±7.2 55 실시예 2Example 2 9090 122.2±6.8122.2±6.8 88 실시예 3Example 3 9595 80.8±5.780.8±5.7 8282 실시예 4Example 4 9393 66.3±6.066.3±6.0 8787 실시예 5Example 5 8080 53.8±5.953.8±5.9 8181 실시예 6Example 6 9494 70.1±6.370.1±6.3 8989 실시예 7Example 7 100100 205.3±5.1205.3±5.1 9292 비교예 1Comparative Example 1 1515 17.9±7.017.9±7.0 8484 비교예 2Comparative Example 2 1010 8.9±6.78.9±6.7 8181 비교예 3Comparative Example 3 2525 47.8±7.347.8±7.3 8383 비교예 4Comparative Example 4 2121 25.0±6.425.0±6.4 8080

상기 표 2에서 보는 바와 같이, 실시예 1 내지 7은 수상에서 우수한 접착성을 가지며, 90% 이상의 제품이 박리 없이 접착성을 유지하는 것을 확인하였다.As shown in Table 2, it was confirmed that Examples 1 to 7 had excellent adhesion in an aqueous phase, and 90% or more of the products maintained adhesion without peeling.

구체적으로, 실시예 1 및 2는 우수한 접착성 및 박리강도를 나타내었으나, 핫멜트 접착제 조성물의 분사 시 필라멘트가 다수 형성됨에 따라 기재에 대한 도포 균일성이 매우 낮았으며, 제조된 일회용 순면 제품에서 특이취가 발생하였다.Specifically, Examples 1 and 2 showed excellent adhesiveness and peel strength, but the uniformity of application to the substrate was very low due to the formation of a large number of filaments when spraying the hot melt adhesive composition. Occurred.

또한, 실시예 3 내지 7은 수상에서 현저히 우수한 접착성을 나타내며, 동시에 박리강도 및 도포 균일성이 모두 우수하였다.In addition, Examples 3 to 7 showed remarkably excellent adhesion in an aqueous phase, and at the same time, both peel strength and coating uniformity were excellent.

반면, 비교예 1 내지 4는 수상에서 순면 시트의 박리가 쉽게 발생하여 일회용 순면 제품의 파손이 일어났으며, 구체적으로 75% 이상의 제품이 접착성을 잃고 모두 박리되는 것을 확인하였다.On the other hand, in Comparative Examples 1 to 4, it was confirmed that peeling of the pure cotton sheet easily occurred in the aqueous phase, resulting in breakage of the disposable pure cotton product, and specifically 75% or more of the product lost adhesiveness and all peeled off.

Claims (14)

융점이 70 내지 120℃인 프로필렌 반복단위을 포함하는 올레핀계 수지; 수소화 스티렌계 블록 공중합체; 및 탄화수소계 점착성 수지를 포함하는 순면 접착용 핫멜트 접착제 조성물.Olefin-based resin containing propylene repeating units having a melting point of 70 to 120°C; Hydrogenated styrene block copolymer; And a hot melt adhesive composition for pure surface bonding comprising a hydrocarbon-based adhesive resin. 제1항에 있어서,
상기 순면 접착용 핫멜트 접착제 조성물은 올레핀계 수지 1 내지 20 중량%, 수소화 스티렌계 블록 공중합체 5 내지 40 중량% 및 탄화수소계 점착성 수지 40 내지 80 중량%를 포함하는 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The hot-melt adhesive composition for pure surface bonding includes 1 to 20% by weight of an olefin-based resin, 5 to 40% by weight of a hydrogenated styrene-based block copolymer, and 40 to 80% by weight of a hydrocarbon-based adhesive resin.
제1항에 있어서,
상기 올레핀계 수지는 프로필렌 반복단위 함량이 50 내지 95 몰%인 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The olefin-based resin has a propylene repeating unit content of 50 to 95 mol%, a hot melt adhesive composition for pure surface bonding.
제1항에 있어서,
상기 올레핀계 수지 및 수소화 스티렌계 블록 공중합체의 중량비는 1 : 1 내지 2인 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The weight ratio of the olefin-based resin and the hydrogenated styrene-based block copolymer is 1: 1 to 2, the hot melt adhesive composition for pure surface adhesion.
제1항에 있어서,
상기 수소화 스티렌계 블록 공중합체는 스티렌-에틸렌-부틸렌-스티렌 블록 공중합체(SEBS), 스티렌-에틸렌-프로필렌-스티렌 블록 공중합체(SEPS), 스티렌-에틸렌-프로필렌 블록 공중합체(SEP), 스티렌-에틸렌-에틸렌-프로필렌-스티렌 블록 공중합체(SEEPS) 및 스티렌-부틸렌-부타디엔-스티렌 블록 공중합체(SBBS)에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The hydrogenated styrene block copolymer is a styrene-ethylene-butylene-styrene block copolymer (SEBS), a styrene-ethylene-propylene-styrene block copolymer (SEPS), a styrene-ethylene-propylene block copolymer (SEP), and styrene. -Ethylene-ethylene-propylene-styrene block copolymer (SEEPS) and styrene-butylene-butadiene-styrene block copolymer (SBBS) any one or a mixture of two or more selected from a hot-melt adhesive composition for pure surface adhesion.
제1항에 있어서,
상기 탄화수소계 점착성 수지는 수첨 탄화수소계 점착성 수지인 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The hydrocarbon-based adhesive resin is a hydrogenated hydrocarbon-based adhesive resin, a hot melt adhesive composition for pure surface adhesion.
제1항에 있어서,
상기 순면 접착용 핫멜트 접착제 조성물은 연화점이 130℃ 이하인 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The hot-melt adhesive composition for pure surface bonding is a hot-melt adhesive composition for pure surface bonding having a softening point of 130°C or less.
제1항에 있어서,
상기 순면 접착용 핫멜트 접착제 조성물은 윤활제, 왁스, 가소제 및 산화 방지제에서 선택되는 어느 하나 또는 둘 이상의 혼합물을 더 포함하는 순면 접착용 핫멜트 접착제 조성물.
The method of claim 1,
The hot-melt adhesive composition for pure surface bonding is a hot-melt adhesive composition for pure surface bonding further comprising any one or a mixture of two or more selected from lubricants, waxes, plasticizers, and antioxidants.
제1기재; 제2기재; 및 상기 제1기재와 제2기재의 계면에 형성되는 핫멜트 접착제 조성물;을 포함하며, 상기 핫멜트 접착제 조성물은 제1항 내지 제8항에서 선택되는 어느 한 항의 순면 접착용 핫멜트 접착제 조성물인 일회용 제품.First description; Second description; And a hot-melt adhesive composition formed at an interface between the first and second substrates, wherein the hot-melt adhesive composition is a hot-melt adhesive composition for pure surface bonding of any one selected from claims 1 to 8. 제9항에 있어서,
상기 일회용 제품은 기저귀, 성인 요실금용 제품, 여성용 위생 제품 및 의료용 밴드에서 선택되는 것인 일회용 제품.
The method of claim 9,
The disposable product is a disposable product selected from diapers, adult incontinence products, feminine hygiene products and medical bands.
제9항에 있어서,
상기 제1기재 및 제2기재 중 적어도 어느 하나 이상이 순면 섬유인 일회용 제품.
The method of claim 9,
A disposable product in which at least one of the first and second substrates is pure cotton fiber.
융점이 70 내지 120℃인 프로필렌 반복단위을 포함하는 올레핀계 수지, 수소화 스티렌계 블록 공중합체 및 탄화수소계 점착성 수지를 포함하는 핫멜트 접착제 조성물을 가온하는 단계;
제1기재에 상기 가온된 핫멜트 접착제 조성물을 도포하는 단계; 및
상기 핫멜트 접착제 조성물이 도포된 제1기재 상에 제2기재를 적층하고 열압착하여 접착시키는 단계;
를 포함하는 일회용 제품의 제조방법.
Heating a hot-melt adhesive composition comprising an olefin-based resin, a hydrogenated styrene-based block copolymer, and a hydrocarbon-based adhesive resin including a propylene repeating unit having a melting point of 70 to 120°C;
Applying the heated hot melt adhesive composition to a first substrate; And
Laminating a second substrate on the first substrate to which the hot-melt adhesive composition is applied, and bonding by thermocompression bonding;
Method for producing a disposable product comprising a.
제12항에 있어서,
상기 핫멜트 접착제 조성물을 도포하는 단계는 80 내지 150℃에서 수행되는 것인 일회용 제품의 제조방법.
The method of claim 12,
The step of applying the hot melt adhesive composition is a method of manufacturing a disposable product that is performed at 80 to 150°C.
제12항에 있어서,
상기 일회용 제품은 순면 섬유를 포함하는 것인 일회용 제품의 제조방법.
The method of claim 12,
The disposable product is a method of manufacturing a disposable product containing pure cotton fibers.
KR1020190072464A 2019-06-18 2019-06-18 Hot melt adhesive composition KR102261405B1 (en)