KR20190097351A - Method for manufacturing ball pad including volcanic stone - Google Patents

Method for manufacturing ball pad including volcanic stone Download PDF

Info

Publication number
KR20190097351A
KR20190097351A KR1020180016645A KR20180016645A KR20190097351A KR 20190097351 A KR20190097351 A KR 20190097351A KR 1020180016645 A KR1020180016645 A KR 1020180016645A KR 20180016645 A KR20180016645 A KR 20180016645A KR 20190097351 A KR20190097351 A KR 20190097351A
Authority
KR
South Korea
Prior art keywords
volcanic stone
cover
volcanic
ball pad
manufacturing
Prior art date
Application number
KR1020180016645A
Other languages
Korean (ko)
Inventor
한선진
Original Assignee
한선진
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한선진 filed Critical 한선진
Priority to KR1020180016645A priority Critical patent/KR20190097351A/en
Publication of KR20190097351A publication Critical patent/KR20190097351A/en

Abstract

The present invention relates to a manufacturing method of a volcanic stone ball pad containing volcanic stones. The manufacturing method of the volcanic stone ball pad comprises the steps of: kneading volcanic stone powder with volcanic stone water to form a specific shape, and then calcining the same at the predetermined temperature to produce volcanic stone balls; inserting a plurality of the volcanic stone balls into a plurality of insertion grooves, respectively, of a first cover, wherein the first cover has the plurality of insertion grooves into which the volcanic stone balls can be inserted; and attaching a second cover having the same shape as the first cover symmetrically to the first cover so as to seal the volcanic stone balls inserted into the insertion groove.

Description

화산석 볼 패드의 제조방법{METHOD FOR MANUFACTURING BALL PAD INCLUDING VOLCANIC STONE}Manufacturing method of volcanic stone ball pad {METHOD FOR MANUFACTURING BALL PAD INCLUDING VOLCANIC STONE}

본 발명은 볼 패드의 제조방법에 관한 것으로, 보다 상세하게는 화산석이 함유된 화산석 볼 패드의 제조방법에 관한 것이다.The present invention relates to a method of manufacturing a ball pad, and more particularly, to a method of manufacturing a volcanic stone ball pad containing volcanic stones.

화산석은 음이온 및 원적외선을 발생시키며, 모공 축소와 모낭충 제거에 효과적이다. 상기 화산석의 예로는 포조란, 벤토나이트 등이 있다. 상기 화산석은 게르마늄 성분을 포함할 수 있다. 게르마늄이 포함된 화산석은 황토보다 186배나 인체에 좋은 활성화 성분을 가지고 있다. Volcanic stones generate negative ions and far-infrared rays, and are effective for shrinking pores and removing Demodex. Examples of the volcanic stone include pozzorans, bentonite, and the like. The volcanic stone may include a germanium component. Germanium-containing volcanic stone has 186 times more active ingredients than human loess.

한편, 최근에는 원적외선 및 음이온 방출 작용뿐만 아니라 탈취효과를 나타내는 화산암류의 광물들이 연구되고 있는데, 그 중 하나가 천연 광물인 포조란이다.On the other hand, in recent years, minerals of volcanic rocks that exhibit not only far-infrared and anion-releasing action but also deodorizing effect have been studied, one of which is natural mineral pozzolan.

포조란 광물은 화산회로 이루어진 것으로서 납석의 일종으로 알려져 있다. 이는 백악기 시대에 생성된 물질로 알려져 있으며, 주요 산지인 이태리의 바리섬 인근 포죠리 마을에서 발견되어 그 명칭이 유래된 광물이다. Pozoran mineral is composed of volcanic ash and is known as a type of feldspar. It is known as a material produced during the Cretaceous period, and it is a mineral derived from Pojori village near Bari Island in Italy, which is a major mountain region.

포조란은 현재까지 원적외선 및 음이온 방출기능, 향균기능, 및 탈취 기능이 있는 것으로 연구되어 있으며, 관련된 선행문헌으로 대한민국 공개특허번호 10-2005-0040476호가 있다. Pozoran has been studied to have far-infrared and anion-releasing function, antibacterial function, and deodorizing function to date, and there is a related prior art document, Republic of Korea Patent Publication No. 10-2005-0040476.

따라서 원적외선 및 음이온 방출기능, 향균기능, 및 탈취 기능을 나타내는 화산석을 일상에서 편리하게 사용할 수 있는 기술에 대한 연구가 필요한 실정이다. Therefore, there is a need for a study on a technology that can conveniently use volcanic stone showing far infrared and anion releasing function, antibacterial function, and deodorizing function in daily life.

본 발명의 목적은 원적외선 및 음이온 방출기능, 향균기능, 및 탈취 기능을 나타내는 화산석 볼 패드의 제조방법을 제공하는 데 있다.An object of the present invention is to provide a method for producing a volcanic stone ball pad exhibiting far infrared rays and anion release function, antibacterial function, and deodorizing function.

상기 목적을 달성하기 위해 본 발명의 일실시예에 의하면, 화산석 분말을 화산석 수로 반죽하여 특정 형상으로 성형한 후 소정 온도에서 소성하여 화산석 볼을 제조하는 단계; 상기 화산석 볼이 삽입될 수 있는 복수 개의 삽입 홈이 형성된 제1커버에 복수 개의 화선석 볼을 각각 상기 삽입 홈에 삽입하는 단계; 및 상기 삽입 홈에 삽입된 상기 화산석 볼이 실링될 수 있도록 상기 제1커버와 동일 형상의 제2커버를 상기 제1커버에 대칭되게 부착하는 단계를 포함하는 것을 화산석 볼 패드의 제조방법이 개시된다. According to an embodiment of the present invention to achieve the above object, the step of producing a volcanic stone ball by kneading the volcanic stone powder with volcanic stone water to form a specific shape and then fired at a predetermined temperature; Inserting a plurality of granite balls into the insertion grooves in a first cover in which a plurality of insertion grooves into which the volcanic stone balls are inserted are formed; And attaching a second cover having the same shape as the first cover to the first cover symmetrically so that the volcanic stone ball inserted into the insertion groove can be sealed. .

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 일상 생활에서 다양한 용도로 편리하게 사용할 수 있다. The volcanic stone ball pad manufactured by the method for manufacturing a volcanic stone ball pad according to an embodiment of the present invention can be conveniently used for various purposes in daily life.

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 베게 속, 베게 밑, 베게 위에 넣어 두게 되면, 원적외선 및 음이온 방출이 방출되어 사람의 건강에 좋고, 항균 및 탈취에도 효과적이다. The volcanic stone ball pad manufactured by the method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention is placed in the pillow, under the pillow, and placed on the pillow, so that far infrared rays and negative ions are released, which is good for human health, antibacterial and deodorant Also effective.

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 방석 위나 아래에 넣어 두거나 애완 동물용 방석으로 사용할 수도 있다. The volcanic stone ball pad manufactured by the method for manufacturing a volcanic stone ball pad according to an embodiment of the present invention may be placed on or under a cushion or used as a pet cushion.

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 침대용 패드나 각종 깔개로 사용하면, 인체에 유익한 원적외선 방출과 악취제거, 습도조절 등의 기능을 발휘할 수 있다. The volcanic stone ball pad manufactured by the method for manufacturing a volcanic stone ball pad according to an embodiment of the present invention can exhibit functions such as far-infrared emission, odor removal, and humidity control, which are beneficial to the human body when used as a bed pad or various types of rugs.

도 1은 본 발명의 일실시예와 관련된 화산석 볼 패드의 제조방법을 나타내는 흐름도이다.
도 2는 도 1의 S110의 세부 공정도이다.
도 3은 도 2의 S230의 세부 공정도이다.
도 4는 본 발명의 일실시예와 관련된 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드의 사시도이다.
도 5는 도 4의 A-A선의 단면도이다.
도 6은 도 5의 "B"부 확대도이다. 1 is a flowchart illustrating a method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention.
FIG. 2 is a detailed process diagram of S110 of FIG. 1.
3 is a detailed process diagram of S230 of FIG. 2.
Figure 4 is a perspective view of a volcanic stone ball pad manufactured by a method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention.
5 is a cross-sectional view taken along the line AA of FIG. 4.
6 is an enlarged view of a portion “B” of FIG. 5.

이하, 본 발명의 일실시예와 관련된 화산석 볼 패드의 제조방법에 대해 도면을 참조하여 설명하도록 하겠다.Hereinafter, a method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention will be described with reference to the drawings.

본 명세서에서 사용되는 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "구성된다" 또는 "포함한다" 등의 용어는 명세서상에 기재된 여러 구성 요소들, 또는 여러 단계들을 반드시 모두 포함하는 것으로 해석되지 않아야 하며, 그 중 일부 구성 요소들 또는 일부 단계들은 포함되지 않을 수도 있고, 또는 추가적인 구성 요소 또는 단계들을 더 포함할 수 있는 것으로 해석되어야 한다.As used herein, the singular forms "a", "an" and "the" include plural forms unless the context clearly indicates otherwise. In this specification, terms such as “consisting of” or “comprising” should not be construed as necessarily including all of the various components or steps described in the specification, and some of the components or some steps It should be construed that it may not be included or may further include additional components or steps.

화산석은 음이온 및 원적외선을 발생시키며, 모공 축소와 모낭충 제거에 효과적이다. 상기 화산석의 예로는 포조란, 벤토나이트 등이 있다. 상기 화산석은 게르마늄 성분을 포함할 수 있다. 화산석 원석은 일본, 이탈리아, 한국(예: 제주도) 등에서 발굴될 수 있다. 또한, 포조란은 송이석, 스콜리아, 부석, 퍼미스(purmice) 등의 다른 명칭으로 명명될 수도 있다. Volcanic stones generate negative ions and far-infrared rays, and are effective for shrinking pores and removing Demodex. Examples of the volcanic stone include pozzorans, bentonite, and the like. The volcanic stone may include a germanium component. Volcanic ore can be found in Japan, Italy and Korea (eg Jeju Island). In addition, Pozoran may be named by other names such as Songseok, Scoli, Pumice, Purmice and the like.

도 1은 본 발명의 일실시예와 관련된 화산석 볼 패드의 제조방법을 나타내는 흐름도이다.1 is a flowchart illustrating a method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention.

먼저, 화산석 볼 패드를 제조하기 위해서 화산석 볼을 제조한다(S110). 상기 화산석 볼은 화산석 분말을 화산석 수로 반죽하여 성형과 소성 과정을 거쳐 제조될 수 있다. First, a volcanic stone ball is manufactured to manufacture a volcanic stone ball pad (S110). The volcanic stone ball may be prepared by kneading volcanic stone powder with volcanic stone water through a molding and firing process.

도 2는 도 1의 S110의 세부 공정도이다.FIG. 2 is a detailed process diagram of S110 of FIG. 1.

화산석 볼을 제조하기 위해서는 먼저, 화산석을 분쇄기를 이용하여 초미세입자로 분쇄한다(S210). 이때 분쇄되는 화산석 입자는 325메쉬(mesh) 이상으로 분쇄하는 것이 바람직하다. 즉, 화산석 입자의 크기가 325메쉬의 채공(空)과 같거나 보다 작은 크기로 분쇄되는 것이 바람직하다.In order to manufacture the volcanic stone ball, first, the volcanic stone is ground into ultrafine particles using a grinder (S210). At this time, the crushed volcanic stone particles are preferably pulverized to 325 mesh (mesh) or more. That is, it is preferable that the size of the volcanic stone particles are crushed to a size equal to or smaller than a 325 mesh hollow.

그리고 분쇄된 화산석에 고체 형태의 물질을 혼합하여 화산석 분말을 제조할 수 있다(S220). 물론 추가 혼합 물질 없이 화산석만으로도 화산석 분말을 제조할 수 있다. In addition, the solid powder may be mixed with the pulverized volcanic stone to prepare a volcanic stone powder (S220). Of course, volcanic stone powder can be produced by volcanic stone alone without additional mixing materials.

예를 들어, 분쇄된 화산석 1중량부에 대해 분말 형태의 바인더를 0.5 중량부 내지 분말 형태의 3중량부의 비로 혼합할 수 있다. For example, the binder in powder form may be mixed at a ratio of 0.5 parts by weight to 3 parts by weight of powder based on 1 part by weight of pulverized volcanic stone.

화산석은 점토와는 달리 표면에너지가 낮아 결합력이 떨어진다. 이러한 화산석을 가능한 한 미세한 분말로 분쇄하게 되면 각 분말의 표면에너지를 높여 분말끼리의 결합력을 높일 수 있다. 따라서, 화산석을 가능한 미세한 크기의 분말로 분쇄하는 것이 바람직하다.Unlike clay, volcanic stone has a low surface energy and thus has low binding strength. When the volcanic stone is pulverized into as fine powder as possible, the surface energy of each powder can be increased to increase the bonding strength between the powders. Therefore, it is desirable to grind the volcanic stone into powder of the finest size possible.

실험을 통하여 확인한 결과, 최소 325메쉬 이상의 채로 걸러진 화산석 분말이어야 후술할 결합액으로 반죽할 때 화산석 분말이 안정적으로 결합될 수 있었다. 또한, 결합력을 강화시키기 위해 바이더를 분쇄된 화산석 입자에 혼합할 수 있다. As a result of the experiment, it was confirmed that the volcanic stone powder was stably mixed with at least 325 mesh when kneaded with a binder solution to be described later. In addition, the provider can be mixed with the crushed volcanic stone particles to enhance the binding force.

그리고 화산석 분말의 결합액으로 사용되는 화산석 수를 수득하는 과정을 수행할 수 있다(S230).In addition, a process of obtaining volcanic stone water used as a binding liquid of volcanic stone powder may be performed (S230).

도 3는 도 2의 S230의 세부 공정도이다.3 is a detailed process diagram of S230 of FIG. 2.

먼저, 소정 용기에 정제수를 채운다(S310). 그리고 정제수가 채워진 용기에 화산석 원석을 투입하고, 상기 화산석 원석이 포함된 정제수를 50℃ 내지 100℃의 온도로 소정시간 가열시킨다(S320). First, purified water is filled in a predetermined container (S310). Then, the raw ore is added to the vessel filled with purified water, and the purified water including the volcanic ore is heated to a temperature of 50 ° C. to 100 ° C. for a predetermined time (S320).

그리고 상기 가열된 정제수를 상기 화산석 원석이 포함된 상태로 2일 내지 3일 숙성시킬 수 있다(S330).Then, the heated purified water may be aged for 2 days to 3 days in the state containing the volcanic stone ore (S330).

상기 제조된 화산석 분말을 상기 화산석 수로 반죽하여 특정 형상으로 성형한 후 소정 온도에서 소성하는 단계를 수행할 수 있다(S240). The prepared volcanic stone powder may be kneaded with the volcanic stone water to be molded into a specific shape and then fired at a predetermined temperature (S240).

상기 화산석 수에 화산석 분말을 혼합하고 반죽한다. 이때, 화산석 분말 1중량부에 대해 화산석 수 0.1 내지 0.4 중량부의 혼합비로 혼합할 수 있다. 상기와 같은 혼합비로 혼합했을 때, 화산석 분말이 잘 결합되는 것을 실험을 통해 발견할 수 있었다. 또한, 상기의 혼합비로 혼합 했을 때 탈취율이 높아지는 것을 실험을 통해 확인할 수 있었다. The volcanic stone powder is mixed and kneaded with the volcanic stone water. At this time, it can be mixed in a mixing ratio of 0.1 to 0.4 parts by weight of the number of volcanic stones with respect to 1 part by weight of volcanic stone powder. When mixed in the above mixing ratio, it was found through the experiment that the volcanic stone powder is well combined. In addition, it was confirmed through experiments that the deodorization rate is increased when mixed in the above mixing ratio.

또한, 화산석 분말, 화산석 수 이외에 약간의 소금 및 소다를 첨가하여 혼합한 후 반죽하는 것이 바람직하다. 소금 및 소다는 소성 작용을 활성화시킬 뿐 아니라 소성시 화산석 분말의 다공성 구조를 유지하는데 도움을 준다. 예를 들어, 소금과 소다의 혼합물을 화산석 분말 1 중량부에 대해 0.03 중량부 내지 0.08 중량부로 혼합할 수 있다.It is also preferable to knead after adding and mixing some salt and soda in addition to volcanic stone powder and volcanic stone water. Salt and soda not only activate the firing action but also help maintain the porous structure of the volcanic stone powder upon firing. For example, a mixture of salt and soda may be mixed in an amount of 0.03 to 0.08 parts by weight based on 1 part by weight of volcanic stone powder.

그렇게 화산석 수에 의해 반죽된 화산석 분말을 특정 형상으로 성형할 수 있다. 상기와 같이 성형된 화산석 분말의 특정 형상은 다양한 형상을 포함할 수 있다. 예를 들어, 상기 특정 형상은 구형상, 내부 빈 공간을 가지며 상하부에 개구부가 형성된 원기둥 형상, 및 육면체 형상 등을 포함할 수 있다. 또한 상기 성형된 화산석 분말의 표면은 매끄럽게 성형될 수도 있고, 돌기가 형성되거나 홈이 형성되도록 성형될 수도 있다. The volcanic stone powder thus kneaded by volcanic stone water can be formed into a specific shape. The specific shape of the volcanic stone powder formed as described above may include various shapes. For example, the specific shape may include a spherical shape, a cylindrical shape having an inner empty space and openings formed at upper and lower portions thereof, and a hexahedral shape. In addition, the surface of the formed volcanic stone powder may be smoothly formed, or may be formed such that protrusions or grooves are formed.

다음으로 상술한 형상으로 성형된 성형물을 950℃~1100℃에서 소성한다.Next, the molded article shape | molded to the shape mentioned above is baked at 950 degreeC-1100 degreeC.

소성시 온도가 너무 높으면 화산석 분말 자체가 녹아내려 화산석 특유의 다공질 구조가 해체되어 탈취율이 떨어지게 된다. 본 발명의 일실시예에 의하면, 탈취율을 유지하기 위해서 950℃~1100℃에서 소성하는 것이 바람직하며, 1000℃~1050℃에서 소성하는 것이 보다 바람직하다If the temperature is too high during firing, the volcanic stone powder itself melts and the porous structure peculiar to volcanic stone is dismantled and the deodorization rate decreases. According to one embodiment of the present invention, in order to maintain the deodorization rate, it is preferable to bake at 950 ° C to 1100 ° C, and more preferably to bake at 1000 ° C to 1050 ° C.

도 4는 본 발명의 일실시예와 관련된 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드의 사시도이고, 도 5는 도 4의 A-A선의 단면도이고, 도 6은 도 5의 "B"부 확대도이다.4 is a perspective view of a volcanic stone ball pad manufactured by a method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention, FIG. 5 is a cross-sectional view taken along line AA of FIG. 4, and FIG. It is also.

도면을 통해 확인할 수 있듯이, 제조된 화산석 볼(150) 각각을 제1커버(120)의 복수 개의 삽입 홈(110)에 삽입할 수 있다(S120). As can be seen through the drawings, each of the manufactured volcanic stone balls 150 may be inserted into the plurality of insertion grooves 110 of the first cover 120 (S120).

그리고 삽입 홈(110)에 삽입된 상기 화산석 볼(150)이 실링될 수 있도록 상기 제1커버(120)와 동일 형상의 제2커버(121)를 상기 제1커버(120)에 대칭되게 부착할 수 있다(S130). The second cover 121 having the same shape as the first cover 120 may be symmetrically attached to the first cover 120 so that the volcanic stone ball 150 inserted into the insertion groove 110 may be sealed. It may be (S130).

상기 제1커버(120) 및 상기 제2커버(121)는 실리콘 재질 또는 천 재질로 이루어질 수 있다. 상기 제1커버(120) 및 상기 제2커버(121)의 재질이 천 인 경우는 공기가 투과하지만, 실리콘인 경우에는 공기가 투과되지 않을 수 있다. 이럴 경우, 상기 삽입 홈(110)을 이루는 제1커버(120) 및 상기 제2커버(121)의 소정 영역에는 공기가 투과될 수 있도록 천공(111)이 형성될 수 있다. The first cover 120 and the second cover 121 may be made of a silicon material or a cloth material. When the material of the first cover 120 and the second cover 121 is a cloth, air is permeable, but in the case of silicon, air may not be permeated. In this case, a perforation 111 may be formed in a predetermined region of the first cover 120 and the second cover 121 forming the insertion groove 110 to allow air to pass therethrough.

전술한 바와 같이, 본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 일상 생활에서 다양한 용도로 편리하게 사용할 수 있다. As described above, the volcanic stone ball pad manufactured by the method for manufacturing a volcanic stone ball pad according to an embodiment of the present invention can be conveniently used for various purposes in daily life.

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 베게 속, 베게 밑, 베게 위에 넣어 두게 되면, 원적외선 및 음이온 방출이 방출되어 사람의 건강에 좋고, 항균 및 탈취에도 효과적이다. Volcanic stone ball pad prepared by the method of manufacturing a volcanic stone ball pad according to an embodiment of the present invention, when put in the pillow, under the pillow, on the pillow, the far infrared and anion emission is released, good for human health, antibacterial and deodorizing Also effective.

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 방석 위나 아래에 넣어 두거나 애완 동물용 방석으로 사용할 수도 있다. The volcanic stone ball pad manufactured by the method for manufacturing a volcanic stone ball pad according to an embodiment of the present invention may be placed on or under a cushion or used as a pet cushion.

본 발명의 일실시예에 의한 화산석 볼 패드의 제조방법에 의해 제조된 화산석 볼 패드는 침대용 패드나 각종 깔개로 사용하면, 인체에 유익한 원적외선 방출과 악취제거, 습도조절 등의 기능을 발휘할 수 있다.The volcanic stone ball pad manufactured by the method for manufacturing a volcanic stone ball pad according to an embodiment of the present invention can exhibit functions such as far-infrared emission, odor removal, and humidity control, which are beneficial to the human body when used as a bed pad or various types of rugs.

상기와 같이 설명된 화산석 볼 패드의 제조방법 및 그 제조방법에 의해 제조된 화산석 볼 패드는 상기 설명된 실시예들의 구성과 방법이 한정되게 적용될 수 있는 것이 아니라, 상기 실시예들은 다양한 변형이 이루어질 수 있도록 각 실시예들의 전부 또는 일부가 선택적으로 조합되어 구성될 수도 있다.The method of manufacturing the volcanic stone ball pad described above and the volcanic stone ball pad manufactured by the manufacturing method are not limited to the configuration and method of the above-described embodiments, and the embodiments may be modified in various ways. All or part of each of the embodiments may be configured to be selectively combined so that.

100: 화산석 볼 패드
110: 삽입 홈
111: 천공
120, 121: 커버
150: 화산석 볼100: volcanic stone ball pad
110: insertion groove
111: perforation
120, 121: cover
150: Volcanic Stone Ball

Claims (5)

화산석 분말을 화산석 수로 반죽하여 특정 형상으로 성형한 후 소정 온도에서 소성하여 화산석 볼을 제조하는 단계;
상기 화산석 볼이 삽입될 수 있는 복수 개의 삽입 홈이 형성된 제1커버에 복수 개의 화선석 볼을 각각 상기 삽입 홈에 삽입하는 단계; 및
상기 삽입 홈에 삽입된 상기 화산석 볼이 실링될 수 있도록 상기 제1커버와 동일 형상의 제2커버를 상기 제1커버에 대칭되게 부착하는 단계를 포함하는 것을 특징으로 하는 화산석 볼 패드의 제조방법.Preparing a volcanic stone ball by kneading the volcanic stone powder into volcanic stone water to form a specific shape and then baking at a predetermined temperature;
Inserting a plurality of granite balls into the insertion grooves in a first cover in which a plurality of insertion grooves into which the volcanic stone balls are inserted are formed; And
And attaching a second cover having the same shape as the first cover to the first cover symmetrically so that the volcanic stone ball inserted into the insertion groove can be sealed. 제1항에 있어서,
상기 제1커버 및 상기 제2커버는 실리콘 재질 또는 천 재질로 이루어진 것을 특징으로 하는 화산석 볼 패드의 제조방법.The method of claim 1,
The first cover and the second cover is a method of manufacturing a volcanic stone ball pad, characterized in that made of silicon or cloth material. 제1항에 있어서,
상기 삽입 홈을 이루는 제1커버 및 상기 제2커버의 소정 영역에는 공기가 투과될 수 있도록 천공이 형성되어 있는 것을 특징으로 화산석 볼 패드의 제조방법.The method of claim 1,
The method of manufacturing a volcanic stone ball pad, characterized in that the perforation is formed in the predetermined region of the first cover and the second cover forming the insertion groove so that air can pass through. 제1항에 있어서, 상기 화산석 볼의 제조단계는
화산석을 분쇄하는 단계;
상기 분쇄된 화산석에 대해 바인더를 소정 비율로 혼합하여 상기 화산석 분말을 제조하는 단계;
정제수로부터 상기 화산석 수를 수득하는 단계; 및
상기 화산석 분말을 화산석 수로 반죽하여 특정 형상으로 성형한 후 성형된 성형물을 950℃~1100℃에서 소성하여 화산석 볼을 제조하는 단계를 포함하는 것을 특징으로 하는 화산석 볼 패드의 제조방법. According to claim 1, wherein the manufacturing step of the volcanic stone ball
Crushing volcanic stone;
Preparing a volcanic stone powder by mixing a binder with respect to the pulverized volcanic stone at a predetermined ratio;
Obtaining the volcanic stone water from purified water; And
And kneading the volcanic stone powder with volcanic stone water to form a specific shape, and then calcining the molded product at 950 ° C to 1100 ° C to produce volcanic stone balls. 제 4 항에 있어서, 상기 화산석 수 수득 단계는
상기 정제수를 용기에 채우는 단계;
상기 정제수에 화산석 원석을 투입하고 상기 화산석 원석이 포함된 정제수를 50℃ 내지 100℃의 온도로 가열시키는 단계; 및
상기 가열된 정제수를 상기 화산석 원석이 포함된 상태로 2일 내지 3일 숙성시키는 단계를 포함하는 것을 특징으로 하는 화산석 볼 패드의 제조방법. According to claim 4, wherein the volcanic stone number obtaining step
Filling the container with purified water;
Injecting the volcanic stone gemstone into the purified water and heating the purified water including the volcanic stone gemstone to a temperature of 50 ° C. to 100 ° C .; And
Method of producing a volcanic stone ball pad, characterized in that it comprises the step of aging the heated purified water in the state containing the volcanic stone ore for 2 to 3 days.
KR1020180016645A 2018-02-12 2018-02-12 Method for manufacturing ball pad including volcanic stone KR20190097351A (en)