KR20190022170A - Functional paper sheet for functional mask, functional mask including the same, and method of preparing the functional mask - Google Patents

Functional paper sheet for functional mask, functional mask including the same, and method of preparing the functional mask Download PDF

Info

Publication number
KR20190022170A
KR20190022170A KR1020170108133A KR20170108133A KR20190022170A KR 20190022170 A KR20190022170 A KR 20190022170A KR 1020170108133 A KR1020170108133 A KR 1020170108133A KR 20170108133 A KR20170108133 A KR 20170108133A KR 20190022170 A KR20190022170 A KR 20190022170A
Authority
KR
South Korea
Prior art keywords
functional
paper sheet
mask
polymer
coating layer
Prior art date
Application number
KR1020170108133A
Other languages
Korean (ko)
Other versions
KR102023097B1 (en
Inventor
최웅철
Original Assignee
국민대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 국민대학교산학협력단 filed Critical 국민대학교산학협력단
Priority to KR1020170108133A priority Critical patent/KR102023097B1/en
Publication of KR20190022170A publication Critical patent/KR20190022170A/en
Application granted granted Critical
Publication of KR102023097B1 publication Critical patent/KR102023097B1/en

Abstract

The present invention relates to a functional paper sheet for a functional mask, capable of providing improved antibacterial and deodorizing multi-functions. The present invention also relates to a functional mask including the same, and a method for manufacturing the functional mask. The functional paper sheet for a functional mask comprises: a paper sheet; and a functional coating layer formed on at least one surface of the paper sheet, wherein the functional coating layer includes a superabsorbent polymer and a hygroscopic inorganic salt.

Description

기능성 마스크용 기능성 종이 시트, 이를 포함하는 기능성 마스크, 및 상기 기능성 마스크의 제조방법{Functional paper sheet for functional mask, functional mask including the same, and method of preparing the functional mask}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a functional paper sheet for a functional mask, a functional mask including the same, and a method for manufacturing the functional mask,

기능성 마스크용 기능성 종이 시트, 이를 포함하는 기능성 마스크, 및 상기 기능성 마스크의 제조방법에 관한 것이다.To a functional paper sheet for a functional mask, a functional mask including the same, and a method for manufacturing the functional mask.

지구의 기후 변화로 자주 발생하는 황사 등 자연적인 대기 환경의 악화와 경제 발전에 따른 급격한 도시화로 인해 대기오염, 인위적인 작업환경에서 발생하는 분진이나 세균 등으로부터 개인의 건강을 보호하기 위하여 마스크를 착용하고 있다.The mask is worn to protect the health of the individual from dust and germs generated in air pollution and artificial working environment due to the deterioration of the natural air environment such as yellow dust often caused by global climate change and the rapid urbanization due to economic development .

또한 근래, 과중한 사회적, 업무적 스트레스를 해소하기 위하여 골프, 야구 등과 같은 야외에서의 스포츠 및 레저활동이 증가하고 있는데, 이러한 스포츠 및 레저활동을 위하여도 마스크를 착용하고 있다.In recent years, sports and leisure activities such as golf, baseball and the like have been increasing in order to solve the heavy social and business stress, and the masks are also worn for such sports and leisure activities.

그러나 사용자는 사용자 자신의 호흡 또는 오염된 외부 환경으로부터 발생하는 습기로 인해 오랫동안 마스크를 착용하는 경우 불쾌감을 느끼게 되고, 이로 인해 세균 및 곰팡이 등이 생기게 되어 한번 사용한 마스크를 다시 사용하지 못하고 버리는 경우가 종종 있다. However, the user feels discomfort when wearing the mask for a long time due to moisture generated from the user's own breathing or contaminated external environment, and because of this, bacteria and fungus are generated, and the mask once used can not be used again often have.

따라서 이러한 문제를 해결하기 위해 여러 번 재사용이 가능한 신규한 기능성 마스크 및 상기 기능성 마스크의 제조방법 등에 대한 요구가 있다.Accordingly, there is a need for a novel functional mask that can be reused many times in order to solve such a problem, a method of manufacturing the functional mask, and the like.

일 측면은 적어도 일면에 형성된 초흡수성(superabsorbent) 고분자 및 흡습성(hygroscopic) 무기염을 포함한 기능성 코팅층을 포함하고, 하나 또는 둘 이상의 개구부를 갖는 기능성 마스크용 기능성 종이 시트를 제공하는 것이다. One aspect is to provide a functional paper sheet for a functional mask comprising a functional coating layer including a superabsorbent polymer and a hygroscopic inorganic salt formed on at least one surface thereof and having one or two or more openings.

다른 측면은 제습, 항균 및 탈취의 복합기능을 갖는 기능성 마스크를 제공하는 것이다.Another aspect is to provide a functional mask having a combined function of dehumidification, antibacterial and deodorization.

또다른 측면은 상기 기능성 마스크의 제조방법을 제공하는 것이다.      Another aspect is to provide a method of manufacturing the functional mask.

일 측면에 따르면, According to one aspect,

종이 시트; 및Paper sheet; And

상기 종이 시트의 적어도 일면에 형성된 기능성 코팅층;을 포함한 기능성 종이 시트를 포함하고,And a functional coating layer formed on at least one side of the paper sheet,

상기 기능성 코팅층은 초흡수성(superabsorbent) 고분자 및 흡습성(hygroscopic) 무기염을 포함하고,Wherein the functional coating layer comprises a superabsorbent polymer and a hygroscopic inorganic salt,

상기 초흡수성 고분자는 55 내지 100% 상대습도의 고습도용 제1 고분자 및 10 내지 45% 상대습도의 저습도용 제2 고분자를 포함하고, Wherein the superabsorbent polymer comprises a first polymer for high humidity at a relative humidity of 55 to 100% and a second polymer for low humidity at a relative humidity of 10 to 45%

상기 기능성 종이 시트는 하나 또는 둘 이상의 개구부를 갖는 기능성 마스크용 기능성 종이 시트가 제공된다.      The functional paper sheet is provided with a functional paper sheet for a functional mask having one or more openings.

다른 측면에 따르면,        According to another aspect,

전술한 기능성 종이 시트를 포함하는 기능성 마스크가 제공된다.       A functional mask comprising the above-described functional paper sheet is provided.

다른 측면에 따르면,       According to another aspect,

종이 시트를 준비하는 단계;       Preparing a paper sheet;

상기 종이 시트의 적어도 일면에 초흡수성(superabsorbent) 고분자, 및 흡습성(hygroscopic) 무기염 수용액을 포함하는 혼합액으로 도포하여 기능성 코팅층을 형성하는 단계;       Forming a functional coating layer on at least one side of the paper sheet by applying a superabsorbent polymer and a hygroscopic inorganic salt aqueous solution;

상기 기능성 코팅층이 형성된 종이 시트를 건조하고 하나 또는 둘 이상의 개구부를 형성하여 기능성 종이 시트를 제조하는 단계; 및      Drying the paper sheet on which the functional coating layer is formed and forming one or more openings to produce a functional paper sheet; And

상기 기능성 종이 시트를 기능성 마스크의 내피, 내부, 및 외피 중 적어도 일 부분에 결합 및 일체화시켜 전술한 기능성 마스크를 제조하는 단계;를 포함하는 기능성 마스크의 제조방법이 제공된다.And bonding and integrating the functional paper sheet to at least a portion of the inner skin, the inner skin, and the outer skin of the functional mask to manufacture the functional mask.

일 측면에 따른 적어도 일면에 형성된 초흡수성(superabsorbent) 고분자 및 흡습성(hygroscopic) 무기염을 포함한 기능성 코팅층을 포함하고, 하나 또는 둘 이상의 개구부를 갖는 기능성 종이 시트를 포함하는 기능성 마스크는 향상된 제습, 항균 및 탈취의 복합기능을 제공할 수 있다. 또한 기능성 마스크의 제조방법은 시간과 비용이 절감되어 대량 생산이 가능하다.A functional mask comprising a functionalized coating layer comprising a superabsorbent polymer and a hygroscopic inorganic salt formed on at least one side along one side and having a functional paper sheet having one or more openings may be used for improved dehumidification, It is possible to provide a complex function of deodorization. In addition, the manufacturing method of the functional mask can be mass-produced because the time and cost are reduced.

도 1은 일 구현예에 따른 기능성 마스크용 기능성 종이 시트(10A)를 개략적으로 나타낸 사시도이다.
도 2는 다른 일 구현예에 따른 기능성 마스크용 기능성 종이 시트(10B)를 개략적으로 나타낸 사시도이다.
도 3은 일 구현예에 따른 기능성 마스크(100)의 구성을 개략적으로 나타낸 사시도이다.
도 4는 다른 일 구현예에 따른 기능성 마스크(100A)의 구성을 개략적으로 나타낸 사시도이다.
도 5는 다른 일 구현예에 따른 기능성 마스크(100B)의 구성을 개략적으로 나타낸 사시도이다.
도 6은 다른 일 구현예에 따른 기능성 마스크(100C)의 구성을 개략적으로 나타낸 사시도이다.
도 7은 다른 일 구현예에 따른 기능성 마스크(100D)의 구성을 개략적으로 나타낸 사시도이다.
도 8a 및 도 8b는 실시예 1에 사용된 기능성 시트의 18 시간 배양 전·후 시험 시료 Escherichia coli (ATCC 8739)에 대한 항균도 측정 결과를 나타낸 사진이다.
도 9a 및 도 9b는 실시예 1에 사용된 기능성 시트의 18 시간 배양 전·후 시험 시료 Staphylococcus aureus (ATCC 6538)에 대한 항균도 측정 결과를 나타낸 사진이다.
도 10a 및 도 10b는 실시예 1에 사용된 기능성 시트의 18 시간 배양 전·후 시험 시료 Salmonella typhimurium (KCTC 1926)에 대한 항균도 측정 결과를 나타낸 사진이다.
도 11a 및 도 11b는 실시예 1에 사용된 기능성 시트의 18 시간 배양 전·후 시험 시료 Pseudomonas aeruginosa (ATCC 9027)에 대한 항균도 측정 결과를 나타낸 사진이다.1 is a perspective view schematically showing a functional paper sheet 10A for a functional mask according to an embodiment.
2 is a perspective view schematically showing a functional paper sheet 10B for a functional mask according to another embodiment.
3 is a perspective view schematically showing a configuration of the functional mask 100 according to one embodiment.
4 is a perspective view schematically showing a configuration of the functional mask 100A according to another embodiment.
5 is a perspective view schematically showing the configuration of the functional mask 100B according to another embodiment.
6 is a perspective view schematically showing a configuration of a functional mask 100C according to another embodiment.
7 is a perspective view schematically showing a configuration of a functional mask 100D according to another embodiment.
8A and 8B are photographs showing results of measurement of antimicrobial activity against the test sample Escherichia coli (ATCC 8739) before and after 18 hours of incubation of the functional sheet used in Example 1. FIG.
FIGS. 9A and 9B are photographs showing results of measurement of antimicrobial activity against the test sample Staphylococcus aureus (ATCC 6538) before and after culturing for 18 hours in the functional sheet used in Example 1. FIG.
10A and 10B are photographs showing results of measurement of antimicrobial activity against the test sample Salmonella typhimurium (KCTC 1926) before and after 18-hour incubation of the functional sheet used in Example 1. FIG.
11A and 11B are photographs showing results of measurement of antimicrobial activity against the test sample Pseudomonas aeruginosa (ATCC 9027) before and after 18-hour incubation of the functional sheet used in Example 1. FIG.

이하에 첨부된 도면을 참조하면서, 예시적인 일 구현예에 따른 기능성 마스크용 기능성 종이 시트, 이를 포함하는 기능성 마스크, 및 상기 기능성 마스크의 제조방법에 대해서 상세하게 설명한다. 이하는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 특허청구범위의 범주에 의해 정의될 뿐이다. Hereinafter, a functional paper sheet for a functional mask, a functional mask including the same, and a method of manufacturing the functional mask according to an exemplary embodiment will be described in detail with reference to the accompanying drawings. The following is presented as an example, and the present invention is not limited thereto, and the present invention is only defined by the scope of the following claims.

일 구현예에 따른 기능성 마스크용 기능성 종이 시트는 종이 시트; 및 상기 종이 시트의 적어도 일면에 형성된 기능성 코팅층;을 포함한 기능성 종이 시트를 포함하고, 상기 기능성 코팅층은 초흡수성(superabsorbent) 고분자 및 흡습성(hygroscopic) 무기염을 포함하고, 상기 초흡수성 고분자는 55 내지 100% 상대습도의 고습도용 제1 고분자 및 10 내지 45% 상대습도의 저습도용 제2 고분자를 포함하고, 상기 기능성 종이 시트는 하나 또는 둘 이상의 개구부를 가질 수 있다. According to one embodiment, a functional paper sheet for a functional mask comprises a paper sheet; And a functional coating layer formed on at least one side of the paper sheet, wherein the functional coating layer comprises a superabsorbent polymer and a hygroscopic inorganic salt, wherein the superabsorbent polymer has a molecular weight of 55 to 100 % Relative humidity and a second polymer for low humidity with a relative humidity of 10 to 45%, wherein the functional paper sheet may have one or more openings.

본 명세서에서 '기능성 종이 시트'는 일반적인 '종이 시트'와는 달리 제습, 항균, 또는 탈취 기능, 또는 이들 복합 기능과 같은 기능을 갖는 종이 시트를 의미한다.As used herein, the term 'functional paper sheet' refers to a paper sheet having functions such as dehumidifying, antibacterial, or deodorizing functions, or a combination thereof, unlike a general 'paper sheet'.

본 명세서에서 '기능성 코팅층'은 제습, 항균, 또는 탈취 기능, 또는 이들 복합 기능과 같은 기능을 제공하는 코팅층을 의미한다.As used herein, the term " functional coating layer " refers to a coating layer that provides functions such as dehumidifying, antibacterial, or deodorizing functions, or a combination thereof.

본 명세서에서 '기능성 마스크'는 전술한 '기능성 종이 시트'를 포함하여 제습, 항균, 또는 탈취 기능, 또는 이들 복합 기능과 같은 기능을 갖게 되는 마스크를 의미한다.Herein, the term "functional mask" refers to a mask including the above-described 'functional paper sheet' and having functions such as dehumidifying, antibacterial, or deodorizing functions, or complex functions thereof.

도 1은 일 구현예에 따른 기능성 마스크용 기능성 종이 시트(10A)를 개략적으로 나타낸 사시도이다. 도 2는 다른 일 구현예에 따른 기능성 마스크용 기능성 종이 시트(10B)를 개략적으로 나타낸 사시도이다.1 is a perspective view schematically showing a functional paper sheet 10A for a functional mask according to an embodiment. 2 is a perspective view schematically showing a functional paper sheet 10B for a functional mask according to another embodiment.

도 1을 참조하면, 기능성 마스크용 기능성 종이 시트(10A)는 종이 시트(1)의 일 면에 기능성 코팅층(2)이 형성되어 있고, 하나의 개구부(3)를 가지고 있다. 도 2를 참조하면, 기능성 마스크용 기능성 종이 시트(10B)는 종이 시트(11)의 일 면에 기능성 코팅층(12)이 형성되어 있고, 랜덤하게 배치된 둘 이상의 개구부(13)를 가지고 있다. Referring to Fig. 1, a functional paper sheet 10A for a functional mask has a functional coating layer 2 formed on one side of a paper sheet 1, and has one opening 3. Referring to FIG. 2, the functional paper sheet 10B for a functional mask has a functional coating layer 12 formed on one side of a paper sheet 11 and has two or more openings 13 randomly arranged.

상기 종이 시트(1, 11)는 시트 형태의 도화지, 박엽지, 포장용지, 인쇄용지, 신문지, 골판지, 백판지, 색판지, 창호지, 습자지, 또는 휴지 등을 포함할 수 있다. 그러나 이에 제한되지 않고 당해 기술분야에서 사용 가능한 시트 형태의 모든 종이 재질의 사용이 가능하다. 일 구현예에 따른 종이 시트(1)는 골판지일 수 있다. 상기 골판지는 기능성 마스크에 사용시 무게가 가볍고 운반이 편리하며 접을 수 있고 외부의 충격에 강한 면이 있다.The paper sheets 1 and 11 may include a sheet of paper in the form of a sheet, a paper sheet, a wrapping paper, a printing paper, a newspaper, a corrugated board, a whiteboard, a color paperboard, a paper sheet, a wet paper, However, the present invention is not limited thereto, and it is possible to use all kinds of sheet materials in sheet form usable in the related art. The paper sheet 1 according to one embodiment may be cardboard. The corrugated cardboard is light in weight when used in a functional mask, is convenient to carry, has a surface that is collapsible and is resistant to external impact.

상기 기능성 코팅층(2, 12)의 두께는 2mm 이하일 수 있다. 예를 들어, 상기 기능성 코팅층(2, 12)의 두께는 0.1mm 내지 2mm일 수 있다. 상기 기능성 코팅층(2, 12)은 상기 종이 시트(1, 11)의 적어도 일면에 상기 범위 내의 얇은 두께로 형성되어, 제습 기능이 효과적으로 구현될 수 있다. The thickness of the functional coating layers 2 and 12 may be 2 mm or less. For example, the thickness of the functional coating layers 2 and 12 may be 0.1 mm to 2 mm. The functional coating layers 2 and 12 are formed on at least one side of the paper sheets 1 and 11 so as to have a small thickness within the above range so that the dehumidifying function can be effectively realized.

상기 기능성 코팅층(2, 12)은 초흡수성 고분자 및 흡습성 무기염을 포함할 수 있다. The functional coating layer (2, 12) may include a superabsorbent polymer and a hygroscopic inorganic salt.

상기 초흡수성 고분자는 55 내지 100% 상대습도의 고습도용 제1 고분자 및 10 내지 45% 상대습도의 저습도용 제2 고분자를 포함할 수 있다. 상기 초흡수성 고분자는 습기 제거를 위해 놓여지는 환경의 상대습도가 하나의 값으로 특정될 수 없기에 상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자를 적절한 비율로 혼합하여 상대습도의 변화에 관계없이 일정 수준의 제습 특성을 얻을 수 있다. 상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자는 혼합되어 약하게 교차 결합된 공중합체를 형성할 수 있다.The superabsorbent polymer may include a first polymer having a high humidity of 55 to 100% relative humidity and a second polymer having a low humidity of 10 to 45% relative humidity. Since the relative humidity of the environment in which the superabsorbent polymer is placed for moisture removal can not be specified as one value, the first polymer for high humidity and the second polymer for low humidity are mixed at an appropriate ratio, A certain level of dehumidification characteristics can be obtained. The first polymer for high humidity and the second polymer for low humidity may be mixed to form a weakly cross-linked copolymer.

상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자의 혼합 중량비는 1:1 내지 1:10 또는 1:1 내지 10:1일 수 있다. 예를 들어, 상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자의 혼합 중량비는 3:7 내지 7:3일 수 있다.The mixing ratio by weight of the first polymer for high humidity and the second polymer for low humidity may be 1: 1 to 1:10 or 1: 1 to 10: 1. For example, the mixing ratio by weight of the first polymer for high humidity and the second polymer for low humidity may be 3: 7 to 7: 3.

기능성 코팅층(2, 12)에 초흡수성 고분자 및 흡습성 무기염이 함께 사용되는 경우 기상물질에 대한 흡수력이 높은 흡습성 무기염이 먼저 습기를 흡수하여 조해(deliquescence)되고, 상기 조해에 의해 생성된 염 용액을 이후 초흡수성 고분자가 흡수하여 유지하는 형태로 제습 메커니즘이 이루어진다. 따라서 상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자의 혼합 중량비는 상대습도 및 흡습성 무기염 용액 중의 염의 농도 등에 따라 달라질 수 있다. 이에 따라, 초흡수성 폴리머에 대한 흡습성 염의 혼합비인 이온 변환 비율이 1일 때 상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자의 혼합 중량비가 상기 범위일 수 있다. When the superabsorbent polymer and the hygroscopic inorganic salt are used together in the functional coating layers 2 and 12, the hygroscopic inorganic salt having a high absorption capacity for the meteorological material first absorbs moisture and deliquescence, and the salt solution The dehydration mechanism is performed in such a manner that the superabsorbent polymer absorbs and retains it. Therefore, the mixing weight ratio of the first polymer for high humidity and the second polymer for low humidity may be varied depending on the relative humidity, the concentration of salt in the hygroscopic inorganic salt solution, and the like. Accordingly, when the ion conversion ratio, which is the mixing ratio of the hygroscopic salt to the SAP, is 1, the mixing weight ratio of the first polymer for high humidity and the second polymer for low humidity may be in the above range.

상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자는 상기 혼합 중량비의 범위 내에서 효과적인 제습이 이루어져 이를 포함하는 기능성 마스크의 반복 사용시 사용자가 쾌적감을 느낄 수 있다. 나아가 이를 포함하는 상기 기능성 마스크는 제습 기능 외에 항균 및 탈취의 복합 기능을 발휘할 수 있다.The first polymer for high humidity and the second polymer for low humidity are effectively dehumidified within the range of the mixing weight ratio, so that the user can feel comfort when repeatedly using the functional mask. Furthermore, the functional mask including the functional mask may exhibit a combined function of antibacterial and deodorizing functions in addition to the function of dehumidifying.

상기 고습도용 제1 고분자는 폴리아크릴산 및 폴리메타크릴산 중에서 선택된 1종 이상을 포함할 수 있다. 상기 고습도용 제1 고분자의 수평균분자량은 예를 들어, 10,000 내지 500,000일 수 있고, 예를 들어, 50,000 내지 400,000일 수 있고, 예를 들어, 100,000 내지 300,000일 수 있다.The high-humidity first polymer may include at least one selected from polyacrylic acid and polymethacrylic acid. The number average molecular weight of the high-humidity first polymer may be, for example, 10,000 to 500,000, for example, 50,000 to 400,000, and may be, for example, 100,000 to 300,000.

상기 저습도용 제2 고분자는 폴리아크릴아미드, 폴리비닐아민, 폴리비닐알코올, 에틸렌옥사이드, 전분, 및 셀룰로오스 중에서 선택된 1종 이상을 포함할 수 있다. 상기 저습도용 제2 고분자의 수평균분자량은 10,000 내지 500,000일 수 있고, 예를 들어, 50,000 내지 400,000일 수 있고, 예를 들어, 100,000 내지 300,000일 수 있다. The low humidity second polymer may include at least one selected from the group consisting of polyacrylamide, polyvinylamine, polyvinyl alcohol, ethylene oxide, starch, and cellulose. The number average molecular weight of the second low humidity polymer may be from 10,000 to 500,000, for example, from 50,000 to 400,000, for example, from 100,000 to 300,000.

상기 초흡수성 고분자는 카르복시메틸셀룰로오스를 더 포함할 수 있다. 카르복시메틸셀룰로오스가 초흡수성 고분자로 더 포함되는 경우 흡습성 염 용액과의 접촉을 통해 이온변환되어 작용할 수 있다. 상기 이온변환된 카르복시메틸셀룰로오스는 과립(granule) 형태로 변할 수 있다. 상기 과립 형태의 카르복시메틸셀룰로오스는 종이 시트(10A, 10B)의 적어도 일 면에 형성된 기능성 코팅층(12)에 고정될 수 있다. 상기 카르복시메틸셀룰로오스가 초흡수성 고분자로 더 포함되는 경우 제습 기능이 보다 효과적으로 구현되어 이를 포함하는 기능성 마스크의 반복 사용시 사용자가 느끼는 쾌적감이 보다 향상될 수 있다.The superabsorbent polymer may further include carboxymethylcellulose. When carboxymethylcellulose is further contained as a superabsorbent polymer, it may be ion-converted through contact with the hygroscopic salt solution. The ion-converted carboxymethylcellulose may be converted into a granule form. The granular form of carboxymethylcellulose may be fixed to the functional coating layer 12 formed on at least one side of the paper sheets 10A and 10B. When the carboxymethyl cellulose is further contained as the superabsorbent polymer, the dehumidification function can be more effectively implemented, and the user can feel more comfort when the functional mask including the carboxymethyl cellulose is repeatedly used.

상기 흡습성 무기염은 염화리튬, 염화마그네슘, 염화칼슘 및 리튬브로마이드 중에서 선택된 1종 이상을 포함할 수 있다. 상기 흡습성 무기염은 흡습성 무기염 수용액에서 3 내지 30 중량%의 농도를 가질 수 있다. 상기 흡습성 무기염은 상기 범위 내의 농도를 갖는 경우 최대이온농도에 대한 제한과 초흡수성 고분자의 최대흡수용량에 대한 제한 사이에서 흡습성 염에 의하여 이온변환된 초흡수성 고분자의 흡습 특성이 최적화될 수 있다.The hygroscopic inorganic salt may include at least one selected from lithium chloride, magnesium chloride, calcium chloride and lithium bromide. The hygroscopic inorganic salt may have a concentration of 3 to 30% by weight in the hygroscopic inorganic salt aqueous solution. When the hygroscopic inorganic salt has a concentration within the above range, the hygroscopic characteristics of the superabsorbent polymer ion-converted by the hygroscopic salt can be optimized between the restriction on the maximum ion concentration and the limitation on the maximum absorption capacity of the superabsorbent polymer.

상기 개구부(3, 13)의 면적은 상기 기능성 종이 시트(10A, 10B) 전체 면적을 기준으로 하여 5% 내지 75%일 수 있다. 예를 들어, 상기 개구부(3, 13)의 면적은 상기 기능성 종이 시트(10A, 10B) 전체 면적을 기준으로 하여 5% 내지 70%일 수 있고, 예를 들어 5% 내지 65%일 수 있고, 예를 들어 5% 내지 60%일 수 있고, 예를 들어 10% 내지 55%일 수 있고, 예를 들어 10% 내지 50%일 수 있다.The areas of the openings 3 and 13 may be 5% to 75% based on the total area of the functional paper sheets 10A and 10B. For example, the areas of the openings 3 and 13 may be 5% to 70%, for example, 5% to 65% based on the total area of the functional paper sheets 10A and 10B, For example from 5% to 60%, for example from 10% to 55%, for example from 10% to 50%.

상기 개구부(3. 13)는 상기 기능성 종이 시트(10A, 10B) 전체 면적을 기준으로 하여 상기 범위 내의 면적을 가짐으로써 제습, 항균, 및 탈취의 복합 기능을 저해하지 않는 범위에서 공기의 통과를 용이하게 하여 이를 포함하는 기능성 마스크의 사용자의 호흡이 불편하지 않게 할 수 있다.The opening (3. 13) has an area within the above range based on the total area of the functional paper sheets (10A, 10B), thereby facilitating passage of air within a range that does not hinder the combined function of dehumidification, antibacterial and deodorization So that the breathing of the user of the functional mask including the mask can be made inconvenient.

다른 일 구현예에 따른 기능성 마스크는 전술한 기능성 종이 시트를 포함할 수 있다.The functional mask according to another embodiment may include the functional paper sheet described above.

상기 기능성 종이 시트는 단일 겹 또는 복수 겹으로 적층될 수 있다.The functional paper sheet may be laminated in a single layer or a plurality of layers.

도 3은 일 구현예에 따른 기능성 마스크(100)의 구성을 개략적으로 나타낸 사시도이다.3 is a perspective view schematically showing a configuration of the functional mask 100 according to one embodiment.

도 3을 참조하면, 기능성 마스크(100)는 얼굴과 가까운 내피(100a)와 얼굴에서 먼 외피(100b) 사이에 복수 겹의 기능성 종이 시트(111)를 포함하고, 상기 기능성 종이 시트(111)는 종이 시트의 일 면에 기능성 코팅층(112)이 형성되어 있고, 그 내부에 하나의 개구부(113)를 가지고 있다. 기능성 마스크(100)는 내피(100a)와 외피(100b)의 단면에 마스크의 귀걸이(미도시)가 위치하고 있는 것으로 간주한다.3, the functional mask 100 includes a plurality of layers of functional paper sheets 111 between an inner layer 100a close to the face and an outer layer 100b far from the face, The functional coating layer 112 is formed on one side of the paper sheet and has one opening 113 in the inside thereof. The functional mask 100 is considered to have the earrings (not shown) of the mask positioned on the end faces of the inner and outer skins 100a and 100b.

상기 기능성 종이 시트는 상기 기능성 마스크와 결합되어 일체화될 수 있다. 본 명세서에서 "기능성 마스크와 결합되어 일체화"된다는 것은 기능성 마스크에 별도의 고정수단 없이 기능성 마스크와 결합되어 움직임 없이 고정되어 일체화됨을 의미한다.The functional paper sheet may be integrated with the functional mask. In the present specification, "integrated with a functional mask" means that the functional mask is fixedly integrated with the functional mask without any additional fixing means.

도 4는 다른 일 구현예에 따른 기능성 마스크(100A)의 구성을 개략적으로 나타낸 사시도이다. 도 5는 다른 일 구현예에 따른 기능성 마스크(100B)의 구성을 개략적으로 나타낸 사시도이다.4 is a perspective view schematically showing a configuration of the functional mask 100A according to another embodiment. 5 is a perspective view schematically showing the configuration of the functional mask 100B according to another embodiment.

도 4, 도 5를 참조하면, 기능성 마스크(100A, 100B)는 얼굴과 가까운 내피(101a, 101c)와 얼굴에서 먼 외피(101b, 101d) 사이에 기능성 코팅층(112a, 112b)이 형성되고 그 내부에 하나의 개구부(113a, 113b)를 갖는 단일 겹의 기능성 종이 시트(111a)를 포함하고 있다. 도 4에 따른 기능성 마스크(100A)는 내피(101a), 외피(101b), 및 기능성 종이 시트(111a)가 모두 같은 크기로 그 측면 둘레를 따라 함께 봉제(105a, 105b)되어 일체화되어 있다. 도 5에 따른 기능성 마스크(100B)는 기능성 종이 시트(111b)가 내피(101c)와 외피(101d) 사이에 작은 크기로 배치되어 내피(101c)와 외피(101d)의 측면 둘레를 따라 봉제(115c, 115d)되면 그 안에서 고정될 수 있다.Referring to FIGS. 4 and 5, the functional masks 100A and 100B have functional coating layers 112a and 112b formed between the endocapsules 101a and 101c close to the face and the outer shells 101b and 101d distant from the face, And a single-layered functional paper sheet 111a having one opening 113a and one opening 113b. The functional mask 100A according to Fig. 4 is an integrated structure in which the inner skin 101a, the outer skin 101b and the functional paper sheet 111a are all sewn together along their side edges with the same size as the sewing cloths 105a and 105b. 5, the functional paper sheet 111b is arranged in a small size between the inner and outer skins 101c and 101d so that the outer periphery of the inner and outer skins 101c and 101d along the circumference of the inner and outer skins 101c and 101d, , 115d).

이 때, 기능성 마스크(100A, 100B)는 내피(101a, 101c)와 외피(101b, 101d)의 단면에 마스크의 귀걸이(미도시)가 위치하고 있는 것으로 간주한다.At this time, the functional masks 100A and 100B are considered to have the earrings (not shown) of the mask placed on the end faces 101a and 101c and the end faces of the outer shells 101b and 101d.

도 6은 다른 일 구현예에 따른 기능성 마스크(100C)의 구성을 개략적으로 나타낸 사시도이다. 6 is a perspective view schematically showing a configuration of a functional mask 100C according to another embodiment.

도 6을 참조하면, 기능성 마스크(100C)는 얼굴과 가까운 내피(101e)의 표면에 포켓(106)이 형성되어 있다. 상기 포켓(106) 내에 기능성 종이 시트(111c)가 배치되고 상기 기능성 종이 시트(111c)는 그 일면에 기능성 코팅층(112c)이 형성되고 그 내부에 하나의 개구부(113c)를 갖고 있다. 상기 기능성 마스크(100C)는 상기 포켓(106) 내에 기능성 종이 시트(111c)가 결합되어 일체화되어 있다. 이 때, 기능성 마스크(100C)는 내피(101e)와 외피(101f)의 단면에 마스크의 귀걸이(미도시)가 위치하고 있는 것으로 간주한다.Referring to Fig. 6, the functional mask 100C has pockets 106 formed on the surface of the inner skin 101e close to the face. A functional paper sheet 111c is disposed in the pocket 106 and a functional coating layer 112c is formed on one side of the functional paper sheet 111c and has one opening 113c in the inside thereof. The functional mask 100C is integrated with the functional paper sheet 111c in the pocket 106. [ At this time, the functional mask 100C is considered to have earrings (not shown) of the mask placed on the end faces of the inner and outer skins 101e and 101f.

도 7은 다른 일 구현예에 따른 기능성 마스크(100D)의 구성을 개략적으로 나타낸 사시도이다.7 is a perspective view schematically showing a configuration of a functional mask 100D according to another embodiment.

도 7을 참조하면, 기능성 마스크(100D)는 얼굴과 가까운 내피(101g)와 얼굴에서 먼 외피(101f) 사이에 지퍼(107)가 위치하고, 그 지퍼(107) 내에 기능성 종이 시트(111d)가 배치되어 있다. 상기 기능성 종이 시트(111d)는 그 일면에 기능성 코팅층(112d)이 형성되고 그 내부에 네 개의 개구부(113d)를 갖고 있다. 상기 기능성 마스크(100D)는 상기 지퍼(107) 내에 기능성 종이 시트(111d)가 결합되어 일체화되어 있다. 이 때, 기능성 마스크(100D)는 내피(101g)와 외피(101h)의 단면에 마스크의 귀걸이(미도시)가 위치하고 있는 것으로 간주한다.7, in the functional mask 100D, the zipper 107 is positioned between the inner surface 101g close to the face and the outer surface 101f distant from the face, and the functional paper sheet 111d is placed in the zipper 107 . The functional paper sheet 111d has a functional coating layer 112d formed on one side thereof and four openings 113d in the functional paper sheet 111d. In the functional mask 100D, the functional paper sheet 111d is combined with the zipper 107 and integrated. At this time, the functional mask 100D is considered to have earrings (not shown) of the mask placed on the end faces of the inner and outer skins 101g and 101h.

상기 기능성 종이 시트(111a, 111b, 111c, 111d)는 30℃의 온도, 90%의 상대습도에서 최대 흡습량이 240% 이상일 수 있다. 상기 기능성 종이 시트(111a, 111b, 111c, 111d)는 암모니아 및 트리메틸아민에 대한 탈취율이 99% 이상일 수 있다. 상기 기능성 종이 시트(111a, 111b, 111c, 111d)는 에쉬리치아(Escherichia coli), 스테필로코쿠스 아우레우스(Staphylococcus aureus), 살모넬라 티피무리움(Salmonella typhimurium), 및 피쉐우도모나스 아루기노사(Pseudomonas aeruginosa)에 대한 항균력이 99% 이상일 수 있다.The functional paper sheets 111a, 111b, 111c and 111d may have a maximum moisture absorption of 240% or more at a temperature of 30 ° C and a relative humidity of 90%. The functional paper sheets 111a, 111b, 111c, and 111d may have a deodorization rate of more than 99% with respect to ammonia and trimethylamine. The functional paper sheets 111a, 111b, 111c, and 111d may be made of a material selected from the group consisting of Escherichia coli, Staphylococcus aureus, Salmonella typhimurium, (Pseudomonas aeruginosa) may be more than 99%.

상기 기능성 마스크(100A, 100B, 100C, 100D)는 제습, 항균 및 탈취의 복합기능을 가질 수 있다. 상기 기능성 마스크(100A, 100B, 100C, 100D)는 스포츠용 또는 황사용일 수 있다.The functional masks 100A, 100B, 100C, and 100D may have a combined function of dehumidification, antibacterial and deodorization. The functional masks 100A, 100B, 100C, and 100D may be for sport or sulfur use.

다른 일 구현예에 따른 기능성 마스크의 제조방법은 종이 시트를 준비하는 단계; 상기 종이 시트의 적어도 일면에 초흡수성(superabsorbent) 고분자, 및 흡습성(hygroscopic) 무기염 수용액을 포함하는 혼합액으로 도포하여 기능성 코팅층을 형성하는 단계; 상기 기능성 코팅층이 형성된 종이 시트를 건조하고 하나 또는 둘 이상의 개구부를 형성하여 기능성 종이 시트를 제조하는 단계; 및 상기 기능성 종이 시트를 기능성 마스크의 내피, 내부, 및 외피 중 적어도 일 부분에 결합 및 일체화시켜 전술한 기능성 마스크를 제조하는 단계;를 포함할 수 있다.A method of manufacturing a functional mask according to another embodiment includes the steps of preparing a paper sheet; Forming a functional coating layer on at least one side of the paper sheet by applying a superabsorbent polymer and a hygroscopic inorganic salt aqueous solution; Drying the paper sheet on which the functional coating layer is formed and forming one or more openings to produce a functional paper sheet; And combining and integrating the functional paper sheet with at least a portion of the inner skin, the inner skin, and the outer skin of the functional mask to produce the functional mask described above.

상기 기능성 마스크의 제조방법은 먼저 종이 시트를 준비한다. 상기 종이 시트의 구체적인 종류에 대해서는 전술한 바와 같으므로 이하 설명을 생략한다.In the method of manufacturing the functional mask, a paper sheet is first prepared. Since the specific kind of the paper sheet is as described above, the description will be omitted.

다음으로, 상기 종이 시트의 적어도 일면에 초흡수성(superabsorbent) 고분자 및 흡습성(hygroscopic) 무기염 수용액을 포함하는 혼합액으로 도포하여 기능성 코팅층을 형성한다. 상기 도포방법은 바코팅, 스프레이 코팅, 스크린 인쇄, 롤 코팅, 에어 나이프 코팅, 또는 블레이드 코팅 등을 이용할 수 있으나 이에 제한되지 않고 당해 기술분야에서 사용 가능한 도포방법의 사용이 가능하다. 상기 초흡수성 고분자 및 흡습성 무기염 수용액의 구체적인 종류, 혼합 중량비, 및 흡습성 무기염의 농도 등에 대해서는 전술한 바와 같으므로 이하 설명을 생략한다.Next, a functional coating layer is formed on at least one side of the paper sheet with a mixed solution containing a superabsorbent polymer and a hygroscopic inorganic salt aqueous solution. The coating method may be a bar coating, a spray coating, a screen printing, a roll coating, an air knife coating, a blade coating, or the like, but the present invention is not limited thereto. The specific kinds, the mixing weight ratio, the concentration of the hygroscopic inorganic salt, and the like of the aqueous superabsorbent polymer and the hygroscopic inorganic salt aqueous solution are as described above, and the description thereof is omitted.

상기 초흡수성 고분자 및 흡습성 무기염 수용액을 포함하는 혼합액을 제조하기 전, 초흡수성 고분자를 진공 건조기에서 건조하는 단계를 더 포함할 수 있다. 상기 초흡수성 고분자의 잔여습기를 가능한 한 극미하게 유지하여, 초흡수성 고분자와 흡습성 무기염 수용액과 혼합할 때 가능한 한 많은 양의 염 수용액의 흡수가 가능하게 할 수 있다.The method may further include drying the superabsorbent polymer in a vacuum dryer before preparing a mixed solution containing the superabsorbent polymer and the hygroscopic inorganic salt aqueous solution. The residual moisture of the superabsorbent polymer is kept as fine as possible so that it is possible to absorb as much amount of aqueous salt solution as possible when mixing the superabsorbent polymer and the hygroscopic inorganic salt aqueous solution.

다음으로, 상기 기능성 코팅층이 형성된 종이 시트를 건조한다. 상기 건조 과정에서 덩어리(lump)가 형성되는 경우 분쇄하는 단계를 더 포함할 수 있다. 분쇄도구로는 예를 들어, 충격 조쇄기(impact crusher) 또는 파쇄기(breaker) 등이 사용가능하나, 이에 제한되지 않고 당해 기술분야에서 사용 가능한 분쇄도구의 사용이 가능하다.Next, the paper sheet on which the functional coating layer is formed is dried. And a step of grinding if a lump is formed in the drying process. As the crushing tool, for example, an impact crusher or a breaker can be used, but the present invention is not limited thereto, and it is possible to use a crushing tool available in the related art.

다음으로, 건조된 기능성 코팅층이 형성된 종이 시트 내에 하나 또는 둘 이상의 개구부를 형성하여 기능성 종이 시트를 제조한다. 개구부를 형성하기 위한 도구로는 펀치 또는 드릴 등이 사용가능하나, 이에 제한되지 않고 당해 기술분야에서 사용 가능한 개구부 형성용 도구의 사용이 가능하다.Next, one or two or more openings are formed in the paper sheet on which the dried functional coating layer is formed to produce a functional paper sheet. As the tool for forming the opening, a punch or a drill can be used, but not limited thereto, it is possible to use a tool for forming an opening usable in the technical field.

다음으로, 상기 기능성 종이 시트를 기능성 마스크의 내피, 내부, 및 외피 중 적어도 일 부분에 결합 및 일체화시켜 전술한 기능성 마스크를 제조한다. 상기 단계는 예를 들어, 도 4, 도 5, 도 6, 및 도 7에 기재하였는바 이에 대한 설명을 생략한다.Next, the above-described functional mask is manufactured by bonding and integrating the functional paper sheet to at least one portion of the inner surface, the inner surface, and the outer surface of the functional mask. The above steps are described in, for example, FIGS. 4, 5, 6, and 7, and a description thereof will be omitted.

상기 기능성 마스크의 제조방법은 제조과정이 복잡하지 않아 시간과 비용이 절감되어 대량 생산이 가능하다.The manufacturing method of the functional mask is not complicated and it is possible to mass-produce the functional mask with reduced time and cost.

이하 본 발명의 실시예 및 비교예를 기재한다. 그러나 하기 실시예는 본 발명의 일 실시예일뿐 본 발명이 하기 실시예에 한정되는 것은 아니다.Hereinafter, examples and comparative examples of the present invention will be described. However, the following examples are only illustrative of the present invention, and the present invention is not limited to the following examples.

[실시예][Example]

실시예Example 1: 기능성 마스크 제조 1: Functional mask manufacturing

약 8cm x 12cm이며 두께가 약 200μm인 시트를 준비하였다. 상기 시트의 일면에, 고습도용 제1 고분자인 폴리아크릴산(분자량: 약 130,000, Aldrich사 제조)과 저습도용 제2 고분자인 폴리아크릴아미드(분자량: 약 150,000, Aldrich사 제조)를 각각 7:3의 중량비로 혼합한 초흡수성(superabsorbent) 고분자와, 약 25중량% 농도의 염화리튬 수용액을 혼합한 혼합액을 바코터로 도포하여 약 2mm 두께의 기능성 코팅층을 형성하였다. 상기 기능성 코팅층이 형성된 시트를 80℃ 오븐에서 약 1시간 동안 건조하고 상기 시트의 중간에 약 1mm 직경의 다수의 개구부를 형성한 기능성 시트를 제조하였다. 상기 기능성 시트를 기능성 마스크의 내피와 외피 사이의 내부에 배치하고 상기 내피와 외피의 양 측면을 따라 봉제하여 결합 및 일체화시킨 기능성 마스크를 제조하였다. A sheet about 8 cm x 12 cm and a thickness of about 200 m was prepared. Polyacrylic acid (molecular weight: about 130,000, manufactured by Aldrich) and polyacrylamide (molecular weight: about 150,000, manufactured by Aldrich), which is a second high molecular compound for low humidity, were mixed in a ratio of 7: 3 A mixture of superabsorbent polymer mixed in a weight ratio and a lithium chloride aqueous solution having a concentration of about 25 wt% was applied by a bar coater to form a functional coating layer having a thickness of about 2 mm. The sheet having the functional coating layer formed thereon was dried in an oven at 80 캜 for about 1 hour to prepare a functional sheet having a plurality of openings each having a diameter of about 1 mm formed in the middle of the sheet. The functional sheet was disposed between the inner skin and the outer skin of the functional mask and sewed along both side surfaces of the inner skin and the outer skin to form a functional mask in which the functional skin was combined and integrated.

비교예Comparative Example 1: 마스크 제조 1: Mask manufacturing

실시예 1의 기능성 시트가 포함되지 않은 마스크를 준비하였다.A mask not containing the functional sheet of Example 1 was prepared.

(기능성 시트의 기능 평가)(Functional Evaluation of Functional Sheet)

평가예Evaluation example 1: 최대  1: maximum 흡습량Moisture absorption amount 측정 Measure

실시예 1에 사용된 기능성 시트를 80℃의 열풍 건조기에서 2시간 동안 사전 건조한 후, 30℃/상대습도 90%를 유지하는 항온 항습기에 보관하면서 시간대 별로 흡습량을 측정하였고, 무게 변화가 없을 때의 흡습량을 측정하여 이로부터 최대 흡습량을 구하였다. 동일한 과정을 4회 반복하여 최대 흡습량을 구한 후 그 평균값을 구하였다. 그 결과를 하기 [표 1]에 나타내었다.     The functional sheet used in Example 1 was preliminarily dried in a hot air drier at 80 ° C for 2 hours and then stored in a thermo-hygrostat maintained at 30 ° C / relative humidity of 90% Was measured, and the maximum moisture absorption amount was determined therefrom. The same procedure was repeated 4 times to obtain the maximum moisture absorption amount, and the average value was obtained. The results are shown in Table 1 below.

구분division 최대 흡습량
(%, 4회 평균값)Maximum moisture absorption
(%, Average of 4 times) 실시예 1Example 1 241.1241.1

상기 [표 1]을 참조하면, 실시예 1에 사용된 기능성 시트는 30℃의 온도, 90%의 상대습도에서 최대 흡습량이 240% 이상임을 확인할 수 있다.Referring to Table 1, it can be confirmed that the functional sheet used in Example 1 has a maximum moisture absorption of 240% or more at a temperature of 30 ° C and a relative humidity of 90%.

평가예Evaluation example 2: 탈취율 측정 2: Measurement of deodorization rate

실시예 1 및 비교예 1에 사용된 기능성 시트에 대하여 80℃의 열풍 건조기에서 3시간 동안 사전건조한 후, 가스검지관법을 이용하여 탈취율(%)을 측정하였다. The functional sheets used in Example 1 and Comparative Example 1 were preliminarily dried for 3 hours in a hot-air drier at 80 ° C, and then the deodorization rate (%) was measured using a gas detection tube method.

·시험편: 10cm x 10cm· Test piece: 10cm x 10cm

·가스백: 5L· Gas bag: 5L

·가스백 내 가스량: 3L· Gas volume in gas bag: 3L

·측정시간: 2시간 · Measurement time: 2 hours

·초기농도(ppm): 암모니아: 100 ppm, 포름알데히드: 15 ppm, Initial concentration (ppm): Ammonia: 100 ppm, Formaldehyde: 15 ppm,

아세트알데히드: 13 ppm, 아세트산: 60 ppm                 Acetaldehyde: 13 ppm, acetic acid: 60 ppm

트리메틸아민: 28 ppm, 메틸메르캅탄: 8 ppm                 Trimethylamine: 28 ppm, methylmercaptan: 8 ppm

·탈취율(%) = [(Cb-Cs)/Cb) x 100]Deodorization rate (%) = [(Cb-Cs) / Cb) x 100]

·Cb는 블랭크, 2시간 경과 후 시험가스 백 안에 남아 있는 시험가스의 농도Cb is the blank, the concentration of the test gas remaining in the test gas bag after 2 hours

·Cs는 시료, 2시간 경과 후 시험가스 백 안에 남아 있는 시험가스의 농도Cs is the concentration of the test gas remaining in the test gas bag after 2 hours

상기 실시예 1에 사용된 기능성 시트의 탈취율(%) 결과를 하기 [표 2]에 나타내었다.The deodorization rate (%) of the functional sheet used in Example 1 is shown in Table 2 below.

시험가스 항목 구분Test Gas Category 탈취율(%)Deodorization rate (%) 암모니아ammonia > 99.8> 99.8 포름알데히드Formaldehyde 20.020.0 아세트알데히드Acetaldehyde > 99.6> 99.6 아세트산Acetic acid 2.52.5 트리메틸아민Trimethylamine 23.123.1 메틸메르캅탄Methyl mercaptan 94.094.0

상기 [표 2]를 참조하면, 상기 실시예 1에 사용된 기능성 시트는 암모니아 및 트리메틸아민에 대한 탈취율이 99% 이상임을 확인할 수 있다.      Referring to Table 2, it can be confirmed that the functional sheet used in Example 1 has a deodorization rate of 99% or more with respect to ammonia and trimethylamine.

반면, 비교예 1에 사용된 기능성 시트는 암모니아, 포름알데히드, 아세트알데히드, 아세트산, 트리메틸아민, 및 메틸메트캅탄에 대한 탈취율이 모두 1% 미만이었다.  On the other hand, the functional sheet used in Comparative Example 1 had less than 1% deodorization rate with respect to ammonia, formaldehyde, acetaldehyde, acetic acid, trimethylamine, and methylmercaptane.

평가예Evaluation example 3: 항균도 측정 3: Antimicrobial activity measurement

실시예 1 및 비교예 1에 사용된 기능성 시트에 대하여 항균도 조사를 KS J 0693법에 따라 실시하였다. 시험균주로 에쉬리치아(Escherichia coli ATCC 8739), 스테필로코쿠스 아우레우스(Staphylococcus aureus ATCC 6538), 살모넬라 티피무리움(Salmonella typhimurium KCTC 1926), 및 피쉐우도모나스 아루기노사(Pseudomonas aeruginosa ATCC 9027)의 공시균을 사용하였다.Example 1 And the functional sheet used in Comparative Example 1 were subjected to the antibacterial activity test according to the method of KS J 0693. As test strains Escherichia coli ATCC 8739, Staphylococcus aureus ATCC 6538, Salmonella typhimurium KCTC 1926, and Pseudomonas aeruginosa ATCC 9027 ) Were used.

·시험조건: 시험균액을 (29 ± 1℃ )에서 18시간 진탕 배양 후 균수 측정 (진탕 횟수 120 회/분)Test conditions: The test strain was incubated with shaking for 18 hours at (29 ± 1 ° C), and the number of bacteria was measured (120 times / minute of shaking)

·시험시료 중량: 0.4gTest sample weight: 0.4 g

·중화용액: 인산완충용액 (pH 7.0 ± 0.2)Neutral solution: Phosphate buffer solution (pH 7.0 ± 0.2)

·감소율(%): [(Mb - Mc) / Mb] x 100Reduction ratio (%): [(Mb - Mc) / Mb] x 100

·Ma: 대조시료의 초기 균수 (평균치)Ma: Initial number of bacteria in the control sample (average value)

·Mb: 18 시간 배양 후 대조 시료의 생균수 (평균치)Mb: the number of living cells of the control sample after 18 hours of culture (average value)

·Mc: 18 시간 배양 후 시험 시료의 생균수 (평균치)Mc: Number of live cells of the test sample after 18 hours of culture (average value)

실시예 1에 사용된 기능성 시트에 대하여 각 실험균주에 대한 항균도(균 감소율, %) 측정 결과를 하기[표 3], 도 8a, 도 8b, 도 9a, 도 9b, 도 10a, 도 10b, 도 11a, 및 도 11b에 나타내었다.The results of measurement of the antibacterial activity (% reduction rate) of each of the experimental strains for the functional sheet used in Example 1 are shown in the following Table 3, 8a, 8b, 9a, 9b, 10a, 10b, 11A and 11B.

시험균주Test strain Ma(CFU/mL)Ma (CFU / mL) MbMb McMc 항균도(%)Antimicrobial activity (%) Escherichia coli
(ATCC 8739)Escherichia coli
(ATCC 8739) 1.0 x 105 1.0 x 10 5 3.2 x 106 3.2 x 10 6 7.0 x 102 7.0 x 10 2 99.999.9 Staphylococcus aureus
(ATCC 6538)Staphylococcus aureus
(ATCC 6538) 1.2 x 105 1.2 x 10 5 3.8 x 106 3.8 x 10 6 9.1 x 102 9.1 x 10 2 99.999.9 Salmonella typhimurium
(KCTC 1926)Salmonella typhimurium
(KCTC 1926) 1.2 x 105 1.2 x 10 5 3.3 x 106 3.3 x 10 6 2.1 x 102 2.1 x 10 2 99.999.9 Pseudomonas aeruginosa
(ATCC 9027)Pseudomonas aeruginosa
(ATCC 9027) 1.1 x 105 1.1 x 10 5 3.5 x 106 3.5 x 10 6 < 10<10 99.999.9

(*CFU = Colony Forming Unit, < = 미만)(* CFU = Colony Forming Unit, <= less)

상기 [표 3], 도 8a, 도 8b, 도 9a, 도 9b, 도 10a, 도 10b, 도 11a, 및 도 11b를 참조하면, 실시예 1에 사용된 기능성 시트는 에쉬리치아(Escherichia coli), 스테필로코쿠스 아우레우스(Staphylococcus aureus), 살모넬라 티피무리움(Salmonella typhimurium), 및 피쉐우도모나스 아루기노사(Pseudomonas aeruginosa)에 대한 항균력이 99% 이상임을 확인할 수 있다.     Referring to Table 3, Figs. 8A, 8B, 9A, 9B, 10A, 10B, 11A, and 11B, the functional sheet used in Example 1 includes Escherichia coli, , Staphylococcus aureus, Salmonella typhimurium, and Pseudomonas aeruginosa are 99% or more in terms of antimicrobial activity.

반면, 비교예 1에 사용된 기능성 시트는 에쉬리치아(Escherichia coli), 스테필로코쿠스 아우레우스(Staphylococcus aureus), 살모넬라 티피무리움(Salmonella typhimurium), 및 피쉐우도모나스 아루기노사(Pseudomonas aeruginosa)에 대한 항균력이 모두 1% 미만이었다.  On the other hand, the functional sheet used in Comparative Example 1 includes Escherichia coli, Staphylococcus aureus, Salmonella typhimurium, and Pseudomonas aeruginosa ) Were all less than 1%.

이상, 첨부도면을 참조하면서 실시예들에 대해서 상세하게 설명하였지만, 본 발명은 관련례에 한정되지 않는다. 본 발명이 속하는 기술분야에 있어서 통상의 지식을 가진 자라면, 특허청구범위에 기재된 기술적 사상의 범주 내에서 각종 변경례 또는 수정례에 생각이 미치는 것은 분명하며, 이들에 대해서도 당연히 본 발명의 기술적 범위에 속하는 것으로 이해된다.While the embodiments have been described in detail with reference to the accompanying drawings, the present invention is not limited to the embodiments. It will be understood by those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the invention as defined in the appended claims. . &Lt; / RTI &gt;

1, 11: 종이 시트,
2, 12, 112, 112a, 112b, 112c, 112d: 기능성 코팅층,
3, 13, 113, 113a, 113b, 113c, 113d: 개구부,
10A, 10B, 111, 111a, 111b, 111c, 111d: 기능성 종이 시트,
100, 100A, 100B, 100C, 100D: 기능성 마스크,
100a, 101a, 101c, 101e, 101g: 내피,
100b, 101b, 101d, 101f, 101h: 외피,
105a, 105b, 115c, 115d: 봉제(선), 106: 포켓, 107: 지퍼1, 11: paper sheet,
2, 12, 112, 112a, 112b, 112c, 112d: a functional coating layer,
3, 13, 113, 113a, 113b, 113c, 113d:
10A, 10B, 111, 111a, 111b, 111c and 111d: a functional paper sheet,
100, 100A, 100B, 100C, 100D: functional mask,
100a, 101a, 101c, 101e, 101g:
100b, 101b, 101d, 101f, 101h:
105a, 105b, 115c, 115d: sewing (line), 106: pocket, 107: zipper

Claims (18)

종이 시트; 및
상기 종이 시트의 적어도 일면에 형성된 기능성 코팅층;을 포함한 기능성 종이 시트를 포함하고,
상기 기능성 코팅층은 초흡수성(superabsorbent) 고분자 및 흡습성(hygroscopic) 무기염을 포함하고,
상기 초흡수성 고분자는 55 내지 100% 상대습도의 고습도용 제1 고분자 및 10 내지 45% 상대습도의 저습도용 제2 고분자를 포함하고,
상기 기능성 종이 시트는 하나 또는 둘 이상의 개구부를 갖는 기능성 마스크용 기능성 종이 시트.Paper sheet; And
And a functional coating layer formed on at least one side of the paper sheet,
Wherein the functional coating layer comprises a superabsorbent polymer and a hygroscopic inorganic salt,
Wherein the superabsorbent polymer comprises a first polymer for high humidity at a relative humidity of 55 to 100% and a second polymer for low humidity at a relative humidity of 10 to 45%
Wherein the functional paper sheet has one or two or more openings. 제1항에 있어서,
상기 기능성 코팅층의 두께는 2mm 이하인 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the thickness of the functional coating layer is 2 mm or less. 제1항에 있어서,
상기 고습도용 제1 고분자와 상기 저습도용 제2 고분자의 혼합 중량비는 1:1 내지 1:10 또는 1:1 내지 10:1인 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the mixing ratio by weight of the first polymer for high humidity and the second polymer for low humidity is 1: 1 to 1:10 or 1: 1 to 10: 1. 제1항에 있어서,
상기 고습도용 제1 고분자는 폴리아크릴산 및 폴리메타크릴산 중에서 선택된 1종 이상을 포함하는 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the high-humidity first polymer comprises at least one selected from the group consisting of polyacrylic acid and polymethacrylic acid. 제1항에 있어서,
상기 저습도용 제2 고분자는 폴리아크릴아미드, 폴리비닐아민, 폴리비닐알코올, 에틸렌옥사이드, 전분, 및 셀룰로오스 중에서 선택된 1종 이상을 포함하는 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the low humidity second polymer includes at least one selected from the group consisting of polyacrylamide, polyvinylamine, polyvinyl alcohol, ethylene oxide, starch, and cellulose. 제1항에 있어서,
상기 초흡수성(superabsorbent) 고분자는 카르복시메틸셀룰로오스를 더 포함하는 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the superabsorbent polymer further comprises carboxymethylcellulose. 제1항에 있어서,
상기 흡습성(hygroscopic) 무기염은 염화리튬, 염화마그네슘, 염화칼슘 및 리튬브로마이드 중에서 선택된 1종 이상을 포함하는 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the hygroscopic inorganic salt comprises at least one selected from the group consisting of lithium chloride, magnesium chloride, calcium chloride, and lithium bromide. 제1항에 있어서,
상기 흡습성(hygroscopic) 무기염은 흡습성(hygroscopic) 무기염 수용액에서 3 내지 30 중량%의 농도를 갖는 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
The hygroscopic inorganic salt has a concentration of 3 to 30% by weight in a hygroscopic inorganic salt aqueous solution. 제1항에 있어서,
상기 개구부의 면적은 상기 기능성 종이 시트 전체 면적을 기준으로 하여 5% 내지 75%인 기능성 마스크용 기능성 종이 시트.The method according to claim 1,
Wherein the area of the opening is 5% to 75% based on the total area of the functional paper sheet. 제1항 내지 제9항 중 어느 한 항에 따른 기능성 종이 시트를 포함하는 기능성 마스크.A functional mask comprising a functional paper sheet according to any one of claims 1 to 9. 제10항에 있어서,
상기 기능성 종이 시트는 단일 겹 또는 복수 겹으로 적층된 기능성 마스크.11. The method of claim 10,
Wherein the functional paper sheet is laminated in a single layer or a plurality of layers. 제10항에 있어서,
상기 기능성 종이 시트는 상기 기능성 마스크와 결합되어 일체화된 기능성 마스크.11. The method of claim 10,
Wherein the functional paper sheet is integrated with the functional mask. 제10항에 있어서,
상기 기능성 종이 시트는 30℃의 온도, 90%의 상대습도에서 최대 흡습량이 240% 이상인 기능성 마스크.11. The method of claim 10,
Wherein said functional paper sheet has a maximum moisture absorption of 240% or more at a temperature of 30 DEG C and a relative humidity of 90%. 제10항에 있어서,
상기 기능성 종이 시트는 암모니아 및 트리메틸아민에 대한 탈취율이 99% 이상인 기능성 마스크.11. The method of claim 10,
Wherein the functional paper sheet has a deodorization ratio of ammonia and trimethylamine of 99% or more. 제10항에 있어서,
상기 기능성 종이 시트는 에쉬리치아(Escherichia coli), 스테필로코쿠스 아우레우스(Staphylococcus aureus), 살모넬라 티피무리움(Salmonella typhimurium), 및 피쉐우도모나스 아루기노사(Pseudomonas aeruginosa)에 대한 항균력이 99% 이상인 기능성 마스크.11. The method of claim 10,
The functional paper sheet has a antibacterial activity against Escherichia coli, Staphylococcus aureus, Salmonella typhimurium, and Pseudomonas aeruginosa of 99 % Functional mask. 제10항에 있어서,
상기 기능성 마스크는 제습, 항균 및 탈취의 복합기능을 갖는 기능성 마스크.11. The method of claim 10,
Wherein the functional mask has a combined function of dehumidification, antibacterial and deodorization. 제10항에 있어서,
상기 기능성 마스크는 스포츠용 또는 황사용 마스크를 포함하는 기능성 마스크.11. The method of claim 10,
Wherein the functional mask comprises a sports or sulfur-use mask. 종이 시트를 준비하는 단계;
상기 종이 시트의 적어도 일면에 초흡수성(superabsorbent) 고분자, 및 흡습성(hygroscopic) 무기염 수용액을 포함하는 혼합액으로 도포하여 기능성 코팅층을 형성하는 단계;
상기 기능성 코팅층이 형성된 종이 시트를 건조하고 하나 또는 둘 이상의 개구부를 형성하여 기능성 종이 시트를 제조하는 단계; 및
상기 기능성 종이 시트를 기능성 마스크의 내피, 내부, 및 외피 중 적어도 일 부분에 결합 및 일체화시켜 제10항에 따른 기능성 마스크를 제조하는 단계;를 포함하는 기능성 마스크의 제조방법.Preparing a paper sheet;
Forming a functional coating layer on at least one side of the paper sheet by applying a superabsorbent polymer and a hygroscopic inorganic salt aqueous solution;
Drying the paper sheet on which the functional coating layer is formed and forming one or more openings to produce a functional paper sheet; And
And bonding the functional paper sheet to at least a portion of the inner skin, the inner skin, and the outer skin of the functional mask to manufacture the functional mask according to claim 10.
KR1020170108133A 2017-08-25 2017-08-25 Functional paper sheet for functional mask, functional mask including the same, and method of preparing the functional mask KR102023097B1 (en)