KR20180114603A - Water solubility flame proof spray composition - Google Patents
Water solubility flame proof spray composition Download PDFInfo
- Publication number
- KR20180114603A KR20180114603A KR1020170046476A KR20170046476A KR20180114603A KR 20180114603 A KR20180114603 A KR 20180114603A KR 1020170046476 A KR1020170046476 A KR 1020170046476A KR 20170046476 A KR20170046476 A KR 20170046476A KR 20180114603 A KR20180114603 A KR 20180114603A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- water
- soluble resin
- composition
- Prior art date
Abstract
Description
본 발명은 수용성 방염 스프레이 조성물에 관한 것이다.The present invention relates to a water-soluble flame retardant spray composition.
방염 스프레이 조성물은 스프레이 기구 등을 통해 산업 현장 등에 뿌려져서, 화재 발생 시에 착화 시간을 지연시켜 주고, 일정 정도 착화 자체도 막아줄 수 있는 조성물을 말한다.The flame retardant spray composition refers to a composition that is sprayed on an industrial site through a spray apparatus or the like to delay ignition time in the event of a fire and also to prevent ignition itself to a certain extent.
이러한 방염 스프레이 조성물의 예로 제시될 수 있는 것이 아래 제시된 특허문헌의 그 것이다.One example of such an anti-fog spray composition is that of the patent literature presented below.
종래에는, 방염 스프레이 조성물로 유성 물질이 많이 이용되었는데, 이러한 유성 물질에 의하면, 용매가 톨루엔 등 인체에 유해한 것이어서, 휘발성유기화합물(VOC) 증가의 원인이 되었다.Conventionally, oily substances are widely used as an anti-flame spray composition. According to such an oily substance, the solvent is harmful to the human body such as toluene, which causes the increase of volatile organic compounds (VOC).
이러한 문제 해소를 위하여, 방염 스프레이 조성물로 수성 물질이 이용되기 위해 시도되고 있는데, 이러한 수성 물질의 경우, 용매가 물이기 때문에, 디메틸에테르가스 등의 충진 가스가 그 물과 만나면서 충진 가스가 분해되어버려 분사가 잘 되지 않는 문제가 있었다.In order to solve such a problem, an attempt has been made to use an aqueous material as an anti-flame spray composition. In the case of such an aqueous material, since the solvent is water, a filling gas such as a dimethyl ether gas, There was a problem that spraying did not work well.
본 발명은 친환경적인 수성 물질이면서도 분사가 잘 이루어질 수 있는 수용성 방염 스프레이 조성물을 제공하는 것을 일 목적으로 한다.It is an object of the present invention to provide a water-based flame retardant spray composition which can be sprayed well even though it is an environmentally friendly aqueous material.
본 발명의 일 측면에 따른 수용성 방염 스프레이 조성물은 인산암모늄(ammonium phosphate)과, 실리카 에어로겔(silica aerogel)과, 에어로졸 조성물로 구성되되, 상기 에어로졸 조성물은 캐리어, 수용성 수지, 소포제, 분산제, 계면활성제, 침강방지제 및 안료로 구성되는 것을 특징으로 한다.The water-soluble flame retardant spray composition according to one aspect of the present invention comprises ammonium phosphate, silica aerogel, and an aerosol composition, wherein the aerosol composition comprises a carrier, a water-soluble resin, a defoamer, a dispersant, An anti-settling agent and a pigment.
본 발명의 일 측면에 따른 수용성 방염 스프레이 조성물에 의하면, 수용성 방염 스프레이 조성물이 인산암모늄과, 실리카 에어로겔과, 에어로졸 조성물로 구성되되, 상기 에어로졸 조성물은 캐리어, 수용성 수지, 소포제, 분산제, 계면활성제, 침강방지제 및 안료로 구성됨으로써, 상기 수용성 방염 스프레이 조성물이 친환경적인 수성 물질이면서도 분사가 잘 이루어질 수 있게 되는 효과가 있다.According to one aspect of the present invention, the water-soluble flame retardant spray composition is composed of ammonium phosphate, silica airgel, and an aerosol composition, wherein the aerosol composition comprises a carrier, a water-soluble resin, a defoamer, a dispersant, An anti-flameproof spray composition can be sprayed well even though it is an environmentally friendly aqueous material.
이하에서는 본 발명의 일 실시예에 따른 수용성 방염 스프레이 조성물에 대하여 설명한다.Hereinafter, a water-soluble flame retardant spray composition according to an embodiment of the present invention will be described.
본 실시예에 따른 수용성 방염 스프레이 조성물은 인산암모늄(ammonium phosphate)과, 실리카 에어로겔(silica aerogel)과, 에어로졸 조성물로 구성되되, 상기 에어로졸 조성물은 캐리어, 수용성 수지, 소포제, 분산제, 계면활성제, 침강방지제 및 안료로 구성되는 것을 특징으로 하여, 방염, 방음, 단열 기능을 제공하는 것이다.The water-soluble flame retardant spray composition according to the present invention is composed of ammonium phosphate, silica aerogel, and an aerosol composition, wherein the aerosol composition comprises a carrier, a water-soluble resin, a defoaming agent, a dispersant, a surfactant, And a pigment, so as to provide flame retarding, soundproofing, and thermal insulation.
본 실시예에서, 상기 수용성 방염 스프레이 조성물 100중량부에 대해, 상기 인산암모늄은 5 내지 15 중량부, 상기 실리카 에어로겔은 25 내지 35 중량부 및 상기 에어로졸 조성물은 55 내지 65 중량부로 구성된다.In this embodiment, 5 to 15 parts by weight of the ammonium phosphate, 25 to 35 parts by weight of the silica airgel, and 55 to 65 parts by weight of the aerosol composition are contained in 100 parts by weight of the water-soluble flame retardant spray composition.
또한, 본 실시예에서는, 상기 캐리어는 35 내지 45 중량부, 상기 수용성 수지는 30 내지 40 중량부, 상기 소포제는 0.1 내지 1.5 중량부, 상기 분산제는 0.1 내지 1.5 중량부, 상기 계면활성제는 0.1 내지 1.5 중량부, 상기 침강방지제는 0.5 내지 1.0 중량부 및 상기 안료는 10 내지 18 중량부의 중량 비율로 상기 에어로졸 조성물에 포함되고, 상기 수용성 수지는 30 내지 35 중량부의 용매, 14 내지 16 중량부의 알킬아크릴레이트, 17 내지 42 중량부의 알킬메타아크릴레이트, 1 내지 3 중량부의 아크릴산, 3 내지 9 중량부의 메타크릴산, 1 내지 2 중량부의 반응성 가교제, 2 내지 3 중량부의 반응성 모노머, 2 내지 5 중량부의 커플링제, 15 내지 20 중량부의 점도조절제 및 1 내지 2 중량부의 촉매를 포함하되, 상기 용매, 상기 알킬아크릴레이트, 상기 알킬메타아크릴레이트, 상기 아크릴산, 상기 메타크릴산, 상기 반응성 가교제, 상기 반응성 모노머, 상기 커플링제, 상기 점도조절제 및 상기 촉매를 포함하여 형성된 상기 수용성 수지의 수평균분자량(Mn)과 산가는 각각 1000 내지 6000과 20 내지 150인 것을 특징으로 할 수 있다.In the present embodiment, the carrier is 35 to 45 parts by weight, the water-soluble resin is 30 to 40 parts by weight, the defoaming agent is 0.1 to 1.5 parts by weight, the dispersant is 0.1 to 1.5 parts by weight, 0.5 to 1.0 part by weight of the anti-settling agent and 10 to 18 parts by weight of the pigment are contained in the aerosol composition, and the water-soluble resin contains 30 to 35 parts by weight of solvent, 14 to 16 parts by weight of alkyl acrylate From 1 to 3 parts by weight of acrylic acid, from 3 to 9 parts by weight of methacrylic acid, from 1 to 2 parts by weight of reactive crosslinking agent, from 2 to 3 parts by weight of reactive monomer, from 2 to 5 parts by weight of a couple 15 to 20 parts by weight of a viscosity modifier and 1 to 2 parts by weight of a catalyst, wherein the solvent, the alkyl acrylate, the alkyl methacrylate, The number average molecular weight (Mn) and the acid value of the water-soluble resin formed from the acrylic acid, the methacrylic acid, the reactive crosslinking agent, the reactive monomer, the coupling agent, the viscosity modifier and the catalyst are 1000 to 6000, 150. ≪ / RTI >
상기 실리카 에어로겔은 비중이 매우 작은 백색 반투명의 고체로, 800℃ 정도까지는 가열에 의해 조직이 변하지 않는 성질이 있어서, 단열 및 방염 성능이 우수하다.The silica airgel is a white translucent solid having a very small specific gravity. The silica airgel has a property that the structure is not changed by heating up to about 800 ° C, and therefore, the silica airgel is excellent in heat insulation and flame retardancy.
상기 수용성 수지는 코팅 도막을 형성하기 위한 것으로, 메탈, 글래스, 우드, 스톤 등과 같은 피착제에 대한 부착성을 향상시키고, 내알칼리성, 내마모성 및 내후성을 증진시킬 수 있다.The water-soluble resin is used for forming a coating film, and it can improve the adhesion to an adherend such as metal, glass, wood, stone and the like, and can improve alkali resistance, abrasion resistance and weather resistance.
상기 에어로졸 조성물은 에어로졸의 용도 특성상 캐리어(분사체)에 안정적이어야 하기 때문에, 물 또는 알코올에 대한 용해성이 우수하여야 하는데, 본 실시예에서는, 아크릴 중합 시 라디칼 반응을 유도하여 금속, 글래스, 우드, 스톤 등과 같이 수성 코팅이 어려운 피착제에 대하여 부착성, 내수성 및 내마모성을 향상시킬 수 있다.Since the aerosol composition must be stable to a carrier (jetting material) due to its application characteristics of the aerosol, it should have excellent solubility in water or alcohol. In the present embodiment, a radical reaction is induced in the polymerization of acrylic to form a metal, glass, It is possible to improve the adhesiveness, water resistance and abrasion resistance of an adherend which is difficult to be water-coated.
본 실시예에서는, 상기 수용성 수지는 용매, 알킬아크릴레이트, 알킬메타아크릴레이트, 아크릴산, 메타크릴산, 반응성 가교제, 반응성 모노머, 커플링제, 점도조절제 및 촉매를 포함하고, 상기 수용성 수지에는 용매 30 내지 35 중량부, 알킬아크릴레이트 14 내지 16 중량부, 알킬메타아크릴레이트 17 내지 42 중량부, 아크릴산 1 내지 3 중량부, 메타크릴산 3 내지 9 중량부, 반응성 가교제 1 내지 2 중량부, 반응성 모노머 2 내지 3 중량부, 커플링제 2 내지 5 중량부, 점도조절제 15 내지 20 중량부 및 촉매 1 내지 2 중량부의 중량비율로 포함될 수 있다.In the present embodiment, the water-soluble resin includes a solvent, an alkyl acrylate, an alkyl methacrylate, an acrylic acid, a methacrylic acid, a reactive crosslinking agent, a reactive monomer, a coupling agent, a viscosity adjusting agent and a catalyst, 35 to 40 parts by weight of an alkyl acrylate, 17 to 42 parts by weight of an alkyl acrylate, 17 to 42 parts by weight of an alkyl acrylate, 1 to 3 parts by weight of an acrylic acid, 3 to 9 parts by weight of a methacrylic acid, 1 to 2 parts by weight of a reactive crosslinking agent, 2 to 5 parts by weight of a coupling agent, 15 to 20 parts by weight of a viscosity modifier and 1 to 2 parts by weight of a catalyst.
또한, 상기 용매, 상기 알킬아크릴레이트, 상기 알킬메타아크릴레이트, 상기 아크릴산, 상기 메타크릴산, 상기 반응성 가교제, 상기 반응성 모노머, 상기 커플링제, 상기 점도조절제 및 상기 촉매를 포함하여 제조되는 상기 수용성 수지는 수평균분자량(Mn)이 1000 내지 6000인 것이 바람직하다.The water-soluble resin, which is prepared by including the solvent, the alkyl acrylate, the alkyl methacrylate, the acrylic acid, the methacrylic acid, the reactive crosslinking agent, the reactive monomer, the coupling agent, the viscosity adjusting agent, (Mn) of 1000 to 6000 is preferable.
상기 용매, 상기 알킬아크릴레이트, 상기 알킬메타아크릴레이트, 상기 아크릴산, 상기 메타크릴산, 상기 반응성 가교제, 상기 반응성 모노머, 상기 커플링제, 상기 점도조절제 및 상기 촉매를 혼합한 혼합물을 85 내지 92℃의 온도에서 2 내지 3시간 동안 중합반응을 진행한 후 2 내지 3시간 동안 정치함으로써, 상기 수용성 수지가 제조될 수 있다.The mixture of the solvent, the alkyl acrylate, the alkyl methacrylate, the acrylic acid, the methacrylic acid, the reactive cross-linking agent, the reactive monomer, the coupling agent, the viscosity modifier and the catalyst is stirred at 85 to 92 ° C The water-soluble resin can be produced by allowing the polymerization reaction to proceed at a temperature of 2 to 3 hours and then allowing to stand for 2 to 3 hours.
상기 수용성 수지의 수평균분자량(Mn)이 6000을 초과하는 경우에는 상기 에어로졸 조성물의 코팅 도포 시, 수지가 미세 분산되지 않고 실처럼 늘어나게 되는 문제점이 발생할 수 있고, 1000 미만인 경우에는 원하는 물성의 에어로졸 조성물을 얻을 수 없게 된다.When the water-soluble resin has a number-average molecular weight (Mn) of more than 6,000, the resin may not be finely dispersed and may be stretched in the form of fibers when the coating of the aerosol composition is applied. Can not be obtained.
또한, 상기 수용성 수지의 산가는 20 내지 150이고, 바람직하게는 40 내지 90일 수 있다.The acid value of the water-soluble resin may be 20 to 150, preferably 40 to 90. [
상기 수용성 수지의 산가가 20 미만인 경우에는, 수용성이 떨어지는 문제점이 있고, 150을 초과하는 경우에는 건조 피막의 내수성이 나빠지는 문제점이 발생할 수 있다.When the acid value of the water-soluble resin is less than 20, there is a problem that the water-solubility is poor. When the acid value is more than 150, there is a problem that the water resistance of the dried coating is deteriorated.
상기 수용성 수지를 구성하는 상기 용매는 에탄올, 메탄올, 이소프로필알코올, 디메틸에테르 및 부틸알코올로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The solvent constituting the water-soluble resin may be at least one selected from the group consisting of ethanol, methanol, isopropyl alcohol, dimethyl ether and butyl alcohol.
상기 수용성 수지를 구성하는 상기 알킬아크릴레이트는 에틸아크릴레이트, 프로필아크릴레이트 및 부틸아크릴레이트로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The alkyl acrylate constituting the water-soluble resin may be at least one selected from the group consisting of ethyl acrylate, propyl acrylate and butyl acrylate.
상기 수용성 수지를 구성하는 상기 반응성 가교제는 카보디이미드(carbodiimide), 폴리아지리딘(polyaziridine) 및 메톡시 메티롤아크릴아마이드로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The reactive crosslinking agent constituting the water-soluble resin may be at least one selected from the group consisting of carbodiimide, polyaziridine, and methoxymethylol acrylamide.
상기 수용성 수지를 구성하는 상기 반응성 모노머는 알릴메타크릴레이트(allylmethacylate), 글리시딜 메타크릴레이트(glycidylmethacylate), β-카르복시에틸 아크릴레이트(β-carboxyethyl acrylate) 및 트리메티롤 프로판 트리메타크릴레이트(trimethylol propane trimethaylate)로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The reactive monomer constituting the water-soluble resin may be at least one selected from the group consisting of allylmethacylate, glycidylmethacylate,? -Carboxyethyl acrylate and trimethylolpropane trimethacrylate trimethylol propane trimethylacetate) may be used.
상기 수용성 수지를 구성하는 상기 커플링제는 N-(2-아미노에틸)-3-아미노프로필트리메톡시실란(N-(2-aminoethyl)-3-aminopropyltrimethoxysilane), 비닐트리에톡시실란(vinyltriethoxysilane), 3-글리시드옥시프로필 트리메톡시실란(3-glycidoxypropyl trimethoxysilane) 및 메타크릴옥시 프로필 트리메톡시실란으로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The coupling agent constituting the water-soluble resin may be selected from the group consisting of N- (2-aminoethyl) -3-aminopropyltrimethoxysilane, vinyltriethoxysilane, At least one selected from the group consisting of 3-glycidoxypropyl trimethoxysilane and methacryloxypropyltrimethoxysilane can be used.
상기 수용성 수지를 구성하는 상기 점도조절제는 상기 수용성 수지의 점도를 조절하기 위한 것으로, 본 실시예에서는 상기 점도조절제로 물이 사용될 수 있다.The viscosity adjusting agent constituting the water-soluble resin is for controlling the viscosity of the water-soluble resin. In this embodiment, water may be used as the viscosity modifier.
상기 수용성 수지를 구성하는 상기 촉매는 AIBN(4-4-azobisisobutyronitrile), BPO(benzoyl peroxide) 및 TBPB(t-butyl peroxy benzoate)로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The catalyst constituting the water-soluble resin may be at least one selected from the group consisting of AIBN (4-4-azobisisobutyronitrile), BPO (benzoyl peroxide) and TBPB (t-butyl peroxy benzoate).
상기 캐리어는 디메틸에테르가 사용될 수 있다.The carrier may be dimethyl ether.
상기 소포제는 NOPCO NXZ(Nopco Chemical사 제조), BYK-019(BYK사 제조) 및 Tego 810(Evonik사 제조)으로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The antifoaming agent may be selected from the group consisting of NOPCO NXZ (manufactured by Nopco Chemical), BYK-019 (manufactured by BYK), and Tego 810 (manufactured by Evonik).
상기 분산제는 BYK-190(BYK사 제조) 또는 Tego 760W(Evonik사 제조) 중에서 선택된 어느 하나 이상이 사용될 수 있다.The dispersant may be at least one selected from BYK-190 (manufactured by BYK) or Tego 760W (manufactured by Evonik).
상기 계면활성제는 폴리실록산 공중합체 및 폴리카복실산 중합체, 고분자량의 블록 공중합체, BYK-348(BYK사 제조) 및 폴리에테르 변성 디메칠 실록산 용액으로 이루어진 군에서 선택된 어느 하나 이상이 사용될 수 있다.The surfactant may be selected from the group consisting of a polysiloxane copolymer and a polycarboxylic acid polymer, a high molecular weight block copolymer, BYK-348 (manufactured by BYK), and a polyether-modified dimethylsiloxane solution.
상기 침강방지제는 BYK-420(BYK사 제조)이 사용될 수 있다.The anti-settling agent may be BYK-420 (manufactured by BYK).
상기 안료로는 통상의 안료가 이용될 수 있다.Conventional pigments may be used as the pigment.
이하에서는 상기 수용성 수지의 중합 실시예를 그 비교예들과 함께 설명한다.Hereinafter, polymerization examples of the water-soluble resin will be described together with comparative examples.
85 내지 92℃에서 용매를 반응기에 넣고 아크릴 모노머와 촉매의 혼합물을 투입한 후, 나머지 조성물을 모두 투입하고, 3시간 동안 중합반응을 진행한 후 85 내지 92℃에서 2시간 30분 정치하였고, 그 정치하는 동안 중합 반응의 연속적 반응이 연장되어 진행된 후 완료되었다. 이후, 물을 투입하여 점도를 6000 내지 8000cps로 조절하였다.A solvent was charged into the reactor at 85 to 92 ° C, and a mixture of the acrylic monomer and the catalyst was added. The remaining components were all charged, and the polymerization reaction was carried out for 3 hours and then allowed to stand at 85 to 92 ° C for 2 hours and 30 minutes. During the settling, the continuous reaction of the polymerization reaction was extended and completed and then completed. Thereafter, water was added to adjust the viscosity to 6000 to 8000 cps.
위와 같은 중합 반응 방법은 상기 수용성 수지의 중합 실시예 및 그 비교예들에서 동일하나, 그 사용된 촉매 및 아크릴 모노머의 종류가 각각 다르다.The above polymerization reaction method is the same in the polymerization examples of the water-soluble resin and the comparative examples, but the types of the catalyst and acrylic monomer used are different from each other.
상기 중합된 수용성 수지 조성물 45 중량부, 안료 16 중량부, BYK-348 0.1 중량부, Tego 760W 1.0 중량부 및 BYK-420 1.0 중량부를 혼합하여 에어로졸 조성물을 제조하였다.45 parts by weight of the polymerized water-soluble resin composition, 16 parts by weight of pigment, 0.1 part by weight of BYK-348, 1.0 part by weight of Tego 760W and 1.0 part by weight of BYK-420 were mixed to prepare an aerosol composition.
< 실시예 ><Examples>
< 비교예 1 >≪ Comparative Example 1 &
< 비교예 2 >≪ Comparative Example 2 &
< 비교예 3 >≪ Comparative Example 3 &
< 비교예 4 >≪ Comparative Example 4 &
< 비교예 5 >≪ Comparative Example 5 &
상기 [표 7]을 참조해 보면, 비교예 1 내지 5의 코팅제의 내마모성은 약 145mg 이었으며, 실시예의 코팅제의 내마모성은 155mg으로 향상되었음을 확인할 수 있었다.Referring to Table 7, the abrasion resistance of the coating materials of Comparative Examples 1 to 5 was about 145 mg, and the abrasion resistance of the coating material of Examples was improved to 155 mg.
도포 후 24시간 경과시킨 결과 비교예 1 내지 5의 코팅제는 수중 용해되었으며, 실시예의 코팅제는 완전히 경화되어 용해되지 않음을 확인할 수 있었다.As a result of lapse of 24 hours after application, the coating agents of Comparative Examples 1 to 5 were dissolved in water, and it was confirmed that the coating agent of the Example was completely cured and not dissolved.
도포 후 72시간 경과 후에는 비교예 1 내지 5의 코팅제도 완전히 경화되었음을 확인할 수 있었다.It was confirmed that the coating agents of Comparative Examples 1 to 5 were fully cured after 72 hours from the application.
접착력은 부착강도(N/mm2)로 확인하였다.The adhesion was confirmed by the adhesion strength (N / mm 2 ).
비교예 1 내지 5의 코팅제는 약 0.70(N/mm2)의 접착력을 보였고, 실시예의 코팅제는 0.77(N/mm2)로 부착강도가 향상되었음을 확인할 수 있었다.The coatings of Comparative Examples 1 to 5 showed an adhesion of about 0.70 (N / mm < 2 >), and the coating agent of Example was 0.77 (N / mm < 2 >).
건조속도는 모두 30 내지 35분 소요되었고, 상기 결과와 같이 완전히 경화되는 데까지 실시예의 코팅제는 24시간, 비교예 1 내지 5의 코팅제는 72시간이 소요됨을 확인할 수 있었다.The drying time was 30 to 35 minutes. As a result, it was confirmed that the coating agent of the present invention took 24 hours and the coating agent of Comparative Examples 1 to 5 took 72 hours to complete curing.
상기와 같이, 상기 수용성 방염 스프레이 조성물이 인산암모늄과, 실리카 에어로겔과, 에어로졸 조성물로 구성되되, 상기 에어로졸 조성물은 캐리어, 수용성 수지, 소포제, 분산제, 계면활성제, 침강방지제 및 안료로 구성됨으로써, 상기 수용성 방염 스프레이 조성물이 친환경적인 수성 물질이면서도 분사가 잘 이루어질 수 있게 된다.As described above, the water-soluble flame retardant spray composition is composed of ammonium phosphate, silica airgel, and an aerosol composition, wherein the aerosol composition is composed of a carrier, a water-soluble resin, a defoaming agent, a dispersant, a surfactant, The flame retardant spray composition can be sprayed well even though it is an environmentally friendly aqueous material.
상기에서 본 발명은 특정한 실시예에 관하여 도시되고 설명되었지만, 당업계에서 통상의 지식을 가진 자라면 이하의 특허청구범위에 기재된 본 발명의 사상 및 영역을 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 알 수 있을 것이다. 그렇지만 이러한 수정 및 변형 구조들은 모두 본 발명의 권리범위 내에 포함되는 것임을 분명하게 밝혀두고자 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention as defined by the following claims And can be changed. However, it is intended that the present invention covers the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents.
본 발명의 일 측면에 따른 수용성 방염 스프레이 조성물에 의하면, 친환경적인 수성 물질이면서도 분사가 잘 이루어질 수 있으므로, 그 산업상 이용가능성이 높다고 하겠다.According to the water-soluble flame retardant spray composition according to one aspect of the present invention, since it can be sprayed well even though it is an environmentally friendly aqueous material, its applicability in industry is high.
Claims (3)
상기 에어로졸 조성물은 캐리어, 수용성 수지, 소포제, 분산제, 계면활성제, 침강방지제 및 안료로 구성되는 것을 특징으로 하는 수용성 방염 스프레이 조성물.An ammonium phosphate, a silica airgel, and an aerosol composition,
Wherein the aerosol composition comprises a carrier, a water-soluble resin, a defoamer, a dispersant, a surfactant, an anti-settling agent and a pigment.
상기 수용성 방염 스프레이 조성물 100중량부에 대해, 상기 인산암모늄은 5 내지 15 중량부, 상기 실리카 에어로겔은 25 내지 35 중량부 및 상기 에어로졸 조성물은 55 내지 65 중량부로 구성되는 것을 특징으로 하는 수용성 방염 스프레이 조성물.The method according to claim 1,
Wherein the water-soluble flame retardant spray composition is composed of 5 to 15 parts by weight of ammonium phosphate, 25 to 35 parts by weight of the silica airgel, and 55 to 65 parts by weight of the aerosol composition, based on 100 parts by weight of the water- .
상기 캐리어는 35 내지 45 중량부, 상기 수용성 수지는 30 내지 40 중량부, 상기 소포제는 0.1 내지 1.5 중량부, 상기 분산제는 0.1 내지 1.5 중량부, 상기 계면활성제는 0.1 내지 1.5 중량부, 상기 침강방지제는 0.5 내지 1.0 중량부 및 상기 안료는 10 내지 18 중량부의 중량 비율로 상기 에어로졸 조성물에 포함되고,
상기 수용성 수지는 30 내지 35 중량부의 용매, 14 내지 16 중량부의 알킬아크릴레이트, 17 내지 42 중량부의 알킬메타아크릴레이트, 1 내지 3 중량부의 아크릴산, 3 내지 9 중량부의 메타크릴산, 1 내지 2 중량부의 반응성 가교제, 2 내지 3 중량부의 반응성 모노머, 2 내지 5 중량부의 커플링제, 15 내지 20 중량부의 점도조절제 및 1 내지 2 중량부의 촉매를 포함하되, 상기 용매, 상기 알킬아크릴레이트, 상기 알킬메타아크릴레이트, 상기 아크릴산, 상기 메타크릴산, 상기 반응성 가교제, 상기 반응성 모노머, 상기 커플링제, 상기 점도조절제 및 상기 촉매를 포함하여 형성된 상기 수용성 수지의 수평균분자량(Mn)과 산가는 각각 1000 내지 6000과 20 내지 150인 것을 특징으로 하는 수용성 방염 스프레이 조성물.3. The method of claim 2,
The carrier contains 35 to 45 parts by weight, the water-soluble resin is 30 to 40 parts by weight, the defoaming agent is 0.1 to 1.5 parts by weight, the dispersant is 0.1 to 1.5 parts by weight, the surfactant is 0.1 to 1.5 parts by weight, Is contained in the aerosol composition in a weight ratio of from 0.5 to 1.0 part by weight and the pigment is from 10 to 18 parts by weight,
The water-soluble resin may contain 30 to 35 parts by weight of a solvent, 14 to 16 parts by weight of alkyl acrylate, 17 to 42 parts by weight of alkyl methacrylate, 1 to 3 parts by weight of acrylic acid, 3 to 9 parts by weight of methacrylic acid, 2 to 3 parts by weight of a reactive monomer, 2 to 5 parts by weight of a coupling agent, 15 to 20 parts by weight of a viscosity modifier and 1 to 2 parts by weight of a catalyst, wherein the solvent, the alkyl acrylate, The number average molecular weight (Mn) and the acid value of the water-soluble resin formed from the latex, the acrylic acid, the methacrylic acid, the reactive cross-linking agent, the reactive monomer, the coupling agent, the viscosity modifier and the catalyst are 1000 to 6000 20 to < RTI ID = 0.0 > 150. ≪ / RTI >